We have investigated the characteristics of a silicon oxynitride/silver/silicon oxynitride [SiON/Ag/SiON] multilayer passivation grown using a specially designed roll-to-roll [R2R] sputtering system on a flexible polyethersulfone substrate. Optical, structural, and surface properties of the R2R grown SiON/Ag/SiON multilayer were investigated as a function of the SiON thickness at a constant Ag thickness of 12 nm. The flexible SiON/Ag/SiON multilayer has a high optical transmittance of 87.7% at optimized conditions due to the antireflection and surface plasmon effects in the oxide-metal-oxide structure. The water vapor transmission rate of the SiON/Ag/SiON multilayer is 0.031 g/m2 day at an optimized SiON thickness of 110 nm. This indicates that R2R grown SiON/Ag/SiON is a promising thin-film passivation for flexible organic light-emitting diodes and flexible organic photovoltaics due to its simple and low-temperature process.
Rapid progress in organic-based flexible optoelectronics such as flexible organic light-emitting diodes [OLEDs] and organic photovoltaics [OPVs] required a high-performance thin-film passivation because both lifetime and performance of the flexible OLEDs and OPVs are critically affected by the quality of the encapsulation [1–3]. The long-term stability of flexible OLEDs and OPVs is still limited due to the instability of the luminescent organic materials and low work function metals, interfacial reactions, and chemical reactions of the organic layers with oxygen and moisture in air . For those reasons, several types of encapsulation techniques have been extensively explored to improve the long-term stability of flexible OLEDs or OPVs. In particular, thin-film passivation has been considered as the most desirable encapsulation for flexible OLEDs and OPVs due to its simplicity, thinness, and flexibility. Although various SiNx, SiOx, SiOxNy, AlOx, and Al2O3:N films have been reported, a single-layer-based thin-film passivation is not sufficiently dense to protect flexible optoelectronic devices from permeation by moisture and oxygen [5–9]. Therefore, multilayer passivation, such as Barix coating or NONON (SiNx/SiO2/SiNx/SiO2/SiNx) structures, has been proposed as a means to achieve ultra high barrier properties for flexible OLEDs or OPVs [10, 11]. However, Barix coating or the NONON structure still has not been employed in mass production of OLEDs due to its complicated process and long process time. We also reported that Al2O3/Ag/Al2O3 multilayer thin-film passivation has a high transmittance of 86.44% and a low water vapor transmission rate [WVTR] due to the SPR effects of the Ag interlayer and the effective multilayer structure that prevent the intrusion of water vapor . In a multilayer barrier, control of the Ag thickness is very important because the antireflection effect for high transparency is critically dependent on the thickness and morphology of the inserted Ag layer. However, a roll-to-roll [R2R] sputter-grown silicon oxynitride/silver/silicon oxynitride [SiON/Ag/SiON] multilayer has not been investigated for thin-film passivation even though it has various advantages such as high transparency and possibility of a simple R2R process.
In this work, we report on the characteristics of SiON/Ag/SiON multilayer passivation grown on a flexible polyethersulfone [PES] substrate using a specially designed R2R sputtering system. Optical, structural, and surface properties of the R2R-grown SiON/Ag/SiON multilayer were investigated as a function of the SiON thickness. Despite the low process temperature used, a SiON/Ag/SiON multilayer passivation showed a low WVTR of 0.031 g/m2 day and a high transmittance of 87.7% at an optimized SiON thickness of 110 nm.
The flexible SiON/Ag/SiON multilayer was sputtered on a flexible PES substrate as a function of the SiON thickness using a continuous R2R sputtering system as shown in Figure 1a. The SiON ceramic and Ag metal targets were placed at a distance of 100 mm from the PES substrate, mechanically contacted on the cooling drum. Before the sputtering of the bottom SiON layer, a flexible PES substrate was pretreated with Ar ion beam treatment at a DC-pulsed power of 100 W to enhance adhesion between the PES substrate and the bottom SiON layer. After the ion beam treatment, the bottom SiON layer was sputtered on the PES substrate at a constant base pressure of 1.0 × 10-6 Torr, a working pressure of 3 mTorr, an Ar/O2 flow rate of 30/2 sccm, and a rolling speed of 0.1 cm/s as a function of the SiON target RF power. Subsequently, a constant Ag layer was sputtered on the bottom SiON layer using a DC power of 350 W. The top SiON layer was sputtered on the Ag layer with identical sputtering conditions used for the bottom SiON layer. As shown in Figure 1a, the SiON/Ag/SiON multilayer was continuously deposited without breaking the vacuum in the R2R sputter system. Figure 1b showed the schematic structure of the SiON/Ag/SiON multilayer sputtered on the PES substrate. The thickness of the SiON/Ag/SiON multilayer was measured by a surface profilometer. The optical transmittance of the SiON/Ag/SiON multilayer was measured in a wavelength range from 300 to 1100 nm using a UV/Visible spectrometer as a function of the SiON thickness. In addition, the surface morphology of the top SiON layer in the SiON/Ag/SiON multilayer was investigated by a field emission scanning electron microscope [FESEM]. Moreover, the structural properties of the SiON/Ag/SiON multilayer were examined by X-ray diffraction [XRD] and high resolution transmission electron microscope [HRTEM]. Furthermore, the WVTR value for the SiON/Ag/SiON multilayer passivation grown on the flexible PES substrate (50 mm × 50 mm) was measured by a MOCON tester (PERMATRAN-W Model 3/33, MOCON Inc., Minneapolis, MN, USA) for 20 h. The calibration was conducted using a standard sample supported by MOCON under a flow of 10 sccm water vapor at 37.8°C.
Results and discussion
Figure 2 shows the optical transmittance of the SiON/Ag/SiON multilayer, with an Ag thickness of 12 nm, grown on the flexible PES substrate as a function of the top and bottom SiON thicknesses of layers from 50 to 130 nm at a constant Ag thickness. It was found that the optical transmittance of the SiON/Ag/SiON multilayer electrode was dependent on the thickness of the SiON layer. The SiON/Ag/SiON multilayers with SiON thicknesses of 50 to 130 nm show a similar optical transmittance. However, the SiON/Ag/SiON multilayer with a SiON thickness of 110 nm shows an abrupt increase in optical transmittance up to 87.7% at a 550-nm wavelength region due to the antireflection and surface plasmon resonance effects caused by the oxide-metal-oxide multilayer structure [12, 14]. However, a further increase in the SiON thickness (130 nm) leads to the decrease of transmittance.
Figure 3 shows the XRD results of SiON/Ag/SiON electrodes as a function of the SiON thickness, with an inset of the cross-sectional HRTEM image of the optimized SiON/Ag/SiON multilayer. All XRD plots of the flexible SiON/Ag/SiON multilayer show only broad peaks at regions 40° to 50° regardless of the SiON thickness, which is indicative of an amorphous structure of SiON layer. Due to the resolution limit of our XRD system, the Ag (12 nm) peak was not detected. Because the PES substrate temperature is effectively kept low during the continuous sputtering process by the cooling drum, all the SiON layers show amorphous structures. As a barrier layer, the amorphous structure is beneficial because there are no paths for intrusion of humidity and oxygen gas. In addition, mechanical properties of the amorphous structure are more robust than that of the crystalline structure when it bent. The cross-sectional images clearly demonstrate well-defined bottom SiON, Ag, and top SiON layers without interface layers. These sharp interfaces indicate that there were no interface reactions and no formation of interfacial oxide layers between the SiON and Ag layers. Moreover, the uniform contrast of the SiON layers indicates that the structures of SiON were completely amorphous as expected from XRD results. However, the inserted Ag layer existed in crystalline form which is inconstant with the XRD results. Although the Ag peak did not appear in the XRD plot due to resolution limitation, the Ag layer had a crystalline structure as reported previously in the OMO structure [12–14].
Figure 4 shows the surface morphology of the top SiON layer as a function of its thickness at a constant Ag thickness of 12 nm. The R2R sputter-grown SiON top layer showed a fairly rough surface morphology. An increase of the SiON thickness from 70 to 130 nm resulted in a rough surface of the top SiON layer. The rough surface of the top SiON layer could be attributed to the high kinetic energy of sputtered SiON particles and reaction with nitrogen of the SiON film with oxygen ambient during the sputtering process. All samples showed an island-like agglomeration on the surface of the top SiON layer.
Figure 5 shows the WVTR value of the SiON/Ag/SiON multilayer passivation grown on the flexible PES substrate as a function of both top and bottom SiON thicknesses. Due to the small size of the SiON/Ag/SiON multilayer samples, the WVTR values for all multilayer passivation were measured by packaging the samples as it is shown in the inset picture. As shown in Figure 5, the WVTR value of the SiON/Ag/SiON multilayer depends on the thickness of the SiON layers. As the SiON thickness in the SiON/Ag/SiON multilayer increases, the WVTR value monotonically decreases because both SiON layers can effectively prevent the intrusion of water vapor. Compared with the WVTR value (0.306 g/m2 day) of the SiON thickness of 50 nm, the WVTR value (0.031 g/m2 day) of the SiON/Ag/SiON multilayer with a SiON thickness of 110 nm is much lower. However, a further increase of the SiON thickness leads to an increase of the WVTR value. The increase in WVTR value of the SiON/Ag/SiON with the 130-nm-thick SiON layer could be attributed to the rough surface as shown in Figure 4d. This rough surface with island-like agglomerated subgrains could lead to the formation of a diffusion path for oxygen atoms or moisture from the surface to the substrate. This rough surface is caused by a chemical reaction of the SiON and oxygen ambient. Due to different bond enthalpies of Si-O (799.6 kJ/mol), O-O (498.4 kJ/mol), N-N (945.3 kJ/mol), and Si-N (470 kJ/mol), the formation of Si-O and N-N bonds are energetically favorable during sputtering of the SiON target in an oxygen ambient. Therefore, the presence of an oxygen ambient leads to the ejection of diatomic nitrogen into the ambient from the SiON target, and this resulted in a SiOx film with a very rough surface morphology. Considering the optical transparency and WVTR value, we decided the optimized thickness value of the top and bottom SiON layers as 110 nm. Compared to a previously reported WVTR value of multilayer thin-film passivation , the SiON/Ag/SiON multilayer passivation showed a higher value due to the rough surface morphology of the SiON layers as shown in Figure 4. Therefore, we believe that further optimization of the top SiON morphology and density could improve the performance of the SiON/Ag/SiON multilayer passivation.
SiON/Ag/SiON multilayer passivation prepared by continuous R2R sputtering was investigated as a function of the top and bottom SiON thickness. The SiON/Ag/SiON multilayer thin-film passivation on the PES substrate has a high transmittance of 87.7% and a low WVTR due to the antireflection and surface plasmon effects of the Ag interlayer and the effective multilayer structure that prevent the intrusion of water vapor. At a SiON thickness of 110 nm, the R2R-grown SiON/Ag/SiON multilayer showed a WVTR value of 0.031 g/m2 day. These findings indicate that R2R-grown SiON/Ag/SiON is a promising thin-film passivation for flexible OLEDs and OPVs due to its simple and low-temperature process.
Lewis JS, Weaver MS: Thin-film permeation-barrier technology for flexible organic light-emitting devices. IEEE J of Sel Top Quantum Electron 2004, 10: 45–57. 10.1109/JSTQE.2004.824072
Kim N, Potscavage WJ, Domercq B, Kippelen B, Raham S: A hybrid encapsulation method for organic electronics. Appl Phys Lett 2009, 94: 163308(1)-163308(3).
Kim KJ, Kim YS, Bae JJ, Kang BH, Yeom SH, Yuan H, Kang SW: Passivation films with SU-8 polymers for organic solar cell protection from ultraviolet ray. Sol Energy Mater Solar Cells 2011, 95: 1238–1242. 10.1016/j.solmat.2010.12.050
Schaer M, Nuesch F, Berner D, Leo W, Zuppiroli L: Water vapor and oxygen degradation mechanisms in organic light emitting diodes. Adv Funct Mater 2001, 11: 116–121. 10.1002/1616-3028(200104)11:2<116::AID-ADFM116>3.0.CO;2-B
Lin H, Xu L, Chen X, Wang X, Sheng M, Stubhan F, Merkel KH, Wilde J: Moisture-resistant properties of SiNxfilms prepared by PECVD. Thin Solid Films 1998, 333: 71–76. 10.1016/S0040-6090(98)00812-8
Kim HK, Kim SW, Kim DG, Kang JW, Kim MS, Cho WJ: Thin film passivation of organic light emitting diodes by inductively coupled plasma chemical vapor deposition. Thin Solid Films 2007, 515: 4758–4762. 10.1016/j.tsf.2006.11.030
Kim HK, Kang JW, Kim JJ, Yi MS: High-quality thin-film passivation by catalyzer-enhanced chemical vapor deposition for organic light-emitting diodes. Appl Phys Lett 2007, 90: 013502(1)-013052(3).
Chen TN, Wuu DS, Wu CC, Chiang CC, Chen YP, Horng RH: High-performance transparent barrier films of SiOx/SiNxstacks on flexible polymer substrates. J Electrochem Soc 2006, 153: F244-F248. 10.1149/1.2335592
Yun SJ, Ko YW, Lim JW: Passivation of organic light-emitting diodes with aluminum oxide thin films grown by plasma-enhanced atomic layer deposition. Appl Phys Lett 2004, 85: 4896–4898. 10.1063/1.1826238
Weaver MS, Michalski LA, Rajan K, Rothman MA, Silvernail JA, Burrows PE, Graff GL, Gross ME, Martin PM, Hall M, Mast E, Bonham C, Bennett W, Zumhoff M: Organic light-emitting devices with extended operating lifetimes on plastic substrates. Appl Phys Lett 2002, 81: 2929–2931. 10.1063/1.1514831
Chwang AB, Rothman MA, Mao SY, Hewitt RH, Chu X, Moro L, Trajewski T, Rutherford N: Thin film encapsulated flexible organic electroluminescent displays. Appl Phys Lett 2003, 83: 413–415. 10.1063/1.1594284
Jeong JA, Kim HK, Yi MS: Effect of Ag interlayer on the optical and passivation properties of flexible and transparent Al2O3/Ag/Al2O3multilayer. Appl Phys Lett 2008, 93: 033301(1)-033301(3).
Park YS, Kim HK: Flexible indium zinc oxide/Ag/indium zinc oxide multilayer electrode grown on polyethersulfone substrate by cost-efficient roll-to-roll sputtering for flexible organic photovoltaics. J Vac Sci Technol A 2010, 28: 41–47. 10.1116/1.3264464
Fan JC, Bachner FJ, Foley GH, Zavracky PM: Transparent heat-mirror films of TiO2/Ag/TiO2for solar energy collection and radiation insulation. Appl Phys Lett 1974, 25: 693–695. 10.1063/1.1655364
This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (2010-0015596) and partially supported by Gyeonggi-do International Collaborative Research Program.
The authors declare that they have no competing interests.
CKC carried out the R2R sputtering process and analysis of the SiON/Ag/SiON multilayer passivation layer. HKK designed the experiments and wrote the manuscript. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Kim, HK., Cho, CK. Transparent SiON/Ag/SiON multilayer passivation grown on a flexible polyethersulfone substrate using a continuous roll-to-roll sputtering system. Nanoscale Res Lett 7, 69 (2012). https://doi.org/10.1186/1556-276X-7-69
- Water Vapor Transmission Rate
- SiON Layer
- Rough Surface Morphology
- Surface Plasmon Resonance Effect
- Surface Plasmon Effect