Abstract
Utilizing first-principles theory, we demonstrate that half-metallicity can be realized in a junction composed of non-magnetic armchair graphene nanoribbon (AGNR) and ferromagnetic Ni electrodes. The half-metallic property originates from the AGNR energy gap of the up spin located at the Fermi energy, while large electronic states are generated for the down spin. By altering the interlayer distance and the contact area, namely, the strength of AGNR-Ni interaction, the efficiency of the spin filter becomes lower, since the energy gap moves away from the Fermi energy with the variation of charge transfer intensity.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Spintronic nanodevices, which are nanoscale devices utilizing spin degrees of freedom of electrons, have attracted a significant amount of attention. One of the significant functions of spintronics is the spin filter effect. High spin filter efficiency is expected to be realized in half-metallic materials with one metallic spin component and the other semiconducting or insulating spin channel. Up to now, half-metallic property has been found not only in some ferromagnetic metals, such as manganese perovskites [1] and Heusler compounds [2], but also in some metal-free materials, for example, carbon nanomaterials [3, 4] and graphitic carbon nitride [5]. Exploring half-metallic materials is of great interest in future spintronic devices, but it still remains a challenge due to the requirement of unique spin-asymmetric electronic states.
Carbon-based nanomaterials, such as graphene, are expected to be promising materials for the realization of spintronics due to the weak spin-orbit coupling and long spin scattering length [6]. The carbon atoms on two sublattices are spin-polarized as two-dimensional (2D) graphene contacts with ferromagnetic metal (FM) [7–9]. Spin-polarized transport behaviors were predicted theoretically in a 2D graphene-FM interface, for both in-plane [10–13] and out-of-plane electron transport [14, 15]. On the other hand, FM-graphene-FM-based spin valve devices were also fabricated experimentally to measure the spin-polarized transport in the direction perpendicular to the graphene plane [16–19]. More recently, both theoretical [20] and experimental studies [21] have found efficient spin injection for the FM-graphene system with the insertion of h-BN layers, though the spin-polarized current is greatly reduced due to the high tunneling barrier of h-BN [20]. However, 2D graphene has conical points located at the Fermi energy (E F) with zero density of states; the gapless property limits its application in half-metallic materials.
It is well known that the energy gap can be engineered by cutting a 2D graphene sheet into a one-dimensional (1D) graphene nanoribbon (GNR), where the edge carbon atoms are passivated by hydrogen. Recently, this nanometer-wide GNR with atomically precise width can be achieved via a surface-assisted bottom-up fabrication [22, 23]. Owing to the quantum confinement, electronic states of GNR are mainly governed by the boundary conditions [24, 25]. Consequently, the function of such a graphene nanoribbon-based device is strongly dependent on the edge structures.
One typical structure of the nanoribbon is the zigzag edge, referred to as a zigzag graphene nanoribbon (ZGNR), which shows flat-band magnetism induced by peculiar localized electronic states at each edge. Recently, the first-principles calculations predicted that anti-ferromagnetic ZGNR shows half-metallicity at a finite external electric field across the ribbon [3, 4]. Motivated by this approach, some alternative methods are also proposed to drive ZGNRs into the half-metallic state, such as edge modification by organic molecules [26], doping B/N atoms [27, 28], and adsorption ferroelectric polymer [29], acceptor/donor functional groups [30], or symmetric- and asymmetric-edge hydrogenations [31]. All these studies indicate that ZGNRs hold promising applications in the spintronic nanodevice.
The other signature shape is the armchair edge, termed as an armchair graphene nanoribbon (AGNR). Although AGNR has a band gap at the Fermi energy depending on the ribbon width, the electronic structure of AGNR is not spin-polarized [32]. Therefore, it is hard to fabricate spintronic devices based on the free-standing AGNR without other modification to control the spin of electrons. On the other hand, when AGNR is adsorbed on metals, such as Au, Cu, and so on, the electronic structure is modified by the interfacial coupling between the metal surface and graphene [23, 33]. Especially contacting with ferromagnetic metal onto the AGNR layer seems to be a feasible way of introducing spin polarization of the AGNR. However, the possibility of the AGNR system as spintronics has not been fully investigated.
In this paper, we demonstrated that the half-metallic property can be realized in the non-magnetic AGNR via contact with Ni substrates (Ni/AGNR/Ni junction). The electron transport property of a two-probe junction, where AGNR is adsorbed on Ni(111) surfaces with an on-top configuration as shown in Fig. 1, was investigated by using first-principles theory. We found that half-metallicity in the Ni/AGNR/Ni junction depends on the interfacial coupling strength, such as interlayer distance and contact area.
Methods
Figure 1 illustrates the studied model of a Ni/AGNR/Ni junction, constructed from three layers of Ni atoms with AGNR adsorbed on the surface. The unit cell used to model the junction is shown by the dotted rectangle in Fig. 1a. In the contact region, one carbon atom locates above a surface Ni atom and the other carbon is above a third-layer Ni atom. The contact area contains three repeating units at each side of the AGNR, and the junction is labeled as M3. The geometric structure of the contact region was firstly optimized with a 1 × 1 unit cell of graphene on three layers of Ni (111) surface (red diamond in Fig. 1a) using the density functional theory (DFT) code PHASE [34]. We used the PW91 functional parametrized by Perdew and Wang for the exchange-correlation term [35] and the Troullier-Martins-type atomic pseudopotentials [36, 37]. A plane-wave basis set with cutoff energy of 25 Ry was employed. A k-mesh of 20 × 20 × 1 was adopted to sample the Brillouin zone (BZ) for structural relaxations. During structural relaxation, the atoms are relaxed until the total energy change is less than 10−9 hartree and the force on each atom is smaller than 10−3 hartree/bohr.
In this structure optimization, we fixed the lattice constant of graphene to be the optimized value, a = 2.458 Å, adopting the same value for lattice constant of the Ni electrodes [38, 39]. With this orientation, the lattice mismatch between graphene and Ni(111) surfaces is about 1.3 %. Both C atoms and Ni atoms (except the Ni atoms in bottom layer) were relaxed to release the strain induced by lattice mismatch. The interlayer distance between the graphene and the Ni(111) surface is optimized to be 1.995 Å, as noted by d eq in Fig. 1(b). This predicted distance of Ni-graphene is close to the experimental value (2.11 ± 0.07 Å) [40], previous LDA reports (2.05 Å) [7, 41] and the DFT calculation with van der Waals (vdW) correction (2.07 Å) [42], in which vdW density functional together with the C09 exchange functional was used.
The spintronic transport calculations were carried out by using the ASCOT code [43, 44] with a non-equilibrium Green’s function (NEGF) method [45] based on the DFT. In the present calculation, the magnetic moments of both ferromagnetic electrodes were aligned parallel to each other. Electron transport occurs in the z direction, and periodic boundary conditions are imposed in the transverse transport direction (x direction). The vacuum region in the y direction is ~10 Å to ensure decoupling between neighboring slabs. We employed the same functional and atomic pseudopotentials as the structure optimization procedure. For a basis set, we employed pseudoatomic orbitals [46], whose cutoff radius and number of primitive orbitals are summarized in Table 1. The energy cutoff for the real space mesh is 100 Ry for the transport calculation. For the self-consistent calculation of the two-probe open system, a k-point mesh of 19 × 1 × 1 was employed along the x, y, and z directions. The NEGF-DFT self-consistency is achieved when the energy difference is less than 10−6 hartree between the iteration steps. For the calculation of the current and the spin-decomposed transmission spectra, that is defined as
We used k-point N k = 201 in the periodic x direction, and 1 in the y and z directions. The energy cutoff and k-point convergences were performed for all calculations.
Results and Discussion
To show the spintronic transport properties of Ni-contacted AGNR, Fig. 2a, b display the spin filter characteristics of the M3 and the spin-decomposed current-voltage curves, respectively. The spin injection factor η is defined as η = (I ↑ − I ↓)/(I ↑ + I ↓), where I σ is the current of each spin σ(=↑,↓). In the bias voltage range V < 0.3 V, the absolute value of η is more than 0.77. Remarkably, a high spin-filtering effect, η of −0.98, is observed at a low bias voltage. This indicates that the current flow in the Ni-contacted AGNR is highly spin-polarized and, as shown in Fig. 2b, the total current is dominated by down spin due to the rather low I ↑, showing a metallic behavior for the down spin while a nearly insulating behavior for the up spin. Notably, the nearly 100 % spin-filtering efficiency is obtained in the junction composed of AGNR without intrinsic magnetism, suggesting that half-metallicity can be realized in a non-magnetic molecule via contact with ferromagnetic metal electrodes.
In order to clarify the origin of the half-metallic property, we show the spin-dependent transmission spectra of the M3 junction in Fig. 3a. At E F, it is found that for up spin, there is a zero-transmission gap with a width of ~0.2 eV, while for down spin, a high transmission coefficient of 0.16 is observed and the zero-transmission gap locates at ~0.4 eV. From the local density of states (LDOS) of AGNR in the Brillouin zone (BZ) and the band structure of an isolated AGNR as shown in Fig. 3b, it can be clearly seen that AGNR states are spin-polarized due to the interaction with Ni substrates. In the middle k-region of the BZ, high states exist in the LDOS, which are induced by strong hybridization between Ni d-states and graphene π-orbitals [38, 39]. At E F, in particular, these generated states are more obvious for down spin, since Ni d-states of the down spin locate in a higher energy region than that of the up spin. This is the reason for the higher transmission observed for the down spin. In addition, by comparing transmission spectra and LDOS, we find that the transmission gap arises from the band gap of the isolated AGNR. The location of the gap closely relates to the interfacial charge transfer intensity, which depends on the strength of the Ni-AGNR interaction, as reported for the Ni-AGNR system in the previous work [39]. In the M3 system, electrons of 1.43 e transfer from AGNR to Ni substrates and the predicted charge transfer direction is in agreement with the experimental result [47]. These features are schematically described in Fig. 3c. In this way, around E F, the transmission of up spin becomes almost zero due to the AGNR gap located at E F, while a higher transmission of down spin is observed because of strong hybridization.
As mentioned above, to realize this half-metallicity, it is necessary to drive the gap of the up spin to reside at E F. The gap location is determined by the strength of interfacial interaction which directly correlates with, for example, the interlayer distance between AGNR and the metal surface and the contact area, because the interaction strength can alter the amount of charge transfer which relates to the gap location. This indicates that the efficiency of the spin filter might be strongly dependent on the interaction strength.
In order to confirm these effects, first, we explore the spin-filtering effect of the M3 junction with different distances varying from 0.90d eq to 1.10d eq, where d eq is the equilibrium distance between AGNR and the Ni surface (1.955 Å). Figure 4a, b displays the η values and the transmission coefficient at E F [T σ(E F)] of all contact structures at zero bias, respectively, where η at zero bias is defined as η = [T ↑(E F) − T ↓(E F)]/[T ↑(E F) + T ↓(E F)]. The spin injection factor of M3 retains −0.98 as the distance is shortened to 0.95d eq, and then η drops down for a much smaller spacing of 0.90d eq. For a larger distance, η is reduced as the distance extends to 1.10d eq. This variation of η is mainly attributed to the increase of the up-spin transmission coefficient at E F for a shorter or larger distance. As shown in Fig. 4b, T ↑(E F) increases from 0.002 (1.00d eq) to 0.035 (0.90d eq) or 0.034 (1.10d eq). The evolution of η and the transmission coefficient can be understood from the location of the AGNR band gap in energy.
To gain insight into the gap location, we show the k-dependent LDOS and band structure of an isolated AGNR in Fig. 5a. As the distance becomes shorter than the equilibrium distance, the gap shifts to the upper energy side, from 0 eV (0.4 eV) of 1.00d eq to 0.25 eV (0.55 eV) of 0.90d eq for the up (down) spin as noted by the arrows. In contrast, weaker interaction for a longer distance causes an opposite shift of the band gap, and the gap approaches −0.2 eV (0.3 eV) of 1.10d eq for the up (down) spin. Figure 5b schematically describes the gap shift, which relates to the variation of interfacial charge transfer intensity, indicating that a stronger interaction leads to a larger amount of charge transfer from AGNR to Ni electrodes. With increase or decrease of the spacing distance, the gap of the up spin gradually moves away from E F, raising the up-spin transmission value at E F, and as a result, the efficiency of the spin filter is reduced.
Next, we study the spin-filtering effect of Ni/AGNR/Ni junctions with different contact areas. The contact area varies from no overlap (M0) to four repeating units of overlap at each side (M4). Figure 6a displays the η values of all contact structures. It is clearly seen that M3 exhibits the largest η value of −0.98 and the absolute value of η becomes smaller with reducing contact area, and then we obtain η of nearly zero for the M0 system. This contact area dependence arises from the following properties of T σ(E F) as shown in Fig. 6b. As the contact area decreases, T ↓(E F) monotonically decreases from 0.16 for M3 to 0.044 for M0. In contrast, T ↑(E F) shows an opposite trend which is slightly enhanced and a minimum value (0.002) is found for the up spin of the M3 system. For M0, the spin dependence is so weak that T σ(E F) is similar for two spin states.
Figure 7a shows the LDOS and band structure of the isolated AGNR in M3, M1, and M0 systems. With varying of the contact area from M3 to M0, the AGNR gap located at E F for up spin shifts to the lower energy side with the reduction of charge transfer intensity. This downward shift of the AGNR gap gives rise to a slight increase of the up-spin transmission at E F, whereas weaker interaction reduces the electronic states of the down spin and induces a lower transmission at E F. The effects of the gap shift and state reduction, which are observed above, are schematically depicted in Fig. 7b. On the other hand, the spin-filtering effect of a case of more overlap, that is, M4, is weaker than that of M3. This is because the stronger interfacial interaction of M4 enhances the transmission of up spin, while the gap location in energy is almost same as M3. The above results suggest that the spin-filtering effect depends strongly on the size of the contact region, which can also change the AGNR gap location, same as the origin of the distance-dependent η. As a consequence, we can confirm that the efficiency of the spin filter is strongly dependent on the strength of the AGNR-Ni interaction. To achieve a high efficiency, a moderate interaction strength which makes the AGNR gap locate at E F for only one spin is required.
At last, it is emphasized that the present system utilizes the non-magnetic carbon nanomaterial in contact with magnetic substrates, distinct from previously predicted half-metals with intrinsic magnetism, such as manganese perovskites [1], Heusler compounds [2], and recently discovered metal-free half-metals (for example, graphitic carbon nitride) [5]. These results may bring us the possibility of fabricating spintronic nanodevices based on non-magnetic 1D graphene nanoribbon by interfacial manipulation.
Conclusions
In summary, we observe the half-metallic property in an armchair graphene nanoribbon in contact with Ni electrodes. The junction exhibits a spin injection value of −0.98, indicating a nearly insulating behavior for up spin and a metallic behavior for down spin. This spin-filtering effect originates from the following mechanisms: Owing to the interaction between AGNR and Ni states, the AGNR energy gap of up spin is located at E F, suppressing the up-spin transmission, while a large transmission of down spin is observed at E F. The efficiency of the spin filter varies with the AGNR gap location, which correlates with the charge transfer intensity determined by the interaction strength between graphene and the Ni surface, that is, the interlayer distance and contact area. This device design suggests a potential application of AGNR-based materials in spintronic nanodevices.
References
Park JH, Vescovo E, Kim HJ, Kwon C, Ramesh R, Venkatesan T (1998) Direct evidence for a half-metallic ferromagnet. Nature 392:794–796
De Groot RA, Mueller FM, Van Engen PG, Buschow KHJ (1983) New class of materials: half-metallic ferromagnets. Phys Rev Lett 50:2024–2027
Son YW, Cohen ML, Louie SG (2006) Half-metallic graphene nanoribbons. Nature 444:347–349
Kan EJ, Li Z, Yang J, Hou JG (2007) Will zigzag graphene nanoribbon turn to half metal under electric field. Appl Phys Lett 91:243116
Du A, Sanvito S, Smith SC (2012) First-principles prediction of metal-free magnetism and intrinsic half-metallicity in graphitic carbon nitride. Phys Rev Lett 108:197207
Novoselov KS, Geim AK, Morozov SV, Jiang D, Zhang Y, Dubonos SV, Grigorieva IV, Firsov AA (2004) Electric field effect in atomically thin carbon films. Science 306:666–669
Khomyakov PA, Giovannetti G, Rusu PC, Brocks G, van den Brink J, Kelly PJ (2009) First-principles study of the interaction and charge transfer between graphene and metals. Phys Rev B 79:195425
Abtew T, Shih B-C, Banerjeeb S, Zhang P (2013) Graphene–ferromagnet interfaces: hybridization, magnetization and charge transfer. Nanoscale 5:1902–1909
Matsumoto Y, Entani S, Koide A, Ohtomo M, Avramov PV, Naramoto H, Amemiya K, Fujikawa T, Sakai S (2013) Spin orientation transition across the single-layer graphene/nickel thin film interface. J Mater Chem C 1:5533–5537
Maassen J, Ji W, Guo H (2011) Graphene spintronics: the role of ferromagnetic electrodes. Nano Lett 11:151–155
Cho Y, Choi YC, Kim KS (2011) Graphene spin-valve device grown epitaxially on the Ni(111) substrate: a first principles study. J Phys Chem C 115:6019–6023
Zhou J, Wang L, Qin R, Zheng J, Mei WN, Dowben PA, Nagase S, Gao Z, Lu J (2011) Structure and electronic and transport properties of transition metal intercalated graphene and graphene-hexagonal-noron-nitride bilayer. J Phys Chem C 115:25273–25280
Kaneko T, Ohno T (2014) Effect of surface oxidation on transport properties in graphene-metal junctions. Jpn J Appl Phys 53:05FD07
Karpan VM, Giovannetti G, Khomyakov PA, Talanana M, Starikov AA, Zwierzycki M, van den Brink J, Brocks G, Kelly PJ (2007) Graphite and graphene as perfect spin filters. Phys Rev Lett 99:176602
Sato R, Hiraiwa T, Inoue J, Honda S, Itoh H (2012) Magnetoresistance in fcc Ni/graphene/fcc Ni(111) junctions. Phys Rev B 85:094420
Cobas E, Friedman AL, van’t Erve OMJ, Robinson JT, Jonker BT (2012) Graphene as a tunnel barrier: graphene-based magnetic tunnel junctions. Nano Lett 12:3000–3004
Iqbal MZ, Iqbal MW, Lee JH, Kim YS, Chun S-H, Eom J (2013) Spin valve effect of NiFe/graphene/NiFe junctions. Nano Res 6:373–380
Singh AK, Eom J (2014) Negative magnetoresistance in a vertical single-layer graphene spin valve at room temperature. Acs Appl Mater Inter 6:2493–2496
Park JH, Lee HJ (2014) Out-of-plane magnetoresistance in ferromagnet/graphene/ferromagnet spin-valve junctions. Phys Rev B 89:165417
Wu Q, Shen L, Bai Z, Zeng M, Yang M, Huang Z, Feng YP (2014) Efficient spin injection into graphene through a tunnel barrier: overcoming the spin-conductance mismatch. Phys Rev Appl 2:044008
Kamalakar MV, Dankert A, Kelly PJ, Dash SP (2016) Inversion of spin signal and spin filtering in ferromagnet | hexagonal boron nitride-graphene van der Waals heterostructures. Sci Rep 6:21168
Cai JM, Ruffieux P, Jaafar R, Bieri M, Braun T, Blankenburg S, Muoth M, Seitsonen AP, Saleh M, Feng XL, Mullen K, Fasel R (2010) Atomically precise bottom-up fabrication of graphene nanoribbons. Nature 466:470–473
Ruffieux P, Cai JM, Plumb NC, Patthey L, Prezzi D, Ferretti A, Molinari E, Feng XL, Mullen K, Pignedoli CA, Fasel R (2012) Electronic structure of atomically precise graphene nanoribbons. ACS Nano 6:6930–6935
Han MY, Özyilmaz B, Zhang Y, Kim P (2007) Energy band-gap engineering of graphene nanoribbons. Phys Rev Lett 98:206805
Carvalho AR, Warnes JH, Lewenkopf CH (2014) Edge magnetization and local density of states in chiral graphene nanoribbons. Phys Rev B 89:245444
Kan EJ, Li ZY, Yang JL, Hou JG (2008) Half-metallicity in edge-modified zigzag graphene nanoribbons. J Am Chem Soc 130:4224–4225
Kan E-J, Wu X, Li Z, Zeng XC, Yang J, Hou JG (2008) Half-metallicity in hybrid BCN nanoribbons. J Chem Phys 129:084712
Li Y, Zhou Z, Shen P, Chen Z (2009) Spin gapless semiconductor-metal-half-metal properties in nitrogen-doped zigzag graphene nanoribbons. ACS Nano 3:1952–1958
Lee YL, Kim S, Park C, Ihm J, Son YW (2010) Controlling half-metallicity of graphene nanoribbons by using a ferroelectric polymer. ACS Nano 4:1345–1350
Guan J, Chen W, Li Y, Yu G, Shi Z, Huang X, Sun C, Chen Z (2013) An effective approach to achieve a spin gapless semiconductor–half-metal–metal transition in zigzag graphene nanoribbons: attaching a floating induced dipole field via π-π interactions. Adv Funct Mater 23:1507–1518
Deng XQ, Zhang ZH, Tang GP, Fan ZQ, Yang CH (2014) Spin filter effects in zigzag-edge graphene nanoribbons with symmetric and asymmetric edge hydrogenations. Carbon 66:646–653
Son YW, Cohen ML, Louie SG (2006) Energy gaps in graphene nanoribbons. Phys Rev Lett 97:216803
Liang L, Meunier V (2012) Electronic structure of assembled graphene nanoribbons: substrate and many-body effects. Phys Rev B 86:195404
Ohno T, Yamamoto T, Kokubo T, Azami A, Sakaguchi Y, Uda T, Yamasaki T, Fukata D, Koga J (2007) Proceedings of the 2007 ACM/IEEE conference on supercomputing, 10–16 November 2007. IEEE, Reno, pp 1–6. PHASE is a program package for first-principles total energy calculations based on the density functional theory and the ultrasoft pseudopotential scheme, developed within the RISS project supported by MEXT of the Japanese government. For details, see the website: http://www.ciss.iis.u-tokyo.ac.jp/english/dl/
Perdew JP, Wang Y (1992) Accurate and simple analytic representation of the electron-gas correlation energy. Phys Rev B 45:13244–13249
Troullier N, Martins JL (1991) Efficient pseudopotentials for plane-wave calculations. Phys Rev B 43:1993–2006
Kleinman L, Bylander DM (1982) Efficacious form for model pseudopotentials. Phys Rev Lett 48:1425–1428
Liu H, Kondo H, Ohno T (2012) Contact effects of nickel and copper on electron transport through graphene. Phys Rev B 86:155434
Liu H, Kondo H, Ohno T (2013) Effect of contact area on electron transport through graphene-metal interface. J Chem Phys 139:074703
Gamo Y, Nagashima A, Wakabayashi M, Terai M, Oshima C (1997) Atomic structure of monolayer graphite formed on Ni(111). Surf Sci 374:61–64
Giovannetti G, Khomyakov PA, Brocks G, Karpan VM, van den Brink J, Kelly PJ (2008) Doping graphene with metal contacts. Phys Rev Lett 101:026803
Hamada I, Otani M (2010) Comparative van der Waals density-functional study of graphene on metal surfaces. Phys Rev B 82:153412
Kondo H, Nara J, Kin H, Ohno T (2008) End-group dependence of transport properties for biphenyl-based molecular junction system. Jpn J Appl Phys 47:4792–4798
The transport properties are calculated by using ASCOT code. For the detail of this code, see Ref. 43
Datta S (1995) Electronic transport in mesoscopic systems. Cambridge University Press, Cambridge
Ozaki T (2003) Variationally optimized atomic orbitals for large-scale electronic structures. Phys Rev B 67:155108
Schultz BJ, Jaye C, Lysaght PS, Fischer DA, Prendergast D, Banerjee S (2013) On chemical bonding and electronic structure of graphene-metal contacts. Chem Sci 4:494–502
Acknowledgements
This work was supported by the RISS Project of the IT program of MEXT and the grant for “Strategic Programs for Innovative Research” from MEXT of the Japanese Government. H. Liu acknowledges the support of the National Natural Science Foundation of China (Nos. 11204120, 11274151, 51431004). We thank the Numerical Materials Simulator in NIMS for providing the computing resources.
Authors’ Contributions
HML carried out the first-principles calculations, analyzed the data, and wrote the manuscript. HK participated in the data analysis and manuscript preparation. TO conceived the idea and supervised the project. All authors discussed, read, and approved the final manuscript.
Competing Interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Liu, H., Kondo, H. & Ohno, T. Spintronic Transport in Armchair Graphene Nanoribbon with Ferromagnetic Electrodes: Half-Metallic Properties. Nanoscale Res Lett 11, 456 (2016). https://doi.org/10.1186/s11671-016-1673-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1673-5