Abstract
A new, apparently metastable, Mo–Ni boride phase has been observed in transmission electron microscope samples of rapidly consolidated MoNiFeB metallic glass powders. The phase is cubic with lattice parameter 1.083 nm. Its space group as determined by electron diffraction is Fd $\overline 3$m and its approximate composition is Mo3Ni3B. Because its structure, its composition, and its role as a transition phase are analogous to those of η carbide (M6C) in steels and cemented carbides, this phase has tentatively been named “η boride.”
Similar content being viewed by others
References
H. L. Marcus, D. L. Bourell, Z. Eliezer, C. Persad, and W. Weldon, J. Metals 39, 6 (1987).
H. J. Goldschmidt, Interstitial Alloys (Plenum, New York, 1967).
J. B. Walters and T. A, Aanstoos, Met. Prog. 127, 25 (1985).
Y. W. Kim, Ph. D. dissertation, The University of Texas at Austin, 1987. Available from University Microfilms, Ann Arbor, MI.
B. F. Buxton, J. A. Eades, J. W. Steeds, and G. M, Rackham, Proc. R. Soc. London 281, 171 (1976).
J. W. Steeds, in Introduction to Analytical Electron Microscopy, edited by J. J. Hren, J. I. Goldstein, and D. C. Joy (Plenum, New York, 1979), pp. 387–422.
M. Raghavan, J. C. Scanlon, and J. W. Steeds, Met. Trans. A 15A, 1299 (1984).
J. Gjønnes and A. F. Moodie, Acta Cryst. 19, 65 (1965).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kim, Y.W., Rabenberg, L. & Bourell, D.L. Identification of an η boride phase as a crystallization product of a NiMoFeB amorphous alloy. Journal of Materials Research 3, 1336–1341 (1988). https://doi.org/10.1557/JMR.1988.1336
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1557/JMR.1988.1336