Abstract
Alumina nanofibers were prepared by a technique that combined the sol–gel and electrospinning methods. The solution to be electrospun was prepared by mixing aluminum isopropoxide (AIP) in ethanol, which was then refluxed in the presence of an acid catalyst and polyvinylpyrolidone (PVP) in ethanol. The characterization results showed that alumina nanofibers with diameters in the range of 102 to 378 nm were successfully prepared. On the basis of the results of the XRD and FT-IR, the alumina nanofibers calcined at 1,100°C were identified as comprising the α-alumina phase, and a series of phase transitions such as boehmite → γ-alumina → α-alumina were observed from 500°C to 1,200°C. The pore size of the obtained γ-alumina nanofibers is approximately 8 nm, and it means that they are mesoporous materials. The kinetic study demonstrated that MO adsorption on alumina nanofibers can be seen that the pseudo-second-order kinetic model fits better than the pseudo-first-order kinetic model.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
In recent years, ceramic with nanostructures has attracted a lot of attention and is being used in the fields of electronics, information technology, and communications [1]. It has found wide application in other areas as well, including the mechanical and chemical sciences and electrical, optical, and electrochemical energy sectors as effective electrode materials [2, 3]. Among various chemical or physical synthetic methods, the electrospinning method is a popular one and involves the use of an electrically charged jet of polymer solution to form the nanofibers. The method can be described as follows. A high voltage is applied to the ceramic material solution with a polymer, and an electric field is generated between the tip of the syringe containing the solution and the collector. The solution is ejected in the form of a jet by electrical repulsion onto the collector, and fibers of nanoscaled diameters with inorganic precursor are formed [4]. The precursor nanofibers at high temperature are calcined to remove the polymers, and ceramic phase is obtained. This technique has been applied for the preparation of various metal oxide and ceramic nanofibers as well [5, 6], which included TiO2[7], ZnO [8], SnO2[9], BaTiO3[10], and Al2O3[2–6, 11].
Alumina (Al2O3) is one of the most important types of ceramic and is applied to the areas of catalysis, reinforcing components, electronic device fabrication, microelectronics, optics, and fire protection [12]. Most recently, alumina has been explored as effective electrode material for electrochemical energy storage device [13–15]. Al2O3 has specific physical, chemical, and mechanical properties, and during the process of forming the stable α-Al2O3, gibbsite is transformed to boehmite and then to a variety of metastable intermediate structures such as χ-, γ-, κ-, δ-, θ-alumina, depending on the temperature [16, 17].
The main objective of the study is to investigate the calcination conditions on morphological appearance and crystal structure of the resulting alumina and the adsorption property of alumina calcined at different temperatures. Therefore, we investigated the synthesis of alumina nanofibers using a technique that combined the sol–gel and electrospinning methods using aluminum isopropoxide (AIP), an organometallic compound, as the precursor and polyvinylpyrolidone (PVP) polymer solution. The formation, morphology, and crystallinity of the electrospun alumina nanofibers were determined through thermogravimetric analysis (TGA), scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared (FT-IR) spectroscopy, Gas Chromatograph (Shimadzu GC-2010 Plus AF) and the alumina nanofiber samples synthesized were evaluated by nitrogen adsorption/desorption analysis. In addition, different phase alumina nanofibers were applied for the adsorption of methyl orange dye (MO) solution.
Methods
The PVP (MW = 1,300,000; Kanto, Japan), AIP (C9H21O3Al) (>97.0%; Sigma-Aldrich Corporation, St. Louis, MO, USA), ethanol (94.0%; Daejung, Korea), and nitric acid (60%; Daejung, Korea) were obtained commercially and used as received without further purification. All the equipment used in the study was thoroughly cleaned prior to the experiments. A typical synthesis run was as follows: A certain amount of nitric acid and 10 mmol of the aluminum precursor AIP were added to 20 mL of ethanol, and the solution was stirred vigorously. The final composition of the mixed solution was such that the molar ratio of AIP/nitric acid/ethanol was 1:m:34, where m (=2.57) is the molar ratio of the acid (HNO3) to the alkoxide [17]. The mixture was covered with polyethylene (PE) film and then stirred vigorously at room temperature for at least 5 h. The PVP solution (10 wt.%) was prepared by dissolving the PVP polymer powder in ethanol under constant and vigorous stirring. The weight ratio of the polymer to the aluminum precursor was maintained at 3:1. The AIP and PVP solutions were then mixed, and the resulting AIP/PVP solution was loaded into a 10-mL syringe (SGE LL type) that was fitted with a metallic needle. The positive terminal of a variable high-voltage power supply was connected to the metallic needle and the negative terminal to a rotating collector (speed = 200 rpm) that was covered with the aluminum foil and served as the counter electrode. During a typical procedure, the voltage and the feeding rate were kept at 18 kV and 1.5 mL/h, respectively. The distance between the needle tip and the collector was maintained at 18 cm.
After the electrospinning was complete, the as-electrospun nanofibers were dried at 80°C for 24 h. Some of the dried nanofibers were used for the characterization by TGA, SEM, energy-dispersive X-ray spectroscopy (EDX), FT-IR spectroscopy, XRD, gas chromatography (Shimadzu GC-2010 Plus AF, Nakagyo-ku, Kyoto, Japan), and Brunauer-Emmett-Teller (BET) analysis. The remaining as-spun AIP/PVP composite nanofibers were calcined at different temperature (500°C to 1,200°C) for 2 h each at a heating rate of 5°C/min in order to obtain alumina nanofibers. Also, calcined alumina nanofibers were used for the characterization analysis and adsorption properties. As mentioned previously, the morphology of the fibers was examined by SEM (S4800, Hitachi Ltd., Tokyo, Japan). The diameters of the nanofiber were calculated from the SEM images using the Image J (National Institutes of Health, USA) software. The X-ray diffraction data was obtained with an X'Pert PRO MPD (PANalytical, B.V., Almelo, The Netherlands) diffractometer using Cu Kα radiation. FT-IR spectroscopy was performed on the samples using a NICOLET6700 (Thermo Scientific, Waltham, MA, USA) spectrometer that had a KBr beam splitter (operational wavelength range = 7,800 to 350 cm−1). TGA (STARSW, Mettler) was conducted up to 1,000°C with a heating rate of 5°C/min under a nitrogen and air atmosphere to evaluate the thermal behavior of the component nanofibers. The specific surface area and pore volume of the prepared alumina nanofibers were measured using the BET equation and the Horvath-Kawazoe (HK) method (ASAP2020, Micromeritics) after preheating the samples to 150°C for 2 h to eliminate adsorbed water. The pore size distributions were obtained by applying the HK method (micro-pore) to the nitrogen adsorption isotherms at 77 K using the software ASAP 2020.
Results and discussion
Figure 1 shows the results of the thermogravimetric curve and the derivative weight loss curve of the as-electrospun PVP and AIP/PVP composite nanofibers. At the AIP/PVP composite nanofiber curve, endothermic and exothermic peaks were observed with a corresponding weight loss of about 20%, in the region extending to 175°C. These peaks were attributed to the vaporization of physically absorbed water and the removal of any remaining solvent from the composite fibers. In the region extending from 200°C to 300°C, an endothermic and exothermic peak was observed that was associated with a weight loss of 30%. This observation was in accordance with the previous report by Kang et al. [18, 19] that a weight loss resulted from the decomposition and burning of the PVP polymer fibers. The peaks were observed between 300°C and 400°C, and the weight loss associated with these peaks was 60% and indicated the complete combustion of the PVP polymer fibers and the organometallic compound of AIP. In contrast to a study on sol–gel process without PVP performed by Xu et al. [17], the prominent exothermic peak was observed at 429°C and indicating the complete combustion of the PVP polymer fibers.
The SEM micrographs of the composite nanofibers show that the as-electrospun fibers as well as those calcined at 800°C and 1,200°C had similar morphologies (Figure 2). As can be readily seen, in addition to their shapes, the continuous morphology of the as-electrospun composite nanofibers was maintained in the calcined nanofibers as well. Cylindrical nanofibers with diameters in the range of 276 to 962 nm could be successfully prepared using AIP as the precursor (Figure 2b). The diameter of these nanofibers decreased after calcinations at 800°C and 1,200°C, and alumina nanofibers with diameters of 114 to 390 nm (Figure 2c) and 102 to 378 nm (Figure 2d) were obtained after the respective heat treatments. In addition, as the calcination temperature increased, the average diameter of the alumina nanofibers decreased continuously, indicating that the organic groups further decrease in diameter for an increase in the calcination temperature beyond 1,200°C. The alumina nanofibers fabricated in this study were thinner and had narrower diameter distributions than those reported by Kang et al. [8]. From the EDX analysis, as-electrospun AIP/PVP nanofibers calcined at 800°C and 1,200°C showed C, O, and Al, and only Al and O, respectively. This result indicates the formation of pure alumina nanofibers. As-electrospun AIP/PVP nanofibers calcined at 800°C had 67.13% of C, 29.37% of O, and 3.5% of Al, and those calcined at 1,200°C had only 61.38% of O and 38.62% of Al, respectively.
Figure 3 shows the XRD spectra of the alumina nanofibers calcined between 500°C and 1,200°C. There was also no distinct diffraction peak appearing for the samples calcined at 500°C and 600°C, and phase structure was found to be amorphous/microcrystalline. However, with the increase of calcination temperature up to 900°C, the typical peak of γ-Al2O3 was displayed with strong diffraction intensity. The γ-phase structure became weak when the temperature was above 1,000°C and completely disappeared at 1,100°C. The XRD spectrum of the sample calcined at 1,200°C indicated that α-alumina phase was formed. All the observed diffraction peaks matched well with those reported by Shanmugam et al. (JCPDS card no. 42-1468) [13]. From the above results, the phase transition of alumina nanofibers in this study can be shown as follows: amorphous/microcrystalline → γ-Al2O3 → α-Al2O3. In the process of heat treatment, the trihydroxide undergoes a series of transformation because of the water loss from hydration.
Figure 4 shows the FT-IR spectra of the alumina fibers obtained after calcination of the composite fibers at 500°C to 1,200°C, AIP solution, AIP/PVP solution, and as-electrospun composite fibers. Three characteristic peaks at 634, 581, and 440 cm−1 for alumina nanofibers calcined at 1,000°C, which it was confirmed α-phase alumina (Figure 4b), were observed, indicating Al-O bending and Al-O stretching. These peaks can be attributed to the presence of alumina; this conclusion is also supported by results of the XRD analysis [13].
The nitrogen adsorption and desorption isotherms and the corresponding pore size distribution of the synthesized alumina nanofiber calcined at 800°C and 1,200°C temperatures are shown in Figure 5. As observed in Figure 5a, both the isotherms were types IV and V, which were related to the mesoporous structure. However, the types of hysteresis loops were different from each other as the calcination temperatures changed. The hysteresis loop type of the alumina nanofiber calcined at 800°C and 1,200°C were H2 and H4 [20]. The surface area of two samples calcined at 800°C and 1,200°C were 177.8 and 42.7 m2/g.
Simple adsorption kinetic experiments were performed at concentrations of 10 mmol/L for MO with α- and γ-alumina nanofibers. In each concentration, a series of 5 mL of MO solutions with 3 mg of alumina nanofiber were placed in residual MO concentrations, and Ct was determined at 460 nm. The pseudo-first-order kinetic model is described by the following equation [20]:
where qe and q t are the capacity of metal ions adsorbed (millimole per gram) at equilibrium and time t (minute) and k1 is the pseudo-first-order rate constant (per minute). The pseudo-second-order model refers that the adsorption process is controlled by chemisorption through sharing of electron exchange between the solvent and the adsorbate [21]. The adsorption kinetic model is expressed as the following equation [20]:
The values of k2 and qe can be calculated from the intercept and the slope of the linear relationship, Equation 2, between t/q t and t. The curves of the plots of t/q t versus t were given in Figure 6, and the calculated qe, k1, k2, and the corresponding linear regression correlation coefficient R2 values are summarized in Table 1. From the relative coefficient (R2), it can be seen that the pseudo-second-order kinetic model fits the adsorption of MO on alumina nanofibers better than the pseudo-first-order kinetic model.
Conclusions
Alumina nanofibers were prepared by combining the sol–gel and electrospinning methods using AIP as an alumina precursor. The thus-produced alumina nanofibers were characterized by TGA, SEM, XRD, FT-IR spectroscopy, and nitrogen adsorption/desorption analysis. It was found from the SEM images of the various samples that the fiber-like shape and continuous morphology of the as-electrospun samples were preserved in the calcined samples. The diameters of the fabricated alumina nanofibers in this study were small and in the range of 102 to 378 nm with thinner and narrower diameter distributions. On the basis of the results of the XRD and FT-IR analysis, the alumina nanofibers calcined at 1,100°C were identified as comprising the α-alumina phase. In addition, a series of phase transitions such as boehmite → γ-alumina → α-alumina were observed from 500°C to 1,200°C. Adsorption kinetic data were analyzed by the first- and second-order kinetic equations. The adsorption property of MO of the α- and γ-alumina nanofibers was confirmed on the basis of the pseudo-second-order rate mechanism. Mesoporous alumina nanofibers prepared by electrospinning method can be successfully applied for the removal of dye pollutant from aqueous solutions.
References
Wu H, PAN W, LIN D, LI H: Electrospinning of ceramic nanofibers: fabrication, assembly and applications. Journal of Advanced Ceramics 2012, 1(1):2–23. 10.1007/s40145-012-0002-4
Li D, Xia Y: Electrospinning of nanofibers: reinventing the wheel? Adv Mater 2004, 16(14):1151–1170. 10.1002/adma.200400719
Yu H, Guo J, Zhu S, Li Y, Zhang Q, Zhu M: Preparation of continuous alumina nanofibers via electrospinning of PAN/DMF solution. Mater Lett 2012, 74: 247–249.
Azad AM, Noibi M, Ramachandran M: Fabrication of transparent alumina (Al2O3) nanofibers by electrospinning. Mater Sci Eng A 2006, 435–436: 468–473.
Panda PK, Ramakrishna S: Electrospinning of alumina nanofibers using different precursors. J Mater Sci 2007, 42: 2189–2193. 10.1007/s10853-007-1581-2
Mahapatra A, Mishra BG, Hota G: Synthesis of ultra-fine α-Al2O3 fibers via electrospinning method. Ceram Int 2011, 37: 2329–2333. 10.1016/j.ceramint.2011.03.028
Lotus AF, Feaver RK, Britton LA, Bender ET, Perhay DA, Stojilovic N, Ramsier RD, Chase GG: Characterization of TiO2–Al2O3 composite fibers formed by electrospinning a sol–gel and polymer mixture. Mater Sci Eng B 2010, 167: 55–59. 10.1016/j.mseb.2010.01.027
Yun S, Lim S: Improved conversion efficiency in dye-sensitized solar cells based on electrospun Al-doped ZnO nanofiber electrodes prepared by seed layer treatment. J Solid State Chem 2011, 184: 273–279. 10.1016/j.jssc.2010.11.024
Zhang R, Wu H, Lin D: Photocatalytic and magnetic properties of the Fe-TiO2/SnO2 nanofiber via electrospinning. J Am Ceram Soc 2010, 93: 605–608. 10.1111/j.1551-2916.2009.03456.x
Mimura KI, Moriya M, Sakamoto W, Yogo T: Synthesis of BaTiO3 nanoparticle/poly(2-hydroxyethyl methacrylate) hybrid nanofibers via electrospinning. Compos Sci Technol 2010, 70: 492–497. 10.1016/j.compscitech.2009.11.026
Maneeratana V, Sigmund WM: Continuous hollow alumina gel fibers by direct electrospinning of an alkoxide-based precursor. Chem Eng J 2008, 137: 137–143. 10.1016/j.cej.2007.09.013
Azad AM, Noibi M, Ramachandran M: Fabrication and characterization of 1-D alumina (Al2O3) nanofibers in an electric field. Bull Polish Acad Tech Scien 2007, 55(2):195–201.
Shanmugam M, Baroughi MF, Galipeau D: Effect of atomic layer deposited ultra thin HfO2 and Al2O3 interfacial layers on the performance of dye sensitized solar cells. Thin Solid Films 2010, 518: 2678–2682. 10.1016/j.tsf.2009.08.033
Huang K-C, Chen P-Y, Vittal R, Ho K-C: Enhanced performance of a quasi-solid-state dye-sensitized solar cell with aluminum nitride in its gel polymer electrolyte. Solar Energy Materials & Solar Cells 2011, 95: 1990–1995. 10.1016/j.solmat.2010.02.047
Wu S, Han H, Tai Q, Zhang J, Xu S, Zhou C, Yang Y, Hu H, Chen BL, Zhao XZ: Improvement in dye-sensitized solar cells employing TiO2 electrodes coated with Al2O3 by reactive direct current magnetron sputtering. J Power Sources 2008, 182: 119–123. 10.1016/j.jpowsour.2008.03.054
Favaro L, Boumaza A, Roy P, Ledion J, Sattonnay G, Brubach JB, Huntz AM, Tetot R: Experimental and ab initio infrared study of χ-, κ-, and α-aluminas formed from gibbsite. J Solid State Chem 2010, 183: 901–908. 10.1016/j.jssc.2010.02.010
Xu L, Song H, Chou L: Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol–gel strategy. Mater Chem Phys 2012, 132: 1071–1076. 10.1016/j.matchemphys.2011.12.069
Yu PC, Yang RG, Tsai YY, Sigmund W, Yen FS: Growth mechanism of single-crystal α-Al2O3 nanofibers fabricated by electrospinning techniques. J Eur Ceram Soc 2011, 31: 723–731. 10.1016/j.jeurceramsoc.2010.11.011
Kang W, Cheng B, Li Q, Zhuang X, Ren Y: A new method for preparing alumina nanofibers by electrospinning technology. Text Res J 2011, 81(2):148–155. 10.1177/0040517510377831
Chen Y, Liu S, Wang G: Kinetics and adsorption behavior of carboxymethyl starch on α-alumina in aqueous medium. J of Colloid and Interface Science 2006, 303: 380–387. 10.1016/j.jcis.2006.08.011
Ho YS, McKay G: Pseudo-second order model for sorption processes. Process Biochem 1999, 34: 451–465. 10.1016/S0032-9592(98)00112-5
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
J-HK, S-JY, D-HK, H-JJ, T-YK, and K-HP participated in the material preparation and data analysis. J-WL drafted the manuscript. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Kim, JH., Yoo, SJ., Kwak, DH. et al. Characterization and application of electrospun alumina nanofibers. Nanoscale Res Lett 9, 44 (2014). https://doi.org/10.1186/1556-276X-9-44
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-44