Abstract
Due to their outstanding performance, low cost, ease of fabrication, diverse photonic, and optoelectronic applications, metal halides perovskite have attracted extensive interest in photodetector applications. Currently, devices made by metal oxides, metal sulfides, and 2D materials had achieved good responsivity, but suffered from high dark current, slow response speed, small on-off ratio, and poor stability. Whole performances of these photodetectors are not satisfactory. Here, a lateral perovskite (CH3NH3PbBr3)/Ethanolamine/TiO2 (in ethanol) trilayer photodetector is designed for achieving high performance. EA treatment enhances electron extraction and reduces undesired recombination. This trilayer device shows good performances with low dark current of 1.5 × 10−11 A, high on-off ratio of 2700, high photodetectivity of 1.51 × 1012 Jones, high responsivity of 0.13 A W−1, and high stability, comparative to conventional single layer devices. This work provides the way to improve the performance of metal halide perovskite photodetectors.
Avoid common mistakes on your manuscript.
Introduction
Photodetectors have wide range applications including optical communication, bio-medical sensing, and environmental pollution monitoring [1,2,3]. In the recent years, organic-inorganic lead halide perovskite materials have attracted excessive consideration due to their exceptional features such as high optical absorption, long charge carrier life time, and long diffusion length [4,5,6,7,8,9]. These characteristics suggested that the organic-inorganic perovskite are excellent materials for photodetector applications [10,11,12,13,14,15,16,17,18,19,20,21]. Up to now, the vertical structure has been widely used for photodetectors [22,23,24,25,26,27]. Recently, Zhang et al. fabricated perovskite photodetector by employing vertical structure [27]. This device demonstrated good light capability and performance, but suffered from high dark current (1.5 nA). Interestingly, lateral structures of photodetectors have attracted tremendous consideration because of low conduction losses and its simple and low-cost fabrication process. Materials such as transition metal dichalcogenides [28, 29], metal oxides [30, 31], and organic materials [32, 33] have been used for photodetector applications, among them perovskite materials attracted a lot of consideration. Single-layer perovskite devices were fabricated, but exhibited low on/off ratio, high dark current, and poor electrical instabilities [34, 35]. For example, Ding et al. fabricated a single-layer device which has high dark current, low detectivity, and low on-off ratio [35]. An organic-perovskite photodetector which is designed by Wang et al. have attained good performance, but have large dark current (ranging from 10−7 to 10−8 A) [36]. Chen et al. fabricated bilayer perovskite photodetector by introducing organic polymer layer and modified heterojunction interface to improve device performance, but still device exhibits large dark current and low detectivity [37]. However, low detectivity (D*) and high dark current is observed because of the poor heterojunction interface barrier mismatch which enhances the carrier recombination. So, suitable material choice for interfacial layer is important for device performance [33, 38]. Single crystal CH3NH3PbBr3 photodetectors have also been fabricated [39,40,41], but their results are not satisfactory because of small on-off ratio and high dark current (≈10−10 A).
Many approaches have been applied to improve the device performance by balancing the carriers transport and minimizing the junction resistance by matching the energy levels between the material layers. For example, metal fluorides [42], conjugated polyelectrolyte [43], and polar solvents [44] were used to reduce the energy barrier mismatch between metal oxides (ZnO, MoO3, ZrO2) and active layers to improve the optoelectronic device performance.
In this paper, we fabricated a lateral trilayer perovskite photodetector by inserting interfacial dipole layer of ethanolamine, which provides the high electron extraction with suppression of undesired carrier recombination, and as a result the device shows improved performance. In this designed structure, light with the intensity of 0.5 mW cm−2 absorbs in CH3NH3PbBr3 film and carrier’s movement is held in the alcoholic TiO2 film. An energy barrier gap between the alcoholic TiO2 and CH3NH3PbBr3 film is reduced by introducing ethanolamine layer. The designed trilayer photodetector shows excellent performance with low dark current of 1.5 × 10−11 A, photodetectivity of 1.51 × 1012 Jones, on-off ratio of 2700, rise time of 0.49 s, decay time of 1.17 s, linear dynamic range (LDR) of 68.6 dB, with high environmental stability.
Results and Discussion
Single and trilayer photodetectors were fabricated on glass substrate as shown in Fig. 1a, b respectively. First of all, the TiO2 (mixed in ethanol) was fabricated on a glass substrate, and then ethanolamine film was deposited on the TiO2, afterwards, 60-nm thick Al electrodes were deposited by thermal evaporation on ethanolamine film by using shadow mask, resulting in channel width of 2000 μm and channel length of 30 μm. Then MAPbBr3 film was deposited on the ethanolamine (EA) film (details are in “Methods/Experimental” section). Figure 1c shows the image of trilayer photodetector.
Figure 2a shows the XRD (X-ray diffraction) pattern of the MAPbBr3 film and the MAPbBr3/EA/TiO2 trilayer film. Four peaks of MAPbBr3 and MAPbBr3/EA/TiO2 trilayer film at 15.16°, 30.32°, 46.04°, and 62.76° are clearly observed. There are no characteristic peaks of PbBr2, alcoholic TiO2, and EA observed in MAPbBr3/EA/TiO2 trilayer film. It shows high purity of the perovskite. The Fig. 2b presents the absorption of single and trilayer films. TiO2 and EA films do not display any absorption. All absorption is done in perovskite film both for single and trilayer device. No prominent absorption difference is observed between the MAPbBr3 film and MAPbBr3/EA/TiO2 trilayer film. A band gap of 2.3 eV is also observed by absorption spectra. Absorption at different (PbBr2) ratios is shown in the Fig. 2c.
The surface morphology of the MAPbBr3 film was studied by scanning electron microscope (SEM). A large number of pin holes and cracks were observed on the perovskite film when annealed at higher temperature, as shown in Fig. 3a. Since the pin holes or cracks act as non-radiative recombination centers which results in adverse device performance [45]. On the other hand, a dense and crack-free morphology was obtained with large grain size when the perovskite film was annealed at 75 °C for 10 min (Fig. 3b). Thus, the optimized annealing temperature helped in obtaining highly crystalline films without pinholes and cracks, which can promote the separation and transportation processes of photo-excited carriers [45, 46].
Figure 4a–c shows the band energy diagrams of the alcoholic TiO2, ethanolamine, and the MAPbBr3 (determined by ultraviolet photoelectron spectroscopy (UPS) measurement). The attained Fermi levels for alcoholic TiO2, ethanolamine, and the perovskite are 3.84, 4.35, and 5 eV respectively. The calculated conduction band maxima (CBM) for alcoholic TiO2, ethanolamine, and the perovskite are 3.81, 3.62, and 3.4 eV respectively. Band energy diagram of MAPbBr3/EA/TiO2 shows that photo-generated excitons are formed in the perovskite film as shown in Fig. 4d. Therefore, electrons and holes can be segregated through the MAPbBr3/EA interface. Electrons will flow to EA and then fall into the TiO2 film, and photoholes would remain in the MAPbBr3 film.
Figure 4e, f presents the I-V curves of the alcoholic TiO2 device, MAPbBr3 device, and the MAPbBr3/EA/TiO2 trilayer device (under dark and under light illumination with intensity of 0.5 mW cm−2). A high dark current with a value of 1.24 × 10−8 A is calculated for alcoholic TiO2 device, while the value of photocurrent is nearly similar to the value of dark current. This high dark current and low photocurrent of device is observed at 5 V bias. The single-layer device fabricated by MAPbBr3 shows the value of dark current is 1.41 × 10−10 A and value of photocurrent is 9.95 × 10−9 A, which shows better performance than alcoholic TiO2-based device. In comparison, the MAPbBr3/EA/TiO2 trilayer device shows lower dark current of 1.51 × 10−11 A and enhanced photocurrent of 4.09 × 10−8 A. The depletion region created around the MAPbBr3/EA interface is the reason of the small amount of dark current in the MAPbBr3/EA/TiO2 trilayer device, due to which conducting areas were contracted and dark current is suppressed. A large recombination occurs in single-layer photodetectors, because of holes and electrons were transported in same layer. That is the reason photocurrent of trilayer photodetector is higher than other single-layer photodetectors. For the trilayer photodetector, photo-generated electrons and holes are separated by heterojunction. Electrons will move from MAPbBr3 film to the EA film and then into alcoholic TiO2 film through the interface. Because of this, electrons will be separated from the holes, due to which carrier recombination reduces dramatically, and this leads to a larger photocurrent. We applied different perovskite ratios to enhance the device performance as shown in Fig. 4g. The optimal perovskite ratio for trilayer photodetector is 1:1.
Responsivity (R) and detectivity (D*) are important factors for photodetector devices. Where responsivity is defined as:
Where Ip represents current under white light and Id represents current in dark. Pin represents the effective incident light power on effective region (electrode channel region) [15]. Responsivity (R) can be enhanced by decreasing the electrode channel length, illumination power Pin, and by increasing bias voltage [30]. According to Eq. (1), responsivity for trilayer photodetector device is 0.13 A W−1 with incident white light intensity of 0.5 mW cm−2, while 0.03 A W−1 responsivity is calculated for single-layer photodetector device. An increased photocurrent and suppressed dark current is the reason for the enhanced responsivity of the trilayer photodetector device. Figure 5a shows the responsivity of the single and trilayer devices.
Detectivity is defined as follows:
Where R is the responsivity of the photodetector device, S is the effective channel region under illumination, and q represents the electronic charge (1.6 × 10−19 C) [16]. Detectivity is an important parameter to signify the light sensitivity of a photodetector. Greater detectivity means larger sensitivity in detecting light signals. Figure 5b shows the detectivity of the single and trilayer devices.
According to Eq. (2), detectivity calculated for trilayer device is 1.51 × 1012 Jones (light intensity is 0.5 mW cm−2 and bias of 5 V), while value of 1.19 × 1011 Jones is calculated for the single-layer MAPbBr3 device. Trilayer device exhibits high detectivity compared to single-layer device. The very high D* of the trilayer device is due to its very low dark current.
Figure 5c, d shows the spectral responsivity and detectivity of the single and trilayer photodetector at 5 V and under light illumination of 10.6 μW cm−2. Trilayer device show high responsivity of 0.33 A W−1 and high detectivity of 4.46 × 1012 Jones at the wavelength of 520 nm. While for the single-layer device, responsivity is 0.14 A W−1 and detectivity is 1.9 × 1012 Jones. This shows that the trilayer photodetector can detect very weak signal of light. External quantum efficiency (EQE) spectra of both devices are measured as shown in Fig. 5e. EQE for single-layer device has been measured up to 30%, and for trilayer device up to 80% at a bias of 5 V. Absorption curve (Fig. 2b) also strengthens the results of EQE spectra.
Signal to noise ratio (SNR) and linear dynamic range (LDR) are two more important parameters to characterize a photodetector, described as:
Where Jlight and Jdark are photocurrent and dark current density respectively [24]. The SNR can provide the detail about the level of a desired signal (photocurrent) to the background noise (dark current); background noise is less prominent when the value of SNR is high. Range of incident light power can be measured by LDR. It is generally reported in decibels (dB). LDR and SNR of the two photodetectors are measured under an applied voltage of 5 V. SNR of the single-layer device is 69. The trilayer photodetector depict a far greater SNR of 2700. The calculated LDR of trilayer photodetector is 68.6 dB, while for single-layer photodetector, LDR is 36.9 dB. The improved responsivity, detectivity, LDR, and SNR clearly shows the advantage of the trilayer photodetector over the single-layer photodetector.
In Fig. 6, on/off switching characteristics of two photodetectors were measured under light intensity of 0.5 mW cm−2 and applied bias of 5 V. Both photodetectors exhibit excellent on-off switching repetitions, shown in Fig. 6a, c. One on-off cycle of both devices are shown in Fig. 6b, d. For single-layer device, current rises and reached to its maximum value, and then decreases slowly under illumination until the light is off. This phenomenon occurs in single-layer photodetector because the photo-generated charge carriers recombine at deep level emission sites, due to which photocurrent decreases with the passage of time. While for trilayer perovskite photodetector, current rises very quickly and reached to its maximum value, then remains stable under illumination until the light is off. This phenomenon occurs because the deep level emission sites do not affect so much photo-generated charge carriers [38]. The calculated on-off ratio was 70 for single-layer photodetector device, and measured rise/decay time is 0.72/1.72 s. While for trilayer device, on-off ratio is 2700 and its rise/decay time is 0.49/1.17 s. Rise/decay time for trilayer photodetector device is smaller comparative to single-layer photodetector device because of faster electrons and holes generation and recombination phenomenon. Time required for the photocurrent in which it reaches to 90% of its maximum value is called rise time, and time required for the photocurrent in which it drops to 10% of its maximum value is called decay time [17]. In conventional semiconductors, value of rise time and decay time is large and it originates due to long-lived traps. Separation and recombination of the charge carriers around the junction is the reason for high on-off ratio, enhanced responsivity, high detectivity, and high LDR [3, 30]. This is the reason due to which shorter rise time and decay time of trilayer photodetector device is achieved.
Lastly, the samples were placed in an ambient environment with 30–40% relative humidity to investigate the environmental stability of the trilayer photodetector. Absorption and XRD were measured for stability as shown in Fig. 7a, b respectively. No specific changes were observed in absorption spectra after 30 days. XRD pattern were almost same after 30 days. Extra characteristic peaks due to environment were not observed. It shows the high stability of our perovskite film. The dark and photocurrent (under white light intensity of 0.5 mW cm−2) remain almost the same after 30 days, as shown in Fig. 7c. Trilayer photodetector device shows nearly stable photocurrent, which represents that our device is stable and less effected by ambient environment.
Overall performance with D* of 1.51 × 1012 Jones, on-off ratio of 2700, rise and decay time of 0.49/1.17 s, LDR of 68.6 dB, and EQE up to 80% is achieved by the trilayer device, which shows high performance of the trilayer photodetector device. Due to the excellent interface between perovskite, EA, and alcoholic TiO2, the excellent performance of detector is obtained. Table 1 shows the results of present metal halide perovskite photodetectors.
Perovskite photodetector based on SnO2 was also fabricated, and due to very low on-off ratio and high dark current, the performance of the photodetector was not satisfactory as shown in Fig. 8a. All this happened due to energy level mismatching [47]. We also used phenyl-C61-butyric acid methyl ester (PCBM) and PCBM:PMMA blend as an electron transport layer to fabricated perovskite photodetector, but the performance of these devices were far much worse than SnO2-based devices as shown in Fig. 8b, c respectively. Choosing a suitable electron transport layer (ETL) is very important for achieving good performance of a photodetector as clearly seen by the experiments. Trilayer photodetector devices with Ag electrodes were also fabricated, but the performance of these devices was not satisfactory due to high dark current and low photocurrent as shown in Fig. 8d.
Methods/Experimental
Material Preparation
PbBr2 and CH3NH3Br were purchased from Xi’an Polymer Light Technology Corporation. DMF, DMSO, Ethanolamine, and 2-Methoxyethanol were purchased from Alfa Aesar, and TiO2 10% soluble in ethanol (30 nm particle size) were purchased from InnoChem. All materials were used without additional purification. Glass slides used as substrates were manufactured by SAIL BRAND.
TiO2 in Alcohol
The TiO2 was mixed into ethanol (ratio of 1:16 by volume) with various concentrations. A 50 μL TiO2 is dissolved in 800 μL ethanol and stirred for 1 h at room temperature. Due to the carriers blocking phenomenon of compact TiO2, it cannot be used as a good electron transport layer [48]. So that, TiO2 mixed in alcohol was used as ETL.
Ethanolamine
EA and 2-methoxyethanol mixture were synthesized by using previously reported method [49]. The ethanolamine 3%wt ratios was mixed into 2-methoxyethanol to prepare solution mixture.
Perovskite
A 1 M solution of CH3NH3PbBr3 was prepared by reacting the CH3NH3Br and PbBr2 at a 1:1 (by weight) in a mixture of dimethylsulfoxide (DMSO) and N,N-dimethylformamide (DMF) with 1:4 (by volume), then stirring was applied at the temperature of 70 °C for overnight.
Device Fabrication
Glass substrates were washed with detergent, deionized water, isopropyl alcohol, and acetone solvents for 20 min each and then dried with N2 air, and were finally cleaned by O2 plasma for 15 min to eliminate the particles left behind on the substrates. Firstly, glass substrates were spin coated by alcoholic TiO2 at the speed of 4000 rpm for 30 s under ambient environment, and then annealed at 150 °C for 30 min. Afterwards, EA in 2-methoxyethanol was deposited on the TiO2 film at the speed of 3000 rpm for 40 s under ambient environment, and then annealed at 130 °C for 10 min. Then, Al (aluminum) electrodes with the thickness of 60 nm were deposited on EA film by thermal evaporation. The channel width of the shadow mask is 2000 μm and the channel length of the shadow mask is 30 μm. Finally, MAPbBr3 solution was spin coated on the EA film by two-step method to complete the fabrication process. In the first step, solution was spin coated with the speed of 1000 rpm for 10 s, and then spin coated with the speed of 5000 rpm for 30 s. During the second step, 50 μL of toluene were dropped on the spinning substrate at 22 s before the spin coating end.
Characterization
Keithley 4200 was used to measure the electrical characterizations under ambient environment at room temperature. XZ-150WA cold light illuminator was used as a source of white light. Before using the white light, the intensity of the light was measured by monosilicon detector. Newport Oriel 200 was used as a source of monochromatic light. SEM (Hitachi S-4800) was used to characterize the surface image and morphology of the film. JASCO V-570 spectrophotometer was used to record the absorption spectra. KRATOS AXIS ULTRA DLD photoelectron spectroscopy system with an unfiltered He I (21.22 eV) gas-discharge lamp was used to record the UPS analysis. Rifaku D/MAX-2004 XRD with Cu K radiation (\( \lambda =1.54178\ \mathrm{\AA} \)) was used to study the phase identification of the film, which is operating at 60 mA and 40 kV.
Conclusions
In conclusion, a perovskite/EA/TiO2 trilayer photodetector was designed and fabricated. The dark current is significantly reduced in trilayer photodetector device because of formed heterojunction. The EA film and the alcoholic TiO2 film were used to fabricate perovskite/EA/TiO2 trilayer photodetector device. In this type of design, light absorbs in perovskite film, and photoelectrons transported in alcoholic TiO2 film, and EA is responsible for decreasing the energy barrier mismatch and enhances the photoelectron extraction. When light is illuminated, charge carriers are separated through the heterojunction. The electrons are transferred into EA layer then transferred and transported in to alcoholic TiO2, and the holes remains in the perovskite layer. As a result, charge carrier’s recombination suppressed and photocurrent enhances. The overall performance of trilayer device shows D* of 1.51 × 1012 Jones, on-off ratio of 2700, R of 0.13 A W−1, rise and decay time of 0.49/1.17 s, and LDR of 68.6 dB. The MAPbBr3/EA/TiO2 photodetector device shows very high whole performance as compare to single crystal-based devices and 2D material-based devices. The stability of the trilayer device in an ambient environment shows high significance in future optoelectronics devices. A modified interfacial layer and electron transport layer can significantly suppress the carrier recombination and improve the performance of perovskite photodetector devices. This approach could play an important role to improve device performance by heterojunction modifications.
Abbreviations
- EA:
-
Ethanolamine
- EQE:
-
External quantum efficiency
- LDR:
-
Linear dynamic range
- PCBM:
-
Phenyl-C61-butyric acid methyl ester
- PMMA:
-
Polymethylmethacrylate
- SEM:
-
Scanning electron microscope
- SNR:
-
Signal to noise ratio
- UPS:
-
Ultraviolet photoelectron spectroscopy
- XRD:
-
X-ray diffraction
References
Cao F, Tian W, Gu B, Ma Y, Lu H, Li L (2017) High-performance UV–vis photodetectors based on electrospun ZnO nanofiber-solution processed perovskite hybrid structures. Nano Res 10:2244–2256
Koppens FH, Mueller T, Avouris P, Ferrari AC, Vitiello MS, Polini M (2014) Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat Nanotechnol 9:780–793
Ren Z et al (2017) Bilayer PbS quantum dots for high-performance photodetectors. Adv mater 29:1702055.
Im JH, Lee CR, Lee JW, Park SW, Park NG (2011) 6.5% efficient perovskite quantum-dot-sensitized solar cell. Nanoscale 3:4088–4093
Wang Y, Zhang Y, Zhang P, Zhang W (2015) High intrinsic carrier mobility and photon absorption in the perovskite CH3NH3PbI3. Phys Chem Chem Phys 17:11516–11520
Shi D, Adinolfi V, Comin R, Yuan M, Alarousu E, Buin A, Chen Y, Hoogland S, Rothenberger A, Katsiev K, Losovyj Y, Zhang X, Dowben PA, OF M, Sargent EH, Bakr OM (2015) Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347:519–522
Stranks SD et al (2013) Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342:341–344
Son D-Y et al (2016) Self-formed grain boundary healing layer for highly efficient CH3 NH3 PbI3 perovskite solar cells. Nature Energy 1:16081
Wang Y et al (2017) Stitching triple cation perovskite by a mixed anti-solvent process for high performance perovskite solar cells. Nano Energy 39:616–625
Marchioro A et al (2014) Unravelling the mechanism of photoinduced charge transfer processes in lead iodide perovskite solar cells. Nat Photonics 8:250–255
Lee Y et al (2015) High-performance perovskite-graphene hybrid photodetector. Adv Mater 27:41–46
Lin Q, Armin A, Lyons DM, Burn PL, Meredith P (2015) Low noise, IR-blind organohalide perovskite photodiodes for visible light detection and imaging. Adv Mater 27:2060–2064
Lu H, Tian W, Cao F, Ma Y, Gu B, Li L (2016) A self-powered and stable all-perovskite photodetector-solar cell nanosystem. Adv Funct Mater 26:1296–1302
Saliba M et al (2016) Incorporation of rubidium cations into perovskite solar cells improves photovoltaic performance. Science 354(6309):206–209
Jin Z, Wang J (2014) PIN architecture for ultrasensitive organic thin film photoconductors. Sci Rep 4:5331
Jana MK, Chithaiah P, Murali B, Krupanidhi SB, Biswas K, Rao CNR (2013) Near infrared detectors based on HgSe and HgCdSe quantum dots generated at the liquid–liquid interface. J Mater Chem C 1:6184
Tian W et al (2013) Low-cost fully transparent ultraviolet photodetectors based on electrospun ZnO-SnO2 heterojunction nanofibers. Adv Mater 25:4625–4630
Shaikh PA et al (2016) Schottky junctions on perovskite single crystals: light-modulated dielectric constant and self-biased photodetection. J Mater Chem C 4:8304–8312
Wang Y et al (2015) Hybrid graphene-perovskite phototransistors with ultrahigh responsivity and gain. Adv Opt Mater 3:1389–1396
Zhuo S, Zhang J, Shi Y, Huang Y, Zhang B (2015) Self-template-directed synthesis of porous perovskite nanowires at room temperature for high-performance visible-light photodetectors Angewandte. Chemie 54:5693–5696
He M, Chen Y, Liu H, Wang J, Fang X, Liang Z (2015) Chemical decoration of CH3NH3PbI3 perovskites with graphene oxides for photodetector applications. Chem Commun 51:9659–9661
Dou L, Yang YM, You J, Hong Z, Chang WH, Li G, Yang Y (2014) Solution-processed hybrid perovskite photodetectors with high detectivity. Nat commun 5:5404
Guo F, Yang B, Yuan Y, Xiao Z, Dong Q, Bi Y, Huang J (2012) A nanocomposite ultraviolet photodetector based on interfacial trap-controlled charge injection. Nat nanotechnol 7:798–802
Gong X et al (2009) High-Detectivity polymer photodetectors with spectral response from 300 nm to 1450 nm. Sci 325:1665–1667
Tang F, Chen Q, Chen L, Ye F, Cai J, Chen L (2016) Mixture interlayer for high performance organic-inorganic perovskite photodetectors. Appl Phys Lett 109:123301
Li C, Han C, Zhang Y, Zang Z, Wang M, Tang X, Du J (2017) Enhanced photoresponse of self-powered perovskite photodetector based on ZnO nanoparticles decorated CsPbBr 3 films. Sol Energy Mater Sol Cells 172:341–346
Zhang T et al (2018) High speed and stable solution-processed triple cation perovskite photodetectors. Adv Opt Mater 6:1701341
Kufer D, Nikitskiy I, Lasanta T, Navickaite G, Koppens FH, Konstantatos G (2015) Hybrid 2D-0D MoS2 -PbS quantum dot photodetectors. Adv Mater 27:176–180
Shim J et al (2016) High-performance 2D rhenium disulfide (ReS2 ) transistors and photodetectors by oxygen plasma treatment. Adv Mater 28:6985–6992
Jin Z et al (2016) Graphdiyne:ZnO nanocomposites for high-performance UV photodetectors. Adv Mater 28:3697–3702
Chaaya AA, Bechelany M, Balme S, Miele P (2014) ZnO 1D nanostructures designed by combining atomic layer deposition and electrospinning for UV sensor applications. J Mater Chem A 2:20650–20658
Jin Z, Zhou Q, Mao P, Li H, Wang J (2016) All-solution-processed PIN architecture for ultra-sensitive and ultra-flexible organic thin film photodetectors. Sci China Chem 59:1258–1263
Li L et al (2013) Organic ultraviolet photodetector based on phosphorescent material. Opt lett 38:3823–3826
Cao M, Tian J, Cai Z, Peng L, Yang L, Wei D (2016) Perovskite heterojunction based on CH3NH3PbBr3 single crystal for high-sensitive self-powered photodetector. Appl Phys Lett 109:233303
Ding J, Du S, Zuo Z, Zhao Y, Cui H, Zhan X (2017) High Detectivity and rapid response in perovskite CsPbBr3 single-crystal photodetector. J Phys Chem C 121:4917–4923
Wang Y et al (2018) Solution processed PCBM-CH3NH3PbI3 heterojunction photodetectors with enhanced performance and stability. Org Electron 57:263–268
Chen S, Teng C, Zhang M, Li Y, Xie D, Shi G (2016) A flexible UV–vis–NIR photodetector based on a perovskite/conjugated-polymer composite. Adv Mater 28:5969–5974
Wei Y et al (2018) Hybrid organic/PbS quantum dot bilayer photodetector with low dark current and high detectivity. Adv Funct Mater 28:1706690
Wang L et al (2016) Tunable bandgap in hybrid perovskite CH3NH3Pb(Br3−yXy) single crystals and photodetector applications. AIP Adv 6:045115
Fang Y, Dong Q, Shao Y, Yuan Y, Huang J (2015) Highly narrowband perovskite single-crystal photodetectors enabled by surface-charge recombination. Nat Photonics 9:679–686
Saidaminov MI et al (2015) Planar-integrated single-crystalline perovskite photodetectors. Nat commun 6:8724
Hung LS, Tang CW, Mason MG (1997) Enhanced electron injection in organic electroluminescence devices using an Al/LiF electrode. Appl Phys Lett 70:152–154
Choi H et al (2011) Combination of titanium oxide and a conjugated polyelectrolyte for high-performance inverted-type organic optoelectronic devices. Adv Mater 23:2759–2763
Lee BR et al (2014) Amine-based polar solvent treatment for highly efficient inverted polymer solar cells. Adv Mater 26:494–500
Brandt RE, Stevanović V, Ginley DS, Buonassisi T (2015) Identifying defect-tolerant semiconductors with high minority-carrier lifetimes: beyond hybrid lead halide perovskites. MRS Commun 5:265–275
Chen L-C, Tseng Z-L, Huang J-K, Chen C-C, Chang S (2016) Fullerene-based Electron transport layers for semi-transparent MAPbBr3 perovskite films in planar perovskite solar cells. Coatings 6:53
Jiang Q et al (2016) Enhanced electron extraction using SnO2 for high-efficiency planar-structure HC(NH2)2PbI3-based perovskite solar cells. Nat Energy 2:16177
Yi X, Ren Z, Chen N, Li C, Zhong X, Yang S, Wang J (2017) TiO2 nanocrystal/perovskite bilayer for high-performance photodetectors. Adv Electron Mater 3:1700251
Yu JC et al (2015) High-performance planar perovskite optoelectronic devices: a morphological and interfacial control by polar solvent treatment. Adv Mater 27:3492–3500
Hu X, Zhang X, Liang L, Bao J, Li S, Yang W, Xie Y (2014) High-performance flexible broadband photodetector based on organolead halide perovskite. Adv Funct Mater 24:7373–7380
Zhou L et al (2017) All-inorganic perovskite quantum dot/mesoporous TiO2 composite-based photodetectors with enhanced performance. Dalton Trans 46:1766–1769
Maculan G et al (2015) CH3NH3PbCl3 single crystals: inverse temperature crystallization and visible-blind UV-photodetector. J Phys Chem Lett 6:3781–3786
Wang F, Mei J, Wang Y, Zhang L, Zhao H, Zhao D (2016) Fast Photoconductive responses in organometal halide perovskite photodetectors. ACS Appl Mater Interfaces 8:2840–2846
Dong Y et al (2016) Improving all-inorganic perovskite photodetectors by preferred orientation and plasmonic effect. Small 12:5622–5632
Acknowledgements
Special thanks to Dr. Deborah Eric from Beijing institute of technology for her valuable suggestions.
Funding
This work was supported by the National Natural Science Foundation of China (NSFC) (No. 61675024, and No. 61874009).
Availability of Data and Materials
The datasets supporting the results of this article are included within the article.
Author information
Authors and Affiliations
Contributions
AAK designed the experiments and fabricate photodetector. AAK and UK perform the characterizations and prepared manuscript. ZY and LD analyzed data and revised the manuscript. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Khan, A.A., Yu, Z., Khan, U. et al. Solution Processed Trilayer Structure for High-Performance Perovskite Photodetector. Nanoscale Res Lett 13, 399 (2018). https://doi.org/10.1186/s11671-018-2808-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2808-7