Abstract
This work reports the color-tunable mixed photoluminescence (PL) emission from an Alq3 organic layer in an Au-Alq3-Au plasmonic structure through the combination of organic fluorescence emission and another form of emission that is enabled by the surface plasmons in the plasmonic structure. The emission wavelength of the latter depends on the Alq3 thickness and can be tuned within the Alq3 fluorescent spectra. Therefore, a two-color broadband, color-tunable mixed PL structure was obtained. Obvious changes in the Commission Internationale d’Eclairage (CIE) coordinates and the corresponding emission colors of Au-Alq3-Au samples clearly varied with the Alq3 thickness (90, 130, and 156 nm).
Avoid common mistakes on your manuscript.
Background
In recent years, organic light-emitting diodes (OLED) have been attracting considerable attention for various illumination applications because they exhibit excellent properties that traditional light sources do not, including high brightness, large size, transparency, and flexibility. OLED have been considered to be potential next generation of light sources [1–3]. To realize full color and white OLED, various color mixing structures, including multiple dopant emissive layers and multiple emissive layers, and down conversion in the optical microcavity, have been utilized with various degrees of success [4–10]. Some methods for generating white color emission from OLED have been developed, such as the method of partial energy transfer in which the OLED materials are doped with fluorescent/phosphorescent dyes [11–20]. The mixing of the EL from the host molecules with excimer/exciplex emissions has also been found to yield white emission [21–23]. Other methods involve stacking red-, green- and blue-emissive components on a charge generation layer (CGL) [24–29]. Recently, metal-dielectric-metal (MDM) surface plasmon (SP) structures, which are similar to planar optical microcavities, have attracted a great deal of attention because they have various potential applications in optoelectronic devices [30–34].
In an MDM structure with semi-infinitely thick metals, if the thickness of the dielectric is smaller than the SP penetration depth at the metal/dielectric interface, then the SPs on both interfaces of the dielectric layer can interact with each other and split into two hybridized SP modes: an odd SP with an anti-symmetric magnetic field distribution and an even SP with a symmetrical magnetic field distribution [30]. The dispersion curve of the odd SP can cross the light line in air and shift up (or down) in energy when the dielectric thickness is reduced (or increased), indicating that the odd SP is not only radiative when one of the two semi-infinite thick metal layers is reduced to a finite and semi-transparent layer but that its energy is also tunable by variation of the dielectric thickness. Therefore, if the dielectric layer in the MDM structure is replaced with an organic emitter layer with a thickness of the order of an optical wavelength, then owing to near-field optics and the Purcell effect, the organic excitons can preferentially recombine into the odd SP that is confined in this metal-organic emitter layer-metal structure, and the radiative odd SP subsequently couples out of the device to photons in the air. This property has been investigated experimentally [32, 33].
However, the application of this light emission has so far received little attention. In this work, a color-tunable mixing method, using a single organic light-emitting layer that is embedded between two metal layers of finite thickness is proposed. When one of the two metals is of finite thickness and is semi-transparent, the organic fluorescence still occurs and serves as a constant source of light. Further light emission is produced through the odd SP, and the wavelength of this emission is tunable by variation of the thickness of the organic layer. Therefore, color-tunable mixed emission from an MDM structure with finite thickness metal layers can easily be realized.
Methods
Design and fabrication of sample
Because the dispersion curves of the coupled SPs in the MDM structure depend mainly on the thickness of the dielectric, calculated dispersion curves are initially obtained to determine the thickness of the dielectric that will produce the specific photon emission energy enabled by the odd SP. Figure 1 plots the calculated dispersion curves of the MDM structure with semi-infinite thick metal layers and dielectric thicknesses of 90, 120, and 150 nm. The refractive index of the dielectric layer is a constant 1.74, which is the refractive index of the organic material, tris(8-hydroxyquinoline) (Alq3), used in the experiment. The wavelength-dependent refractive index for the Au metal is taken from the literature [35]. As shown, the odd SP energies associated with the parallel component of the wave vector k x =0, which is the photon emission energy in the direction normal to the sample surface, are approximately 1.77 eV (700 nm), 2.03 eV (610 nm), and 2.30 eV (539 nm) for MDM structures with 150-, 120-, and 90-nm-thick dielectric layers, respectively.
Based on an analysis of the dispersion curve, three MDM samples, A, B, and C, with Alq3 thicknesses of 90, 120, and 150 nm, respectively, embedded between two 20-nm-thick Au layers were fabricated. Two reference samples, consisting of glass/120-nm-thick Alq3 and glass/20-nm-thick Au/120-nm-thick Alq3, were fabricated and are shown in Figure 2a,b, respectively. The organic material was subjected to temperature-gradient sublimation under a high vacuum before use. The organic and metal layers were deposited by vacuum vapor deposition in a vacuum chamber with a base pressure of <10-6 Torr. The deposition system permitted the fabrication of the complete device structure in a single vacuum pump-down without breaking the vacuum. The deposition rate of organic layers was kept at approximately 0.1 nm/s. The area of the MDM structure was 3 × 3 cm2, defined by a shadow mask. Figure 2c shows the MDM structure.
Results and discussion
Figure 3 shows the transmittance spectra of the three MDM samples with the different Alq3 thicknesses, measured using a Lambda 35 UV-vis spectrophotometer (PerkinElmer Inc., Waltham, MA, USA). Because both Au layers are sufficiently thin, externally incident light can be transmitted through the MDM structure by resonant transmission with the radiative optical modes that are present in the MDM structure. Therefore, the peaks that are induced by the odd SP can be observed in the transmittance spectra. To support the determination of the exact structure, the transmittance of a p-polarized plane wave in air, incident on 30-nm-thick Au/90, 130, and 156-nm-thick Alq3/30-nm-thick Au structures, was simulated using the software that was written by the authors and based on the solution for the boundary conditions of the electromagnetic waves, and the results thus obtained are also shown in Figure 3. The calculated and measured transmission peak positions match each other closely, and the transmitted wavelength depends sensitively on the thickness of Alq3 layer. From Figure 3, the wavelengths of the photons whose emission is enabled by the odd SP in the normal direction for samples A, B, and C are approximately 550, 650, and 750 nm, respectively.
Figure 4 shows the photoluminescence (PL) spectra in the normal direction from samples A, B, and C and from the reference sample with the glass/120-nm-thick Alq3 structure. As expected, the emission peaks around 550, 650, and 750 nm for samples A, B, and C closely match the peaks in the transmittance spectra in Figure 3. The PL intensity at the wavelength of 750 nm is smaller than that at 550 or 650 nm because the population of excitons with an energy that corresponds to 750 nm is smaller than that with an energy that corresponds to 550 or 650 nm. From the PL spectrum of sample C, the organic excitons recombine into the odd SP very well, even if the peak wavelength of approximately 750 nm is at the edge of the Alq3 fluorescent spectrum, while the emission peak at around 530 nm in the green region almost overlaps that in the PL spectrum from the reference sample, demonstrating that fluorescence from the Alq3 emissive layer is produced in MDM structures with metal layers of finite thickness.The Commission Internationale d’Eclairage (CIE) coordinates of the PL in the normal direction from samples A, B, and C and from the reference sample are (0.42, 0.55), (0.47, 0.48), (0.37, 0.54), and (0.34, 0.56), respectively, as shown in Figure 5. Figure 4 presents photographs of the PL emissions. The CIE coordinates of the PL from samples A, B, and C obviously shifted in comparison with that from the reference sample and thus the corresponding emission color changed owing to color mixing with the added emission color that was enabled by the odd SP in the MDM structure. These experimental results indicate that the color mixing of the PL emission can be obtained from a single emitting layer by forming an MDM structure and that the emission color can be tuned by varying the thickness of the emitting middle layer.
Conclusions
Color-tunable mixed PL emission was achieved by insertion of an emitting layer between two metal layers of finite thickness to form an MDM structure. The PL emission is produced by the combination of two kinds of emission. The first is the organic fluorescent emission; the second is enabled by the odd SP in the MDM structure, and its wavelength is tunable, resulting in a color-tunable mixed emission. This emission process provides a feasible approach to generating two-primary white light.
References
D’Andrade BW, Forrest SR: White organic light-emitting device for solid-state lighting. Adv Mater 2004, 16: 1585–1595. 10.1002/adma.200400684
Kido J, Kimura M, Nagai K: Multilayer white light-emitting organic electroluminescent device. Science 1995, 267: 1332–1334. 10.1126/science.267.5202.1332
Ko CW, Tao YT: Bright white organic light-emitting diode. Appl Phy Lett 2001, 79: 4234–4236. 10.1063/1.1425454
Lin CL, Lin HW, Wu CC: Examining microcavity organic light-emitting devices having two metal mirrors. Appl Phy Lett 2005, 87: 021101–1–3.
Wu CC, Chen CW, Lin CL, Yang CJ: Advanced organic light-emitting devices for enhancing display performances. J Displ Technol 2005, 1: 248–266. 10.1109/JDT.2005.858942
Lin CL, Chang HC, Tien KC, Wu CC: Influences of resonant wavelengths on performances of microcavity organic light-emitting devices. Appl Phy Lett 2005, 90: 071111–1–3.
Peng H, Sun J, Zhu X, Yu X, Wong M, Kwok HS: High-efficiency microcavity top-emitting organic light-emitting diodes using silver anode. Appl Phy Lett 2006, 88: 073517–1–3.
Liu R, Xu C, Biswas R, Shinar J, Shinar R: MoO3 as combined hole injection layer and tapered spacer in combinatorial multicolor microcavity organic light emitting diodes. Appl Phy Lett 2011, 99: 093305–1–3.
Hofmann S, Thomschke M, Freitag P, Furno M, Lüssem B, Leo K: Top-emitting organic light-emitting diodes: influence of cavity design. Appl Phy Lett 2010, 97: 253308–1–3.
Chang CH, Cheng HC, Lu YJ, Tien KC, Lin HW, Lin CL, Yang CJ, Wu CC: Enhancing color gamut of white OLED displays by using microcavity green pixels. Org Lett 2010, 11: 1241–1244.
Kido J, Hongawa K, Okuyama K, Nagai K: White light-emitting organic electroluminescent devices using the poly(N‒vinylcarbazole) emitter layer doped with three fluorescent dyes. Appl Phys Lett 1994, 64: 815–817. 10.1063/1.111023
Kido J, Shionoya H, Nagai K: Single-layer white light-emitting organic electroluminescent devices based on dye-dispersed poly(N-vinylcarbazole). Appl Phys Lett 1995, 67: 2281–2283. 10.1063/1.115126
Tokito S, Iijima T, Tsuzuki T, Sato F: High-efficiency white phosphorescent organic light-emitting devices with greenish-blue and red-emitting layers. Appl Phys Lett 2003, 83: 2459–2461. 10.1063/1.1611620
Wang L, Lei G, Qiu Y: Bright white organic light-emitting diodes based on two blue emitters with similar molecular structures. J Appl Phys 2005, 97: 114503–1–6.
Sun Y, Giebink NC, Kanno H, Ma B, Thompson ME, Forrest SR: Management of singlet and triplet excitons for efficient white organic light-emitting devices. Nature 2006, 440: 908–912. 10.1038/nature04645
Huang J, Hou WJ, Li JH, Li G, Yang Y: Improving the power efficiency of white light-emitting diode by doping electron transport material. Appl Phys Lett 2006, 89: 133509–1–3.
Seo JH, Park JH, Kim YK, Kim JH, Hyung GW, Lee KH, Yoon SS: Highly efficient white organic light-emitting diodes using two emitting materials for three primary colors (red, green, and blue). Appl Phys Lett 2007, 90: 203507–1–3.
Jou JH, Wu MH, Wang CP, Chiu YS, Chiang PH, Hu HC, Wang RY: Efficient fluorescent white organic light-emitting diodes using co-host/emitter dual-role possessed di(triphenyl-amine)-1,4-divinyl-naphthalene. Org Electron 2007, 8: 735–742. 10.1016/j.orgel.2007.06.010
Jou JH, Chiu YS, Wang CP, Wang RY, Hu HC: Efficient, color-stable fluorescent white organic light-emitting diodes with single emission layer by vapor deposition from solvent premixed deposition source. Appl Phys Lett 2006, 88: 193501–1–3.
Tsai YC, Jou JH: Long-lifetime, high-efficiency white organic light-emitting diodes with mixed host composing double emission layers. Appl Phys Lett 2006, 89: 243521–1–3.
D’Andrade BW, Brooks J, Adamovich V, Thompson ME, Forrest SR: Controlling exciton diffusion in multilayer white phosphorescent organic light emitting devices. Adv Mater 2002, 14: 1032–1036. 10.1002/1521-4095(20020805)14:15<1032::AID-ADMA1032>3.0.CO;2-6
Williams EL, Haavisto K, Li J, Jabbour GE: Excimer-based white phosphorescent organic light‒emitting diodes with nearly 100% internal quantum efficiency. Adv Mater 2007, 19: 197–202. 10.1002/adma.200602174
Kalinowski J, Cocchi M, Virgili D, Fattori V, Williams JAG: Mixing of excimer and exciplex emission: a new way to improve white light emitting organic electrophosphorescent diodes. Adv Mater 2007, 19: 4000–4005. 10.1002/adma.200700655
Shen Z, Burrows PE, Bulović V, Forrest SR, Thompson ME: Three-color, tunable, organic light-emitting devices. Science 1997, 276: 2009–2011. 10.1126/science.276.5321.2009
Liao LS, Klubek KP, Tang CW: High-efficiency tandem organic light-emitting diodes. Appl Phys Lett 2004, 84: 167–169. 10.1063/1.1638624
Kanno H, Holmes RJ, Sun Y, Kena-Cohen S, Forrest SR: White stacked electrophosphorescent organic light-emitting devices employing MoO3 as a charge-generation layer. Adv Mater 2006, 18: 339–342. 10.1002/adma.200501915
Ho MH, Chen TM, Yeh PC, Hwang SW, Chen CH: Highly efficient p-i-n white organic light emitting devices with tandem structure. Appl Phys Lett 2007, 91: 233507–1–3.
Lee TW, Hoh T, Choi BK, Kim MS, Shin DW, Kido J: High-efficiency stacked white organic light-emitting diodes. Appl Phys Lett 2008, 92: 043301–1–3.
Liao LS, Slusarek WK, Hatwar TK, Ricks ML, Comfort DL: Tandem organic light-emitting diode using hexaazatriphenylene hexacarbonitrile in the intermediate connector. Adv Mater 2008, 20: 324–329. 10.1002/adma.200700454
Chen NC, Lu CY, Huang YL, Liao CC, Ke WC, Huang BR: Properties of coupled surface plasmon-polaritons in metal-dielectric-metal structures. J Appl Phys 2012, 112: 033111–1–3.
Feng J, Okamoto T, Simonen J, Kawata S: Color-tunable electroluminescence from white organic light-emitting devices through coupled surface plasmons. Appl Phys Lett 2007, 90: 081106–1–3.
Liu JSQ, Brongersma ML: Omnidirectional light emission via surface plasmon polaritons. Appl Phys Lett 2007, 90: 091116–1–3.
Hayashi S, Maekawa A, Kim SC, Fujii M: Mechanism of enhanced light emission from an emitting layer embedded in metal-insulator-metal structures. Phys Rev B 2010, 82: 035441–1–3.
Huang BR, Liao CC, Fan WT, Wu JH, Chen CC, Lin YP, Li JY, Chen SP, Ke WC, Chen NC: Photoluminescence emission from Alq3 organic layer in metal–Alq3–metal plasmonic structure. Appl Surf Sci 2014, 303: 319–323.
Johnson PB, Christy RW: Optical constants of the noble metals. Phys Rev B 1972, 6: 4370–4379. 10.1103/PhysRevB.6.4370
Acknowledgements
The authors would like to thank the Ministry of Science and Technology and the Bureau of Energy, Ministry of Economic Affairs of Taiwan, for financially supporting this research. Ted Knoy is appreciated for his editorial assistance.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
NCC and CCL carried out the study of coupled surface plasmon in MDM structure and participated in the sequence alignment and drafted the manuscript. CCC participated in the design of the study and sequence alignment. WTF, JHW, JYL, and SPC fabricated the MDM samples, measured the optical properties, and helped to draft the manuscript. BRH and LLL conceived of the study, participated in its design and coordination, and helped draft the manuscript. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (https://creativecommons.org/licenses/by/4.0), which permits use, duplication, adaptation, distribution, and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Chen, NC., Liao, CC., Chen, CC. et al. Color-tunable mixed photoluminescence emission from Alq3 organic layer in metal-Alq3-metal surface plasmon structure. Nanoscale Res Lett 9, 569 (2014). https://doi.org/10.1186/1556-276X-9-569
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-569