Phase equilibria was investigated in the Ti-Fe-P system at T = 1070 K in the region 0–67 at.% of P, employing X-ray powder diffraction. The two ternary compounds, namely Ti0.5–0.8Fe1.5−1.2P (Co2Si-type; space group Pnma; a = 0.5964(2)–0.6011(3), b = 0.3575(3)–0.3600(1), c = 0.6828(2)–0.6882(2) nm) and Ti0.85−1.25Fe1.15−0.75P (ZrNiAl-type; space group P-62m; a = 0.6071(4)–0.6117(1), c = 0.3510(9)–0.3506(1) nm) exist in the Ti-Fe-P system at this temperature. The crystal structure of the Ti0.85–1.25Fe1.15−0.75P compound was additionally determined by X-ray single crystal diffraction on the phase with stoichiometric composition. The substitutions of Ti by Fe were observed for Ti5P3.16, Ti3P and TiP phases, and Fe for Ti in the case of Fe3P, Fe2P binary compounds.
Graphical abstract
Similar content being viewed by others
References
A.O. Oliynyk, Y.F. Lomnytska, M.V. Dzevenko, S.S. Stoyko, A. Mar, Inorg. Chem. 52, 983 (2013)
H. Kaneko, T. Nishizawa, K. Tamaki, J. Jpn. Inst. Met. 29, 159 (1965)
S. Rundqvist, P.C. Nawapong, Acta Chem. Scand. 20(8), 2250 (1966)
H. Ohtani, N. Hanaya, M. Hasebe, S.-i. Teraoka, M. Abe, Calphad. 30, 147 (2006)
L.G. Akselrud, P.Yu. Zavalii, Yu.N. Grin, V.K. Pecharski, B. Baumgartner, E. Wölfel, Mat. Sci. Forum 133–136, 335 (1993)
N. Masciocchi, The Rigaku Journal 14(2), 9 (1997)
J. Rodriguez-Carvajal, Commission on powder diffraction (IUCr). Newsl. 26, 12 (2001)
G.M. Sheldrick, SHELXL-97, Program for Crystal Structure Refinement (University of Göttingen, Germany, 1997) 12–19
T.B. Massalski (Ed.), Binary Alloy Phase Diagrams, 2nd edition (ASM International, Materials Park, OH, 1990) 827
P. Villars (Ed.), Pearson’s Handbook Desk Edition. Crystallographic Data for Intermetallic Phases (Metals Park, OH 44070, 1997) 2888
P.J. Brown, J. Deportes, B. Ouladdiaf, J. Phys.: Condens. Matter. 4(49), 10015 (1992)
M. Gemmi, X.-D. Zou, S. Hovmoeller, A. Migliori, M. Vennstrom, Y. Andersson, Acta Cryst. A. 59, 117 (2003)
T. Lundstroem, P.O. Snell, Acta Chem. Scand. 21, 1343 (1967)
J. Emsley, The Elements, 3th edition (Oxford University Press, Oxford, 1998) 300
V.S. Babizhetskyy, Ya.F. Lomnytska, Inorg. Mater. 38(9), 905 (2002)
Ya.F. Lomnytska, Inorg. Mater. 37(1), 9 (2001)
Ya.F. Lomnytska, L.P. Agatiska, Yu.B. Kuzma, Ukr. Chim. Journal. 47(2), 142 (1981) (in Russian)
S.V. Muchnik, Ya.F. Lomnytska, V.B. Chernogorenko, K.A. Lynchak, Poroshkovaya Metallurgia 2, 71 (1989) (in Russian)
Yu.B. Kuzma, Ya.F. Lomnytska, V.V. Sapovskiy, Neorg. Mater. 17(4), 647 (1981) (in Russian)
M. Klimczak, E. Talik, J. Jarosz, T. Mydlarz, Mater. Sci. Poland. 26(4), 35 (2008)
J. F. Riecken, G. Heymann, H. Huppertz, R. Pöttgen, Z. Anorg. Allg. Chem. 633(5–6), 869 (2007)
A. Nylund, A. Roger, J.P. Senateur, R. Fruchart, Monatsh. Chem. 102(5), 1631 (1971)
Author information
Authors and Affiliations
Corresponding author
About this article
Cite this article
Toma, O., Dzevenko, M., Oliynyk, A. et al. The Ti-Fe-P system: phase equilibria and crystal structure of phases. cent.eur.j.chem. 11, 1518–1526 (2013). https://doi.org/10.2478/s11532-013-0282-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.2478/s11532-013-0282-8