Abstract
High-resolution transmission electron microscopy was used to characterize the microstructures of ZnSe nanotrenches induced by mobile Au-alloy droplets. The contact side interfaces between the AuZnδ alloy droplets and the ZnSe as well as the four side walls of the resulting <011>-oriented nanotrenches were found all belong to the {111} plane family, with the front and back walls being the {111}A planes while the other two side walls being the {111}B planes. These findings offer a deeper understanding on the formation mechanism of the nanotrenches. Pure Au nanodashes were formed upon further deposition of Au on the nanotrenches.
PACS: 61.46.Df, Structure of nanocrystals and nanoparticles. 81.16.Rf, Micro and nanoscale pattern formation. 68.37.Og, High resolution transmission electron microscopy.
Avoid common mistakes on your manuscript.
Introduction
As length scales decrease below the range easily accessible by lithographic patterning, there is great interest in developing processes to form surface structures spontaneously [1]. Among the different approaches used for fabricating nanostructures, deposition of functionalized materials into patterned nanotrenches on a substrate has attracted increasing interest. This approach has been applied to various applications, such as chemical sensing, dimensional crossover influence in granular electronic systems, heterojunction tunneling field effect transistors, and precise quantum dot placement [2–6]. Fabrication of nanotrenches structures can be achieved by a number of different ways, such as electron-beam lithography [7], focused ion beam [2, 8] milling, and nanoimprint lithography [5, 9]. These three approaches enjoy the advantage of being able to create highly ordered patterns; however, they suffer from the need of much time-consuming and contaminating processing. Using metal-assisted-chemical-reaction etching without fluoride, Sun and Akinaga [10] have fabricated noodle-like nanotrenches on porous silicon substrates. However, they were not highly aligned and ordered, and it was difficult to reach a truly nanoscale width. Byon and Choi [11] have demonstrated using single-walled carbon nanotubes (SWNTs) to selectively etch one-dimensional nanotrenches in SiO2. The shape, length, and trajectory of the nanotrenches are fully guided by the SWNTs. The challenge for realizing ordered nanotrenches using this approach will be the need for sophisticated techniques that permit the alignment of the carbon nanotubes. Recently, some mobile metallic nanoparticles (NPs) were found to act as catalyst to induce nanotrench formation. Byon and Choi [12] reported that Fe NPs could initiate the carbothermal reduction to form SiO2 nanotrenches. In the recent years, using the state of the art molecular beam epitaxy (MBE) technique, we have been able to study the growth mechanism and the quantum size effects of several self-assembled nanostructures [13–15]. Recently, we reported that highly aligned nanotrenches were produced during the thermally agitated migration of AuZnδ alloy droplets through a catalytic reaction with an underlying ZnSe thin film [16]. More recently, Amalric et al. [17] further reported that nucleation of Au catalyst in ZnSe nanotrenches assists the growth of ZnSe and ZnSe/CdSe nanowires preferentially in directions orthogonal to the trenches. In this study, we report high-resolution transmission electron microscopy (HRTEM) imaging of Au-alloy droplet-driven ZnSe nanotrenches, which provides a deeper understanding on the nanotrench formation mechanism. The use of the nanotrenches as a template for fabricating Au nanodashes is also presented.
Experiment
In this study, the samples were fabricated on GaAs (100) substrates in a VG V80H MBE system. A ZnSe layer (100 nm) was first grown at 250°C using a ZnSe compound source. Sample #1 was then deposited with a 0.45-nm Au at 150°C followed by a thermal annealing at 550°C for 20 min to generate the nanotrenches. Sample #2 was deposited with a 0.23-nm Au layer instead so as to generate narrower nanotrenches. After the thermal annealing, sample #2 was then cooled down to 500°C followed by a further Au deposition of 0.9 nm with the expectation of forming Au nanostructures within the nanotrenches. A JEOL 2010F HRTEM and a JEOL JSM6700F high-resolution scanning electron microscope (HRSEM) were used for structural characterization. Chemical analysis was performed using the energy-dispersive X-ray spectroscopy (EDS) facility built into the HRTEM.
Results and discussion
In a recent article, Amalric et al. [17] reported that some short trenches with irregular shape mainly oriented along the <011> direction were observed to present at a bare ZnSe surface at temperature ≥400°C. They argued that the trenches are more probably related to a sublimation mechanism of the ZnSe layer alone. However, they also observed that with the presence of Au NPs at the ZnSe surface, annealing at 530°C can generate much longer and well-aligned trenches with the AuZnδ particles all localized at the extremities of the trenches the same as what we have reported earlier [16]. In a recent report on the <011>-oriented self-assembled formation of nano-groove structure at the surface of an annealed Fe/ZnSe bilayer [18], we have also pointed out that a bare ZnSe surface annealed at high temperature can itself generate an imperfect nano-groove structure; however, the presence of the Fe catalyst layer plays a role in enhancing the formation of the 1D nanostructure to a great extent in its perfection at a lower annealing temperature. We believe that the above observations are all correlated with each other confirming that annealing of a bare ZnSe surface can induce an imperfect <011>-oriented trench/groove structure to a certain extent being attributed to the minimization of the surface energy. The migration of the AuZnδ NPs and their induced catalytic decomposition of the several top layers of ZnSe lead to the formation of the long and well-aligned nanotrenches, similar to the role of the Fe catalytic layer in enhancing the formation of the nano-groove structure. In our most recent top-view SEM study, it was found that if a bare ZnSe surface was heated to a certain high temperature, then some Se dots with perfectly spherical shape were generated. Figure S1 in Additional file 1 shows the SEM image of these Se dots. With the presence of AuZnδ NPs, the induced nanotrenches were found to penetrate across the Se dots that were observed to be distorted into an elongated shape being attributed to the cross-over migration of the AuZnδ NPs. Figure S2 in Additional file 2 shows the SEM image of the distorted Se dots resting on the nanotrenches passing through them. This provides further evidence that the long and well-aligned nanotrenches were indeed induced by the migration of the NPs and their catalytic decomposition of ZnSe.
Figure 1 shows a cross-sectional TEM view of a number of nanotrenches on a piece cut from sample #1 with the viewing zone axis along the [011] direction, that is, along the nanotrench orientation; we term this as a front view observation. The AuZnδ NPs of two of these nanotrenches are by chance located in the viewing zone of this cross-sectional sample, while the rest of them just display the front view of the "empty" trench body. One can see that the front view cross section of the nanotrenches has a V shape in general, while that of the AuZnδ NPs has a V shape for the portion embedded in the ZnSe layer and an arc shape for the portion above the trench body. The bottom-left inset in Figure 1 shows an HRTEM image of the AuZnδ NP on the left side of this figure. In this inset, a Fourier transform pattern of the ZnSe lattice near the NP is also shown. Using the Fourier transform pattern as references, both the interfaces of the V shape are found to be the members of the {111} plane family of ZnSe as indicated in the bottom-left inset of Figure 1. In a previously published article, we have identified that the nanotrenches are along either the [011] or directions that are anti-parallel with each other, in which the identification was based on the orientation of the resulting nanotrenches formed on a GaAs(100) substrate with a pretilting angle of 2° off toward the [111]A direction [16]. Figure S3 in Additional file 3 shows the planar representation of the orientation relationship of the crystal planes of the ZnSe(100) layer, which is deduced from the relevant data given by the manufacturer of the GaAs(100) wafers used in this study. As can be seen in Figure S3, the interfacial planes of the V shape shown in Figure 1 are B plane and B planes, respectively, and both are Se-terminated planes. The top-right inset in Figure 1 shows the HRTEM image of a portion of the AuZnδ NP on the right side of this figure. The moire fringes located near the V-shaped region within the NP together with the regular lattice pattern in the rest of the NP region indicate that it is single crystalline. We have performed separately a detailed analysis on the microstructure of a few NPs of this sample using the built-in electron diffraction technique. It was found that the NPs are FCC structures with various orientation relationships with the underlying ZnSe lattice and their lattice constants are slightly smaller than that of pure Au lattice being attributed to the inclusion of small amount of Zn as reported in our previous publication [16].
The side-view cross-sectional HRTEM image of a nanotrench with the viewing zone at 90° off the [011] direction, that is, perpendicular to the nanotrench orientation, is shown in Figure 2. This side-view image together with the Fourier transform pattern of the ZnSe lattice as shown in its inset reveals that the left contact interface between the NP and the ZnSe lattice and the right-end surface of the nanotrench are both members of Zn-terminated {111}A surface family. From Figure S3 in Additional file 3 they can be determined to be either the (111)A or the A plane. It is also worthy to note that the non-contacted portion of the surface of the NP is of an arc shape as can be seen in Figure 2.
The HRTEM observations described above offer more insightful details than what we have reported previously on the formation mechanism of the nanotrenches induced by the mobile catalytic particles. Our further understanding on the formation mechanism is illustrated as follows. At the annealing temperature, Au droplets first react with the ZnSe thin film to form AuZnδ alloy droplets. During this process, the droplets fall into the ZnSe layer by a fraction of their size. As described earlier, the portion fell into the ZnSe lattice has four contact surfaces, all of them belong to the {111} plane family. In our previously published article regarding the study on the growth mechanism of ultra-thin ZnSe nanowires using Au NPs as the catalyst, we have shown that the interfaces between the catalyst particles and the ZnSe NWs were always {111} planes regardless of whether their growth directions are along [111], [211], or [110]. We have argued that this feature is likely driven by the minimization of the total energy of the nanowire system and the fact that {111} planes of ZnSe have the lowest interface energy [15]. We believe that all the four contact surfaces of the AuZnδ catalyst droplets for the formation of the nanotrenches represent {111} planes because of the same origin of driving force as just described for the growth of ZnSe nanowires. The observed arc shape of the non-contacted portion of the AuZnδ catalyst droplets shares the same cause as well since it is well known that a spherical shape for a non-contacted nanodroplet has the smallest surface area so as to minimize its surface energy.
In our previously published article, we have discussed the reason for the nanotrenches induced by the migration of AuZnδ being only oriented along a specific pair of <011> direction although there are four <011> directions on the surface of a (100)-oriented substrate of zinc-blended structure [16]. This is because the [011]/ and the pairs are not identical because of the inversion symmetry on the (100) plane of a zinc-blended structure. As viewed along the [011] and directions, the zigzag atomic chains presented on the viewing planes are in fact 180° off with regard to the location of the Zn and Se atoms, with Zn atoms at the top as viewed along the [011] direction while Se atoms at the top as viewed along the direction. We further argue that AuZnδ droplets prefer to attack Zn atoms more than Se atoms because it is more energetically favorable because the heat of formation of Au-Zn (-0.27 eV/atom) [19] is lower than that of Au-Se (-0.15 eV/atom) [20]. This study further reveals that the contact interfaces between the AuZnδ droplet and the ZnSe lattice are {111}A and {111}B planes for the [011]/ and the pairs, respectively, which in fact provides further evidence in support of our explanation described above. Figure 3a, b displays the tilted views of a ZnSe lattice as viewed along the [011] and directions, with the top surface terminated at (111)A and B, respectively. These schematic drawings are applicable to the views along the and directions as well. The inclined top surfaces represent the direct contact surface between a AuZnδ droplet and the ZnSe lattice. As can be seen in Figure 3, the contact surfaces for the [011]/ directions are Zinc terminated, while those for the directions are Se terminated. Being attributed to the difference between the heat of formation of Au-Zn and Au-Se, the [011]/ directions represent the preferred directions for the formation of the ZnSe nanotrenches since the migration of the AuZnδ droplets and their catalytic decomposition reaction are more favorable along these anti-parallel directions than along the directions.
Recently, Xue et al. [21] have demonstrated the fabrication of ultrafine protein arrays on Au nanowires arrays through the interactions of protein-mercaptoundecanoic acid and gold. In this study, using a sample with aligned nanotrenches as a template, further Au deposition of 9.1 Ǻ in nominal thickness was carried out at a lower growth temperature with the expectation that the deposited Au in the second growth step may fall into the nanotrenches to form 1D Au nanostructure. Figure 4a shows the SEM image of a typical resulting surface of this sample, which is named as sample #2. One can see that the resulting nanotrenches are partially filled with high-density nanostructures of which their top-view shapes are either square or rectangle with sharp corners, which are in high contrast with the spherical shape of the catalyst particles. Some of these nanostructures have higher aspect ratio, although they are rare. The inset in Figure 4a shows one of these "nanodashes" with a length of about 140 nm. Figure 4b displays the HRTEM images of a completely filled-in nanodash with both the front and back contact surfaces being the {111}A planes while Figure 4c displays one that is located within a nanotrench with both the front and back surfaces being non-contacted with arc shapes. The shapes of the contact surfaces and the non-contacted surfaces of the filled-in nanostructures shown in these images offer further evidence that the shape of the filled-in nanostructures is also driven by the minimization of the system energy. One thing is worth pointing out that both subsequent EDS analysis and a detailed study performed on the Fourier transform pattern taken at the regular lattice pattern of the nanodash shown in Figure 4c reveal that the filled in material is pure Au with epitaxial relationship of [100]Au//[100]ZnSe in contrast to the AuZnδ alloy phase and the lattice misalignment of the catalytic droplets. It is believed that the nanodashes filled in the nanotrenches are pure Au instead of AuZnδ alloy because a lower substrate temperature of 500°C was used for the secondary Au deposition that only lasts for 2.5 min, which lacks sufficient energy to initiate the Au-Zn alloying process, whereas the first Au deposition having been annealed at 550°C for 20 min is capable of resulting in the formation of AuZnδ alloy NPs. The formation of Au nanodashes demonstrated in this study indicates that it is indeed possible for using the ZnSe nanotrenches as a template to fill in other materials to form novel low-dimensional nanostructures.
Conclusions
In summary, the three-dimensional shapes of ZnSe nanotrenches induced by mobile AuZnδ droplets were investigated using cross-sectional HRTEM imaging technique, revealing that the contact side interfaces between the AuZnδ alloy droplets and the ZnSe lattice are all belong to the {111} plane family. The front and back walls of the resulting <011>-oriented nanotrenches were found to be Zn-terminated {111}A planes while the other two side walls are Se-terminated {111}B planes. These findings further provide the explanation for the [011]/ directions being the preferred directions for the formation of the ZnSe nanotrenches. We have also demonstrated the formation of pure Au nanodashes inside the nanotrenches. Further study is being carried out in our laboratory to investigate the possibility of forming 1D nanostructures of other materials using the developed nanotrenches as a highly aligned template.
Abbreviations
- EDS:
-
energy-dispersive X-ray spectroscopy
- HRSEM:
-
high-resolution scanning electron microscope
- HRTEM:
-
high-resolution transmission electron microscopy
- MBE:
-
molecular beam epitaxy
- NPs:
-
nanoparticles
- SWNTs:
-
single-walled carbon nanotubes.
References
Chason E, Aziz MJ: Spontaneous formation of patterns on sputtered surfaces. Scr Mater 2003, 49: 953–959. 10.1016/S1359-6462(03)00474-3
Favier F: Nanogaps for sensing. Proc Chem 2009, 1: 746–749. 10.1016/j.proche.2009.07.186
Tenhaeff WE, McIntosh LD, Gleason KK: Synthesis of poly(4-vinylpyridine) thin films by initiated chemical vapor deposition (iCVD) for selective nanotrench-based sensing of nitroaromatics. Adv Funct Mater 2010, 20: 1144–1151. 10.1002/adfm.200901890
Xu K, Qin LD, Heath JR: The crossover from two dimensions to one dimension in granular electronic materials. Nat Nanotechnol 2009, 4: 368–372. 10.1038/nnano.2009.81
Wang C, Chou SY: Self-aligned fabrication of 10 nm wide asymmetric trenches for Si/SiGe heterojunction tunneling field effect transistors using nanoimprint lithography, shadow evaporation, and etching. J Vac Sci Technol B 2009, 27: 2790–2794. 10.1116/1.3237138
Chen KH, Chien CY, Li PW: Precise Ge quantum dot placement for quantum tunneling devices. Nanotechnology 2010, 21: 055302. 10.1088/0957-4484/21/5/055302
Xiong X, Makaram P, Busnaina A, Bakhtari K: Large scale directed assembly of nanoparticles using nanotrench templates. Appl Phys Lett 2006, 89: 193108. 10.1063/1.2385067
Kim S, Chang IS, McDevitt JT: Self-assembled monolayer cleaning methods: towards fabrication of clean high-temperature superconductor nanostructures. Appl Phys Lett 2005, 86: 154104. 10.1063/1.1899753
Zhang L, Li CF, Li J, Zhang F, Shi L: Design and fabrication of metal-wire nanograting used as polarizing beam splitter in optical telecommunication. J Optoelectron Adv Mater 2006, 8: 847–850.
Sun ZG, Akinaga H: Enhanced coercive field of cobalt film deposited on noodle-like porous silicon substrates. Appl Phys Lett 2005, 86: 181904. 10.1063/1.1921331
Byon HR, Choi HC: Carbon nanotube guided formation of silicon oxide nanotrenches. Nat Nanotechnol 2007, 2: 162–166. 10.1038/nnano.2007.26
Byon HR, Choi HC: Mobile iron nanoparticle and its role in the formation of SiO 2 nanotrench via carbon nanotube-guided carbothermal reduction. Nano Lett 2008, 8: 178–182. 10.1021/nl072379u
Cai Y, Chan SK, Sou IK, Chan YF, Su DS, Wang N: Temperature-dependent growth direction of ultrathin ZnSe nanowires. Small 2007, 3: 111–115. 10.1002/smll.200600266
Lok SK, You B, Zhang B, Zhang XX, Sou IK, Wong GKL: MBE-grown Fe magnetic quantum dots in ZnS matrix. IEEE Trans Magn 2007, 43: 3127–3129. 10.1109/TMAG.2007.893859
Cai Y, Chan SK, Sou IK, Chan YF, Su DS, Wang N: The size-dependent growth direction of ZnSe nanowires. Adv Mater 2006, 18: 109–114. 10.1002/adma.200500822
Chan SK, Lok SK, Wang G, Cai Y, Wang YJ, Wang N, Sou IK: Formation mechanism of nanotrenches induced by mobile catalytic nanoparticles. Appl Phys Lett 2008, 92: 183102. 10.1063/1.2912130
Amalric EB, Jamroz ME, Bougerol C, Hertog MD, Genuist Y, Bounouar S, Poizat JP, Kheng K, André R, Tatarenko S: Epitaxial growth of ZnSe and ZnSe/CdSe nanowires on ZnSe. Phys Status Solidi C 2010, 7: 1526–1529. 10.1002/pssc.200983254
Wang G, Lok SK, Chan SK, Wang C, Wong GKL, Sou IK: The formation of an aligned 1D nanostructure on annealed Fe/ZnSe bilayers. Nanotechnology 2009, 20: 215607. 10.1088/0957-4484/20/21/215607
Mills KC: Thermodynamic Data for Inorganic Sulphides, Selenides and Tellurides. London: Butterworths; 1974.
Hultgren RH: Selected Values of Thermodynamics Properties of Binary Alloys. Metals Park, OH: American Society for Metals; 1973.
Xue MQ, Guo S, Zhao XS, Cao TB: Fabrication of ultrafine protein arrays on easy-fabricated metallic nanostructures. Scr Mater 2008, 58: 854–857. 10.1016/j.scriptamat.2008.01.012
Acknowledgements
The study was substantially supported by grants from the Research Grants Council of the Hong Kong Special Administrative Region, China (Project No. 602808).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
GW participated in the design of the study, MBE growth, HRSEM, and HRTEM analysis and drafted the manuscript. SKL participated extensively in HRTEM imaging and experimental data analyses. IKS coordinated the design of the study, proposed the phenomenological model and significantly contributed to the drafting of this manuscript. All the authors have read and approved the final manuscript.
Electronic supplementary material
11671_2010_202_MOESM1_ESM.TIFF
Additional file 1:Figure S1. SEM image of the round dots resulted from a bare ZnSe surface annealed at 550°C for 10 min. Separate EDS analysis performed on these dots reveals that they are Se dots. (TIFF 4 MB)
11671_2010_202_MOESM2_ESM.TIFF
Additional file 2:Figure S2. SEM image of the distorted Se dots passed through by nanotrenches. The inset is an AFM image that reveals the dark spots in this SEM image are indeed elongated particles. (TIFF 2 MB)
11671_2010_202_MOESM3_ESM.TIFF
Additional file 3:Figure S3. Planar representation of the orientation relationship of the crystal planes of the ZnSe(100) layer. (TIFF 108 KB)
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Wang, G., Lok, S.K. & Sou, I.K. ZnSe nanotrenches: formation mechanism and its role as a 1D template. Nanoscale Res Lett 6, 272 (2011). https://doi.org/10.1186/1556-276X-6-272
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-6-272