Abstract
The grain refinement effect of a pulsed magnetic field on superalloy IN718 was investigated. The experimental results show that fine equiaxed grains are acquired under the pulsed magnetic field. The refinement effect of the pulsed magnetic field is affected by the mold temperature. And the mixed grains are found in the solidified microstructures under the pulsed magnetic field. The origin of nuclei under the pulsed magnetic field is from the mold wall because of the rough mold surface, the undercooling, and the melt vibration, which all contribute to the refinement of solidified grains.
Similar content being viewed by others
References
B.T. Zi, Q.X. Ba, J.Z. Cui, Y.G. Bai, and X.J. Yan: Effect of strong pulsed electromagnetic field on metal’s solidified structure. Acta Physica Sinica 49, 1010 (2000).
Y.L. Gao, Q.S. Li, Y.Y. Gong, and Q.J. Zhai: Comparative study on structural transformation of low-melting pure Al and high-melting stainless steel under external pulsed magnetic field. Mater. Lett. 61, 4011 (2007).
Q.S. Li, C.J. Song, H.B. Li, and Q.J. Zhai: Effect of pulsed magnetic field on microstructure of 1Cr18Ni9Ti austenitic stainless steel. Mater. Sci. Em., A 466, 101 (2007).
Q. Zhou, Y.S. Yang, and J.C. Ma: Effect of pulsed magnetic field on solidified structure of AZ91D magnesium alloy. Foundry 56, 148 (2007).
B. Wang, Y.S. Yang, J.X. Zhou, and W.H. Tong: Microstructure refinement of AZ91D alloy solidified with pulsed magnetic field. Trans. Nonferrous Met. Soc. China 18, 536 (2008).
X.P. Ma, Y.J. Li, Y.S. Yang: Grain refinement effect of pulsed magnetic field on as-cast superalloy K417. J. Mater. Res. 24, 2670 (2009).
X.P. Ma, Y.J. Li, Y.S. Yang: Grain refinement effect of pulsed magnetic field on solidified microstructure of superalloy IN718. J. Mater. Res. 24, 3174 (2009).
A. Ohno: Solidification, the Separation Theory and Its Practical Applications (Springer-Verlag Press, Berlin, Germany, 1987), p. 15.
A. Ohno, T. Motegi, and H. Soda: Origin of the equiaxed crystals in castings. Transactions ISIJ 11, 18 (1971).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ma, X., Li, Y. & Yang, Y. The origin of nuclei and the refinement mechanism for solidified superalloy IN718 under pulsed magnetic field. Journal of Materials Research 24, 3689–3692 (2009). https://doi.org/10.1557/jmr.2009.0445
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/jmr.2009.0445