Abstract
Background
Although microbial fuel cells (MFCs) represent a promising technology for capturing renewable energy from wastewater, their scaling-up is significantly limited by a slow-rate cathodic oxygen reduction reaction (ORR) and the development of a resilient anodic microbial community. In this study, mixed transition metal oxides of nickel and copper (Ni and Cu), supported on a graphene (G) (NiO–CuO/G) electrocatalyst, were synthesized and tested as a cost-effective cathode for ORR in MFCs. Electrochemical measurements of electrocatalyst were conducted using a rotating disk electrode (RDE) and linear sweep voltammetry (LSV) in a neutral electrolyte, and compared with a benchmark Pt/C catalyst. Furthermore, the long-term performance of the as-synthesized electrocatalyst was evaluated in a single-chamber MFC by measuring organic matter removal and polarization behavior. The successful enrichment of electroactive biofilm was also monitored using transmission electron microscopy and the Vitek2 compact system technique.
Results
When compared with the benchmark platinum cathode, the NiO–CuO/G electrocatalyst exhibited high selectivity toward ORR. The rotating disk electrode (RDE) experiments reveal that ORR proceeds via a 4-electron ORR mechanism. Furthermore, the NiO–CuO/G electrocatalyst also exhibited a high power density of 21.25 mW m−2 in an air-cathode MFC, which was slightly lower than that of Pt/C-based MFC (i.e., 50.4 mW m−2). Biochemical characterization of the most abundant bacteria on anodic biofilms identified four genera (i.e., Escherichia coli, Shewanella putrefaciens, Bacillus cereus, and Bacillus Thuringiensis/mycoides) that belonged to Gammaproteobacteria, and Firmicutesphyla.
Conclusions
This study demonstrates that the NiO–CuO/G cathode had an enhanced electrocatalytic activity toward ORR in a pH-neutral solution. This novel mixed transition metal oxide electrocatalyst could replace expensive Pt-based catalysts for MFC applications.
Similar content being viewed by others
Background
Microbial fuel cells (MFCs) are anaerobic biotechnology systems that convert the stored chemical energy in waste streams into electricity through the metabolic pathway of microbial communities [1, 2]. The bioelectrochemical reactions that generate electricity in MFCs involve the oxidation of organic matter in the anode chamber and the reduction of electron acceptors (ideally oxygen) in the cathode chamber. The hallmark of an MFC is the ability of electroactive biofilms (known as electricigens or anode-respiring bacteria) to oxidize organic matter and respire resultant electrons to anode surfaces, which are then transferred to the cathode via an external circuit. This sticky biofilm matrix consists of extracellular proteins, sugars, and a complex bacterial milieu [3]. Concurrently, generated protons (H+) move into the electrolyte (leading to a negative anode potential) via a semi-permeable ion exchange membrane, where the reduction of an electron acceptor (ideally Oxygen) occurs to form H2O [4, 5].
The major limiting issues affecting MFCs efficiency is the low power output, which currently restricted due to either the cathodic reaction efficiency or high internal resistance [6]. Therefore, it is essential to categorize the foremost limiting parameters that affecting its performance. These are can be classified into three categories: (1) system architecture, (2) biological conditions, and (3) operational conditions. These parameters include anodic microbial communities, mediators, substrate types, catalyst materials, and membranes. Standard operating conditions are facilitated by pH, external resistance, temperature, ionic concentration, and the catholyte aeration flow rate. Thus, because of these limiting parameters, the technological implementation of MFCs for industrial, and social applications is restricted [7, 8].
However, considerable research has sought to address these limitations [7]. A commonly used low-cost design is the air-cathode, single-chamber MFC, which lacks an ion exchange membrane between anode and cathode. When compared with other MFC configurations, the air-cathode MFC approach is a promising option for wastewater treatment owing to the availability and high redox potential of electron acceptors (i.e., air) [9]. For instance, Ieropoulos et al. [10] demonstrated that mediator-less, single-chambered MFCs (SCMFCs) were advantageous for wastewater treatment and power generation when compared with two-chambered systems. This was due to mediator-less SCMFCs’ higher power densities, lower internal resistance, and simple configuration.
Although early studies showed the possibility of using pure cultures in MFCs for generating electricity from simple donor substrates, mixed-culture microbial communities offer an ecological advantage for producing electricity when complex waste streams (e.g., real wastewater) are used as the sole substrates [11]. In this context, Watson and Logan [12] compared power production by Shewanella oneidensis MR-1 to mixed cultures in a cube-shaped MFC and observed that power production (148 mW m−2) was lower than that by mixed cultures (858 mW m−2). They reported that mixed cultures were more desirable than pure cultures because of their easy access, broader adaptability of feedstock, simple operating requirements, advantages in practical applications, and high functional redundancy [12]. In terms of pH, Gil et al. [13] detected a pH difference of 4.1 units after a 5-h operation when an initial pH of 7 was used without buffering. The addition of a phosphate buffer (pH 7.0) shifted the MFC pH to less than 0.5 units, and the current output increased by approximately 2-fold. It is likely that the buffer compensated for the slow proton transport rate and improved proton availability for cathodic reactions.
The cathodic catalyst material considered as one of the main limiting issues that plays a noteworthy function in improving the MFCs efficiency due to its direct effect on the oxygen reduction reactions (ORR) [14] since the kinetic rate of ORR in the neutral pH aqueous electrolyte requires high activation energy of approximately 498 kJ mol−1 to split the oxygen (O2) [15]. Thus, to enhance the efficiency of MFCs, modification of electrode materials using highly effective ORR electrocatalysts is warranted [16]. Although platinum (Pt) has been commonly used as an electrocatalyst because of its high electrocatalytic activity toward ORR [17], its practical applications are restricted by high costs, low stability during long-term operations, and availability [18, 19]. Over the past decade, several studies have replaced expensive Pt electrocatalysts using cost-effective, non-precious metal oxide electrocatalysts, such as Pt-free transition metals oxides, e.g., cobalt (Co), iron (Fe), and manganese (Mn)-base electrocatalysts [20]. These oxides have gained increasing attention owing to their durability, high performance, and relatively low cost [21]. The use of transition mixed metal oxides electrocatalysts as cathode in MFCs demonstrates high catalytic enhancement activities, through which one metal oxide accelerates the cleavage of the O=O bond of molecular O2. After that, the cleavage is followed by the migration of the adsorbed O2 atoms into the other metal oxide, where the electro-reduction step takes place [22], e.g., the introduction of MFC enhancing metallic oxides such as MnOX [23], Co–Al2O3–rGO [24], (SSM/Co3O4) [25], Ppy/MoO 2[26], and Co0.5Zn0.5Fe2O4 [27, 28].
To date, only a small number of studies have investigated the use of non-precious nickel (Ni)-based electrocatalysts. Valipour et al. [5] studied the feasibility of Ni nanoparticles on a reduced graphene oxide (RGO) as a high efficient ORR cathode electrocatalysts in SCMFCs with a maximum power density of 581 ± 19 mW m−2, which was slightly lower than Pt/C cathode. Moreover, Huang et al. [29] suggested that Ni oxide supported on a carbon nanotube (NiO/CNT) is a promising non-precious metal composite for ORRs in SCMFCs. The system produced a maximum power density of 670 mW m−2. An SCMFC with a Pt-Ni nanoparticle alloy dispersed on carboxyl multi-wall CNTs produced a maximum power density of 1220 mW m−2 [16]. In addition, Ghasemi et al [28] generated a power density of approximately 94.4 mW m−2 with Ni nanoparticles using two cube-shaped chambers. Similarly, Liu and Vipulanandan [30] used Ni nanoparticles for two-chambered MFC application generated a power density of 0.07 mW m−2. In another study, Kartick et al. [31] investigated a dual-chamber MFC using a Ni nano fiber hybrid electrocatalyst supported on graphene (G) and reported a power density of 34 mW m−2. Furthermore, Champavert et al. [32] modified tetra Sulfonated phthalocyanine electrocatalysts with Ni and used them in a high-performance dual-chamber MFC that generated a maximum power density of 21.6 mW m−2. Additionally, Mohamed et al. [14] found that Ni nanoparticles had a maximum power density of 1630.7 mW m−2 in tested cobalt (Co)- and Cadmium (Cd)-based reagents. In addition, Chaturvedi et al. [33] accomplished the synthesis of different weight ratios of Co–Ni nanoparticles supported on an alumina-graphene oxide (Al2O3–GO) matrix to determine ORR activity in MFCs. The approach revealed that the Co–Ni(2:1)/Al2O3–GO catalyst exhibited an improved ORR rate with a maximum power density of 168 mW m−2, when compared with 102 mW m−2 for Pt/C.
Support materials are also essential for dispersing electrocatalyst particles, preventing self-aggregation, and improving MFC performance. In this regard, G is typically used as electrocatalyst support because of its large specific surface, high electrical conductivity combined with low internal resistance, and high chemical stability and anti-corrosion properties [34]. In addition, it possesses abundant surface functional groups that provide accessible active sites.
In this study, the feasibility of using NiO–CuO/G as a cathode electrocatalyst in MFCs was explored. Physical and electrochemical characterizations of the nano-electrocatalyst and isolated anodic strains were performed. Optimization of different operating conditions for MFCs was evaluated using the nano-electrocatalyst as a cathode, and the biochemical properties of isolated anodic strains were identified using the Vitek2 compact system method.
Methods
Chemicals
Hexahydrates of Ni and copper Cu nitrates (Ni(NO3)2.6H2O and Cu(NO3)2.6H2O) were purchased from Fisher Scientific (USA). Graphene (G) powder (average pore diameter 100 ± 10 Å) and 5wt.% Nafion solutions were purchased from Sigma-Aldrich (MO, USA). Pt on carbon Vulcan (30% Pt/C, E-tek, USA) electrocatalyst was obtained from the Fuel Cell Store (TX, USA). All supplies and chemical materials were of analytical grade purity and were used without further purification. All aqueous solutions were freshly prepared using double distilled water.
Synthesis of NiO–CuO/G electrocatalyst
NiO–CuO/G composites were prepared using a co-precipitation method [29]. In a typical synthesis, the mixed metal salt precursors of Ni(NO3)2.6H2O and Cu (NO3)2.6H2O were dispersed on high surface area G in double-distilled water. Then, pH was adjusted to approximately 10 using the drop-wise addition of 1.0 M NaOH using Benchtop pH meter (Adwa AD1000, Hungary) followed by vigorous stirring for 3 h to avoid agglomeration and to generate a homogeneous dispersion. The resulting black metal-hydroxide precipitate was filtered and washed several times using double-distilled water and adjusted to pH 7. After this, the final product was generated by drying the precipitate at 80 °C (TiTANOX oven, Italy) for 6 h to remove excess water. The dried precipitate was calcinated for 3 h at 300 °C in a muffle furnace (ShinSaeng Scientific, Korea) to form metal oxides. The corresponding mass ratio in the NiO–CuO/G was 30% of NiO–CuO to 70% of Graphene.
Electrochemical measurements using a rotating disk electrode
Electrochemical measurements were performed at room temperature (25 ± 1 °C) using an electrochemical workstation (PST006 Voltamaster, USA) and a rotating disk electrode (RDE; CTV 101 speed control unit, USA). The working electrode (with a geometrical surface area of 0.196 cm2) was either NiO–CuO/G- or Pt/C-deposited thin film on the surface of the glassy carbon electrode (GCE), while Pt wire and Ag/AgCl (Metrohm, Netherlands) were used as counter and reference electrodes, respectively. Before depositing the catalyst layer on the GCE, the GCE was mechanically polished using 0.05 μm alumina slurry on a soft cloth to generate a mirror-like surface. Finally, the GCE was rinsed in double-distilled water and acetone. Following this, 1.0 mg of electrocatalyst was sputtered and mixed with a drop of isopropanol on the GCE. After the isopropanol was dried, a drop of Nafion solution (5%) was pipetted onto the GCE surface to form a homogeneous thin layer. Finally, a second drop of isopropanol was added, and the electrocatalyst film dried at room temperature overnight.
Linear sweep voltammetry (LSV) studies were conducted in a 50-mM phosphate buffer solution (PBS, pH 7.2) at a scan rate of 10 mV s−1 in a potential range of (− 1000 to + 1000 mV vs. Ag/AgCl) (equivalent to − 780 to + 1220 mV vs. standard hydrogen electrode (SHE)) with different rotation speeds (i.e., 0 to 2400 rpm). Before electrochemical measurements were conducted, the electrolyte was sparged with ultra-pure oxygen (O2) for 30 min. For comparison, all electrochemical measurements were performed in nitrogen-saturated PBS. A schematic summary is presented in Figure S1.
Kinetic parameters were analyzed based on the Koutechy-Levich (K-L) equation derived from RDE studies to calculate electron transfer numbers (n) involved in the ORR process [35] as follows:
Where Id is the disk current density; Ik is the electrode potential-dependent kinetic current density; ω is the angular momentum (rads−1s1/2); n is the average number of electrons in the catalytic reaction; F is Faraday’s constant (96,485 C mol−1); D and C are the diffusion coefficient of dissolved oxygen (1.9 × 10−5 cm2 s−1) and the concentration of dissolved oxygen in 50 mM PBS (1.117 × 10−6 mol mL−1), respectively; v is the kinetic viscosity of the electrolyte (0.01073 cm2 s−1); and A is the geometric area of the disk electrode (0.196 cm2) [36].
MFC configuration
All MFC studies were conducted using single-chamber, air-cathode MFCs (6 cm long, 4.6 cm in diameter, total working volume = 100 mL) as described elsewhere [37] and illustrated in Figure S2. Anodes were three-dimensional carbon felt glued to the top of an externally connected anode port with effective dimensions of 2.5 × 2.5 × 0.6 cm and a projected surface area of 18.50 cm2. They were positioned on the other side of the cell (Parallel to the cathode) at a distance of ~ 5 cm from the cathode. Gas diffusion carbon cloth electrodes were used as cathode electrodes (6 × 6 cm each; surface area = 16.63 cm2) with a catalyst loading of 0.30 mg/cm2. Titanium wire were used as current collectors for both electrodes.
Cathode electrodes preparation
Cathode electrodes were prepared as described elsewhere [38]. The catalyst was maintained on the water-facing side of a cathode at a mass loading of 0.3 mg cm−2. Before coating, catalyst slurry was prepared by mixing NiO–CuO/G composites with a 5% Nafion solution. The mixture was ultra-sonicated at 60 °C for 30 min and uniformly dispersed onto the carbon cloth surface electrode (mesoporous gas diffusion; Fuel Cell Store, TX, USA). To reach the load of the electrode (0.3 mg cm−2), multiple catalyst ink layers were deposited on top of each other. Electrodes were dried at room temperature for 24 h before MFC studies. For comparison, 30 wt.% of a Pt catalyst on carbon Vulcan (surface area = ~ 220 m2 g−1; E-Tek, USA) was used as a cathode at a catalyst mass loading of 0.3 mg cm−2, using the same procedure as previously described.
MFC operation and analysis
MFCs were inoculated with aerobic activated sludge from a local municipal wastewater treatment plant (Benha, Egypt) and operated under a fed-batch mode for 60 days to allow biofilms to grow on anode surfaces [39]. MFCs were fed with artificial wastewater containing sodium acetate (2.0 g L−1) as the sole organic substrate in 50 mM phosphate buffer solution (BPS) (chemical oxygen demand (COD) concentration = 1472 ± 17 mg/L) supplemented with a 12.5 mL mineral solution and a 12.5 mL vitamin solution. The 50 mM PBS solution contained: NaHCO3: 2.5 g/L, NH4Cl: 0.2 g/L, KH2PO4: 13.6 g/L, KCl: 0.33 g/L, NaCl: 0.3 g/L, K2HPO4: 17.4 g/L, CaCl2.2H2O: 0.15 g/L, MgCl2: 3.15 g/L, and a yeast extract: 1 g/L. All MFC studies were conducted in triplicate to calculate average values.
MFCs were operated in a fed-batch mode at room temperature. They were monitored using a data acquisition system (LabJack U6-PRO, USA) connected to a personal computer. An external resistance of 1000 Ώ was used, unless otherwise stated. Current (mA m−2) and power densities (mW m−2) were calculated according to Ohm’s law as previously described [5, 37]. Polarization and power curves were plotted using a single-cycle technique by recording the pseudo-steady-state voltage across different external resistances, ranging from 175 KΩ to 50 Ω [40]. Internal resistance (Rint) was determined using linear regression corresponding to the Ohmic zone on the linear section of the polarization curve [41].
Influent and effluent COD concentrations were analyzed according to APHA standard methods for water and wastewater examination [42]. Organic concentrations were calculated as COD removal efficiency (COD R%), which was calculated using the following equation:
Where CODinitial is the COD concentration in the influent (mg COD/L), and CODfinal is the COD concentration in the final effluent at the end of MFC batch cycles (mg COD/L).
The Coulombic efficiency (CE) was calculated by normalizing the measured current with respect to the theoretical current based on consumed COD as follows:
Where CT is the theoretical coulombs and was estimated according to the following formula: CT = (F × N × W × V)/M), where F is Faraday’s constant (96,485 C mol−1), N is number of moles of electrons (8 mol mol−1), W is the daily COD load removed (g L−1), M is the molecular weight of acetate (59 g mol−1), and V is the medium volume (100 mL) [43]. CP is the Coulombs equivalent to the actual current produced during one batch cycle.
Physical characterization of NiO–CuO/G and anodic biofilms
X-ray diffraction (XRD) patterns
In order to determine the physical characteristics of NiO–CuO/G (such as lattice composition and distinctive crystallite size), XRD was performed using an XRD–RIGAKU-D/MAX-PC 2500 X-ray diffractometer fitted with Ni-filtered Cu Kα as the radiation source (λ = 0.154056 nm) at a tube current of 40 mA with a 40-kV voltage. The 2θ angular regions were detected at a scan rate of 10° min−1 from 10° to 80°. XRD data analyses were conducted using the Materials Studio (Accelrys, USA) software suite Reflex module.
Scanning electron microscopy(SEM) analysis of electrocatalysts and biofilms
Anodic biofilm growth characterization on bioanode electrode surfaces was visualized at the end of batch studies using SEM (JEOL JAX-840A, Japan). The anode was fixed in 2.5% (w/v) glutaraldehyde for 4 h. Following fixation, samples were washed three times in DI water and dehydrated in ascending ethanol gradient steps (30% to 100% with 10 min for each step) to avoid artifact drying. Finally, samples were sputtered with gold and imaged using SEM at 20 kV. Energy dispersive X-rays (EDX) were mapped using SEM instrumentation.
Transmission electron microscopy(TEM) of electrocatalysts and biofilms
The JEOL-JEM 2010 TEM, Japan was used to determine NiO–CuO/G microstructures and particles sizes and to understand the internal morphological characteristics of the isolated bacterial strains. TEM analytical procedures for isolated anodic bacterial strains were conducted under sterile conditions at room temperature (23 °C) by inoculating 100 μL bacterial cultures into a 5-mL sterilized nutrient broth and incubating them at 37 °C for 18–20 h before TEM analysis. Then, samples were fixed in 2.5% glutaraldehyde (w/v) at 4 °C for 10 min. Before TEM imaging, harvested bacterial cells were deposited on the TEM grid, stained with 2% uranyl acetate for 3–5 s on a carbon-coated mesh Cu grid, and air-dried. The Gatan program was used for data processing and particle size measurement [44].
Biochemical identification of isolated anodic bacterial communities
The isolated anodic bacterial communities were identified using Vitek 2 manufacturer’s instructions (Biomeriux VITEK-2 Compact Reference Manual-Ref-414532) [45]. A sufficient quantity of anodic biofilm was transferred using a sterile swab into a polystyrene test tube containing 3 mL sterile saline, and mixed in a suspension well. Turbidity was adjusted to the equivalent of 0.5–0.63 McFarl and turbidity units using a turbidity meter (VITEK®2 DensiCHEK™, France). The biofilm suspension was incubated in a vacuum chamber station with data collected at different time intervals to measure suspension turbidity and/or by-products from donor substrate metabolism. Finally, raw data were processed using a special algorithm to eliminate false readings.
Results
Physical characterization of NiO–CuO/G
The crystalline features and structural properties of the NiO–CuO/G composite were examined using XRD analysis (Fig. 1). A sharp and powerful diffraction peak was observed at a 2θ value of 25.914° (002 plane). Moderately wide distinguished diffraction peaks of four primary planes occurred at 2θ values of ~ 43.04°, 54.56°, 64.96°, and 78.88°. In addition, five broad peaks were observed at 2θ values of 35.60°, 38.70°, 48.80°, 58.40°, and 74.10°.
TEM analysis was performed to characterize NiO–CuO/G composite microstructures and deep surface morphology (Fig. 2). Large quantities of NiO–CuO metal particles had aggregated along with G to form an agglomeration of the electrocatalyst on the G surface (dark spots). High-resolution TEM images of the NiO–CuO/G composite showed hexagonal graphitic edges with parallel alignment to the longitudinal axis of graphitic layers, with typical crumpled structures consisting of several G layers [46].
SEM was used to study surface morphology and electrocatalyst composition (Figure S3). The distribution of synthesized composites was observed as granular patterns on the G surface. In addition, a large number of small particulates (white spots) with random aggregation (packed uniformly) was observed on wrinkled and crumpled G structures (gray area). EDX data, in addition to elemental mapping images (Fig. 3), indicated that carbon, oxygen, nickel, and copper were components of the synthesized electrocatalyst. The weights and atomic percentages of different elements are presented in Supplementary Table S1.
Electrochemical measurements using a rotating disk electrode
Figure 4 represents the polarization curves of Pt/C and NiO–CuO/G electrodes in O2-saturated PBS at a scan rate of 10 mV s−1 and a rotation speed of 1200 rpm. The onset potential of Pt/C had a more positive value (400 mV) than that of NiO–CuO/G (163 mV). The current densities at - 0.40 V (vs. SHE) were 4.16 and 4.78 mA cm−2 for NiO–CuO/G and Pt/C, respectively.
To explore the diffusion zone of current densities of Pt/C and NiO–CuO/G, LSV was performed at different rotational speeds, ranging from 200 to 2400 rpm in O2-saturated PBS at a scan rate of 10 mV s1 (Fig. 5). From Pt/C LSV curves, the reduction current density increased from − 3.22 to − 4.97 mA cm−2 with an increase in rotation speed from 200 to 2400 rpm and decreased the potential scan to more negative values. When compared with the benchmark Pt/C electrocatalyst, the NiO–CuO/G electrocatalyst exhibited similar behaviors; the reduction current density increased from − 2.22 to − 4.87 mA cm−2 at a potential range of − 0.10 to − 0.40 mV.
RDE polarization curve data were used to plot K–L relationships, where the inverse current density (j−1) was directly related to the inverse square root of the rotation rate (ω−1/2) at different potential values (i.e., − 100 to – 400 mV vs. SHE) (Fig. 5c, d). The K–L plots for both electrocatalysts were distinctly parallel and linear; this signified an enhanced electrocatalytic behavior toward ORR (kinetically more facile). The number of electrons (n) transferred with ORR was determined from the K–L plot slopes as follows: 3.94 at – 0.10 mV and 4 at – 0.40 mV for Pt/C and ~ 4 at – 0.10 mV and 3.56 at – 0.40 mV for NiO–CuO/G.
Performance of NiO–CuO/G in MFC
Electricity generation
Biochemical and electrochemical reaction rates and the long-term stability of the NiO–CuO/G were evaluated in MFCs under open-circuit voltage conditions (OCV) using acetate as the sole electron donor and compared to a Pt/C-based MFC (Figure S4). Improvements in anodic metabolic activity led to substrate oxidation and an increase in OCV during subsequent cycles. After operating for 62 days, MFCs exhibited a stable OCV of 835 mV for the Pt/C-based MFC and 654 mV for the NiO–CuO/G-based MFC. The closed-circuit cell potential for both MFCs was measured across an external resistance of 1000 Ω. The power density (PD) and potential generation (V) curves during three cycles as a function of the current density (j) are shown in Fig. 6. The maximum closed-circuit voltage output of the NiO–CuO/G-based MFC was slightly lower than that of the Pt/C-based MFC (541 and 720 mV, respectively).
The Pt/C cathode exhibited a maximum PD generation value of 50.4 mW m−2 at a cell current density of 152 mA m−2, which was 2-fold higher than that of the NiO–CuO/G cathode; 21.3 mW m−2 at a cell current density of 113.04 mA m−2 (Fig. 7). In addition, the NiO–CuO/G had significantly less activation potential loss in the high current region of the range (0–124 mA m−2) than that of Pt/C (0–160 mA m−2). These results reveal that the major basis for a better catalytic activity of the prepared catalyst is mainly due to improvements in O2 mass transfer [47]. The internal resistance of NiO–CuO/G (1120 Ω) was slightly higher than Pt/C (947 Ω).
Organic matter removal
For the NiO–CuO/G-based MFC, the COD removal percentage was (92% ± 1.1%), which was slightly lower than that for the Pt/C MFC (93% ± 0.43%). Moreover, the Pt/C displayed significantly higher CE (35% ± 0.69%) than that of NiO–CuO/G (25% ± 0.71%).
Visualization of electroactive anodic biofilms
The surface morphologies of fixed, intact anodic biofilms on carbon felt electrodes and bare carbon felt anodes were investigated using SEM. As illustrated in Supplementary Figure S5, the surface morphology of bare carbon felt was very smooth with multiple carbon fibers crossed over one another, forming a mesh-like structure of approximately 20 μm in diameter. However, the formed anodic biofilm covered the surface and internal pores of the carbon felt anode. Furthermore, bacteria appeared as rod-shaped cells, approximately 1.3 μm long.
TEM provided information on the internal structures of anodic biofilms, microbial physiology, and the relationship between microbes and minerals. TEM images (Fig. 8) indicate that four isolates (named 1C to 4C) had ultrastructurer rod-shaped surface. Major cellular ultrastructural properties in lipid membranes and the cytoplasm were observed. The cytoplasmic lipid inclusions of isolates were found to be accumulated from the mild amount (1C and 4C) to severe (2C and 3C). Isolates of this bacterial layer had a thickness of approximately 1 μm on their lateral dimension.
Biochemical identification of isolated anodic communities
MFC anodic communities were biochemically identified using the Vitek2 compact system method. The analysis revealed the existence of four distinct dominant bacterial classes, with three Gram-negative classes (Table 1), which are commonly found in MFC anodes, e.g., Gammaproteobacteria [48] and Firmicutes [49]. Interestingly, the high relative abundance of Gammaproteobacteria in bioelectrochemical systems is commonly associated with the production of high current and power output [50, 51]. Several members of the Firmicutes phylum were found to respire electrons directly onto anode surfaces, such as Bacillus cereus and Bacillus Thuringiensis/mycoides.
Discussion
In this study, the NiO–CuO/G electrocatalyst was developed as a promising cathode catalyst for MFC applications. Successful catalyst preparation was confirmed using XRD, TEM, SEM, and EDX analyses. First, XRD data revealed that the crystalline nature of the graphite framework supported the electrocatalyst [24]. Furthermore, the C (002) peak became softer as the metal particles on the G fill-up the diffraction toward the composites, leading to a G peak reduction. The 2θ values indicated the presence of crystal planes (111), (200), (220), and (311) of NiO and CuO, which were assigned to (− 111), (200), (− 202), (202), and (220) planes. Thus, mixed metal oxides could exist as NiO and CuO, suggesting the effective synthesis of a NiO/CuO composite [52, 53]. The representative peaks (Fig. 1) confirmed the with successful deposition of NiO and CuO on G [54]. This deposition may have been due to G’s elevated surface area and conductivity with available active sites, which may have enhanced the bioelectrochemical efficiency of NiO–ORR [28]. Second, TEM observations agreed with those by Li et al. [55], who prepared a G–Co/Ni composite on carbon cloth electrodes(G–Co/Ni–CC). These researchers reported large amounts of small-sized Co/Ni composites randomly deposited on the surface of crumpled G sheets. Third, from SEM and EDX analyses, NiO and CuO were effectively precipitated on G using the in situ preparation method, with percentages close to the nominal ratio of C, O, Ni, and Cu. These findings indicated that NiO and CuO was successfully deposited on the G surface.
The electrochemical characterization of as-synthesized electrocatalyst when compared with the Pt toward ORR in neutral media was evaluated by LSV. These data suggested that NiO–CuO/G considerably enhanced redox reaction performance and exhibited an electrochemical activity toward ORR comparable with Pt. The current density increased with an increase in rotation speed and a decrease in potential scan to more negative values. This was explained by the transmission of steady streams of the bulk solution to the electrode surface during high rotations, whereas the bulk solution that is far from the electrode surface remains well stirred by the convection and the shortened diffusion distance at subjected speeds [29, 56]. Moreover, kinetic analyses (based on the K-L relationship) revealed that the four-electron pathway directly to water mainly dominates the ORR in Pt/C similar to ORR catalyzed by NiO–CuO/GG according to the following equation:
These results demonstrated an improved electron transfer for the NiO–CuO/G electrode. The distribution of electron transfer numbers confirmed that NiO–CuO/G improved the ORR and improved the performance of the cathode in MFCs in neutral media. These data agreed with a previous study in which silver-tungsten carbide (Ag–WC)/C nano-hybrids showed a comparable ORR efficiency to Pt/C in MFCs [35]. This high ORR activity might have been due to synergistic effects between carbon, WC, and Ag nanoparticles. The NiO–CuO/G contributed to an efficient catalytic ORR activity. Therefore, catalytic activity toward ORR was identified from the combined impact of NiO and CuO loaded onto G. Furthermore, the elevated ORR performance of NiO–CuO was due to the high catalytic surface area of NiO–CuO particles, there by facilitating high deposition rates of the catalyst onto G surfaces and the high porosity of the composites. These results provided evidence on the use of cheaper Pt-free mixed metal oxides as electrocatalysts in MFCs, without significantly impeding performance.
The evaluation of electrocatalyst performance in MFCs showed that maximum OCV values were correlated with an increase in reaction rates, thereby allowing the adsorption and diffusion of higher amounts of O2 onto the electrocatalyst surface [57]. The performance of the NiO–CuO/G cathode in MFCs was comparable to Pt/C during the biofilm acclimation period (62 days). NiO–CuO/G-based MFCs had a maximum PD of 21.3 mW m−2 and CE of 25% ± 0.71%, which is somewhat close to Pt/C-based MFCs (e.g., PD = 50.4 mW m−2 and CE = 35 ± 0.69). These data suggested that CE was determined mainly by cathode variations, but they might have been attributable to the ideal properties of the NiO–CuO/G electrocatalyst. The formation of the biofilm is dependent on the intensive development of the bacterial cells at a high COD removal value. It can be presumed that the higher COD removal is directly correlated to the enhanced substrate utilization and the comparatively higher performance with improved power output [24, 28]. The high surface area of G’s uniform distribution and dispersion of the prepared catalyst led to a higher voltage. This led to a higher current output of the system, with higher power output. Thus, the overall reaction of the NiO–CuO/G, with a high COD removal efficiency, revealed that NiO–CuO/G cathode may be efficiently used as an electrocatalyst for MFC applications.
Surface analyses of anodic biofilms using SEM and TEM indicate that bacterial cells were rod-shaped structures indicative of electroactive microorganisms and thus confirming that the generated electricity was due to electroactive biofilms on the surface of anodic electrodes. In addition, the biochemical characterization of anodic bacterial communities revealed a possible mechanism for the isolation of electrochemically active bacteria (EAB). These analyses indicate that the anode itself is supposed to be a pathway through an anaerobic enrichment of anodic biofilm. The approach considers the fundamental properties of living organisms to absorb respiratory energy via electrons. Bacteria use this energy as an alternative to direct respiration in the absence of an electron acceptor.
The literature survey yielded that non-precious Ni-based electrocatalysts generally exhibited good catalytic activity and stability comparable to Pt/C cathode in MFCs (Table 2).
Ni-based electrocatalysts could be used as a cathode catalyst in the MFC as evidenced by the high PD in MFCs. The as-synthesized electrocatalyst was found to be more efficient than those reported by Liu and Vipulanandan [30]. These authors used Ni nanoparticles for a two-chamber MFC application that generated a PD of 0.07 mW m−2. In another study, Champavert et al. [32] fabricated a carbon felt cathode modified with poly Ni (II) tetra sulfophthalocyanine for a dual-chamber MFC. This generated a PD of 21.6 mW m−2, which was comparable to our results (21.3 mW m−2). This difference in PD may have been due to several factors, including operational conditions, MFC design, anode type and surface area, differences in bacterial communities, and differences in supporting material for the electrocatalyst and its projected surface area.
Our research provides new perspectives for effective non-precious mixed metal oxide (NiO–CuO/G) cathode electrocatalysts as replacements for noble and costly Pt/C for practical MFC applications. The enhanced electrocatalytic activity of NiO–CuO/G might have been primarily due to its high surface area and synergistic effects between NiO/CuO and G. These synergistic effects provided NiO/CuO surfaces with high quantities of active sites, thereby confirming electrocatalyst stability, electrical conductivity, and enhanced MFC performance.
Conclusions
To the best of our knowledge, it was the first time to use this combination of mixed metal oxides (NiO–CuO/G) for application in MFC as a cathode electrocatalyst. The successful preparation of NiO–CuO/G electrocatalyst was confirmed by XRD, TEM, SEM, and EDX analysis. The electrochemical characterization showed high selectivity and electrocatalytic activity of the electrocatalyst towards the ORR that follows the four-electron pathway. The efficiency of NiO–CuO/G in MFCs yielded a maximum PD of 21.3 mW m−2 with a CE of 25 ± 0.71%. These results were slightly lower than Pt/C based MFCs (PD = 50.4 mW m−2 and CE = 35 ± 0.69%). The enhanced electrocatalytic activity of NiO–CuO/G may be mainly due to its high surface area and synergistic effect between NiO/CuO and graphene. These synergistic effects provide NiO/CuO surface with large amounts of active sites, resulting in high stability of the electrocatalyst and enhanced electrical conductivity. This enhanced the performance of MFCs. Both SEM and TEM analysis of anodic biofilm showed the rod-shaped structure of electroactive microorganisms, confirming that the generated electricity was due to the formed electroactive biofilm on the surface of the anodic electrode. In addition, the biochemical characterization of the anodic communities reveals a possible pathway for the isolation of EAB via anaerobic enrichment and was primarily anticipated as a tool for selecting EAB consortia. This research provides new perspectives into discovering effective non-precious mixed metal oxides (NiO–CuO/G) cathode electrocatalyst as a replacement for noble and very costly Pt/C for practical applications of MFCs. The future work will be relying on exploring different combinations of transition metal oxides as ORR electrocatalysts, such as nickel along with cobalt or manganese oxides. The performance of these electrocatalysts will be evaluated using different physical and electrochemical techniques. Moreover, their applications in MFC with different constructions and operating conditions will be performed.
Availability of data and materials
All data generated or analyzed during this study are included in this published article and its supplementary information files.
Abbreviations
- CE:
-
Coulombic efficiency
- COD:
-
Chemical oxygen demand
- DI:
-
De-ionized
- EDX:
-
Energy dispersive X-ray spectroscopy
- GCE:
-
Glassy carbon electrode
- LSV:
-
Linear sweep voltammetry
- MEC:
-
Microbial electrolysis cell
- MFC:
-
Microbial fuel cell
- OCV:
-
Open-circuit voltage
- ORR:
-
Oxygen reduction reactions
- PBS:
-
Phosphate buffer solution
- PD:
-
Power density
- RDE:
-
Rotating disk electrode
- SEM:
-
Scanning electron microscopy
- TEM:
-
Transmission electron microscopy
- XRD:
-
X-ray diffraction
References
Ji B, Zhao Y, Vymazal J, Mander Ü, Lust R, Tang C (2021) Mapping the field of constructed wetland-microbial fuel cell: a review and bibliometric analysis. Chemosphere 262:128366. https://doi.org/10.1016/j.chemosphere.2020.128366
Munoz-Cupa C, Hu Y, Xu C, Bassi A (2021) An overview of microbial fuel cell usage in wastewater treatment, resource recovery and energy production. Sci Total Environ 754:142429. https://doi.org/10.1016/j.scitotenv.2020.142429
Lovley D (2006) Bug juice: harvesting electricity with microorganisms. Nat Rev Microbiol 4:497–508
Lefebvre O, Tan Z, Kharkwal S, Ng HY (2012) Effect of increasing anodic NaCl concentration on microbial fuel cell performance. Bioresour Technol 112:336–340. https://doi.org/10.1016/j.biortech.2012.02.048
Valipour A, Ayyaru S, Ahn Y (2016) Application of graphene-based nanomaterials as novel cathode catalysts for improving power generation in single chamber microbial fuel cells. J Power Sources 327:548–556. https://doi.org/10.1016/j.jpowsour.2016.07.099
Parkash A (2016) Microbial Fuel Cells : A Source of Bioenergy. J Microb Biochem Technol 8:247–255. https://doi.org/10.4172/1948-5948.1000293
Slate AJ, Whitehead KA, Brownson DAC, Banks CE (2019) Microbial fuel cells : An overview of current technology. Renew Sust Energy Rev 101:60–81. https://doi.org/10.1016/j.rser.2018.09.044
Kumar SS, Kumar V, Malyan SK, Sharma J, Mathimani T (2019) Microbial fuel cells ( MFCs ) for bioelectrochemical treatment of different wastewater streams. Fuel 254:115526. https://doi.org/10.1016/j.fuel.2019.05.109
Youngho A (2013) Implementation of microbial fuel cells ( MFCs ) -based wastewater treatment. Adv Mat Res 684:230–233. https://doi.org/10.4028/www.scientific.net/AMR.684.230
Ieropoulos I, Greenman J, Melhuish C, Hart J (2005) Comparative study of three types of microbial fuel cell. Enzyme Microb Technol 37:238–245. https://doi.org/10.1016/j.enzmictec.2005.03.006
Cao Y, Mu H, Liu W, Zhang R, Guo J, Xian M et al (2019) Electricigens in the anode of microbial fuel cells: pure cultures versus mixed communities. Microb Cell Fact 18:1–14. https://doi.org/10.1186/s12934-019-1087-z
Watson VJ, Logan BE (2010) Power production in MFCs inoculated with Shewanella oneidensis MR-1 or mixed cultures. Biotechnol Bioeng 105:489–498.
Gil GC, Chang IS, Kim BH, Kim M, Jang JY, Park HS et al (2003) Operational parameters affecting the performance of a mediatorless microbial fuel cell. Biosens Bioelectron 18:327–334
Mohamed HO, Sayed ET, Obaid M, Choi Y-J, Park S-G, Al-Qaradawi S et al (2018) Transition metal nanoparticles doped carbon paper as a cost-effective anode in a microbial fuel cell powered by pure and mixed biocatalyst cultures. Int J Hydrog. Energy 43:21560–21571
Wang Z, Cao C, Zheng Y, Chen S, Zhao F (2014) Abiotic oxygen reduction reaction catalysts used in microbial fuel cells. ChemElectroChem:1813–1821. https://doi.org/10.1002/celc.201402093
Yan Z, Wang M, Huang B, Zhao J, Liu R (2012) Carboxyl multi-wall carbon nanotubes supported Pt-Ni alloy nanoparticles as cathode catalyst for microbial fuel cells. Int J Electrochem Sci 7:10825–10834
Chaturvedi A, Kundu PP (2021) Recent advances and perspectives in platinum-free cathode catalysts in microbial fuel cells. J Environ Chem Eng 9:105662. https://doi.org/10.1016/j.jece.2021.105662
Qiu S, Guo Z, Naz F, Yang Z, Yu C (2021) An overview in the development of cathode materials for the improvement in power generation of microbial fuel cells. Bioelectrochemistry 141:107834. https://doi.org/10.1016/j.bioelechem.2021.107834
Peera SG, Maiyalagan T, Liu C, Ashmath S, Lee TG, Jiang Z et al (2021) A review on carbon and non-precious metal based cathode catalysts in microbial fuel cells. Int J Hydrogen Energy 46:3056–3089. https://doi.org/10.1016/j.ijhydene.2020.07.252
Gautam RK, Verma A (2019) Electrocatalyst materials for oxygen reduction reaction in microbial fuel cell. Microbial electrochemical technology: sustainable platform for fuels, chemicals and remediation biomass. Biofuels. Biochem:451–483
Zhang P, Li K, Liu X (2014) Carnation-like MnO 2 modi fi ed activated carbon air cathode improve power generation in microbial fuel cells. J Power Sources 264:248–253. https://doi.org/10.1016/j.jpowsour.2014.04.098
Lima FHB, De CJFR, Ticianelli EA (2006) Silver-cobalt bimetallic particles for oxygen reduction in alkaline media. J Power Sources 161:806–812. https://doi.org/10.1016/j.jpowsour.2006.06.029
Burkitt R, T. Whiffen EHY. (2016) Iron phthalocyanine and MnOx composite catalysts for microbial fuel cell applications. Appl Catal Environ 181:279–288
Papiya F, Nandy A, Mondal S, Paban P (2017) Co/Al 2O3 -rGO nanocomposite as cathode electrocatalyst for superior oxygen reduction in microbial fuel cell applications : The effect of nanocomposite composition. Electrochim Acta 254:1–13. https://doi.org/10.1016/j.electacta.2017.09.108
Gong X, You S, Wang X, Zhang J, Gan Y, Ren N (2014) A novel stainless steel mesh / cobalt oxide hybrid electrode for efficient catalysis of oxygen reduction in a microbial fuel cell. Biosens Bioelectron 55:237–241. https://doi.org/10.1016/j.bios.2013.12.015
Karthick S, Haribabu K (2020) Bioelectricity generation in a microbial fuel cell using polypyrrole- molybdenum oxide composite as an e ff ective cathode catalyst. Fuel 275:117994. https://doi.org/10.1016/j.fuel.2020.117994
Das I, Noori T, Bhowmick GD, Ghangrekar MM (2018) Application of low-cost transition metal based Co0.5Zn0.5Fe2O4 as oxygen reduction reaction catalyst for improving performance of microbial fuel cell. MRS Adv:3171–3179. https://doi.org/10.1557/adv.2018.450
Ghasemi M, Ramli W, Daud W, Rahimnejad M, Rezayi M (2013) Copper-phthalocyanine and nickel nanoparticles as novel cathode catalysts in microbial fuel cells. Int J Hydrogen Energy:1–8. https://doi.org/10.1016/j.ijhydene.2013.01.177
Huang J, Zhu N, Yang T, Zhang T, Wu P (2015) Nickel oxide and carbon nanotube composite ( NiO / CNT ) as a novel cathode non-precious metal catalyst in microbial fuel cells. Biosens Bioelectron 72:332–339. https://doi.org/10.1016/j.bios.2015.05.035
Liu J, Vipulanandan C (2014) Nickel nanoparticles catalyst enhanced performance of microbial fuel cell. CIGMAT-2014 Conf Exhib:1–2
Kartick B, Srivastava SK, Chandra A (2016) Graphene/nickel nanofiber hybrids for catalytic and microbial fuel cell applications. J Nanosci Nanotechnol 16:303–311. https://doi.org/10.1166/jnn.2016.10667
Champavert J, Ben RS, Innocent C, Pontié M (2015) Microbial Fuel Cell based on Ni- Tetra Sulfonated phthalocyanine cathode and graphene modified bioanode. J Electroanal Chem. https://doi.org/10.1016/j.jelechem.2015.09.012
Chaturvedi A, Chaturvedi A, Nagaiah TC, Kundu PP (2021) Synthesis of Co/Ni @ Al2O3-GO as novel oxygen reduction electrocatalyst for sustainable bioelectricity production in single-chambered microbial fuel cells. J Environ Chem Eng 9:106054. https://doi.org/10.1016/j.jece.2021.106054
Shaari N, Kamarudin SK (2017) Graphene in electrocatalyst and proton conductiong membrane in fuel cell applications: An overview. Renew Sustain Energy Rev 69:862
Gong X, You S, Wang X, Gan Y, Zhang R, Ren N (2013) Silver- tungsten carbide nanohybrid for efficient electrocatalysis of oxygen reduction reaction in microbial fuel cell. J Power Sources 225:330–337. https://doi.org/10.1016/j.jpowsour.2012.10.047
Rojas-carbonell S, Santoro C, Serov A, Atanassov P (2017) Transition metal-nitrogen-carbon catalysts for oxygen reduction reaction in neutral electrolyte. Electrochem Commun 75:38–42. https://doi.org/10.1016/j.elecom.2016.12.011
Khater DZ, El-Khatib KM, Hassan HM (2017) Microbial diversity structure in acetate single chamber microbial fuel cell for electricity generation. J Genet Eng Biotechnol 15. https://doi.org/10.1016/j.jgeb.2017.01.008
Zeng L, Zhang L, Li W, Zhao S, Lei J, Zhou Z (2010) Molybdenum carbide as anodic catalyst for microbial fuel cell based on Klebsiella pneumoniae. Biosens Bioelectron 25:2696–2700. https://doi.org/10.1016/j.bios.2010.05.002
Lee K, Zhang L, Lui H, Hui R, Shi Z, Zhang JJ (2009) Oxygen reduction reaction (ORR) catalyzed by carbon-supported cobalt polypyrrole (Co-PPy/C) electrocatalysts. Electrochim Acta 54:4704–4711
Watson VJ, Logan BE (2011) Analysis of polarization methods for elimination of power overshoot in microbial fuel cells. Electrochem Commun 13:54–56
Picoreanu C, Head IM, Katuri KP, van Loosdrecht MCM, Scoot K (2007) Computational model for biofim-based microbial fuel cells. Water Res 41:2921–2940
APHA, Standard Methods for the Examination of Water and Wastewater, American Public Health Association, Washington, DC, 21st edn, 2005.
Feng Y, Wang X, Logan BE, Lee H (2008) Brewery wastewater treatment using air-cathode microbial fuel cells. Appl Microbiol Biotechnol 78:873–880
Maruthupandy M, Anand M, Maduraiveeran G, Sait A, Beevi H, Priya RJ (2015) Electrical conductivity measurements of bacterial electrical conductivity measurements of bacterial nanowires from Pseudomonas aeruginosa. Adv Nat Sci Nanosci Nanotechnol 6:045007–045013
BioMérieux. (2006) Vitek2 product information, document 510769-4EN1. bioMérieux,. Inc, Durham
Oh H, Oh J, Hee W, Kim H, Kim H (2011) The influence of the structural properties of carbon on the oxygen reduction reaction of nitrogen modified carbon based catalysts. Int J Hydrogen Energy 36:8181–8186. https://doi.org/10.1016/j.ijhydene.2011.04.139
Haoyu E, Cheng S, Scott K, Logan B (2007) Microbial fuel cell performance with non-Pt cathode catalysts. J Power Sources 171:275–281. https://doi.org/10.1016/j.jpowsour.2007.07.010
Ishii S, Suzuki S, Norden-Krichmar TM, Phan T, Wanger G, K.H. Nealson YS, Y.A. Gorby OB. (2014) Microbial population and functional dynamics associated with surface potential and carbon metabolism. ISME J 8:963–978
Wrighton KC, Agbo P, Warnecke F, Weber KA, Brodie EL, DeSantis TZ, P, Hugenholtz, G.L. Andersen JDC. (2008) A novel ecological role of the Firmicutes identified in thermophilic microbial fuel cells. ISME J 2:1146–1156
Daniel Aguirre de carcer, Phuc Thi Ha JK& ln SC (2011) Microbial community differences between propionate- fed microbial fuel cell systems under open and closed circuit conditions. AApplied Microbiol. Biotechnol 89:605–612
Xin S, Shen J, Liu G, Chen Q, Xiao Z (2020) Electricity generation and microbial community of single-chamber microbial fuel cells in response to Cu 2 O nanoparticles / reduced graphene oxide as cathode catalyst. Chem Eng J 380:122446. https://doi.org/10.1016/j.cej.2019.122446
He Y, Chen W, Li X, Zhang Z, Fu J, Zhao C, Xie E (2013) Free standing three-dimensional graphene/MnO2 composite networks as ultralight and flexible supercapacitor electrodes. ACS Nano 7:174
Jiang L-CZW-D (2010) A highly sensitive nonenzymatic glucose sensor based on CuO nanoparticles-modified carbon nanotube electrode. Biosens Bioelectron 25:1402–1407
Savy M, Coowar F, Riga J, Verbits JJ, Bronoe¨ l G BS. (1990) Investigation of O2 reduction in alkaline media on macrocyclic chelates impregnated on different supports: influence of the heat treatment on stability and activity. J Appl Electrochem 20:260–268
Li L, Liu S, Wang H, Yang P (2018) Application of graphene-cobalt/nickel composite-carbon cloth modified electrode in microbial fuel cell. Environ Eng Sci 35:1–11. https://doi.org/10.1089/ees.2017.0543
Scott K (2015) Electrochemical principles and characterization of bioelectrochemical system. Microb Electrochem Fuel Cell:29–66
Pareek A, Sravan JS, Mohan SV (2019) Exploring chemically reduced graphene oxide electrode for power generation in microbial fuel cell. Mater Sci Energy Technol 2:600–606. https://doi.org/10.1016/j.mset.2019.06.006
Rae JK, Kim JY, Han SB, Kyung-Won Park KW, Saratale GD, Oh SE (2011) Application of Co-naphthalocyanine (CoNPc) as alternative cathode catalyst and support structure for microbial fuel cells. Bioresource Technology 102(1):342–347. https://doi.org/10.1016/j.biortech.2010.07.005
Acknowledgements
This study was financially supported by the National Research Centre, Egypt. We also are grateful to the Pilot Plant Department staff of the Engineering and Renewable Energy Research Institute at the National Research Centre for their help throughout this study.
Funding
This research was financially supported by the National Research Centre, Egypt.
Author information
Authors and Affiliations
Contributions
Dena Z Khater conceived, performed, and designed the research; analyzed the data; and wrote the first draft of the manuscript. R. S. Amin conceptualization and methodology. Monera O. Zhran contributed analytical tools for isolation and identification of microbial community. Zeinab K. Abd El-Aziz contributed analytical tools for isolation and identification of microbial community. Mohamed Mahmoud interpreted and analyzed the data, Helmy M. Hassan contributed analytical tools for isolation and identification of microbial community. K.M. El-Khatib interpreted and analyzed the data and designed the research. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
This article does not contain any studies with human participants or animals performed by any of the authors.
Consent for publication
Not applicable.
Competing interests
The authors declare that they have has no competing interests.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Additional file 1:
Figure S1. Illustrating the synthesis of NiO-CuO/G electrocatalysts by precipitation of metal salts precursors and its techniques for the ORR in neutral PBS and its application in MFCs. Figure S2. MFC configuration. Figure S3. SEM images of 30 wt % NiO-CuO/G composite: (a) high-magnification image and (b) low-magnification image. Figure S4. Open circuit potential for a) Pt/C- and b) NiO-CuO/G-based MFCs. Figure S5. SEM images of (a) bare carbon felt anode and (b) carbon felt anode after 90 days operation. Table S1. Weight and Atomic percentages of elements forming NiO-CuO/G electrocatalyst.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Khater, D.Z., Amin, R.S., Zhran, M.O. et al. The enhancement of microbial fuel cell performance by anodic bacterial community adaptation and cathodic mixed nickel–copper oxides on a graphene electrocatalyst. J Genet Eng Biotechnol 20, 12 (2022). https://doi.org/10.1186/s43141-021-00292-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s43141-021-00292-2