Electromigration study in the eutectic SnBi solder joint on the Ni/Au metallization

  • Article
  • Published:
Journal of Materials Research Aims and scope Submit manuscript

Abstract

Microstructural evolution and interfacial reaction in the eutectic SnBi solder joint on the Ni/Au metallization with and without the current stressing of 6.5 × 103 A/cm2 at 70 °C for 5 to 15 days were investigated. Electromigration is found to have significant effects not only on the phase formation at the joint interface but also on the phase coarsening and mass accumulation of Bi in the solder. In the solder joint without the current stressing, only a thin Ni3Sn4 phase was formed at the joint interface. For the solder joint with the current stressing, in addition to the Ni3Sn4 phase, a thick Au–Ni–Bi–Sn phase was formed at the joint interface after 10 days. However, the Au–Ni–Bi–Sn phase was not observed at the anode-side joint interface after 15 days of current stressing. Coarsening of the Bi-rich grain in the solder joint with the current stressing was much faster than that without the current stressing. Mass accumulation of Bi was observed at the anode side of the solder joint with the current stressing and the thickness of the Bi-rich accumulation layer increased with current stressing time. Based on the accumulation rate of the Bi-rich layer and the growth rate of the Bi-rich grain, the product of diffusivity and effective charge number of Bi in the eutectic SnBi solder is calculated to be 4.72 × 10−10 cm2/s.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. F. Hua, Z. Mei, and J. Glazer: Eutectic Sn–Bi as an alternative to Pb-free solders, in Proc. 48th Electronic Components and Technology Conf. (IEEE, New York, 1998), p. 277.

    Google Scholar 

  2. P.S. Ho, T. Kwok: Electromigration in metals. Rep. Prog. Phys. 52, (3), 301 (1989).

    Article  Google Scholar 

  3. K.N. Tu: Recent advances on electromigration in very-large-scale-integration of interconnects. J. Appl. Phys. 94, 5451 (2003).

    Article  CAS  Google Scholar 

  4. E.C.C. Yeh, W.J. Choi, K.N. Tu, P. Elenius, H. Balkan: Current-crowding-induced electromigration failure in flip chip solder joints. Appl. Phys. Lett. 80, 580 (2002).

    Article  CAS  Google Scholar 

  5. Y.C. Hu, Y.H. Lin, C.R. Kao, K.N. Tu: Electromigration failure in flip chip solder joints due to rapid dissolution of copper. J. Mater. Res. 18, 2544 (2003).

    Article  CAS  Google Scholar 

  6. S. Brandenburg and S. Yeh: Electromigration studies of flip chip bump solder joints. Proc. Surface Mount Int. Conf. and Exposition, SM198, San Jose, CA, Aug. 23–27 (Edina, MN: SMTA, 1998), p. 337.

    Google Scholar 

  7. T.Y. Lee, K.N. Tu, S.M. Kuo, D.R. Frear: Electromigration of eutectic SnPb solder interconnects for flip chip technology. J. Appl. Phys. 89, 3189 (2001).

    Article  CAS  Google Scholar 

  8. J.Y. Choi, S.S. Lee, Y.C. Joo: Electromigration behavior of eutectic SnPb solder. Jpn. J. Appl. Phys. 41, 7487 (2002).

    Article  CAS  Google Scholar 

  9. G.A. Rinne: Issues in accelerated electromigration of solder bumps. Microelectron. Reliab. 43, 1975 (2003).

    Article  CAS  Google Scholar 

  10. H. Ye, C. Basaran, D.C. Hopkins: Damage mechanics of microelectronics solder joints under high current densities. Int. J. Solids Struct. 40, 4021 (2003).

    Article  Google Scholar 

  11. H. Ye, C. Basaran, D.C. Hopkins: Pb phase coarsening in eutectic Pb/Sn flip chip solder joints under current stressing. Int. J. Solids Struct. 41, 2743 (2004).

    Article  Google Scholar 

  12. C.M. Chen, S.W. Chen: Electromigration effect upon the Sn–0.7 wt% Cu/Ni and Sn–3.5 wt% Ag/Ni interfacial reactions. J. Appl. Phys. 90, 1208 (2001).

    Article  CAS  Google Scholar 

  13. S.W. Chen, C.M. Chen: Electromigration effects upon interfacial reactions. JOM 55, 62 (2003).

    Article  CAS  Google Scholar 

  14. Binary Alloy Phase Diagrams, edited by T.B. Massalski (ASM International, Materials Park, OH, 1990).

    Google Scholar 

  15. B.L. Young, J.G. Duh: Interfacial reaction and microstructural evolution for electroplated Ni and electroless Ni in the under bump metallurgy with 42Sn58Bi solder during annealing. J. Electron. Mater. 30, 878 (2001).

    Article  CAS  Google Scholar 

  16. C.S. Huang, J.H. Yeh, B.L. Young, J.G. Duh: Phenomena of electroless Ni–P and intermetallic-compound stripping and dissolving in Sn–Bi and Sn–Pb solder joints with Au/EN/Cu metallization. J. Electron. Mater. 31, 1230 (2002).

    Article  CAS  Google Scholar 

  17. B.L. Young, J.G. Duh, G.Y. Jang: Compound formation for electroplated Ni and electroless Ni in the under-bump metallurgy with Sn-58Bi solder during aging. J. Electron. Mater. 32, (12), 1463 (2003).

    Article  Google Scholar 

  18. C.L. Luo Master thesis, National Central University, Chungli City, Taiwan, 2000.

    Google Scholar 

  19. K.N. Tu: Electromigration in stressed thin films. Phys. Rev. B 45, 1409 (1992).

    Article  CAS  Google Scholar 

  20. J. Glazer: Metallurgy of low temperature Pb-free solders for electronic assembly. Int. Mater. Rev. 40, (2), 65 (1995).

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Chemical Engineering, National Chung-Hsing University, Taichung, 402, Taiwan, Republic of China

    Long-tai Chen & Chih-ming Chen

Authors
  1. Long-tai Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Chih-ming Chen
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Chih-ming Chen.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Chen, Lt., Chen, Cm. Electromigration study in the eutectic SnBi solder joint on the Ni/Au metallization. Journal of Materials Research 21, 962–969 (2006). https://doi.org/10.1557/jmr.2006.0113

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1557/jmr.2006.0113

Search

Navigation