Abstract
The migration characteristics of carbon nanotubes from liquid phase to vapor phase in the refrigerantbased nanofluid pool boiling were investigated experimentally. Four types of carbon nanotubes with the outside diameters from 15 to 80 nm and the lengths from 1.5 to 10 μm were used in the experiments. The refrigerants include R113, R141b and npentane. The oil concentration is from 0 to 10 wt.%, the heat flux is from 10 to 100 kW·m^{2}, and the initial liquidlevel height is from 1.3 to 3.4 cm. The experimental results indicate that the migration ratio of carbon nanotube increases with the increase of the outside diameter or the length of carbon nanotube. For the fixed type of carbon nanotube, the migration ratio decreases with the increase of the oil concentration or the heat flux, and increases with the increase of the initial liquidlevel height. The migration ratio of carbon nanotube increases with the decrease of dynamic viscosity of refrigerant or the increase of liquid phase density of refrigerant. A model for predicting the migration ratio of carbon nanotubes in the refrigerantbased nanofluid pool boiling is proposed, and the predictions agree with 92% of the experimental data within a deviation of ±20%.
Introduction
Nowadays, the researchers show great interest in the possible application of refrigerantbased nanofluids (i.e., the mixtures of nanopowders and conventional pure refrigerants) for improving the performance of refrigeration systems. The researches showed that the refrigerantbased nanofluids have higher thermal conductivity than those of conventional pure refrigerants [1], the addition of nanoparticles enhances the solubility of mineral oil in HFC refrigerant [2], and the addition of nanoparticles can save energy consumption of airconditioner and refrigerator [3, 4]. Comparing with the spherical metal or metal oxide nanoparticles used in these researches, carbon nanotubes (CNTs) have one or two orders of magnitude higher in thermal conductivity, and CNTs can significantly enhance the thermal conductivity of base fluid [5–8] as well as the convective heat transfer coefficient of base fluid [9], so CNTs have great potential for improving the performance of refrigeration systems. For applying CNTs in refrigeration systems, the phasechange heat transfer characteristics of refrigerantCNT nanofluid and the cycle behavior of CNTs in refrigeration systems should be known. The migration of CNTs from liquid phase to vapor phase in the pool boiling process of refrigerantCNT nanofluid determines the distribution of CNTs concentration in the liquid phase and vapor phase, and then has significant effect on the phasechange heat transfer characteristics of refrigerantCNT nanofluid as well as the cycle behavior of CNTs. Therefore, in order to evaluate the phasechange heat transfer characteristics of refrigerantCNT nanofluid and the cycle behavior of CNTs, the migration of CNTs in the pool boiling process of refrigerantCNT nanofluid should be researched.
The migration of CNTs from liquid phase to vapor phase in the refrigerantbased nanofluid pool boiling can be divided to the following four physical processes: (1) the departure of bubble from the heating surface, (2) the movement of bubble and CNTs in the liquid phase, (3) the capture of CNTs by bubble, and (4) the escape of CNTs from the liquidvapor interface. From the above analysis, it can be seen that the interaction between CNTs and bubble is the key factor causing the migration of CNTs from liquid phase to vapor phase. The existing flotation theory can accurately describe the interaction between particles and bubbles. However, they can not directly used to predict the migration of CNTs from liquid phase to vapor phase during pool boiling because they are aimed at the conditions without phase change. The present investigation is beneficial to reveal the mass transfer mechanism of nanoscale solid powders from liquid phase to vapor phase during the phasechange process of fluid, and provides the theoretical basis for evaluating the phasechange heat transfer characteristics of refrigerantCNT nanofluid and the cycle behavior of CNTs.
Until now, there is no published research on the migration characteristics of CNTs in the pool boiling of refrigerantbased nanofluid. The migration characteristics of nanopowders are mentioned only by the paper of Ding et al. [10], and are focused on one type of spherical nanoparticle (CuO). In the paper, the authors found that the migrated mass of CuO nanoparticles in the pool boiling increases with the increase of the original mass of nanoparticles or the original mass of refrigerant. As the structure and the thermophysical properties of CNTs are different from those of spherical nanoparticles, the migration characteristics of CNTs in the pool boiling of refrigerantbased nanofluid may be different from those of spherical nanoparticles, and should be investigated.
The existing researches on the pool boiling heat transfer characteristics of nanofluids containing CNTs can be divided into three categories as follows: (1) Pool boiling heat transfer of waterCNTs nanofluids. The experimental results showed that CNTs can enhance the pool boiling heat transfer of water [11–13] or deteriorate the pool boiling heat transfer of water [14], and the influence of CNTs on the pool boiling is related to CNTs concentration [13]. (2) Pool boiling heat transfer of pure refrigerantCNTs nanofluids. The experiments by Park and Jung [11, 15] showed that CNTs can enhance the pool boiling heat transfer of pure refrigerants (R22, R123, and R134a), and the enhancement is related to the heat flux. (3) Pool boiling heat transfer of refrigerantoil mixtures with CNTs. Experiments by Peng et al. [16] showed that CNTs can enhance the pool boiling heat transfer of refrigerantoil mixtures, and the enhancement increases with the decrease of CNTs' outside diameter or CNTs' nanolubricant mass fraction, while increases with the increase of CNTs' length or CNTs' mass fraction in the CNTs' nanolubricant. From the above researches, it can be seen that the CNTs physical dimension (i.e., the outside diameter and the length of CNTs), refrigerant type, CNTs concentration, oil concentration, and heat flux have influences on the pool boiling heat transfer of refrigerantbased nanofluid. Therefore, the influences of the above factors on the migration characteristics of CNTs need be concerned. In addition, the initial liquidlevel height affects the pool boiling heat transfer, so the influence of initial liquidlevel height on the migration characteristics of CNTs also needs be concerned.
The objective of this paper is to experimentally investigate the influences of CNTs physical dimension, refrigerant type, oil concentration, heat flux, and initial liquidlevel height on the migration characteristics of CNTs in the refrigerantbased nanofluid pool boiling at different original CNTs concentrations, and to propose a model for predicting the migration ratio of CNTs in the refrigerantbased nanofluid pool boiling.
Experiments
Test conditions and experimental objects
Test conditions are divided into five categories, as tabulated in Table 1.
The objective of category 1 is to investigate the influences of CNTs physical dimension on the migration characteristics of CNTs. Four types of CNTs with different physical dimensions (numbered as CNT#1, CNT#2, CNT#3, and CNT#4) produced by the chemical vapor deposition method are used in these test conditions. The physical dimensions of these four types of CNTs are shown in Table 2 and the TEM (transmission electron microscope) photographs of the CNTs are shown in Figure 1. In these test conditions, the other influence factors including the refrigerant type, oil concentration, heat flux and initial liquidlevel height are fixed.
The objective of category 2 is to investigate the influences of refrigerant type on the migration characteristics of CNTs. Three types of refrigerants including R113, R141b, and npentane are used in these test conditions, belonging to CFC refrigerant, HCFC refrigerant, and alkane refrigerant, respectively. The reasons for choosing these three types of refrigerants are as follows: (1) R113, R141b and npentane are in liquid state at room temperature and atmospheric pressure while the widely used refrigerants (e.g., R410A) are in vapor state, so it is much easier to prepare refrigerantbased nanofluids based on R113, R141b, or npentane. (2) These three types of refrigerants have different chemical and thermophysical properties including molecular mass, density, dynamic viscosity, etc. The properties of these three refrigerants are given in Table 3. In these test conditions, the other influence factors including the CNTs physical dimension, oil concentration, heat flux and initial liquidlevel height are fixed.
The objective of category 3 is to investigate the influences of oil concentration on the migration characteristics of CNTs. The lubricating oil RB68EP is used in the experiments. RB68EP is an ester oil with a density of 0.964 g·cm^{3} at 15°C and kinematic viscosities of 66.79 and 8.23 mm^{2·}s^{1} at 40°C and 100°C, respectively, as reported by the manufacturer. The oil concentration is from 0 to 10 wt.%, covering the oil concentration in the actual refrigeration system. In these test conditions, the other influence factors including the CNTs physical dimension, refrigerant type, heat flux and initial liquidlevel height are fixed.
The objective of category 4 is to investigate the influences of heat flux on the migration characteristics of CNTs. The heat flux is from 10 to 100 kW·m^{2}, covering the heat flux in the actual refrigeration system. In these test conditions, the other influence factors including the CNTs physical dimension, refrigerant type, oil concentration and initial liquidlevel height are fixed.
The objective of category 5 is to investigate the influences of initial liquidlevel height on the migration characteristics of CNTs. The initial liquidlevel height is from 1.3 to 3.4 cm. In these test conditions, the other influence factors including the CNTs physical dimension, refrigerant type, oil concentration, and heat flux are fixed.
Experimental apparatus
The experimental apparatus used for testing the migration characteristics of CNTs in the refrigerantbased nanofluid pool boiling mainly consists of a pool boiling device, a capture cover and a digital electronic balance, as schematically shown in Figure 2. The pool boiling device mainly consists of a boiling vessel and an electric heating membrane. The boiling vessel is a cylindrical glass container with the inside diameter of 50 mm and the height of 95 mm. The vessel is insulated with glass fibers to reduce heat loss to the surroundings. The electric heating membrane is connected with the directcurrent voltage power supply. The ampere meter with the calibrated precision of 0.5% is used for reading electric current supplied to the heating surface, and a data acquisition system with the calibrated precision of 0.002% is used to measure the voltage across the heating surface. The heat flux through the heating surface is controlled by adjusting the heating power of the plate heater, and is calculated by the measured electric current, voltage, and heating surface area. The uncertainty of heat flux is estimated to be smaller than 1.2%. The capture cover is used to collect the CNTs spouted to the environment. The measurement range of the digital electronic balance is from 10.0 mg to 210.0000 g, and the maximum error is 0.1 mg. All the experiments are performed at atmospheric pressure (101.3 kPa) by venting the boiling vessel to ambient.
Experimental method
The objective of the measurements is to get the migrated mass of CNTs from liquid phase to vapor phase in the refrigerantbased nanofluid pool boiling. Ding et al. [10] have proposed the weighing method to obtain the migrated mass of spherical nanoparticles, and this method is also used in the present study to get the migrated mass of CNTs.
The experimental procedure for the refrigerantbased nanofluid without oil consists of the following steps: (1) adding CNTs with the original mass of m_{n0} to the boiling vessel; (2) weighing the total mass of the boiling vessel and the CNTs, m_{1}; (3) adding refrigerant with the original mass of m_{r0} to the boiling vessel; (4) opening the directcurrent voltage power supply and heating the refrigerantbased nanofluid to be boiling; (5) adjusting the voltage to control the heat flux; (6) weighing the total mass of the boiling vessel and the CNTs, m_{2}, when the refrigerant is entirely evaporated (the signal for the entire evaporation is that the mass of mixture does not change for 12 h); (7) calculating the migrated mass of CNTs with the equation Δm_{n} = m_{1}  m_{2}.
The experimental procedure for the refrigerantbased nanofluid with oil consists of the following steps: (1) adding CNTs with the original mass of m_{n0} and oil with the mass of m_{o} to the boiling vessel; (2) weighing the total mass of the boiling vessel, the CNTs and oil, m_{3}; (3) adding refrigerant with the original mass of m_{r0} to the boiling vessel; (4) opening the directcurrent voltage power supply and heating the refrigerantbased nanofluid with lubricating oil to be boiling; (5) adjusting the voltage to control the heat flux; (6) weighing the total mass of the boiling vessel, the CNTs and oil, m_{4}, when the refrigerant is entirely evaporated (the signal for the entire evaporation is that the mass of mixture does not change for 12 h); (7) calculating the migrated mass of CNTs with the equation Δm_{n} = m_{3}  m_{4}.
Data reduction and uncertainty
In order to quantitatively evaluate the migration degree of CNTs, the migration ratio of CNTs, ζ, is defined by Eq. 1:
where, Δm_{n} is the migrated mass of CNTs, and m_{n0} is the original mass of CNTs.
The original CNTs concentration is defined as the original volume fraction of CNTs in the liquid phase (liquid refrigerant or liquid refrigerantoil mixture), presented as Eq. 2:
where, m_{r0}, m_{o} are the original mass of refrigerant and the mass of oil, respectively; ρ_{n}, ρ_{r, L}, ρ_{o} are the density of CNTs, liquidphase refrigerant and oil, respectively.
The oil concentration is defined as the original mass fraction of oil in the liquid refrigerantoil mixture, presented as Eq. 3:
The relative uncertainty of migration ratio of CNTs is calculated as:
Determined by the accuracy of the digital electronic balance, the maximum uncertainties of the measured migrated mass of CNTs (δ Δm_{n}) and original mass of CNTs (δm_{0}) are 0.2 mg and 0.1 mg, respectively. The maximum relative uncertainty of migration ratio of CNTs is obtained at the condition of the smallest migrated mass of CNTs and the migrated mass of CNTs, and calculated to be 2.5%.
Tests under several conditions were repeated for three times, and it shows that the differences among the three testing results under each condition are less than 3%. Therefore, the experimental results are reproducible.
Experimental results and analysis
Influence of CNTs physical dimension on the migration of CNTs
Figure 3 shows the migration ratio (ζ) of CNTs as a function of original CNTs concentration (φ_{n}) for CNTs with different physical dimensions. The values of ζ under these test conditions are in the range of 5.1% to approximately 27.8%. For fixed CNTs physical dimension, ζ decreases with the increase of φ_{n}. For example, ζ for CNT#1 decreases by 15.8% with the increase of φ_{n} from 0.56 to 3.77 vol.%.
From Figure 3 it can be seen that the migration ratio (ζ) of CNTs increases with the increase of the outside diameter of CNTs (d_{out}) when the length of CNTs (l) is fixed. For example, at the condition of l = 1.5 μm, the value of ζ increases by maximally 286.4% with the increase of d_{out} from 15 to 80 nm. It also can be seen from Figure 3 that the migration ratio (ζ) of CNTs increases with the increase of the length of CNTs (l) when the outside diameter of CNTs (d_{out}) is fixed. For example, at the condition of d_{out} = 15 nm, the value of ζ increases by maximally 25.7% with the increase of l from 1.5 to 10 μm. The possible reasons for the above phenomenon are as follows: The capture of CNTs by the bubbles generated in the pool boiling leads to the migration of CNTs. Brownian diffusion, interception, gravity settling and inertial impaction are four mechanisms for the capture of particles by bubbles [17]. As the CNTs do not exhibit Brownian motion due to their high aspect ratio [18, 19], the capture efficiency of CNTs by bubbles can be considered as the sum of the capture efficiencies caused by interception, gravity settling, and inertial impaction. Each of the above three captured efficiencies increases with Stokes diameter of CNTs. The increase of the outside diameter or the length of CNTs causes the increase of Stokes diameter of CNTs [20], thus the captured efficiency of CNTs by bubbles increases, which leads to the migration ratio (ζ) of CNTs increasing with increase of the outside diameter or the length of CNTs.
Influence of refrigerant type on the migration of CNTs
Figure 4 shows the migration ratio (ζ) of CNTs as a function of original CNTs concentration (φ_{n}) for different types of refrigerants. The values of ζ under these test conditions are in the range of 3.8% to approximately 8.2%. For fixed refrigerant type, ζ decreases with the increase of φ_{n}. For example, ζ for R141b decreases by 19.5% with the increase of φ_{n} from 0.56 to 3.77 vol.%.
From Figure 4 it can be seen that the migration ratio (ζ) of CNTs are in the order of R141b > R113 > npentane, the value of ζ in the R141bbased nanofluid is by maximally 10.7% larger than that in the R113based nanofluid, and is by maximally 77.4% larger than that in npentanebased nanofluid. The possible reasons for the above phenomenon are as follows: (1) The dynamic viscosity values for these three refrigerants are in the order of R113 (5 × 10^{4} Pa·s) > R141b (3.78 × 10^{4} Pa·s) > npentane (1.91 × 10^{4} Pa·s). The larger dynamic viscosity causes the smaller capture efficiencies caused by gravity settling and inertial impaction, which leads to the smaller migration ratio of CNTs. (2) The liquidphase density values of for these three refrigerants are in the order of R113 (1,508 kg·m^{3}) > R141b (1,220 kg·m^{3}) > npentane (606 kg·m^{3}). The larger liquidphase density means the larger mass of liquidphase refrigerant at fixed liquidlevel height, thus the amount of bubbles generated in the pool boiling is larger, which leads to the larger migration ratio of CNTs. The influence of refrigerant type on the migration ratio of CNTs is determined by the conjunct role of the above two aspects, and follows the order of R141b > R113 > npentane. It can be concluded that the migration ratio of carbon nanotube increases with the decrease of dynamic viscosity of refrigerant or the increase of liquidphase density of refrigerant.
Influence of oil concentration on the migration of CNTs
Figure 5 shows the migration ratio (ζ) of CNTs as a function of original CNTs concentration (φ_{n}) for different oil concentrations (x_{o}). The values of ζ under these test conditions are in the range of 1.3% to approximately 7.4%. For fixed x_{o}, ζ decreases with the increase of φ_{n}. For example, at the condition of x_{o} = 5 wt.%, ζ decreases by 28.2% with the increase of φ_{n} from 0.56 to 3.77 vol.%.
From Figure 5 it can be seen that the migration ratio (ζ) of CNTs decreases by maximally 70.7% with the increase of oil concentration (x_{o}) from 1 to 10 wt.%. The possible reasons are as follows: (1) The dynamic viscosity and surface tension of lubricating oil RB68EP are larger than those of pure refrigerant, causing the dynamic viscosity and surface tension of liquidphase refrigerantoil mixture increase with the increase of x_{o}. (2) The increase of dynamic viscosity of liquidphase refrigerantoil mixture results in the decrease of capture efficiencies caused by gravity settling and inertial impaction, which leads to ζ decreasing with the increase of x_{o}. (3) The increase of surface tension of liquidphase refrigerantoil mixture causes the increase of bubble departure diameter in the pool boiling, thus the capture efficiencies caused by interception, gravity settling, and inertial impaction decrease, which leads to ζ decreasing with the increase of x_{o}.
Influence of heat flux on the migration of CNTs
Figure 6 shows the migration ratio (ζ) of CNTs as a function of original CNTs concentration (φ_{n}) for different heat fluxes (q). The values of ζ under these test conditions are in the range of 5.5% to approximately 9.2%. For fixed q, ζ decreases with the increase of φ_{n}. For example, at the condition of q = 10 kWm^{2}, ζ decreases by 21.5% with the increase of φ_{n} from 0.56 to 3.77 vol.%.
From Figure 6 it can be seen that the migration ratio (ζ) of CNTs decreases by maximally 33.9% with the increase of heat flux (q) from 10 to 100 kWm^{2}. The possible reasons are as follows: (1) The increase of heat flux causes the increase of the velocity of departure bubble [21], thus the velocity of rising bubble increases. (2) The increase of velocity of rising bubble results in the decrease of capture efficiency caused by gravity settling, which leads to the decrease of ζ. (3) The increase of velocity of rising bubble results in the increase of capture efficiency caused by inertial impaction, which leads to the increase of ζ. (4) The increase of velocity of rising bubble results in the decrease of the bubble rising time in the liquid phase, causing the decrease of the amount of CNTs captured by bubbles, which leads to the decrease of ζ. The conjunct role of the above aspects leads to the migration ratio of CNTs (ζ) decreasing with the increase of heat flux.
Influence of liquidlevel height on the migration of CNTs
Figure 7 shows the migration ratio (ζ) of CNTs as a function of original CNTs concentration (φ_{n}) for different initial liquidlevel heights (L). The values of ζ under these test conditions are in the range of 3.2% to approximately 19.8%. For fixed L, ζ decreases with the increase of φ_{n}. For example, at the condition of L = 2.7 cm, ζ decreases by 16.5% with the increase of φ_{n} from 0.56 to 3.77 vol.%.
From Figure 7 it can be seen that the migration ratio (ζ) of CNTs increases by maximally 446.9% with the increase of initial liquidlevel height (L) from 1.3 to 3.4 cm. The possible reasons are as follows: (1) The increase of initial liquidlevel height causes the increase of the bubble rising time in the liquid phase, thus the amount of CNTs captured by bubbles, which leads to ζ increasing with the increase of liquidlevel height. (2) The increase of initial liquidlevel height causes the increase of CNTs escape probability on the liquidvapor interface, which leads to ζ increasing with the increase of liquidlevel height.
Prediction of migration ratio of CNTs in the refrigerantbased nanofluid pool boiling
As there is no published literature on the model for predicting the migration ratio of CNTs in the refrigerantbased nanofluid pool boiling, the development of a new model is needed. The CNTs physical dimension, refrigerant type, oil concentration, heat flux, and initial liquidlevel height are five important factors influencing the migration of CNTs, and should be reflected in the new model.
From the beginning of the pool boiling t_{0} to the moment of t, the migration ratio of CNTs can be expressed as:
where, m_{n,t}is the mass of CNTs in the liquid phase at the moment of t; m_{n0} is the original mass of CNTs.
According to the principle of mass conservation, the mass of CNTs in the liquid phase changed with time can be expressed as:
where, K is the migration coefficient of CNTs (i.e., the migration proportion of CNTs caused by single bubble); n_{b} is the number of generated bubbles per unit time.
From Eq. 6, the following equation can be obtained.
Combing Eqs. 5 and 7, can be calculated as:
Therefore, from the beginning to the end of pool boiling, the migration ratio of CNTs is:
In Eq. 9, N_{b} is the total number of generated bubbles from the beginning to the end of pool boiling.
1. The calculation of K
The migration of CNTs can be considered as the capture of CNTs by bubbles combining the escape of CNTs from the liquidvapor interface. In order to describe the capture process of CNTs by bubbles, the capture efficiencies of CNTs caused by interception, gravity settling and inertial impaction should be included in K. In order to describe the escape process of CNTs from the liquidvapor interface, the escape probability of CNTs should be included in K. The original CNTs concentration has influences on the bubble diameter and bubble rising velocity during the pool boiling process of refrigerantbased nanofluid, and then has influence on the migration of CNTs. Therefore, the CNTs concentration impact factor should also be included in K. The expression of K is as follows:
where, α_{I}, α_{G}, and α_{IN} are the capture efficiencies of CNTs caused by interception, gravity settling, and inertial impaction, respectively; β is the escape probability of CNTs; γ is the CNTs concentration impact factor. α_{I}, α_{G}, α_{IN}, β, and γ are expressed as Eqs. 11 to 15, respectively.
In Eqs. 11 to 15, D and H are the bottom diameter and height of boiling vessel, respectively; ρ_{L}, ρ_{b}, ρ_{n} are the density of liquid refrigerantoil mixture, bubble and CNT, respectively; μ_{L} is the dynamic viscosity of liquid refrigerantoil mixture; d_{s} is the Stokes diameter; d_{b} is the diameter of bubble; u_{b} is the bubble rising velocity. The calculation of ρ_{L} and m_{L} are presented in Table 4.
d_{s} can be calculated by Eq. 16 [20]:
d_{b} can be calculated by ColeRohsenow correlation [22], as shown in Eq. 17:
u_{b} can be calculated by Malenkov correlation [21], as shown in Eq. 18:
In Eqs. 17 and 18, C_{p, L}, is the isobaric specific heat of liquid refrigerantoil mixture; σ is the surface tension of refrigerantoil mixture; T_{sat} is the saturation temperature; h_{fg} is the latent heat of vaporization. The calculation of C_{p, L}and σ are presented in Table 4.
2. The calculation of N_{b}
As the original mass of refrigerant is equal to the total mass of generated bubbles from the beginning to the end of pool boiling, N_{b} can be calculated by Eq. 19.
The nine coefficients of a_{1}, a_{2}, a_{3}, a_{4}, b_{1}, b_{2}, b_{3}, b_{4}, and b_{5} in Eqs. 11 to 15 are fitted based on total 105 experimental data in this study. By nonlinear programming solution method, the nine coefficients of a_{1}, a_{2}, a_{3}, a_{4}, b_{1}, b_{2}, b_{3}, b_{4}, and b_{5} can be determined as 0.1, 6.3 × 10^{6}, 1,995.3, 66.9, 2.34, 0.4, 2.26, 8.78, and 0.09, respectively. Therefore, the model for predicting the migration ratio of CNTs in the refrigerantbased nanofluid pool boiling is expressed Eq. 20.
Figure 8a to e shows the comparison between the predicted values of the model with the experimental data for different CNTs physical dimensions, refrigerant types, oil concentrations, heat fluxes, and liquidlevel heights, respectively. It can be seen from Figure 8a to e that the migration ratio of CNTs predicted by the model and the experimental data have the same tendency changing with the CNTs physical dimension, refrigerant type, oil concentration, heat flux, or initial liquidlevel height. The predicted values of the model agree with 92% of the experimental data of migration ratio of CNTs within a deviation of ± 20%, and the mean deviation is 9.96%.
Conclusions
Migration characteristics of CNTs from liquid phase to vapor phase in the pool boiling process of refrigerantbased nanofluid are investigated experimentally, and some conclusions are obtained.

1.
The migration ratio of CNTs increases with the increase of the outside diameter of CNTs or the length of CNTs.

2.
The migration ratio of carbon nanotube increases with the decrease of dynamic viscosity of refrigerant or the increase of liquidphase density of refrigerant. Under the present experimental conditions, the migration ratio of CNTs in the R141bbased nanofluid is by maximally 10.7% larger than that in the R113based nanofluid, and is by maximally 77.4% larger than that in npentanebased nanofluid.

3.
The migration ratio of CNTs decreases with the increase of oil concentration. Under the present experimental conditions, the migration ratio decreases by maximally 70.7% with the increase of oil concentration from 1 to 10 wt.%.

4.
The migration ratio of CNTs decreases with the increase of heat flux. Under the present experimental conditions, the migration ratio decreases by maximally 33.9% with the increase of heat flux from 10 to 100 kWm^{2}.

5.
The migration ratio of CNTs increases with the increase of initial liquidlevel height. Under the present experimental conditions, the migration ratio increases by maximally 446.9% with the increase of initial liquidlevel height from 1.3 to 3.4 cm.

6.
A model for predicting the migration ratio of CNTs in the refrigerantbased nanofluid pool boiling is proposed, and the predicted values of the model can agree with 92% of the experimental data of migration ratio of CNTs within a deviation of ± 20%.
References
Jiang WT, Ding GL, Peng H, Gao YF, Wang KJ: Experimental and model research on thermal conductivity of nanorefrigerant. HVAC&R Research 2009, 15(3):651–669.
Wang RX, Hao B, Xie GZ: A refrigerating system using HFC134a and mineral lubricant appended with nTiO_{2}(R) as working fluids. Proceedings of the 4th International Symposium on HAVC, Tsinghua University Press, Beijing, China 2003, 888–892.
Wang KJ, Shiromoto K, Mizogami T: Experiment study on the effect of nanoscale particle on the condensation process. Proceedings of the 22nd International Congress of Refrigeration, Beijing, China, Paper No 2007. B1–1005 B11005
Bi SS, Shi L, Zhang LL: Application of nanoparticles in domestic refrigerators. Applied Thermal Engineering 2008, 28: 1834–1843. 10.1016/j.applthermaleng.2007.11.018
Choi US, Zhang ZG, Yu W, Lockwood FE, Grulke EA: Anomalous thermal conductivity enhancement in nanotube suspensions. Applied Physics Letters 2001, 79: 2252–2254. 10.1063/1.1408272
Xie HQ, Lee H, Youn W, Choi M: Nanofluids containing multiwalled carbon nanotubes and their enhanced thermal conductivities. Journal of Applied Physics 2003, 94: 4967–4971. 10.1063/1.1613374
Assael MJ, Chen CF, Metaxa I, Wakeham WA: Thermal conductivity of suspensions of carbon nanotubes in water. International Journal of Thermophysics 2004, 25: 971–985. 10.1023/B:IJOT.0000038494.22494.04
Hwang YJ, Ahn YC, Shin HS, Lee CG, Kim GT, Park HS, Lee JK: Investigation on characteristics of thermal conductivity enhancement of nanofluids. Current Applied Physics 2006, 6: 1068–1071. 10.1016/j.cap.2005.07.021
Ding YL, Alias H, Wen DS, Williams RA: Heat transfer of aqueous suspensions of carbon nanotubes (CNT nanofluids). International Journal of Heat and Mass Transfer 2006, 49(1–2):240–250. 10.1016/j.ijheatmasstransfer.2005.07.009
Ding GL, Peng H, Jiang WT, Gao YF: The migration characteristics of nanoparticles in the pool boiling process of nanorefrigerant and nanorefrigerantoil mixture. International Journal of Refrigeration 2009, 32(1):114–123. 10.1016/j.ijrefrig.2008.08.007
Park KJ, Jung DS: Enhancement of nucleate boiling heat transfer using carbon nanotubes. International Journal of Heat and Mass Transfer 2007, 50: 4499–4502. 10.1016/j.ijheatmasstransfer.2007.03.012
Kathiravan R, Kumar R, Gupta A, Chandra R, Jain PK: Pool boiling characteristics of carbon nanotube based nanofluids over a horizontal tube. Journal of Thermal Science and Engineering Applications 2009, 1(2):022001.. 10.1115/1.4000042
Liu ZH, Yang XF, Xiong JG: Boiling characteristics of carbon nanotube suspensions under subatmospheric pressures. International Journal of Thermal Sciences 2010, 49(7):1156–1164. 10.1016/j.ijthermalsci.2010.01.023
Park KJ, Jung DS, Shim SE: Nucleate boiling heat transfer in aqueous solutions with carbon nanotubes up to critical heat fluxes. International Journal of Multiphase Flow 2009, 35: 525–532. 10.1016/j.ijmultiphaseflow.2009.02.015
Park KJ, Jung DS: Boling heat transfer enhancement with carbon nanotubes for refrigerants used in building airconditioning. Energy and Buildings 2007, 39(9):1061–1064. 10.1016/j.enbuild.2006.12.001
Peng H, Ding GL, Hu HT, Jiang WT: Influence of carbon nanotubes on nucleate pool boiling heat transfer characteristics of refrigerantoil mixture. International Journal of Thermal Sciences 2010, 49(12):2428–2438. 10.1016/j.ijthermalsci.2010.06.025
Edzwald JK, Malley JP, Yu C: A conceptual model for dissolved air flotation in water treatment. Water Supply 1990, 8: 141–150.
Prasher R, Phelan PE, Bhattachary P: Effect of aggregation kinetics on the thermal Conductivity of nanoscale colloidal solutions (nanofluid). Nano Letters 2006, 6(7):1529–1534. 10.1021/nl060992s
Xie HQ, Chen LF: Adjustable thermal conductivity in carbon nanotube nanofluids. Physics Letters A 2009, 373: 1861–1864. 10.1016/j.physleta.2009.03.037
Henn AR: Calculation of the stokes and aerodynamic equivalent diameters of a short reinforcing fiber. Particle & Particle Systems Characterization 1996, 13(4):249–253.
Malenkov IG: Detachment frequency as a function of size for vapor bubbles. Journal of Engineering Physics and Thermophysics 1971, 20(6):704–708.
Cole R, Rosenhow W: Correlation of bubble departure diameters for boiling of saturated liquids. Chem Eng Prog Symp Ser 1969, 65(92):211–213.
Jensen MK, Jackman DL: Prediction of nucleate pool boiling heat transfer coefficients of refrigerantoil mixtures. Journal of Heat Transfer 1984, 106: 184–190. 10.1115/1.3246632
Kedzierski MA, Kaul MP: Horizontal nucleate flow boiling heat transfer coefficient measurements and visual observations for R12, R134a, and R134a/ester lubricant mixtures. Proceedings of the 6th International Symposium on Transport Phenomena in Thermal Engineering 1993, 1: 111–116.
Acknowledgements
The authors gratefully acknowledge the support from the National Natural Science Foundation of China (Grant No. 50976065).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
HP carried out the experimental study and model development. GD participated in the model development and design of the experiments. HH participated in the experimental study. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Peng, H., Ding, G. & Hu, H. Migration of carbon nanotubes from liquid phase to vapor phase in the refrigerantbased nanofluid pool boiling. Nanoscale Res Lett 6, 219 (2011). https://doi.org/10.1186/1556276X6219
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556276X6219
Keywords
 Heat Flux
 Capture Efficiency
 Migration Characteristic
 Inertial Impaction
 Pool Boiling Heat Transfer