Abstract
Photoinduced threshold switching processes that lead to bistability and the formation of metastable phases in photoinduced phase transition of VO2 are elucidated through ultrafast electron diffraction and diffusive scattering techniques with varying excitation wavelengths. We uncover two distinct regimes of the dynamical phase change: a nearly instantaneous crossover into an intermediate state and its decay led by lattice instabilities over 10 ps timescales. The structure of this intermediate state is identified to be monoclinic, but more akin to M2 rather than M1 based on structure refinements. The extinction of all major monoclinic features within just a few picoseconds at the above-threshold-level (~20%) photoexcitations and the distinct dynamics in diffusive scattering that represents medium-range atomic fluctuations at two photon wavelengths strongly suggest a density-driven and nonthermal pathway for the initial process of the photoinduced phase transition. These results highlight the critical roles of electron correlations and lattice instabilities in driving and controlling phase transformations far from equilibrium.
Similar content being viewed by others
Introduction
Phase transitions are often discussed within the context of thermal equilibrium where distinct phase change phenomena are described in the complex phase diagram in which temperature, chemical doping, or pressure are steady-state tuning parameters. Much less is understood in terms of excited states and dynamical phase transitions induced after sudden excitations using intense laser pulses1,2. In this strongly nonequilibrium condition, the thermodynamic ground state may become less stable than its counterparts and metastable new phases may emerge3,4. Characterizing the nonequilibrium transformations between two thermodynamic phases directly or through a metastable phase indirectly may provide valuable insights regarding the nature of these states, the interactions, and the active coordinates involved in these phase transitions5.
As a prime example of phase transitions, the metal-to-insulator transition in VO2 has attracted wide-spread attention and is one of the best studied at the ground states near equilibrium. Pristine VO2 crystals undergo a first-order transition from a high-temperature metallic phase with a rutile (R) structure to a low-temperature insulating phase with a monoclinic (M1) structure at the transition temperature Tc = 340 K6,7,8. The introduction of electron9 and hole10 doping changes the transition temperature, as well as leads to the appearance of new phases such as M2 and T, resulting in a complex phase diagram as illustrated in Fig. 1(a). To decipher the apparent synergy between the electronic and lattice degrees of freedom culminating to a large-scale electronic switching11,12, scenarios involving both Mott-Hubbard10,13 and Peierls14,15 physics were proposed, and their verifications have been the subjects of intense experimental investigation, particularly using ultrafast pump-probe approaches15,16,17,18,19,20,21,22 to transiently isolate the active components.
Phase transitions of VO2.
(a) Layout of the phase diagram of VO2, along with the schematic diagram of structural displacements in each phase. (b) The time-dependent diffraction curves from VO2 films driven by 800 nm pulses, presented in difference map (reference −20 ps). The simulated diffraction curves, in log scale along with the corresponding Miller indices, based on known crystalline phases are overlaid atop the difference map for comparison. (c) The M1-to-R transition curves under the steady-state heating (black) and under excitations of near-IR (800 nm, blue) pulses, mid-IR (2000 nm, red) pulses. The solid curves are error function fittings to derive the critical energy density ΔHC and transition window specified by ΔHC ± 2σ. The initial sample temperature is 294 K.
Among the established work, ultrafast insulator-metal transition (IMT) has been the early focus using ultrafast optical pump-probe techniques. A view based on the temporal hierarchy suggested a nonequilibrium nature of transformations, judged from the ~100 fs timescale optical responses22,23,24 and x-ray absorption changes25, which clearly is decoupled from the structural transitions expected to proceed on ps electron-phonon coupling or longer timescale. This ultrashort temporal response in optical properties may reflect the differences in heat capacity in electronic and lattice degrees of freedom, thus yielding different response times in suppressing the respective order parameters (optical gap and diffraction intensity) through coupling between transiently isolated sub-systems26,27. However, through pump-fluence dependent studies, the evidences of decoupling on the long-range scale between electronic and structural phases were demonstrated in the observation of a threshold for the onset of IMT to be ≤ 1 mJ/cm2 20,24, in distinct contrast to the onset fluence of 4–8 mJ/cm2, identified for the monoclinic–to-rutile structural changes using electron16,27,28 and x-ray17 diffraction or from persistent THz conductivity20,21. From the viewpoint of displacive excitation of coherent phonons29, the interplay between the electronic and lattice degrees of freedom were examined. Notably, structural bottleneck in IMT is proposed based on a minimum transition time of ~75 fs, which corresponds to one-half period of the Ag phonon modes that stretch and twist the V-V dimers as the active modes driving the electronic changes15. More detailed classification of the modes18,20,30 and their role as active modes pertaining to insulating or metallic phase30, as well as emerging anisotropy near critical temperature26, were reported, suggesting the involvements of different phonon modes during the phase transitions. In particular, two distinct symmetry changes involving the initial steps of monoclinic-to-rutile transformation were identified through ultrafast electron diffraction16,28. Meanwhile, in the strongly driven regime, a sub-60 fs band-gap collapse breaking the structural bottleneck timescale was demonstrated in ultrafast photoemission studies, implying the dominant energy scale at the Fermi energy being the electron correlations22,31. Given the temporal hierarchy and the distinct thresholds between the electronic and structural transitions, a new monoclinic metallic phase that bridges the two transition has been suggested18,27 and their presence as a long-lived metastable state induced under photoexcitations28,32,33, or induced under strong stress34,35 and/or carrier doping27,35 were increasingly reported. Identifying the emergence of such a new state and clarifying its role in mediating the electronic and structural transformations are of major interests to address key open questions regarding the apparent complexities involved in the phase transition of VO2.
In this work, we present controlled studies to examine the transient emergence of new metastable phases and their nonequilibrium dynamics during photoinduced phase transitions of VO2 using femtosecond electron diffraction16,36,37 and diffusive scattering techniques, which allow us to directly monitor the momentum-dependent lattice dynamics. With different wavelengths of optical pumping, we demonstrate that the photoinduced phase transitions in VO2 is non-thermal, evidenced by the fact that the optical threshold of the phase transition is best described in terms of photodoping rather than the energy density. By investigating the transient diffraction patterns, we discover a unique interaction-driven monoclinic emergent state that, interestingly, has a similar crystal symmetry as the thermodynamic M2 phase. Our results show that the photoinduced phase switching between the insulating M1 and the metallic R phases can be significantly more efficient by accessing the intermediate phase and the new correlation-driven pathways.
Results and Discussion
In our experiments, we employed ultrafine films of VO2 nanocrystalline grains (size 31 ± 7 nm) prepared on a 9 nm amorphous Si membrane using vapor deposition method (see Methods). The grain size and nanofilm settings were chosen to leverage their flexibility on the nanometer scale to avoid excessive stress27,38 that may otherwise develop during disruptive structural transitions. These samples display high crystallinity from clear crystalline powder diffraction (see Supplementary Fig. S1). Using the ultrafast electron diffraction setup5 (see Methods), the patterns of time-dependent diffraction are recorded in the difference map in Fig. 1(b), where the patterns from different known VO2 crystalline phases39,40,41 are also shown. Sufficiently low repetition rates (≤500 Hz) were employed to avoid irreversible changes [see Supplementary Information (SI) for details]. The major sequence of events associated with symmetry-recovery phase transition from M1 to R can be identified based on the evolution of relative Bragg intensities. Such evolution is sensitive to changes in the two critical lattice distortions (pairing and twisting) along the V-V sub-lattice chains (A and B), as depicted in Fig. 1(a). For example, the ultrafast transformation of the distorted M1 is measured by diminishing pairing-specific reflections [e.g. (3, 0, −2), (1, 0, −2), (3, 1, −3)] in the early transition, whereas at the later times formation of the undistorted R is confirmed from specific enhancements and movements of the high-symmetry peaks.
Our controlled studies were based on femtosecond (45 fs) infrared (IR) pumping using two different photon wavelengths, 800 nm and 2 μm (photon energy Eλ = 1.55 and 0.62 eV respectively), through which different energy densities were absorbed by the VO2 crystals to produce a similar number of electron-hole pairs. The transition curves presented in Fig. 1(c) were obtained by incrementally increasing the laser fluence while observing the intensity of order-parameter reflection (3, 0, −2) at +150 ps delay. Indeed, using near-IR (800 nm) pump pulses we observed clear threshold switching behavior with the transition at a critical fluence FC ~ 7 mJ/cm2 (determined by fitting with the error function) at room temperature. This is within the range of previously identified thresholds (4–8 mJ/cm2) also under 800 nm photoexcitation16,19,20,22,27,28,30,31. We note that in order to precisely determine the pump-laser fluence, we measure the pump-laser spot size in situ by the knife-edge and laser-electron cross-correlation measurements (see Methods and SI). The error of fluence measurements introduced by laser-spot size measurements is no more than 25%. To compare with thermal transition, the absorbed optical energy density ΔH is calculated from the applied fluence F by ΔH = Fγ/d, where d is the film thickness. The absorption coefficient γ is carefully determined through measuring the wavelength-dependent transmittance and reflectance using the transfer matrix method on the as-grown VO2 films (see SI for details). Based on FC, the critical energy dose ΔHC for 800 nm pump is ~2 eV/nm3 which is close to the thermal requirement (2.32 eV/nm3) for transition between M1 and R42, calculated based on integrating heat capacity and latent heat (see SI for details). This similarity between ΔHC estimated from photoinduced and thermal transitions has been the reason behind considering the near-IR-driven phase transition as quasi-thermal in the established work. However, we show that the mid-IR (2 μm) pumping leads to a much smaller critical dose (ΔHC ~1 eV/nm3). This unexpected result is demonstrated over a range of temperatures [Fig. 2(a)], where we consistently observe a subthermal critical dose under mid-IR whereas the transition under near-IR occurs close to the thermal threshold. However, this disparity may be reconciled by converting the critical energy density to the absorbed photon density nC = ΔHc/Eλ depicted in Fig. 2(b). The critical lines separating M1 and R as defined by nC determined using the two optical excitations then agree quite well. This result thus indicate that the fundamental process of photoinduced phase transitions is very different from a thermally induced transition, and strongly suggests a density-driven mechanism at play in the photoinduced phase transition between M1 and R phases1.
Phase transitions of VO2 under optical pumping.
(a) The transition critical energy density, ΔHC (solid) and ΔHC ± σ (dash), as a function of crystal temperature TB under two different optical excitations. The thermal critical threshold (dash, black) is also plotted for comparison. The inset in (a) shows the efficiency based on normalizing the ΔHC associated with the photoinduced transitions obtained for each TB with the corresponding ΔHC from the thermal transition. (b) The optical doping – temperature phase diagram, converted from (a), where the photon density n = ΔH/Eλ, the doping x = n·VR, and the VO2 formula volume VR = 2.96 × 10−23 cm3. (c,d) The diffraction difference curves ΔI(s, t) obtained by subtracting the reference ground state curve (−20 ps) from the time-dependent diffraction curve I(s, t). To highlight the trend of the diffusive scattering evolution, curves are obtained by fitting the baseline line using a 4th order polynomial function via maximizing the non-negativeness of ΔI(s, t) (see text). The inset in (c) shows the temperature-dependent diffusive scattering curves obtained at 150 ps. The inset in (d) illustrates the interband transitions induced by 800 nm and 2 μm pump lasers from the d|| band to the π* band of VO2. The density of states qualitatively reproduce the results in ref. 11.
We note that our results are distinctly different from the conclusions drawn in ref. 24, which we believe can be attributed to the difference in experimental approaches. In ref. 24, the optical response shortly after pump excitation (+200 fs) was monitored leading to the reported thresholds of the absorbed energy density several times smaller than our results and other work16,18,19,20,21,28,30. Indeed, as shown in previous THz spectroscopy studies18,19,20,21, even though the optical conductivity is increased by laser-induced photodoping in ~100 fs, such increment decays within 1 ps so that it does not persist to induce a full phase transition in VO2. In our experiments, however, we monitor the VO2 structure at a time well after pump laser excitation (+150 ps) in order to observe the threshold of the full photoinduced phase transitions.
The discovery that the mid-IR-driven structural transformation is significantly subthermal has direct ramifications in understanding the unconventional features of photoinduced phase transitions in VO2. In particular, the fact that ΔHC required for driving transition from M1 to R by pumping VO2 with the mid-IR photons is even below the thermal latent heat (1.47 eV/nm3)42,43 [Fig. 2(a)] suggests a very different pathway that does not involve significant entropy and that may be facilitated by strongly interacting electrons similar to the pathway of chemical doping as elucidated by the phase diagram [Fig. 1(a)]. In such a scenario, the photoexcitation explores excited energy landscape with new emergent properties as defined by a reconstructed energy landscape induced by photodoping, which are not the same as those pertaining to the temperature-driven phases3,4,5. Nonetheless, thus far, the understanding of the emergent state properties focuses on the effect of photodoping, whereas the frequently used near-IR pulses (Eλ = 1.55 eV) not only excite charge carriers that promptly induce doping of correlated electron orbitals, but also impart their excessive photon energy (Δ = Eλ − Eg, Eg = 0.6 eV is the optical gap44,45) which can translate to the lattice as stochastic heating at a timescale of 10 ps and longer. The application of mid-IR pulses (0.62 eV) thus represent an important test scenario where at the same level of charge carrier excitation, their initial excessive photon energy is reduced by nearly an order of magnitude compared to near-IR excitations. To carefully evaluate the impact of both doping and thermal effects, we resort to directly observing the details of the nonequilibrium dynamics under two different photon wavelengths. To follow the coherent structural evolution driven by the sudden electronic impact, we examine the time-dependent coherent Bragg diffraction. Meanwhile, to gauge the role of lattice instabilities and thermal fluctuations we monitor the diffusive scattering away from the Bragg peaks.
Given the short wavelength of the electron beam, the large Ewald sphere associated with ultrafast electron diffraction experiments provides an easy access to short and long-range scale dynamics manifested in both Bragg diffraction and diffusive scattering channels in the reciprocal space that are simultaneously recorded with an area detector. First, we examine the lattice structural evolution during VO2 phase transition, where the critical lattice distortions (pairing and twisting) along the chains A and B [Fig. 1(a)] are at the level of 7% of the interatomic V-V distance (~2.8 Å) or less. These subtle changes lead to only a few percent adjustments of key Bragg peak intensities and are best described in the diffraction difference curve ΔI(s, t) at different pump-probe time delays (t) as depicted in Fig. 2(c) and (d). Here, ΔI(s, t) = I(s, t) − I(s, t < 0), where I(s, t) is the 1D scattering wave-vector (s)-dependent pattern reduced by radially averaging the 2D powder diffraction patterns as shown in the Supplementary Fig. S2(b). We note Fig. 2(c) and (d) are obtained using two different pump lasers (800 nm and 2 μm) set at the upper density threshold [nc2 = ΔHc2/Eλ, see Fig. 1(c)], but differing in energy density delivered to VO2 nanocrystals. It is intriguing to see that despite of very different excess energy imparted in VO2 crystals, the ultrafast timescale relative changes in the Bragg diffraction show nearly synchronous evolution between the near-IR and mid-IR excitations. These ultrafast cooperative evolutions feature the suppression of pairing-specific peaks and the transfer of scattering weight to higher symmetric peaks. These processes describe a transition from M1 to a new state with lower lattice distortions being induced by carrier excitations rather than heating.
Next, we turn our attention to the evolution of diffusive scattering (DS) in the region between the Bragg peaks. In the steady-state investigation, DS has traditionally been the source of information for probing the lattice fluctuations and inhomogeneous strain46, and in the case of 2D diffraction from nanocrystals, such signals are isotropically integrated, forming a smooth background underneath the Bragg peaks. In ultrafast diffraction, the time-independent common background of I(s, t < 0), predominantly consisted of incoherent features such as the atomic background and elastic scattering from atomic impurities, are effectively removed in ΔI(s, t). Therefore, the observed background changes represent the photoinduced features, including inelastic phonon scattering and inhomogeneous strain that evolves as a function of time after pump-laser excitation. Two distinctive dynamics differentiated by their momentum transfer (s) and timescale are observed. First, in proximity to the Bragg peaks, the diffusive background exhibits sub-ps suppression. This feature correlates well with an ultrafast shift in the bonding state featured also in the recovery of local symmetry witnessed earlier in the Bragg diffraction on a similar timescale. Here, the suppression of DS represents a reduction of non-uniform strain present in nanocrystals, as part of global symmetry recovery dynamics. Meanwhile, we observe an increase of DS at the small s (in regions below the coherent Bragg diffraction) that continues over ps timescales. This enhanced DS at small s signifies the emergence of unique longer wavelength correlations, which is highly dependent on the excitation wavelength. We can correlate the contrasting long-wavelength DS in Fig. 2(c) and (d), drawn on the same relative scale, with the different applied photon excess energies. Much larger increase is seen on ~10 ps timescale under 800 nm excitation than under 2 μm excitation. The correlation between such DS and crystal temperature can also be established from the temperature-dependent studies [see inset of Fig. 2(c)], where such an enhancement is reduced at lower temperature under the same optical dose (Δnc2) over a longer time (+150 ps). Note, to guild the eyes, the overall trend of DS can be followed through the curves underneath the ΔI(s, t), and those presented for the temperature-dependent studies, generated through a 4th order polynomial fit of ΔI(s, t) via optimizing the non-negativeness – a practice also used in isolating the incoherent scattering background contribution in powder diffraction curves47,48. The fact that a significantly lower level of lattice instabilities was found when the mid-IR pump was applied compared to the near-IR one suggests a much lower energy dose being transferred to the lattice. These clear wavelength-dependent results support that the initial photoinduced phase transition is indeed nonthermal.
To further identify the density-driven state featured by the coherent structural evolution, we examine the transient evolution of the intensity and position of phase-sensitive Bragg peaks over s = 3.5 to 4.5 Å−1 (Fig. 3). These changes are monitored in reference to the initial (M1) and final (R) state parameters both in the longer [Fig. 3(a)] and in the ultrafast [Fig. 3(b)] timescales. Judging from the Bragg peak intensity changes [(4, 0, −2) and (2, 2, 0)/(2, −1, 1) in Fig. 3(a)], we find that the transition into a metastable phase, which is neither M1 nor R, is established following initial cooperative structural evolutions (stages I & II, to be discussed later), as further detailed in Fig. 3(b) along with several other reflections. The metastable phase starts its relaxation into R at a well-defined onset time ~15 ps as characterized by a sharp drop of (4, 0, −2) and (2, 2, 0)/(2, −1, 1) intensity (stage IV) as depicted in Fig. 3(c). But the changes are different over two different excitations, in particular with regard to generation of acoustic oscillations that are seen in the modulation of the Bragg intensities. Scenarios to a stable excited electronic manifold due to the soft-band effect in the narrow-gap Mott insulator VO2 have recently been proposed theoretically49. In our experiments, the above-the-gap photoexcitations inject electrons into the spatially extended π* (V3d-O2p), and leave holes in the localized spin-singlet d|| (V3d-V3d) orbitals (see inset of Fig. 2(d))8,11, effectively prompting hole doping. Given the spatially decoupled orbital symmetry between these states that weakens excitonic coupling50, the long-lived excited charge carriers can drive ps timescale structural evolution into a new state which is a local minimum in the excited energy landscape. Furthermore, given the strongly interacting nature44,51 the evolution may proceed beyond the rigid-band picture11,12, and establish a new metastable state. This correlation-driven dynamics for reconstructing the electronic energy landscape can be reconciled with the density-driven characteristics as witnessed here, and more specifically the relevant energy scale for triggering the phase transition is set by the hole doping concentration defining the well-established threshold behavior5. Meanwhile, with the elevated transient photo-carrier concentration (up to ~1021 cm−3) the emergent state could exhibit metallic transmissivity28 and THz conductivity18,20, despite that it is not in a true metallic ground state.
Ultrafast evolutions of Bragg diffraction and diffusive scattering.
(a) The intensity and position evolutions of the selected Bragg peaks during structural phase transition from M1 to R. The laser doses for two different excitations (800 nm and 2 μm) are set to nc2 ~ 1.85 nm−3, which is above the transition critical dose (nc = 1.25 nm−3) at crystal temperature TB = 294 K. (b) The scale-up view of the transitions for the first 10 ps, during the formation of metastable phase M2*, under 800 nm excitation, including both low-symmetry pairing specific and higher-symmetry reflections. (c) The scale-up view of the transitions in the intermediate timescale where the decay of metastable phase occurs. The evolution of diffusive scattering amplitude monitored at s = 1.7 Å−1 are also depicted for comparison. (d) Scale-up view of the center-of-mass position evolution of the (2, 2, 0) & (2, −1, 1) diffraction groups.
According to our results shown in Fig. 3, there appears to be no direct pathway connecting M1 to R over the excited landscape in the density-driven regime. The cooperative structural evolutions into the metastable phase presented here were obtained at the same doping level nc2, which is ~20% above the mean threshold of the transition. Meanwhile, an excitation-wavelength-dependent contrasting build-up of the long-wavelength diffusive scattering [Fig. 3(c)] on the timescale of the decay reflects the different applied photon energies translating into lattice instabilities. The relaxation of the emergent state, which, according to its correlation to the diffusive scattering changes, can be associated with instability-driven decay of charge carriers. The process is disruptive enough to initiate strain waves manifested in the breathing mode of VO2 nanograins, as observed in the oscillations of the diffraction intensity in Fig. 3(c). The oscillations are more pronounced when driven by the near-IR photons, which also leads to a shorter decay time (6 ps), as compared to the mid-IR pump (40 ps). The timescales are fitted with a function of exponential decay modulated by chirped harmonic oscillations. The oscillation period shifts from ~13 ps at the onset to ~25 ps near the end of each decay, suggesting a varying sound speed from 4.5 km/s to 2.5 km/s (based on breathing mode over ~30 nm grains). It is worth to mention that the lattice softening leading to a similar change of the sound velocity during monoclinic-to-rutile phase transition was also observed previously52. Given that the supporting ultrathin Si film for growing the VO2 is amorphous, it is expected that the sample-substrate strain mismatch as shown in previous work34 does not contribute to our results. Therefore, we expect the evolution of the strain is intrinsic to the VO2 nanocrystal induced during phase transitions. It is also worth noting that the onset of the transition correlates well with a build-up of long-wavelength fluctuations near unitcell distance or longer (~2π/sC, sC ≥ 1.7 Å−1) revealed in the diffusive scattering [Fig. 3(c)], suggesting median range lattice fluctuations to be effective in facilitating carrier relaxations.
The energy-dependent nonequilibrium dynamics reported here elucidate the exceptional nature of the density-driven photoinduced phase transitions in VO2, which may be similar to the photoinduced insulator-metal transition involving charge-density wave transformation in TaS25. In particular, the density-driven emergent state offers a new pathway to reach a stable R phase by circumventing the energy and time consuming entropic barrier. Regarding the identity of the emergent state, we conduct structure analysis based on the integrated intensity evolution leading to such a phase, as depicted in Fig. 4(a) [compared to Fig. 3(b), the intensity is integrated over the Bragg peak envelop after removing the scattering background]. The transition shown in the evolution of (2, 2, 0), (2, 3, 1) and (4, 0, −2) intensities over stages I&II indicates separate steps of lattice relaxations. The suppression up to 70% of (3, 0, −2), (3, 1, −3) intensities is the dominant feature during stage I, which indicates a de-pairing process based on symmetry argument. Meanwhile, changes over higher symmetry reflections along different planes are also observed, suggesting a three-dimensional structural changes. With the lattice parameters frozen, we conduct analyses on the initial different structural transformations directed along the two critical structural modes (pairing and twisting) on the A and B sub-lattice chains.
Ultrafast transformation pathways of VO2.
(a) The integrated intensity changes based on the data presented in Fig. 3 (with diffusive background subtraction) under 800 nm excitation. The dashed lines are drawn as a guide to the eyes. (b) Simulated intensity changes based on a two-step transition model along the pathways to reduce the lattice distortions along two critical modes [coordinates depicted in (c)]: (I) from M1 to M2* (transition state), and (II) from M2* towards R. (c) Conceptual depiction of interaction energy landscape in the multistep phase evolutions along with a plot depicting the corresponding time steps and changes along de-pairing and detwisting coordinates estimated from the experimental data.
We find that processes in stages I&II depicted in the diffraction intensity evolution [Fig. 4(a)] can be emulated through a pathway in which M2* (*denotes nonequilibrium, excited nature) serves as a metastable intermediate structural motif, where half of the chains are unpaired, while the other half are untwisted, as shown in Fig. 4(b) [skeleton evolution depicted in Fig. 4(c)]. In contrast, simultaneously or sequentially reducing the pairing and twisting of both sublattice chains cannot capture the key features of the experimental data (see SI for details). From the perspective of crystalline state evolution, the initial switchover to M2* is also identified from the appearance of M2 (1, 1, 3) reflection (representing unitcell doubling in the basal plane) near s = 4 Å−1 as shown in Fig. 1(b). The transition into this new motif and its relaxation can be analyzed from monitoring the center-of-mass evolution of the reflection group containing the M2-specific reflection and nearby monoclinic (2, 2, 0) and (2, −1, 1) reflections in total diffraction. As shown in Fig. 3(d), the center-of-mass position initially moves toward strengthening the M2 characters, opposite to what would occur if the structure directly evolves into R, which occurs only after the second transition (stage IV) as shown in Fig. 3(a).
Conclusion
Based on the excitation dose, wavelength, and temperature-controlled studies, the photoinduced phase transitions of VO2 are inspected over the dynamical signatures from multiple scattering channels, including Bragg diffraction, diffusive scattering, and coherent oscillation as a probe for acoustic waves. Several new observations were made which can be correlated with earlier pump-probe and thermodynamic measurements to address the on-going questions. Firstly, we show that the ultrafast dynamics of photoinduced phase transition in VO2 is density-driven and can be significantly subthermal using long wavelength photons. Secondly, we demonstrate that the phase transition involves at least two main steps with a well distinguishable intermediate state taking on a motif akin to M2, coupling to concerted detwisting and depairing along two different V-V sublattice chains. This symmetry change is consistent with the hole- doping picture10 for the initial evolution, but the extent of excess holes at the threshold level may be adequate to drive the system metallic22,24. Thirdly, we identify the unusual roles of the transient stress and their remediation through the launch of impulsive acoustic waves coupled to wavelength-dependent diffusive signatures of lattice instabilities that trigger such events. Given the decisive role of this strain relief in transitioning into the final rutile phase, one may envision using strain as a control parameter for phase transition. This may also help understand several recent accounts of unusually stable photoinduced monoclinic metal under the influence of stress33,35. Conversely, by exploiting the flexibility associated with amorphous-membrane-supported ultrafine VO2 nanocrystalline systems to reduce the role of the transient stress, a relatively unhindered high speed interaction-driven switching may be established.
Regarding whether the results reported here are applicable to single-crystal systems, we first draw comparisons between the temperature-mediated and photoinduced phase transition in both single-crystal and polycrystalline systems. Previous study of VO2 nanobeams gently placed (nearly stress-free) on a substrate showed extremely narrow transition width for both thermally and optically induced transitions (<0.2 K, <0.1 mJ/cm2 respectively)27, whereas the phase transitions in epitaxially grown VO2 sample can be broadened by up to tens of K due to the static strain induced by sample-substrate mismatch34. Meanwhile, in the nanocrystalline film reported here, the thermal transition is inhomogeneously broadened due to surface stress while experiencing lesser external stress from the substrate due to its amorphous nature. It is expected that this inhomogeneous broadening will be translated to optically driven transformation, nonetheless, we demonstrate that the difference in the thresholds observed here using two different photon wavelengths greatly exceeds the inhomogeneous widths of the respective transformations [Fig. 1(c)]. Therefore, the underlying physics of the interaction-driven transition and the emergence of transient metastable state are robust against inhomogeneity. It is interesting to point out that while the onset threshold of our experiments is found to be consistent with earlier studies using both polycrystalline and single-crystal samples16,20,21,22,28, the full switching threshold witnessed here is substantially lower than earlier results because of the avoidance of excessive transient stress. We expect the same processes to occur in single-crystal VO2 systems, particularly when steps are taken to reduce the external constraint to avoid both static and transient stress that may serve as a feedback to influence the phase transition dynamics as described earlier. Future more sensitive experiments on isolated single-crystal nanobeams under controlled stress and excitation wavelengths should provide more information on the anisotropic phonon softening tied to the phase transition and elaborate on the mechanism responsible for the decay of the metastable phase under the influence of stress.
Finally, the findings presented here should be relevant to the development of new electronic applications. Our observations suggest that carrier doping to be the key mechanism to induce the metastable M2* doorway state, which facilitates the ultrafast conversion of insulating M1 into metallic phase, even under a subthermal scenario. It is therefore reasonable to suggest that such a channel might be active through the nonequilibrium transport studies where hot carriers could be directly injected via intense current pulse or electrostatic gating. Indeed, tantalizing evidences of nonthermal insulator-metal switching53,54 operated at very high speed (~1 ns, resolution-limited) in sandwiched nanoscale VO2 film has recently been reported55. Whether or not a similar pathway is involved in the electrically driven transition as in the photo-doping scenario awaits further elucidation. It would be very interesting to explore the avenue of optically assisted insulator-metal transition using lower-energy photons taking advantage of their large penetration depth in such device implementation by leveraging the carrier-driven emergent state to circumvent thermodynamic limitations for more efficient and ultrafast switching56.
Methods
Sample synthesis
The VO2 thin film samples used in the experiments were prepared via pulsed laser deposition57,58 on 9 nm thick amorphous silicon (a-Si) 100 μm × 100 μm TEM membrane windows (SIMPore: US100-A09Q33). The TEM windows were first attached to a silicon substrate, which was then loaded into a custom-built vacuum chamber for the deposition of VO2 thin films. Before the deposition started, the background pressure was lowered to 8 × 10−6 Torr to remove impurity ambient gases. Upon deposition, the temperature of the sample was increased to ~550 °C, whereas the oxygen was introduced in the chamber at a constant rate of 20 standard cubic centimeters per minute (sccmm). Meanwhile, the pressure was controlled by a butterfly control valve to maintain at 15 mTorr. A krypton fluoride (KrF) excimer laser was operated at 10 Hz under a pulse energy of ~350 mJ (fluence of approximately 2 J/cm2) to ablate vanadium from a solid metallic target inside the chamber to grow VO2 films on the substrate. During deposition, the sample was constantly rotated for an even distribution of heat and material deposition. Upon completion of the deposition time, the laser was turned off and the sample went through a 30 minute annealing process under the same environment conditions. Under this process, it took ~7 minutes and 30 seconds to grow ~50 nm thick films, which was confirmed by using AFM. Using a scanning electron microscope (SEM), we can differentiate the nanosized grain composition and establish a grain size distribution to be around 31 ± 7 nm, as shown in Supplementary Fig. S1.
Characterization
The steady-state insulator-metal transition of the as-prepared VO2 thin film was confirmed by temperature-dependent resistance measurement depicted in Supplementary Fig. S2(a), showing 2 orders of magnitude change in resistance across the transition temperature TC ~ 340 K6. A dispersion of ~8 K is also identified, which we attributed to the inhomogeneity-induced broadening, rather than the intrinsic property of VO2, as evidenced in recent studies of single-crystal nanobeams27,38,59. Also shown is the structure phase transition (see Supplementary Fig. S2(b)), monitored through the electron diffraction, in which the (3, 0, −2) intensity is used as an order parameter to gauge the degree of phase transition. We note that the measured resistivity continues to change beyond the structural transition region. This trend is indicative of a continuous change in the electronic property of VO2 beyond TC, not correlated with the structural phase transition38,59.
Ultrafast electron diffraction
The ultrafast electron diffraction experiments were conducted using the ultrafast electron crystallography (UEC) and the ultrafast electron microdiffraction (UEmD) systems. The low temperature studies were performed in the UEC system where the sample goniometer can be cooled to 20 K5. Temperature was measured with 0.01 K precision at the back of sample holder, which was in a solid thermal contact with the sample grid, which was clamped into a copper counter sink on the sample holder. The probe size was controlled via adjusting a condenser lens in front of the sample to 30 μm in full-width-at-half-maximum (FWHM) in this experiment ensuring the electron beam was fully contained near the center of the VO2 film deposited on the 100 um × 100 um TEM membrane window. The pump pulse was generated by an optical parametric amplifier driven by a 45 fs, 800 nm amplified laser system (Spectra Physics, Ti: Sapphire, Regenerative Amplification), and can be tuned from 200 nm to 3000 nm in wavelength. In this experiment, primarily 800 nm and 2000 nm wavelength were used. The size of the pump beam at different wavelength was adjusted by varying the position of a focusing lens. Its size along x direction (see Supplementary Fig. S3(a)) was directly measured via knife-edge measurement in situ, while the aspect ratio of the pump laser spot was determined in situ using laser-electron cross-correlation approach (see SI). Part of the incident laser beam was also split off by a beam splitter before entering the diffraction chamber, which was monitored with a beam profiler to cross check the size and intensity of the beam during the experiment. We set the pump size to be ~400 μm in FWHM, which was significantly larger than the probe size to ensure that within the probed area the sample was homogeneously illuminated by the pump laser. The room temperature studies were also conducted using the UEmD system where the beam energy can be adjusted up to 100 keV. We determine the normalized diffraction intensity changes do not vary strongly over the beam energy. We kept the repetition rate to be ≤500 Hz to ensure there was no residual heating effect that would change the initial state. This is verified by in situ monitoring the diffraction patterns produced at negative timeframes to be consistent with that obtained from the sample without optical pumping, and the threshold dose at a given temperature is independent of the exposure time (see Supplementary Fig. S4).
Additional Information
How to cite this article: Tao, Z. et al. The nature of photoinduced phase transition and metastable states in vanadium dioxide. Sci. Rep. 6, 38514; doi: 10.1038/srep38514 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Nasu, K. Photoinduced phase transitions. (World Scientific Pub. Co. Inc., 2004).
Fausti, D. et al. Light-induced superconductivity in a stripe-ordered cuprate. Science 331, 189–191 (2011).
Stojchevska, L. et al. Ultrafast switching to a stable hidden quantum state in an electronic crystal. Science 344, 177–180 (2014).
Ichikawa, H. et al. Transient photoinduced ‘hidden’ phase in a manganite. Nat. Mater. 10, 101–105 (2011).
Han, T.-R. T. et al. Exploration of metastability and hidden phases in correlated electron crystals visualized by femtosecond optical doping and electron crystallography. Sci. Adv. 1, e1400173 (2015).
Morin, F. J. Oxides which show a metal-to-insulator transition at the neel temperature. Phys. Rev. Lett. 3, 34–36 (1959).
Whittaker, L., Patridge, C. J. & Banerjee, S. Microscopic and nanoscale perspective of the metal-insulator phase transitions of VO2: Some new twists to an old tale. J. Phys. Chem. Lett. 2, 745–758 (2011).
Eyert, V. The metal-insulator transitions of VO2: A band theoretical approach. Ann. Phys. 11, 650–702 (2002).
Wu, Y. et al. Depressed transition temperature of WxV1-xO2: mechanistic insights from the X-ray absorption fine structure (XAFS) spectroscopy. Phys. Chem. Chem. Phys. 16, 17705 (2014).
Pouget, J. P. et al. Dimerization of a linear Heisenberg chain in the insulating phases of V1-xCrxO2 . Phys. Rev. B 10, 1801–1815 (1974).
Biermann, S., Poteryaev, A., Lichtenstein, A. I. & Georges, A. Dynamical singlets and correlation-assisted peierls transition in VO2 . Phys. Rev. Lett. 94, 26404 (2005).
Weber, C. et al. Vanadium dioxide: A peierls-mott insulator stable against disorder. Phys. Rev. Lett. 108, 1–5 (2012).
Zylbersztejn, A. & Mott, N. F. Metal-insulator transition in vanadium dioxide. Phys. Rev. B 11, 4383–4395 (1975).
Goodenough, J. B. The two components of the crystallographic transition in VO2 . J. Solid State Chem. 3, 490–500 (1971).
Cavalleri, A., Dekorsy, T., Chong, H. H. W., Kieffer, J. C. & Schoenlein, R. W. Evidence for a structurally-driven insulator-to-metal transition in VO2: A view from the ultrafast timescale. Phys. Rev. B 70, 161102(R) (2004).
Baum, P., Yang, D.-S. & Zewail, A. H. 4D visualization of transitional structures in phase transformations by electron diffraction. Science 318, 788–792 (2007).
Cavalleri, A. et al. Femtosecond structural dynamics in VO2 during an ultrafast solid-solid phase transition. Phys. Rev. Lett. 87, 237401 (2001).
Cocker, T. L. et al. Phase diagram of the ultrafast photoinduced insulator-metal transition in vanadium dioxide. Phys. Rev. B 85, 155120 (2012).
Hilton, D. J. et al. Enhanced photosusceptibility near Tc for the light-induced insulator-to-metal phase transition in vanadium dioxide. Phys. Rev. Lett. 99, 226401 (2007).
Kübler, C. et al. Coherent structural dynamics and electronic correlations during an ultrafast insulator-to-metal phase transition in VO2 . Phys. Rev. Lett. 99, 116401 (2007).
Pashkin, A. et al. Ultrafast insulator-metal phase transition in VO2 studied by multiterahertz spectroscopy. Phys. Rev. B 83, 1–9 (2011).
Wegkamp, D. et al. Instantaneous band gap collapse in photoexcited monoclinic VO2 due to photocarrier doping. Phys. Rev. Lett. 113, 2–6 (2014).
Becker, M. F. et al. Femtosecond laser excitation of the semiconductor-metal phase transition in VO2 . Appl. Phys. Lett. 65, 1507–1509 (1994).
Rini, M. et al. Optical switching in VO2 films by below-gap excitation. Appl. Phys. Lett. 92, 181904 (2008).
Cavalleri, A. et al. Band-selective measurements of electron dynamics in VO2 using femtosecond near-edge X-ray absorption. Phys. Rev. Lett. 95, 67405 (2005).
Tao, Z., Han, T. R. T. & Ruan, C. Y. Anisotropic electron-phonon coupling investigated by ultrafast electron crystallography: Three-temperature model. Phys. Rev. B 87, 235124 (2013).
Tao, Z. et al. Decoupling of structural and electronic phase transitions in VO2 . Phys. Rev. Lett. 109, 166406 (2012).
Morrison, V. R. et al. A photoinduced metal-like phase of monoclinic VO2 revealed by ultrafast electron diffraction. Science 346, 445–448 (2014).
Zeiger, H. J. et al. Theory for displacive excitation of coherent phonons. Phys. Rev. B 45, 768–778 (1992).
Wall, S. et al. Ultrafast changes in lattice symmetry probed by coherent phonons. Nat. Commun. 3, 721 (2012).
O’Callahan, B. T. et al. Inhomogeneity of the ultrafast insulator-to-metal transition dynamics of VO2 . Nat. Commun. 6, 6849 (2015).
Kim, H.-T. et al. Monoclinic and correlated metal phase in VO2 as evidence of the mott transition: Coherent phonon analysis. Phys. Rev. Lett. 97, 266401 (2006).
Laverock, J. et al. Direct observation of decoupled structural and electronic transitions and an ambient pressure monocliniclike metallic phase of VO2 . Phys. Rev. Lett. 113, 216402 (2014).
Liu, M. K. et al. Anisotropic electronic state via spontaneous phase separation in strained vanadium dioxide films. Phys. Rev. Lett. 111, 96602 (2013).
Hsieh, W.-P. et al. Evidence for photo-induced monoclinic metallic VO2 under high pressure. Appl. Phys. Lett. 104, 21917 (2014).
Sciaini, G. & Miller, R. J. D. Femtosecond electron diffraction: heralding the era of atomically resolved dynamics. Reports Prog. Phys. 74, 96101 (2011).
Ischenko, A. & Aseyev, S. A. Eds. Time-resolved electron diffraction: For chemistry, biology and materials science, in Advances in Imaging and Electron Physics. 184, http://www.sciencedirect.com/science/article/pii/B9780128001455210010 (Elsevier, 2014).
Wei, J., Wang, Z., Chen, W. & Cobden, D. H. New aspects of the metal-insulator transition in single-domain vanadium dioxide nanobeams. Nat. Nanotechnol. 4, 420–424 (2009).
Marezio, M., McWhan, D. B., Remeika, J. P. & Dernier, P. D. Structural aspects of the metal-insulator transitions in Cr-doped VO2 . Phys. Rev. B 5, 2541–2551 (1972).
Longo, J. M. & Kierkegaard, P. A refinement of the structure of VO2 . Acta Chem. Scand. 24, 420–426 (1970).
Kucharczyk, D. & Niklewski, T. Accurate X-ray determination of the lattice parameters and the thermal expansion coefficients of VO2 near the transition temperature. J. Appl. Crystallogr. 12, 370–373 (1979).
Berglund, C. N. & Guggenheim, H. J. Electronic properties of VO2 near the semiconductor-metal transition. Phys. Rev. 185, 1022–1033 (1969).
Budai, J. D. et al. Metallization of vanadium dioxide driven by large phonon entropy. Nature 515, 535–539 (2014).
Koethe, T. C. et al. Transfer of spectral weight and symmetry across the metal-insulator transition in VO2 . Phys. Rev. Lett. 97, 116402 (2006).
Verleur, H. W., Barker, A. S. & Berglund, C. N. Optical properties of VO2 between 0.25 and 5 eV. Rev. Mod. Phys. 40, 737 (1968).
Guinier, A. X-ray diffraction in crystals, imperfect crystals, and amorphous bodies. (Dover Publications, 1994).
Ruan, C.-Y. et al. The development and applications of ultrafast electron nanocrystallography. Microsc. Microanal. 15, 323–337 (2009).
Farrow, C. L., Ruan, C. Y. & Billinge, S. J. L. Quantitative nanoparticle structures from electron crystallography data. Phys. Rev. B 81, 134104 (2010).
He, Z. & Millis, A. J. Photoinduced phase transitions in narrow-gap Mott insulators: The case of VO2 . Phys. Rev. B 93, 115126 (2016).
Yuan, X., Zhang, W. & Zhang, P. Hole-lattice coupling and photoinduced insulator-metal transition in VO2 . Phys. Rev. B 88, 35119 (2013).
Haverkort, M. W. et al. Orbital-assisted metal-insulator transition in VO2 . Phys. Rev. Lett. 95, 196404 (2005).
Maurer, D., Leue, A., Heichele, R. & Müller, V. Elastic behavior near the metal-insulator transition of VO2 . Phys. Rev. B 60, 13249–13252 (1999).
Stabile, A. a. et al. Separating electric field and thermal effects across the metal-insulator transition in vanadium oxide nanobeams. Appl. Phys. Lett. 107, 13503 (2015).
Wu, B. et al. Electric-field-driven phase transition in vanadium dioxide. Phys. Rev. B 84, 241410(R) (2011).
Zhou, Y. et al. Voltage-triggered ultrafast phase transition in vanadium dioxide switches. IEEE Electron Device Lett. 34, 220–222 (2013).
Zhou, Y. & Ramanathan, S. Correlated electron materials and field effect transistors for logic: A review. Crit. Rev. Solid State Mater. Sci. 38 (2013).
Rúa, A., Fernández, F. E. & Sepúlveda, N. Bending in VO2 -coated microcantilevers suitable for thermally activated actuators. J. Appl. Phys. 107, 74506 (2010).
Cabrera, R., Merced, E. & Sepúlveda, N. A micro-electro-mechanical memory based on the structural phase transition of VO2 . Phys. Status Solidi A 9, 1704–1711 (2013).
Cao, J. et al. Strain engineering and one-dimensional organization of metal-insulator domains in single-crystal vanadium dioxide beams. Nat. Nanotechnol. 4, 732–737 (2009).
Acknowledgements
The authors acknowledge S.B. Mahanti, P.M. Duxbury, and J. McGuire for useful discussions, and R. Loloee and B. Bi for assistance in preparing and characterizing the VO2 films. The work was funded by DOE grant DE-FG02-06ER46309 and supported by NSF MRI facility grant DMR 1126343.
Author information
Authors and Affiliations
Contributions
C.-Y.R. and Z.T. conceived the experiments. Z.T., F.Z., T.-R.T.H., K.C. and C.-Y. R performed the ultrafast diffraction and microscopy measurements. M.Y. and R.R.L. performed the optical measurements. D.T., T.W. and N.S. prepared the samples. Z.T., F.Z., T.-R.T.H. and C.-Y.R. did the analyses. C.-Y.R. and Z.T. wrote the paper. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Tao, Z., Zhou, F., Han, TR. et al. The nature of photoinduced phase transition and metastable states in vanadium dioxide. Sci Rep 6, 38514 (2016). https://doi.org/10.1038/srep38514
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep38514
- Springer Nature Limited
This article is cited by
-
Millimeter-wave to near-terahertz sensors based on reversible insulator-to-metal transition in VO2
Communications Materials (2023)
-
Transient dynamics of the phase transition in VO2 revealed by mega-electron-volt ultrafast electron diffraction
Nature Communications (2023)
-
Pivotal role of reversible NiO6 geometric conversion in oxygen evolution
Nature (2022)
-
Large non-thermal contribution to picosecond strain pulse generation using the photo-induced phase transition in VO2
Nature Communications (2020)
-
Non-thermal resistive switching in Mott insulator nanowires
Nature Communications (2020)