Abstract
We first verify the critical impact of evaporation on the formation of zigzag hollow cracks by regulating the drying micro-environment of silver nanoparticle film. Uneven evaporation and component segregation contributes to the flows along the surface and inside of droplets. Asymmetric vapor concentration distribution is capable of weakening the surface flow of droplets, thus suppressing the inner compressive stress of nanoparticles and leading to a surface morphology with less cracks. Although defect-free and surface smooth nanoparticle film deposited by a solution-based method remains a big challenge, our work has referential significance to optimize high-quality nanoparticle film with appropriate deposition and curing processes. Moreover, an optimization possibility through the drying micro-environment should be considered in high-end applications due to its enhanced effect on high-resolution patterns.
Avoid common mistakes on your manuscript.
Introduction
Precursor inks (silver, gold, copper, etc.) are compatible with flexible fabrication due to their low processing temperature (< 200 °C) [1]. However, crack problem remains unsolved and will deteriorate the conductivity and adhesion properties of the deposited film [2]. The underlying mechanism is worth further exploring, while most previous reports concentrate on some external effect, such as laser [3], intense pulsed light [4], and ions [5]. Uneven evaporation nature is underrated to some extent, although the coffee ring effect has been proven in numerous studies [6]. Fast evaporation flux of the periphery area and the pinning of the triple line contribute to the outward compensation flow inside of droplets. Accordingly, directional surface flow can be induced with component segregation [7].
Evaporation dynamics, chemical reduction, microfluidic regulation, and nanoparticle assembly have been discussed here to achieve a comprehensive understanding of the crack-forming process. To explore the critical impact of the drying micro-environment on the forming of zigzag hollow cracks, the coffee ring effect is enhanced by the ink formulation, so as to (1) drive nanoparticles to the periphery area and make them self-assembled to form the surface film, (2) promote the forming of cracks by increasing the compressive stress, (3) increase the air pressure between two neighboring droplets, which avoids their coalescence and leads to a self-aligning phenomenon, making the distance of the droplet boundaries short enough to present the obvious effect of the drying micro-environment.
The regulation of the drying micro-environment directly proves the close relationship between the forming of cracks and solvent evaporation. It has certain innovations and advantages in determining the critical impact of evaporation on the forming of surface cracks, while other factors are controlled to be unchanged. According to the proposed mechanism, wet film cured without the forming of cracks has been achieved here by enhancing the chemical reduction, or by reducing the size of droplets using inkjet printing technology. This work has referential significance to optimize high-quality nanoparticle film deposited using solution-based methods.
Materials and Methods
Silver acetate (2.5 g), ethyl alcohol (EA, 3 ml), and Octylamine (OA, 3 ml) are mixed with stirring at room temperature for 2 h. The prepared ink is filtered (0.22 μm) before using. Glass substrate is cleaned by DI water, isopropyl, and tetrahydrofuran in an ultrasonic cleaner for 10 min in sequence. A syringe with a nozzle diameter of 0.25 mm is used to release droplets (d ~ 5 mm) (Fig. 1a). The increased drying time of large size droplets (tdrying ~ r2) makes the observation easier. Hotplate and UV equipment (IntelliRay 600 W, Uvitron, USA) are used to promote chemical reduction with different evaporation dynamics. The UV equipment is equipped with a light filter, which eliminates its hydrophilic effect. Surface morphology was observed with an optical microscope up to 1000× (Nikon Eclipse E600 POL) and a scanning electron microscope (SEM, NOVA NANOSEM 430) installed with an energy-dispersive X-ray spectrometer (EDS) module.
Results and Discussion
The coffee ring effect and the induced Marangoni flow are schematically described in Fig. 1b. The OA/EA ratio increases at the periphery area, on account of the higher evaporation rate, as well as the higher surface tension and boiling point of OA (28 dyn/cm, 176 °C) than EA (22 dyn/cm, 78 °C). The surface tension difference results in an outward Marangoni flow. Three different regions (I, II, and III) appear after 2 cycles of UV irradiation (60 s/cycle) (Fig. 1c). The intervals of each cycle are used to remove the thermal effect. Solutes aggregate at region I due to the outward compensation flow and is solidified soon because of the fierce evaporation. Regions II and III are nanoparticle suspensions, but the latter is more sparse. More cycles of irradiation make region III transformed from ripples (3 cycles) to cracks (10 cycles), while region II is rough, and region I keeps smooth (Fig. 1d, e). The adhesion property is seriously deteriorated when cracks are formed. Figure 1f schematically describes the underlying mechanism. Monodispersed nanoparticles (Additional file 1: Figure S1) tend to be self-assembled and form compact surface film due to the outward Marangoni flow, the evaporation driving up force, and the surface tension (large specific surface area). The film thickness decreases from region I to III, accordingly making the strains increased under compressive stress, and even radial ripples can be resulted. The periphery surface film suppresses the evaporation of the underneath liquid, thus the compensation flow is reversed, leading to the drop of the liquid level, and inducing a compressive stress in chord direction.
Solution-processed films cured by UV irradiation have the weaker coffee ring effect due to its moderate evaporation rate than thermally treated ones [8]. It contributes to the difference on the formation of surface films (Fig. 2a). Thermal effect should be considered when wet film is continuously UV irradiated for 5 min, resulting in zigzag-shaped ripples at the periphery area (Fig. 2b). The deformation in chord direction originates from the increased radial compressive stress, which is induced by the enhancing of the outward surface flow and the evaporation difference. More regular zigzag-shaped ripples can be observed when a moderate temperature is applied to the substrate (Ts = 60 °C). The sintering time (5 to 15 min) independence of ripples demonstrates their forming before being completely solidified (Fig. 2c). Liquid-supported surface thin film is easily deformable under the compressive stress, and cracks generate along the ripples (Fig. 2d). As the drying process continues, the reversed compensation flow will leave a hollow inside topography of ripples, which can be evidenced by the EDS area scanning for silver element.
The critical impact of evaporation on the forming of cracks has been discussed above. The drying micro-environment is capable of regulating the distribution of evaporation flux, which is studied in-depth in our previous report [9, 10], and therefore is also likely to have an impact on crack formation. Based on the simplified vapor diffusion model of solvent evaporation (cρ = rc0/ρ), a color map of the vapor concentration (c) can be drawn to describe the influences of the drying micro-environment on the evaporation of two neighboring droplets (Fig. 3a). Asymmetrical evaporation flux can be achieved when another droplet is released nearby. A closer distance of droplet boundaries suppresses the evaporation and the surface flow [11] (Additional file 1: Figure S2), accordingly reducing the tendency to form ripples, especially zigzag-shaped ones. Outward surface flow increases the air pressure between droplets, thus making them self-aligned to achieve a short distance of only tens of microns. Even no ripples formed at the nearest region, and then the ripple length increases and finally recovers to zigzag shape with the increased distance of droplet boundaries (Fig. 3b, c). The area of the smooth periphery region enlarges due to the more time for nanoparticle reduction and aggregation before they are self-assembled to form thick film under the premise of evaporation suppression. Furthermore, the suppression effect is more apparent for the first droplet, which is released 60 s earlier than the second one. The earlier formed surface film of the first droplet diminishes its evaporation effect on the drying micro-environment of the second droplet, while the evaporation of the second droplets will influence the whole ripple-forming process of the first droplet.
It should be emphasized that regulation of the drying micro-environment not only acts as a method to suppress zigzag hollow cracks but also directly proves the close relationship between the forming of cracks and solvent evaporation. This work has referential significance to optimize high-quality nanoparticle film, especially for precursor ink. When droplets are still released by the syringe, the cracks can be easily removed by enhancing the rate of chemical reduction under the premise that the evaporation is less affected (Additional file 1: Figure S3). A thin surface film on liquid, which can be easily deformed, can form under the action of evaporation, when the reduced nanoparticles are few. Therefore, the accelerated chemical reduction will make the solute concentration high enough to form a thick self-assembled surface nanoparticle film and then avoid the forming of cracks. Another effective way to deal with the cracks can be achieved by reducing the size of droplets (Additional file 1: Figure S4). Inkjet printing is a potential technique to deposit wet film consisting of tiny droplets (diameter ~ 50 μm). Inkjet-printed films using the same ink system can be solidified without ripples and cracks, even cured at a high temperature of 100 °C for 30 min, taking advantages of [1] the quicker solidification process, [2] the weaker local evaporation rate, [3] the weaker fluid flows, [4] the higher local solute concentration, and [5] the changed drying micro-environment of each droplet.
Conclusion
The critical impact of evaporation on the forming cracks of solution processed nanoparticle film has been studied considering various aspects. The thickness of the liquid-supported surface film formed during the solidification process has a major influence on the topography under compressive stress. The size and shape of ripples can be continuously regulated by changing its drying micro-environment. This work provides a feasible way to accurately suppress the surface cracks and may have referential significance to optimize high-quality nanoparticle film deposited using solution-based methods.
Abbreviations
- DI:
-
Deionized
- EA:
-
Ethyl alcohol
- EDS:
-
Energy-dispersive X-ray spectrometer
- OA:
-
Octylamine
- SEM:
-
Scanning electron microscope
- UV:
-
Ultraviolet
References
Li Y, Wu Y, Ong BS (2005) Facile synthesis of silver nanoparticles useful for fabrication of high-conductivity elements for printed electronics. J Am Chem Soc 127:3266–3267
Liu H, Xu W, Tan W, Zhu X, Wang J, Peng J, Cao Y (2016) Line printing solution-processable small molecules with uniform surface profile via ink-jet printer. J Colloid Interface Sci 465:106–111
Giust GK, Sigmon TW (1997) New ripple patterns observed in excimer-laser irradiated SiO2/polycrystalline silicon/SiO2 structures. Appl Phys Lett 70:3552–3554
Gokhale P, Mitra D, Sowade E, Mitra KY, Gomes HL, Ramon E, Al-Hamry A, Kanoun O, Baumann RR (2017) Controlling the crack formation in inkjet-printed silver nanoparticle thin-films for high resolution patterning using intense pulsed light treatment. NANOTECHNOLOGY 28:495301
Mishra P, Ghose D (2009) Effect of initial target surface roughness on the evolution of ripple topography induced by oxygen sputtering of Al films. J Appl Phys 105:014304
Deegan RD, Bakajin O, Dupont TF, Huber G, Nagel SR, Witten TA (1997) Capillary flow as the cause of ring stains from dried liquid drops. NATURE 389:827–829
Eales AD, Dartnell N, Goddard S, Routh AF (2016) Thin, binary liquid droplets, containing polymer: an investigation of the parameters controlling film shape. J Fluid Mech 794:200–232
Tao R, Ning H, Chen J, Zou J, Fang Z, Yang C, Zhou Y, Zhang J, Yao R, Peng J (2018) Inkjet printed electrodes in thin film transistors. IEEE J ELECTRON DEVI 6:774–790
Tao R, Ning H, Fang Z, Chen J, Cai W, Zhou Y, Zhu Z, Yao R, Peng J (2017) Homogeneous surface profiles of inkjet-printed silver nanoparticle films by regulating their drying microenvironment. J Phys Chem C 121:8992–8998
Tao R, Fang Z, Zhang J, Ning H, Chen J, Yang C, Zhou Y, Yao R, Lin W, Peng J (2018) Critical impact of solvent evaporation on the resolution of inkjet printed nanoparticles film. ACS APPL MATER INTER 10:22883–22888
Pradhan TK, Panigrahi PK (2016) Influence of an adjacent droplet on fluid convection inside an evaporating droplet of binary mixture. COLLOID SURFACE A 500:154–165
Funding
This work was supported by National Key R&D Program of China (No.2016YFB0401504), National Natural Science Foundation of China (Grant.51771074, 51521002 and U1601651), National Key Basic Research and Development Program of China (973 program, Grant No.2015CB655004) Founded by MOST, National Science Foundation for Distinguished Young Scholars of China (Grant.51725505), Guangdong Natural Science Foundation (No.2016A030313459 and 2017A030310028), Guangdong Science and Technology Project (No.2016B090907001, 2016A040403037, 2016B090906002, 2017B090907016 and 2017A050503002), Guangzhou Science and Technology Project (201804020033).
Availability of data and materials
The datasets used for analysis can be provided on a suitable request, by the corresponding author.
Author information
Authors and Affiliations
Contributions
RT proposed the research work and wrote the paper. RT, JC, CY, and YZ carried out the statistical design of experiment and prepared the measurements. JZ, ZF, HN, RY, and YS analyzed the data. All authors helped to correct and polish the manuscript and read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Additional file
Additional file 1:
Figure S1. Monodispersed nanoparticles obtained after UV irradiation for 60 s. Figure S2. Schematic of asymmetrical directional flows of two neighboring droplets. Figure S3. High-quality nanoparticle film optimized with enhanced chemical reduction. (a) Schematic of wet film cured with different distance (8 cm, 24 cm) from the UV lamp. The side wall of the curing box is specially designed to achieve uniform UV irradiation, whose strength can be significantly increased when a closer distance from the UV lamp is applied (E1<<E2). (b) Syringe released droplets cured with cycles of UV irradiation at a distance of 24 cm from the UV lamp. (c) Syringe released droplets cured with cycles of UV irradiation at a distance of 8 cm from the UV lamp. Figure S4. High-quality nanoparticle film optimized using an inkjet printer (DMP-2831, FUJIFILM Dimatix, USA) with nozzle diameter of 16 μm. (a) Microscope photo with a magnification of 100×, and (b) 3D profile of the deposited film thermally cured at 100 ˚C for 30 min. The surface fluctuation can be ascribed to the travel line of inkjet printing with set drop space of 35 μm. (DOCX 1720 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Tao, R., Zhang, J., Fang, Z. et al. Zigzag Hollow Cracks of Silver Nanoparticle Film Regulated by Its Drying Micro-environment. Nanoscale Res Lett 13, 354 (2018). https://doi.org/10.1186/s11671-018-2777-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2777-x