Abstract
This work is devoted to the effect of processes initiated by the combined action of aging (A) and accumulative roll bonding (ARB) on the evolution of the microstructure and the mechanical characteristics of an Al–0.2 wt % Zr alloy. Upon solution treatment (ST), followed by aging at temperatures of 350 and 450°C, the specimens were subjected to deformation to a degree of deformation of 80% using ARB. The evolution of the microstructure was examined using atomic force microscopy and the mechanical characteristics of the specimens were determined using tensile tests and Vickers microhardness measurements. The results have shown that, upon ten ARB cycles, the grain size decreased to 0.3, 0.4, and 0.32 μm in the specimens subjected to ST followed by ARB (ST–ARB), ST followed by A at a temperature of 350°C and ARB (350°C–A–ARB), and ST followed by A at a temperature of 450°C and ARB (450°C–A–ARB), respectively. This study has also shown that the combined use of preliminary A and subsequent ARB holds promise in enhancing the mechanical characteristics of the alloy due to precipitates that appear in the course of annealing. Fracture surfaces of the rolled specimens subjected to the tensile tests were examined using scanning electron microscopy. The results of these examinations have shown that in the specimens subjected to ST followed by ARB brittle fracture has been observed at the stage of the final ARB cycles, while in the A–ARB specimens cleavage facets (sites of fracture over the cleavage plane) and river lines have appeared on the fracture surfaces.
Similar content being viewed by others
References
B. Azad and E. Borhani, “Pre-aging time dependence of microstructure and mechanical properties in nano-structured Al–2 wt % Cu alloy,” J. Metall. Mater. Int. 22, 243–251 (2016).
R. Z. Valiev, R. K. Islamgaliev, and I. V. Alexandrov, “Bulk nanostructured materials from severe plastic deformation,” Prog. Mater. Sci. 45, 103–189 (2000).
B. Azad and E. Borhani, “The effect of Al2Cu precipitate size on microstructure and mechanical properties of Al–2 wt % Cu alloys fabricated by ARB,” J. Mater. Eng. Perf. 24, 4789–4796 (2015).
E. Borhani, H. Jafarian, A. Shibata, and N. Tsuji, “Texture evolution in Al–0.2 mass % Sc alloy during ARB process and subsequent annealing,” Mater. Trans. 53, 1863–1869 (2012).
E. Borhani, H. Jafarian, D. Terada, H. Adachi, and N. Tsuji, “Microstructural evolution during ARB process of Al–0.2 mass % Sc alloy containing Al3Sc precipitates in starting structures,” Mater. Trans. 53, 72–80 (2011).
Y. Saito, H. Utsunomiya, N. Tsuji, and T. Sakai, “Novel ultra-high straining process for bulk materials— Development of the accumulative roll-bonding (ARB) process,” Acta Mater. 47, 579–583 (1999).
J. Richert and M. Richert, “A new method for unlimited deformation of metals and alloys,” Aluminum 62, 604–607 (1986).
R. Z. Valiev, N. A. Krasilnikov, and N. K. Tsenev, “Plastic deformation of alloys with submicro-grained structure,” Mater. Sci. Eng., A 137, 35–40 (1991).
Z. Horita, D. J. Smith, M. Furukawa, M. Nemoto, R. Z. Valiev, and T. G. Langdon, “An investigation of grain boundaries in submicrometer-grained Al–Mg solid solution alloys using high-resolution electron microscopy,” J. Mater. Res. 11, 1880–1890 (1996).
K. E. Knipling, D. C. Dunand, and D. N. Seidman, “Precipitation evolution in Al–Zr and Al–Zr–Ti alloys during isothermal aging at 375–425°C,” Acta Mater. 56, 114–127 (2008).
K. E. Knipling, D. C. Dunand, and D. N. Seidman, “Precipitation evolution in Al–Zr and Al–Zr–Ti alloys during aging at 450–600 C,” Acta Mater. 56, 1182–1195 (2008).
E. Borhani, H. Jafarian, T. Sato, D. Terada, Y. Miyajima, and N. Tsuji, “Effect of pre-aging on microstructure and mechanical property of Al–0.2 wt % Sc deformed by ARB,” Proc. 12th Int. Conf. on Aluminum Alloy, Japan, 2010.
K. E. Knipling, D. C. Dunand, and D. N. Seidman, “Criteria for developing castable, creep-resistant aluminum- based alloys—A review,” Z. Metallkd. 97, 246–265 (2006).
F. J. Humphreys and M. Hatherly, Recrystallization and Related Annealing Phenomena (Pergamon, New York, 2004).
T. Sato, D. Terada, and N. Tsuji, “Microstructure and aging behavior of Al-0.2 wt%Zr alloy heavily deformed by ARB process,” Mater. Sci. Forum 584–586, 728–733 (2008).
A. L. Berezina, T. O. Monastyrska, O. A. Molebny, V. K. Nosenko, and A. V. Kotko, “Formation processes of nanocomposite strengthening particles in rapidly quenched Al–Sc–Zr alloys,” J. Nano. Electron. Phys. 4, 01006 (2012).
S. G. Jia, M. S. Zheng, P. Liu, F. Z. Ren, B. H. Tian, G. S. Zhou, and H. F. Lou, “Aging properties studies in a Cu–Ag–Cr alloy,” Mater. Sci. Eng., A 419, 8–11 (2006).
J. Zhi-Hong, J. P. Couzinie, N. Cherdoudi, I. Guillot, L. Arnberg, P. Asholt, S. Brusethaug, B. Barlas, and D. Massinon, “Precipitation behavior of Al3Zr precipitate in Al–Cu–Zr and Al–Cu–Zr–Ti–V alloys,” Trans. Nonferrous Met. Soc. China 22, 1860 (2012).
S. H. Lee, T. Sakai, Y. Saito, H. Utsunomiya, and N. Tsuji, “Strengthening of sheath-rolled aluminum based MMC by ARB process,” Mater. Trans. JIM 40, 1422–1428 (1999).
S. Tamimi, M. Ketabchi, N. Parvin, M. Sanjari, and A. Lopes, “Accumulative roll bonding of pure copper and IF steel,” Inter. J. Met. 2014 179723 (2014). doi 10.1155/2014/179723
R. W. Hertzberg, Deformation and Fracture Mechanics of Engineering Materials (Wiley, Singapore, 1989), 3rd ed.
ASM Metals Handbook. Vol. 12: Fractography (ASM, Metals Park, 1987).
B. Azad and E. Borhani, “A study on the effect of nanoprecipitates on fracture behavior of nano-structured Al–2 wt % Cu alloy fabricated by accumulative roll bonding (ARB) process,” J. Min. Metall. Sect. 52, 93–98 (2016).
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © B. Azad, H.M. Semnani, E. Borhani, 2017, published in Fizika Metallov i Metallovedenie, 2017, Vol. 118, No. 1, pp. 91–100.
Rights and permissions
About this article
Cite this article
Azad, B., Semnani, H.M. & Borhani, E. The combined effect of aging and accumulative roll bonding on the evolution of the microstructure and mechanical characteristics of an Al–0.2 wt % Zr alloy. Phys. Metals Metallogr. 118, 87–95 (2017). https://doi.org/10.1134/S0031918X16120024
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0031918X16120024