Abstract
A low cost and non-precious metal composite material g-C3N4-LaNiO3 (CNL) was synthesized as a bifunctional electrocatalyst for the air electrode of lithium-oxygen (Li-O2) batteries. The composition strategy changed the electron structure of LaNiO3 and g-C3N4, ensures high Ni3+/Ni2+ ratio and more absorbed hydroxyl on the surface of CNL that can promote the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER). The composite catalyst presents higher activities than the individual components g-C3N4 and LaNiO3 for both ORR and OER. In non-aqueous Li-O2 batteries, CNL shows higher capacity, lower overpotentials and better cycling stability than XC-72 carbon and LaNiO3 catalysts. Our results suggest that CNL composite is a promising cathode catalyst for Li-O2 batteries.
Similar content being viewed by others
Introduction
Li-O2 battery is a promising energy storage solution, as it has a theoretical specific energy of 5200 Wh kg−1 (including O2), much higher than the state-of-the-art Li-ion battery1,2,3. A typical non-aqueous Li-O2 cell is composed of a piece of lithium metal as the anode, electrolyte and a piece of porous air electrode as the cathode. During the discharge reaction, the oxygen reduction reaction happens in the cathode producing lithium peroxides (Li2O2)4. During the charge, a reversal reaction of oxygen evolution reaction happens, decomposing Li2O2 to oxygen and Li-ions again5. It is crucial to utilize highly efficient catalysts to promote the ORR/OER process. So far, many metals, metal oxides, carbonaceous materials and redox media have been reported as cathode catalysts in Li-O2 batteries6,7,8,9,10. The noble metal and noble metal oxide nanoparticles are usually the highly efficient catalyst, however, the high cost of the noble metals have limited their large-scale applications11,12.
Graphitic carbon nitride (g-C3N4) polymer, has a planar phase analogous to graphite. Unlike graphite, however, g-C3N4 has both 3-fold-coordinated (graphite-like) and 2-fold-coordinated (pyridine-like) nitrogen atoms and every carbon atom is bonded to three nitrogen atoms, including both pyridinic and graphitic nitrogen moieties13. g-C3N4 is an attractive catalysis material due to its properties like high chemical stability, low-cost preparation and specificity in the structure and composition14. So far, it has been used in many areas, such as the photochemical splitting of water, fuel cells and metal-free heterogeneous catalysis of various organic reactions15,16,17,18,19,20. In particular, g-C3N4 contains alleged “nitrogen pots” with six nitrogen lone-pair electrons, which enable the material to modify the electronic structures of the molecular and to be ideal sites for metal inclusion21,22. However, the poor electroconductivity and the relatively low ORR catalytic activity limit the electrocatalytic application of g-C3N423. These problems can be solved by composting g-C3N4 with other materials which have better electrical conductivity. For example, g-C3N4 combined with non-noble metals like Co-g-C3N424, Fe-g-C3N425 and Ni-Co3O4-C3N426 have been investigated as the effective catalysts in fuel cells and Li-O2 batteries. The composites have shown promising ORR and OER activity and tolerance ability that are comparable to commercial Pt/C.
Perovskite oxides (ABO3) have been widely used as catalysts for fuel cells and metal-O2 batteries27, owing to their unique structures, excellent oxygen mobility and low cost. LaNiO3 has the intrinsic activity for both ORR and OER among the perovskite type oxides, because Ni3+ at B site in the perovskite structure has single electron-filled eg orbit and therefore, provides the favorable bond energy of M (B site)-O bond for ORR and OER28. In addition, the catalytic activity of LaNiO3 could be readily enhanced through increasing the Ni3+/Ni2+ ratio by replacing part of Ni ions with Mg or Fe ions. g-C3N4 has a large number of removable electronic between layers and cavities encircling with some pyridine-like nitrogen29. So it has a high ability to complex with abundant metal ions and adjust its conjugation structure subsequently. Therefore combining g-C3N4 with LaNiO3 can theoretically improve the electron transfer and catalytic activity of the CNL composite. However, to the best of our knowledge, g-C3N4 have never been composited with LaNiO3 to explore the enhanced the catalytic activity for both ORR and OER.
In this work, we synthesized a composite catalyst g-C3N4-LaNiO3 (CNL) and demonstrated that the CNL has significantly enhanced electrocatalytic activity for OER and ORR compared with individual component g-C3N4 or LaNiO3 in an alkaline electrolyte. Furthermore, CNL exhibited improved round-trip efficiency and cycling stability in Li-O2 batteries. These results suggest that the CNL is a promising bi-functional catalyst for oxygen oxidation/evolution reactions.
Results and Discussion
Characterization of CNL catalyst
Figure 1 depicts the synthetic process of CNL catalyst and the molecular structure of the catalytic spots of CNL catalyst. Figure 2 displays the XRD patterns of pure g-C3N4, LaNiO3 and the hybrid catalyst CNL with different weight percent of g-C3N4. It can be seen that the pure g-C3N4 has two distinct peaks. The strong peak at 27.39°, corresponding to the (002) peak with in-planar distance of 0.326 nm (JCPDS 87–1526), is attributed to the long-range in-planar stacking of aromatic units30. Another peak at 13.08°, with a much weaker intensity, can be assigned to (100) diffraction peak20, which corresponds to a distance of 0.686 nm, belongs to tri-s-triazine units, due to the interlayer stacking. After the LaNiO3 being composited with g-C3N4, the CNL hybrids show a coexistence phases of both g-C3N4 and LaNiO3, although the characteristic peak of g-C3N4 was not obvious for the 5 wt.% and 10 wt.% CNL hybrids.
For the further information of the materials microstructure, Fig. 3 shows the SEM images of g-C3N4, LaNiO3 and 10 wt.% CNL. Pure g-C3N4 shows an aggregated layered structure with smooth surface. The agglomerate size is several micron meters. LaNiO3 particles are hundreds nanometers large, more than one order of magnitude smaller than g-C3N4. As to the image of 10 wt.% CNL, LaNiO3 particles are deposited on the surface of g-C3N4.
In this study we used the X-ray photoelectron spectra to research the physical and chemical characteristic of the composite catalyst surface. Figure 4a shows the O 1s XP-spectra of g-C3N4, LaNiO3 and CNL catalysts. The O 1s XP-spectra contains four distinct species. Two low binding energy peaks located at 528.6 eV and 530.1 eV are ascribed to the lattice oxygen, O2− species in lanthanum oxide and nickel oxide31. The peaks located at 531.5 eV and 532.2 eV are from lanthanum and nickel hydroxides32,33. With the increase of g-C3N4, the peaks at low binding energy become weaken and the peaks at high binding energy become stronger, indicating that the g-C3N4 compositing LaNiO3 can promote the adsorption of hydroxyl on the surface of the composite catalyst and the covalency of Ni-O bond become stronger34. It has been demonstrated that the rate of O22−/OH− displacement and OH− regeneration dominate the ORR kinetics and the great covalence of the Ni-O bond can promote the ORR kinetics30. Furthermore, OER is either through chemisorbed OOH− formation or oxidation of surface OH−. The rate-determining step of the OER on perovskite oxides is governed by the concentration of hydroxide species that participate in the formation of the O-O bond in hydroperoxide. Thus, the high lattice hydroxide concentration on the surface can promote the HOO− forms and consequently has a positive effect on OER activity.
The N 1s XPS spectrum of the g-C3N4 shown in Fig. 4b can be fitted into three peaks at 398.8, 400.5 and 404.7 eV, corresponding to pyridine-like N, pyrrole-like N and oxidized N, respectively35,36. After adding g-C3N4, a new peak emerged at 398.2 eV, which also corresponds to pyridine-like N. The reason why it was lower than 398.8 eV, can be explained by the existence of chemical bonds in the g-C3N4-LaNiO3 heterojunction.
Ni 2p3/2 was deconvoluted into two peaks. The binding energy of 854.3 eV was due to Ni2+ and 856 eV was due to Ni3+ as shown in Fig. 4c 31. The peak intensity of the lower oxidation state (Ni2+) is weakening and the higher oxidation state (Ni3+) is enhancing with the increase of g-C3N4 in the composite. It suggests that through heat treating LaNiO3 could be doped with nitrogen-atoms forming LaNiO3−xNx, which promoted the formation of Ni3+ on the surface of the composite catalyst. According to previous report, the existence of Ni3+ in LaNiO3 are beneficial to both ORR and OER activities of the material37.
Electrocatalytic performance
The typical polarization curves for the ORR was investigated in O2 saturated 0.1 M KOH solution, shown in Fig. 5a. The ORR onset potential of 10 wt.% CNL is about −0.286 V, the most positive among that of LaNiO3 (−0.304 V), 20 wt.% CNL (−0.319 V), 30 wt.% CNL (−0.315 V), g-C3N4 (−0.315 V) and XC-72 (−0.314 V). And the half-wave potential of 10 wt.% CNL is −0.35 V, ~350 mV higher than the 2nd high value of 5 wt.% CNL. In additional that the 10 wt.% CNL also exhibits the largest diffusion-limiting current and the limiting current was 4.36 mA cm−2, much higher than 2.82 mA cm−2 of LaNiO3. Furthermore, for kinetic analysis the current-potential curves at various rotation speeds were also analyzed with the Koutecky-Levich equation:
This equation has been widely used to analyze the ORR reaction kinetics38,39,40, where id is the tested disk currentdensity, n is the number of electron transfer in the ORR, k is the Boltzmann constant, F is the Faraday constant, A is the geometric area of the disk electrode, CO is the saturated concentration of oxygen in 0.1 M KOH solution, DO is the diffusion coefficient of oxygen, ν is the kinematic viscosity of the 0.1 M KOH solution and ω is the electrode rotation rate. There should be a linear relationship between id−1 and ω−1/2, the intercept is equal to ik−1 and n could be calculated from the slope.
Figure 5b shows the Koutecky-Levich plots of XC-72, g-C3N4 and CNLs based on ORR polarization curves at −0.6 V with rotation speed of 2000, 1600, 1200 and 900 rpm. All curves exhibit good linear characteristic, indicating the first-order kinetics characteristics of the ORR. According to equations (3 and 4), the n value could be calculated as shown in Table 1. The n value of 10 wt.% CNL is about 3.86, indicating the ORR was a four-electrons process. In comparison with LaNiO3 catalyst, as-synthesized 10 wt.% CNL material delivers a better ORR activity and kinetics. The higher electrocatalytic activity is due to the high Ni3+/Ni2+ ratio in 10 wt.% CNL, which could promote adsorption/desorption of oxygen and thus the ORR activity in an alkaline electrolyte. Therefore in this work, the composite strategy has demonstrated to be highly effective to improve the ORR catalytic activity of the components.
The catalytic activity of the synthesized CNL for OER was also investigated by the RDE technique by measuring the polarization curves in O2 saturated 0.1 M KOH solution from 0.0 V to 1.2 V, at a scan rate of 5 mV s−1 and a rotation speed of 1600 rpm. As shown in Fig. 5c, all the synthesized composite catalysts exhibit much better catalytic activity for OER than XC-72 carbon and LaNiO3. The OER onset potential for LaNiO3 is 0.70 V and the OER diffusion-limiting current density at 1.2 V is 20.2 mA cm−2. For a comparison, the 10 wt.% CNL has a more negative onset potential of 0.63 V and the current density is 47.0 mA cm−2 at 1.2 V remarkably higher than that of LaNiO3.
This improved property of 10 wt.% CNL is mainly due to the enhanced adsorption of hydroxyl on the surface of CNL composite. The hydroxyl participates in the formation of HOO− and the increase of the HOO− concentration leads to the high OER electrocatalytic activity. As to the elexctrocatalytic activity of g-C3N4, due to the stronger electro-negativity of N than C, the electron will transfer from C to adjacent N, while the π-conjugation causes the electrons to return to the adjacent Cp2 orbital41,42. These donation and back-donation processes not only help the O2− adsorption by the strong chemical bond between O and C, but also promote O2 desorption on the adjacent C atoms, resulting in enhanced ORR and OER activity. The reason that ORR and OER activities of the 20 wt.% CNL and 30 wt.% CNL are lower than these of 10 wt.% CNL, can be interpreted by the worsen electron conductive environment due to too much non-conductive in the composites.
XRD was used to confirm the formation and decomposition of Li2O2 on the 10 wt.% CNL cathode during the charge-discharge process in non-aqueous Li-O2 batteries. Figure 6 shows XRD patterns of the 10 wt.% CNL cathode at pristine,1st discharge and 1st recharge condition. After 1st discharge, compared to the XRD pattern of the pristine cathode, some diffraction peaks at 34.7, 40.3, 58.3 and 70.5° appear, which can be ascribed to Li2O2 formation during the discharging process. After the 1st charge process, the diffraction peaks of Li2O2 disappear, indicating that the formed Li2O2 in the 1st discharge is decomposed during the charging process. This XRD pattern evolution demonstrates the rechargeability of this 10 wt.% CNL cathode.
We further investigated the catalyst activity of the composites in non-aqueous Li-O2 batteries. The first discharge and charge profiles of XC-72, LaNiO3 and 10 wt.% CNL in the Li-air batteries were compared at a current density of 50 mA g−1 (Fig. 7a). In particular, the initial discharge capacity of the 10 wt.% CNL is 5500 mAh g−1, higher than that of LaNiO3 (4600 mAh g−1) and XC-72 carbon (3600 mAh g−1). Also, it can be clearly seen that the discharge voltage plateau of the 10 wt.% CNL catalyst was ~2.8 V, higher than that of the LaNiO3 (~2.7 V) and the XC-72 carbon (~2.7 V). The charge voltage plateau of the 10 wt.% CNL was ~4.0 V, lower than that of LaNiO3 (~4.3 V) and XC-72 carbon (~4.4 V). The smaller overvoltages of CNL suggests the higher catalytic activity than LaNiO3 and XC-72. In additional, 10 wt.% CNL catalyst presented 65 cycles between voltage window of 2.6 V to 4.7 V as shown in Fig. 7b. While the performance of the LaNiO3 and XC-72 carbon catalyst are only up to 32 and 25 cycles respectively. These results indicate that the 10 wt.% CNL as air electrode catalyst enhanced the capacity and cyclability of Li-O2 batteries.
In conclusion, LaNiO3 and g-C3N4 composite was made as the bi-functional catalyst for oxygen reactions. The composite material delivers batter ORR and OER activities than individual LaNiO3 and g-C3N4, the reason is that the CNL catalyst has a high Ni3+/Ni2+ ratio that can promote adsorption/desorption of oxygen in an alkaline electrolyte and more absorbed hydroxyl on the surface of CNL that can promote HOO− formation. LaNiO3 and g-C3N4 composite is for the first time used as the bi-functional catalysts for lithium air batteries. The composite presents enhanced specific capacity and cycle stability. The results suggest CNL composite can be a potential bifunctional catalyst for the Li-O2 batteries and the composite strategy is worth of further investigation.
Methods
Synthesis of LaNiO3 NPs and g-C3N4 sheets
LaNiO3 nanoparticles (NPs) were synthesized by a sol-gel method. 1.3 g La2O3 (Sinopharm, reagent grade) was dissolved in 10 mL HNO3 solution (65% ≤ HNO3 ≤ 68%), obtaining the La(NO3)3 · xH2O solution. Then 2.37 g Ni(NO3)2 · 6H2O (Sinopharm, reagent grade) and the La(NO3)3 · xH2O were dissolved in 100 ml de-ion water. Subsequently, the mixture of 6.75 g citric acid (HOC(COOH)(CH2COOH)2 ≥ 99.5%) and 3.6 mL ethylene glycol (HOCH2-CH2OH, 99.8%) were dropwise added into the metal nitrates under magnetic stirring at 80 °C. The molar ratios of total metal cations: citric acid: ethylene glycol were 1:2:4. Then the resulting solution was stirred at 80 °C to evaporate water forming a viscous gel. The gel was heated at 400 °C for 1 hour and the amorphous citrate precursor was obtained. The precursor was milled and then calcinated in oxygen atmosphere at 750 °C for 5 hours to obtain final LaNiO3 powders.
Bulk g-C3N4 sheets were synthesized by pyrolysis method. Briefly, 5 g melamine were heated at 550 °C for 2 hours with a heating rate of 5 °C min−1. The resultant agglomerates were ground for 1 hour in a mortar, then further heated at 550 °C for 2 hours. Then the as-prepared bulk g-C3N4 were obtained.
Synthesis of CNL composite material
The CNL were synthesized as follows: 0.04 g g-C3N4 were dispersed in 50 mL ethanol in a beaker and treated by ultrasonic for 30 min to fully disperse g-C3N4. Then 0.4 g LaNiO3 NPs were added into the g-C3N4 suspension and the mixture were further dispersed by the ultrasonic treatment for 30 min and then heated under reflux for 6 hours at 90 °C with stirring. Then evaporated the alcohol completely with stirring, a precipitate was obtained. The precipitate was collected and heated at 550 °C for 2 hours in nitrogen atmosphere. Then the resultant compound were ground for 1 hour in the mortar, to make the final 10 wt.% CNL composite material (the weight percentage number imply the g-C3N4). By this method, CNL catalysts in different mass ratios (5 wt.% CNL, 20 wt.% CNL and 30 wt.% CNL) were also prepared.
Characterization of materials
The crystal phase and purity of the as-prepared powders were determined by X-ray powder diffraction with Cu Kα radiation (λ = 0.154056 nm) from 10° to 90°. The structures of the samples were determined by field-emission scanning electron microscope (SEM) performed on a Hitachi SU8020 at an acceleration voltage of 3 kV. X-ray photoelectron spectra (XPS) data were obtained on a Rigaku D/MAX2500V X-ray photoelectron spectrometer with an exciting source of Al Kα (1486.6 eV).
Electrochemical measurements
Electrochemical characterizations of the samples were performed on a rotating-disk electrode (RDE, ATA-1B) with a three-electrode cell. A platinum electrode was used as the counter electrode. A saturated calomel electrode was used as the reference electrode. A glassy carbon electrode was used as the working electrode. 0.1 M potassium hydroxide (KOH) solution was used as the electrolyte. For CV, ORR and OER studies, the 1 mg composite catalyst powder was mixed with 2.5 mg XC-72 carbon to ensure sufficient electronic conductivity. The as-prepared catalyst and 30 μL of 5 wt.% Nafion solutions were dispersed in 1 mL de-ion water/isopropanol solution (the volume ratio of de-ion water: isopropanol is 5:1), with an ultrasonic treatment for 40 min to make a homogeneous ink. The glassy carbon electrodes (3 mm diameter, 0.071 cm2 area) were polished on a clean polishing cloth with the 0.05 μm alumina slurry, rinsed and dried. Then we pipeted 2.8 μL of the suspension drop-cast and loaded it on the glassy carbon, which was dried slowly inside a closed container. The glassy carbon electrode loaded with catalyst was immersed into a N2-saturated KOH electrolyte for the steady-state CVs. The N2 was switched to O2 and purged for another 30 min. After that the ORR polarization curve was measured from 0 V to −1.0 V. Then, switched the O2 to N2 and purged for 30 min. Subsequently, the OER polarization curve were examined by a voltage scan from 0.0 V to 1.2 V. Electrochemical data were collected with an Autolab electrochemical workstation.
For Li-O2 battery studies, the battery were fabricated in a glove box which was filled with pure argon gas. A lithium foil was used as the anode, 1 M LiCF3SO3 in tetraethylene glycol dimethyl ether (TEGDME) as the electrolyte, glass fiber filter paper as separator, carbon-paper-supported catalysts as the cathode electrode and two piece of nickel foam (1 mm thick) as the cathode current collector43,44. The oxygen electrodes were prepared by mixing the as-prepared CNL catalysts, XC-72 carbon, 5 wt.% polyvinylidene fluoride (PVDF) and solvent N-methyl-2-pyrrolidone (NMP) and the mass ratio of CNL catalyst: XC-72 carbon: 5 wt.% PVDF is 1:2:3. The uniform slurry was coated onto the carbon-paper by a brush and dried in vacuum at 80 °C for 12 hours. The ready-made Li-O2 battery were transferred into a sealed bottle which was filled with pure oxygen and linked with the multichannel battery testing system (LAND CT 2001A). Galvanostatic discharge of the battery were studied in a potential range of 4.5–2.0 V. The first discharge cycle performances were conducted at the current density of 50 mA g−1. The following cycle performances were conducted at the current density of 250 mA g−1 and the capacity was limited to 500 mAh g−1. It should be noted that the current density and capacity were all calculated based on the mass of catalyst loaded on the cathode.
Additional Information
How to cite this article: Wu, Y. et al. Electrocatalytic performances of g-C3N4-LaNiO3 composite as bi-functional catalysts for lithium-oxygen batteries. Sci. Rep. 6, 24314; doi: 10.1038/srep24314 (2016).
References
Abraham, K. M. & Jiang, Z. A polymer electrolyte-based rechargeable lithium/oxygen battery. J. Electrochem. Soc. 143, 1–5 (1996).
Liu, T. et al. Cycling Li-O2 batteries via LiOH formation and decomposition. Science 350, 530–533 (2015).
Xu, J. J., Wang, Z. L., Xu, D., Zhang, L. L. & Zhang, X. B. Tailoring deposition and morphology of discharge products towards high-rate and long-life lithium-oxygen batteries. Nat. Commun. 4, 2438 (2013).
Shui, J. L. et al. Reversibility of anodic Lithium in rechargeable Lithium-oxygen batteries. Nat. Commun. 4, 1161–1171 (2013).
Liu, Q. C., Xu, J. J., Xu, D. & Zhang, X. B. Flexible lithium-oxygen battery based on a recoverable cathode. Nat. Commun. 6, 7892 (2015).
Shui, J. L., Karan, N. K., Balasubramanian, M., Li, S. Y. & Liu, D. J. Fe/N/C composite in Li-O2 battery: studies of catalytic structure and activity toward oxygen evolution reaction. J. Am. Chem. Soc. 134, 16654–16661 (2012).
Rao, C. V., Cabrera, C. R. & Ishikawa, Y. In search of the active site in nitrogen-doped carbon nanotube electrodes for the oxygen reduction reaction. J. Phys. Chem. Lett. 1, 2622–2627 (2010).
Nam, G. et al. Metal-free Ketjenblack incorporated nitrogen-doped carbon sheets derived from gelatin as oxygen reduction catalysts. Nano lett. 14, 1870–1876 (2014).
Kwon, K., Sa, Y. J., Cheon, J. Y. & Joo, S. H. Ordered mesoporous carbon nitrides with graphitic frameworks as metal-free, highly durable, methanol-tolerant oxygen reduction catalysts in an acidic medium. Langmuir 28, 991–996 (2011).
Oh, M. Y., Jeon, J. S., Lee, J. J., Kim, P. & Nahm, K. S. The bifunctional electrocatalytic activity of perovskite La0.6Sr0.4CoO3−δ for oxygen reduction and evolution reactions. RSC Adv. 5, 19190–19198 (2015).
Yang, Y., Shi, M., Zhou, Q. F., Li, Y. S. & Fu, Z. W. Platinum nanoparticle-graphene hybrids synthesized by liquid phase pulsed laser ablation as cathode catalysts for Li-air batteries. Electrochem. Commun. 20, 11–14 (2012).
Li, H. et al. Nitrogen-doped carbon nanotubes with high activity for oxygen reduction in alkaline media. Int. J. Hydrogen Energ. 36, 2258–2265 (2011).
Dai, L. M., Xue, Y. H., Qu, L. T., Choi, H. J. & Baek, J. B. Metal-Free Catalysts for Oxygen Reduction Reaction. Chem. Rev. 115, 4823–4892 (2015).
Kwon, K., Sa, Y. J., Cheon, J. Y. & Joo, S. H. Ordered mesoporous carbon nitrides with graphitic frameworks as metal-free, highly durable, methanol-tolerant oxygen reduction catalysts in an acidic medium. Langmuir 28, 991–996 (2012).
Li, X. H., Wang, X. & Antonietti, M. Solvent-free and metal-free oxidation of toluene using O2 and g-C3N4 with nanopores: nanostructure boosts the catalytic selectivity. ACS Catal. 2, 2082–2086 (2012).
Chen, X. F., Zhang, J. S., Fu, X. Z., Antonietti, M. C. & Wang, X. C. Fe-g-C3N4-catalyzed oxidation of benzene to phenol using hydrogen peroxide and visible light. J. Am. Chem. Soc. 131, 11658–11659 (2009).
Katsumata, H., Sakai, T., Suzuki, T. & Kaneco, S. Highly efficient photocatalytic activity of g-C3N4/Ag3PO4 hybrid photocatalysts through Z-scheme photocatalytic mechanism under visible light. Ind. Eng. Chem. Res. 53, 8018–8025 (2014).
Kumar, S., Kumar, B., Baruah, A. & Shanker, V. Synthesis of magnetically separable and recyclable g-C3N4-Fe3O4 hybrid nanocomposites with enhanced photocatalytic performance under visible-light irradiation. J. Phys. Chem. C 117, 26135–26143 (2013).
Shi, H. F., Chen, G. Q., Zhang, C. L. & Zou, Z. G. Polymeric g-C3N4 coupled with NaNbO3 nanowires toward enhanced photocatalytic reduction of CO2 into renewable fuel. ACS Catal. 4, 3637–3643 (2014).
Yao, Y. J. et al. Magnetic ZnFe2O4-C3N4 hybrid for photocatalytic degradation of aqueous organic pollutants by visible light. Ind. Eng. Chem. Res. 53, 17294–17302 (2014).
Chen, X. F., Zhang, J. S., Fu, X. Z., Antonietti, M. & Wang, X. C. Fe-g-C3N4-catalyzed oxidation of benzene to phenol using hydrogen peroxide and visible light. J. Am. Chem. Soc. 131, 11658–11659 (2009).
Wang, X. C., Chen, X. F., Thomas, A., Fu, X. Z. & Antonietti, M. Metal-Containing Carbon Nitride Compounds: A New Functional Organic-Metal Hybrid Material. Adv. Mater. 21, 1609–1612 (2009).
Tian, J. Q. et al. Three-Dimensional Porous Supramolecular Architecture from Ultrathin g-C3N4 Nanosheets and Reduced Graphene Oxide: Solution Self-Assembly Construction and Application as a Highly Efficient Metal-Free Electrocatalyst for Oxygen Reduction Reaction. ACS Appl. Mater. Inter. 6, 1011–1017 (2014).
Liu, Q. & Zhang, J. Graphene supported Co-g-C3N4 as a novel metal-macrocyclic electrocatalyst for the oxygen reduction reaction in fuel cells. Langmuir 29, 3821–3828 (2013).
Wang, M. Q. et al. Pyrolyzed Fe-N-C composite as an efficient non-precious metal catalyst for oxygen reduction reaction in acidic medium. ACS Catal. 4, 3928–3936 (2014).
Zou, X. X. et al. Efficient oxygen evolution reaction catalyzed by low-density Ni-doped Co3O4 nanomaterials derived from metal-embedded graphitic C3N4 . Chem. Commun. 49, 7522–7524 (2013).
Wang, Z. L., Xu, D., Xu, J. J. & Zhang, X. B. Oxygen electrocatalysts in metal-air batteries: from aqueous to nonaqueous electrolytes. Chem. Soc. Rev. 43, 7746–7786 (2014).
Du, Z. Z. et al. Electrocatalytic performances of LaNi1−xMgxO3 perovskite oxides as bi-functional catalysts for lithium air batteries. J. Power Sources 265, 91–96 (2014).
Li, S. S., Cong, H. P., Wang, P. & Yu, S. H. Flexible nitrogen-doped graphene/carbon nanotube/Co3O4 paper and its oxygen reduction activity. Nanoscale 6, 7534–7541 (2014).
Ye, L. Q., Liu, J. Y., Jiang, Z., Peng, T. Y. & Zan, L. Facets coupling of BiOBr-g-C3N4 composite photocatalyst for enhanced visible-light-driven photocatalytic activity. Appl. Catal. B-Environ. 142, 1–7 (2013).
Mickevičius, S. et al. Investigation of epitaxial LaNiO3−x thin films by high-energy XPS. J. Alloy. Compd. 423, 107–111 (2006).
Barr, T. L. An ESCA study of the termination of the passivation of elemental metals. J. Phys. Chemistry 82, 1801–1810 (1978).
Liu, Q. C. et al. Artificial Protection Film on Lithium Metal Anode toward Long Cycle-Life Lithium-Oxygen Batteries. Adv. Mater. 27, 5241–5247 (2015).
Suntivich, J. et al. Design principles for oxygen-reduction activity on perovskite oxide catalysts for fuel cells and metal-air batteries. Nat. Chem. 3, 546–550 (2011).
Niu, W. H. et al. Mesoporous N-Doped Carbons Prepared with Thermally Removable Nanoparticle Templates: An Efficient Electrocatalyst for Oxygen Reduction Reaction. J. Am. Chem. Soc. 137, 5555–5562 (2015).
Lin, L., Zhu, Q. & Xu, A. W. Noble-metal-free Fe-N/C catalyst for highly efficient oxygen reduction reaction under both alkaline and acidic conditions. J. Am. Chem. Soc. 136, 11027–11033 (2014).
Suntivich, J., May, K. J., Gasteiger, H. A., Goodenough, J. B. & Shao-Horn, Y. A perovskite oxide optimized for oxygen evolution catalysis from molecular orbital principles. Science 334, 1383–1385 (2011).
Jin, C., Yang, Z. B., Cao, X. C., Lu, F. L. & Yang, R. Z. A novel bifunctional catalyst of Ba0.9Co0.5Fe0.4Nb0.1O3−δ perovskite for lithium-air battery. Int. J. of Hydrogen Energ. 39, 2526–2530 (2014).
Zhao, Y. L. et al. Hierarchical mesoporous perovskite La0.5Sr0.5CoO2.91 nanowires with ultrahigh capacity for Li-air batteries. P. Natl. Acad. Sci. 109, 19569–19574 (2012).
Zhang, D. W. et al. Active LaNi1−xFexO3 bifunctional catalysts for air cathodes in alkaline media. J. Mater. Chem. A 3, 9421–9426 (2015).
Dai, L., Xue, Y., Qu, L., Choi, H. J. & Baek, J. B. Metal-Free Catalysts for Oxygen Reduction Reaction. Chem. Rev. 115, 4823 (2015).
Deng, D. H. et al. Toward N-doped graphene via solvothermal synthesis. Chem. Mater. 23, 1188–1193 (2011).
Xu, J. J. et al. Synthesis of Perovskite-Based Porous La0.75Sr0.25MnO3 Nanotubes as a Highly Efficient Electrocatalyst for Rechargeable Lithium-Oxygen Batteries. Angew. Chem. Int. Edit. 52, 3887–3890 (2013).
Liu, Q. C. et al. Flexible and Foldable Li-O2 Battery Based on Paper-Ink Cathode. Adv. Mater. 27, 8095–8101 (2015).
Acknowledgements
Dawei Zhang thanks the National Natural Science Foundation of China (Grant No. 51472070, No. 51272004 and U1361110) and CAS Key Laboratory of Materials for Energy Conversion (Grant No. KF2014004). JianglanShui thanks the “1000 plan” program of the Chinese Government and the Fundamental Research Funds for the Central Universities.
Author information
Authors and Affiliations
Contributions
D.Z. conceived the project. Y.W. designed the experiments. Y.W. and T.W. performed the experiments, characterization and electrochemical performance test. Y.W., Y.Z., X.H. and S.X. analysed the results. All authors discussed the results and wrote the manuscript. J.S. and D.Z. revised the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wu, Y., Wang, T., Zhang, Y. et al. Electrocatalytic performances of g-C3N4-LaNiO3 composite as bi-functional catalysts for lithium-oxygen batteries. Sci Rep 6, 24314 (2016). https://doi.org/10.1038/srep24314
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep24314
- Springer Nature Limited
This article is cited by
-
La1.5Nd0.3Pr0.2NiO4.16: A New Cathode Material for IT-Solid Oxide Fuel Cells
Electrocatalysis (2023)
-
Preparation and characterization of graphitic carbon nitride-supported l-arginine as a highly efficient and recyclable catalyst for the one-pot synthesis of condensation reactions
Scientific Reports (2021)
-
Hybrid nanostructures of Pd–WO3 grown on graphitic carbon nitride for trace level electrochemical detection of paraoxon-ethyl
Microchimica Acta (2021)
-
LaNiO3 modified with Ag nanoparticles as an efficient bifunctional electrocatalyst for rechargeable zinc–air batteries
Frontiers of Materials Science (2019)
-
Efficient Photocatalytic Bilirubin Removal over the Biocompatible Core/Shell P25/g-C3N4 Heterojunctions with Metal-free Exposed Surfaces under Moderate Green Light Irradiation
Scientific Reports (2017)