Porous- and hollow-structured LiNb3O8 anode material was prepared by a hydrothermal-assisted sintering strategy for the first time. The phase evolution was studied, and the formation mechanism of the porous and hollow structure was proposed. The formation of the unique structure can be attributed to the local existence of liquid phase because of the volatilization of Li element. As the anode material, the initial discharge capacity is 285.1 mAhg−1 at 0.1 C, the largest discharge capacity reported so far for LiNb3O8. Even after 50 cycles, the reversible capacity can still maintain 77.6 mAhg−1 at 0.1 C, about 2.5 times of that of LiNb3O8 samples prepared by traditional solid-state methods. The significant improvement of Li storage capacity can be attributed to the special porous and hollow structure, which provides a high density of active sites and short parallel channels for fast intercalation of Li+ ions through the surface.
In recent years, much attention has been paid to hollow and porous structures due to their widespread applications in catalysis, energy, environmental engineering, drug delivery, and sensor systems [1,2,3,4]. Compared with other new energy batteries, lithium-ion batteries (LIBs) have gained commercial success as the predominant power source for portable electronics and show great potential in large-scale applications because of its high energy density, long lifespan, and environmental benignity . To obtain high electrochemical performance, the electrodes of LIBs always have open structures, which can provide a high density of active sites and parallel channels for faster intercalation of Li+ ions through the surface . However, it is challenging to synthesize the nanomaterials with open structures including porous and hollow architectures.
To improve LIBs performances, people have been seeking for high-performance electrode materials, including anode and cathode materials. LiFePO4 , LiCoO2 , LiMn2O4 , LiVPO4F , and various hybrid materials [11, 12] have been seriously considered as candidates for cathode materials. For anode materials, many different materials have been investigated as alternatives to graphite-based anode materials, such as transition metal oxides (TMOs) , molybdenum disulfide (MoS2), and graphene-based hybrids . In recent literature, niobium has been shown to have superior electrochemical performance ; some traditional compounds doped with Nb element and novel Nb-based compounds are well developed [16,17,18,19]. Nb-based oxides have been considered as promising anode materials for LIBs with improved safety. Compared with Li4Ti5O12 (with a theoretical capacity of 175 mAhg−1), Nb-based oxides have a relatively high theoretical capacity of 389 mAhg−1. Also, it is notable that the two Nb redox couples, Nb5+/Nb4+ and Nb4+/Nb3+, can suppress the formation of solid electrolyte interface (SEI) film during cycling . LiNb3O8, a well-known material, always appear in the preparation process of LiNbO3 as an impurity phase due to Li volatilization . Jian et al. firstly introduced LiNb3O8 material prepared by a solid-state reaction as an anode for LIBs. It is found that the as-prepared LiNb3O8 sample ball-milled with acetylene black (LiNb3O8-BM) largely improved the initial discharge/charge capacities (351 and 212 mAhg−1) than those of the as-prepared LiNb3O8 sample (250 and 170 mAhg−1) at 0.05 C; after 50 cycles, the capacity reached 150 mAhg−1 for LiNb3O8-BM at 0.1 C, only 30 mAhg−1 for LiNb3O8 sample . Porous LiNb3O8 nanofibers also exhibited improved capacity and cyclability in virtue of the high surface area, small nanocrystals, and porous structure with the initial discharge capacity of 241.1 mAhg−1 at 0.1 C . Due to the difficulty to obtain pure phase, as a novel anode material with high theoretical capacity, LiNb3O8 has rarely been studied.
In this paper, porous- and hollow-structured LiNb3O8 anode material was successfully prepared by a hydrothermal-assisted sintering process. The phase evolution was studied, and the formation mechanism of the porous and hollow structure was proposed. The morphological and electrochemical properties of LiNb3O8 as the anode material were also studied in detail.
Preparation of Samples
LiNb3O8 powders were prepared by the hydrothermal-assisted sintering process. Lithium hydroxide monohydrate (LiOH·H2O, Aladdin, ACS, ≥98.0%) and niobium pentoxide (Nb2O5, Aladdin, AR, 99.9%) were purchased as raw materials without further purification. First, 3.5 mmol of Nb2O5 was dispersed into 35 ml of LiOH·H2O transparent aqueous solution (the mole ratio of Li:Nb = 8:1) with magnetic stirring for 1 h. Then, the suspension solution was put into a 50-ml Teflon-lined hydrothermal synthesis autoclave reactor. After that, the reactor was sealed and maintained at 260 °C for 24 h and then cooled down to room temperature naturally. Finally, the as-prepared products were centrifuged and rinsed with deionized water and ethanol. After drying in an oven at 60 °C for 12 h, the white Li-Nb-O powders were collected and calcined at various temperatures from 500 to 800 °C for 2 h with a ramp rate of 5 °C/min.
The thermal decomposition characteristic of Li-Nb-O powder was studied by a thermogravimetric and differential scanning calorimeter (TG/DSC, Netzsch STA 409 PC/PG) from room temperature to 1200 °C with a ramp rate of 10 °C/min under N2 atmosphere. The crystal structures of the calcined powders were analyzed using X-ray powder diffraction (XRD; Bruker D8 Discover) with Cu Kα radiation. The morphologies of the calcined powders were characterized by scanning electron microscopy (SEM; JSM-6700F). X-ray photoelectron spectroscopy (XPS) analysis was performed on a Thermo-Fisher Escalab 250Xi instrument.
The LiNb3O8 electrodes were prepared by spreading slurry of LiNb3O8 powders, carbon black, and polyvinylidene fluoride (PVDF) with a weight ratio of 8:1:1 onto an aluminum foil. Afterward, the electrode was dried at 120 °C in a vacuum oven overnight. The anodes were punched into disks with a diameter of 16 mm. For the electrochemical measurements, CR2025 coin-type cells were assembled in an argon-filled glove box using lithium foil as the counter electrode and polypropylene microporous membrane (Celgard 2320) as a separator to isolate the two electrodes, and then, the 1.0-M LiPF6 electrolyte was dissolved in a mixture of ethylene carbonate and dimethyl carbonate (1:1 by volume). Galvanostatic charge-discharge tests of the cells were performed using a Land electric test system (Wuhan Land Electronics Co., Ltd., China) between 0 and 3 V (vs. Li/Li+) at different current densities of 0.1–1 C (1 C = 389 mAhg−1). Cyclic voltammetry (CV) curves were recorded on an electrochemical workstation (CHI604E, Shanghai Chenhua Instruments Co., Ltd., China) in the voltage range of 1–3 V.
Results and Discussion
Figure 1 plots the TG/DSC curves of the powder obtained after hydrothermal reaction without further calcination. The weight loss of the powder is very small, about 5%, even as the temperature reaches to 1100 °C, but the loss is occurring throughout the entire calcination process. This can be attributed to the evaporation of Li element due to its low melting temperature, which is confirmed by the DSC results with endothermic reaction process throughout the entire calcination process. At 330 °C, an endothermic peak occurs, which may originate from the formation of LiNbO3. An exothermic reaction occurs at 580 °C resulting from the reaction between LiNbO3 and Nb2O5 to form LiNb3O8. As seen in the DSC curve, beyond 1100 °C, the exothermic reaction becomes strong due to the decomposition of LiNb3O8.
The XRD patterns of Li-Nb-O powders calcined at different temperatures are shown in Fig. 2. It can be seen that the major phases are LiNbO3 and Nb2O5 at 500 °C. With the increase of calcination temperature, the diffraction peak at 30.26° appears which can be indexed as the (410) plane of monoclinic LiNb3O8. The reaction can be described by Eq. (1) not Eq. (2) :
At 700 °C, the monoclinic LiNb3O8 is the predominant phase with almost negligible impurity. The pure phase of LiNb3O8 is obtained at 800 °C with all the diffraction peaks indexed to the monoclinic phase (JCPDS card no. 36–0307), a space group of P21/a. Compared with the traditional solid-state method, the pure phase of LiNb3O8 is more easily obtained using the hydrothermal-assisted sintering process.
The SEM images of LiNb3O8 powder calcined at 800 °C with different magnifications are presented in Fig. 3. The porous and hollow structure that resembles a honeycomb is formed by LiNb3O8 nanoparticles with the length of several micrometers. The structure is not flat, with obvious warping, and even forms closed tubby-like structures. It is fully different from the particle aggregation that results from conventional solid-state reactions. The size of the LiNb3O8 particle is about 200 nm, as shown in Fig. 3c. The small particle size and unique structure are beneficial to ion intercalation . The formation of the unique structure can be attributed to the lithium volatilization during the calcination process, as proved by TG-DSC results. As the easy volatilization of Li element, the excess Li element existing in the powder easily migrates to the surface of particles and turns into liquid phase. The local existence of liquid phase is conducive to the formation of new LiNb3O8 particles at the site and also encourages the formation of networks between the particles.
To further confirm the elemental compositions and the electronic state, the porous- and hollow-structured LiNb3O8 powders are analyzed by XPS, as shown in Fig. 4. The XPS data were calibrated using C 1s as a reference with the binding energy at 284.6 eV. In Fig. 4a, two peaks at 207.1 and 209.8 eV correspond to Nb 3d5/2 and 3d3/2, respectively, indicating the Nb5+ state in LiNb3O8 . The XPS spectra of O 1s in Fig. 4b can be deconvoluted into two peaks at 530.3 and 532 eV. The former is assigned to the Nb-O bonds, and the latter is related to nonlattice oxygen [22, 23].
To investigate the electrochemical performance of the as-prepared LiNb3O8 sample, the tests of CV and galvanostatic discharge-charge cycling were performed. The first three CV curves of LiNb3O8 powder at a scanning rate of 0.1 mV/s in the range of 3~1 V are shown in Fig. 5. In the first cycle, two pronounced peaks (Li insertion) are observed at 1.13 and 1.30 V; the former can be attributed to the partial reduction of Nb4+ to Nb3+, while the latter can be related to the full valence variation of Nb5+ to Nb4+ [18, 19]. As seen in Fig. 5, the subsequent cycles are quite different from the first cycle. The disappearance of the peaks at 1.13 and 1.30 V implies the phase transition in the first cycle is irreversible. Only the oxidation (Li extraction) peaks at 1.71 and 1.96 V remain stable upon cycling, implying the structure change of the LiNb3O8 sample in subsequent cycles is reversible.
Figure 6 shows the discharge-charge curves of the LiNb3O8 powder at 0.1 C (here, 1 C = 389 mAhg−1) between 3 and 1 V in the first, second, tenth, thirtieth, and fiftieth cycles. In the first discharge curve, two obvious potential plateaus can be observed at approximately 1.13 and 1.30 V, which is in good agreement with the CV results that two phase reactions, Nb4+ → Nb3+ and Nb5+ → Nb4+, take place. However, in the subsequent cycles, the plateaus that exist in the first cycle are replaced by sloping curves, implying different reactions between the first and subsequent cycles. At the same time, the initial discharge capacity of the LiNb3O8 sample is 285.1 mAhg−1 at 0.1 C, the largest discharge capacity reported so far for LiNb3O8 anode materials [18, 19]. 4.4 Li per unit formula can be inserted into the LiNb3O8 material, corresponding to a composition of Li5.4Nb3O8. However, the charge capacity in the first cycle is 106.4 mAhg−1, indicating that only 1.6 Li can be extracted reversibly. The big loss of 2.8 Li is ambiguous at present.
Figure 7 shows the cycling performance of LiNb3O8 sample at different current rates up to 50 cycles. The initial discharge capacities of LiNb3O8 powder at rates of 0.1, 0.5, and 1 C are 285.1, 250, and 228 mAhg−1, respectively. At a current rate of 0.1 C, the reversible capacity can still maintain 77.6 mAhg−1, about 2.5 times of that of LiNb3O8 samples prepared by traditional solid-state method (about 30 mAhg−1 at 0.1 C, Ref. ). The significant improvement of Li storage capacity can be attributed to the special porous and hollow structure of LiNb3O8 sample, which provides a high density of active sites and short parallel channels for faster intercalation of Li+ ions through the surface . When the rates increase to 0.5 and 1 C, the discharge capacities after 50 cycles remain 39.7 and 29.4 mAhg−1, respectively. It is expected that the capacity stability can be improved by suitable surface modification on LiNb3O8 material.
In summary, porous- and hollow-structured LiNb3O8 anode material was successfully prepared by the hydrothermal-assisted sintering strategy. The phase evolution was studied, and the formation mechanism of the porous and hollow structure was proposed. The formation of the unique structure can be attributed to the local existence of liquid phase because of the Li volatilization. As the anode material, the initial discharge capacity is 285.1 mAhg−1 at 0.1 C, the largest discharge capacity reported so far for LiNb3O8. After 50 cycles, the reversible capacity can still maintain 77.6 mAhg−1, about 2.5 times of that of the LiNb3O8 samples prepared by traditional solid-state methods. The significant improvement of Li storage capacity can be attributed to the special porous and hollow structure of LiNb3O8 powder, which provides a high density of active sites and short parallel channels for fast intercalation of Li+ ions through the surface.
Liu J, Xue DF (2008) Thermal oxidation strategy towards porous metal oxide hollow architectures. Adv Mater 20:2622–2627
Sheng T, Xu YF, Jiang YX, Huang L, Tian N, Zhou ZY, Broadwell I, Sun SG (2016) Structure design and performance tuning of nanomaterials for electrochemical energy conversion and storage. Acc Chem Res 49:2569–2577
Sun MH, Chen C, Chen LH, Su BL (2016) Hierarchically porous materials: synthesis strategies and emerging applications. Front Chem Sci Eng 10:301–347
Barhoum A, Melcher J, Van Assche G, Rahier H, Bechelany M, Fleisch M, Bahnemann D (2017) Synthesis, growth mechanism, and photocatalytic activity of zinc oxide nanostructures: porous microparticles versus nonporous nanoparticles. J Mater Sci 52:2746–2762
Zhang JJ, Huang T, Liu ZL, Yu AS (2013) Mesoporous Fe2O3 nanoparticles as high performance anode materials for lithium-ion batteries. Electrochem Commun 29:17–20
Xu GL, Wang Q, Fang JC, Xu YF, Li JT, Huang L, Sun SG (2014) Tuning the structure and property of nanostructured cathode materials of lithium ion and lithium sulfur batteries. J Mater Chem A 2:19941–19962
Islam MS, Driscoll DJ, Fisher CAJ, Slater PR (2005) Atomic-scale investigation of defects, dopants, and lithium transport in the LiFePO4 olivine-type battery material. Chem Mater 17:5085–5092
Okubo M, Hosono E, Kim J, Enomoto M, Kojima N, Kudo T, Zhou HS, Honma I (2007) Nanosize effect on high-rate Li-ion intercalation in LiCoO2 electrode. J Am Chem Soc 129:7444–7452
Kim DK, Muralidharan P, Lee HW, Ruffo R, Yang Y, Chan CK, Peng H, Huggins RA, Cui Y (2008) Spinel LiMn2O4 nanorods as lithium ion battery cathodes. Nano Lett 8:3948–3952
Reddy MV, Subba Rao GV, Chowdari BVR (2010) Long-term cycling studies on 4V-cathode, lithium vanadium fluorophosphates. J Power Sour 195:5768–5774
Wei CL, He W, Zhang XD, Shen JX, Ma JY (2016) Recent progress in hybrid cathode materials for lithium ion batteries. New J Chem 40:2984–2999
Kong JZ, Zhai HF, Qian X, Wang M, Wang QZ, Li AD, Li H, Zhou F (2017) Improved electrochemical performance of Li1.2Mn0.54Ni0.13Co0.13O2 cathode material coated with ultrathin ZnO. J Alloy Compd 694:848–856
Gao GX, Wu HB, Dong BT, Ding SJ, Lou XW (2015) Growth of ultrathin ZnCo2O4 nanosheets on reduced graphene oxide with enhanced lithium storage properties. Adv Sci 2:1400014
Zhang F, Tang YB, Liu H, Ji HY, Jiang CL, Zhang J, Zhang XL, Lee CS (2016) Uniform incorporation of flocculent molybdenum disulfide nanostructure into three-dimensional porous graphene as an anode for high-performance lithium ion batteries and hybrid supercapacitors. ACS Appl Mater Interfaces 8:4691–4699
Augustyn V, Come J, Lowe MA, Kim JW, Taberna PL, Tolbert SH, Abruña HD, Simon P, Dunn B (2013) High-rate electrochemical energy storage through Li+ intercalation pseudocapacitance. Nat Mater 12:518–522
Reddy MV, Subba Rao GV, Chowdari BVR (2013) Metal oxides and oxysalts as anode materials for Li ion batteries. Chem Rev 113:5364–5457
Anji Reddy M, Varadaraju UV (2011) Lithium insertion into niobates with columbite-type structure: interplay between structure-composition and crystallite size. J Phys Chem C 115:25121–25124
Jian ZL, Lu X, Fang Z, Hu YS, Zhou J, Chen W, Chen LQ (2011) LiNb3O8 as a novel anode material for lithium-ion batteries. Electrochem Commun 13:1127–1130
Xu HH, Shu J, Hu XL, Sun YM, Luo W, Huang YH (2013) Electrospun porous LiNb3O8 nanofibers with enhanced lithium-storage properties. J Mater Chem A 1:15053–15059
Zielińska B, Borowiak-Palen E, Kalenzuk RJ (2008) Preparation and characterization of lithium niobate as a novel photocatalyst in hydrogen generation. J Phys Chem Solids 69:236–242
Akazawaa H, Shimada M (2007) Mechanism for LiNb3O8 phase formation during thermal annealing of crystalline and amorphous LiNbO3 thin films. J Mater Res 22:1726–1736
Atuchin VV, Kalabin IE, Kesler VG, Pervukhina NV (2005) Nb 3d and O 1s core levels and chemical bonding in niobates. J Electron Spectrosc Relat Phenom 142:129–134
Zhai HF, Kong JZ, Yang JE, Xu J, Xu QR, Sun HC, Li AD, Wu D (2016) Resistive switching properties and failure behaviors of (Pt, Cu)/amorphous ZrO2/Pt sandwich structures. J Mater Sci Technol 32:676–680
This work is financially supported by the National Natural Science Foundation of China (No. 51202107) and Foundation of Henan Educational Committee (No. 16A140028).
The authors declare that they have no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Zhai, H., Liu, H., Li, H. et al. Hydrothermal-Assisted Sintering Strategy Towards Porous- and Hollow-Structured LiNb3O8 Anode Material. Nanoscale Res Lett 12, 463 (2017). https://doi.org/10.1186/s11671-017-2234-2
- Lithium-ion batteries
- Porous and hollow structure