Abstract
Protected by extracellular polymers, microbes within biofilms are significantly more resistant to disinfectants. Current research has been instrumental in identifying nitric oxide donors and hydrogels as potential disinfectant additives. Nitric oxide (NO) donors are considered a very promising molecule as biofilm dispersal agents and hydrogels have recently attracted a lot of interest due to their biocompatible properties and ability to form stable thin films. When the NO donor MAHMA NONOate was dissolved in phosphate saline buffer, it was able to reduce the biomass of well-established biofilms up to 15% for at least 24 h of contact time. Encapsulation of MAHMA NONOate and molsidomine within a hydrogel composed of cellulose nanocrystals (CNC) has shown a synergistic effect in dispersing well-established biofilms: after 2 h of exposure, moderate but significant dispersion was measured. After 6 h of exposure, the number of cells transitioning from the biofilm to the planktonic state was up to 0.6 log higher when compared with non-treated biofilms. To further explore the transport processes of NO donors within hydrogels, we measured the nitric oxide flux from gels, at 25°C for a composite of 0.1 µM MAHMA NONOate–CNC. Nitric oxide diffuses up to 500 µm from the hydrogel surface, with flux decreasing according to Fick’s law. 60% of NO was released from the hydrogel composite during the first 23 min. These data suggest that the combined treatments with nitric oxide donor and hydrogels may allow for new sustainable cleaning strategies.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Biofilms formed on washing systems in produce production facilities can be recalcitrant reservoirs of human pathogens, which are difficult to control and can potentially cause costly outbreaks (Srey et al. 2013). Pathogens in biofilms are resistant to common disinfectants and contribute to an increased risk in contamination of produce by potentially contaminated water (Zhang and Mah 2008; Corcoran et al. 2014). Several disinfectants, antibiotics and messenger molecules have been studied for their ability to dislodge existing biofilms (Barraud et al. 2006, 2009a, 2012). Of these, nitric oxide (NO) appears to be very promising, and currently nitric oxide donors are used clinically. Nitric oxide is effective as a biofilm dispersant, functioning as a messenger rather than a generic poison (Barraud et al. 2006, 2009a, 2012; Marvasi et al. 2014). Nitric oxide can be delivered to biofilms by using donor molecules (Wang et al. 2005), and the application of nitric oxide donors has the same effect as the direct addition of nitric oxide gas (Barraud et al. 2009b). In bacteria, nitric oxide acts as an active signaling molecule at very low concentrations and is able to disperse preformed biofilms at nano- or picomolar concentration, indicating that truly minute quantities of the chemical are sufficient for dislodging much of the biofilm (Barraud et al. 2006, 2009a, 2012; Marvasi et al. 2014). Nitric oxide could have a universal effect on dispersal of bacteria biofilm including both Gram-positive and Gram-negative bacteria (Xiong and Liu 2010). The mechanisms of biofilm dispersion are not clear, but it appears to function in the transition of sessile biofilm organisms to free-swimming bacteria. For example, microarray studies have revealed that genes involved in adherence are downregulated in Pseudomonas aeruginosa upon exposure to nitric oxide donors (Firoved et al. 2004).
Over 105 nitric oxide donors have been characterized, and 6 have been currently tested as biofilm dispersal. Among these, the main studied are the sodium nitroprusside, (Barraud et al. 2006; Marvasi et al. 2014; Charville et al. 2008; Barraud et al. 2009a), molsidomine, diethylamine NONOate diethylammonium, NONOate diethylammonium, MAHMA nonoate (Marvasi et al. 2014), NORS (sodium nitrite citric acid) (Regev-Shoshani et al. 2013) and NO-releasing silica nanoparticles (Hetrick et al. 2009). Among these, MAHMA NONOate is one of the best candidates in biofilm dispersion: it spontaneously dissociates in a pH/temperature dependent manner, in serum it has a half-life of 1 and 3 min at 37°C and 22–25°C respectively, at pH 7.4 to liberate 2 mol of NO per mole of parent compound (Wang et al. 2005; Keefer et al. 1996; Hrabie et al. 1993). Interesting, when MAHMA NONOate was used to disperse Salmonella enterica and Escherichia coli biofilms (24-h old), up to 50% of Salmonella 14028 and a cocktail of six Salmonella outbreak strains biofilms were dispersed when incubated for 6 and 24 h at 22°C (both p < 0.0001). About 40% of dispersion was measured also for the pathogenic Escherichia coli O157:H7 when exposed at room temperature for 6 and 24 h (Marvasi et al. 2014).
Nitric oxide donors can be associated with other disinfectants obtaining a synergistic effect in terms of biofilm dispersion. For example, a 20-fold increase in the efficiency was observed when nitric oxide was applied together with chlorine in removing multispecies biofilms (Barraud et al. 2009b). In addition, we recently showed that the nitric oxide donor MAHMA NONOate and molsidomine were also able to increase up to 15% Salmonella biofilm dispersion when associated with the industrial disinfectant SaniDate 12.0 (Marvasi et al. 2014).
We used this foundation to hypothesize that nitric oxide donors can also be applied to hydrogels in order to obtain a synergistic effect in terms of biofilm dispersal. Hydrogels have recently attracted a lot of interest due to high strength/stiffness, optical transparency, biocompatibility, biodegradability, and highly porous structural network (Klemm et al. 2011; Siro and Plackett 2011) and the ability to carry bactericidal molecules (Azizi et al. 2013; Drogat et al. 2011; Feese et al. 2011). Hydrogels are water-swollen, and cross-linked polymeric network produced by the simple reaction of one or more monomers (Ahmed 2013). The industrial applications of hydrogels are extremely heterogeneous, ranging from agriculture, drug delivery systems, food additives, biomedical applications such as implants, and separation of biomolecules (Thakur and Thakur 2014).
Among the hydrogels, cellulose nanocrystals (CNC) is one of the most promising polymer because it is an eco-friendly product, cheap and safe (George et al. 2011). CNC has high crystallinity, high water holding capacity and excellent mechanical and thermal properties (George et al. 2011). For our scope, CNC was procured from a process development center that focuses on production of wood-derived renewable nanomaterials. CNC was selected as the hydrogel base because this material has an ionic charged surface appropriate for binding biofilm outer extracellular polymeric substances (EPS) (Marvasi et al. 2014; George et al. 2011; Marvasi et al. 2010).
The main objective of this study was to measure the synergistic effect of the nitric oxide donor MAHMA NANOate in association with CNC during nitric oxide-mediated biofilm dispersion of S. enterica sv Typhimurium. We focused our experiments on well-structured biofilms and we measured the shortest effective exposure. The nitric oxide release profile, diffusion and flux rate were also measured during MAHMA NONOate–CNC association.
Materials and methods
Bacterial strains and culture media
Salmonella enterica serovar Typhimurium ATCC14028, was used in this study. pGFP-ON, a strongly fluorescent construct carrying GFP protein expressed from the Salmonella dppA promoter (Noel et al. 2010), was transformed into the strains of interest by electroporation.
All strains were maintained as frozen glycerol stocks, and were sub-cultured into Luria–Bertani medium with appropriate antibiotics (50 µg mL−1 kanamycin, 100 µg mL−1 ampicillin).
Chemicals and materials for microelectrode preparation
Single layer graphene oxide (SLGO; 0.8 nm thickness, 1–5 µm diameter, 99% purity) was obtained from ACS Materials. Methanol, ascorbic acid and lead acetate were purchased from Fisher Scientific (Atlanta, GA, USA). Cerium (IV) oxide (nanoparticles dispersion, <25 nm particle size, 10 wt% in H2O) and chloroplatinic acid (8 wt%) were procured from Sigma-Aldrich (St. Louis, MO, USA). Nafion (5% aliphatic alcohol) and o-phenylenediamine were acquired from Acros organics (Newark, NJ, USA). Nitric oxide gas (CP grade 99%) was purchased from AirGas (Gainesville, FL, USA).
Nitric oxide donors
MAHMA NONOate and molsidomine were purchased from Sigma-Aldrich (St. Luois, MO, USA). For each compound, 1 mmol L−1 stock solutions were prepared in phosphate-buffered saline (PBS), pH 7.3 (PBS, Fisher, Waltham, MA, USA) and aliquots were stored at −80°C. For the assays, serial dilutions were always prepared fresh in ice-cold PBS just before the experiments and used within 5 min of their preparation. The biofilm dispersion potential was tested on polystyrene 96-well plates (Fisher, Waltham, MA, USA).
Biofilm formation and dispersal on plastics
Overnight Luria–Bertani cultures of Salmonella S. typhimurium 14028 or S. typhimurium 14028 pGFP-ON (with 100 µg mL−1 ampicillin) were diluted 1:100 in CFA medium as described previously (Teplitski et al. 2006), and 100 µL of the diluted cultures were aliquoted into wells of 96-well polypropylene and polystyrene plates (Fisher, Waltham, MA, USA). Plates with bacteria were incubated for 24 h or 1 week (well established biofilm) at 37°C inside a Ziploc bag to prevent dehydration.
Measurement of biofilms dispersal
Upon completion of the incubation, the medium with planktonic bacteria was removed and serial dilutions of nitric oxide donors in PBS or CNC (in 200 µL) were added to the wells with biofilms. Dispersal experiments were conducted at 22°C for a time ranging from 1 to 24 h. The dispersion of biofilms treated with the nitric oxide donor dissolved in PBS was measured by staining the remaining biofilms with 1% crystal violet in ethanol, as described previously (O’Toole and Kolter 1998; Merritt et al. 2005).
Biofilms dispersion treated with CNC (or control, CNC + PBS) was measured by directly monitoring the increase of fluorescence of planktonic cells of S. typhimurium 14028 pGFP-ON. At the end of the period of exposure, 170 µL of CNC-nitric oxide solution were transferred into a black 96-wells plate and fluorescence was measured by using Victor-2 multimode plate reader with a 485 nm/535 nm excitation/emission filter (Perkin Elmer, Waltham, MA, USA). Increase of fluorescent intensity was used to represent an increase of detached cells.
Luminescence tests
Effects of selected nitric oxide donors on light production by a constitutively luminescent Salmonella strain were characterized as indirect assessments of toxicity of the compounds. 1 mL of S. typhimurium 14028 pTIM2442 (harboring the luxCDABE driven by a strong constitutive phage, Alagely et al. 2011) were washed with BPS and mixed with opportune reagents (BPS, molsidomine, CNC) and grown in black polystyrene plates (Corning, New York, USA). Molsidomine was diluted in PBS (9.89 g L−1) or CNC (Fisher Scientific, Waltham, MA, USA) to final concentrations of 10 µmol L−1. PBS + CNC and PBS alone were used as a control. Luminescence of S. typhimurium 14028 pTIM2442 was measured over time using Victor-2 multimode plate reader (Perkin Elmer, Waltham, MA, USA). Each experiment included 12 replicas.
CNC-nitric oxide preparation
1 mmol L−1 stock solutions of MAHMA NONOate or molsidomine were prepared in PBS, pH 7.3 (PBS, Fisher, Waltham, MA, USA). Final solutions to 1 µM were prepared by dispersing the nitric oxide stock solution in an opportune volume of CNC. The solution was further vortexed for 30 s and applied of prewashed biofilm formed into polypropylene plates.
Nitric oxide measurement
NO microelectrodes were prepared using the methods in Chaturvedi et al. (2014). Pt/Ir microelectrodes (2 µm tip diameter, 5.1 cm length, 81 µm shaft diameter; MicroProbe, Inc., Gaithersburg, MD, USA) were rinsed in methanol prior to use. Nafion, nanoceria, nanoplatinum, and reduced graphene oxide were deposited based on the methods in Chaturvedi et al. (2014) and Vanegas et al. (2014). Briefly, microelectrodes were platinized via pulsed-sonoelectrodeposition at 10 mV for 60 cycles (each cycle consisted of 1 s electroplating pulse followed by 1 s sonication pulse) in a plating solution of 0.002% lead acetate and 1.44% chloroplatinic acid. Thereafter, electrodes were dip coated for 5 min in a suspension of 10 wt% cerium oxide with 0.8 wt% ascorbic acid and 0.2 wt% SLGO. Electrodes were then dried at 100°C for 20 min. Next, electrodes were dip coated in 5% Nafion and dried at 110°C for 20 min; this step was repeated twice. Finally, an OPD membrane was formed on the tip of the probe by polarizing the electrodes at 900 mV in a solution of 5 mM OPD and 0.1 mM ascorbic acid in PBS (pH 7.4) until a stable current was recorded (less than 2% variability) (Friedemann et al. 1996; Koehler et al. 2008; Porterfield et al. 2001). The working principle for the NO microelectrode is based on oxidation of NO at the surface of the nanocomposite, generating the nitrosonium cation (NO+) and one free electron based on Eq. 1 below; free electrons are detected as oxidative current versus a reference electrode
NO microelectrode calibration and flux measurements
All measurements were performed at a working potential of +500 mV versus a reference electrode composed of a Ag/AgCl wire immersed in 3 M KCl and inserted into a half-cell microelectrode holder (World Precision Instruments, Inc., Sarasota, FL, USA). For electrode calibration, a PBS solution was polarized for 1 h at +900 mV; current output was measured at constant potential while successively injecting NO stock solution prepared based on Porterfield et al. (2001). Calibrated microsensors were used to measure NO flux in the self referencing (SR) modality as described in detail by McLamore and Porterfield (2011). The SR microsensor technique is designed to measure flux within the concentration boundary layer, and involves computer-controlled translation of a microelectrode between two positions separated by a known distance (dX). Differential concentration (dC) is recorded in real time and flux is then calculated using Fick’s first law of diffusion (J = −D × dC dX − 1). The diffusion coefficient (D) for NO used in all experiments was 2.21 × 10−5 cm2 s−1 based on and Zacharia and Deen (2005).
Statistical analysis
The statistical package JMP (SAS) was used to infer the ANOVA analysis (p < 0.05). Tukey means separation analysis was inferred in order to group the means.
Results
Synergistic effect of the association of nitric oxide donors with CNC
The effect of MAHMA NONOate as biofilm dispersal was previously assessed in our recent publication in a range of biofilm-forming microorganisms of industrial and/or clinical significance including S. enterica (Marvasi et al. 2014). Our previous efforts were focused on studying young biofilms (maximum 24 h old) and exposure time up to 6 h. In order to focus on more applicative approaches of the nitric oxide donor technology, we tested the nitric oxide donors on well-structured biofilms (1-week old biofilms) and for a shorter contact time (up to 1 h of exposure).
As a first approach, we exposed a 24-h old Salmonella biofilm for a minimum of 2 h to different concentrations of MAHMA NONOate dissolved in PBS (10 µM, 10 nM and 10 pM): no significant results were measured (Figure 1a). The experiment was repeated with the nitric oxide donor, molsidomine, observing a similar result (Figure 1b). In further experiments, MAHMA NONOate or molsidomine were dissolved into CNC hydrogel to 10 µM (CNC–NONOate or CNC–molsidomine) to test whether the association of CNC was instrumental in increasing the dispersion potential of the nitric oxide donors within the 2 h. A fluorescent Salmonella 14028 pGFP-ON biofilm preformed on polypropylene was treated with 10 µM NONOate–CNC or 10 µM molsidomine–CNC. Fluorescence of the planktonic cells was measured after 2 and 1 h of exposure to the nitric oxide donors. The fraction of cells switching to the planktonic state was significant after 2 h of exposure (Figure 1c), but not significant after 1 h of exposure (Figure 1d).
24-h old Salmonella biofilm dispersal by MAHMA NONOate dissolved in BPS and CNC. Biofilms were preformed by S. enterica typhimurium 14028 for 24 h on polystyrene prior to the treatment with MAHMA NONOate and molsidomine. Contact time at which biofilms were exposed to the nitric oxide donor is listed on each panel. a, b The decreasing of biofilm formation was measured by using the technique of crystal violet staining. c, d Fluorescent Salmonella 14028 pGFP-ON biofilm was treated with MAHMA NONOate and molsidomine dissolved in CNC. Increase in fluorescence of the planktonic cells was measured at 485 nm/535 nm. The box-plots encompass the lower and upper quartiles, thick lines within the box are the median values, and the whiskers indicate the degree of dispersion of the data. Outliers are shown as dots. Dotted line represents the grand mean. Letters above each box represent the Tukey means separation: different letters are significant different means.
To determine the viability of Salmonella during the exposure to CNC, the luminescence of Salmonella 14028 pTIM2442 upon association of CNC and molsidomine was measured. The general metabolic state of the cells was assessed by using the pTIM2442 system (Alagely et al. 2011). No variation in terms of viability was reported during a period of 8 h when CNC exposure was compared with the controls (Additional file 1: Figure S1).
To measure the responsiveness of a well-established biofilm such as a 1-week old biofilm, Salmonella 14028 biofilms were exposed to different concentrations of MAHMA NONate dissolved in PBS for 24 and 6 h. 24 h of exposure to MAHMA NONOate reduced the biomass up to 15% (Figure 2a). However, 6 h of exposure did not significantly reduce the biomass (Figure 2b). As before, we tested whether the association of CNC was instrumental in increasing the dispersal potential of the nitric oxide donor. MAHMA NONOate and molsidomine were dissolved into CNC at a concentration of 10 µmol L−1. Interestingly, total fluorescence of the planktonic cells increased significantly in the wells with biofilms treated with both the donors (Figure 2c, d), reflecting an increase in cellular detachment at the tested concentrations. The biofilm exposed for 2 h showed an average of 0.3 log increase in fluorescence when compared with the control (PBS) (Figure 2c). When the same treatment was extended for 6 h, a difference up to 0.6 log was measured (Figure 2d). One-hour exposure was also tested but it was not significant (data not shown).
One-week old Salmonella biofilm dispersal by MAHMA NONOate dissolved in BPS and CNC. Biofilms were preformed by S. enterica typhimurium 14028 for 1-week on polystyrene prior to the treatment with MAHMA NONOate and molsidomine. Contact time at which biofilms were exposed to the nitric oxide donor is listed on each panel. a, b Decreasing of biofilm formation measured by using the technique of crystal violet staining. c, d A fluorescent Salmonella 14028 pGFP-ON biofilm was treated with MAHMA NONOate or molsidomine dissolved in CNC. Increase in fluorescence of the planktonic cells was measured at 485 nm/535 nm. The box-plots encompass the lower and upper quartiles, thick lines within the box are the median values, and the whiskers indicate the degree of dispersion of the data. Outliers are shown as dots. Dotted line represents the grand mean. Letters above each box represent the Tukey means separation: different letters are significant different means.
CNC was also tested on 1-week old biofilms at 4 and 37°C, to determine the effect of temperature on the dispersion potential. No significant differences were determined on 1-week old biofilm when exposed to molsidomine + CNC versus the control CNC + PBS. Biofilms were exposed for 6 h. 22°C seems to be the most appropriate temperature for obtaining a significant dispersal.
Releasing profile of MAHMA NONOate in BPS and CNC
To better understand the synergistic effect of CNC–MAHMA NONOate composites, the diffusion of NO from the hydrogel was studied in the absence of biofilms. Electrodes were first calibrated in buffer solution (Figure 3a, b). The average sensitivity of the NO microelectrodes was 10.5 ± 0.1 pA nM−1 within the range of 20 pM–100 nM. The average response time of the electrodes was 0.65 ± 0.24 s.
Microelectrodes were used to directly measure NO flux from CNC hydrogels to better understand the mass transfer under abiotic conditions. A microelectrode was positioned at the surface of a hydrogel immediately after mixing the CNC and MAHMA NONOate while continuously measuring surface concentration and flux. At 25°C, nitric oxide dissociated from the MAHMA NONOate–CNC hydrogel. The surface concentration was 98.8 ± 0.1 µmol L−1 and the boundary layer was approximately 400 µm from the surface of the gel (Figure 4). The surface flux of nitric oxide was 0.92 ± 0.01 pmol cm2 s−1, and the decay profile was modeled using Fick’s first law (R = 0.989; Figure 4b) based on the methods in McLamore et al. (2009). As expected, the nitric oxide surface concentration (10.1 ± 0.6 µmol L−1), surface flux (0.36 ± 0.26 pmol cm2 s−1), and boundary layer thickness (approximately 150 µm) were significantly lower when the MAHMA NONOate was diluted 1:10 in the CNC hydrogel (Figure 4b). For the diluted sample, the regression coefficient correlating the measured flux profile and the predicted behavior using Fick’s first law decreased significantly (R = 0.713; Figure 4b).
Nitric oxide diffusion in CNC. MAHMA NONOate was mixed with cellulose nanocrystals (whisker type) and a hydrogel was formed with a final concentration of 1 mM. A microcapilary was tapered with a tip diameter of ca. 10 μm using a glass puller. Consequently the hydrogel–NONOate was injected into the microcapillary and the microcapillary was placed into a phosphate buffer solution (PBS). A nitric oxide microsensor was immediately used to measure release of NO (both concentration and flux). a Nitric oxide concentration profiles from the hydrogel surface. b Nitric oxide flux profiles. 10:1 represent a 10 times dilution of the MAHMA NONOate dissolved in CNC. Error bars represent the standard error of three replicas.
Although the exact amount of nitric oxide liberated within biofilms from nitric oxide donors have not yet been established, we measured the release rate of nitric oxide from the CNC hydrogel enriched with MAHMA NONOate. MAHMA NONOate was initially dissolved in PBS to a concentration of 500 mM, and then it was dissolved in CNC at a final concentration of 1 µM. A nitric oxide microelectrode was used to measure the release rate (Figure 5). Our measurements (three replicas) showed that 60% of the nitric oxide is released as gas during the first 23 min (~725 s); the decay constant was 4.1 ± 0.4 h−1. As expected, a 1:10 dilution of MAHMA NONOate in CNC significantly decreased the surface concentration/flux, and the time required for approximately 60% of nitric oxide released as gas (~1125 s) was significantly longer; the decay constant was 2.3 ± 1.1 h−1.
Nitric oxide release profiles of hydrogel-NONOate. Time 0 represents injection of the CNC:NONOate hydrogel into a glass capillary. 10:1 represent a 10 times dilution of the MAHMA NONOate dissolved in CNC. Experiment has been replicated three times. The graph represents an average of the three experiments.
Discussion
Every wet surface is a substrate for microbial biofilms and in food handling facilities biofilms can be particularly problematic. Protected by extracellular polymers, microbes within biofilms are significantly more resistant to chlorine and other disinfectants (Corcoran et al. 2014). As a result, several disinfectants have been used to remove biofilm, however disinfectants fail to completely eradicate biofilms from food contact surface materials (Corcoran et al. 2014). Current research has been instrumental in identify nitric oxide as potential additive to disinfectant (Barraud et al. 2006; Marvasi et al. 2014).
To focus on applicative approaches of the nitric oxide donor technology, we focused on dispersing well-established biofilms in the shortest time possible. To meet this need, a composite of nitric oxide and a hydrogel was used, considering the attractive physicochemical properties of hydrgoels as reviewed by Malmsten (2011). Nitric oxide donors have been combined with a number of hydrogels in preliminary studies (Koehler et al. 2008), but to date no hydrogels have been developed with nitric oxide donors which can potentially be scaled up for commercial applications. In this work, CNC was selected as a candidate for potential large scale application because the material is produced in large batches by a commercial forest based nanomaterial processing facility. In addition, CNC has an ionic charged surface that can facilitate attachment of biofilm EPS (Marvasi et al. 2010). For the first time, we show that association of MAHMA NONOate and molsidomine with CNC improved the biofilm dispersion potential when compared with PBS (Figures 1, 2). CNC–MAHMA NONOate allowed the dispersion of 1-week old biofilm with a contact time of at least 2 h; This can be ascribed to the combination of two different factors: (1) the cells do not have enough time to switch from the biofilm state to the planktonic state in less than 2 h; (2) the nitric oxide diffusion into the biofilm requires a certain amount of time (based on concentration of the nitric oxide donor in the gel). Temperature seems also to play a role on the dispersion potential. In terms of dispersal the exposure to 22°C results to be the most appropriate temperature when compared with 4 and 37°C. We can hypothesize that at 37°C the nitric oxide is completely depleted within a short time. On the opposite at lower temperature the nitric oxide releasing prolife is reduced in CNC. It is well known that properties of CNC change according with the temperature (George et al. 2011).
Due to the porous network, diffusion is the predominant transport process within hydrogels and cell aggregates. We measured the nitric oxide diffusion from CNC, observing that nitric oxide can diffuse up to 500 µm from the capillary opening, which is an important observation since 1-week old biofilms rarely have a thickness greater than 0.5 mm (Paramonova et al. 2007). With reference of the releasing time, our measurements show that 60% of the nitric oxide is released as gas during the first 12 min. In the literature, similar release profiles in PBS were observed with the nitrosothiols S-nitroso-N-acetylpenicillamine (SNAP), S-nitroso-l-glutathione (GSNO) and sodium nitroprusside (Barraud et al. 2009b).
Finally, it is worth mentioning that the improved ability of MAHMA NONOate-CNC association to disperse biofilm may be due to the low-moderate antimicrobial activity of CNC (Azizi et al. 2013), even though in our experimental conditions, CNC did not show any significant antimicrobial activity. In literature other molecules have been associated with CNC to improve its antimicrobial effectiveness: for example, CNC stabilized with ZnO–Ag exhibited greater bactericidal activity against Salmonella choleraesuis and Staphylococcus aureus compared to cellulose-free ZnO–Ag heterostructure nanoparticles of the same particle size (Azizi et al. 2013). Association of porphyrin (Feese et al. 2011) and silver nanoparticles (Drogat et al. 2011).
Further studies should also be addressed in associating nitric oxide donors with nanoparticle composites with effective antibacterial and biofilm-disrupting properties. To that end several polymers can be used, for example silk fibroin–silver nanoparticle composite showed both an effective antibacterial activity against the methicillin-resistant S. aureus and as inhibitor of biofilm formation (Fei et al. 2013).
The mechanical and physical properties of the bio-composites can also be interesting to study in association with nitric oxide donors. It is well known that bacterial adhesion was sensitive to surface roughness and enhanced as the roughness of composite in catheters surfaces (Cheng et al. 2013). For example Staphylococcus epidermidis adhesion and growth were markedly higher on rough titanium surfaces than on smooth surfaces (Cheng et al. 2013). Nitric oxide may help in fostering a better dispersion over these surfaces.
To our knowledge, this is the first study that shows the association of nitric oxide donors with CNC as a biofilm dispersant agent. Further studies can determine the association of other additives and further applications in foaming solution, in addition to testing different hydrogels. This, in turn, can implement new sustainable cleaning strategies by expanding the tool-kit of pro-active practices for “Good Agricultural Practices (GAPs), “Hazard Analysis and Critical Control Point” (HACCP) and Cleaning-in-place protocols (CIP).
References
Ahmed EM (2013) Hydrogel: Preparation, characterization, and applications (2015). J Adv Res. doi:10.1016/j.jare.2013.07.006
Alagely A, Rajamani S, Teplitski M (2011) Luminescent reporters and their applications for the characterization of signals and signal-mimics that alter LasR-mediated quorum sensing. Methods Mol Biol 692:113–130. doi:10.1007/978-1-60761-971-0_9
Azizi S, Ahmad MB, Hussein MZ, Ibrahim NA (2013) Synthesis, antibacterial and thermal studies of cellulose nanocrystal stabilized ZnO–Ag heterostructure nanoparticles. Molecules 18:6269–6280. doi:10.3390/molecules18066269
Barraud N, Hassett DJ, Hwang SH, Rice SA, Kjelleberg S, Webb JS (2006) Involvement of nitric oxide in biofilm dispersal of Pseudomonas aeruginosa. J Bacteriol 188:7344–7353. doi:10.1128/JB.00779-06
Barraud N, Schleheck D, Klebensberger J, Webb JS, Hassett DJ, Rice SA et al (2009a) Nitric oxide signaling in Pseudomonas aeruginosa biofilms mediates phosphodiesterase activity, decreased cyclic di-GMP levels, and enhanced dispersal. J Bacteriol 191:7333–7342. doi:10.1128/JB.00975-09
Barraud N, Storey MV, Moore ZP, Webb JS, Rice SA, Kjelleberg S (2009b) Nitric oxide-mediated dispersal in single- and multi-species biofilms of clinically and industrially relevant microorganisms. Microb Biotechnol 2:370–378. doi:10.1111/j.1751-7915.2009.00098.x
Barraud N, Kardak BG, Yepuri NR, Howlin RP, Webb JS, Faust SN et al (2012) Cephalosporin-3′-diazeniumdiolates: targeted NO-donor prodrugs for dispersing bacterial biofilms. Angew Chem Int Ed Engl 51:9057–9060. doi:10.1002/anie.201202414
Charville GW, Hetrick EM, Geer CB, Schoenfisch MH (2008) Reduced bacterial adhesion to fibrinogen-coated substrates via nitric oxide release. Biomaterials 29:4039–4044. doi:10.1016/j.biomaterials.2008.07.005
Chaturvedi P, Vanegas DC, Taguchi M, Burrs SL, Sharma P, McLamore ES (2014) A nanoceria–platinum–graphene nanocomposite for electrochemical biosensing. Biosens Bioelectron 58:179–185. doi:10.1016/j.bios.2014.02.021
Cheng M, Yu Q, Sun H (2013) Review: Novel strategies for the prevention and treatment of biofilm related infections. Int J Mol Sci 14:18488–18501. doi:10.3390/ijms140918488
Corcoran M, Morris D, De Lappe N, O’Connor J, Lalor P, Dockery P et al (2014) Commonly used disinfectants fail to eradicate Salmonella enterica biofilms from food contact surface materials. Appl Environ Microbiol 80:1507–1514. doi:10.1128/AEM.03109-13
Drogat N, Granet R, Sol V, Memmi A, Saad N, Klein Koerkamp C et al (2011) Antimicrobial silver nanoparticles generated on cellulose nanocrystals. J Nanoparticle Res 13:1557–1562. doi:10.1007/s11051-010-9995-1
Feese E, Sadeghifar H, Gracz HS, Argyropoulos DS, Ghiladi RA (2011) Photobactericidal porphyrin-cellulose nanocrystals: synthesis, characterization, and antimicrobial properties. Biomacromolecules 12:3528–3539. doi:10.1021/bm200718s
Fei X, Jia M, Du X, Yang Y, Zhang R, Shao Z et al. (2013) Green synthesis of silk fibroin–silver nanoparticle composites with effective antibacterial and biofilm-disrupting properties. Biomacromolecules 9;14(12):4483–4488. doi:10.1021/bm4014149
Firoved AM, Wood SR, Ornatowski W, Deretic V, Timmins GS (2004) Microarray analysis and functional characterization of the nitrosative stress response in nonmucoid and mucoid Pseudomonas aeruginosa. J Bacteriol 186:4046–4050. doi:10.1128/JB.186.12.4046-4050.2004
Friedemann MN, Robinson SW, Gerhardt GA (1996) o-Phenylenediamine-modified carbon fiber electrodes for the detection of nitric oxide. Anal Chem 68:2621–2628. doi:10.1021/ac960093w
George J, Ramana KV, Bawa AS, Siddaramaiah (2011) Bacterial cellulose nanocrystals exhibiting high thermal stability and their polymer nanocomposites. Int J Biol Macromol 48:50–57. doi:10.1016/j.ijbiomac.2010.09.013
Hetrick EM, Shin JH, Paul HS, Schoenfisch MH (2009) Anti-biofilm efficacy of nitric oxide-releasing silica nanoparticles. Biomaterials 30:2782–2789. doi:10.1016/j.biomaterials.2009.01.052
Hrabie JA, Klose JR, Wink DA, Keefer LK (1993) New nitric oxide-releasing zwitterions derived from polyamines. J Org Chem 58:1472–1476. doi:10.1021/jo00058a030
Keefer LK, Nims RW, Davies KM, Wink DA (1996) “NONOates” (1-substituted diazen-1-ium-1,2-diolates) as nitric oxide donors: convenient nitric oxide dosage forms. Methods Enzymol 268:281–293. doi:10.1016/S0076-6879(96)68030-6
Klemm D, Kramer F, Moritz S, Lindstrom T, Ankerfors M, Gray D et al (2011) Nanocelluloses: a new family of nature-based materials. Angew Chem Int Ed Engl 50:5438–5466. doi:10.1002/anie.201001273
Koehler JJ, Zhao J, Jedlicka SS, Porterfield DM, Rickus JL (2008) Compartmentalized nanocomposite for dynamic nitric oxide release. J Phys Chem B 112:15086–15093. doi:10.1021/jp803276u
Malmsten M (2011) Antimicrobial and antiviral hydrogels. Soft Matter 7:8725–8736. doi:10.1039/C1SM05809F
Marvasi M, Visscher PT, Casillas Martinez L (2010) Exopolymeric substances (EPS) from Bacillus subtilis: polymers and genes encoding their synthesis. FEMS Microbiol Lett 313:1–9. doi:10.1111/j.1574-6968.2010.02085.x
Marvasi M, Chen C, Carrazana M, Durie I, Teplitski M (2014) Dispersal of biofilms formed by Salmonella enterica and Escherichia coli O157:H7 by nitric oxide donors. Appl Microbiol Biotech Express 4:42. doi:10.1186/s13568-014-0042-y
McLamore ES, Porterfield DM (2011) Non-invasive tools for measuring metabolism and biophysical analyte transport: self-referencing physiological sensing. Chem Soc Rev 40:5308–5320. doi:10.1039/c0cs00173b
McLamore ES, Porterfield DM, Banks MK (2009) Non-invasive self-referencing electrochemical sensors for quantifying real-time biofilm analyte flux. Biotechnol Bioeng 102:791–799. doi:10.1002/bit.22128
Merritt JH, Kadouri DE, O’Toole GA (2005) Growing and analyzing static biofilms. Curr Protoc Microbiol Chapter 1: Unit 1B 1. doi: 10.1002/9780471729259.mc01b01s00
Noel JT, Arrach N, Alagely A, McClelland M, Teplitski M (2010) Specific responses of Salmonella enterica to tomato varieties and fruit ripeness identified by in vivo expression technology. PLoS One 5:e12406. doi:10.1371/journal.pone.0012406
O’Toole GA, Kolter R (1998) Initiation of biofilm formation in Pseudomonas fluorescens WCS365 proceeds via multiple, convergent signalling pathways: a genetic analysis. Mol Microbiol 28:449–461. doi:10.1046/j.1365-2958.1998.00797.x
Paramonova E, de Jong ED, Krom BP, Can DM, Busscher HJ, Sharma PK (2007) Low-load compression testing: a novel way of measuring biofilm thickness. Appl Environ Microbiol 73:7023–7028. doi:10.1128/AEM.00935-07
Porterfield DM, Laskin JD, Jung SK, Malchow RP, Billack B, Smith PJ et al (2001) Proteins and lipids define the diffusional field of nitric oxide. Am J Physiol Lung Cell Mol Physiol 281:L904–L912
Regev-Shoshani G, Crowe A, Miller CC (2013) A nitric oxide-releasing solution as a potential treatment for fungi associated with tinea pedis. J Appl Microbiol 114:536–544. doi:10.1111/jam.12047
Siro I, Plackett D (2011) Microfibrillated cellulose and new nanocomposite materials: a review. Cellulose 17:459–494. doi:10.1007/s10570-010-9405-y
Srey S, Jahid IK, Ha S (2013) Biofilm formation in food industries: a food safety concern. Food Control 31:572–585. doi:10.1016/j.foodcont.2012.12.001
Teplitski M, Al-Agely A, Ahmer BMM (2006) Contribution of the SirA regulon to biofilm formation in Salmonella enterica serovar Typhimurium. Microbiol Sgm 152:3411–3423. doi:10.1099/mic.0.29118-0
Thakur VK, Thakur MK (2014) Recent advances in green hydrogels from lignin: a review. Int J Biol Macromol 72:834–847. doi:10.1016/j.ijbiomac.2014.09.044
Vanegas DC, Taguchi M, Chaturvedi P, Burrs S, Tan M, Yamaguchi H et al (2014) A comparative study of carbon–platinum hybrid nanostructure architecture for amperometric biosensing. Analyst 139:660–667. doi:10.1039/c3an01718d
Wang PG, Cai TB, Taniguchi N (2005) Nitric oxide donors. Wiley, Weinheim
Xiong Y, Liu Y (2010) Biological control of microbial attachment: a promising alternative for mitigating membrane biofouling. Appl Microbiol Biotechnol 86:825–837. doi:10.1007/s00253-010-2463-0
Zacharia IG, Deen WM (2005) Diffusivity and solubility of nitric oxide in water and saline. Ann Biomed Eng 33:214–222. doi:10.1007/s10439-005-8980-9
Zhang L, Mah TF (2008) Involvement of a novel efflux system in biofilm-specific resistance to antibiotics. J Bacteriol 190:4447–4452. doi:10.1128/JB.01655-07
Authors’ contributions
All authors read and approved the final manuscript. MM, ESM conceived experiments. MM wrote the manuscript and ESM helped to draft the manuscript. MM performed the statistical analysis. IAD, DCV, PC carried out the experiments. MM, ESM analyzed data.
Acknowledgements
This research was supported by funding provided by the Florida Tomato Committee, Grant #106486 (MM, University of Florida) and by the UC-Davis Center for Produce Safety (MM, ESM), Grant #2014-308 (University of Florida) and MM start-up Grant from Middlesex University, London.
Compliance with ethical guidelines
Competing interest The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Additional files
Additional file 1: Figure S1.
Luminescence of Salmonella 14028 pTIM2442 upon exposure to CNC and molsidomine. General metabolic state of the cells was assessed using the redox-coupled FMNH2/Luciferase produced by a S. Typhimurium ATCC14028 strain harboring high copy number plasmid in which the luxCDABE operon is under the phage λ promoter (pTIM2442). Concentrations of molsidomine was 10 µM. Combination of molecules to which cultures of Salmonella 14028 pTIM2442 were exposed are listed on the figure. Each graph represents the average of 12 replicas.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Marvasi, M., Durie, I.A., McLamore, E.S. et al. Salmonella enterica biofilm-mediated dispersal by nitric oxide donors in association with cellulose nanocrystal hydrogels. AMB Expr 5, 28 (2015). https://doi.org/10.1186/s13568-015-0114-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s13568-015-0114-7