Abstract
Cubic PtCu nanocages (NCs) were successfully synthesized through a redox reaction using cuprous oxide (Cu2O) as a sacrificial template and reducing agent. The porous PtCu NCs were composed of amounts of PtCu nanograins with an average particle size of 2.9 nm. The electrocatalytic performance of the PtCu NC electrode towards H2O2 was studied by cyclic voltammetry (CV) and chronoamperometry. The prepared PtCu NC electrode exhibited excellent electrocatalytic activity towards H2O2, with a wide liner range from 5 μM to 22.25 mM, a relatively high sensitivity of 295.3 μA mM-1 cm-2, and a low detection limit of 5 μM (S/N = 3). The hollow porous nanostructure has potential applications in biosensors.
Avoid common mistakes on your manuscript.
Background
Quantitatively accurate and fast determination of H2O2 is extremely important in the field of food industry, pharmaceutical, clinical, industrial, and environmental analyses [1]. Among the several analytical techniques, electrochemical analysis is widely used due to the fast response, high sensitivity, and excellent selectivity [2, 3]. Although enzyme-modified electrode is always used to build H2O2 biosensor due to its high selectivity, the enzymatic biosensors still suffer from the insufficient stability which originated from the nature of enzymes [4]. Therefore, the study of nonenzymatic H2O2 sensors is aroused in this field. It is known that platinum shows excellent electroactivity because of the efficient electron transfer rate [5, 6]. Platinum with special morphologies, such as spherical [7], cubic [8], nanowires [9], nanoflowers [10], have been reported to construct biosensors. In addition, specific surface area is also a key factor affecting the performance of the biosensor. Therefore, how to increase the specific surface area is the focus in scientific research. Hollow structures have attracted extensive attentions for their special frame and composition. Large inner surface area can be obtained because of the inner void space of hollow structure. In recent years, hollow noble metals have been applied in the field of electrocatalyst due to the high electron transfer rate and large surface area [11]. However, few articles reported the applications of hollow noble metals in the field of biosensors.
In the present work, cubic PtCu NCs were fabricated using cuprous oxide (Cu2O) crystals as sacrificial templates, and their electrocatalytic activity towards H2O2 was investigated. The nonenzymatic H2O2 sensors exhibited excellent electrocatalytic performance with a high sensitivity and wide linear range for the determination of H2O2.
Methods
Reagents
Chloroplatinic acid, H2O2 (30 wt.% in H2O) and Nafion solution (5.0 wt.% in a mixture of lower aliphatic alcohols and water) were purchased from Sigma-Aldrich (St. Louis, MO, USA). All other reagents were of analytical grade and used as received without further purification (Chengdu Kelong, Chengdu, China). High-quality deionized water (resistivity > 18.0 MΩ cm-1) used for all experiments was prepared by a Water Purification System (UPT-II-10 T) provided by Chengdu YouPu, Chengdu, China.
Preparation of PtCu NCs
Cubic Cu2O template was prepared according to the previous report [12]. Ten milliliters of NaOH aqueous solution (2 M) was added dropwise into the stirred CuCl2 · 2H2O (100 mL, 0.01 M) at 55°C. After stirring for 0.5 h, 10.0 mL ascorbic acid solution (0.6 M) was added. The final products were collected by centrifugation after 3 h, followed by drying in vacuum at 40°C for 24 h.
In order to prepare PtCu NCs, 10 mg prepared Cu2O was dispersed in 10 mL distilled water by ultrasonic for 15 min and then 40 mg sodium citrate was added. After stirring for 15 min, 1 mL chloroplatinic acid (20 mM) was added. After reacting for 20 min, 1 mL of dilute HNO3 (5 mM) was injected into the above solution to etch the Cu2O cores. After 40 min, the ultimate products were separated by mild centrifugation and dried at 40°C for 24 h in an oven.
Electrochemical measurements
All electrochemical measurements were performed on a μIII Autolab electrochemical workstation in 0.1 M phosphate-buffered solution (PBS, pH = 7.0). Neutral PBS was obtained by mixing NaH2PO4 and Na2HPO4 solution (0.1 M). A conventional three-electrode system was used with Ag/AgCl (saturated with KCl) and platinum as the reference electrode and counter electrode, respectively. PtCu NC modified glassy carbon electrode (GCE, Ф = 3 mm) served as the working electrode. Typically, GCE was carefully polished with 0.05 μm alumina powders. Then, 5 μL of PtCu NC suspension (5 mg/mL) was cast onto the GCE and dried in air. Finally, 3 μL 1% Nafion solution was dipped onto the modified electrode.
Results and discussion
Characterizations
As shown in Figure 1a, no Cu2O (JCPDS 65–3288) residue remains in the final products. Compared to pure Pt (JCPDS 65–2868), all diffraction peaks shift to large angle direction. The diffraction peaks located at around 41.2°, 48.1°, and 70° can be indexed to cubic PtCu alloy (JCPDS 48–1549). The average particle size of PtCu was calculated to be 2.9 nm according to the Scherrer equation:
where B is the full width at half maximum (FWHM), λ is the X-ray wavelength (1.5406 Å), and K is a shape factor (about 0.89). On account of the fact that the Cu2O/Cu redox pair value is 0.36 V, which is much lower than that of PtCl62-/Pt (0.735 V), therefore, Cu2O crystals can be used as the reducing agent and sacrificial template for the synthesis of cubic PtCu NCs. The formation process of PtCu NCs can be explained in the following equations:
According to the above equations, the coexistence of Cu can be attributed to the disproportionation reaction of Cu (I). The reactions can simultaneously produce metallic Cu and Pt in the presence of H+, resulting in the formation of PtCu alloy. Figure 1b,c shows the scanning electron microscope (SEM) images of the prepared Cu2O template and the cubic PtCu NCs, respectively. The cubic Cu2O crystals have an average edge length about 200 nm, and the surface of the Cu2O crystals is smooth, uniform, and regular. However, the surface of PtCu NCs changes into rough and porous, indicating the formation of PtCu aggregates. It is clear that the PtCu NCs maintain the morphology of the Cu2O template and the interiors are hollow. The transmission electron microscope (TEM) image of PtCu NCs (Figure 1d) further provides convincing evidence of the hollow structure. For a further investigation, high-resolution transmission electron microscope (HRTEM) images were taken and displayed in Figure 1e,f. It is displayed that the shell of the PtCu NCs is porous (Figure 1e), and the porous shell is composed of amounts of PtCu nanograins. The porous structure possesses large specific surface area, which is beneficial for the electrocatalysis of H2O2. The inserted selected area electron diffraction (SAED) pattern indicates that the PtCu NCs have a polycrystalline structure. From Figure 1f, the size of the nanograins is about 2 to 4 nm, which agrees well with the value calculated from X-ray diffraction (XRD). The spacing for marked adjacent lattice fringes of PtCu NCs is about 0.22 nm, which is consistent with the standard value of PtCu (111) lattice spacing (0.219 nm).
Electrochemical performances of the PtCu NC electrode
In order to estimate the kinetics of the electrode, the cyclic voltammetries (CVs) of cubic PtCu NC electrode were measured in 0.1 M PBS containing 1.0 mM H2O2 at different scan rates. As can be seen from Figure 2a, both the anodic and cathodic peak currents are proportional to the square root of the scan rate, indicating that the electrocatalytic process is diffusion-controlled. CVs of PtCu NC electrode in 0.1 M PBS with different concentrations of H2O2 were illustrated in Figure 2b. With the increase of the concentration, both the anodic and cathodic peak currents linearly change, showing a linear dependence between the peak current and the concentration of H2O2. As can be seen from Figure 2b, peaks 1 and 2 corresponding to hydrogen adsorption are clearly investigated. Peaks 3 and 4 are the oxidation peaks of Cu and Pt in the alloy, respectively. Peak 5 corresponds to metal oxide reduction. With the reduction of Pt, more active sites are obtained, and the response current is clearly investigated.
Figure 3 displays the amperometric response of the cubic PtCu NC electrode at -0.45 V to successive injection of a certain amount of H2O2 into the stirred 0.1 M PBS, and the corresponding calibration curve is exhibited in the inset. After the injection of H2O2 into the 0.1 M PBS, a well-defined, stable, and fast amperometric response was observed. The linear relationship was obtained for concentration ranging from 5 μM to 22.25 mM. The linear regression equation was given as y = -20.862x - 32.157 [I (μA); x (mM)], with a correlation coefficient of R = 0.9990. The detection limit of H2O2 was found to be 5 μM (S/N = 3) with a relatively high sensitivity of 295.3 μA mM-1 cm-2. The sensitivity and linear range obtained at PtCu NC electrode are better than those for HRP immobilized at multiwalled carbon nanotube/alumina-coated silica nanocomposite modified glassy carbon electrode (157 μA mM-1 cm-2; 1 to 500 μM) [13] and nano-Au monolayer supported by carbon ceramic electrode (290 μA mM-1 cm-2; 12.2 μM to 1.1 mM) [14]. The excellent performance may be attributed to the possible synergetic effect between Pt and Cu [15] and the porous structure of the PtCu NCs, which provide a large specific surface area. In terms of the synergetic effect, Cu atom in the PtCu alloy acts both as promoting centers for the generation of the Cu-OHad species and as an electron donor to Pt in the PtCu alloy. The incorporation of Cu atom decreases the Pt 4f binding energies and consequently reduces the Pt-OHad bond strength. Therefore, the intimate contact between Pt and Cu domains in the PtCu alloy greatly promotes the regeneration of Pt sites for high electrochemical activity towards hydrogen peroxide.
To estimate the effective surface area of the PtCu NC electrode, cyclic voltammograms on PtCu NC electrode in a solution containing 5 mM K3Fe(CN)6 and 0.1 M KCl were performed [16]. According to the Randles-Sevcik equation [17],
where A is the effective surface area (cm2), Ip is the peak current of the redox reaction of [Fe(CN)6]3-/4- (A), n is the number of electrons transferred (n = 1), D is the diffusion coefficient (0.76 × 10-5 cm2 s-1), v is the scan rate (V s-1), and C is the concentration of K3Fe(CN)6 (5 mM). The calculated value of A is 0.83 cm2 for the PtCu NC electrode, which is 11.75 times of the bare GCE.
Conclusions
Cubic PtCu NCs were successfully synthesized using Cu2O as the template. The PtCu NC electrode exhibited excellent electrocatalytic activity towards H2O2. The observed detection limit and sensitivity for PtCu NC electrode was 5 μM and 295.3 μA mM-1 cm-2, respectively, with a wide linear range from 5 μM to 22.25 mM. On the basis of our research, the PtCu NC electrode has potential applications for the design of hydrogen peroxide sensor.
References
Lian W, Wang L, Song Y, Yuan H, Zhao S, Li P, Chen L: A hydrogen peroxide sensor based on electrochemically roughened silver electrodes. Electrochim Acta 2009, 54: 4334–4339. 10.1016/j.electacta.2009.02.106
Wang MY, Shen T, Wang M, Zhang D, Chen J: One-pot green synthesis of Ag nanoparticles-decorated reduced graphene oxide for efficient nonenzymatic H2O2 biosensor. Mater Lett 2013, 107: 311–314.
Cheng ZP, Xu JM, Zhong H, Chu XZ, Song J: Hydrogen peroxide-assisted hydrothermal synthesis of hierarchical CuO flower-like nanostructures. Mater Lett 2011, 65: 2047–2050. 10.1016/j.matlet.2011.04.021
Ansari A, Solanki P, Malhotra B: Hydrogen peroxide sensor based on horseradish peroxidase immobilized nanostructured cerium oxide film. J Biotechnol 2009, 142: 179–184. 10.1016/j.jbiotec.2009.04.005
Strbac S: The effect of pH on oxygen and hydrogen peroxide reduction on polycrystalline Pt electrode. Electrochim Acta 2011, 56: 1597–1604. 10.1016/j.electacta.2010.10.057
Huang K, Li Y, Xing Y: Increasing round trip efficiency of hybrid Li-air battery with bifunctional catalysts. Electrochim Acta 2013, 103: 44–49.
Hrapovic S, Liu Y, Male K, Luong JHT: Electrochemical biosensing platforms using platinum nanoparticles and carbon nanotubes. Anal Chem 2004, 76: 1083–1088. 10.1021/ac035143t
Ren J, Shi WT, Li K, Ma ZF: Ultrasensitive platinum nanocubes enhanced amperometric glucose biosensor based on chitosan and nafion film. Sensor Actuat B-Chem 2012, 163: 115–120. 10.1016/j.snb.2012.01.017
Lingane JJ, Lingane PJ: Chronopotentiometry of hydrogen peroxide with a platinum wire electrode. J Electroanal Chem 1963, 5: 411–419.
Guo MQ, Hong HS, Tang XN, Fang HD, Xu XH: Ultrasonic electrodeposition of platinum nanoflowers and their application in nonenzymatic glucose sensors. Electrochim Acta 2012, 63: 1–8.
Yang L, Hu CG, Wang JL, Yang ZX, Guo YM, Bai ZY, Wang K: Facile synthesis of hollow palladium/copper alloyed nanocubes for formic acid oxidation. Chem Commun 2011, 47: 8581–8583. 10.1039/c1cc12528a
Zhang DF, Zhang H, Guo L, Zheng K, Han XD, Zhang Z: Delicate control of crystallographic facet-oriented Cu2O nanocrystals and the correlated adsorption ability. J Mater Chem 2009, 19: 5220–5225. 10.1039/b816349a
Huang JL, Tsai YC: Direct electrochemistry and biosensing of hydrogen peroxide of horseradish peroxidase immobilized at multiwalled carbon nanotube/alumina-coated silica nanocomposite modified glassy carbon electrode. Sensor Actuat B-Chem 2009, 140: 267–272. 10.1016/j.snb.2009.04.033
Lei CX, Hu SQ, Gao N, Shen GL, Yu RQ: An amperometric hydrogen peroxide biosensor based on immobilizing horseradish peroxidase to a nano-Au monolayer supported by sol–gel derived carbon ceramic electrode. Bioelectrochemistry 2004, 65: 33–39. 10.1016/j.bioelechem.2004.06.002
Wang DS, Li YD: Bimetallic nanocrystals: liquid-phase synthesis and catalytic applications. Adv Mater 2011, 23: 1044–1060. 10.1002/adma.201003695
Tian LL, Liu BT: Fabrication of CuO nanosheets modified Cu electrode and its excellent electrocatalytic performance towards glucose. Appl Surf Sci 2013, 283: 947–953.
Bard AJ, Faulkner LR: Electrochemical Methods: Fundamentals and Applications. 2nd edition. New York: Wiley; 2001.
Acknowledgements
This study is supported by the National Natural Science Foundation of China (21101136), Foundation of Scientific and Technological Research Program of Chongqing Municipal Education Commission (grant no. KJ121213), Chongqing Natural Science Foundation (cstc2013jcyjA20023), Talent Introduction Foundation of Chongqing University of Arts and Sciences (R2012cl14, R2013CJ05), Foundation of Chongqing University of Arts and Sciences (Z2011XC15, Z2013CJ01), and Graphene Research Project of Research Center for Materials Interdisciplinary Science.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
LT designed the experiment and wrote the paper. XZ and WH prepared the solution and the modified electrode. BL carried out the synthesis of PtCu nanocage. YL did the electrochemical measurements. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Tian, L., Zhong, X., Hu, W. et al. Fabrication of cubic PtCu nanocages and their enhanced electrocatalytic activity towards hydrogen peroxide. Nanoscale Res Lett 9, 68 (2014). https://doi.org/10.1186/1556-276X-9-68
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-68