Abstract
TiO2 NSAs/graphene/Cu2O was fabricated on the carbon fiber to use as photocastalysts by coating Cu2O on the graphene (G) decorated TiO2 nanosheet arrays (NSAs). The research focus on constructing the composite structure and investigating the reason to enhance the photocatalytic ability. The morphological, structural, and photocatalytic properties of the as-synthesized products were characterized. The experimental results indicate that the better photocatalytic performance is ascribed to the following reasons. First, the TiO2 NSAs/graphene/Cu2O composite structure fabricated on the carbon cloth can form a 3D structure which can provide a higher specific surface area and enhance the light absorption. Second, the graphene as an electron sink can accept the photoelectrons from the photoexcited Cu2O which will reduce the recombination. Third, the TiO2 nanosheet can provide more favorable carrier transportation channel which can reduce the recombination of carriers. Finally, the Cu2O can extend the light absorption range.
Avoid common mistakes on your manuscript.
Background
Recently, application of semiconductor photocatalyst titanium dioxide (TiO2) in environmental purification has attracted great attention owing to its tremendous advantages, such as stability, nontoxicity, and low cost [1,2,3]. Based on the fact that photocatalytic reactions mainly take place on the surfaces of the photocatalysts, the morphology is the crucial factor to determine the efficiency [4]. Up to now, many efforts have been made to fabricate TiO2 nanocrystals, nanowires, nanorods, and nanotubes [5,6,7,8]. However, the application of TiO2 nanosheet arrays with larger specific surface area in photocatalytic degradation is rarely reported. Especially, TiO2 nanosheet arrays grown on the carbon cloth can construct three-dimensional (3D) structures to improve the specific surface area.
Unfortunately, the wide bandgap of TiO2 limits the effective absorption of visible light [9]. In order to overcome the shortcoming, one strategy is to modify TiO2 with narrow bandgap semiconductors [10,11,12]. Among them, cuprous oxide (Cu2O) with narrow bandgap can be a promising candidate for expanding the absorption spectra range. [13,14,15,16,17,18] Moreover, the built-in electric field between P-type Cu2O and N-type TiO2 can accelerate the separation of carriers.
However, the poor interfacial feature between different semiconductors directly influences the separation efficiency of carriers. Therefore, the interfacial optimization is an effective way to enhance photocatalytic degradation efficiency [19, 20]. The previous researches indicate that graphene (G) shows excellent interfacial optimization function between different semiconductors due to its high conductivity and two-dimensional structure, which facilitates the interfacial contact and carrier transportation [21,22,23,24,25]. However, it is difficult to make graphene well disperse between different semiconductors. In this paper, a modified method is applied to fabricate the homogeneously dispersed G between TiO2 nanosheet and Cu2O.
In this study, the composite structure of TiO2 NSAs/G/Cu2O has been prepared (Fig. 1). The significant enhancement of photocatalytic activities was observed, and the corresponding results were analyzed. The proposed mechanism of the photocatalytic degradation was also discussed. As we know, there are no related reports on TiO2 NSAs/G/Cu2O photocatalysts up to now, so and thus it will be a meaningful reference for designing and fabricating this kind of photocatalyst used in photocatalytic degradation.
Methods
Preparation of TiO2 NSAs/G/Cu2O
The fabrication of TiO2 NSAs is the following. TiO2 sol was prepared using a previously reported method [10]. In brief, TiO2 seed layer was deposited on carbon cloth (2 cm × 3 cm) by immersing in TiO2 sol for 10 min. Then, the seed layer was calcined at 400 °C for 1 h. The Teflon-lined stainless steel autoclave (100 mL in volume) filled with 40 mL of aqueous solution of 10 M NaOH and 0.2 g of activated carbon was placed in an oven at 180 °C for 24 h. After the autoclave cooled down to room temperature, the prepare samples were rinsed with DI water to remove the residual activated carbon, followed by soaking with 0.1 M hydrochloric acid for 1 h, then washed to neutral with DI water.
For the composite structure of TiO2 NSAs/G, 0.2 g of graphene replacing activated carbon was added into the Teflon-lined stainless steel autoclave ethanol solution.
Cu2O layer was deposited by the following procedures. 2.3 mmol of Cu(CH3COO)2 and 2.3 mmol of CH3CONH2 were dissolved into 100 mL of diethylene glycol (DEG) under ultrasonication to prepare the reaction solution. Then, TiO2 NSAs or TiO2 NSAs/G substrate was immersed into the solution. Subsequently, it was heated to 120° under magnetic stirring and kept at this temperature for 6 h. After cooling down to room temperature in air, TiO2 or TiO2 NSAs/G substrate coated with Cu2O was washed with absolute ethanol and DI water for five times in sequence and dried in air.
Characterization
The morphologies of the samples were investigated by a field emission scanning electron microscopy (FE-SEM, Quanta FEG250). The crystal structure of samples was examined by X-ray diffraction (XRD, D8 Advance) with Cu K α at λ = 0.15406 nm radiation. XPS spectra were recorded on a Thermo Fisher ESCALAB 250Xi system with Al Kα radiation, operated at 150 W. The absorption spectrum of the samples was measured using a UV–vis spectrophotometer (TU-1901). The Raman spectrum of the sample was characterized by Raman spectroscopy (LabRAM HR800).
Photoelectrochemical Measurement
Photocurrent density was measured using an electrochemical workstation (CS2350) in a three-electrode electrochemical cell with 1 M Na2SO4 as the electrolyte, in which the as-prepared samples were acted as the working electrode, Pt and Ag/AgCl electrode were used as the counter and reference electrodes, respectively. The I–t curve was recorded under Xe lamp (153 mW/cm2) irradiation.
Measurement of Photocatalytic Activity
The photocatalytic activity was evaluated toward the photodegradation of RhB. A 500 W Xe lamp was used as the light source. The samples with same size 2 cm × 3 cm were placed into 20 ml RhB solution (10 mg/L). After irradiation for a designated time (30 min), 3 mL of RhB solution was taken out to identify the concentration of RhB using UV–vis spectrophotometer (TU-1901). All of these measurements were carried out at room temperature.
Results and Discussion
Figure 2a–c, the obtained TiO2 NSAs characterized by FE-SEM, shows that the uniform TiO2 NSAs with about 40–60 nm in width and 1.5 μm in height vertically grew on the surface of carbon cloth. These results illustrate that the morphology in favor of the enhancement of photocatalytic performance. As shown in Fig. 2d–f, Cu2O particles have been successfully deposited on the surface of the nanosheets. Unfortunately, G cannot be directly observed in Fig. 1d, e, though it could be confirmed by XPS measurement.
XRD patterns were performed to investigate the crystal phase structure of photocatalyst. The XRD patterns of TiO2 NSAs, TiO2 NSAs/G, and TiO2 NSAs/G/Cu2O are shown in Fig. 3. For TiO2 NSAs (curve a), five distinctive peaks match well with TiO2. In curve b (for TiO2 NSAs/G), there are the same diffraction peaks with curve a. The phase on G is not detected because the content is low. From the curve c (TiO2 NSAs/G/Cu2O), the diffraction peaks on Cu2O are observed.
X-ray photoelectron spectroscopy (XPS) was used to confirm the existence of G. The XPS survey spectrum of TiO2 NSAs/G composite shows the elements C, O, and Ti (Fig. 4a–c). The presence of these elements proves the method to fabricate TiO2 NSAs/G composite is feasible. XPS spectrum of C1s located at 284.77 eV can be corresponded to carbon-containing species on the surface, which is the dominant existence form (Fig. 4a). Moreover, the 288.37 eV indicates the tiny existence of C–O bond. The peak located at 529.78 eV is related to the oxygen bonded with metal as Ti–O, and the 534.98 eV is the adsorbed oxygen or hydroxyl species (Fig. 4b). It can be seen that the spectra of catalysis showed two peaks at 458.38 and 464.03 eV. These peaks can be assigned to 3d5/2 and 3d3/2 spin orbital components of Ti4+ species (Fig. 4c) [26, 27]. In order to confirm the existence of graphene, furtherly, the Raman spectrum was characterized. The typical Raman spectra of TiO2 NSAs/G are shown in Fig. 4d. There are two typical Raman peaks corresponding to the typical D band and G band of graphene, respectively.
The photocatalytic properties of the as-obtained samples were investigated by decomposition of RhB (Fig. 5a). Before irradiation started, the system was kept in dark for 1 h to reach the adsorption–desorption equilibrium. There is almost no change in the concentration of the solution when RhB solution is irradiated without any catalysts. After 180 min, the degradation ratio of RhB was almost 80% in the presence of TiO2 NSAs/G/Cu2O, whereas 50 and 40% of RhB was decomposed by TiO2 NSAs and TiO2 NSAs/ Cu2O, respectively. All of these measurements show that TiO2 NSAs/G/Cu2O exhibits more prominent photocatalytic activity compared with other samples. A very important reason for the advantage of TiO2 NSAs/Cu2O on the photodegradation of RhB is that Cu2O plays a significant role in extending light absorption spectrum. In addition, TiO2 NSAs/G/Cu2O exhibits a better photocatalytic activity than TiO2 NSAs/Cu2O which results from the presence of graphene. The graphene as an electron sink to accept the photoelectrons from the photoexcited Cu2O will reduce the recombination of photoelectron-hole pairs, resulting in a higher photocatalytic activity. The stability of the TiO2 NSAs/G/Cu2O was carried out, and the results (Fig. 5b) show that TiO2 NSAs/G/Cu2O has good stability.
Generally, responding ability to light is one of the most important factors for evaluating photocatalytic performance. Therefore, UV–vis absorption spectra of samples were characterized as shown in Fig. 6. The absorption of TiO2 NSAs is located in the UV region. Compared with TiO2 NSAs, the absorption edge of TiO2 NSAs/Cu2O shows redshift. This larger absorption would result in the improvement of the photocatalytic property of TiO2 NSAs/Cu2O.
To further understand the improvement of photocatalytic activity, the I–t response of TiO2 NSAs, TiO2 NSAs /Cu2O, and TiO2 NSAs/G/Cu2O were observed, as shown in Fig. 7. It can be found that TiO2 NSAs/G/Cu2O exhibits enhanced photocurrents compared with TiO2 NSAs and TiO2 NSAs/Cu2O. The higher photocurrent density of TiO2 NSAs/G/Cu2O indicates an enhanced light absorption and higher separation efficiency of photogenerated electrons and holes.
The improved photocatalytic property of TiO2 NSAs/G/Cu2O may be attributed to the following factors. First, the introduction of Cu2O can extend the light absorption range, and thus, the photocatalytic activities are enhanced. Second, the limitation of carrier recombination is a key factor to enhance the photocatalytic property. The graphene as an electron sink can accept the photoelectrons from the photoexcited Cu2O which will reduce the recombination. Besides, TiO2 nanosheet structure can provide more favorable carrier transportation channel. Third, the better photocatalytic property can take advantage of large specific surface area. TiO2 NSAs/G/Cu2O structure fabricated on the carbon cloth can form a 3D structure which can provide a higher specific surface area. The high surface area of the 3D structure allows not only more surfaces to be reached by the incident light but also more sites on the surface for the adsorption and photodegradation of RhB, which results in enhanced photocatalytic performance. Finally, the 3D structure can enhance the photon utilization efficiency. The structure allows a great number of the photons to penetrate deep inside the photocatalyst, and most photons are trapped within the 3D structure until being completely absorbed.
The corresponding mechanism of electron transfer has been illustrated in Fig. 8. Both TiO2 and Cu2O can be photoexcited under the light irradiation. Because the E VB of TiO2 is more positive than that of Cu2O, holes in the VB of TiO2 can migrate to the VB of Cu2O by the interface. Similarly, the E CB of Cu2O is higher than that of TiO2, so the electrons in the CB of Cu2O can transfer to the CB of TiO2. More importantly, graphene as electronic exchange medium can promote electron transfer ability between Cu2O and TiO2.
Conclusions
In summary, the novel 3D TiO2 NSAs/G/Cu2O structure is prepared via a simple and efficient method. Importantly, the composite structure exhibits excellent photocatalytic degradation properties. The enhanced performance can be ascribed to its extended light absorption range, large specific surface area, enhanced photon utilization efficiency, improved charge transfer efficiency and suppressed photoelectron-hole recombination. Furthermore, the photocatalysts grown on carbon cloths make the collection and recycle of photocatalysts much easier.
References
Schneider J, Matsuoka M, Takeuchi M, Zhang J, Horiuchi Y, Anpo M, Bahnemann DW (2014) Understanding TiO2 photocatalysis: mechanisms and materials. Chem Rev 114:9919–9986
Zhang Z, Huang Y, Liu K, Guo L, Yuan Q, Dong B (2015) Multichannel-improved charge-carrier dynamics in well-designed hetero-nanostructural plasmonic photocatalysts toward highly efficient solar-to-fuels conversion. Adv Mater 27:5906–5914
Fu K, Huang J, Yao N, Xu X, Wei M (2015) Enhanced photocatalytic activity of TiO2 nanorod arrays decorated with CdSe using an upconversion TiO2:Yb3+, Er3+ thin film. Ind Eng Chem Res 54:659–665
Tian J, Hao P, Wei N, Cui H, Liu H (2015) 3D Bi2MoO6 nanosheet/TiO2 nanobelt heterostructure: enhanced photocatalytic activities and photoelectochemistry performance. ACS Catal 5:4530–4536
Wang J, Ji G, Liu Y, Gondal MA, Chang X (2014) Cu2O/TiO2 heterostructure nanotube arrays prepared by an electrodeposition method exhibiting enhanced photocatalytic activity for CO2 reduction to methanol. Catal Commun 46:17–21
Yan W, He F, Gai S, Gao P, Chen Y, Yang P (2014) A novel 3D structured reduced graphene oxide/TiO2 composite: synthesis and photocatalytic performance. J Mater Chem A 2:3605–3612
Huang J, Fu K, Yao N, Deng X, Ding M, Shao M, Xu X, Wei M (2016) Enhanced photocatalytic performance using one dimensional ordered TiO2 nanorods modified by graphene oxide. J Nanosci Nanotechnol 16:14771482
Wei X, Shao C, Li X, Lu N, Wang K, Zhang Z, Liu Y (2016) Facile in situ synthesis of plasmonic nanoparticles-decorated g-C3N4/TiO2 heterojunction nanofibers and comparison study of their photosynergistic effects for efficient photocatalytic H2 evolution. Nanoscale 8:11034–11043
Yao N, Huang J, Fu K, Liu S, E D, Wang Y, Xu X, Zhu M, Cao B (2014) Efficiency enhancement in dye-sensitized solar cells with down conversion material ZnO: Eu3+, Dy3+, J Power Sources 267:405–410
Fu K, Huang J, Yao N, Deng X, Xu X, Li L (2016) Hybrid nanostructure of TiO2 nanorod arrays/Cu2O with a CH3NH3PbI3 interlayer for enhanced photocatalytic activity and photoelectrochemical performance. RSC Adv 6:57695–57770
Huang J, Liu S, Kuang L, Zhao Y, Jiang T, Liu S, Xu X (2013) Enhanced photocatalytic activity of quantum-dot-sensitized one-dimensionally-ordered ZnO nanorod photocatalyst. J Environ Sci 25:2487–2491
Dutta SK, Mehetor SK, Pradhan N (2015) Metal semiconductor heterostructures for photocatalytic conversion of light energy. J Phys Chem Lett 6:936–944
Hara M, Kondo T, Komoda M, Ikeda S, Kondo J, Domen K, Hara M, Shinohara K, Tanaka A (1998) Cu2O as a photocatalyst for overall water splitting under visible light irradiation. Chem Commun 3:357–358
Paracchino A, Laporte V, Sivula K, Grätzel M, Thimsen E (2011) Highly active oxide photocathode for photoelectrochemical water reduction. Nat Mater 10:456–461
Li C, Li Y, Delaunay J (2013) A novel method to synthesize highly photoactive Cu2O microcrystalline films for use in photoelectrochemical cells. ACS Appl Mater Interfaces 6:480–486
Tilley S, Schreier M, Azevedo J, Stefik M, Graetzel M (2014) Ruthenium oxide hydrogen evolution catalysis on composite cuprous oxide water-splitting photocathodes. Adv Funct Mater 24:303–311
Li C, Hisatomi T, Watanabe O, Nakabayashi M, Shibata N, Domen K, Delaunay J (2015) Positive onset potential and stability of Cu2O-based photocathodes in water splitting by atomic layer deposition of a Ga2O3 buffer layer. Energy Environ Sci 8:1493–1500
Li C, Hisatomi T, Watanabe O, Nakabayashi M, Shibata N, Domen K, Delaunay J (2016) Simultaneous enhancement of photovoltage and charge transfer in Cu2O-based photocathode using buffer and protective layers. Appl Phys Lett 109:033902
Fan W, Yu X, Lu H, Bai H, Zhang C, Shi W (2016) Fabrication of TiO2/RGO/Cu2O heterostructure for photoelectrochemical hydrogen production. Appl Catal Environ 181:7–15
Fu K, Huang J, Yao N, Xu X, Wei M (2016) Enhanced photocatalytic activity based on composite structure with down-conversion material and graphene. Ind Eng Chem Res 55:1559–1565
Li X, Yu J, Jaroniec M (2016) Hierarchical photocatalysts. Chem Soc Rev 45:2603–2636
Li J, Wu N (2015) Semiconductor-based photocatalysts and photoelectrochemical cells for solar fuel generation: a review. Catal Sci Technol 5:1360–1384
Li X, Yu J, Wageh S, Al-Ghamdi AA, Xie J (2016) Graphene in photocatalysis: a review. Small 12:6640–6696
Ge M, Li S, Huang J, Zhang K, Al-Deyab SS, Lai Y (2015) TiO2 nanotube arrays loaded with reduced graphene oxide films: facile hybridization and promising photocatalytic application. J Mater Chem A 3:3491–3499
Li Q, Li X, Wageh S, Al-Ghamdi AA, Yu J (2015) CdS/graphene nanocomposite photocatalysts. Adv Energy Mater 5:1500010
Bhosale RR, Pujari SR, Muley GG, Patil SH, Patil KR, Shaikh MF, Gambhire AB (2014) Solar photocatalytic degradation of methylene blue using doped TiO2 nanoparticles. Sol Energy 103:473–479
Alsawat M, Altalhi T, Gulati K, Santos A, Losic D (2015) Synthesis of carbon nanotube–nanotubular titania composites by catalyst-free CVD Process: insights into the formation mechanism and photocatalytic properties. ACS Appl Mater Interfaces 7:28361–28368
Acknowledgements
This work was supported by the Natural Science Foundation of Shandong Provience (Grant Nos. ZR2016FM30, ZR2016JL015), the Science-Technology Program of Higher Education Institutions of Shandong Province (Grant No. J14LA01), the Graduate Innovation Foundation of University of Jinan, GIFUJN, (Grant No. YCXS15006), the Open Project Program of Key Laboratory for Photonic and Electric Bandgap Materials, Ministry of Education, Harbin Normal University (Grant No. PEBM201505), and National Natural Science Foundation of China (Grant Nos. 51672109, 61504048, 21505050).
Authors’ contributions
Y.N.N. and H.J.Z. designed the experiments. Y.N.N. and F.K. performed the experiments. D.X.L. performed the SEM observations. Y.N.N., H.J.Z., D.X.L., and W.M.Z. discussed and commented on the experiments and results and wrote the paper. All authors read and approved the final manuscript.
Competing interests
The authors declare that have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Huang, J., Fu, K., Deng, X. et al. Fabrication of TiO2 Nanosheet Aarrays/Graphene/Cu2O Composite Structure for Enhanced Photocatalytic Activities. Nanoscale Res Lett 12, 310 (2017). https://doi.org/10.1186/s11671-017-2088-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-017-2088-7