Abstract
The adsorption of proteins onto carbon-based nanomaterials (CBNs) is dictated by hydrophobic and π-π interactions between aliphatic and aromatic residues and the conjugated CBN surface. Accordingly, protein adsorption is highly sensitive to topological constraints imposed by CBN surface structure; in particular, adsorption capacity is thought to increase as the incident surface curvature decreases. In this work, we couple Molecular Dynamics (MD) simulations with fluorescence spectroscopy experiments to characterize this curvature dependence in detail for the model protein bovine serum albumin (BSA). By studying BSA adsorption onto carbon nanotubes of increasing radius (featuring descending local curvatures) and a flat graphene sheet, we confirm that adsorption capacity is indeed enhanced on flatter surfaces. Naïve fluorescence experiments featuring multi-walled carbon nanotubes (MWCNTs), however, conform to an opposing trend. To reconcile these observations, we conduct additional MD simulations with MWCNTs that match those prepared in experiments; such simulations indicate that increased mass to surface area ratios in multi-walled systems explain the observed discrepancies. In reduction, our work substantiates the inverse relationship between protein adsorption capacity and surface curvature and further demonstrates the need for subtle consideration in experimental and simulation design.
Similar content being viewed by others
Introduction
Since the discoveries of fullerene C60 in 19851, carbon nanotubes (CNTs) in 19912 and graphene in 20043, carbon-based nanomaterials (CBNs) have attracted considerable attention in various biomedical fields4,5 (including those related to gene delivery6, optical imaging7 and nanotherapeutics)8,9,10,11,12 because of their excellent mechanical, optical and electrical properties13,14,15. However, growing concerns over pathologies CBNs might effect on human patients have established the study of nanotoxicity as an important element of nanoscience and nanotechnology16,17,18,19. Notably, single-wall carbon nanotubes (SWCNTs) have been shown to disrupt the active sites of WW domains and compete with native ligands (proline rich motifs) of SH3 domains. Given the ubiquity and criticality of such proteins in signaling and regulatory pathways20,21,22, interactions between CBNs and WW and SH3 domains are particularly disconcerting. Fullerenes and metallofullerenols have also been shown to inhibit the functions of WW/SH3 domains17,23 and other proteins like HIV protease24. Graphene nanosheets possess the strongest observed capacities for disrupting protein structure among CBNs of various topologies25. Furthermore, graphene and graphene derivatives are known to cause extensive damage to cellular membranes, suggesting, in the face of diminished toxicity to eukaryotes, their excellent prospects for use as anti-bacterial agents26,27,28. Various strategies have been proposed to mitigate the cytotoxicity of CBNs to normal cells29,30 and to target CBN cytotoxicity toward tumor and bacteria cells31,32. Passivation of CBNs for in-vivo applications is commonly achieved through the coating and functionalization of CBN surfaces33,34,35. Many cellular targeting and delivery approaches exploit the adhesion of serum proteins29,30 to CBNs or make use of CBN aggregation corona that form in the presence of other proteins36.
Such interest in designing biocompatible nanoparticles for medical applications has prompted a preponderance of theoretical and experimental studies related to protein-CBN interactions31,37,38. Our previous work suggests that favorable hydrophobic and π-π stacking interactions facilitate the packing of proteins onto CBN surfaces21,22. Varying topological and chemical features like length39, curvature40,41, surface functionalization42 allow CBNs, in principle, to be tuned for specific applications; questions remain, however, concerning just how these properties alter protein adsorption capacity and kinetics. Similarly, it is interesting to consider the role protein structure assumes throughout the adsorption process43. CBN surface curvature is generally believed to deprecate adsorption capacity, but, heretofore, systematic studies related to this phenomenon have been sparse.
In this Article, we combine MD simulations with fluorescence spectroscopic measurements to study the adsorption of bovine serum albumin (BSA) onto CBNs with various surface curvatures. Our data derived from MD simulations of SWCNTs support the hypothesized inverse relationship between adsorption capacity and local curvature. However, we find that simple spectroscopic experiments on MWCNTs, when not renormalized for inherent differences in mass-to-surface area ratios, support an inverse trend. To validate this explanation for the observed discrepancy, we conduct additional simulations on several multi-walled CNTs (MWCNTs); we indeed find that increasing mass-to-surface area ratios in larger MWCNTs lead to aberrant reductions in adsorption capacities. Thus, under “corrected” or normalized conditions, we expect both simulation and experiment to confirm that protein adsorptive capacity is enhanced by decrease in surface curvature. The current study illustrates the necessity for designing complementary simulation and experimental protocols, an often non-trivial task in systems existing at the nanoscale.
Results
MD simulations reveal the expected adsorption capacity trend with CBN surface curvature
In order to investigate the relation between adsorption capacity and surface curvature of CBNs, two sets of five simulation systems were constructed (see Fig. 1 and Fig. S1), each consisting of a BSA protein molecule and a CBN segment featuring a given surface curvature ((15,15)-, (20,20)-, (25,25)-, (30,30)-SWCNTs and graphene). All systems were started at identical volumes to ensure consistent BSA and CBN concentrations and the initial minimum distance between the two molecules in each system was set at 1.0 nm. All-atom MD simulations started from each configuration were carried out for a minimum of 200 ns.
System setup of BSA(cyan) and 5 different CBNs(tan) in the first set of simulations: a (15,15)-SWCNT, a (20,20)-SWCNT, a (25,25)-SWCNT, a (30,30)-SWCNT and a graphene sheet. Systems are independent but juxtaposed for visualization purposes. At the start of each simulation, the BSA and CBN are separated by 1.0 nm.
Heavy atom contact numbers, contact surface areas and van der Waals (vdW) interaction energies within each BSA and CBN pair were computed for analysis (Fig. 2). Heavy atom contact numbers (Fig. 2A) indicate that protein adsorption steadily becomes more prominent as the surface curvature of CBNs decreases. After equilibration, average contact numbers corresponding to the graphene and largest-diameter CNT were nearly equal; protein contacts with the narrower CNTs, however, were reduced by a factor of ~2. Contact surface areas and vdW interaction energies exhibited a similar trend (Fig. 2B,C). Results from other simulation trajectories are also consistent (see Fig. S2). To further quantify the relationship between the adsorption capability of CBNs with its curvature, a diagram of heavy atom contact numbers vs curvature was plotted in Fig. 3. Here, the surface curvature was defined as usual:
The heavy atom contact number (A), contact surface area (B) and vdW interaction energy (C) between BSA and (15,15)-SWCNT(black), (20,20)-SWCNT(red), (25,25)-SWCNT(blue), (30,30)-SWCNT(magenta) and graphene (green). Collectively, these plots demonstrate that the BSA adsorption capacity increase (measured by more stable adsorption, higher contact numbers and higher contact surface areas), as the CBN curvature decreases.
![](http://media.springernature.com/lw43/springer-static/image/art%3A10.1038%2Fsrep10886/MediaObjects/41598_2015_Article_BFsrep10886_Equ1_HTML.gif)
where k represents the curvature and r represents the radius of the (n,m)-CNT. As shown in Fig. 3, a sigmoidal-like (monotonic but non-linear) dependence of protein adsorption on CBN’s curvature can be observed. Interestingly, the adsorption behavior can be categorized roughly into three curvature regimes (I, 0—0.5 nm−1; II, 0.5—0.75 nm−1; III, 0.75—1 nm−1). In regime I and III, the protein adsorption capability increases slowly with the decrease of the curvature, whereas in regime II, it increases sharply with the decrease of the curvature. These data validate our conjecture that the protein adsorption capacity CBNs should increase with decreasing surface curvature. Notably, the large jumps evident in these property traces correspond to sudden adsorption events seen in our simulations. To better illustrate this phenomenon, two such jumps are exemplified in Fig. S3 (see SI) for the (15,15)-SWCNT/BSA system. From 73 ns to 80 ns, surface contacts involving aliphatic residues Ala581 and Leu582 emerged (as highlighted by the dashed area in Fig. S3A); Fig. S3B shows that a new surface contact involving the aromatic residue Phe501 forms ~180 ns into the simulation. The latter interaction provides an example of π−π stacking between an aromatic side chain and the SWCNT surface; at −6 to −13.5 kcal/mol,44 such interactions are thought to be particularly important in adsorption processes.
To further explore the binding mechanism of BSA adsorbed onto the surface of CBNs, the final snapshots for all the five SWCNT systems were examined, with the contact regions highlighted. Meanwhile, all the key residues were identified if their contact probability with CBNs is larger than 0.6 and then further classified into five categories, aromatic, nonpolar, polar, acidic and basic (see Table. S1). As shown in Fig. S4, the exact contact region between BSA and CBNs of various curvatures can be quite different. However, due to the high hydrophobic nature of CBNs, the hydrophobic regions (including nonpolar and aromatic residues) of BSA are more likely to contact with CBNs, despite that the exact contacting residues can be different (Fig. S4 and Table S1).
To probe trade-offs between adsorption and protein-solvent energetics, we computed the vdW interaction energies corresponding to BSA-CBN and BSA-solvent contacts (Fig. 4). Based on these data, we observe that (i) the vdW energy between BSA and CBNs decreases along the adsorption process (i.e., favorable) and decreases more as the curvature of the CBN decreases and (ii) the vdW energy between BSA and its solvent increases slightly as adsorptive processes occur in simulation. In addition, we also computed the electrostatic interaction energy between BSA and the solvent (Fig. S5), which increases as the simulation time progresses. Clearly, the changes in both the vdW and electrostatic interactions between BSA and the solvent are positive (i.e., unfavorable) for the adsorption of BSA onto the CBNs. In general, it is not the total interaction energy, but the change in the interaction energy that matters. If the energy change during the adsorption process is negative, then this energy component is favorable which helps driving the adsorption process. As we can see from Fig. 4, there is a strong negative change in the vdW interaction between BSA and CNT, thus very favorable for the adsorption process. On the other hand, both the changes in the vdW (Fig. 4) and electrostatic (Fig. S5) interactions between BSA and water are positive and thus unfavorable (due to the removal of water from its interface with CNT once combined). Essentially, the strong and favorable vdW interaction between BSA and CNT drives the adsorption of BSA onto CNT, which partially offsets the net loss in the BSA-water (and CNT-water) interactions. Taken together, the driving force for BSA adsorption is the direct van der Waals (dispersion) interactions between BSA and CBNs, in addition to the hydrophobic interactions (water push both BSA and CBNs together).
The “validating” fluorescence spectroscopy experiment shows the opposite trend
In an attempt to validate our simulation results with experimental data, we prepared five CNT systems with different outer diameters (8–15, 10–20, 20–30, 30–50 and > 50 nm) in fixed concentration suspensions and incubated each system in the presence of excess BSA. To our surprise, the fluorescence data exhibited a trend in complete opposition to our simulation results (Fig. 5A), wherein adsorption capacity seems to decrease with decreasing curvature. Measured kinetic curves (Fig. 5B) also appear to support the opposing adsorption trend.
Contradiction between experiments and simulations resolved
To reconcile this apparent contradiction, one must make note of a subtle difference between our simulation and experimental protocols. In our simulation systems, the CBNs (SWCNTs, along with graphene) were constrained to have the same mass; in the experimental systems, however, MWCNTs suspensions were prepared at equal concentrations based on the total mass of suspended nanomaterial, due to the inherent difficulty in preparing single-walled CNTs with larger radii in experiment (also the precise size and exact number of walls are still impossible to determine even with today’s state-of-the-art techniques). As the number of layers in a MWCNT increases, its mass increases much more rapidly than its surface area. Accordingly, the adsorption area per unit mass decays as MWCNTs increase in size, explaining the spurious trend observed in our experiment.
To validate this reasoning, we initiated two respective simulation systems containing BSA and MWCNTs with different radii (Fig. 6). The number of carbon atoms and BSA concentrations are constant in each setup and the initial CBN-BSA distance was again set to 1 nm. Because of the imposed extensive constraint on the CBNs, the length of (20,20)-MWCNT (27.3 nm) is much longer than that of the (40,40)-MWCNT (8.2 nm), correspondingly the effective surface area of the former (233.2 nm2) is much larger than the latter (142.3 nm2) and the observed adsorption properties are perturbed accordingly. As illustrated by the heavy atom contact number as a function of the simulation time (Fig. 7), BSA molecules do initially adsorb more quickly onto the (40,40)-MWCNT than onto its more highly curved (20,20)-MWCNT counterpart. However, due to the much larger effective surface adsorption area present in the (20,20)-MWCNT, both such relative adsorbing rates and capacities were quickly reversed. After only about 1.9 ns, the contact number related to the (20,20)-MWCNT already exceeded that of the (40,40)-MWCNT and after 3.0 ns the adsorption rate of the longer, narrower tube outpaced that of the wider CNT. At simulation’s end, the adsorption capacity of the (20,20)-MWCNT is about twice that of the (40,40)-MWCNT system. Analysis of the contact surface areas and vdW interaction energies exhibited a similar trend as the heavy atom contact number (Fig. S6). Therefore, the results obtained from the simulations on MWCNTs are in excellent agreement with our experimental data.
It should be stressed though that for MWCNTs the effective surface area (the outer surface which could be coated by the proteins) is smaller than SWCNTs with the same mass, which is the quantity used in experiment. The mass to effective-surface area ratio for all the SWCNTs is essentially the same, thus the difference in adsorption capacity is solely due to the surface curvature. While for MWCNTs, the mass to effective-surface area ratio can differ due to the different layers of CNTs contained. Once normalized by this ratio (691.5 and 1147.3 dalton/nm2 for (20,20)-MWCNT and (40,40)-MWCNT respectively), the result will show a similar trend with respect to the surface curvature, i.e. the (20,20)-MWCNT will show a lower effective adsorption capacity (contact number ~7,150, averaged over the last 20 ns data, once normalized to the (40,40)-MWCNT value) than the (40,40)-MWCNT (7,180, averaged over the last 50 ns data, which serves as the base here, see Fig. 7), thus consistent with the above single wall results.
Given these supporting simulations, we can confidently argue that the adsorption capacity of proteins on the surface of CBNs increases as the surface curvature decreases. Our study also reinforces, however, the importance of ensuring that underlying simulation models are as consistent as possible with experimental conditions.
Conclusions
Several theoretical studies25,45 have shown that protein adsorption onto the surface of CBNs becomes more prominent as the local curvature of the CBNs decreases. Here, we sought to validate this notion using both simulation and experimental methodologies, and, in summary, we succeeded in doing so. But while our initial simulation-based data confirmed the aforementioned hypothesis, seemingly subtle differences in protocol led to drastic deviations between simulation-based and experimental observations that then required additional reconciliation. As the study of nanotoxicity advances in coming years, both simulation and experimental techniques will be of paramount importance; as demonstrated by the present work, however, their harmony must be carefully contrived.
Methods
Molecular Dynamics Simulations
All the CBNs coordinates (including (10,10), (15,15), (20,20), (25,25) and (30,30)-SWCNTs, graphene and (40,40) and (20,20)-MWCNTs) were generated using VMD46 (Visual Molecular Dynamics) with all carbon atoms assigned uncharged Lennard-Jones parameters of εcc = 0.36 kJ/mol and σcc = 3.4 Å37,47. (15,15), (20,20), (25,25) and (30,30)-SWCNT had lengths of 12.65 nm, 9.33 nm, 7.49 nm and 6.14 nm with the same carbon atoms number at 3120. The configuration of a SWCNT can be conceptually constructed by “rolling up” a graphene nanosheet into a seamless cylinder. The pattern the graphene is wrapped can be characterized by a pair of indices (n,m). The integers n and m stand for the number of unit vectors along two directions in the honeycomb crystal lattice of graphene. If m = 0, the CNT are called zigzag CNT and if n = m, they are called armchair CNT. Otherwise, they are called chiral nanotubes. In our study, all the SWCNTs and MWCNTs are the armchair nanotube. The graphene was set to 7.94 nm × 9.95 nm including 3114 carbon atoms (roughly same carbon atoms with CNTs). For all the simulation systems of SWCNTs and graphene, the concentrations of BSA and CBNs were identical. To examine the influence of initial orientation of BSA with respect to the surface of CBNs (SWCNTs and graphene) on the adsorption process and possible binding mechanism, two sets of simulations were carried out for all the five systems, with the protein orientation rotated by 180° (see Fig .1 and Fig. S1, respectively). The (40,40)-MWCNTs had a length of 8.2 nm and consisted of 4 nested layers: (40,40), (30,30), (20,20) and (10,10)-CNTs, specifically. The (20,20)-MWCNT had a length of 27.3 nm and it contained 2 nested layers (composed of (20,20) and (10,10)-CNTs). Both MWCNTs contained the same number of carbon atoms and were subjected to identical BSA concentrations. A crystal structure of BSA (PDB ID: 4F5S48) was used to initialize BSA configurations. All the CBNs/BSA complexes were solvated in water boxes, minimized and equilibrated before production runs in accordance with protocols used in our previous studies49,50,51,52,53. MD simulations were carried out on a Linux cluster using the software package GROMACS54 (version 4.6.4) with CHARMM 27 force field55. The temperature and pressure were set at constant to 300 K and 1 bar by using v-rescale thermostat56 and Parrinello-Rahman57 pressure coupling scheme, respectively. PME (Particle Mesh Ewald)58,59 was applied to treat long-range electrostatic interactions and the cut-off for handling the van der Waals interactions was set to 10 Å. The TIP3P water model60 was used in all simulations.
Fluorescence spectroscopy
MWCNTs (purity > 90 wt%) with outer diameters of 8-15, 10-20, 20-30, 30-50 and > 50 nm were bought from Chengdu Organic Chemical Company, Chinese Academy of Science. BSA was purchased from Solarbio science &technology (Beijing, China).
MWCNT suspensions (outer diameters of 8-15, 10-20, 20-30, 30-50 and > 50 nm) were prepared by dispersing in pure water and BSA solutions of the same concentration were prepared in standard phosphate buffer saline (PBS). Then, equal volumes and concentrations (100μg/ml) of MWCNT suspensions and BSA solutions were mixed and shaken at 37 ℃ prior to centrifugation at 14,800 × g for 10 min. After discarding the sediments, the contents of free protein in supernatant were probed by fluorescence spectroscopy. Using the protein standard curve (A = 752.56*C + 20.902, R2 = 0.99968, where “A” and “C” represented absorbency and concentration of BSA, respectively), we calculated the percent of protein adsorption on MWCNTs by subtracting the protein content of the supernatant from the total quantity of protein in the system.
Additional Information
How to cite this article: Gu, Z. et al. Surface Curvature Relation to Protein Adsorption for Carbon-based Nanomaterials. Sci. Rep. 5, 10886; doi: 10.1038/srep10886 (2015).
References
Kroto, H. W., Heath, J. R., Obrien, S. C., Curl, R. F. & Smalley, R. E. C60: Buckminsterfullerene. Nature 318, 162–163 (1985).
Iijima, S. Helical microtubules of graphitic carbon. Nature 354, 56–58 (1991).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Lee, J. S., Joung, H. A., Kim, M. G. & Park, C. B. Graphene-based chemiluminescence resonance energy transfer for homogeneous immunoassay. ACS Nano 6, 2978–2983 (2012).
Cha, C. Y., Shin, S. R., Annabi, N., Dokmeci, M. R. & Khademhosseini, A. Carbon-based nanomaterials: multifunctional materials for biomedical engineering. ACS Nano 7, 2891–2897 (2013).
Bao, H. Q. et al. Chitosan-functionalized graphene oxide as a nanocarrier for drug and gene delivery. Small 7, 1569–1578 (2011).
Li, B. L. et al. Direct optical imaging of graphene in vitro by nonlinear femtosecond laser spectral reshaping. Nano Lett. 12, 5936–5940 (2012).
Li, M., Yang, X. J., Ren, J. S., Qu, K. G. & Qu, X. G. Using graphene oxide high near-infrared absorbance for photothermal treatment of Alzheimer’.s disease. Adv. Mater. 24, 1722–1728 (2012).
Yang, K. et al. The influence of surface chemistry and size of nanoscale graphene oxide on photothermal therapy of cancer using ultra-low laser power. Biomaterials 33, 2206–2214 (2012).
Wang, X., Yang, L. L., Chen, Z. & Shin, D. M. Application of nanotechnology in cancer therapy and imaging. CA-Cancer J. Clin. 58, 97–110 (2008).
Shin, D. M. Application of nanotechnology in cancer therapy and imaging. Drug Metab. Rev. 42, 13–13 (2010).
Yang, Z. X., Kang, S. G. & Zhou, R. H. Nanomedicine: de novo design of nanodrugs. Nanoscale 6, 663–677 (2014).
Feng, L. Z. & Liu, Z. A. Graphene in biomedicine: opportunities and challenges. Nanomedicine 6, 317–324 (2011).
Sanchez, V. C., Jachak, A., Hurt, R. H. & Kane, A. B. Biological interactions of graphene-family nanomaterials: an interdisciplinary review. Chem. Res. Toxicol. 25, 15–34 (2012).
Geim, A. K. Graphene: status and prospects. Science 324, 1530–1534 (2009).
Zuo, G. H., Kang, S. G., Xiu, P., Zhao, Y. L. & Zhou, R. H. Interactions between proteins and carbon-based nanoparticles: exploring the origin of nanotoxicity at the molecular level. Small 9, 1546–1556 (2013).
Kang, S. G., Huynh, T. & Zhou, R. H. Non-destructive inhibition of metallofullerenol Gd@C82(OH)22 on WW domain: implication on signal transduction pathway. Sci Rep 2, 7 (2012).
Zhang, Y. B. et al. Toxicity and efficacy of carbon nanotubes and graphene: the utility of carbon-based nanoparticles in nanomedicine. Drug Metab. Rev. 46, 232–246 (2014).
Lanone, S., Andujar, P., Kermanizadeh, A. & Boczkowski, J. Determinants of carbon nanotube toxicity. Adv. Drug Deliv. Rev. 65, 2063–2069 (2013).
Zuo, G. H., Huang, Q., Wei, G. H., Zhou, R. H. & Fang, H. P. Plugging into proteins: poisoning protein function by a hydrophobic nanoparticle. ACS Nano 4, 7508–7514 (2010).
Zuo, G. H., Gu, W., Fang, H. P. & Zhou, R. H. Carbon nanotube wins the competitive binding over proline-rich motif ligand on SH3 domain. J. Phys. Chem. C 115, 12322–12328 (2011).
Zuo, G. H., Xiu, P., Zhou, X., Zhou, R. H. & Fang, H. P. Conformational changes of the protein domains upon binding with carbon nanotubes studied by molecular dynamics simulations. Curr. Phys. Chem. 2, 12–22 (2012).
Kang, S. G., Huynh, T. & Zhou, R. H. Metallofullerenol Gd@C82(OH)22 distracts the proline-rich-motif from putative binding on the SH3 domain. Nanoscale 5, 2703–2712 (2013).
Friedman, S. H. et al. Inhibition of the HIV-1 protease by fullerene derivatives: model building studies and experimental verification. J. Am. Chem. Soc. 115, 6506–6509 (1993).
Zuo, G. H., Zhou, X., Huang, Q., Fang, H. P. & Zhou, R. H. Adsorption of villin headpiece onto graphene, carbon nanotube and C60: effect of contacting surface curvatures on binding affinity. J. Phys. Chem. C 115, 23323–23328 (2011).
Tu, Y. S. et al. Destructive extraction of phospholipids from Escherichia coli membranes by graphene nanosheets. Nat. Nanotechnol. 8, 594–601 (2013).
Hu, W. B. et al. Graphene-Based Antibacterial Paper. ACS Nano 4, 4317–4323 (2010).
Akhavan, O. & Ghaderi, E. Toxicity of graphene and graphene oxide nanowalls against bacteria. ACS Nano 4, 5731–5736 (2010).
Ge, C. C. et al. Binding of blood proteins to carbon nanotubes reduces cytotoxicity. Proc. Natl. Acad. Sci. U. S. A. 108, 16968–16973 (2011).
De Paoli, S. H. et al. The effect of protein corona composition on the interaction of carbon nanotubes with human blood platelets. Biomaterials 35, 6182–6194 (2014).
Kang, S. G. et al. Molecular mechanism of pancreatic tumor metastasis inhibition by Gd@C-82(OH)(22) and its implication for de novo design of nanomedicine. Proc. Natl. Acad. Sci. U. S. A. 109, 15431–15436 (2012).
Tu, Y. S. et al. Destructive extraction of phospholipids from Escherichia coli membranes by graphene nanosheets. Nat Nanotechnol 8, 594–601 (2013).
Zhao, W., Song, C. H. & Pehrsson, P. E. Water-soluble and optically pH-sensitive single-walled carbon nanotubes from surface modification. J. Am. Chem. Soc. 124, 12418–12419 (2002).
Sitko, R., Zawisza, B. & Malicka, E. Modification of carbon nanotubes for preconcentration, separation and determination of trace-metal ions. Trac-Trends Anal. Chem. 37, 22–31 (2012).
Du, J. F. et al. The interaction of serum proteins with carbon nanotubes depend on the physicochemical properties of nanotubes. J. Nanosci. Nanotechnol. 11, 10102–10110 (2011).
Cai, X. N. et al. Characterization of carbon nanotube protein corona by using quantitative proteomics. Nanomed.-Nanotechnol. Biol. Med. 9, 583–593 (2013).
Shi, B. Y., Zuo, G. H., Xiu, P. & Zhou, R. H. Binding preference of carbon nanotube over proline-rich motif ligand on SH3-domain: a comparison with different force fields. J. Phys. Chem. B 117, 3541–3547 (2013).
Mu, Q. X. et al. Protein binding by functionalized multiwalled carbon nanotubes is governed by the surface chemistry of both parties and the nanotube diameter. J. Phys. Chem. C 112, 3300–3307 (2008).
Az’hari, S. & Ghayeb, Y. Effect of chirality, length and diameter of carbon nanotubes on the adsorption of 20 amino acids: a molecular dynamics simulation study. Mol. Simul. 40, 392–398 (2014).
Balamurugan, K., Singam, E. R. A. & Subramanian, V. Effect of curvature on the alpha-helix breaking tendency of carbon based nanomaterials. J. Phys. Chem. C 115, 8886–8892 (2011).
Raffaini, G. & Ganazzoli, F. Surface topography effects in protein adsorption on nanostructured carbon allotropes. Langmuir 29, 4883–4893 (2013).
Baweja, L., Balamurugan, K., Subramanian, V. & Dhawan, A. Hydration patterns of graphene-based nanomaterials (GBNMs) play a major role in the stability of a helical protein: a molecular dynamics simulation study. Langmuir 29, 14230–14238 (2013).
Balamurugan, K. & Subramanian, V. Length-dependent stability of alpha-helical peptide upon adsorption to single-walled carbon nanotube. Biopolymers 99, 357–369 (2013).
Yang, Z. X., Wang, Z. G., Tian, X. L., Xiu, P. & Zhou, R. H. Amino acid analogues bind to carbon nanotube via pi-pi interactions: comparison of molecular mechanical and quantum mechanical calculations. J. Chem. Phys. 136, 025103 (2012).
Mesaric, T. et al. Effects of surface curvature and surface characteristics of carbon-based nanomaterials on the adsorption and activity of acetylcholinesterase. Carbon 62, 222–232 (2013).
Humphrey, W., Dalke, A. & Schulten, K. VMD: Visual molecular dynamics. J. Mol. Graph. 14, 33–38 (1996).
Hummer, G., Rasaiah, J. C. & Noworyta, J. P. Water conduction through the hydrophobic channel of a carbon nanotube. Nature 414, 188–190 (2001).
Bujacz, A. Structures of bovine, equine and leporine serum albumin. Acta Crystallogr. Sect. D-Biol. Crystallogr. 68, 1278–1289 (2012).
Eleftheriou, M., Germain, R. S., Royyuru, A. K. & Zhou, R. Thermal denaturing of mutant lysozyme with both the OPLSAA and the CHARMM force fields. J. Am. Chem. Soc. 128, 13388–13395 (2006).
Liu, P., Huang, X., Zhou, R. & Berne, B. J. Observation of a dewetting transition in the collapse of the melittin tetramer. Nature 437, 159–162 (2005).
Zhou, R. H. Trp-cage: folding free energy landscape in explicit water. Proc. Natl. Acad. Sci. U. S. A. 100, 13280–13285 (2003).
Zhou, R. H., Das, P. & Royyuru, A. K. Single mutation induced H3N2 hemagglutinin antibody neutralization: a free energy perturbation study. J. Phys. Chem. B 112, 15813–15820 (2008).
Zhou, R. H., Huang, X. H., Margulis, C. J. & Berne, B. J. Hydrophobic collapse in multidomain protein folding. Science 305, 1605–1609 (2004).
Lindahl, E., Hess, B. & van der Spoel, D. GROMACS 3.0: a package for molecular simulation and trajectory analysis. J. Mol. Model. 7, 306–317 (2001).
MacKerell, A. D. et al. All-atom empirical potential for molecular modeling and dynamics studies of proteins. J. Phys. Chem. B 102, 3586–3616 (1998).
Bussi, G., Donadio, D. & Parrinello, M. Canonical sampling through velocity rescaling. J. Chem. Phys. 126, 7 (2007).
Parrinello, M. & Rahman, A. Polymorphic transitions in single crystals: A new molecular dynamics. J. Appl. Phys. 52, 7182–7190 (1981).
Darden, T., York, D. & Pedersen, L. Particle mesh Ewald: An N•log(N) method for Ewald sums in large systems. J. Chem. Phys. 98, 10089–10092 (1993).
Essmann, U. et al. A smooth particle mesh Ewald method. J. Chem. Phys. 103, 8577–8593 (1995).
Jorgensen, W. L., Chandrasekhar, J., Madura, J. D., Impey, R. W. & Klein, M. L. Comparison of simple potential functions for simulating liquid water. J. Chem. Phys. 79, 926–935 (1983).
Acknowledgements
We thank Zhifang Chai, Yuliang Zhao, Guangxin Duan, Tien Huynh and Bo Zhou for useful discussions and insightful comments. This work is partially supported by the National Natural Science Foundation of China (grant nos 11374221, 21320102003 and 11404233). R.Z. acknowledges the financial support from the IBM BlueGene Science Program. A Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD) and Jiangsu Provincial Key Laboratory of Radiation Medicine and Protection.
Author information
Authors and Affiliations
Contributions
R.Z. conceived and designed the research. Z.G., R.Z., J.K.W., D.R.B. and Z.Y. co-wrote the manuscript. Z.G. and Z.Y. carried out the molecular dynamics simulations. Y.C. and C.G. performed the fluorecence spectroscopy experiments. Z.G., Y.Z., J.K.W., D.R.B., Y.C., C.G. and R.Z. analyzed the data. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Gu, Z., Yang, Z., Chong, Y. et al. Surface Curvature Relation to Protein Adsorption for Carbon-based Nanomaterials. Sci Rep 5, 10886 (2015). https://doi.org/10.1038/srep10886
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep10886
- Springer Nature Limited
This article is cited by
-
Industrial applications of immobilized nano-biocatalysts
Bioprocess and Biosystems Engineering (2022)
-
Toxicology data of graphene-family nanomaterials: an update
Archives of Toxicology (2020)
-
Evaluation of the elastic Young’s modulus and cytotoxicity variations in fibroblasts exposed to carbon-based nanomaterials
Journal of Nanobiotechnology (2019)
-
An investigation into non-covalent functionalization of a single-walled carbon nanotube and a graphene sheet with protein G:A combined experimental and molecular dynamics study
Scientific Reports (2019)
-
Dynamic changes of protein corona compositions on the surface of zinc oxide nanoparticle in cell culture media
Frontiers of Chemical Science and Engineering (2019)