Abstract
For InAs/GaAs(001) quantum dot (QD) system, the wetting layer (WL) evolution and its temperature dependence were studied using reflectance difference spectroscopy and were analyzed with a rate equation model. WL thicknesses showed a monotonic increase at relatively low growth temperatures but showed an initial increase and then decrease at higher temperatures, which were unexpected from a thermodynamic understanding. By adopting a rate equation model, the temperature dependence of QD formation rate was assigned as the origin of different WL evolutions. A brief discussion on the indium desorption was given. Those results gave hints of the kinetic aspects of QD self-assembly.
Avoid common mistakes on your manuscript.
Background
Epitaxial semiconductor quantum dots (QDs) have attracted much attention because of their application potential in novel optoelectronic devices [1–3]. They are usually fabricated utilizing the lattice mismatch between the epitaxial layer and substrate or the Stranski-Krastanov (SK) growth mode. It can be described as follows: for small coverage, two-dimensional (2D) layer-by-layer growth and pseudomorphic formation of wetting layer (WL) take place. When the WL reaches a certain critical thickness (CT), a 2D to three-dimensional (3D) transition starts, and QDs form on the substrate. QDs with high homogeneity in their size and shape are highly advantageous in applications. Basically, the WL configuration would also influence the optical properties of QDs and the performance of QD-based devices [4–7]. A controllable growth of QDs with desired properties requires a comprehensive understanding on the growth process. Therefore, it is necessary to have a clear understanding of the WL evolution during the QD self-assembly.
The commonly accepted thermodynamic understanding of the SK mode describes the QD formation on top of a WL of a certain thickness. However, it is not accurate in real situations. It has been reported that in the Ge/Si QD system, the WL thickness decreases after QD formation [8–10]. It is interpreted in the regime of kinetically controlled QD formation and growth. Since material transfer from WL to QDs sustains the QD formation and growth, a large material consumption rate by QD formation may induce the observed WL erosion [8, 9]. As for InAs/GaAs system, a step erosion of WL has also been observed after QD formation [11, 12]. Until now, there is no complete description of the WL evolution and its growth condition dependence. In our previous work, reflectance difference spectroscopy (RDS) was used to study the WLs in self-assembled nanostructures. Due to its sensitivity, heavy hole (HH)- and light hole (LH)-related transition energies before and after QD formation can be directly obtained from the resonant structures in the spectra [13–16]. In this paper, we studied the WL evolution and its temperature dependence based on RDS measurements. We found that, generally, there were two kinds of WL evolution, with deposition depending on growth temperatures. They were well explained in the regime of temperature dependence of QD growth rate with a rate equation model. The concave-up style of evolution was considered as a clear evidence for a non-zero QD growth rate when the WL thickness was smaller than the CT. We also gave a simple discussion on indium desorption during self-assembly. All of these results showed the kinetic aspects of WL evolution in the SK growth.
Methods
Six InAs/GaAs(001) QD samples with different growth temperatures (from 490°C to 540°C, with an increment of 10°C) were grown in our Riber-32p molecular beam epitaxy (MBE) system. A 100-nm GaAs buffer layer was firstly deposited on 2-in semi-insulating GaAs substrates at 600°C. A nominal InAs amount of 2.0 monolayer (ML) (1.9 ML for the sample grown at 510°C) was then deposited with a calibrated rate of 0.1 ML/s at a controlled substrate temperature. A gradually changed InAs amount was achieved by stopping the substrate rotation. This method was widely used in studying the QD growth dynamics and to fabricate QD samples with low areal density [8, 10, 13, 17]. The effective indium flux and real deposition amount could be calibrated based on the cosine law for certain configurations of the MBE source beam [18]. Growth interruption (GI) of 10 s was introduced after InAs layer deposition. A 100-nm GaAs capping layer was then grown at 600°C. Details of the sample growth processes can be found in another study [16]. For further spectroscopy measurements, the samples were cut into 16 pieces along the direction corresponding to which the InAs amount increased gradually. To evaluate the WL information, the relative reflectance difference in the sample surface plane, i.e., , was measured with the RDS technique in ambient conditions. The setup of our RDS was reported elsewhere [19].
Results and discussion
Figure 1a shows the intensity map of the second-derivative spectra obtained from the samples grown at 530°C, in which the distinctive features of the GaAs band edge, LH and HH, of the WLs can be distinguished. For the horizontal axis, the InAs deposition rate is calibrated with the cosine law mentioned above. One can see the LH and HH transition energies redshift almost linearly up to an InAs deposition rate of 0.085 ML/s (corresponding to an InAs amount of 1.7 ML), which is commonly known as the CT of InAs QD formation, then gradually saturate for further deposition. In order to have an intuitive understanding on the evolution, we calibrate the WL thicknesses based on the transition energies obtained from the spectra [20]. Figure 1b gives the WL thickness evolution of the six samples. The WL thicknesses are signed with open symbols for 2D growth stage and solid symbols for 3D growth stage based on our previous results [16]. In general, two distinct evolution processes can be discerned. An initially increased and then saturated evolution mode was observed in the samples grown at lower temperatures, while distinct concave-up features of the WL evolution for samples with relatively higher growth temperatures appeared right after QD formation. They are unexpected based on thermodynamic understanding of the SK growth, for which a stable WL thickness is expected during and after QD formation. There is another decrease of the WL thickness for the last three pieces of each sample. The generation of large QDs, dislocation during the QD ripening process, and the enhanced indium absorption abilities by them can be accounted for the decrease [14, 21].
In describing the WL growth dynamics, we consider three main InAs distribution processes. The newly deposited InAs can be incorporated into the WL and QDs or re-evaporated through the indium desorption process. Other processes, such as the formation of quasi-QDs or indium droplets, are neglected for their relatively lower rates [22, 23]. In our previous works, the CTs of those samples were successfully determined, which enabled us to consider the 2D and 3D growth stages separately in this rate equation model [16]. For 2D growth stage, the deposited material contributes to a pseudomorphic growth of the WL and the formation of QDs is neglected. Based on material balance, the rate equation can be written as follows:
where θ is the WL thickness, t c is the time of the 2D growth stage, and G is the InAs deposition rate. The indium desorption rate is presumed to be proportional to the InAs amount in WL, and τ des represents the desorption time constant. The indium desorption process is generally considered as thermally activated [23, 24]; τ des can be written as , where v0 is a pre-exponential factor and E des is the activation energy of the indium desorption process. By solving Equation 1, the WL thickness versus growth time can be written as follows:
Above the CT, a large amount of QDs appears, and the newly deposited InAs are mainly consumed by them. The rate equation can be written as follows:
Here F QD is used to represent the InAs consumption rate by the QD formation and growth [25]. F QD is determined by the instability of WL and the material diffusion from WL to QDs [26]. The diffusion rate can be written as D In = (2k B T / h) exp (−E dif / k B T), [26] where k B is Boltzmann's constant, h is Planck's constant, T is the substrate temperature and E dif is the energy barrier. In previous works, for a WL thickness of θ, the instability of WL is commonly considered as (θ − θ c ). The driving force of QD growth, which is known as ‘superstress’, is defined as ξ = (θ − θ c ) / θ c [27]. However, it is not suitable in describing our experimental results. The concave-up style of evolution shown in the upper panel of Figure 1b means a non-zero QD growth rate when the WL thickness is slightly below the CT, or else, the WL thickness would not reduce below the CT in the presence of sufficient InAs supply. A non-stopping QD formation when the WL thickness is smaller than the CT is also documented in previous experiments [28–30]. Hence, the unstable part of WL is written as (θ − αθ c ), (0 < α < 1); correspondingly, the superstress is written as ξ = (θ − αθ c ) / αθ c (0 < α < 1). The QD formation and growth rate γ is considered to be exponentially dependent on the superstress or γ = b exp (βξ), where b and β were constant parameters [31, 32]. Consequently, F QD can be written as follows:
From Equation 3, it is clear that an equilibrium WL thickness is reached when the deposition rate equals to the WL consumption rate by QD formation and indium desorption. The last two processes show strong temperature dependence. Thus, in principle, WL growth has deposition rate and temperature dependences. WL growth dynamics at different conditions can be obtained from Equation 2 and by solving Equation 3 numerically. The calculation results for two different temperatures, and varied deposition rates are shown in Figure 2. The 2D to 3D transition (where the WL thickness exceeds the CT) will not necessarily appear during the growth, depending on the deposition rate and time. Generally speaking, firstly, the WL thickness shows a nearly linear increase and then is saturated after QD formation. After that, the newly deposited InAs is mainly consumed by the formation of QDs. WL growth tends to reach equilibrium. The larger the InAs deposition rate is, the thicker the steady-state WL. Concerning the influence of growth temperature, distinct differences can be found by comparing the 3D growth stage in Figure 2a,b. For the low-temperature case, the WL thickness increases to equilibrium values which are always above the CT. On the other hand, for high-temperature grown samples, they show WL erosion at the beginning of the 3D growth stage, and WL thicknesses stable at values smaller than the CT. WL erosion disappears by increasing the deposition rates. According to Equation 3, the appearance of WL erosion (dθ / dt < 0) resulted from the temperature dependence of QD formation rate, F QD . WL thickness would suffer a decrease if the deposition rate is not large enough to sustain the QD growth at the beginning of the 3D evolution stage. F QD then drops correspondingly according to its dependence on the superstress. It takes some time for the WL thickness to be stable to a certain value, for which the material deposition and the QD growth reach a balance. The bigger the deposition rate is, the thicker the stabilized WL. However, if the QD formation rate for the critical WL thickness is lower than the corresponding deposition rate, e.g., a lower growth temperature, WL thickness would keep on increasing after QD formation, which is the case in Figure 2a.
To understand the experimental results, we have to apply the above-mentioned model to the non-rotating samples. The WL thicknesses after deposition can be known by calculating the resulting WL thicknesses with gradually changed InAs deposition rates and a given deposition time. Considering the WL evolution during GI, one can simply set G = 0 in Equations 2 and 3 and calculate with the WL thicknesses after deposition as initial values. The simulation results of WL evolution at different temperatures are shown in Figure 3a. One could see that the main features are well reproduced compared with the experimental results. The WL thickness shows a monotonic increase if the temperature is set at 490°C but shows a concave-up evolution for temperatures of 520°C and 540°C. According to the discussion above, we know that the slowed down increase observed at lower temperature is because of the deposition rate dependence of the equilibrium WL thickness. For higher growth temperatures, the elevated QD formation rate at the beginning of the 3D growth stage led to WL erosion, which corresponds to the decrease of WL thickness on those non-rotating samples. WL thickness increases again with the deposition rate when the growth reaches equilibrium. It should also be noted that the simple equations do not reproduce the experimental results quantitatively because of their semi-empirical nature and the use of some adjustable parameters.
We would like to comment on a special feature of those non-rotating samples. The material deposition rate changes gradually at different positions of a sample, which leads to the same behavior of deposition amount for a given growth time. Considering a weak dependence of the CT on deposition rate, one would expect that it takes different times at those positions of the sample to enter the 3D growth stage. The 2D growth time t 2D can be calculated respectively from Equation 2 by taking θ = θ c . One then obtains the 3D growth time t 3D = t InAs − t 2D . The inset of Figure 3a shows the 3D growth time with deposition rates. It should be noticed that at some positions, they have very small values. Apparently, a near-zero 3D growth time cannot ensure an equilibrium quantum dot growth nor provide a steady-state WL thickness. It leads to stronger kinetic control characters on those samples.
We come back to the 2D growth stage and to study another kinetic problem during growth - the indium desorption. In Figure 1b, for samples with the same deposition amount but different growth temperatures, WL thicknesses varied a lot. From Equation 1, we know that it is because of the temperature dependence of indium desorption rate. From Equation 2 and from further considering the WL evolution during GI, the resulting WL thickness in the 2D growth stage can be written as follows:
where t InAs is the InAs deposition time and t GI is the GI time. The kinetic parameter of indium desorption, E des , and ν 0 , can be extracted from Equation 5 and Figure 1b. We adopt the WL thicknesses of the first four pieces of each sample with effective InAs deposition amounts of 1.14, 1.24, 1.34, and 1.45 ML to fit E des and ν 0 , respectively. The obtained E des = 3.68 eV and ν 0 are around 5.5 × 1022. The activation energy is close to previously reported InAs decomposition energy and indium desorption activation energy from InGaAs [23, 33]. We notice that the fitting ν 0 is such a big number; ν 0 stands for the attempt frequency of desorption, which is commonly known with the order of 1012 to 1014 s−1 for desorption from metal and semiconductor surfaces. Such a big transition frequency obtained here is also reported by other groups in investigating the InAs/GaAs QD desorption [33] or As desorption from GaAs surface [34]. It is considered as physically achievable and could explain several characteristic features in InAs MBE growth [34]. The inset of Figure 3b shows the temperature dependence of the desorption life time (τ des ) for samples with different InAs deposition amounts based on the fitting results. The time constants show a weak dependence on the indium flux but strongly decrease with increasing temperature; τ des decreases from 1,063 s at 490°C to 35 s at 540°C for samples with a deposition amount of 1.45 ML. The same strong dependence is also mentioned elsewhere [35]. Those time constants could be used to estimate the degree of desorption during the growth of InAs/GaAs(001) QDs at a certain temperature.
Conclusions
In conclusion, two kinds of WL evolution process of InAs/GaAs(001) QD system have been discussed based on RDS measurements and a rate equation model. They were well understood in the regime of material balance of WL growth/consumption and temperature dependence of QD formation. The concave-up style of evolution is also an evidence of a non-zero QD growth rate when the WL thickness was slightly lower than the critical value. We also gave a brief discussion on the indium desorption process during growth. Those results helped us in understanding the kinetically controlled QD growth process.
References
Bimberg D, Grundmann M, Ledentsov NN: Quantum Dot Heterostructures. Chichester: Wiley; 1999.
Weng GE, Ling AK, Lv XQ, Zhang JY, Zhang BP: III-Nitride-based quantum dots and their optoelectronic applications. Nano-Micro Lett 2011, 3: 200–207.
Ellis B, Mayer MA, Shambat G, Sarmiento T, Harris J, Haller EE, Vuckovic J: Ultralow-threshold electrically pumped quantum-dot photonic-crystal nanocavity laser. Nat Photon 2011, 5: 297–300. 10.1038/nphoton.2011.51
Sanguinetti S, Henini M, Grassi Alessi M, Capizzi M, Frigeri P, Franchi S: Carrier thermal escape and retrapping in self-assembled quantum dots. Physical Review B 1999, 60: 8276. 10.1103/PhysRevB.60.8276
Wang LJ, Krapek V, Ding F, Horton F, Schliwa A, Bimberg D, Rastelli A, Schmidt OG: Self-assembled quantum dots with tunable thickness of the wetting layer: role of vertical confinement on interlevel spacing. Physical Review B 2009, 80: 085309.
Deppe DG, Huffaker DL: Quantum dimensionality, entropy, and the modulation response of quantum dot lasers. Appl Phys Lett 2000, 77: 3325. 10.1063/1.1328090
Matthews DR, Summers HD, Smowton PM, Hopkinson M: Experimental investigation of the effect of wetting-layer states on the gain-current characteristic of quantum-dot lasers. Appl Phys Lett 2002, 81: 4904–4906. 10.1063/1.1532549
Bergamaschini R, Brehm M, Grydlik M, Fromherz T, Bauer G, Montalenti F: Temperature-dependent evolution of the wetting layer thickness during Ge deposition on Si(001). Nanotechnology 2011, 22: 285704. 10.1088/0957-4484/22/28/285704
Osipov AV, Schmitt F, Kukushkin SA, Hess P: Stress-driven nucleation of coherent islands: theory and experiment. Appl Surf Sci 2002, 188: 156–162. 10.1016/S0169-4332(01)00727-9
Brehm M, Montalenti F, Grydlik M, Vastola G, Lichtenberger H, Hrauda N, Beck MJ, Fromherz T, Schäffler F, Miglio L, Bauer G: Key role of the wetting layer in revealing the hidden path of Ge/Si(001) Stranski-Krastanow growth onset. Physical Review B 2009, 80: 205321.
Placidi E, Arciprete F, Sessi V, Fanfoni M, Patella F, Balzarotti A: Step erosion during nucleation of InAs/GaAs(001) quantum dots. Appl Phys Lett 2005, 86: 241913–3. 10.1063/1.1946181
Arciprete F, Placidi E, Sessi V, Fanfoni M, Patella F, Balzarotti A: How kinetics drives the two- to three-dimensional transition in semiconductor strained heterostructures: the case of InAs/GaAs(001). Appl Phys Lett 2006, 89: 041904. 10.1063/1.2234845
Chen YH, Jin P, Liang LY, Ye XL, Wang ZG, Martinez AI: Evolution of the amount of InAs in wetting layers in an InAs/GaAs quantum-dot system studied by reflectance difference spectroscopy. Nanotechnology 2006, 17: 2207–2211. 10.1088/0957-4484/17/9/022
Chen YH, Sun J, Jin P, Wang ZG, Yang Z: Evolution of wetting layer of InAs∕GaAs quantum dots studied by reflectance difference spectroscopy. Appl Phys Lett 2006, 88: 071903. 10.1063/1.2175489
Zhou GY, Chen YH, Yu JL, Zhou XL, Ye XL, Jin P, Wang ZG: The transition from two-stage to three-stage evolution of wetting layer of InAs/GaAs quantum dots caused by postgrowth annealing. Appl Phys Lett 2011, 98: 071914. 10.1063/1.3552967
Zhou GY, Chen YH, Tang CG, Liang LY, Jin P, Wang ZG: The two- to three-dimensional growth transition of InAs/GaAs epitaxy layer studied by reflectance difference spectroscopy. J Appl Phys 2010, 108: 083513. 10.1063/1.3494043
Peng J, Ye XL, Wang ZG: Growth of low-density InAs/GaAs quantum dots on a substrate with an intentional temperature gradient by molecular beam epitaxy. Nanotechnology 2005, 16: 2775. 10.1088/0957-4484/16/12/005
Herman MA, Sitter H: Molecular Beam Epitaxy: Fundamental and Current Status. Berlin: Springer; 1989.
Chen YH, Ye XL, Wang JZ, Wang ZG, Yang Z: Interface-related in-plane optical anisotropy in GaAs/AlxG1−xAs single-quantum-well structures studied by reflectance difference spectroscopy. Physical Review B 2002, 66: 195321.
Geddo M, Capizzi M, Patane A, Martelli F: Photoreflectance study of growth mode in InAs-GaAs quasimonolayer single quantum wells. J Appl Phys 1998, 84: 3374–3377. 10.1063/1.368494
Daruka I, Barabasi AL: Dislocation-free island formation in heteroepitaxial growth: a study at equilibrium. Phys Rev Lett 1997, 79: 3708–3711. 10.1103/PhysRevLett.79.3708
Heitz R, Ramachandran TR, Kalburge A, Xie Q, Mukhametzhanov I, Chen P, Madhukar A: Observation of reentrant 2D to 3D morphology transition in highly strained epitaxy: InAs on GaAs. Phys Rev Lett 1997, 78: 4071. 10.1103/PhysRevLett.78.4071
Mozume T, Ohbu I: Desorption of indium during the growth of GaAs/InGaAs/GaAs heterostructures by molecular-beam epitaxy Japanese. J Appl Phys 1992, 31: 3277–3281. 10.1143/JJAP.31.3277
Heyn C, Endler D, Zhang K, Hansen W: Formation and dissolution of InAs quantum dots on GaAs. J Cryst Growth 2000, 210: 421–428. 10.1016/S0022-0248(99)00901-X
Osipov A, Kukushkin S, Schmitt F, Hess P: Kinetic model of coherent island formation in the case of self-limiting growth. Physical Review B 2001, 64: 205421.
Dobbs HT, Vvedensky DD, Zangwill A, Johansson J, Carlsson N, Seifert W: Mean-field theory of quantum dot formation. Phys Rev Lett 1997, 79: 897–900. 10.1103/PhysRevLett.79.897
Dubrovskii VG, Cirlin GE, Ustinov VM: Kinetics of the initial stage of coherent island formation in heteroepitaxial systems. Physical Review B 2003, 68: 075409.
Kim C: Optical observation of quantum-dot formation in sub-critical CdSe layers grown on ZnSe. J Cryst Growth 2000, 214: 761–764.
Song H, Usuki T, Nakata Y, Yokoyama N, Sasakura H, Muto S: Formation of InAs∕GaAs quantum dots from a subcritical InAs wetting layer: a reflection high-energy electron diffraction and theoretical study. Physical Review B 2006, 73: 115327.
Tonkikh A, Cirlin G, Dubrovskii V, Samsonenko Y, Polyakov N, Egorov V, Gladyshev A, Kryzhanovskaya N, Ustinov V: Quantum dots in InAs layers of subcritical thickness on GaAs(100). Technical Physics Letters 2003, 29: 691–693. 10.1134/1.1606790
Balzarotti A: The evolution of self-assembled InAs/GaAs(001) quantum dots grown by growth-interrupted molecular beam epitaxy. Nanotechnology 2008, 19: 505701. 10.1088/0957-4484/19/50/505701
Tonkikh AA, Dubrovskii VG, Cirlin GE, Egorov VA, Ustinov VM, Werner P: Temperature dependence of the quantum dot lateral size in the Ge/Si(100) system. Physica Status Solidi B-Basic Research 2003, 236: R1-R3. 10.1002/pssb.200301758
Heyn C: Stability of InAs quantum dots. Physical Review B 2002, 66: 075307.
Sasaoka C, Kato Y, Usui A: Anomalous As desorption from InAs(100) 2x4. Appl Phys Lett 1993, 62: 2338–2340. 10.1063/1.109410
Heyn C, Hansen W: Desorption of InAs quantum dots. J Cryst Growth 2003, 251: 218–222. 10.1016/S0022-0248(02)02379-5
Acknowledgments
The work was supported by the National Natural Science Foundation of China (no. 60990313), the 973 program (2012CB921304, 2012CB619306), and the 863 program (2011AA 03A 101).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
HZ carried out the analysis and simulation. GZ and CT did the measurements. HZ and YC drafted the manuscript. YC and ZW supervised the works. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Zhang, H., Chen, Y., Zhou, G. et al. Wetting layer evolution and its temperature dependence during self-assembly of InAs/GaAs quantum dots. Nanoscale Res Lett 7, 600 (2012). https://doi.org/10.1186/1556-276X-7-600
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-7-600