Abstract
Ag-TiO2@polyethylene glycol (PEG) nanoparticles were continuously obtained in a single-pass configuration by appropriately reacting freshly flame-synthesized TiO2 with Ag formed in an ultrasonic aqueous medium containing PEG. When the proposed synthesis was kept constant, the production rate for Ag-TiO2@PEG nanoparticles reached approximately 3 g/h while only using a combination of a lab-scale inverse-diffusion flame (16 mm head diameter) and an ultrasonic Ag(I) cell (50 mL). The synthesized nanoparticles were employed as inducers for in vitro photoinduced therapy to kill cancer cells at different light wavelengths. Measurements of the nanoparticle cytotoxicity revealed that PEG incorporation with the Ag-TiO2 particles significantly decreased the cytotoxicity (cell viability of more than ~91% at 200 μg mL−1 particle concentration) of Ag, and this was comparable with that of TiO2 particles (cell viability of more than ~90%). When 632 nm and 808 nm light was applied to the nanoparticles in the HeLa cells, the viability of the cells was significantly affected [decreased to ~4% (632 nm) and ~26% (808 nm) at 200 μg mL−1, 5 min irradiation time] by surface plasmon resonance heating and photothermal therapy.
Similar content being viewed by others
![](https://media.springernature.com/w215h120/springer-static/image/art%3A10.1007%2Fs00396-020-04721-5/MediaObjects/396_2020_4721_Fig1_HTML.png)
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Strategic incorporation between isomers may help enhance composite nanoplatforms, which can provide multi-functionalities in specific technological areas that are difficult to achieve with one-component nanoparticles. Therefore, it is important to develop improved metallic nanoparticles containing composite materials. In particular, there is an increasing interest in developing biocompatible functional materials for metallic nanoparticle technology, with an aim to combine the relevant properties of metals with the peculiar performance of biomaterials1. However, currently available metallic nanoparticles usually have poor compatibility with organic components, and it is therefore rather difficult to homogeneously incorporate them into an organic matrix. This limits the extension of their use in biomedical applications.
Numerous approaches have been proposed for fabricating multifunctional biocompatible nanomaterials that consist of inorganic-organic nanocomponents for application in diagnostic and therapeutic fields. These nanomaterials usually contain metallic nanoparticles as the core components with biofunctional polymers that endow the nanomaterial with unique physicochemical properties for diagnostic and therapeutic purposes2,3,4. Many formulations based on wet chemistry introduced as suspension of solid particles have been proposed for biomedical applications, and these may only be workable with desired performance in a short period of time5. Moreover, organic or polymeric components incorporated with metallic nanoparticles are normally unstable owing to gradual degradation by hydrolysis; biofunctional nanomaterials in a suspension or colloidal form would therefore not be recommended. As a result, there is a need for a paradigm shift in the strategy for preparing stable organic-inorganic hybrid nanomaterials with simpler and more versatile processing for efficient use in biomedical applications6. Gas-phase processing is an alternative method for preparing such nanomaterials with fewer preparation steps, and it could allow long-term storage of the prepared nanomaterials in a powder form7. Employing gas-phase processing further enhances the process continuity in production, and this implies that only simple mechanical collection of materials is required and large amounts of waste are not generated. Moreover, employing wet chemistry approaches has been recently shown to achieve better selectivity and safety in hazardous chemical processes and to exhibit many advantages over conventional batch chemical processes3.
Flame synthesis, which is one of the most promising gas-phase routes, has been utilized for preparing a wide range of mono- and multicomponent functional nanoparticles with low cost and high yield in commercial quantities1, and it could be scaled up to a production rate of several hundred grams per hour without significant change in material property8. However, conventional flame synthesis of functional nanoparticles is commonly performed in high temperature conditions (over 1,700 °C). Since temperatures over 300 °C can decompose most organic materials (i.e. biofunctional soft materials), the use of conventional flame synthesis would be only feasible to synthesize hard or inorganic nanoparticles9. Thus, for producing inorganic parts for hybrid nanomaterials is a single-pass configuration, flame pyrolysis would not be suitable without the need for post-treatment or post-functionalization steps; hence, this technique is still limited with respect to its use in a wide range of biomedical applications10. Nevertheless, more recently, flame-synthesized nanoparticles have often been employed as active materials for biomedical applications via successive incorporation with biocompatible overlayers in a continuous manner1,6,11. However, since this technique works only for inorganic biomaterials, its application is still limited for generalized use. There have been several studies on biomedical applications using metallic core-polymer shell nanocomposites that exhibit high absorption at wavelengths longer than that of visible light. Even though there are previous reports regarding organic matter/polymer incorporation with flame-synthesized nanoparticles12,13, it is still desirable to conceive of simple, continuous, and efficient methodologies for biomedical applications of flame-synthesized nanoparticles.
This work introduces the potential use of Ag-TiO2@polyethylene glycol (PEG) nanoparticles as photoinducers for killing cancer cells via flame-based gas-liquid-gas single-pass processing. The flame-synthesized TiO2 nanoparticles were employed as a biocompatible support14 to produce Ag-TiO2 nanobunches in order to enhance photoinduced cancer cell killing by exploiting localized surface plasmon resonance including photocatalytic activity15. To functionalize the flame-synthesized TiO2 particles with organic components in a continuous manner, an ultrasound Ag(I)-PEG reaction cell is employed both for efficient hydrosolization of the TiO2 particles and for subsequent incorporation with Ag and PEG on the TiO2 domains (Fig. 1). PEG is employed as overlayers for the Ag-TiO2 nanoparticles since it is known to be nontoxic to mammalian cells (i.e. biocompatible) and non-antigenic16, which may also help it bond with metallic ions17.
Results and Discussion
To understand the formation of the Ag-TiO2@PEG nanocomposites through the proposed hybrid processing, the samples electrostatically deposited as TiO2, Ag@PEG, and Ag-TiO2@PEG [(using a commercial particle collector (NPC-10, HCT, Korea)] directly on carbon-coated copper grids in the gas-phase were analyzed using a transmission electron microscope (TEM, JEM-3010, JEOL, Japan). The gas-phase sampling flow rate was of 1.0 L min−1 in the collector. As shown in Fig. 2a, the primary TiO2 particles (~28 nm lateral dimension) were agglomerated, implying that the primary particles collided with each other after they formed near the flame. As seen in the inset of Fig. 2a, a lattice spacing of approximately 0.35 nm was most frequently observed, which could be matched to the (101) plane of anatase TiO218. In Fig. 2b (Ag@PEG sample), a darker contrast of spherical particles exhibits the Miller plane (111) owing to a 0.24 nm face-centered cubic (fcc) Ag lattice (inset), whereas lighter-contrast overlayers on the spherical particles are attributable to the PEG. Thus, it was clearly observed that ultrasonically formed Ag (from Ag+ to Ag0) particles (8.8 ± 1.7 nm lateral dimension) could be successively incorporated with PEG via successive reaction and electrospray processes. In the case of Ag-TiO2@PEG, as shown in Fig. 2c, the different particles (different size and gradation) are combined as a single agglomerate, and it was clearly observed that darker dots (because of Ag’s higher density than TiO2) were randomly located on the TiO2 domains, which confirmed that the Ag-TiO2 hybrid structures were successfully assembled. The lattice spacing of the darker dots was ~0.24 nm corresponding to the Miller plane (111) of Ag, while that of the lighter-contrast dots was ~0.35 nm corresponding to the (101) plane of TiO2, implying coupling between distinct phase domains. The corresponding fast Fourier transform images are also attributable to the fcc Ag and anatase TiO2, respectively (Fig. 2d). As further evidence, the X-ray diffraction (XRD, RINT-2100, Rigaku, Japan) analysis of the TiO2 and Ag-TiO2 particles revealed that Ag particles formed in the aqueous solution collided with incoming TiO2 particles (Supplementary Fig. S1a). This implies that the process enables incorporation of Ag particles at several sites on the continuously incoming TiO2 particles. Furthermore, the Ag agglomerates (shown in Fig. 2b) were redistributed on the TiO2 domains due to deagglomeration (Eq. S1, Supplementary Information, by setting the mechanical force from a pressure drop on an agglomerate of certain size owing to the remarkable changes in pressure between the both sides of a nozzle for the electrospray). When the agglomerated Ag@PEG passes through the nozzle, it undergoes significant changes in mechanical conditions such as pressure and velocity across the nozzle which induce a structural change of the Ag@PEG before entering the nozzle. Figure 2c also displays the incorporation of PEG on Ag-TiO2 particles, which may have originated both from the Ag-PEG binding during Ag formation (Eq S2, Supplementary Information) in the ultrasound reaction cell and from adsorptive incorporation during electrospray. To confirm the latter, adsorption isotherms (Supplementary Fig. S2) were measured using the Micromeritics ASAP 2010 apparatus. A difference in the pore size distribution (inset) also supports the PEG incorporation, which shows a significant decrease in the pore volume at meso- and macro-porous regions after the PEG incorporation, implying that this adsorptive property also might enhance the PEG incorporation on the Ag-TiO2 particles19. Figure 2d shows the energy dispersive X-ray (EDX, JED-2300, JEOL, Japan) spectrum for the Ag-TiO2@PEG sample. The low- and high-magnification scanning electron microscopy (SEM, JSM-6500F, JEOL, Japan) images and the EDX spectrum peaks correspond to Ag, Ti and O, and arrows in the high-magnification image indicate the positions of Ag, Ti, and O in the sample. The weight fraction of Ag in the Ag-TiO2 was ~40.1% in the present work, and this further confirmed the Ag incorporation on TiO2 domains. When the system operation is kept constant, the production rate for Ag-TiO2@PEG particles reached approximately 3 g/h, and scale-up of this system may achieve higher production rates (from kilograms to tons per day).
Low- and high-magnification electron microscope images to verify the morphologies of the synthesized particles: (a) flame-synthesized TiO2 nanoparticles; (b) ultrasound-assisted polyol synthesized-electrosprayed Ag@PEG nanoparticles; (c) ultrasound-assisted-electrosprayed Ag-TiO2@PEG nanoparticles; and (d) SEM images and corresponding EDX profile, and FFT image for Ag-TiO2@PEG nanoparticles.
The formation of Ag-TiO2 particles was also verified by means of UV-vis absorption spectroscopy (330, Perkin-Elmer, US, Supplementary Fig. S3a). This is also attributed to the dispersity of the Ag particles on the TiO2 domains by the ultrasonic Ag(I) reduction and this induces an enhancement in the Ag particle dispersity owing to increased interaction between the Ag and TiO2 particles, resulting in a broadening of the absorption. The inset of Supplementary Fig. S3a shows the X-ray photoelectron spectroscopy (XPS, AXIS HIS, Kratos Analytical, Japan) spectrum of the Ag-TiO2 nanoparticles. The characteristic peaks at 458.1 eV and 463.7 eV shown in Supplementary Fig. S1b are attributable to Ti 2p3/2 and Ti 2p1/2, respectively. There are two more characteristic peaks at 367.5 eV and 373.5 eV in Supplementary Fig. S1b, which are attributable to Ag 3d5/2 and Ag 3d3/2, respectively, proving the existence of a metallic Ag. Supplementary Fig. S3b displays Fourier transform infrared spectra (FTIR, IFS 66/S, Bruker Optics, Germany) of the TiO2, Ag@PEG, and Ag-TiO2@PEG samples. The bands around 1,270 and 1,005 cm−1 for the Ag@PEG and Ag-TiO2@PEG samples may have arisen from C-O, C-O-C stretches, and C-O-H bendings vibrations of the Ag particles in the PEG matrix20.
Flame-synthesized TiO2 particles were successively injected into an aqueous Ag(I)-PEG solution in the presence of ultrasound to achieve bubble implosion for efficient collection. To verify the quantitative collection of TiO2 particles, we measured the size distributions both in the absence and the presence of ultrasound application. Most incoming TiO2 particles were trapped (~98.5% efficiency) in the aqueous solution during ultrasound irradiation. This may be due to bubble implosion before they reach the surface of the solution, resulting in hydrosolization of nearly all TiO2 particles. The particle size distribution was analyzed using a scanning mobility particle sizer (SMPS, 3936, TSI, USA) to verify the number concentration, mean diameter, and standard deviation of the electrosprayed Ag-TiO2@PEG particles. The measured concentration, diameter, and deviation were 7.09 × 106 particles cm−3, 125.0 nm, and 1.95, respectively, as shown in Fig. 3. The same data for TiO2 particles are 3.05 × 106 particles cm−3, 61.1 nm, and 1.84, respectively, and for the atomized Ag@PEG particles are 5.32 × 106 particles cm−3, 115.8 nm, and 1.97, respectively. The data for the Ag-TiO2@PEG particles were closer to that for the Ag@PEG particles compared to that of the TiO2 particles. There was no additional peak and only an apparent increase in concentration, not in size, suggesting that the TiO2 particles were well merged with the Ag particles and thus forming Ag-TiO2@PEG nanoparticles. In addition, the mass fractions of Ag, TiO2, and PEG in the Ag-TiO2@PEG nanoparticle were measured using a piezobalance particle monitor (3522, Kanomax, Japan) to be 0.38, 0.46, and 0.16, respectively.
We tested the cytotoxicity of the TiO2, Ag-TiO2, and Ag-TiO2@PEG nanoparticles. In the case of Ag-TiO2, a part of the dispersion was placed on HeLa cells to compare the cytotoxicity among the samples. The MTT [3-(4,5-dimethylthiazol-2-yl)-diphenyltetrazolium bromide] assay was employed to evaluate cell viability by using incubation cells with samples for 24 h (Fig. 4a). Measurements of cell viability showed that the TiO2 nanoparticles had a cell viability of ~90% at 200 μg mL−1, which indicates biocompatibility21, whereas the measured viabilities of the Ag and Ag-TiO2 nanoparticles were significantly lower than that for the TiO2 nanoparticles. The higher cytotoxicities for the Ag and Ag-TiO2 particles may be due to the release of Ag ions in water from the Ag particles (8.8 nm), and the released fraction of Ag ions reached approximately 38.4 wt% (using inductively coupled plasma optical emission spectrometry, Optima 8300, PerkinElmer, USA), which is consistent with a previous report (4~9 nm, Ag particle size)22. Analogous data for Ag-TiO2@PEG nanoparticles has the highest cell viability, i.e. ~92% at 200 μg mL−1. Although Ag-TiO2 nanoparticles released the metallic component to clearly contribute toward cytotoxicity, the released fraction of the PEG incorporated particles were not affected significantly because of the biocompatible organic overlayers, as shown in Fig. 2c. This tendency is consistent with a previous report, which described that protective PEG overlayers could decrease the cytotoxicity of nanoparticles to mammalian cells23,24. This suggests that the Ag-TiO2@PEG nanoparticles from the successive Ag-PEG incorporation of flame-synthesized TiO2 particles warrant further investigation for their usage as photoinducers for HeLa cell killing. The zeta potential of Ag-TiO2@PEG nanoparticles was +2.2 mV at pH 7.4, and this value was relatively more positive than that for the PEG-capped Ag particles prepared by wet chemistry25, hence this may provide higher affinity with negatively charged biological membranes. According to a common protocol for testing the photothermal activity of Ag-TiO2@PEG nanoparticles, we first measured the temperatures of the media in the presence of light irradiation for a duration of 5 min. The nanoparticle solution embedded in agar was exposed to laser of wavelength 632 nm or 808 nm (2.15 W cm−2). These wavelengths were chosen since they are within the absorption range of the Ag-TiO2 nanoparticles (Supplementary Fig. S3a). The absorption spectra of Ag-TiO2 particles showed a significant shift towards the longer wavelength (480~650 nm) compared with TiO2 particles, which is comparable with results from a previous report26. The broadened and shifted spectra may be due to the surface plasmons of Ag particles that depend on the morphology (i.e., nanobunches) and surrounding environment. The red shift in the spectra may have resulted from the interaction between Ag and TiO2 particles, where the Ag particles were deposited on the TiO2 surface27. The temperature, which was measured using an IR thermometer with a thermal camera (Supplementary Fig. S4), increased with an increase in laser irradiation time, and the local temperature reached 51.5 °C. Hence, the maximum values (23.1 °C at 632 nm and 16.3 °C at 808 nm) of ∆T (Eq S3, Supplementary Information) could be realized at 200 μg mL−1 of mass concentration, while the analogous value for the 365 nm wavelength was 0.2 °C. From the temperature measurements, it can be concluded that the Ag-TiO2 nanoparticles absorbed the irradiated laser light, and the light was successively converted into thermal energy. Based on this photothermal conversion of the Ag-TiO2 particles upon 632 nm or 808 nm excitation, in vitro photothermal therapy using Ag-TiO2@PEG nanoparticles was investigated. To measure the photothermal activity of the nanoparticles for cell killing (Fig. 4b), adenosine triphosphate (ATP) assay was employed. The thermal energy obstructed the ATP production of the cells owing to the heat when the laser irradiated the culture medium. According to previous reports28,29,30, the positive effect of temperature on photoinduced reactions in the presence of plasmonic and nonplasmonic noble metal nanoparticles is interpreted in terms of the redistribution of the metal electron into higher energy levels and the increase in vibrationally excited states with increasing temperature. Thus, the cell viability significantly decreased from thermo/chemical reactions with the embedded nanoparticles. Live or dead cells were differentiated by calcein AM (live cells, green fluorescence, Life Technologies, USA) and propidium iodide (dead cells, red fluorescence, Life Technologies, USA) after laser irradiation (inset of Fig. 4b). In the control group (Ag-TiO2@PEG nanoparticles only), nearly all cells displayed green fluorescence, so the particles themselves have no significant cytotoxic effects. When the nanoparticles are exposed to laser with different wavelengths, the particles show a photothermal effect on HeLa cells; hence, only cells within the laser spot were killed, showing homogeneous red fluorescence. The cells outside the region of the spot were mostly kept alive, showing green fluorescence. In particular, when the concentration is 90 μg mL−1, the viability of the cells incubated with Ag-TiO2@PEG nanoparticles decreased significantly with irradiation (2.15 W cm−2), and more than 80% of the cells were killed within 5 min of irradiation (632 nm). This performance is comparable with that in a previous report31 where modified TiO2 nanoparticles were employed with 5 min of irradiation (2.00 W cm−2). Even though there is a difference in the maximum temperature between the current and previous results for 5 min of laser irradiation, both results reveal temperatures over 50 °C that can easily kill cancer cells32. This implies that the proposed approach has feasibility that may be investigated further. In addition, the analogous result for the 365-nm wavelength did not show significant enhancement (more than ~80% in cell viability even at 200 μg mL−1) in cell killing, implying that the produced heat was rather critical for the cytotoxic effect. The weaker performance at the UV case may be due to significant UV absorption (~70% for <400 nm wavelength) by a silicon-coated polyethylene terephthalate (PET, 125-μm thickness, Loparex, USA) film33 that was employed to simulate the laser irradiation on skin34,35.
Furthermore, another scenario for parenteral applications was considered, where the Ag-TiO2@PEG nanoparticles are administered to tissues that attract activated macrophages. In order to suppress inflammatory responses, nanoparticle interaction with biological system has recently been studied for biofunctional nanoparticulate systems36. The results (Fig. 5) show that the Ag-TiO2@PEG nanoparticles could more significantly suppress the macrophage inflammatory protein (MIP) production from lipopolysaccharide (LPS)-challenged macrophages than those from polyethyleneimine (PEI) or poly-l-lysine (PLL) [as well as phosphate buffered saline (PBS)] incorporated Ag-TiO2 nanoparticles (insets of Fig. 5). The smaller MIP productions of the Ag-TiO2@PEG nanoparticles than that from the PEI or PLL incorporated particles indicate that the tendency may be related to the amine content (i.e., no amine groups in PEG).
A continuous aqueous Ag-PEG capping of flame-synthesized TiO2 nanoparticles via gas-liquid hybrid processing was employed for the first time for scalable production of inorganic-organic nanoplatforms. The fabricated nanoplatforms were directly employed to evaluate their biocompatibility and photothermal activity for killing cancer cells. A further study to optimize the proposed method for realistic applications regarding modulation of optical property and cytotoxicity is now in preparation for publication elsewhere. This strategy could allow on-demand fabrication of fresh biomaterials for use in biomedical applications, and may also hold immense promise in biomaterial coatings. These results further establish continuous hybrid processing as an efficient, green, and scalable design and fabrication methodology, which is generalizable to a wide range of therapeutic and diagnostic agents for both biomedical and scientific purposes.
Materials and Methods
Nanoparticles synthesized in the gas-phase can be suspended into a liquid for coupling to wet-chemistry routes, thus enabling development of other innovative methods for novel material synthesis37,38,39. When incorporating metal in a liquid state, hydrated electrons produced during mixing and heating could reduce metal ions to metal particles of zero valences. In the present work, the flame-synthesized TiO2 inorganic particles were injected into an Ag(I)-PEG containing aqueous solution in the presence of ultrasound for capping of the TiO2 particles with newly formed Ag-PEG (Fig. 1). The TiO2 particles were ultrasonically trapped in the solution when the ultrasound reached the bubbles containing TiO2 particles in the solution. When solutions containing AgNO3 and PEG were separately injected into the reactor containing TiO2 particles, the Ag ions would reduce and subsequently deposit on the trapped TiO2 particle by ultrasound-assisted reaction and mixing. They were then aerosolized via electrospray to fabricate nanoscale PEG incorporated Ag-TiO2 photoinducers, and finally employed to kill human epithelial carcinoma (HeLa, ECACC No. 93021013) cells upon light irradiation (with a 632 nm or 808 nm wavelength, VA-I-DC, Rhysics Phototronics, Korea).
Specifically, as shown in Fig. 1, a commercial co-flow quartz burner (141/18/60, Arnold Gruppe, Germany) equipped with a bubbler was employed to produce TiO2 nanoparticles. The H2 (fuel) intake is made through 4 capillaries, and the TiCl4 precursor (208566, Sigma-Aldrich, USA) was fed to the flame via bubbling air passing around the 4 capillaries after mixing with another air acting as oxidant and sheathing gas. The H2 flow rate was 1.2 L min−1, and the air flow rates for bubbling and oxidation were 0.3 and 6.0 L min−1, respectively. The flow rates were separately controlled with mass flow controller (Tylan, USA). The synthesized TiO2 particles passed through the tube furnace containing silica gel and activated carbon pellets to remove extracted solvent and were driven to a conical chimney, which directly drove the part of particles using a vacuum transducer pump into the ultrasonic the Ag(I) cell containing PEG to employ as domains for synthesizing Ag-TiO2 nanoparticles in Ag(I)-PEG solution. In the reaction cell, solutions 1 and 2 were injected with the aid of a peristaltic pump (323Du/MC4, Watson-Marlow Bredel Pump, USA) at constant rates of 0.42 and 2.08 mL min−1, respectively. 85 milligrams of AgNO3 (205052, Sigma-Aldrich, USA), used as a precursor of Ag, was dissolved in 5 mL of deionized water (Solution 1). 0.2 grams of PEG (81253, Sigma-Aldrich, USA), used both as a reducing agent and a stabilizing agent, dissolved in 25 mL of distilled water (Solution 2). An ultrasound probe (VCX 750, 20 kHz, Sonics & Materials Inc., USA) was immersed into the solution. The probe acted as an ultrasound irradiator (10 W mL−1 input power density) and the active part of the probe was the planar circular surface, of area 1.3 cm2, at the bottom of the probe. Upon the start of reactions, the pale yellow solution changed to light brown indicating the reduction of Ag(I).
The Ag-TiO2@PEG suspension was aerosolized via electrospray, by means of the equipment assembled in-house. In brief, the equipment consisted of another peristaltic pump (07522-30, Masterflex, USA), a stainless-steel nozzle (inner diameter 0.3 mm), a high-voltage power supply (10/40A, Trek, USA), and a stainless steel plate placed directly below the nozzle as the grounded count electrode at a distance of 40 mm between the capillary and the substrate. The prepared solution was electrosprayed (16 μL min−1) in a heated tube installed between a capillary and a polytetrafluoroethylene substrate (66042, Satorius, Germany) using the pump (3032, TSI, USA) to perform a deposition of Ag-TiO2@PEG nanoparticles on the substrate. The detached nanoparticles from the substrate were then employed to evaluate their cytotoxicity and photothermal activity upon light irradiation.
Synthesized Ag-TiO2@PEG nanoparticles were evenly dispersed in 2% agar (Invitrogen, USA) at concentrations of 20, 50, 90, 140, and 200 μg mL−1. The gels were formed in shallow, 35 mm diameter plastic petri dishes. For exposure, the gel phantom samples at room temperature were exposed to a photoirradiation system passing through a silicon-coated PET film (to simulate the laser irradiation on skin) with different wavelength ranges (365, 632, and 808 nm). The gel samples were positioned in the light and irradiated by the beam (2.15 W cm−2 irradiation intensity) for a fixed duration of 5 min. In order to evaluate the application to photothermal cell killing, ATP assay (BioVision, USA) was employed, which is based on a highly sensitive firefly reaction to determine the level of cellular ATP as a surrogate marker for the number of live cells. After a 24 h incubation with Ag-TiO2@PEG nanoparticles, the cells were washed three times with a Hank buffered salt solution (H9394, Sigma-Aldrich, USA), and 0.1 mL of CellTiter-Glo Luminescent (Promega, USA) assay reagent was added to each well, and the plate was then mixed using an orbital shaker for 2 min, followed by 10 min incubation to stabilize the luminescence signals. Luminescence was read using a luminometer (GloMax 20/20, Promega, USA).
Peritoneal macrophages (ATCC CRL-2457) were seeded in 24-well plates at a density of 105 cells per well in 1 mL of medium. After overnight incubation, 0.1 mL of the Ag-TiO2@PEG nanoparticle solution was injected to each well to set the particle concentration in medium to 2 mg mL−1. For comparison purposes, 0.1 mL of polyethyleneimine (PEI, 765090, Sigma-Aldrich, USA), poly-l-lysine (PLL, P4707, Sigma-Aldrich, USA), or PEG was injected in lieu of the Ag-TiO2@PEG nanoparticle solutions. After 24 h incubation, the culture media were centrifuged at 2000 rpm for 10 min to separate supernatants. Macrophages were challenged by adding lipopolysaccharide (LPS) to the media in the final concentration of 1 μg mL−1 shortly before the comparisons. Enzyme-linked immunosorbent assay (ELISA) was performed to determine the MIP levels using MIP-2 ELISA kit (R&D Systems, USA). The supernatants collected from LPS-challenged macrophages were always diluted 10 times prior to the analysis. The differences were considered significant for p < 0.01.
All experiments were performed in triplicate, and the results were reported as average values and standard deviations.
Additional Information
How to cite this article: Byeon, J. H. Scalable hybrid chemical manufacture to photothermal therapy: PEG-capped phototransducers. Sci. Rep. 6, 31351; doi: 10.1038/srep31351 (2016).
References
Li, Y. et al. Double-faced γ-Fe2O3//SiO2 nanohybrids: flame synthesis, in situ selective modification and highly interfacial activity. Nanoscale 5, 5360–5367 (2013).
Kwon, K. C. et al. Proteinticle/gold core/shell nanoparticles for targeted cancer therapy without nanotoxicity. Adv. Mater. 26, 6436–6441 (2014).
Todorova, N. et al. Surface presentation of functional peptides in solution determines cell internalization efficiency of TAT conjugated nanoparticles. Nano Lett. 14, 5229–5237 (2014).
Yang, Y.-S. et al. Enhancing radiotherapy by lipid nanocapsule-mediated delivery of amphiphilic gold nanoparticles to intracellular membranes. ACS Nano 8, 8992–9002 (2014).
Wei, D. et al. The synthesis of chitosan-based silver nanoparticles and their antibacterial activity. Carbohydr. Res. 344, 2375–2382 (2009).
Sotiriou, G. A. et al. Photothermal killing of cancer cells by the controlled plasmonic coupling of silica-coated Au/Fe2O3 nanoaggregates. Adv. Funct. Mater. 24, 2818–2827 (2014).
Shields, S. P., Richards, V. N. & Buhro, W. E. Nucleation control of size and dispersity in aggregative nanoparticle growth. a study of the coarsening kinetics of thiolate-capped gold nanocrystals. Chem. Mater. 22, 3212–3225 (2010).
Gröhn, A. J. et al. Scale-up of nanoparticle synthesis by flame spray pyrolysis: the high-temperature particle residence time. Ind. Eng. Chem. Res. 53, 10734–10742 (2014).
Thimsen, E. Single-step aerosol synthesis and deposition of Au nanoparticles with controlled size and separation distributions. Chem. Mater. 23, 4612–4617 (2011).
Raemy, D. O. et al. Effects of flame made zinc oxide particles in human lung cells - a comparison of aerosol and suspension exposures. Part. Fibre Toxicol. 9, 33 (2012).
Hu, Y. et al. Highly compressible magnetic liquid marbles assembled from hydrophobic magnetic chain-like nanoparticles. RSC Adv. 4, 3162–3164 (2014).
Teleki, Y., Bjelobrk, N. & Pratsinis, S. E. Continuous surface functionalization of flame-made TiO2 nanoparticles. Langmuir 26, 5815–5822 (2010).
Starsich, F. H. L. et al. Gas-phase synthesis of magnetic metal/polymer nanocomposites. Nanotechnology 25, 505602 (2014).
Chandran, R. et al. Highly biocompatible TiO2:Gd3+ nano-contrast agent with enhanced longitudinal relaxivity for targeted cancer imaging. Nanoscale 3, 4150–4161 (2011).
Abdulla-Al-Mamun, M. et al. Synergistic cell-killing by photocatalytic and plasmonic photothermal effects of Ag@TiO2 core-shell composite nanoclusters against human epithelial carcinoma (HeLa) cells. Appl. Catal. A: Gen. 398, 134–142 (2011).
Stiufiuc, R. et al. SERS-active silver colloids prepared by reduction of silver nitrate with short-chain polyethylene glycol. Nanoscale Res. Lett. 8, 47 (2013).
Shameli, K. et al. Investigation of antibacterial properties silver nanoparticles prepared via green method. Chem. Cent. J. 6, 73 (2012).
Su, C. et al. Fabrication of Ag/TiO2 nanoheterostructures with visible light photocatalytic function via a solvothermal approach. CrystEngComm 14, 3989–3999 (2012).
Liufu, S., Xiao, H. & Li, Y. Investigation of PEG adsorption on the surface of zinc oxide nanoparticles. Powder Technol. 145, 20–24 (2004).
Wang, A. et al. Synergistic effect of silver seeds and organic modifiers on the morphology evolution mechanism of silver nanoparticles. Appl. Surf. Sci. 254, 6527–6536 (2008).
Wu, S. et al. Functionalized TiO2 based nanomaterials for biomedical application. Adv. Funct. Mater. 24, 5464–5481 (2014).
Sotiriou, G. A. et al. Quantifying the origin of released Ag+ ions from nanosilver. Langmuir 28, 15929–15936 (2012).
Zhai, J. et al. Lipid-PEG conjugates sterically stabilize and reduce the toxicity of phytantriol-based lyotropic liquid crystalline nanoparticles. Langmuir 31, 10871–10880 (2015).
Mano, S. S. et al. Effect of polyethylene glycol modification of TiO2 nanoparticles on cytotoxicity and gene expressions in human cell lines. Int. J. Mol. Sci. 13, 3703–3717 (2012).
Mandal, A. et al. Synthesis, characterization and comparison of antimicrobial activity of PEG/TritonX-100 capped silver nanoparticles. Colloid Surf. B-Biointerfaces 90, 191–196 (2012).
Khan, M. M. et al. Highly visible light active Ag@TiO2 nanocomposites synthesized using an electrochemically active biofilm: a novel biogenic approach. Nanoscale 5, 4427–4435 (2013).
Zhang, H. & Chen, G. Potent antibacterial activities of Ag/TiO2 nanocomposite powders synthesized by a one-pot sol-gel method. Environ. Sci. Technol. 43, 2905–2910 (2009).
Byeon, J. H. & Kim, Y.-W. Chitosan-conjugated dendritic Ag nanopowders for photothermal therapy applications. ACS Macro Lett. 3, 205–210 (2014).
Christopher, P. et al. Singular characteristics and unique chemical bond activation mechanisms of photocatalytic reactions on plasmonic nanostructures. Nat. Mater. 11, 1044–1050 (2012).
Sarina, S. et al. Viable photocatalysts under solar-spectrum irradiation: nonplasmonic metal nanoparticles. Ang. Chem.-Int. Ed. 53, 2935–2940 (2014).
Ren, W. et al. A near infrared light triggered hydrogenated black TiO2 for cancer photothermal therapy. Adv. Healthcare Mater. 4, 1526–1536 (2015).
Chou S. S. et al. Chemically exfoliated MoS2 as near-infrared photothermal agents. Ang. Chem.-Int. Ed. 52, 4160–4164 (2013).
Tricot, F. et al. Photochromic Ag:TiO2 thin films on PET substrate. RSC Adv. 4, 61305–61312 (2014).
Aoki, S. et al. A new cell-free bandage-type artificial skin for cutaneous wounds. Wound Rep. Reg. 23, 819–829 (2015).
Katika, K. M. & Pilon, L. Steady-state directional diffuse reflectance and fluorescence of human skin. Appl. Opt. 45, 4174–4183 (2006).
Dobrovolskaia, M. A. et al. Preclinical studies to understand nanoparticle interaction with the immune system and its potential effects on nanoparticle biodistribution. Mol. Pharmaceut. 5, 487–495 (2008).
Sanedrin, R. G. et al. Seed-mediated growth of bimetallic prisms. Adv. Mater. 17, 1027–1031 (2011).
Tour, J. M. Materials chemistry: seeds of selective nanotube growth. Nature 512, 30–31 (2014).
Boissiere, C. et al. Aerosol route to functional nanostructured inorganic and hybrid porous materials. Adv. Mater. 23, 599–623 (2011).
Acknowledgements
This work was supported by the National Research Foundation of Korea Grant funded by the Korean Government (NRF-2015R1A2A2A04005809).
Author information
Authors and Affiliations
Contributions
J.H.B. conceived the project, and designed and performed the experiments, and wrote the manuscript. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The author declares no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Byeon, J. Scalable hybrid chemical manufacture to photothermal therapy: PEG-capped phototransducers. Sci Rep 6, 31351 (2016). https://doi.org/10.1038/srep31351
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep31351
- Springer Nature Limited