Abstract
It is known that diamond films display poor adhesion on metals such as copper and steel. One solution to overcome the poor adhesion is to use interlayer materials. In this study we report results of an investigation of the adhesion behavior of diamond on pure chromium (Cr) and titanium (Ti) substrates. Cr and Ti are promising interlayer materials for adhering diamond to stainless steel. The coating adhesion was studied using indentation tests combined with acoustic emission signals during loading. It was found that a 105-N load indentation caused the film to delaminate from the Cr substrate, while the diamond film remained attached to the titanium even after the indentation at 180 N. Micro-Raman spectroscopy was used to monitor the film stress. The diamond films grown on Ti substrates were found to be less stressed than the films grown on Cr substrates. Therefore, Ti was used in thin-film form to obtain adherent diamond coatings on steel.
Similar content being viewed by others
References
Properties of Natural and Synthetic Diamond, edited by J.E. Field (Academic Press, San Diego, CA, 1992), p. 667.
J.C. Angus and C.C. Hayman, Science 241, 913 (1988).
K.E. Spear, J. Am. Ceram. Soc. 72, 171 (1989).
W.A. Yarbrough and R. Messier, Science 247, 688 (1990).
M. Nesladek, J. Spinnewyn, C. Asinari, R. Lebout, and R. Lorent, Diamond Relat. Mater. 3, 98 (1993).
T.P. Ong and R.P.H. Chang, Appl. Phys. Lett. 58, 358 (1991).
P.S. Weiser, S. Prawer, A. Hoffman, R.R. Manory, P.J.K. Paterson, and S-A. Stuart, J. Appl. Phys. 72, 4643 (1992).
M.N.R. Ashfold, P.W. May, C.A. Rego, and N.M. Everitt, Chem. Soc. Rev. 23, 21 (1994).
M.L. Hartsell and L.S. Plano, J. Mater. Res. 9, 921 (1994).
Q.H. Fan, J. Grácio, and E. Pereira, J. mater. Res. 13, 2787 (1998).
V.G. Ralchenko, E.D. Obraztsova, K.G. Korotoushenko, S.M. Pimenov, A.A. Smolin, V.G. Pereverzev, Y.V. Lakhotin, and E.N. Loubnin, Proceedings of the Applied Diamond Conference 1995, Aug. 21–24, Gaithersburg, MD (1995), p. 635–8.
J. Narayan, V.P. Godbole, G. Matera, and R.K. Singh, J. Appl. Phys. 71, 966 (1992).
O. Glozman, A. Bener, D. Shechtman, A. Hoffman, Diamond Relat. Mater. 7, 597 (1998).
Q.H. Fan, A. Fernandes, E. Pereira, and J. Grácio, J. Mater. Res. 14, 1142 (1999).
S.J. Bull and D.S. Rickerby, in Advanced Surface Coatings: A Handbook of Surface Engineering, edited by D.S. Rickerby and A. Matthews (Chapman and Hall, New York, 1991), p. 315.
CRC Materials Science and Engineering Handbook, edited by J.F. Shackelford, W. Alexander, and J.S. Park (CRC Press, Boca Raton, FL, 1994), p. S-20.
J.W. Ager and M.D. Drory, Phys. Rev. B 48, 2601 (1993).
V.G. Ralchenko, A.A. Smolin, V.G. Pereverzev, E.D. Obraztsova, K.G. Korotoushenko, V.I. Konov, Y.V. Lakhotkin, and E.N. Loubnin, Diamond Relat. Mater. 4, 754 (1995).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Fan, Q.H., Grácio, J., Pereira, E. et al. Study of diamond adhesion behavior on chromium and titanium for obtaining adherent diamond coatings on steel. Journal of Materials Research 15, 2330–2335 (2000). https://doi.org/10.1557/JMR.2000.0335
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.2000.0335