Abstract
We investigated the effect of the Ag nanoparticles on the ferroelectric and piezoelectric properties of Ag/poly(vinylidenefluoride-trifluoroethylene) (P(VDF-TrFE)) composite films. We found that the remanent polarization and direct piezoelectric coefficient increased up to 12.14 μC/cm2 and 20.23 pC/N when the Ag concentration increased up to 0.005 volume percent (v%) and decreased down to 9.38 μC/cm2 and 13.45 pC/N when it increased up to 0.01 v%. Further increase in Ag concentration resulted in precipitation of Ag phase and significant leakage current that hindered any meaningful measurement of the ferroelectric and piezoelectric properties. 46% increase of the remanent polarization value and 27% increase of the direct piezoelectric coefficient were observed in the film with the 0.005 v% of the Ag nanoparticles added without significant changes to the crystalline structure confirmed by both X-ray diffraction (XRD) and Fourier transform infrared (FT-IR) experiments. These enhancements of both the ferroelectric and piezoelectric properties are attributed to the increase in the effective electric field induced by the reduction in the effective volume of P(VDF-TrFE) that results in more aligned dipoles.
Similar content being viewed by others
Introduction
Emerging needs for clean and sustainable power sources for wireless sensor networks (WSNs) require research and development of materials, materials integration and design and fabrication of devices suitable for energy harvesting of ambient sources such as solar, thermal, wind and vibration energy. Among them, piezoelectric energy harvesters (PEHs) have drawn attention as efficient transduction devices, which convert ambient vibrational energy into usable electrical energy. We expect that PEHs will be implemented into WSNs to provide sustainable power1,2,3,4,5.
PEHs, in particular, have several advantages over existing power sources that have limited lifetime and require constant replacement6. For example, the wireless sensors for real-time structural health monitoring of bridges, aircrafts and power plants are essential to prevent catastrophic failure of such infrastructures7. The operation of such WSNs requires small and sustainable power source, which can be implemented successfully using PEHs.
Using piezoelectric polymers for PEHs comes with several advantages when applied to WSNs for their flexibility, lightness and relatively simple manufacturing process. However, the biggest challenge with piezoelectric polymer has been their insufficient power generation for practical applications due to small amount of current produced from PEHs. In order to harness their full potential, it is necessary to develop creative and disruptive materials and structure design at both micro- and nano-scale.
To achieve this, we propose to use conductive silver (Ag) nanoparticles, which are relatively cheap and eco-friendly, as additives to improve the properties of piezoelectric polymer, poly(vinylidenefluoride-trifluoroethylene) (P(VDF-TrFE)), which is one of the widely studied piezoelectric polymers for its high piezoelectric response8,9.
Most of the studies about the effects of Ag nanoparticles on piezoelectric polymers have focused on the percolation effect of the nanoparticles on the electric properties as well as dialectic properties in terms of energy storage of the polymer10,11,12. However, there is still under controversial debate whether the Ag nanoparticles improves or deteriorates the electric properties13,14,15. Furthermore, there has been no systematic study about the effect of Ag nanoparticles on the piezoelectric properties, which are crucial for applications to PEHs. Therefore, understanding the mechanism behind the change of piezoelectric properties as a function of Ag nanoparticle concentration in P(VDF-TrFE) films remains of particular scientific and technological interest in view of designing a novel piezoelectric polymer based PEHs.
In this study, we present the effect of addition of Ag nanoparticles into P(VDF-TrFE) films and the optimum concentration of Ag nanoparticles to enhance the piezoelectric properties.
Results and Discussion
Figure 1 shows the cross-section SEM images of the films embedded with Ag nanoparticles from 0 to 1 v%. When more than 0.1 v% of Ag nanoparticles were added to P(VDF-TrFE) films, instead of well dispersing, Ag particles agglomerated together to form larger clusters showing brighter contrast in scanning electron microscopy (SEM) images. These phases are also noticed in optical images of top view of films (see Supplementary Fig. S1 online). Energy-dispersive X-ray spectroscopy (EDS) spectrum analysis indicated that the bright part corresponds to Ag.
Figure 2 displays the FT-IR spectroscopy of P(VDF-TrFE) films, from which we can identify the conformation of the polymer chains in the films. We found almost identical spectra for Ag/P(VDF-TrFE) composite films from 0 to 0.1 v% of Ag nanoparticles concentration. This indicates that addition of Ag nanoparticles in P(VDF-TrFE) films has insignificant effect on the internal structures of the films within the detection limit of FT-IR.
The XRD patterns shown in Fig. 3 also indicate that the addition of Ag nanoparticles has little impact on the crystallographic orientation of the polymer chain structures in P(VDF-TrFE) films. The intensities of the peak at 19.7° associated with the crystalline (110) and (200) planes of all-trans conformation16 are comparable in four different Ag nanoparticles concentration while the (111) planes in Ag at 38.14°17 appeared when Ag concentration increased above 0.5 v%. This data agrees with the results shown in Fig. 2 where we found that the addition of Ag nanoparticles does not affect substantially the internal structure of the polymer film.
The polarization vs. electric field (P-E) hysteresis loops for the films from 0 to 0.01 v% of Ag concentration are shown in Fig. 4. Each polarization value was measured as the external electric field was applied from −100 to 100 MV/m. The coercive field (Ec) values were almost constant in five different concentrations but the remanent polarization values were substantially different. The remanent polarization (Pr) values indicate the internal dipole moment per unit volume when the applied electric field is zero. The values increased until the concentration of Ag nanoparticles reached 0.005 v% and decreased with larger nanoparticles concentration above 0.005 v%. When the Ag nanoparticles were added more than 0.01 v% to the films, P-E hysteresis loops were not obtained in the same range of applied electric fields due to the large leakage current through the films.
Also the piezoelectric charge coefficient (d33) values followed the same trend with the remanent polarization, having the largest value in the 0.005 v% of Ag/P(VDF-TrFE) composite film (Fig. 5). According to Figs 4 and 5, adding 0.005 v% of Ag nanoparticles to the P(VDF-TrFE) film enhances the ferroelectric and piezoelectric properties. This result is also supported by piezoresponse force microscopy (PFM) imaging results, which shows the highest amplitude signal in the 0.005 v% sample (see Supplementary Fig. S4 online)18,19. Based on our results, we found that 0.005 v% is the optimized condition for the highest piezoresponse of the Ag/P(VDF-TrFE) film.
We attempt to explain the results of P-E hysteresis loops and d33 by assuming that there are two competing effects when Ag nanoparticles are added. One is dipole alignment effect and the other is dipole pinning effect. The dipole alignment effect relates to the fact that Ag nanoparticles can act as the center of field concentration that enhances the dipoles to align with the external electric field. In the meantime, the dipole pinning effect refers to the pinning of ferroelectric domain walls at the Ag nanoparticles due to the strong interaction between them, which is commonly observed in ferroelectric ceramic thin films20.
When the electric field is applied to the pure P(VDF-TrFE) film, we think that only a few dipoles will be aligned (Fig. 6(a)) along the electric field due to insufficient electric field to switch all the dipoles in one direction. As we increase the amount of Ag nanoparticles as shown in Fig. 6(b), the imbedded Ag nanoparticles increases the effective electric fields by reducing the effective volume of the polymer in the films. This is the case for Ag particles with less than 0.005 v%. When we increase the concentration above 0.005 v%, however, the dipoles of polymer are pinned by the surface charges or defects at the interface between the matrix and the Ag particles (Fig. 6(c))21,22. The pinned dipoles cause the decrease in the remanent polarization. However, the coercive voltage remains the same for each film as the field concentration, which tends to decrease the coercive field and the dipole pinning, which tends to increase the coercive field, compete in the opposite directions.
One more aspect that needs to be considered is the effect of nanoparticle size as the nanoparticles agglomerate as a function of the concentration. It is known that the strength of the field concentration decreases as the size increases. Therefore, the field concentration effect will stop increasing as the Ag nanoparticles start to agglomerate and increase their size as we increase the volume percentage of the Ag nanoparticles. This may explain, in addition to the dipole pinning effect, the decrease of the piezoelectric properties when the concentration increases beyond 0.005 v%. Finally, when we increase the amount of Ag particles further, they will percolate to create conduction path that results in leakage current (Fig. 6(d)).
Conclusions
We varied the amount of Ag nanoparticles inside the Ag/P(VDF-TrFE) composite films and studied its impact on the piezoelectric properties. We found that adding Ag nanoparticles into the composites had little effects on the internal crystalline structures of polymer chains, which was supported by XRD and FT-IR results. However, the remanent polarization increased from 8.29 to 12.14 μC/cm2 when the Ag concentration increased to 0.005 v% and decreased from 12.14 to 9.38 μC/cm2 when the Ag concentration increased to 0.01 v%. Likewise, the film with 0.005 v% of Ag nanoparticles also had the highest piezoelectric charge coefficient values, 20.23 pC/N. We believe that the presence of the nanoparticles up to an optimum amount facilitates the dipole direction to align well under external electric fields, which leads to increase in the polarization of the entire film. On the other hand, the nanoparticles agglomerate to enhance the charge transport, which leads to increase in leakage current and decrease in piezoelectric properties.
Methods
To make Ag/P(VDF-TrFE) composite solution, dispersed Ag nanoparticles (Ditto Technology Co.) in methyl ethyl ketone (MEK) solvent and 15 weight percent (wt%) of P(VDF-TrFE) (75/25 mol%) were mixed through sonication method for 2 hours. We varied the amount of Ag nanoparticles from 0 to 1 v% in the solution. Films with 15 μm thickness were fabricated by tape casting method23. The prepared solution was dropped on to commercially available indium tin oxide (ITO)/polyethylene naphthalate (PEN) films (DuPont, Inc.) and spread by a doctor blade. To increase the crystallinity and align the internal dipoles of the films, we annealed the films in a vacuum oven at 135 °C for an hour. The platinum (Pt) top electrodes were deposited by a dc magnetron sputtering system over shadow mask having 1 mm diameter holes.
The cross-section of the films was observed by SEM with back scattering detector (BSE) mode to distinguish Ag particles clearly and the built-in EDS was used for the element analysis of the samples. Due to low electrical conductivity of P(VDF-TrFE), a few nm thick platinum film was deposited on the cross-section surface for clear SEM image. Characterization of polymer chain structures was conducted by thin film XRD and FT-IR analysis.
The effects of Ag nanoparticles on the ferroelectric properties of P(VDF-TrFE) were studied by measuring polarization hysteresis loops (P-E loops) using the standardized ferroelectric test system, RT66A tester (Radiant technology, Inc.) applying triangular pulses from −100 to 100 MV/m between top and bottom electrodes of the samples. The piezoelectric properties were characterized by measuring piezoelectric coefficient using the d33 meter (Piezotest, Inc.) at 110 Hz followed by 15 minute process under 1000 V (66.7 MV/m).
Additional Information
How to cite this article: Paik, H. et al. Effect of Ag nanoparticle concentration on the electrical and ferroelectric properties of Ag/P(VDF-TrFE) composite films. Sci. Rep. 5, 13209; doi: 10.1038/srep13209 (2015).
References
Roundy, S. & Wright, P. K. A piezoelectric vibration based generator for wireless electronics. Smart Mater. Struct. 13, 1131 (2004).
Beeby, S. P., Tudor, M. J. & White, N. M. Energy harvesting vibration sources for microsystems applications. Meas. Sci. Technol. 17, R175 (2006).
Anton, S. R. & Sodano, H. A. A review of power harvesting using piezoelectric materials (2003–2006). Smart Mater. Struct. 16, R1 (2007).
Kim, D. et al. A spring-type piezoelectric energy harvester. RSC Adv. 3, 3194 (2013).
Priya, S. Advances in energy harvesting using low profile piezoelectric transducers. J. Electroceram. 19, 167–184 (2007).
Sodano, H. A., Park, G. & Inman, D. J. Estimation of electric charge output for piezoelectric energy harvesting. Strain 40, 49–58 (2004).
Roundy, S., Wright, P. K. & Rabaey, J. A study of low level vibrations as a power source for wireless sensor nodes. Comput. Commun. 26, 1131–1144 (2003).
Zhang, Q. M., Bharti, V. & Zhao, X. Giant electrostriction and relaxor ferroelectric behavior in electron-irradiated poly (vinylidene fluoride-trifluoroethylene) copolymer. Science 280, 2101–2104 (1998).
Xiao, Z., Poddar, S., Ducharme, S. & Hong, X. Domain wall roughness and creep in nanoscale crystalline ferroelectric polymers. Appl. Phys. Lett. 103, (2013).
Lu, J., Moon, K.-S. & Wong, C. P. Silver/polymer nanocomposite as a high-k polymer matrix for dielectric composites with improved dielectric performance. J. Mater. Chem. 18, 4821 (2008).
Huang, X., Jiang, P. & Xie, L. Ferroelectric polymer/silver nanocomposites with high dielectric constant and high thermal conductivity. Appl. Phys. Lett. 95, 242901 (2009).
Xie, L. et al. Core–satellite Ag@BaTiO3 nanoassemblies for fabrication of polymer nanocomposites with high discharged energy density, high breakdown strength and low dielectric loss. Phys. Chem. Chem. Phys. 15, 17560–17569 (2013).
Hadji, R., Nguyen, V. S., Vincent, B., Rouxel, D. & Bauer, F. Preparation and characterization of P (VDF-TrFE)/Al2O3 nanocomposite. Ultrasonics, Ferroelectrics and Frequency Control, IEEE Transactions on 59, 163–167 (2012).
Chae, D. W. et al. Influence of High Contents of Silver Nanoparticles on the Physical Properties of Poly(Vinylidene Fluoride). Mol. Cryst. Liq. Cryst. 464, 233/[815]–241/[823] (2007).
Miranda, D. et al. Influence of Silver Nanoparticles Concentration on the α-to β-Phase Transformation and the Physical Properties of Silver Nanoparticles Doped Poly (vinylidene fluoride) Nanocomposites. J. Nanosci. Nanotech 9, 2910–2916 (2009).
Choi, Y. Y. et al. Nanoscale piezoresponse of 70 nm poly(vinylidene fluoride-trifluoro-ethylene) films annealed at different temperatures. Phys. Stat. Sol. (RRL) 4, 94–96 (2010).
Choi, Y.-J., Huh, U. & Luo, T.-J. M. Spontaneous formation of silver nanoparticles in aminosilica. J. sol-gel Sci. Techn. 51, 124–132 (2009).
Kholkin, A. L., Kalinin, S. V., Roelofs, A. & Gruverman, A. Review of Ferroelectric Domain Imaging by Piezoresponse Force Microscopy 173–214 (Springer: New York, 2007).
Kalinin, S. & Bonnell, D. Imaging mechanism of piezoresponse force microscopy of ferroelectric surfaces. Phys. Rev. B 65, 125408 (2002).
Kim, Y. et al. Origins of domain wall pinning in ferroelectric nanocapacitors. Nano Converg 1, 24 (2014).
Manna, S., Batabyal, S. K. & Nandi, A. K. Preparation and Characterization of Silver−Poly(vinylidene fluoride) Nanocomposites: Formation of Piezoelectric Polymorph of Poly(vinylidene fluoride). J. Phys. Chem. B 110, 12318–12326 (2006).
Kühn, M. & Kliem, H. Monte Carlo Simulations of Ferroelectric Properties for PVDF and BaTiO3. Ferroelectrics 370, 207–218 (2008).
Ahn, G. et al. Facile preparation of ferroelectric poly(vinylidene fluoride- co-trifluoroethylene) thick films by solution casting. Polym. Eng. Sci. 54, 466–471 (2013).
Acknowledgements
This research was supported by the Mid-career Researcher Program (No. 2010-0015063) and Conversion Research Center Program (No. 2011K000674) through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (MEST) and the New & Renewable Energy of the Korea Institute of Energy Technology Evaluation and Planning (KETEP) grant (No. 20103020060010) funded by the Ministry of Knowledge Economy, Korea. Work at Argonne National Laboratory (Y.C., S.H., data analysis and writing of manuscript) was supported by UChicago Argonne, a U.S. DOE Office of Science Laboratory, operated under Contract No. DE-AC02-06CH11357.
Author information
Authors and Affiliations
Contributions
H.P. and S.H. wrote the main manuscript text and Y.C. prepared the PFM data and analysis. H.P., Y.C. S.H. and K.N. contributed to the data analysis and reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Paik, H., Choi, YY., Hong, S. et al. Effect of Ag nanoparticle concentration on the electrical and ferroelectric properties of Ag/P(VDF-TrFE) composite films. Sci Rep 5, 13209 (2015). https://doi.org/10.1038/srep13209
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep13209
- Springer Nature Limited
This article is cited by
-
Optically Controlled Coercive Field of MAPbl3/P(VDF-TrFE) Ferroelectric Composite Films
Chemical Research in Chinese Universities (2023)
-
P(VDF-TrFE)/ZnO nanocomposite synthesized by electrospinning: effect of ZnO nanofiller on physical, mechanical, thermal, rheological and piezoelectric properties
Polymer Bulletin (2023)
-
Hybrid biodegradable electrospun scaffolds based on poly(l-lactic acid) and reduced graphene oxide with improved piezoelectric response
Polymer Journal (2022)
-
P(VDF-TrFE)/ZnO nanofiber composite based piezoelectric nanogenerator as self-powered sensor: fabrication and characterization
Journal of Polymer Research (2022)
-
Effect of rare earth Er and Dy on the Curie temperature and interfacial charge mobility of electrocaloric PVDF-HFP composites
Journal of Materials Science: Materials in Electronics (2020)