Abstract
Serving as shape control agent, polyvinyl pyrrolidone (PVP) has been widely used in chemical synthesis of metal nanoparticles. However, the role of molecular weight (MW) of PVP has been rarely concerned. In this study, we show a facile method to control the shapes of silver nanocrystals using PVP with different MWs. PVPMW=8,000, PVPMW=29,000, PVPMW=40,000, and PVPMW=1,300,000 are compared in the present study. Surprisingly, high-yield silver rodlike nanostructures, nanospheres, and nanowires can be obtained under the same growth environment and reactant concentrations by simply changing the MW of PVP. The mechanism studies of the role of PVP with different MWs in the growth process were carried out systemically using the morphology and spectroscopic measurement, FT-IR spectrum analysis, and seed crystallization monitoring. The results indicate that the MW of PVP plays a determinant role in the morphology and optical property control of the silver nanocrystals. Meantime, the concentration of PVP was found to be an assistant factor to further improve the shape and the yield of the synthesized nanocrystals.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
The synthesis of metal nanoparticles with high uniformity attracts considerable attentions due to their fantastic optical properties arising from localized surface plasmon resonance (LSPR) [1–3]. Such plasmonic nanoparticles, especially silver, are widely used in catalysis [4, 5], biological and chemical sensors [6–8], and surface-enhanced Raman spectroscopy [9–11]. It has been recognized that the optical spectral signatures of plasmonic nanoparticles are primarily dependent on their shapes [12–14]. Leading works in the synthesis of silver nanoparticles have focused on the shape control of silver nanocrystals via various routes. Wiley et al. [15] controlled the shapes of silver nanocrystals by varying reaction conditions such as the precursor concentration, molar ratio of the surfactant, and silver ions. As well known, the final structure of the nanocrystals are mainly determined by the crystallinity of seeds produced in the early stage of the reaction. Xia's group prepared silver pentagonal nanowires, nanocubes, and bipyramids from multiply twinned decahedral seeds, single-crystalline seeds, and single-twinned seeds, respectively [16]. As for the crystals' control of seeds, Xia et al. introduced Cl- or Br- as etchants combined with oxygen to avoid the formation of undesired seeds [17]. Another factor that influences the shape uniformity of the nanocrystals is self-nucleation in the reaction process. Self-nucleation of reductive silver atoms usually blocks the seed growth process resulting in the formation of spherical by-productions. The solution to the problem is to decrease the reduction rate of silver ions. Zhang et al. [18] applied a weak reductant to control the reduction rate. Meantime, citrate ligands used can also decrease the reduction rate because of complexation between silver ions and citrate ligands. Using polyol reduction method in the presence of polyvinyl pyrrolidone (PVP), Sun and co-workers successfully prepared silver nanowires [19–22]. Alternatively, the addition of as-prepared seeds [19] in the initial growth step has been suggested to induce the formation of nanowires preferentially. However, these reaction processes are usually complex or difficult to control. Without fine control of reactant concentrations and growth process, the obtained silver nanowires are always in low yield accompanied by large amounts of by-products such as nanocubes or nanospheres growing from isotropic seeds. In these cases, the post processing, such as low rotation-rate centrifugation [20] or special separation technique [23] to purify nanowires, is usually indispensable. Therefore, it is highly desirable to develop a reliable and facile method for the synthesis of silver nanocrystals in high yield with uniform size.
In the polyol process, acting as stabilizer, PVP plays an important role in controlling the shape. Chou et al. [24] compared the ability of PVP to stabilize silver colloids in the presence of NaOH or Na2CO3. Liu et al. [25] also proposed that the crystal structure shape was related to the capping modes between PVP with different molecular weights (MWs) and silver nanocrystals. Although the changes arising from the addition of PVP with different MWs have been observed in previous works, the exact function of the MW of PVP on the formation of silver nanocrystals has not been clarified until now. In this work, we deeply studied the role of MW of PVP in the shape control of silver nanocrystals. According to optical spectroscopic analysis and statistic of the yield and average size of each product prepared by varying the MW and concentration of PVP, we obtained the relationship between the MW of PVP and preferential products. By analyzing the interaction between PVP with different MW and silver crystals by Fourier transform infrared (FT-IR)spectroscopy, we deduce the role of PVP in the nucleation and growth processes. The results suggest that we provide a facile and robust strategy for the synthesis of well-shaped silver nanocrystals in high yield.
Methods
Silver nitrate (AgNO3 99 + %), sodium chloride (NaCl), and ethylene glycol (EG) were all purchased from Nanjing Chemical Reagent Co. Ltd (Nanjing, People's Republic of China). Polyvinyl pyrrolidone (PVPMW=8,000, PVPMW=1,300,000) were purchased from Aladdin (Shanghai, People's Republic of China). PVPMW=29,000 and PVPMW=40,000 were purchased from Sigma-Aldrich (St. Louis, MO, USA).
We used a colloidal synthesis method improved from the literature [26]. The method is one of the main methods for silver nanowire preparation. However, we found that when PVPMW=40,000 was used in this method, there are always plenty of by-products such as nanospheres and nanocubes unless the reaction condition was strictly controlled. It provides us an opportunity to exhibit the role of MW and the concentration of PVP in the synthesis process using this method. In each synthesis, l-mL EG solution of AgNO3 (0.9 M) and 0.6-mL EG solution of NaCl (0.01 M) were added into 18.4-mL EG solution of PVP (0.286 M). Then, the mixture was refluxed at 185°C for 20 min. After these processes, the excess PVP and EG were removed by adding deionized water centrifuged at 14,000 rpm for 10 min, three times. The centrifugation ensures that all the products can be collected for the sake of statistics of shapes and size.
The morphologies of the prepared silver samples were observed by transmission electron microscopy (TEM; JEM-2100, JEOL Ltd., Akishima, Tokyo, Japan) and scanning electron microscopy (SEM; SIRION, Durham, NH, USA). FT-IR analysis was conducted on the FT-IR spectrum (NICOLET 5700, Thermo Fisher Scientific, Waltham, MA, USA). UV-visible near-infrared (NOR) spectra were recorded by a fiber-optic spectrometer (PG2000, Ideaoptics Technology Ltd., Shanghai, People's Republic of China).
Results and discussion
Morphology characterization
The experimental results shown in Figure 1 indicate that the MW of PVP plays a key role in the shape control of silver nanocrystals. Figure 1 shows a series of silver nanocrystals prepared in the presence of PVP with different MWs. The inset pictures were taken in a dark room under the exposure of white LED panel light from the bottom which is similar to natural light having a wide spectral range. Different colors of silver colloids corresponding to different morphologies can be observed easily. Figure 1a presents the rodlike silver nanostructures synthesized using PVPMW=8,000. As shown in Figure 1a, two or more silver nanorods are melded together randomly in several types such as end-to-end, end-to-side, or parallel nanojoint, which has potential applications in nanocircuits [27]. Such typical morphology corresponds to the white color colloids that can be seen from the photograph in the inset of Figure 1a. When PVPMW=29,000 was used, a generation of bright yellow-green colloids was observed as shown in the inset of Figure 1b. The SEM image indicates that such color corresponds to the formation of high-yield silver nanospheres with uniform size around 60 nm [28]. Apparently, it provides a facile method for the synthesis of monodisperse silver nanospheres with high uniformity using PVPMW=29,000. Colloids in the inset of Figure 1c appear to be a muddy and dark yellow color when PVPMW=40,000 was used which is similar to that of the inset in Figure 1b. The reason is that the two colloids both have absorption of blue light shown in extinction spectra which will be discussed in the next Section. A large number of nanoparticles and a small amount of nanowires are observed in Figure 1c. However, the morphologies of silver nanoparticles are irregular and the sizes are nonuniform. It indicates that monodisperse silver particles with uniform shape and size can be hardly obtained when PVPMW=40,000 was used as a capping agent in the current synthesis process. When PVPMW=1,300,000 was used, it can be seen clearly that high-yield (>90 %) silver nanowires were obtained, as shown in Figure 1d. The color of silver colloids is yellowish white, similar to the highly purified silver nanowire colloids obtained after cross-flow filtration [23]. Although the color in the inset of Figure 1d is similar to that of in Figure 1a, the extinction spectrum of rodlike nanocrystal has a broad scattering band from the visible to the near-infrared wavelengths, while the extinction spectrum of silver nanowire has absorption of short wavelength light leading to exhibiting yellowish white rather than white. Compared with the result of Tsuji et al. [26], we can synthesize silver nanowires in higher yield using a simpler and faster method which obviates bubbling O2 and controlling the heating up time from room temperature to 185°C.
The concentration dependence of PVP in the synthesis is also investigated. Table 1 presents the yield and average size of each product prepared by varying the concentrations of PVP with MWs of 29,000, 40,000, and 1,300,000. Figure 2 shows the SEM images of silver nanoparticles prepared at different concentrations of PVPMW=29,000. It can be observed that in Figure 2a, 15% silver nanowires and other various shapes of nanoparticles were obtained at a concentration of 0.143 M. When the concentration of PVP was 0.286 M, high-yield nanospheres with about 1% nanowires were prepared as shown in Figure 2b. Figure 2c shows that the average size of nanospheres was smaller with 0.572 M PVP due to the high concentration offering a stronger stable ability to prevent the aggregation of nanoparticles. The same trend can be seen in Figure 2d,e which shows the SEM images of silver nanoparticles obtained using PVPMW=40,000 with different concentrations of PVP. We found that the yield of silver nanowires was about 20%, 5%, and 1% at concentrations of 0.143, 0.286, and 0.572 M, respectively. Figure 2 indicates that with the increase of concentration of PVP, the shape and size of silver nanoparticles became more uniform. The reason may be that a higher concentration of PVP forms a thicker coating over the surface of silver nanoparticles leading to a weaker selective adsorption of PVP which induces isotropic growth into the nanospheres [29].
Figure 3 presents SEM images of silver nanocrystals obtained at different concentrations of PVP using PVPMW=1,300,000. By comparing three SEM images of Figure 3, one can see that the concentration of PVP has less influence on the yield of silver nanowires when PVPMW=1,300,000 was used. However, it is found that the concentration of PVP contributes to the control of diameter of the synthesized nanowire. In Figure 3a, there are short nanorods, long nanowires, and some nanoparticles (<10%). Figure 3b shows the yield of silver nanowires with uniform diameter and length increased to about 95% which is similar to the result shown in Figure 3c. From the above comparison study, it should be noted that varying the MWs of PVP is more efficient on the shape control of silver nanocrystals than varying the concentrations of PVP.
Optical property characterization
UV-visible NIR spectrophotometer can also be used to confirm the morphologies of silver nanocrystals. The resonance bands of the plasmonic nanocrystals are mainly dependent on the distribution of the electromagnetic field on the surface of the metal nanocrystals. In other words, metal nanoparticles with different shapes and sizes should have different optical signatures. Figure 4a exhibits the extinction spectra of the silver solution with different PVPs at 0.286 M. As shown in Figure 4a, the rodlike shape prepared with PVPMW=8,000 has a broad scattering band from the visible to the near-infrared wavelengths leading to the white color shown in the inset in Figure 1a. Because the structure joined together can trap light effectively [30], such rodlike nanostructure can be used as a hot spot. The extinction spectra of the silver nanostructure solution using PVPMW=29,000 have a main resonance peak at 430 nm and a shoulder peak at 360 nm corresponding to the nanosphere [17]. In comparison, that of PVPMW=40,000 exhibits a redshift and broader absorption range ascribed to the irregular shapes of the products. In the extinction spectrum of the solution with PVPMW=1,300,000, there are two resonance peaks at 390 and 350 nm belonging to the optical signature of silver nanowire [19].
Figure 4b,c,d shows the extinction spectra of the silver nanostructure solution obtained at different concentrations of PVPMW=29,000, PVPMW=40,000, and PVPMW=1,300,000, respectively. We find that when the concentration of PVP increases, the resonance peaks blue-shifted and extinction bands became narrow. The reason is that with the decrease of the nanoparticle size, the resonance peak will shift towards the shorter wavelength and uniform size will cause narrow extinction bands [31], which correspond to our experimental results.
Supporting evidence for the function of MW of PVP
In this section, we show the reason why PVP can affect the silver nanostructure, and it is because PVP prefers to adsorb on the (100) facets of silver nanocrystals in EG [32]. The interaction process can be given by Equation 1. To determine the strength of adsorption between Ag+ ions and different PVPs, we resort to FT-IR analysis. Figure 5 presents the FT-IR spectra of pure PVP and Ag/PVP. In the spectra of pure PVP, the absorption peak locates at around 1,660 cm-1 ascribed to the stretching vibration of C = O which is slightly dependent on the MW of PVP. Compared with the free C = O stretching band of pure PVP, the adsorption peaks of Ag/PVP all shift towards the lower wave number due to the coordination between Ag+ ions and carbonyl oxygen. The positions of free and coordinated C = O bands in Ag/PVP with four kinds of MW are shown in Table 2. Because the strength of the coordination interaction between Ag+ ions and PVP can be estimated in terms of the magnitude of band shifts [33], the sequence of the strength of the coordination interaction between Ag+ ions and PVP occurs as follows: PVPMW=1,300,000 > PVPMW=40,000 > PVPMW=8,000 > PVPMW=29,000. The larger extent of blue shift band indicates a stronger selective adsorption on the (100) facets of silver nanocrystals, which is one of the important factors giving rise to the different morphologies of silver nanocrystals produced with different PVPs. As can be seen in Figure 5a,c,d, there is a peak at about 880 cm-1 assigned to the breathing vibration of the pyrrolidone ring, indicating that the pyrrolidone ring may be tilted on the surface of silver nanowires [34]. In addition, in these three figures, the peak at 2,970 cm-1 ascribed to asymmetric stretching vibration of CH2 in the skeletal chain of PVP, which implies that the CH2 chain is close to the surface of silver nanowires. Therefore, the conformation of PVP makes the fine and close adsorption on the (100) facets of silver nanocrystals. Conversely, both peaks in Figure 5b are weak, leading to the formation of high-yield silver nanospheres which is consistent with the result shown in Figure 1b.
Another factor influencing the morphology of silver nanocrystals with different PVPs is the steric effect. Shorter chains of PVP cause a smaller steric effect which can combine PVP with silver nanoparticles in the colloid better but also results in incomplete coating of silver nanocrystals. In this case, silver nanocrystals may aggregate together. On the contrary, PVP with longer chains can protect silver nanocrystals from aggregation. However, a thicker coating on the surface of silver nanocrystals may decrease the strength of the coordination interaction between Ag+ ions and PVP.
Thus, considering the combined effect of chemical adsorption and steric effect, we can deduce the growth mechanism of silver nanocrystals with these four PVPs. The formation process of silver nanocrystals can be divided into three stages. In the first stage, Ag+ ions were reduced by EG following the reaction in Equations 2 and 3. Then, silver nucleus formed with the protection of PVP. As soon as the color of the solution changed, the seeds began to exit. The last step is the growth of silver nanocrystals with the protection of PVP:
It is well known that the morphologies of silver nanocrystals strongly depend on the seeds formed in the initial stage. In order to compare the seeds in the presence of different PVPs visually, we prepared seeds at 100°C at the PVP of 0.286 M without any change of other conditions. Figure 6 shows the silver nanoparticles prepared at 100°C with different PVPs. The shortest PVPMW=8,000 are easier to cover with the surface of silver nucleus than other PVPs because of the smallest steric effect resulting in a stronger adsorption interaction between the PVP and silver nucleus. However, PVPMW=8,000 has less power to go against the aggregation of nanoparticles; thus, in Figure 6a, these silver nanoparticles gathered together. With the increased temperature, some of the nanoparticles grew into nanowires while others aggregated into plates which can be observed in Figure 6e. Because the activity of the end of nanowires without coverage of PVP is high [35], it would be likely to form an end-to-end or end-to-side connection of silver nanowires, except that some silver nanowires may aggregate in a parallel way.
Compared with PVPMW=8,000, PVPMW=29,000 with longer chains is able to offer more protection against aggregation, but weakest selective adsorption of PVP on the (100) facets of silver nanocrystals leads to the formation of isotropic seeds. Hence, in Figure 6b, one can see seeds prepared at 100°C mainly involving quasi-spherical seeds. Finally, these seeds evolved into nanospheres. The moderate selective adsorption of PVPMW=40,000 on the (100) facets results in exits of anisotropic seeds such as nanoplate and twinned pentahedron as shown in Figure 6c. Because each facet has different growth resistances, in different conditions, silver seeds evolve into different shapes [16]. According to our observations, this is the main reason why PVPMW=40,000 is the commonest capping agent used for the preparation of silver nanoparticles. However, any undesired disturbance can greatly influence the morphologies of silver nanocrystals. For example, Tsuji et al. [26] demonstrated that there was a significant difference in the yield and average size of silver nanowires when they varied the reaction temperature or reaction atmosphere with PVPMW=40,000. As a result, although numerous nanocrystals have been obtained, PVPMW=40,000 is not the best choice for high-yield synthesis of silver nanocrystals due to limitations in production efficiency, yield, and reproducibility. PVPMW=1,300,000 has both the strongest interaction of PVP on the surface of silver nanocrystals and the ability of anti-agglomeration arising from longest chains, inducing the formation of twinned pentahedron seeds which can be observed in Figure 6d. According to the growth mechanism of silver nanowires reported by Xia et al. [29], twinned pentahedron seeds will evolve into nanowires finally.
Conclusions
In this study, we exhibit that the MW of PVP plays a critical role in the shape control of silver nanocrystals. The function of PVP on the shape control of silver nanocrystals can be discussed from two aspects: adsorption effect and steric effect. Results suggest that adsorption effect holds the dominated position in the selective adsorption of PVP on (100) facets of silver nanocrystals when the MW of PVP is very small, while with the increase of MW, the chemical adsorption gradually takes the place of the former. Therefore, different silver nanocrystals can be obtained by varying MWs of PVP. In addition, compared with the products obtained by varying the concentrations of PVP, we find that the MW of PVP plays a more efficient role in shape control. Our study on the effect of PVP with different MWs paves the way for the synthesis of silver monodisperse nanospheres and nanowires in high yield.
References
Personick ML, Langille MR, Zhang J, Wu J, Li S, Mirkin CA: Plasmon-mediated synthesis of silver cubes with unusual twinning structures using short wavelength excitation. Small 2013, 9: 1947–1953. 10.1002/smll.201202451
Zhang XY, Hu AM, Zhang T, Lei W, Xue XJ, Zhou YH, Duley WW: Self-assembly of large-scale and ultrathin silver nanoplate films with tunable plasmon resonance properties. ACS Nano 2011, 5: 9082–9092. 10.1021/nn203336m
Zhang X-Y, Zhang T, Hu A, Song Y-J, Duley WW: Controllable plasmonic antennas with ultra narrow bandwidth based on silver nano-flags. Appl Phys Lett 2012, 101: 153118. 10.1063/1.4759122
Butun S, Sahiner N: A versatile hydrogel template for metal nano particle preparation and their use in catalysis. Polymer 2011, 52: 4834–4840. 10.1016/j.polymer.2011.08.021
Harish S, Sabarinathan R, Joseph J, Phani KLN: Role of pH in the synthesis of 3-aminopropyl trimethoxysilane stabilized colloidal gold/silver and their alloy sols and their application to catalysis. Mater Chem Phys 2011, 127: 203–207. 10.1016/j.matchemphys.2011.01.060
Hong Y, Huh Y-M, Yoon DS, Yang J: Nanobiosensors based on localized surface plasmon resonance for biomarker detection. J Nanomater 2012, 2012: 1–13.
Stewart ME, Anderton CR, Thompson LB, Maria J, Gray SK, Rogers JA, Nuzzo RG: Nanostructured plasmonic sensors. Chem Rev 2008, 108: 494–521. 10.1021/cr068126n
Valsecchi C, Brolo AG: Periodic metallic nanostructures as plasmonic chemical sensors. Langmuir 2013, 29: 5638–5649. 10.1021/la400085r
Yang J, Wang Z, Zong S, Song C, Zhang R, Cui Y: Distinguishing breast cancer cells using surface-enhanced Raman scattering. Anal Bioanal Chem 2012, 402: 1093–1100. 10.1007/s00216-011-5577-z
Zhu SQ, Zhang T, Guo XL, Wang QL, Liu X, Zhang XY: Gold nanoparticle thin films fabricated by electrophoretic deposition method for highly sensitive SERS application. Nanoscale Res Lett 2012, 7: 613. 10.1186/1556-276X-7-613
Yang J, Wang Z, Tan X, Li J, Song C, Zhang R, Cui Y: A straightforward route to the synthesis of a surface-enhanced Raman scattering probe for targeting transferrin receptor-overexpressed cells. Nanotechnology 2010, 21: 345101. 10.1088/0957-4484/21/34/345101
Pietrobon B, Kitaev V: Photochemical synthesis of monodisperse size-controlled silver decahedral nanoparticles and their remarkable optical properties. Chem Mater 2008, 20: 5186–5190. 10.1021/cm800926u
Ray PC: Size and shape dependent second order nonlinear optical properties of nanomaterials and their application in biological and chemical sensing. Chem Rev 2010, 110: 5332–5365. 10.1021/cr900335q
Pignataro B, De Bonis A, Compagnini G, Sassi P, Cataliotti RS: The role of micro- and nanomorphology of rough silver surfaces of different nature in surface enhanced Raman scattering effect: a combined study of scanning force microscopy and low-frequency Raman modes. J Chem Phys 2000, 113: 5947. 10.1063/1.1311782
Wiley B, Sun YG, Mayers B, Xia YN: Shape-controlled synthesis of metal nanostructures: the case of silver. Chemistry 2005, 11: 454–463. 10.1002/chem.200400927
Wiley B, Sun YG, Xia YN: Synthesis of silver nanostructures with controlled shapes and properties. Acc Chem Res 2007, 40: 1067–1076. 10.1021/ar7000974
Wiley BJ, Im SH, Li ZY, McLellan J, Siekkinen A, Xia YN: Maneuvering the surface plasmon resonance of silver nanostructures through shape-controlled synthesis. J Phys Chem B 2006, 110: 15666–15675. 10.1021/jp0608628
Zhang Q, Hu Y, Guo S, Goebl J, Yin Y: Seeded growth of uniform Ag nanoplates with high aspect ratio and widely tunable surface plasmon bands. Nano Lett 2010, 10: 5037–5042. 10.1021/nl1032233
Sun YG, Yin YD, Mayers BT, Herricks T, Xia YN: Uniform silver nanowires synthesis by reducing AgNO3 with ethylene glycol in the presence of seeds and poly(vinyl pyrrolidone). Chem Mater 2002, 14: 4736–4745. 10.1021/cm020587b
Sun YG, Xia YN: Large-scale synthesis of uniform silver nanowires through a soft, self-seeding, polyol process. Adv Mater 2002, 14: 833–837. 10.1002/1521-4095(20020605)14:11<833::AID-ADMA833>3.0.CO;2-K
Sun YG, Gates B, Mayers B, Xia YN: Crystalline silver nanowires by soft solution processing. Nano Lett 2002, 2: 165–168. 10.1021/nl010093y
Korte KE, Skrabalak SE, Xia YN: Rapid synthesis of silver nanowires through a CuCl- or CuCl2-mediated polyol process. J Mater Chem 2008, 18: 437–441. 10.1039/b714072j
Pradel KC, Sohn K, Huang J: Cross-flow purification of nanowires. Angew Chem Int Ed Engl 2011, 50: 3412–3416. 10.1002/anie.201100087
Chou KS, Lai YS: Effect of polyvinyl pyrrolidone molecular weights on the formation of nanosized silver colloids. Mater Chem Phys 2004, 83: 82–88. 10.1016/j.matchemphys.2003.09.026
Liu XH, Zhang F, Huang R, Pan CF, Zhu J: Capping modes in PVP-directed silver nanocrystal growth: multi-twinned nanorods versus single-crystalline nano-hexapods. Cryst Growth Des 2008, 8: 1916–1923. 10.1021/cg701128b
Tang X, Tsuji M, Jiang P, Nishio M, Jang S-M, Yoon S-H: Rapid and high-yield synthesis of silver nanowires using air-assisted polyol method with chloride ions. Colloids Surf A Physicochem Eng Asp 2009, 338: 33–39. 10.1016/j.colsurfa.2008.12.029
Chen D, Gao L: Large-scale growth and end-to-end assembly of silver nanorods by PVP-directed polyol process. J Cryst Growth 2004, 264: 216–222. 10.1016/j.jcrysgro.2003.12.019
Li H, Xia H, Wang D, Tao X: Simple synthesis of monodisperse, quasi-spherical, citrate-stabilized silver nanocrystals in water. Langmuir 2013, 29: 5074–5079. 10.1021/la400214x
Sun YG, Mayers B, Herricks T, Xia YN: Polyol synthesis of uniform silver nanowires: a plausible growth mechanism and the supporting evidence. Nano Lett 2003, 3: 955–960. 10.1021/nl034312m
Zhang XY, Zhang T, Zhu SQ, Wang LD, Liu X, Wang QL, Song YJ: Fabrication and spectroscopic investigation of branched silver nanowires and nanomeshworks. Nanoscale Res Lett 2012, 7: 596. 10.1186/1556-276X-7-596
Li L, Sun J, Li X, Zhang Y, Wang Z, Wang C, Dai J, Wang Q: Controllable synthesis of monodispersed silver nanoparticles as standards for quantitative assessment of their cytotoxicity. Biomaterials 2012, 33: 1714–1721. 10.1016/j.biomaterials.2011.11.030
Tsuji M, Tang X, Matsunaga M, Maeda Y, Watanabe M: Shape evolution of flag types of silver nanostructures from nanorod seeds in PVP-assisted DMF solution. Cryst Growth Des 2010, 10: 5238–5243. 10.1021/cg101041m
Kim JH, Min BR, Kim CK, Won J, Kang YS: Spectroscopic interpretation of silver ion complexation with propylene in silver polymer electrolytes. J Phys Chem B 2002, 106: 2786–2790. 10.1021/jp010481o
Gao Y, Jiang P, Liu DF, Yuan HJ, Yan XQ, Zhou ZP, Wang JX, Song L, Liu LF, Zhou WY, Wang G, Wang CY, Xie SS, Zhang JM, Shen AY: Evidence for the monolayer assembly of poly(vinylpyrrolidone) on the surfaces of silver nanowires. J Phys Chem B 2004, 108: 12877–12881. 10.1021/jp037116c
Peng P, Liu L, Gerlich AP, Hu A, Zhou YN: Self-oriented nanojoining of silver nanowires via surface selective activation. Particle & Particle Systems Characterization 2013, 30: 420–426. 10.1002/ppsc.201200099
Acknowledgements
This work is supported by NSFC under grant number 61307066, Doctoral Fund of Ministry of Education of China under grant numbers 20110092110016 and 20130092120024, Natural Science Foundation of Jiangsu Province under grant number BK20130630, the National Basic Research Program of China (973 Program) under grant number 2011CB302004, and the Foundation of Key Laboratory of Micro-Inertial Instrument and Advanced Navigation Technology, Ministry of Education, China under grant number 201204.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
YJS carried out the main part of synthetic and analytic works and drafted the manuscript. XYZ and JYW participated in synthetic and analytic works. MLW and TZ participated in the discussion of experimental details and participated in the draft preparation. All authors read and approved the final manuscript.
Yuan-Jun Song, Xiao-Yang Zhang, Jing-Yuan Wu contributed equally to this work.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Song, YJ., Wang, M., Zhang, XY. et al. Investigation on the role of the molecular weight of polyvinyl pyrrolidone in the shape control of high-yield silver nanospheres and nanowires. Nanoscale Res Lett 9, 17 (2014). https://doi.org/10.1186/1556-276X-9-17
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-17