Abstract
A facile method termed magneto-mechanical drawing is used to produce polymer composite microfibers. Compared with electrospinning and other fiber spinning methods, magneto-mechanical drawing uses magnetic force generated by a permanent magnet to draw droplets of polymer/magnetic nanoparticle suspensions, leading to fabrication of composite microfibers. In addition, because of the rotating collector, it is easy to control the fiber assembly such as fibrous array in parallel or crossed fibrous structure. The general applicability of this method has also been proved by spinning different polymers and magnetic nanoparticles. The resultant fibers exhibit good superparamagnetic behavior at room temperature and ultrahigh stretchability (~443.8 %). The results indicate that magneto-mechanical drawing is a promising technique to fabricate magnetic and stretchable microfibers and devices.
Background
Micro-/nanofibers have exhibited a lot of outstanding performance due to a very high specific surface-to-mass ratio and attracted much attention of various applications in the past two decades, such as filtration [1–3], biomedical science [4, 5], high-performance textile [6, 7], and catalysis [8]. By now, different methods have been developed to generate micro-/nanofibers, such as melt-blowing [9, 10], electrospinning [11–13], and jet spinning [14, 15]. Melt-blowing is capable of producing high yield microfibers with an average diameter within several microns. Electrospinning is one of the most versatile and efficient methods and has been explored extensively recently in the laboratory and applied to industry [16]. The electrospinning process can be simply summarized as the high voltage applies to the polymer solution, causing the solution electrification and leading to the fabrication of fibers. The fibers were stretched in the air with the solvent evaporated and finally collected on the collection device in the form of non-woven [17]. Each of these methods has their advantages; however, each of them has some deficiencies. For instance, the distribution of melt-blown fiber diameters is uneven [10]. The electric force generated by high voltage is needed to the formation of Taylor cone in electrospinning. The high voltage ranging from several kilovolts to tens of kilovolts may bring potential danger if improperly operated [18].
For the aim of increasing production, optimizing spinning process, and getting better micro-/nanofibers, the magnetic field has already been introduced into the spinning. For example, Wu et al. controlled stability of the electrospun fiber by applying a magnetic field in the electrospinning process [19]. Yang et al. also obtained aligned fibrous arrays and multilayer grids by appending the magnetic field generated by two parallel-positioned permanent magnets above the collection device [20]. Similar to Yang et al., Liu et al. introduced two bar magnets to the conventional configuration at the collector region, and electrospinning of aligned straight and wave polymeric nanofibers was achievable [21]. In these approaches, the magnetic field affects the movements of charged jet to get fibers with different arrangements and to control instability in electrospinning. However, the high voltage was still applied while the magnetic field just played an auxiliary role.
In this study, we use a facile method termed magneto-mechanical drawing to prepare microfibers. In this method, we regard the magnetic field as the main part of the spinning. Spinning solution droplet doped with magnetic nanoparticles was stretched under the magnetic force generated by a revolving permanent magnet to form a bridge and finally translated into continuous fibers. Magneto-mechanical drawing possesses lots of advantages compared with other common spinning methods. The equipment of magneto-mechanical drawing is low cost, safe, simple, and convenient without high voltage or high temperature. The resultant continuous fibers are aligned in regular order and can be easily transferred onto other substrates, like glass, silicon wafer, and plastic sheet. The resultant fibers that contain magnetic nanoparticles show excellent superparamagnetic behavior and ultrahigh stretchability and may have potential application in magnetic sensor or targeted drug delivery.
Methods
Materials
Poly(vinylidene fluoride) (PVDF; M w ~ 550,000) and polymethyl methacrylate (PMMA; M w ~ 350,000) were purchased from Aladdin and Sigma-Aldrich, respectively. Solvents we used include N, N-dimethylformamide (DMF; HCON(CH3)2) and acetone (CH3COCH3). Three kinds of magnetic nanoparticles (γ-Fe2O3, Fe3O4, and NiO) with average diameters of 20 nm were supplied by Aladdin.
Preparation of Magneto-Mechanical Drawing Solution
The viscosity of solution and existence of magnetic nanoparticles are the decisive factors for the success of spinning. In this study, different concentrations of polymer and nanoparticles were studied to obtain suitable spinning solutions. It is found that the solution containing 20–25 wt.% PVDF and 2.0 ± 0.5 wt.% magnetic nanoparticles was a suitable proportion. When the concentration of magnetic nanoparticles was less than 2.0 ± 0.5 wt.%, magnetic force is not strong enough to attract the spinning droplet under higher rotating speed. On the other hand, fiber diameter will become larger when the concentration of magnetic nanoparticles was more than 2.0 ± 0.5 wt.%. Table 1 shows different concentrations of PVDF solutions, their viscosities, and the spinning results. In order to prepare the magneto-mechanical drawing solution with PVDF concentration of 22 wt.%, 2.2 g PVDF was dissolved into 7.8 g mixed solution of DMF and acetone (50/50, w/w) with magnetic stirring at 40 °C for 2.5 h to form the precursor solution. Then 0.2 g γ-Fe2O3 nanoparticles were added into the prepared solution. After 10-min vibration under ultrasonic accompanied by mechanical stirring, the final solution was stirred for another 10 min to ensure a better dispersion of γ-Fe2O3 nanoparticles in the solution. The Erlenmeyer flask, as the reaction vessel, was enclosed by sealing film because of the volatility of acetone. Meanwhile, γ-Fe2O3 can be replaced by other magnetic nanoparticles. Additional file 1: Figure S1 shows the viscosity versus shear rate curves for different PVDF/magnetic nanoparticle solutions.
Magneto-Mechanical Drawing Set-up
Magneto-mechanical drawing set-up requires no high voltage or other harsh terms, it is simpler, easier to assemble, and safer compared with common spinning methods like electrospinning, melt-blowing. It mainly consists of three parts, including feeding device (a syringe pump (Longer Pump LSPO1-1A) and a syringe for solution), collection device (a stage (r = 4.5 cm) on which equipped with a permanent magnet (1 cm × 1 cm × 2.2 cm) and several pillars (h = 2.5 cm)) and a rotary motor. The rotary motor is connected to the stage and used to control the rotating speed of the stage. The magnet and pillars are vertically glued onto the stage. The pinhead is placed perpendicular to the direction of the pillar. The distance between them can adjust to several millimeters.
Magneto-Mechanical Drawing Process
Generally speaking, magneto-mechanical drawing uses the magnetic force generated by a revolving permanent magnet to draw droplets of polymer suspensions with magnetic particles, leading to fabrication of microfibers. In a typical procedure, magneto-mechanical drawing solution is pushed out of the needle by the syringe pump, forming droplet at the pinpoint because of the surface tension (Fig. 1a). The stage with magnet starts to rotate at the same time. The magnet attracts droplet to form a bridge when it approaches to the needle tip (Fig. 1b, c). As the stage keeps rotating, the bridge stretches rapidly, forming the fiber (Fig. 1d). Fiber diameter decreases with its elongation. And fiber is drawn continually with the solvent evaporated. Once the fiber breaks, the droplet could be attracted to the magnet again. This process ensures the continuity of spinning. As shown in Fig. 2a, b, fibers are twining around the pillars and magnet to form a fibrous array in parallel. Besides parallel fibers, fibers with vertical cross structure can also be prepared by changing a removable box frame-collector.
Characterization
The resultant composite fibers were characterized by a scanning electron microscope (SEM; JEOL, JSM-7500F), a transmission electron microscope (TEM; JEOL, JEM-2100F), and a Fourier transform infrared (FTIR) spectrometer (Thermo Scientific Nicolet iN10). The average diameter of the fibers was measured by using a SEM image analysis software (Smile View). The viscosities of different spinning solutions were measured by a rheometer (Physica MCR 301). The magnetic properties of the fibers were measured using a vibrating sample magnetometer (VSM) of physical properties measurement system (PPMS) of quantum design) by sweeping the external field from −25,000 to 25,000 Oe at 300 K. The stress-strain characteristic curve of fiber bundle (fiber number ~100, average fiber bundle diameter ~10 μm) was obtained by a dynamic mechanical analyzer (Q-800, TA Scientific).
Results and Discussions
Morphology and Structure of PVDF/γ-Fe2O3 Fibers
Figure 3a shows the SEM image of the PVDF/γ-Fe2O3 fibers. The average diameter of the fibers was confirmed as 8.4 μm. PVDF/γ-Fe2O3 fibers are drawn with solvent evaporated rapidly, so all fibers exhibited rough surfaces. More details about the inner structure of the fiber are shown in the TEM image (Fig. 3b). It is apparent that most γ-Fe2O3 nanoparticles are agglomerating because it is difficult to disperse the nanoparticles uniformly in the spinning solution with high viscosity. The average diameter of the dispersed nanoparticles is about 20 nm.
Infrared Spectroscopy of PVDF Powder and PVDF/γ-Fe2O3 Fibers
PVDF is a semi-crystalline polymer and its structure is long molecule chain, which consists of repeated unit CH2CF2 [22]. Infrared spectroscopy was applied to characterize the structure of the PVDF powder and the resulting PVDF/γ-Fe2O3 fibers. Fig. 4 shows the FTIR spectra of the composite fibers and PVDF powder. The bands appearing at 3020 and 1401 cm−1 are assigned to C–H stretching and C–H deformation, respectively [23]. Band at 1180 cm−1 is assigned to C–F stretching [24]. Moreover, absorption bands at 1072, 878, and 840 cm−1 are indications of β-crystal of PVDF [25–27]. The wavenumbers of the FTIR peaks and their assignments of different groups and crystallites are exhibited in Table 2. Here, it is noted that the characteristic peaks of γ-Fe2O3 did not appear in the infrared spectra of the PVDF/γ-Fe2O3 fibers. So, the FTIR spectra of the composite fibers are quite similar to the PVDF powder.
The Relation Between Rotating Speed and Fiber Diameter
In this method, fiber diameter can be changed by adjusting the rotating speed of the collecting stage. The relationship between rotating speed and fiber diameter was also studied. The distance between magnet and the tip of needle was insured as 7 mm. The rotating speed was set at 65, 115, 165, and 215 rpm (revolutions per minute), respectively. Fibers produced under different rotating speed are shown in Fig. 5. It can be seen obviously that fiber tapers with the increasing rotating speed. But when the rotating speed is beyond 215 rpm, fiber breakage frequency will increase during magneto-mechanical drawing process. When the rotating speed is too quick, the droplet transition from the needle to the magnet cannot succeed. The droplet is not able to overcome the surface tension and cannot attach to the magnet.
Preparation of Well-organized Fibers
Because of magneto-mechanical drawing mechanism and set-up, we can easily produce fibers in parallel. Fibers with vertical cross structure can also be prepared by changing the collecting device. A schematic diagram of improved equipment for vertical cross fibers is well presented in Fig. 6a, and the rotating stage was replaced by a removable box frame-collector. The red and gray colors of the box represent, respectively, the magnet and pillar. Firstly, fibers were collected on the frame via a few minutes of magneto-mechanical drawing. Then rotate the frame by 90°. And magneto-mechanical drawing continued for few minutes, resulting in vertical crossed fibers. This is a fast and practical method to fabricate crossed fibers or devices. Figure 6b shows the optical photograph of vertical crossed fibers.
Magneto-Mechanical Drawing Other Composite Fibers
Moreover, we use different polymers in this study to ensure the general applicability of magneto-mechanical drawing, including PVDF and PMMA. Three kinds of magnetic nanoparticles, including γ-Fe2O3, Fe3O4, and NiO, are also used. Similar to the process of preparing PVDF solution, 22 wt.% PMMA in DMF with 2 wt.% γ-Fe2O3 nanoparticles can be obtained. Besides, γ-Fe2O3 can be replaced by other magnetic nanoparticles. Additional file 1: Figure S2 shows the viscosity versus shear rate curves for different PMMA/magnetic nanoparticle solutions. As shown in Fig. 7, composite fibers of different materials were successfully produced by magneto-mechanical drawing. Figure 7g shows the effect of different polymer and magnetic nanoparticles on fiber diameter. The average diameter of PMMA/nanoparticle microfibers is larger than that of PVDF/nanoparticle fibers. Different types of magnetic nanoparticles have little influence on the average fiber diameter.
Mechanical Property of PVDF/γ-Fe2O3 Fibers
In order to find the potential application of fibers in stretchable component, mechanical deformation of PVDF/γ-Fe2O3 fibers was investigated by the stress-strain curve. A bunch of fibers (average bundle diameter ~10 μm) was stretched under increasing strain in longitudinal direction. The curve in Fig. 8 shows the mechanical properties of fibers: yield stress of 0.51 MPa, tensile strength of 0.88 MPa, yield strain of 24 % with an elongation at break of 444 %. Besides, three regions were exhibited in this curve. The elastic region is about 0 to 24 %, the plastic region is from 24 to 444 %, and the fracture region is from 444 to 483 %.
Magnetic Property of the Fibers
Figure 9 and Additional file 1: Figure S3 show the magnetization curves of PVDF/nanoparticles microfibers and PMMA/nanoparticles microfibers at room temperature, respectively. Each of the magnetization curves shows a very small hysteresis loop that is hardly observed. The coercive force and remnant magnetization are almost zero, which indicates the superparamagnetic behavior of the fibers. The superparamagnetic phenomenon is due to the small size of magnetic nanoparticles (spherical single particle with diameter of 20 nm) inside the fibers [28, 29]. However, it should be noted that the coercive force does not decrease to zero, which could be attributed to the aggregated nanoparticles, as shown in Fig. 3b. The magnetic property may demonstrate potential applications of the composite fibers in magnetic sensors and drug delivery.
Conclusions
In this study, a facile magneto-mechanical drawing method has been used to prepare magnetic composite microfibers. This method utilizes magnetic force generated by a revolving permanent magnet to draw polymer/magnetic nanoparticle solutions, which is simple, energy-saving, and safe. PVDF/γ-Fe2O3 fibers with parallel and crossed structures were successfully prepared by this method. SEM and TEM images indicate that the average fiber diameter is 8.4 μm and magnetic γ-Fe2O3 nanoparticles are distributed in the PVDF matrix. In addition, the fiber diameter decreases gradually by increasing rotating speed of collecting stage. Different polymers and magnetic nanoparticles have also been applied in this work successfully to prove the general applicability of the method. Particularly, the resultant fibers show excellent superparamagnetic behavior and ultra-high stretchability (~440 %), indicating potential applications in functional fibers, stretchable devices/sensors, and magnetic drug delivery.
References
Zhou Z, Lin W, Wu XF (2015) Electrospinning ultrathin continuous cellulose acetate fibers for high-flux water filtration. Colloids Surf A 494:21–29
Wang Q, Bai Y, Xie J, Jiang Q, Qiu Y (2016) Synthesis and filtration properties of polyimide nanofiber membrane/carbon woven fabric sandwiched hot gas filters for removal of PM 2.5 particles. Powder Technol 292:54–63
Anka FH, Balkus KJ Jr (2013) Novel nanofiltration hollow fiber membrane produced via electrospinning. Ind Eng Chem Res 52:3473–3480
Jalaja K, Anil Kumar PR, Dey T, Kundu SC, James NR (2014) Modified dextran cross-linked electrospun gelatin nanofibres for biomedical applications. Carbohydr Polym 114:467–475
Hild N, Schneider OD, Mohn D, Luechinger NA, Koehler FM, Hofmann S, Vetsch JR, Thimm BW, Müller R, Stark WJ (2011) Two-layer membranes of calcium phosphate/collagen/PLGA nanofibres: in vitro biomineralisation and osteogenic differentiation of human mesenchymal stem cells. Nanoscale 3:401–409
Brozena AH, Oldham CJ, Parsons GN (2016) Atomic layer deposition on polymer fibers and fabrics for multifunctional and electronic textiles. J Vac Sci Technol A 34:010801
Gorji M, Jeddi AAA, Gharehaghaji AA (2012) Fabrication and characterization of polyurethane electrospun nanofiber membranes for protective clothing applications. J Appl Polym Sci 125:4135–4141
Bueres RF, Asedegbega-nieto E, Díaz E, Ordóñez S, Díez FV (2008) Preparation of carbon nanofibres supported palladium catalysts for hydrodechlorination reactions. Catal Commun 9:2080–2084
Tan DH, Zhou C, Ellison CJ, Kumar S, Macosko CW, Bates FS (2010) Meltblown fibers: influence of viscosity and elasticity on diameter distribution. J Non-Newtonian Fluid Mech 165:892–900
Ellison CJ, Phatak A, Giles DW, Macosko CW, Bates FS (2007) Melt blown nanofibers: fiber diameter distributions and onset of fiber breakup. Polymer 48:3306–3316
Greiner A, Wendorff JH (2007) Electrospinning: a fascinating method for the preparation of ultrathin fibers. Angew Chem Int Ed 46:5670
Huang ZM, Zhang YZ, Kotaki M, Ramakrishna S (2003) A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos Sci Technol 63:2223–2253
Reneker DH, Chun I (1996) Nanometre diameter fibres of polymer, produced by electrospinning. Nanotechnology 7:216–223
Borkar S, Gu B, Dirmyer M, Delicado R, Sen A, Jackon BR, Badding JV (2006) Polytetrafluoroethylene nano/microfibers by jet blowing. Polymer 47:8337–8343
Badrossamay MR, Mcllwee HA, Goss JA, Parker KK (2010) Nanofiber assembly by rotary jet-spinning. Nano Lett 10:2257–2261
Zhou FL, Gong RH (2008) Manufacturing technologies of polymeric nanofibres and nanofibre yarns. Polym Int 57:837–845
Frenot A, Chronakis IS (2003) Polymer nanofibers assembled by electrospinning. Colloid Interface Sci 8:64–75
Li D, Xia Y (2004) Electrospinning of nanofibers: reinventing the wheel? Adv Mater 16:1151–1170
Wu Y, Yu JY, He JH, Wan YQ (2007) Controlling stability of the electrospun fiber by magnetic field. Chaos, Solitons Fractals 32:5–7
Yang D, Lu B, Zhao Y, Jiang X (2007) Fabrication of aligned fibrous arrays by magnetic electrospinning. Adv Mater 19:3702–3706
Liu Y, Zhang X, Xia YN, Yang H (2010) Magnetic-field-assisted electrospinning of aligned straight and wavy polymeric nanofibers. Adv Mater 22:2454–2457
EI Mohajir BE, Heymans N (2001) Changes in structural and mechanical behaviour of PVDF with processing and thermomechanical treatments. 1. Change in structure. Polymer 42:5661–5667
Yu LY, Xu ZL, Shen HM, Yang H (2009) Preparation and characterization of PVDF–SiO2 composite hollow fiber UF membrane by sol–gel method. J Membr Sci 337:257–265
Saikia D, Kumar A (2004) Ionic conduction in P(VDF-HFP)/PVDF-(PC + DEC)–LiClO4 polymer gel electrolytes. Electrochim Acta 49:2581–2589
Luo H, Huang Y, Wang D (2013) The crystallization and crystal transition of PVDF in PAN nano-tube. Polymer 54:4710–4718
Agyemang FO, Sheikh FA, Appiah-Ntiamoah R, Chandradass J, Kim H (2015) Synthesis and characterization of poly(vinylidene fluoride)-calcium phosphate composite for potential tissue engineering applications. Ceram Int 41:7066–7072
Salimi A, Yousefi AA (2003) Analysis method: FTIR studies of β-phase crystal formation in stretched PVDF films. Polym Test 22:699–704
Tang B, Wang G, Zhuo L, Ge J, Cui L (2006) Facile route to α-FeOOH and α-Fe2O3 nanorods and magnetic property of α-Fe2O3 nanorods. Inorg Chem 45:5196–5200
Zhu Y, Zhao W, Chen H, Shi J (2007) A simple one-pot self-assembly route to nanoporous and monodispersed Fe3O4 particles with oriented attachment structure and magnetic property. J Phys Chem C 111:5281–5285
Acknowledgements
This work was supported by the National Natural Science Foundation of China (51373082, 51673103, and 11304173), the Taishan Scholars Programme of Shandong Province, China (ts20120528), and the Postdoctoral Scientific Research Foundation of Qingdao.
Authors’ Contributions
YZL developed the concept and designed the experiments. JTL, XSJ, and XXH performed the experiments. YZL, JTL, and GFY contributed to data analysis. All authors wrote and revised the paper. All authors read and approved the final manuscript.
Competing Interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Additional file
Additional file 1: Figure S1.
Viscosity versus shear rate curves for different PVDF/magnetic nanoparticle solutions (22 wt.% PVDF, 2 wt.% nanoparticles): (a) PVDF, (b) PVDF/γ-Fe2O3, (c) PVDF/Fe3O4, and (d) PVDF/NiO. Figure S2. Viscosity versus shear rate curves for different PMMA/magnetic nanoparticle solutions (22 wt.% PMMA, 2 wt.% nanoparticles): (a) PMMA/γ-Fe2O3, (b) PMMA/Fe3O4, (c) PMMA, and (d) PMMA/NiO. Figure S3. Magnetic hysteresis loops of PMMA composite fibers with different magnetic nanoparticles: (a) PMMA/Fe3O4, (b) PMMA/NiO, and (c) PMMA/γ-Fe2O3. (DOC 306 kb)
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Li, JT., Jia, XS., Yu, GF. et al. Fabrication of Continuous Microfibers Containing Magnetic Nanoparticles by a Facile Magneto-Mechanical Drawing. Nanoscale Res Lett 11, 426 (2016). https://doi.org/10.1186/s11671-016-1646-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1646-8