Abstract
The thermal stability of surface plasmon resonance in a-C:H〈Ag〉 and a-C:H〈Ag + TiО2〉 nanocomposite films is studied. The films were deposited by ion-plasma magnetron sputtering of a combined graphite-metal target in the atmosphere of the argon and methane mixture. The structure and optical properties of nanocomposite films were studied using transmission electron microscopy and optical spectroscopy, respectively. It is found that surface plasmon resonance in the a-C:H〈Ag + TiО2〉 films persists to the annealing temperature of 450°C in argon atmosphere, whereas in a-C:H〈Ag〉 films, surface plasmon resonance disappears at the annealing temperature of 350°C. It is shown that annealing at 350°C leads to the significant increase in the diameter of silver nanoparticles in the structure of the a-C:H〈Ag〉 films. In the a-C:H〈Ag + TiO2〉 films, along with the appearance of silver nanoparticles with a large diameter, silver nanoparticles with a small diameter are present, which remain after annealing at this temperature. The higher thermal stability of surface plasmon resonance in the a-C:H〈Ag + TiО2〉 films is explained by the presence of TiO2 nanoparticles in the structure of films, which inhibit the coalescence of silver nanoparticles at high temperatures.
Similar content being viewed by others
REFERENCES
O. A. Yeshchenko, I. M. Dmitruk, A. A. Alexeenko, A. V. Kotko, J. Verdal, and A. O. Pinchuk, Plasmonics 7, 685 (2012).
Sh. Sarsembinov, O. Prikhodko, A. Ryaguzov, S. Ya. Maksimova, Ye. A. Daineko, and F. A. Mahmoud, Phys. Status Solidi C 7, 805 (2010).
A. D. Muradov, K. M. Mukashev, G. Sh. Yar-Mukhamedova, and N. E. Korobova, Tech. Phys. 62, 1692 (2017).
O. Pena-Rodríguez and U. Pal, Nanoscale Res. Lett. 6, 279 (2011).
K. Lee and M. A. El-Sayed, J. Phys. Chem. B 110, 19220 (2006).
M. K. Hedayati, F. Faupel, and M. Elbahri, Materials 7, 1221 (2014).
J. Okumu, D. Kohl, A. Sprafke, G. von Plessen, and M. J. Wuttig, Appl. Phys. 108, 063529 (2010).
M. Kumar, K. K. Parashar, S. K. Tandi, T. Kumar, D. C. Agarwal, and A. Pathak, J. Spectrosc. 2013, 491716 (2013).
Y. Ohko, T. Tatsuma, T. Fujii, K. Naoi, C. Niwa, Y. Kubota, and A. Fujishima, Nat. Mater. 2, 29 (2003).
L. Armelao, D. Barreca, G. Bottaro, A. Gasparotto, C. Maccato, E. Tondello, O. I. Lebedev, S. Turner, G. van Tendeloo, C. Sada, and U. L. Stangar, Chem. Phys. Chem. 10, 3249 (2009).
S. A. Khan, D. K. Avasthi, D. C. Agarwal, U. B. Singh, and D. Kabiraj, Nanotecnology 22, 235305 (2011).
J. Garcia-Serrano and U. Pal, Int. J. Hydrogen Energy 28, 637 (2003).
R. J. Sernaa, J. M. Ballesterosa, J. Solisa, C. N. Afonsoa, D. H. Osborneb, R. F. Haglund, and A. K. Petford-Longc, Thin Solid Films 318, 96 (1998).
M. Kumar and G. B. Reddy, Phys. Status Solidi B 246, 2232 (2009).
M. Kumar and G. B. Reddy, Phys. E (Amsterdam, Neth.) 43, 470 (2010).
M. Kumar, P. K. Kulriya, J. C. Pivin, and D. K. Avasthi, J. Appl. Phys. 109, 044311 (2011).
K. Manish, C. S. Suchand Sandeep, G. Kumar, Y. K. Mishra, R. Philip, and G. B. Reddy, Plasmonics 9, 129 (2014).
Š. Meškinis, A. Čiegis, and A. Vasiliauskas, Nanoscale Res. Lett. 11, 146 (2016).
U. Kreibig and M. Vollmer, Optical Properties of Metal Clusters (Springer, Berlin, Heidelberg, 1995).
A. Stalmashonak, G. Seifert, and A. Abdolvand, Ultra-Short Pulsed Laser Engineered Metal-Glass Nanocomposites, Springer Briefs in Physics (Springer, Berlin, 2013).
O. A. Yeshchenko, I. S. Bondarchuk, V. S. Gurin, I. M. Dmitruk, and A. V. Kotko, Surf. Sci. 608, 275 (2013).
S. A. Maier, Plasmonics: Fundamentals and Applications (Springer, New York, 2007).
M. Kumar, T. Kumar, and D. K. Avasthia, Scr. Mater. 105, 46 (2015).
O. Yu. Prikhodko, S. L. Mikhailova, Ye. S. Mukhametkarimov, S. Ya. Maksimova, N. K. Manabaev, and K. Dauthan, Proc. SPIE 9929, 99291G (2016).
O. Prikhodko, S. Mikhailova, Ye. Mukhametkarimov, K. Dauthan, and S. Maksimova, Opt. Spectrosc. 123, 383 (2017).
D. Manikandan, S. Mohan, and K. G. Nair, Mater. Res. Bull. 38, 1545 (2003).
Y. H. Kim, C. W. Kim, H. G. Cha, D. K. Lee, B. K. Jo, G. W. Ahn, E. S. Hong, J. C. Kim, and Y. S. Kang, J. Phys. Chem. 113, 5105 (2009).
ACKNOWLEDGMENTS
We are grateful to V.N. Mochalin (Missouri University of Science and Technology, Rolla, Missouri, United States) for the fruitful discussion of experimental results. The work was supported by the Committee of Science of the Ministry of Education and Science of the Republic of Kazakhstan (project no. AR05132897).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated by L. Mosina
Rights and permissions
About this article
Cite this article
Prikhod’ko, O.Y., Mikhailova, S.L., Mukhametkarimov, E.S. et al. Thermal Stability of Surface Plasmon Resonance Absorption in а-С:Н〈Ag + TiО2〉 Nanocomposite Films. Opt. Spectrosc. 125, 864–869 (2018). https://doi.org/10.1134/S0030400X18120160
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0030400X18120160