ZnO:Al (ZAO) films were deposited on fused silica substrates heated to 350 °C by dc magnetron reactive sputtering from a Zn target mixed with 1.5 wt% Al. Films deposited on a substrate heated to a temperature between room temperature and 300 °C were (001)-oriented crystals, but those grown at 350 °C consisted of crystallites with (001) and (101) orientations. The dependence of electrical properties such as resistivity, carrier concentration, and Hall mobility on temperature was measured. The results indicate that the carrier concentration and Hall mobility increase with increasing temperature up to 250 °C, though the Al content remains unchanged in this temperature range. The probable mechanisms are discussed. The minimum resistivity of ZAO films is 4.23 × 10−4 Ω cm, with a carrier concentration of 9.21 × 1020 cm−3 and a Hall mobility of 16.0 cm2 v−1 s−1. The films show a visible transmittance of above 80%.
Similar content being viewed by others
References
G.A. Hirata, J. Mckittrik, T. Cheeks, J.M. Siqueiros, J.A. Diaz, O. Contreras, and O.A Lopez, Thin Solid Films 288, 29 (1996).
P. Nunes, B. Fernandes, E. Fortunan, P. Vilarinlo, and R. Martins, Thin Solid Films 337, 176 (1999).
K.T.R. Reddy and R.W. Miles, J. Mater. Sci. Lett. 17, 279 (1998).
Z.C. Jin, I. Hamberg, and C.G. Granqvist, J. Appl. Phys. 64, 5117 (1988).
S. Major, S. Kumar, M. Bhatnagar, and K.L. Chopra, Appl. Phys. Lett. 40, 394 (1986).
Y. Igasaki and H. Saito, J. Appl. Phys. 69, 2190 (1991).
R. Cebulla, R. Wendt, and K. Ellmer, J. Appl. Phys. 83, 1087 (1998).
K.C. Park, D.Y. Ma, and K.H. Kim, Thin Solid Films 305, 201 (1997).
K. Ellmer, F. Kudella, R. Mientus, R. Schieck, and S. Fiechter, Thin Solid Films 247, 15 (1994).
G.L. Harding, B. Window, and E.C. Horrigan, Sol. Energy Mater. 22, 69 (1991).
M. Chen, C. Sun, J. Gong, R.F. Huang, and L.S. Wen, The ‘99 Asian Conference on Electrochemistry, (The Electrochemical Society of Japan, May 19–21, 1999) Japan, p. 29.
A. Segmuller and M. Murakami, in Analytical Techniques for Thin Films, edited by K.N. Tu and R. Rosenberg (Academic, Boston, MA, 1988), p. 143.
A. Kuroyanagi, J. Appl. Phys. 66, 5492 (1989).
V. Gupta and A. Mansingh, J. Appl. Phys. 80, 1063 (1996).
O. Kuvaschewski and C.B. Alocok, Metallurgical Thermochemistry, 5th ed. (Pergamon, London, U.K., 1979), p. 376.
M. Chen, X. Wang, Z.L. Pei, C. Sun, and L.S. Wen, Appl. Surf. Sci. 158, 134 (2000).
M. Chen, Z.L. Pei, X. Wang, Y.H. Yu, R.F. Huang, and L.S. Wen, J. Phys. D: Appl. Phys. 33, 2538 (2000).
L. Bárdoš and M. Libra, Vacuum 39, 33 (1989).
Y. Qu, T.A. Gessert, K. Ramanathan, R.G. Dhere, R. Noufi, and T.J. Coutts, J. Vac. Sci. Technol. A11, 996 (1993).
S. Ghosh, A. Sarkar, S. Chaudhuri, and A.K. Pal, Thin Solid Films 205, 64 (1991).
M. Chen, Ph.D. Thesis, Institute of Metal Research, Chinese Academy of Science (June 1999).
M. Chen, X.D. Bai, J. Gong, C. Sun, R.F. Huang, and L.S. Wen, J. Mater. Sci. Technol. 16, 281 (2000).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chen, M., Pei, Z.L., Wang, X. et al. Dependence of structural, electrical, and optical properties of ZnO:Al films on substrate temperature. Journal of Materials Research 16, 2118–2123 (2001). https://doi.org/10.1557/JMR.2001.0288
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2001.0288