Abstract
When investigating the diffusion layers grown by the reaction couple method at the Ni-Zn interface at 350 and 400 ‡C, the homogeneity ranges of the 5 and γ phases were found to be 87.5 ± 0.2 to 89.0 ± 0.2 at. % Zn and 73.1 ±03 to 86.2 ± 0.3 at. % Zn, respectively. Chemical compositions of the phases investigated can therefore be expressed in the simplest form as δNiZn7 to 8 and γNiZn3 to 6.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
Cited References
M. Hansen and K. Anderko,Constitution of Binary Alloys, McGraw-Hill, NewYork(1958).
P. Nash and Y. Y Pan, “The Ni-Zn (Nickel-Zinc) System,”Bull. Alloy Phase Diagrams, 8, 422(1987).
T.B. Massalski, J.L. Murray, L.H. Bennett, and H. Baker, Ed.,Binary Alloy Phase Diagrams, Vol 2, American Society for Metals, Metals Park, OH, 1778(1986).
V.I. Dybkov,Growth Kinetics of Chemical Compound Layers, Cambridge International Science Publishing, Cambridge (1998).
J.K. Critchley and S. Denton, “The Crystal Structure of δ-Ni-Zn,”J. Inst. Metals, 99, 26 (1979).
W. Heike, J. Schramm, and O. Vaupel, “The System Nickel-Zinc,”Metallwirtschaft, 15, 655 (1936) in German.
K. Tamaru and A. Osawa, “On a Further Investigation of the Equilibrium Diagram of the Nickel-Zinc System,”Sci Rep. Tohoku Imp. Univ., 23, 794 (1935).
G. Nover and K. Schubert, “The Crystal Structure of NiZn3.r,”J. Less-CommonMet., 75, 51 (1980).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dybkov, V.l., Duchenko, O.V. The homogeneity ranges of the delta (δ) and gamma (γ) phases of the Ni-Zn binary system grown by the reaction couple method. JPE 19, 434 (1998). https://doi.org/10.1361/105497198770341914
Received:
Revised:
DOI: https://doi.org/10.1361/105497198770341914