Abstract
Two-dimensional (2D) van der Waal (vdW) heterostructures composed of vertically-stacked multiple transition metal dichalcogenides (TMDs) such as molybdenum disulfide (MoS2) and tungsten disulfide (WS2) are envisioned to present unprecedented materials properties unobtainable from any other material systems. Conventional fabrications of these hybrid materials have relied on the low-yield manual exfoliation and stacking of individual 2D TMD layers, which remain impractical for scaled-up applications. Attempts to chemically synthesize these materials have been recently pursued, which are presently limited to randomly and scarcely grown 2D layers with uncontrolled layer numbers on very small areas. Here, we report the chemical vapor deposition (CVD) growth of large-area (>2 cm2) patterned 2D vdW heterostructures composed of few layer, vertically-stacked MoS2 and WS2. Detailed structural characterizations by Raman spectroscopy and high-resolution/scanning transmission electron microscopy (HRTEM/STEM) directly evidence the structural integrity of two distinct 2D TMD layers with atomically sharp vdW heterointerfaces. Electrical transport measurements of these materials reveal diode-like behavior with clear current rectification, further confirming the formation of high-quality heterointerfaces. The intrinsic scalability and controllability of the CVD method presented in this study opens up a wide range of opportunities for emerging applications based on the unconventional functionalities of these uniquely structured materials.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
The quest for the fundamental physics and exciting new phenomenon inherent to 2D TMDs has opened new avenues in the field of 2D vdW heterostructures1,2,3. Motivated by the well-established heterojunction engineering of traditional semiconductor thin films, developing new hybrid materials by stacking up dissimilar 2D TMDs allows for the realization of unique and superior materials properties that cannot be obtained otherwise1,2. For example, theoretical4,5,6,7,8,9,10 and experimental11,12,13,14,15,16,17,18,19,20,21 studies have demonstrated intriguing band alignment and tunneling transports as well as fast charge transfer and strong interlayer coupling in vertically-stacked 2D heterostructures employing molybdenum (Mo) or tungsten (W)-based TMDs. An important attribute of these atomically assembled hybrid materials is the seamless stitching of dissimilar 2D TMDs via weak vdW forces benefiting from relaxed lattice mismatch constriction1. The anisotropic bonding nature of the layered TMDs also enables them to grow aligning their 2D layers in two distinct directions22,23,24, further emphasizing the importance of controlling their morphology for desired materials functionalities. Thus, establishing reliable methods that can stack up multiple 2D TMDs with well-defined components and orientations will greatly broaden their horizons in a wide range of applications such as flexible electronics and optoelectronics utilizing their extraordinary opto-electrical properties and extremely high strain limit25,26. Considerable efforts to integrate vertically-stacked 2D TMDs have been mainly driven by the manual exfoliation and stacking of individual 2D layers as demonstrated in MoS2/WSe211,12,13,14,15,16, MoS2/WS217,18, MoS2/MoSe219 and MoSe2/WSe220. However, this mechanical transfer approach produces 2D layers with low yield and arbitrary spatial distribution, intrinsically lacking a capability of scalable materials production. Alternatively, chemical vapor deposition (CVD) has been employed for the growth of large-area TMDs and it has recently been extended to grow vertically-stacked 2D TMD heterostructures. A few successful CVD growths of vertically-stacked WS2/MoS221,27,28, WSe2/MoS2 (or, MoS2/WSe2)29 and WSe2/MoSe230 as well as vdW heteroepitaxy-based MoS2 heterostructures31 have been demonstrated either via the co-reaction of metal-based precursors with chalcogens or via the sequential growth of one material on the other. However, all these CVD-grown 2D TMD heterostructures are presently limited to be demonstrated on very small areas lacking a control of their location, size, thickness and uniformity. Thus, much effort is still needed to develop viable approaches to synthesize vertically-stacked 2D TMD heterostructures in a highly scalable and controlled manner to realize their true potential.
Herein, we report the scalable and patterned CVD growth of vertically-stacked few layer 2D MoS2/WS2 heterostructures with well-defined heterointerfaces on a large area (>2 cm2). Detailed structural and electrical characterizations reveal that these hybrid materials well preserve their structural integrity and intrinsic electrical properties of individual constituting 2D TMDs.
Results and Discussion
Few layer, vertically-stacked 2D MoS2/WS2 heterostructures were grown using a two-step process of metal deposition followed by sulfurization in a low-pressure CVD (LPCVD) chamber. Figure 1(a) is a schematic illustration of the growth procedure. Stacks of high quality W and Mo films were sequentially deposited on silicon dioxide (SiO2)/silicon (Si) wafers using magnetron sputtering of W and Mo targets, respectively. A metal shadow mask was used for the patterned deposition of Mo/W stacked films. The deposited metal films were subsequently sulfurized in a LPCVD furnace at 600 °C under argon (Ar) environment, which converts Mo and W to MoS2 and WS2, respectively. As a result, vertically-stacked 2D MoS2/WS2 films composed of few layer MoS2 and WS2 were realized only on the areas where Mo and W were initially deposited. Figure 1(b) is an optical image of a vertically-stacked 2D MoS2/WS2 heterostructure film, demonstrating the scalability and patternability of the presented method.
(a) Schematic for the large-area, patterned CVD growth of few-layer only, vertically-stacked 2D MoS2/WS2 heterostructure films. Mo and W films are sequentially patterned and deposited on SiO2/Si growth substrates. Subsequent sulfurization converts the Mo and W to few layer 2D MoS2 and WS2, respectively. (b) Optical image of an as-grown vertically-stacked 2D MoS2/WS2 heterostructure film on a SiO2/Si substrate.
Raman spectroscopy has become a very powerful tool for studying various 2D materials to quantify their atomic layer numbers32. The Raman spectra in Fig. 2(a) confirms the typical in-plane (E′) and out of plane (A′1) vibration modes of individual WS2 (green) and MoS2 (black) films collected at 532 nm laser line. The Raman spectrum from the MoS2/WS2 heterostructure film (red) exhibits the distinguishable peaks corresponding to a summation of the Raman modes from each WS2 and MoS2. This observation indicates that our CVD method indeed yields heterostructures that maintain the characteristics of individual constituent 2D TMDs rather than alloyed MoxW1−xS2 which generally exhibit Raman peaks positioned intermediary to the those from pure MoS2 or WS233,34. The difference between the E′ and A′1 modes (Δf ) is a reliable quantity to determine the number of 2D atomic layers35. The Δf calculated from the individual WS2 and MoS2 films were 65 cm−1 and 24 cm−1, respectively, which correspond to the formation of ~4–5 atomic layers in each material36,37. Furthermore, atomic force microscopy (AFM) height profile measurements were performed across the edge of an as-grown MoS2/WS2 heterostructure film to assess its thickness (Fig. 2(b)). The average height of the film as measured from the underlying SiO2/Si substrate surface corresponds to ~7–8 nm indicating a growth of ~4–5 layers for each MoS2 and WS2, consistent with the Raman characterization.
The morphology of the stacked MoS2/WS2 films was further assessed by various TEM characterizations. Figure 3(a) shows a cross-sectional bright-field HRTEM micrograph of a stacked MoS2/WS2 film, revealing that the film consists of horizontally-grown 2D MoS2 and WS2 layers. Each material is indeed composed of ~4–5 layers, consistent with the results from the Raman and AFM characterizations. The inset shows the zoom-in image of the red boxed region showing the periodically-stacked 2D MoS2 in hexagonal (002) basal planes. Moreover, the image clearly reveals nearly atomically-sharp interfaces between MoS2 and WS2, further evidencing that the stacked MoS2/WS2 film well maintains the structural integrity of their constituting materials without alloying. The darker bright-field TEM imaging contrast from WS2 over MoS2 reflects that W is heavier than Mo. This observation is consistent with previous studies with mechanically stacked 2D TMDs38 and also confirms the ordered stacking of MoS2 and WS2 with seamless heterointerfaces. Further structural and chemical analysis of the MoS2/WS2 films was performed by scanning TEM (STEM) and energy dispersive x-ray spectroscopy (EDS) characterizations. Figure 3(b) shows an annular dark-field (ADF)-STEM image of a cross-sectioned MoS2/WS2 film different from the one in Fig. 3(a). The image clearly reveals a brighter image contrast for WS2 over MoS2 with a reversed image contrast in comparison to the bright-field TEM image, which is also consistent with previous observations with other in-plane 2D heterostructures21,27,39. The chemical compositions of vertically-stacked MoS2/WS2 films were characterized in EDS-STEM mode. Figure 3(c) shows the EDS-STEM elemental mapping image of the red boxed region in Fig. 3(b), revealing a highly localized spatial distribution of Mo and W on either side of the MoS2/WS2 stack. Figure 3(d–f) show plane-view dark-field TEM images of a vertically-stacked MoS2/WS2 film. Figure 3(d) shows that the MoS2/WS2 heterostructure material is a continuous film which possesses the poly-crystalline multiple layers composed of individual planar 2D grains. This poly-crystalline nature of the film is also confirmed by its corresponding fast Fourier transform (FFT) in the inset. Close-up inspections (Fig. 3(e,f)) further reveal multiple Moiré patterns with distinct fringe orientations at different locations (A,B in Fig. 3(d)) on the same sample. Figure 3(e) shows Moiré patterns resulting from stacks of multiple 2D layers whose basal planes are misaligned and rotated with respect to the [001] zone axis. This finding is qualitatively consistent with recent observations with vertically-stacked bilayer 2D TMD heterostructures integrated by manual exfoliations15. Meanwhile, Fig. 3(f) shows nearly single crystalline-like Moiré patterns which are attributed to that multiple 2D layers grew with aligned lattices on their basal planes. Such an epitaxial growth of MoS2/WS2 heterostructures was previously reported with materials grown by a co-evaporation CVD method27, which is attributed to that both MoS2 and WS2 possess identical lattice constants on their basal planes40. These characterizations together with the cross-sectional structural and chemical TEM analysis directly evidence that our CVD method produces 2D heterostructures composed of multiple MoS2 and WS2 layers in stacks with high spatial and chemical homogeneities.
(a) Cross-sectional HRTEM of a vertically-stacked MoS2/WS2 heterostructure film, revealing a nearly clean heterointerface of MoS2/WS2. (b) Cross-sectional ADF-STEM image of a vertically-stacked MoS2/WS2 heterostructure and (c) its corresponding EDS elemental mapping image. (d) Plane-view dark-field TEM image of a vertically-stacked MoS2/WS2 heterostructure film. (e,f) Close-up dark-field TEM images to show multiple Moiré fringes (e): obtained from the red boxed region A in Figure (d). (f): obtained from the yellow boxed region B in Figure (d).
In order to further assess the material quality of the vertical MoS2/WS2 heterostructure films, we performed electrical transport measurements across their heterointerfaces. One major advantage of these materials is their potential for novel device building blocks for large-area electronic devices compatible with unconventional substrates such as flexible polymers. To demonstrate this feasibility, we transferred the vertically-stacked MoS2/WS2 film onto a polyethylene terephthalate (PET) substrate by following a known polymethyl methacrylate (PMMA)-based transfer method41. Figure 4(a) shows an optical image of a large-area (~2 cm2) vertically-stacked MoS2/WS2 film transferred onto a PET substrate with a pre-deposited bottom electrode prior to the deposition of a top electrode. Figure 4(b) demonstrates the mechanical fleixlbity of the transferred film under bending. Two-terminal electrical characterizations were performed on the transferred film where metal contacts were separately made on MoS2 and WS2 as shown in the schematic in Fig. 4(c) inset. Figure 4(c) shows current-voltage (I–V) characteristics of a vertically-stacked MoS2/WS2 heterostructure film on a flexible PET substrate under a two-terminal room temperature transport measurement. A clear diode-like behavior with current ratio of >103 at ±0.5 V is observed, which reflects current rectification across the hetorointerface. To confirm that the diode-like behavior was indeed originated from the heterointerface, two-terminal transport measurements were performed on MoS2-only and WS2-only films as shown in Fig. 4(d). Linear I–V characteristics reflecting ohmic transports were observed from the individual 2D films without heterointerfaces, which confirms that the rectification was resulted from the heterointerfaces. Figure 4(e) illustrates the ideal energy band structure of the MoS2/WS2 heterointerface, indicating a formation of type II heterojunction and built-in potentials which are responsible for the observed rectification9. Our results are also consistent with recent observations of recifications from vertically-stacked multilayer MoS2/WS2 heterostructure films demonstrated either by the manual integration42 or by the co-evaparition or sequential CVD methods27,43,44. It is worth pointing out that all these previous results were demonstrated with very small films (<10 μm2) unlike our present study.
(a) Large area, vertically-stacked MoS2/WS2 heterostructure film transferred to a flexible insulating substrate with a pre-deposited electrode. The arrow indicates an area of the transferred film (b) The transferred film is under mechanical bending. (c) Two-terminal I–V measurement across a MoS2/WS2 heterointerface showing current rectification. (d) Two-terminal I–V measurements on individual MoS2 and WS2 films showing ohmic transports. (e) Energy band structure of a vertically-stacked MoS2/WS2 heterointerface.
Conclusion
In summary, we report the centimeter-scale CVD growth of vertically-stacked few-layer 2D MoS2/WS2 heterostructure materials by sulfurizing stacks of Mo/W films. Comprehensive structural characterizations employing Raman spectrocscopy, AFM and TEM/STEM evidenced that these novel materials are composed of 2D MoS2 and WS2 with well defined layer number, chemical homogeneity and vdW heterointerfacs. Thorough elecrtrical characterizations revealed diode-like current rectification from these materials, further confirming that they preserve the electrical characteristics of individual constituent 2D components. The growth method presented in this study is intrinsically scalable and compatible with the existing complementary metal-oxide semiconductor (CMOS) process, suggesting high promise for developing novel electronic materials beyond contemporary Si technologies.
Methods
Growth Method
High quality Mo (thickness ~1–2 nm)/W (thickness ~1–2 nm) stacked films were fabricated by sequential magnetron sputtering of W and Mo targets (99.99% purity) on Si/SiO2 (300 nm SiO2) substrates at room temperature. Prior to the seed metal films deposition, Si substrates were thoroughly cleaned in acetone, isopropanol and deionized water for 10 minutes, followed by drying using nitrogen gas. The as-deposited Mo/W films were then placed at the center of a LPCVD furnace equipped with a four inch quartz tube. Inside the tube, 100 mg of sulfur powder (99.5%, Sigma Aldrich) was placed in a separate alumina boat located at the upstream of the furnace. The tube was pumped down to 1 mTorr using a mechanical pump followed by heating up to 600 °C in 30 minutes with a held time of two hours. Throught the reaction, vaporized sulfur was carried by Ar gas to react with the metal films, which converts Mo/W films to MoS2/WS2 stacked films. Stacks of W/Mo films were also tested for the growth of vertically-stacked WS2/MoS2 films under the same growth conditions, which did not result in any noticeable difference compared to MoS2/WS2 films.
Characterization
Thickness and surface morphology measurements of the grown films were performed by an AFM (Parks NX-10) system. Raman spectra of the films were collected in Almega XR Raman spectrometer equipped with an Olympus BX51 microscope and spatial resolution of 1 μm with laser wavelength of 532 nm. Most of the structural and chemical analysis of the films were performed using a JEOL ARM200F FEG-TEM/STEM with a Cs-corrector for the electron probe. ADF STEM was performed with probe current of ~20 pA, condenser aperture of 30 μm, camera length of 8 cm and collection inner angle of ~70 mrad. The scanning rate of the ADF images was employed with 6 μs per pixel and 512 × 512 pixels. STEM-EDS analysis was performed with EDAX detector (SDD type 80 T) and analysis software (AZtecTEM, Oxford). The cross-sectional TEM image in Fig. 3(a) was taken by TECNAI F20 S-Twin (FEI Co, Netherland) TEM. All TEM/STEM operations were conducted at an accelerating voltage of 200 kV. Cross-sectional TEM samples were prepared by focused ion beam (FIB)-based milling and lift-out techniques. As-grown MoS2/WS2 films were coated with a carbon film of ~100 nm thickness (108 C auto carbon coater, Cressington Scientific Instruments) and were subsequently cross-sectioned inside a FIB (Quanta 2D FEG, FEI). Ga ion milling (30 keV) was performed until the target area became electron transparent suitable for TEM imaging and the prepared specimen was transferred to a Cu TEM grid with a micromanipulator (Omniprobe) inside the FIB. For electrical measurements, as-grown MoS2/WS2 films on SiO2/Si substrates were first coated with PMMA thin films by spin-coating at 2500 rpm for 30 s, followed by baking at 130 °C for 30 min. The PMMA-covered substrates were then immersed in a buffered oxide etchant (BOE: aqueous NH4-HF solution), which led to the separation of the MoS2/WS2 stacked fims from the substrate etching away SiO2. The separted films were subseuently transferred to insulating substrates with pre-deposited bottom metal electrodes. Finally, PMMA was rinsed away with acetone and dionized water followed by the deposition of top electrodes on the MoS2/WS2 stacked fims. Gold (Au) was used for the electrode materials. Electrical measurements were performed at room temperature using an Agilent B2912A precision source/measure unit connected to a probe station with tungsten probes.
Additional Information
How to cite this article: Choudhary, N. et al. Centimeter Scale Patterned Growth of Vertically Stacked Few Layer Only 2D MoS2/WS2 van der Waals Heterostructure. Sci. Rep. 6, 25456; doi: 10.1038/srep25456 (2016).
References
Geim, A. K. & Grigorieva, I. V. Van der Waals heterostructures. Nature 499, 419–425 (2013).
Lotsch, B. V. Vertical 2D heterostructures. Annu. Rev. Mater. Res. 45, 85–109 (2015).
Bhimanapati, G. R. et al. Recent advances in two-dimensional materials beyond graphene. ACS Nano 9, 11509–11539 (2015).
Kang, J., Li, J., Li, S. S., Xia, J. B. & Wang, L. W. Electronic structural Moiré pattern effects on MoS2/MoSe2 2D heterostructures. Nano Lett. 13, 5485−5490 (2013).
Bernardi, M., Palummo, M. & Grossman, J. C. Extraordinary sunlight absorption and one nanometer thick photovoltaics using two-dimensional monolayer materials. Nano Lett. 13, 3664−3670 (2013).
Terrones, H., Urías, F. L. P. & Terrones, M. Novel hetero-layered materials with tunable direct band gaps by sandwiching different metal disulfides and diselenides. Sci. Rep. 3, 1549 (2013).
Kou, L., Frauenheim, T. & Chen, C. Nanoscale multilayer transition-metal dichalcogenide heterostructures: band gap modulation by interfacial strain and spontaneous polarization. J. Phys. Chem. Lett. 4, 1730−1736 (2013).
Komsa, H. K. & Krasheninnikov, A. V. Electronic structures and optical properties of realistic transition metal dichalcogenide heterostructures from first principles. Phys. Rev. B 88, 085318 (2013).
Kang, J., Tongay, S., Zhou, J., Li, J. & Wu, J. Band offsets and heterostructures of two-dimensional semiconductors. Appl. Phys. Lett. 102, 012111 (2013).
Gong, C. et al. Band alignment of two-dimensional transition metal dichalcogenides: Application in tunnel field effect transistors. Appl. Phys. Lett. 103, 053513 (2013).
Nourbakhsh, A., Zubair, A., Dresselhaus, M. S. & Palacios, T. Transport properties of a MoS2/WSe2 heterojunction transistor and its potential for application. Nano Lett. 16, 1359–1366 (2016).
Lee, C. H. et al. Atomically thin p–n junctions with van der Waals heterointerfaces. Nat. Nanotechnol. 9, 676–681 (2014).
Furchi, M. M., Pospischil, A., Libisch, F., Burgdörfer, J. & Mueller, T. Photovoltaic effect in an electrically tunable van der Waals heterojunction. Nano Lett. 14, 4785−4791 (2014).
Chiu, M. H. et al. Spectroscopic signatures for interlayer coupling in MoS2-WSe2 van der Waals stacking. ACS Nano 8, 9649–9656 (2014).
Fang, H. et al. Strong interlayer coupling in van der Waals heterostructures built from single-layer chalcogenides. Proc. Natl. Acad. Sci. 111, 6198–6202 (2014).
Chiu, M.-H. et al. Determination of band alignment in the single-layer MoS2/WSe2 heterojunction, Nat. Commun. 6, 7666 (2015).
Hong, X. et al. Ultrafast charge transfer in atomically thin MoS2/WS2 heterostructures. Nat. Nanotechnol. 9, 682–686 (2014).
Tongay, S. et al. Tuning interlayer coupling in large-area heterostructures with CVD-grown MoS2 and WS2 monolayers. Nano Lett. 14, 3185–3190 (2014).
Ceballos, F., Bellus, M. Z., Chiu, H.-Y. & Zhao, H. Ultrafast charge separation and indirect exciton formation in a MoS2–MoSe2 van der Waals heterostructure. ACS Nano 8, 12717–12724 (2014).
Rivera, P. et al. Observation of long-lived interlayer excitons in monolayer MoSe2–WSe2 heterostructures. Nat. Commun. 6, 6242 (2015).
Yu, Y. et al. Equally efficient interlayer exciton relaxation and improved absorption in epitaxial and nonepitaxial MoS2/WS2 heterostructures. Nano Lett. 15, 486–491 (2015).
Kong, D. et al. Synthesis of MoS2 and MoSe2 films with vertically aligned layers. Nano Lett. 13, 1341–1347 (2013).
Jung, Y., Shen, J., Sun, Y. & Cha, J. J. Chemically synthesized heterostructures of two-dimensional molybdenum/tungsten-based dichalcogenides with vertically aligned layers. ACS Nano 8, 9550–9557 (2014).
Jung, Y. et al. Metal seed layer thickness-induced transition from vertical to horizontal growth of MoS2 and WS2 . Nano Lett. 14, 6842–6849 (2015).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Akinwande, D., Petrone, N. & Hone, J. Two-dimensional flexible nanoelectronics. Nat. Commun. 5, 5678 (2014).
Gong, Y. et al. Vertical and in-plane heterostructures from WS2/MoS2 monolayers. Nat. Mater. 13, 1135–1142 (2014).
Heo, H. et al. Rotation-misfit-free heteroepitaxial stacking and stitching growth of hexagonal transition-metal dichalcogenide monolayers by nucleation kinetics controls. Adv. Mater. 27, 3803–3810 (2015).
Lin, Y.-C. et al. Atomically thin resonant tunnel diodes built from synthetic van der Waals heterostructures. Nat. Commun. 6, 7311 (2015).
Gong, Y. et al. Two-step growth of two-dimensional WSe2/MoSe2 heterostructures. Nano Lett. 15, 6135–6141 (2015).
Zhang, X. et al. Vertical heterostructures of layered metal chalcogenides by van der Waals epitaxy. Nano Lett. 14, 3047–3054 (2014).
Zhang, X. et al. Phonon and Raman scattering of two-dimensional transition metal dichalcogenides from monolayer, multilayer to bulk material. Chem. Soc. Rev. 44, 2757–2785 (2015).
Zhang, M. et al. Two-dimensional molybdenum tungsten diselenide alloys: photoluminescence, raman scattering and electrical transport. ACS Nano 8, 7130–7137 (2014).
Chen, Y. et al. Tunable band gap photoluminescence from atomically thin transition-metal dichalcogenide alloys. ACS Nano 7, 4610–4616 (2013).
Li, H. et al. From bulk to monolayer MoS2: evolution of Raman scattering. Adv. Funct. Mater. 22, 1385–1390 (2012).
Choudhary, N., Park, J., Hwang, J. Y. & Choi, W. Growth of large-scale and thickness-modulated MoS2 nanosheets. ACS Appl. Mater. Interfaces 6, 21215–21222 (2014).
Berkdemir, A. et al. Identification of individual and few layers of WS2 using Raman spectroscopy. Sci. Rep. 3, 1755 (2013).
Duan, X., Wang, C., Pan, A., Yu, R. & Duan, X. Two-dimensional transition metal dichalcogenides as atomically thin semiconductors: opportunities and challenges. Chem. Soc. Rev. 44, 8859–8876 (2015).
Duan, X. et al. Lateral epitaxial growth of two-dimensional layered semiconductor heterojunctions. Nat. Nanotechnol. 9, 1024–1030 (2014).
Molina-Sanchez, A. & Wirtz, L. Phonons in single-layer and few-layer MoS2 and WS2 . Phys. Rev. B. 84, 155413 (2011).
van der Zande, A. M. et al. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 12, 554–561 (2013).
Huo, N. et al. Abnormal photocurrent response and enhanced photocatalytic activity induced by charge transfer between WS2 nanosheets and WO3 nanoparticles. Adv. Func. Mater. 24, 7025 (2014).
Chen, K. et al. Electronic properties of MoS2-WS2 heterostructures synthesized with two-step lateral epitaxial strategy. ACS Nano 9, 9868–9876 (2015).
Xue, Y. et al. Scalable production of a few-layer MoS2/WS2 vertical heterojunction array and its application for photodetectors, ACS Nano 10, 573–580 (2016).
Acknowledgements
Y.J. acknowledges the financial support from a start-up fund from the University of Central Florida and the use of Materials Characterization Facility, AMPAC, at the University of Central Florida. W.C. acknowledges the financial support from a Research SEED Grant program from the University of North Texas. S.I.K. acknowledges partial support by the National Aeronautics & Space Administration through the University of Central Florida’s NASA Florida Space Grant Consortium and Space Florida. H.-S.C. was supported by National Research Foundation of Korea (NRF) grant funded by the Korea Government (MSIP) (No. 2015R1C1A1A01052727) and Korea Basic Science Institute (Grant No. C36250).
Author information
Authors and Affiliations
Contributions
N.C. and J.P. synthesized and characterized the materials under the guidance of W.C. and Y.J., J.Y.H. and H.-S.C. conducted the TEM characterizations. N.C., S.I.K. and K.H.D. conducted the electrical measurements. W.C., S.I.K. and Y.J. edited the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Choudhary, N., Park, J., Hwang, J. et al. Centimeter Scale Patterned Growth of Vertically Stacked Few Layer Only 2D MoS2/WS2 van der Waals Heterostructure. Sci Rep 6, 25456 (2016). https://doi.org/10.1038/srep25456
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep25456
- Springer Nature Limited
This article is cited by
-
Strong coupling and pressure engineering in WSe2–MoSe2 heterobilayers
Nature Physics (2021)
-
Monolayer MoS2 epitaxy
Nano Research (2021)
-
Scalable lateral heterojunction by chemical doping of 2D TMD thin films
Scientific Reports (2020)
-
Towards Scalable Fabrications and Applications of 2D Layered Material-based Vertical and Lateral Heterostructures
Chemical Research in Chinese Universities (2020)
-
Centimeter-scale Green Integration of Layer-by-Layer 2D TMD vdW Heterostructures on Arbitrary Substrates by Water-Assisted Layer Transfer
Scientific Reports (2019)