Abstract
Co3O4 was prepared by rheological phase reaction, and the effect of pyrolyzing temperature on the electrochemical performance of Co3O4 was investigated. XRD shows that higher temperature treatment results in sharper diffraction peaks, indicating an increase of particle size of Co3O4. The result of TEM shows that the particle sizes of Co3O4 are about 200 nm. The optimum pyrolyzing temperature is confirmed to be 600°C, and Co3O4 prepared at this temperature exhibits 390.8 F g−1 of specific capacitance in 6 M KOH electrolyte at the scan rate of 5 mV s−1. Co3O4 prepared at the temperature of 600°C shows an excellent cyclability.
Similar content being viewed by others
References
Kötz, R. and Careln, M., Electrochim. Acta, 2000, vol. 45, p. 2483.
Frackowiak, E. and Beguin, F., Carbon, 2001, vol. 39, p. 937.
Vol’fkovich, Y.M., Mikhalin, A.A., and Bograchev, D.A., Russ. J. Electrochem., 2012, vol. 48, p. 467.
Wang, L., Liu, X., and Wang, X., Curr. Appl. Phys., 2010, vol. 10, p. 1422.
Xu, J., Ga, L., and Cao, Electrochim. Acta, 2010, vol. 56, p. 732.
Lin, C., Ritter, J.A., and Popov, B.N., J. Eletrochem. Soc., 1998, vol. 145, p. 4097.
Cui, L., Li, J., and Zhang, X., J. Appl. Electrochem., 2009, vol. 39, p. 1871.
Wu, J.B., Lin, Y., and Xia, X.H., Electrochim. Acta, 2011, vol. 56, p. 7163.
Qing, X., Liu, S., and Huang, K., Electrochim. Acta, 2011, vol. 56, p. 4985.
Gao, Y., Chen, S., Cao, D., Wang, G., and Yin, J., J. Power Sources, 2010, vol. 195, p. 1757.
Xu, J., Gao, L., Cao, J., Wang, W., and Chen, Z., Electrochim. Acta, 2010, vol. 56, p. 732.
Wang, L., Liu, X., Wang, X., Yang, X., and Lu, L., Curr. Appl. Phys., 2010, vol. 10, p. 1422.
Cui, L., Li, J., and Zhang, X., J. Appl. Electrochem., 2009, vol. 39, p. 1871.
Xia, X., Tu, J., Mai, Y., Wang, X., Gu, C., and Zhao, X., J. Mater. Chem., 2011, vol. 21, p. 9319.
Srinivasan, V. and Weidner, J.W., J. Power Sources, 2002. vol. 108, p. 15.
Yuan, Z., Huang, F., and Feng, C., Mater. Chem. Phys., 2003, vol. 79, p. 1.
Yan, J., Wei, T., and Qiao, W., Electrochim. Acta, 2010, vol. 55, p. 6973.
Author information
Authors and Affiliations
Corresponding author
Additional information
Published in Russian in Elektrokhimiya, 2013, Vol. 49, No. 11, pp. 1174–1178.
The article is published in the original.
Rights and permissions
About this article
Cite this article
Zhao, J.C., Gu, Y.J., Lou, J. et al. Rheological phase synthesis and electrochemical performance of Co3O4 for supercapacitors. Russ J Electrochem 49, 1053–1056 (2013). https://doi.org/10.1134/S1023193513110141
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1023193513110141