Abstract
Lateral diffusion couples containing Al islands on Pd–Si multiple layers are used to study Al–Pd2Si reactions. The Pd2Si phase was first formed in the Pd–Si multiple-layer region after furnace annealing at 225 °C. Then, the Al–Pd2Si lateral couples were in situ annealed in a transmission electron microscope at temperatures ranging from 377–438 °C. The laterally growing region is composed of the Al3Pd2 compound and Si precipitates, as identified by selected area diffraction (SAD). During the in situ anneals, transmission electron microscopy (TEM) images were recorded by a video cassette recorder allowing thereafter a kinetic study. The lateral growth is parabolically dependent on the annealing time. An activation energy of 1.7 eV is found for this diffusion process.
Similar content being viewed by others
References
H. H. Hosack, J. Appl. Phys. 44, 3476 (1973).
U. Köster, P. S. Ho, and J. E. Lewis, J. Appl. Phys. 53, 7436 (1982).
P. O. Ho, J. E. Lewis, and U. Köster, J. Appl. Phys. 53, 7445 (1982).
E. Kökelek and G. Y. Robinson, Thin Solid Films 53, 135 (1978).
G. J. van Gurp, J. L. C. Daams, A. van Oostrom, L. J. M. Augustus, and Y. Tamminga, J. Appl. Phys. 50, 6915 (1979).
L. R. Doolittle, Nucl. Instrum. Methods B9, 344 (1985).
E. G. Colgan, J. Appl. Phys. 62, 2269 (1987).
Joyce C. Liu, B. Blanpain, and J. W. Mayer (unpublished research).
G. V. Samsonov and I. M. Vinitiskii, Handbook of Refractory Compounds (IFI/Plenum, New York, 1980).
R. Ferro and R. Capelli, Atti. Accad. Naz. Lincei, Rend. Classe Sci. Fis. Mat. Nat. 34, 659 (1963).
E. G. Colgan, Ph.D. Thesis, Cornell University, 1987.
S. P. Murarka, Silicides for VLSI Applications (Academic Press, New York, 1983), p. 157.
A. J. McAlister, Bull, of Alloy Phase Diagrams 7, 368 (1986).
R. W. Bené, J. Appl. Phys. 61, 1826 (1987).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Liu, J.C., Mayer, J.W. Compound formation and kinetics in Al–Pd2Si reactions. Journal of Materials Research 4, 336–342 (1989). https://doi.org/10.1557/JMR.1989.0336
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1989.0336