Abstract
The isothermal section of the Ti-Ni-Si ternary system at 1100 °C was constituted. Twenty-one single-phase areas were determined. The binary Ti3Si phase proposed to occur at 1100 °C was not found in the investigation. A new phase, with the composition of NiTi4Si4 named H, was detected. Some of the ternary compounds show noticeable composition ranges, especially G′-Ni3Ti2Si.
Similar content being viewed by others
References
J.H. Westbrook, R.K. Di Cerbo, and A.J. Peat, Rep. 58-rc-2117, General Electronic Research Laboratory, 1958
V.Ya. Markiv, E.I. Gladyshevskii, P.I. Kripyakevich, and T.I. Fedouk, Inorganic Mater., TR: Izv. Akad. Nauk SSSR, Neorgan. Mater, Vol 2 (No. 7), 1966, p 1126
K.J. Williams, J. Inst. Met., Vol 99, 1971, p 310
H.J. Beattie, Jr. and F.L. Ver Snyder, Nature, Vol 178, 1956, p 20
H.J. Beattie, Jr. and W.C. Hagel, Trans. Met. Soc. AIME, Vol 209, 1957, p 911
E.I. Gladyshevskii, Sov. Powder Metall. Met. Ceram., Vol 1, 1962, p 262
D.I. Bardos, K.P. Gupta, and PA. Beck, Trans. Met. Soc. AIME, Vol 221, 1961, p 1087
J. Steinmets, J.-M. Albrecht, and B. Malaman, C.R. Hebd. Seánces Acad. Sci., Ser. C, Sci. Chem., Vol 279C, 1974, p 1119
W. Jeitschko, A.G. Jordan, and PA. Beck, Trans. Met. Soc. AIME, Vol 245, 1969, p 335
F.X. Spiegel, D.I. Bardos, and PA. Beck, Trans. Met. Soc. AIME, Vol 227, 1963, p 575
C.B. Shoemaker and D.P Shoemaker, Acta Crystallogr., Vol 18, 1965, p 900
L.S. Hung and J.W. Mayer, J. Appl. Phys., Vol 60 (No.3), 1986, p 1002
X. Hu, Y. Liu, G. Chen, and K. Ni, J. Mater. Sci. Technol., Vol 14 (No.2), 1998, p 121
J.L. Murray, Phase Diagrams of Titanium Alloys, ASM International, 1987
P. Nash and A. Nash, in Binary Alloy Phase Diagrams, American Society for Metals, 1986, p 1755
M. Hansen, H.D. Kessler, and D.J. McPherson, Trans. ASM, Vol 44, 1952, p 518
V.N. Svechnikov, Yu.A. Kocherzhisky, and L.M. Yupko, Dokl. Akad. Nauk SSSR, Vol 193 (No. 2), 1970, p 393
H.J. Seifert, H.L. Lukas, and G. Petzow, Z. Metallkde., Vol 87 (No. 1), 1996, p 2
O. Schob, H. Nowotny, and F. Benesovsky, Pulver-metall., Vol 10, 1962, p 65
W. Rossteutscher and K. Schubert, Z. Metallkde., Vol 56, 1965, p 813
J.J. Nickl and H. Sprenger, Z. Metallkde., Vol 60, 1969, p 136
J.J. Nickl and K.K. Schweitzer, Z. Metallkde., Vol 61, 1970, p 54
W.J.J. Wakelkamp, F.J.J. van Loo, and R. Metselaar, J. Eur. Ceram. Soc, Vol 8, 1991, p 135
W. Buher, R. Gotthardt, A. Kulik, O. Mercier, and F. Staub, J. Phys., F: Met. Phys., Vol 13, 1983, p L77
X. Hu, G. Chen, and K. Ni, J. Univ. Sci. Technol. Beijing (English ed.), Vol 4 (No. 3, 5), 1997, p 5
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Hu, X., Chen, G., Ion, C. et al. The 1100 °C isothermal section of the Ti-Ni-Si ternary system. JPE 20, 508 (1999). https://doi.org/10.1361/105497199770340761
Received:
Revised:
DOI: https://doi.org/10.1361/105497199770340761