Abstract.
We have used ellipsometry to measure the glass transition temperature T g of high molecular weight (M w =790 × 103), freely-standing films of atactic poly(methyl methacrylate) (a-PMMA), as well as films of the same polymer supported on two different substrates: the native oxide layer of silicon (Si) and gold-covered Si. We observe linear reductions in T g with decreasing film thickness h for the freely-standing PMMA films with 30 nm <h<100 nm, which is qualitatively similar to previous results obtained for freely-standing polystyrene (PS) films. However the magnitude of the T g reductions for PMMA is much less than for freely-standing films of PS of comparable molecular weight and thickness. We also find that for films supported on either substrate, with thicknesses as small as 30 nm, the T g values do not deviate substantially from the value measured for thick films.
Similar content being viewed by others
References
1. J.L. Keddie, R.A.L. Jones, R.A. Cory, Europhys. Lett. 27, 59 (1994)
2. See, for example, Eur. Phys. J. E 8, 99–266 (2002)
3. For a recent review, see J.A. Forrest, K. Dalnoki-Veress, Adv. Colloid Interface Sci. 94, 167 (2001)
4. J.A. Forrest, K. Dalnoki-Veress, J.R. Stevens, J.R. Dutcher, Phys. Rev. Lett. 77, 2002 (1996); 77, 4108 (1996)
5. J.A. Forrest, K. Dalnoki-Veress, J.R. Dutcher, Phys. Rev. E 56, 5705 (1997)
6. J.A. Forrest, J. Mattsson, Phys. Rev. E 61, R53 (2000)
7. K. Dalnoki-Veress, J.A. Forrest, C. Murray, C. Gigault, J.R. Dutcher, Phys. Rev. E 63, 031801 (2001)
8. A.M. Mayes, Macromolecules 27, 3114 (1994)
9. S. Herminghaus, K. Jacobs, R. Seemann, Eur. Phys. J. E 5, 531 (2001)
10. S. Herminghaus, Eur. Phys. J. E 8, 237 (2002)
11. P.-G. de Gennes, Eur. Phys. J. E 2, 201 (2000)
12. K. Ngai, Rizos, Mater. Res. Soc. Proc. 455, 147 (1997)
13. K. Ngai, Eur. Phys. J. E 8, 225 (2002)
14. D. Long, F. Lequeux, Eur. Phys. J. E 4, 371 (2001)
15. Physical Properties of Polymers Handbook, ed. J.E. Mark (Springer-Verlag, New York, 1996)
16. Y. Grohens, M. Brogley, C. Labbe, M.-O. David, J. Schultz, Langmuir 14, 2929 (1998)
17. Obtained from PSS Polymer Standards Service GmbH.
18. P.J. Flory, Principles of Polymer Chemistry (Cornell University Press, Ithaca, 1953)
19. L.S.A. Smith, V. Schmitz, Polymer 29, 1871 (1988)
20. R.M.A. Azzam, N.M Bashara, Ellipsometry and Polarized Light (North-Holland Publishing Company, Amsterdam, 1977)
21. Optrel GbR, Berlin, Germany
22. Handbook of Optical Constants of Solids, edited by E.D. Palik (Academic, Orlando, 1985)
23. J.L. Keddie, R.A.L. Jones, R.A. Cory, Faraday Discuss. 98, 219 (1994)
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Roth, C., Dutcher, J. Glass transition temperature of freely-standing films of atactic poly(methyl methacrylate). Eur. Phys. J. E 12 (Suppl 1), 103–107 (2003). https://doi.org/10.1140/epjed/e2003-01-024-2
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1140/epjed/e2003-01-024-2