Abstract
Upconversion nanoparticles (UCNPs) have been extensively explored for photodynamic therapy (PDT) and imaging due to their representative large anti-Stokes shifts, deep penetration into biological tissues, narrow emission bands and high spatial-temporal resolution. Conventional UCNP-based PDT system, however, utilizes exitation at 980 nm, at which water has significant absorption, leading to a huge concern that the cell killing effect is from the irradiation due to overheating effect. Here we report an efficient nanoplatform using 808-nm excited NaYbF4:Nd@NaGdF4:Yb/Er@NaGdF4 core−shell−shell nanoparticles loaded with Chlorin e6 and folic acid for simultaneous imaging and PDT. At this wavelength, the absorption of water is minimized. High energy transfer efficiency is achieved to generate cytotoxic singlet oxygen. Our nanoplatform effectively kills cancer cells in concentration-, time- and receptor-dependent manners. More importantly, our nanoplatform is still able to efficiently generate singlet oxygen beneath 15-mm thickness of muscle tissue but 980 nm excitation cannot, showing that a higher penetration depth is achieved by our system. These results imply that our nanoplatform has the ability to effectively kill intrinsic tumor or the center of large tumors through PDT, which significantly improves the anticancer efficacy using UCNP-based PDT system and broadens the types of tumors that could be cured.
Similar content being viewed by others
Introduction
Photodynamic therapy (PDT) has a long history to treat cancer patients and has now been widely used in the clinic against various types of cancer1,2. PDT utilizes tissue oxygen and photosensitizers that are excited by visible light to generate highly cytotoxic singlet oxygen (1O2) and other reactive oxygen species (ROS), which damage cancer cells and lead to cell death2. Compared with conventional chemotherapy, PDT is able to specifically eradicate tumors by controlling the location of light exposure3. The activation wavelength of most clinically used photosensitizers, however, is usually in a spectrum window of around 630-700 nm1, in which tissue penetration depth is limited. Thus, PDT has limited therapeutic effect against internal or large tumors4. In addition, the biodistribution of photosensitizers is not controlled, resulting in toxicity issues3,5.
One way to avoid the aforementioned issues is to shift the excitation wavelength to near infrared (NIR) area. In this region, biological tissues have the minimal light absorption and increased penetration depth could be achieved in the tumor site4. Upconversion nanoparticles (UCNPs) excited by NIR light greatly meet the demands6,7,8. Lanthanide-doped UCNPs have shown exciting biomedical applications including bioimaging, sensing and drug delivery9,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24,25,26,27. In the upconversion process, two or more low-energy photons from NIR light are absorbed to produce higher energy emission in the visible region, which could be further applied in a PDT process28,29,30,31,32,33. The utilization of NIR light rather than visible light as the excitation source ensures low photo-damage, low-autofluorescence background and deep penetration into biological tissue, which, in combination with the long lifetime of the lanthanide-doped UCNPs, leads to high spatial-temporal resolution34. Conventional UCNPs use Yb3+ as the light harvesting ion and can respond to a narrow NIR band at around 980 nm35,36. Nanoplatforms utilizing such UCNPs and different photosensitizers for PDT of cancer have been extensively explored37,38,39. The absorption of water at 980 nm, however, is significant40,41, leading to an overheating issue and relatively low penetration depth of tissue. This drawback has significantly limited the biomedical applications of conventional UCNPs for imaging and photodynamic therapy.
Efforts have been made to adjust the excitation window of UCNPs. Different metal ions and organic dyes have been incorporated into the system as sensitizers to upconvert NIR light in the medical spectral window (i.e. ~700-900 nm)36. At around 800 nm, water has minimized absorption and there is limited overheating effect. Very recently, Nd3+-sensitized upconversion process utilizing a new excitation wavelength at around 800 nm has been reported35,36,40,41,42,43. In the core-shell nanoparticles, the successive Nd3+→Yb3+→ activator energy transfer enables the excitation at a shorter wavelength of 808 nm41. Another report showed that Nd3+-sensitized core-shell nanoparticles containing a series of lanthanide activators have remarkably enhanced upconversion luminescence, which provide a more sensitive biomarker for bioimaging without autofluorescence35. Most of the reports on Nd3+-sensitized UCNPs using 808 nm excitation focused on the fabrication of nanoparticles and the biomedical application of UCNPs excited by 808 nm, especially on PDT, is still a nascent area.
Herein we fabricated a nanoplatform based on NaYbF4:Nd@NaGdF4:Yb/Er@NaGdF4 core−shell−shell nanoparticles that convert NIR light for simultaneous fluorescence imaging and photodynamic therapy against cancer. This highly efficient system utilizes an energy transfer from 808 nm NIR light to two upconversion luminescence bands at around 550 and 660 nm for simultaneous imaging and therapy (Fig. 1). Chlorin e6 (Ce6), a commonly used and highly efficient photosensitizer, was covalently conjugated with surface-functionalized core-shell-shell nanoparticles at a high efficiency of around 4,000 molecules per nanoparticle44. The energy transfer from nanoparticles to photosensitizers was confirmed by upconversion luminescence spectra, luminescence decay lifetimes and their ability to generate singlet oxygen. The biomedical applications of our nanoplatform were further illustrated by in vitro fluorescence imaging using different cancer cells and by its killing cancer cells in a very effective way upon 808 nm irradiation for just 5 min. To the best of our knowledge, the present study is the first to show the biomedical applications of a nanoplatform utilizing NaYbF4:Nd@NaGdF4:Yb/Er@NaGdF4 core−shell−shell nanoparticles that convert NIR light at 808 nm for its biocompatibility, imaging and PDT ability. Our study paves the way for the further development of such nanoparticle-based theranostic agents with high energy transfer efficiency and minimized overheating effects.
Results
In the clinical PDT, tumor site will be irradiated by light for a great amount of time. A prerequisite of an ideal nanoplatform upconverting NIR light into visible light for PDT is that the normal tissues shielding the tumor site along the irradiation pathway will not be damaged by the light source. We therefore tested the viability of human cells upon irradiation by 808 nm NIR (1 W/cm2). KB, a folate receptor (FR)-expressing human mouth epidermal carcinoma cell line and A549, a FR-negative human non-small cell lung cancer cell line, were irradiated for up to 30 min and further incubated for 48 h before cell viability measurements. Irradiation at 976 nm (1 W/cm2) was used as a control (Fig. 2). Cell viability upon 808 nm laser irradiation did not change significantly but it greatly reduced upon 976 nm laser irradiation. For example, after 30 min irradiation, 96.1% of KB cells remained confluent when subjected to an 808 nm laser but the cell viability dramatically reduced to 15.0% when a 976 nm laser was used. The identical effect was observed in A549 cells. This result indicates that the 808 nm laser irradiation itself does not affect the cell viability for biomedical studies and therefore does not contribute to the cell killing effect from a nanoplatform upconverting 808 nm NIR for PDT. The effect from a 976 nm laser itself on the cell viability, however, especially when the irradiation is longer than 10 min, is a huge concern. One of the best explanations for this phenomenon is the overheating effect from a 976 nm laser, which has been observed previously35,40,41. We also measured the viability of A549 and KB cells upon irradiation at 808 nm at different power densities ranging from 0 to 6 W/cm2 and at different time points at 6 W/cm2 (see Supplementary Fig. S1 online). The results clearly show that the irradiation at 808 nm has negligible effect on the cell growth of both A549 and KB cells.
We next constructed a biocompatible and tumor-targeting nanoplatform converting 808 nm NIR light to singlet oxygen for PDT. A NaYbF4:Nd@NaGdF4:Yb/Er@NaGdF4 core−shell−shell nanostructure was synthesized to carry out the photon upconversion36. In comparison with Nd3+-sensitized upconversion nanoparticles developed by the groups of Yan and Liu35,41, our nanostructure accommodates a higher content of Yb3+, which promotes the red emission band of Er3+ to ensure efficient energy transfer to Ce6 displaying an absorption maximum at ~660 nm. It is noted that the nanostructure also upconverts 976 nm NIR light due to the NaGdF4:Yb/Er inner shell layer (Fig. 3a), thereby providing a continent platform for assessing the effect of irradiation wavelength on the PDT.
a) Photoluminescent spectra of UCNPs under 808 nm and 976 nm excitation (6 W/cm2). b) TEM images of OA-UCNPs (left) and NH2-UCNPs (right). c) Photoluminescent spectra of OA-UCNPs and NH2-UCNPs under 808 nm laser irradiation (6 W/cm2). d) FT-IR spectra of OA-UCNPs, NH2-UCNPs, Ce6-UCNPs and PEG-Ce6-UCNPs.
The nanoparticles were functionalized with photosensitizers and cancer-targeting moieties. Amino-functionalized UCNPs (NH2-UCNPs) capped with 2-aminoethyl dihydrogen phosphate (AEP) were fabricated by a phase transfer process from hydrophobic oleic acid-UCNPs (OA-UCNPs). As confirmed by TEM, NH2-UCNPs showed the same morphology and high monodispersity compared with OA-UCNPs (Fig. 3b). The upconversion luminescence spectrum of NH2-UCNPs remained the same as that of OA-UCNPs (Fig. 3c), showing that the surface modification with amino groups hardly alters the optical properties of the nanoparticles. Two emission bands at 520-540 nm and 540-560 nm in the green spectral region are attributed to Er transitions from 2H11/2 to 4I15/2 and 4S3/2 to 4I15/2, respectively and the emission band in the red spectral region at 640-680 nm is due to the Er transition from 4F9/2 to 4I15/2 (Fig. 3c). FT-IR analysis showed that the peaks belonging to C-H stretching in oleic acid at 2920 and 2850 cm−1 in OA-UCNPs disappeared after phase transfer (Fig. 3d). The peaks at 1633 and 1383 cm−1 in NH2-UCNPs were from N-H bending and C-N stretching vibration, respectively, confirming the successful surface modification with amino groups. Different amount of Ce6 was covalently loaded onto NH2-UCNPs via a carbodiimide cross-linking reaction between the amino groups on UCNPs and the carboxylate groups of Ce645. FT-IR analysis of the Ce6-loaded UCNPs showed that the peak at 1637 cm−1 was associated with the C=O stretching vibration from the amide group and the 1736 cm−1 peak was from the unreacted carboxylate groups in Ce6 since the molecule contains three carboxylate groups (Fig. 3d). Finally, the nanoparticles were capped with PEG and folic acid (FA)-PEG to obtain FA-PEG-Ce6-UCNPs (Scheme 1). The functionalization of UCNPs with Ce6, PEG and FA was further confirmed by FT-IR and UV-Vis spectroscopy (Fig. 3d, Supplementary Figs. S2 and S3). It is estimated that 1,000 FA molecules were conjugated on each nanoparticle46.
The energy transfer process from the nanoparticles to the photosensitizers (Ce6) was first characterized by photoluminescence spectroscopy. We measured the UV-vis absorbance of Ce6 and confirmed that the absorption peak matches well with the emission peak of NH2-UCNPs at around 660 nm (Fig. 4a). Steady-state upconversion luminescence measurements showed that increasing amount of loaded Ce6 resulted in decreasing emission at around 660 nm but not at around 550 nm from Ce6-loaded nanoparticles, indicating the selective energy transfer to Ce6 (Fig. 4b). The Förster resonance energy transfer (FRET) efficiency was determined to be over 70% according to the emission intensity of UCNPs at 660 nm with and without Ce6 modification31. This selective energy transfer can be visualized by NIR excitation of the NH2-UCNPs and the Ce6-loaded UCNPs. A clear color change from the yellow color of the NH2-UCNPs to the green color of the FA-PEG-Ce6-UCNPs upon 808 nm excitation was recorded by a regular digital camera (Fig. 4c). The energy transfer process was further studied by measuring the temporal behavior of upconversion luminescence. The emission decay curves of the NH2-UCNPs and the FA-PEG-Ce6-UCNPs at 550 and 660 nm are shown in Fig. 4d. In the presence of Ce6, the average decay time at 550 nm slightly decreased from 84.16 μs to 64.03 μs, partly attributing to the weak absorption of Ce6 at 550 nm (Fig. 4a). Notably, the decay time at 660 nm significantly decreased from 218.92 μs to 63.61 μs. This effect was attributed to the strong absorption of Ce6 at around 660 nm, confirming the selective and highly efficient energy transfer from the UCNPs to the photosensitizers.
a) Photoluminescent spectrum of NH2-UCNPs under 808 nm laser (6 W/cm2) irradiation (black) and UV-Vis spectrum of Chlorin e6 (red). b) Normalized photoluminescent spectra (by the emission peak at 550 nm) of PEG-Ce6-UCNPs with different loading amount under 808 nm laser irradiation. c) Photos of NH2-UCNPs and FA-PEG-Ce6-UCNPs under 808 nm laser (6 W/cm2) irradiation. d) Luminescence decay curves of the emission at 550 nm and 660 nm of NH2-UCNPs and FA-PEG-Ce6-UCNPs excited by an 808 nm flash laser.
The ability of PEG-Ce6-UCNPs to generate cytotoxic 1O2 was assessed using one of the most well-known chemical probes, 1,3-diphenylisobenzofuran (DPBF)28. DPBF reacts with 1O2 rapidly and specifically with high sensitivity and is inert with the ground state (triplet) molecular oxygen nor with the superoxide anion. o-Dibenzoylbenzene was formed through a [4 + 2] cycloaddition of 1O2 after oxidation, inducing the bleaching of DPBF, which can be measured spectroscopically47. Under 808 nm laser irradiation at a power density of 3 W/cm2, UCNPs without Ce6 loading were unable to induce the bleaching of DPBF, indicating that UCNPs themselves cannot generate 1O2 under an 808 nm laser. Notably, UCNPs loaded with various amounts of Ce6 induced significant DPBF bleaching, especially at a higher loading amount, confirming the efficient generation of 1O2 by our UCNP-based nanoplatform (Fig. 5a). Without NIR laser irradiation, the bleaching of DPBF in the presence of different Ce6 loaded samples was negligible (Fig. 5b). Since 10% (w/w) of Ce6 loading achieved the highest 1O2 generation ability, we used this sample for the following biological tests.
a) Singlet oxygen generation ability under 808 nm laser irradiation (3 W/cm2) and b) without 808 nm laser irradiation by DPBF assay with different Ce6 loading amount. c) Scheme of the singlet oxygen test in the presence of pork muscle tissue placed between 808 nm or 976 nm laser (6 W/cm2) and the UCNPs/DPBF solution. d) Singlet oxygen generation in the presence of different thickness of pork muscle tissue under 808 nm or 976 nm laser (6 W/cm2). ns, not significant; *, p < 0.05 ; **, p < 0.01.
A deeper tissue penetration depth is pivotal for broader applications of PDT. To compare the singlet oxygen generation ability of our nanoplatform beneath different depths of tissue, pork muscle tissues of varying thickness were located between the NIR power source and the PEG-Ce6-UCNPs samples and the singlet oxygen generation upon 5 min irradiation at 808 nm or 976 nm with the same intensity was measured using DPBF assay (Fig. 5c). The decrease of absorbance at 418 nm in the presence of pork muscle tissue was normalized to that without pork muscle tissue for 808 nm and 976 nm irradiation, respectively (Fig. 5d). Singlet oxygen generation ability of the nanoparticle system decreased upon different thickness of pork under both 808 nm and 976 nm excitation wavelengths but the ability decreased more quickly for 976 nm. For instance, when a pork muscle tissue of 8 mm thickness was applied, the generated amount of singlet oxygen decreased to 17.2% and 3.6% of the corresponding controls for 808 nm and 976 nm excitation, respectively. For 15 mm thickness, the singlet oxygen generation remains at 7.6% for 808 nm excitation but there was no detectable singlet oxygen generation for 976 nm excitation. In another word, in the potential clinical application, when our nanoplatform is under 15 mm thickness of the patient tissue and excited by a NIR light source, 808 nm excitation is still able to generate singlet oxygen, although the amount will decrease, but 976 nm excitation cannot. Therefore, 808 nm excitation has deeper tissue penetration depth than 976 nm excitation to generate singlet oxygen using our nanoplatform. Together with our results from the cell viability test using different NIR light sources (Fig. 2), our nanoplatform is able to be effective even deep in the tissue but will be safe using 808 nm excitation. Therefore, compared with the system using excitation at 976 nm, our system is more applicable for an efficient PDT.
To ensure the energy transfer process within the cells, Ce6 should be stably conjugated on the surface of the nanoparticles and should not release quickly from the complex. We therefore measured the release profile of Ce6 in UCNPs loaded with the photosensitizers. The release of free Ce6 was monitored by dialysis of FA-PEG-Ce6-UCNPs in PBS of pH 7.4 and pH 6.0. The result is shown in Supplementary Figure S4. At pH 7.4 after 2 h, 95.3% of Ce6 still remained in the nanoparticles and the number was 90.3% after 4 h, indicating that most of the photosensitizers stayed in the nanoparticles. The identical stability was observed at pH 6.0, which is the pH of early endosome48. Other reports have supported the notion that most of the nanoparticles have entered cells within this time frame30,46. Therefore, our nanoconstruct is stable and will still have high energy transfer efficiency after their entrance into cells.
The bioimaging properties of FA-PEG-Ce6-UCNPs are shown in Fig. 6a. KB, a folate receptor (FR)-expressing human mouth epidermal carcinoma cell line and A549, a FR-negative human non-small cell lung cancer cell line, were utilized. Cells were treated with 100 μg/mL nanoparticles and washed three times before confocal imaging. Upconversion luminescence of 500-700 nm channel was monitored. Bright field images of both KB and A549 cells treated with nanoparticles showed that the cells maintained normal morphology, indicating the great biocompatibility of the nanoparticles. The nanoparticles were able to enter FR-positive KB cells likely through FR-mediated endocytosis46 and the nanoparticles located in the cytoplasm of KB cells. Conversely, in FR-negative A549 cells, few nanoparticles were able to enter cells. To further confirm the specificity of FR-mediated targeting ability, the FR receptor of KB cells was blocked by excessive free FA, assigned as KB (FR-) cells, before incubation with FA-PEG-Ce6-UCNPs. Significantly weak upconversion luminescence signals were observed from this blocked cells compared with KB (FR+) cells (Fig. 6a). These data indicated the selectivity of FA-PEG-Ce6-UCNPs against FR-positive human cancer cells and the capability of our nanoplatform in bioimaging and diagnosis.
a) Upconversion luminescence imaging (λem = 500-700 nm) of KB (FR+), KB (FR−) and A549 cells incubated with 100 μg/mL nanoparticles for 4 h at 37 °C. Overlay of luminescence image and bright field image were also shown. b) Cell viability of KB cells treated with 200 μg/mL FA-PEG-Ce6-UCNPs under 808 nm laser irradiation (6 W/cm2) for different amount of time. Cell viability of c) KB cells and d) A549 cells treated by different concentration of FA-PEG-Ce6-UCNPs under 5 min of 808 nm laser irradiation at 6 W/cm2.
NIR-induced in vitro photodynamic therapy of cancer cells using our nanoplatform was tested. KB cells were incubated with 200 μg/mL Ce6-loaded nanoparticles before the cells were exposed to 808 nm NIR light at a density of 6 W/cm2 for 1, 2, 5 and 10 min. Cell viability was determined using a standard 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay. The result is shown in Fig. 6b. When the cells were exposed for 2 min, FA-PEG-Ce6-UCNPs were able to effectively kill cancer cells and 43.2% of the cells remained viable. The cell killing effect was more dramatic when the cells were exposed for a longer time. For example, cell viability reduced significantly to 1.6% and 8.3% under 5 min and 10 min NIR light exposure, respectively, confirming that the nanoplatform was able to kill FR-positive human cancer cells with a very high efficiency. Concentration-dependent cell killing effect was also evaluated. Without exposure to NIR light, viability of KB cells remained above 95% under all the concentrations tested, indicating the dark toxicity of our nanoplatform is negligible, which is the key for its biomedical applications in vivo. When the cells were exposed to NIR light for 5 min, the nanoplatform killed KB cells in a concentration-dependent manner (Fig. 6c). For instance, when cells were treated with 100 μg/mL FA-PEG-Ce6-UCNPs, the cell viabilities without laser irradiation and with laser irradiation were 97.2% and 4.5%, respectively, further proving the photodynamic effect of FA-PEG-Ce6-UCNPs. At higher nanoparticle concentrations, KB cells were also effectively killed by the nanoparticles upon irradiation. Conversely, FA-PEG-Ce6-UCNPs were not able to effectively kill A549 cells at 100 μg/mL under the same irradiation condition (Fig. 6d). This result is in agreement with our upconversion luminescence imaging results that under the same concentration the functionalized nanoparticles were hardly able to enter into A549 cells. Notably, at higher concentrations, FA-PEG-Ce6-UCNPs were still able to effectively kill A549 cells upon laser irradiation. This effect was likely from the non-receptor-mediated cellular uptake under high nanoparticle concentrations46,49.
Conclusions
In conclusion, we have successfully developed a novel nanoplatform based on NaYbF4:Nd@NaGdF4:Yb/Er@NaGdF4 core−shell−shell nanoparticles excited by 808 nm NIR light to generate 1O2 via efficient energy transfer from the nanoparticles to photosensitizers. Ce6 was covalently conjugated with surface-functionalized nanoparticles and a high loading efficiency was realized. The energy transfer process was confirmed by upconversion luminescence and luminescence decay. The FA-functionalized nanoparticles were able to efficiently and selectively enter FR-positive human cancer cells. Upon 808 nm irradiation, the Ce6-loaded nanoparticles effectively killed cancer cells in time- and nanoparticle concentration-dependent manners. More importantly, irradiation of 976 nm laser significantly reduced cell viability but the 808 nm laser did not alter cell viability even after an exposure of 30 min. Therefore, our system is able to be exposed to NIR light for a long time without damaging the tissue between the light source and the nanoparticles, leading to safer biomedical applications. In addition, 808 nm NIR has a deeper tissue penetration depth than 976 nm NIR, as evidenced by the observation that our nanoplatform excited by 808 nm NIR was able to generate 1O2 even under a 15-mm thickness of pork muscle tissue. Thus, compared with conventional UCNP-based PDT system utilizing 976 nm excitation, our nanoplatform bears the ability to effectively kill intrinsic tumor or the center of large tumors through PDT, which significantly improves the anticancer efficacy using UCNP-based PDT system and broadens the types of tumors that could be cured by PDT. Our study paves the way for the further development of this multifunctional core-shell-shell nanoplatform as an effective theranostic agent for diagnosis and PDT of cancer in preclinical and even clinical settings.
Methods
Materials
2-aminoethyl dihydrogen phosphate (AEP) was purchased from J&K Scientific Ltd. Chlorin e6 (Ce6) was obtained from Frontier Scientific. H2N-PEG-COOH (MW 5,000) was purchased from Nanocs. Methoxy poly(ethylene glycol) succinimidyl ester (mPEG-SC) was from Sinopeg Biotech Co. Ltd. N-(3-dimethylaminopropyl)-N’-ethylcarbodiimide hydrochloride (EDC), N-hydroxysuccinimide (NHS) and 1,3-diphenylisobenzofuran (DPBF) were purchased from Sigma-Aldrich. Folic acid was from Acros Organics. 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) was purchased from Life Technologies. All reagents were used as received. KB cells were kindly provided by Mr. Kenneth K. K. Lau of Department of Biology and Chemistry at the City University of Hong Kong and A549 cells were from American Type Culture Collection (ATCC).
Preparation of NH2-UCNPs
Core-shell-shell upconversion nanoparticles [NaYbF4:Nd@NaGdF4:Yb/Er@NaGdF4] were synthesized following a protocol that we have established previously with modifications36. UCNPs capped with hydrophobic oleic acid were transferred to aqueous phase by ligand exchange. Briefly, 30 mg of UCNPs was first precipitated by ethanol and then redispersed in 2 mL of chloroform by sonication. A volume of 15 mL AEP solution containing 100 mg AEP in milli-Q water and ethanol (3:2 v/v) was added to the chloroform solution of UCNPs and the mixture was stirred for 48 h at room temperature. The transfer of UCNPs from the bottom chloroform layer into the upper aqueous layer was confirmed by the emission of aqueous layer under 808 nm laser excitation (data not shown). The aqueous phase was subsequently dialyzed (MWCO, 10K) against deionized water for 1 day at room temperature to remove unreacted AEP. Finally, the sample was lyophilized overnight to obtain NH2-UCNPs.
Modification of NH2-UCNPs with chlorin e6
Chlorin e6 was dissolved in dimethyl sulfoxide (DMSO) and excess amount of EDC and NHS was added to activate carboxylate for 30 min at room temperature. NH2-UCNPs were resuspended into DMSO and ultrasonicated for 10 min; the solution was then added to the activated Ce6 solution containing trace amount of triethylamine (TEA) and stirred overnight. The solution containing Ce6-UCNPs was dialyzed (MWCO, 10K) against deionized water for 1 day at room temperature followed by lyophilization.
Modification of H2N-PEG-COOH with folic acid
Folic acid was activated by EDC and NHS as mentioned above. H2N-PEG-COOH (MW 5,000) was dissolved in DMSO, added into the solution of folic acid containing TEA and stirred overnight at room temperature. Acetone was added to precipitate the unreacted folic acid. FA-PEG-COOH was dialyzed (MWCO, 10K) against deionized water at room temperature for 2 days followed by lyophilization to obtain a light yellow product.
Modification of Ce6-UCNPs with PEG
FA-PEG-COOH together with EDC and NHS were first dissolved in DMSO and stirred overnight. Ce6-UCNPs were resuspended in DMSO and sonicated for 5 min. mPEG-SC and activated FA-PEG-COOH in DMSO together with TEA was then added and the mixture was stirred overnight at room temperature. Afterward, the PEG-Ce6-UCNPs were dialyzed (MWCO, 10K) against deionized water and subsequently lyophilized for 1 day.
Characterizations of modified UCNPs
UV-visible spectrum was recorded on a Shimazu UV-1700 UV-Vis spectrophotometer. Fourier transform infrared (FT-IR) was performed on an AVATAR-360 FT-IR spectrophotometer (Nicolet, USA). Transmission Electron Microscopy (TEM) measurements were carried out on a Philips CM-20 TEM (Philips Technai 12). Photoluminescence (PL) was measured using an F-4600 spectrophotometer (Hitachi) with the excitation source adapted to fiber coupled diode lasers. Decay curves of the emission of at both 550 nm and 660 nm of NH2-UCNPs and FA-PEG-Ce6-UCNPs were recorded on FLSP920 fluorescence spectrophotometer (Edinburgh Instruments) equipped with an 808 nm VD-IIA DPSS Laser Driver.
Detection of singlet oxygen
Singlet oxygen was determined by DPBF according to a previously published report28. FA-PEG-Ce6-UCNPs was sonicated and dispersed in DMSO containing 200 μM DPBF. The resulting solution was added in a 96-well plate and irradiated by an 808 nm laser for different amount of time and the absorbance at 418 nm was recorded. The generation of singlet oxygen by FA-PEG-Ce6-UCNPs bleaches DPBF, thus the decreased absorption of DPBF at 418 nm reflects the singlet oxygen level produced by FA-PEG-Ce6-UCNPs.
Near infrared (NIR) induced PDT efficiency of modified UCNPs
A549 and KB cells were seeded in 96-well culture plates at a density of 1,500 and 2,000 cells/well, respectively and cultured in 5% CO2 at 37 °C for 48 h. The cells were then treated with different concentrations of FA-PEG-Ce6-UCNPs for 2 h and irradiated with an 808 nm laser for 5 min/well (6 W/cm2). The cells were incubated for another 48 h in the dark before the standard MTT assay. Cell viabilities were normalized to the viabilities of untreated cells with irradiation.
In vitro cell imaging
KB (FR+) cells were cultured in FA-free RPMI-1640 medium (Gibco) supplemented with 10% (v/v) fetal bovine serum and 50 units/mL penicillin/streptomycin at 37 °C under humidified air containing 5% CO2. For KB (FR-) cells, the KB cells were cultured in RPMI-1640 medium supplemented with free folic acid (1 μg/mL), thus the folate receptors on the KB cells membrane were blocked by free folic acid. A549 cells were cultured in DMEM supplemented with 10% (v/v) fetal bovine serum and 50 units/mL penicillin/streptomycin at 37 °C under humidified air containing 5% CO2. Cells were then seeded onto coverglass bottom culture dish and allowed to adhere for 40 h. The cells were incubated in fresh medium containing 100 μg/mL nanoparticles for 4 h and then washed three times with PBS to sufficiently remove excessive nanoparticles. Cell imaging was performed on a Leica SP5 confocal microscope. The upconversion luminescence emission of UCNPs (emission range 500-700 nm) were excited by an 808 nm laser.
Note
During the preparation of this manuscript, a related work using 808 nm-excited UCNPs for photodynamic therapy was reported (D. Wang, B. Xue, X. Kong, L. Tu, X. Liu, Y. Zhang, Y. Chang, Y. Luo, H. Zhao and H. Zhang, Nanoscale, 2015, 7, 190-197, First published online 03 Nov 2014).
Additional Information
How to cite this article: Ai, F. et al. A core-shell-shell nanoplatform upconverting near-infrared light at 808 nm for luminescence imaging and photodynamic therapy of cancer. Sci. Rep. 5, 10785; doi: 10.1038/srep10785 (2015).
References
Dolmans, D. E. J. G. J., Fukumura, D. & Jain, R. K. Photodynamic therapy for cancer. Nat. Rev. Cancer 3, 375–380 (2003).
Castano, A. P., Mroz, P. & Hamblin, M. R. Photodynamic therapy and anti-tumour immunity. Nat. Rev. Cancer 6, 535–545 (2006).
Dougherty, T. J., et al. Photodynamic therapy. J. Natl. Cancer Inst. 90, 889–905 (1998).
Weissleder, R. & Ntziachristos, V. Shedding light onto live molecular targets. Nat. Med. 9, 123–128 (2003).
Kim, S., Ohulchanskyy, T. Y., Pudavar, H. E., Pandey, R. K. & Prasad, P. N. Organically modified silica nanoparticles co-encapsulating photosensitizing drug and aggregation-enhanced two-photon absorbing fluorescent dye aggregates for two-photon photodynamic therapy. J. Am. Chem. Soc. 129, 2669–2675 (2007).
Haase, M. & Schäfer, H. Upconverting nanoparticles. Angew. Chem. Int. Ed. 50, 5808–5829 (2011).
Xue, X., Wang, F. & Liu, X. Emerging functional nanomaterials for therapeutics. J. Mater. Chem. 21, 13107–13127 (2011).
Jayakumar, M. K. G., Idris, N. M. & Zhang, Y. Remote activation of biomolecules in deep tissues using near-infrared-to-UV upconversion nanotransducers. Proc. Natl. Acad. Sci. U.S.A. 109, 8483–8488 (2012).
Wang, F. & Liu, X. Multicolor tuning of lanthanide-doped nanoparticles by single wavelength excitation. Acc. Chem. Res. 47, 1378–1385 (2014).
Chen, X., Peng, D., Ju, Q. & Wang, F. Photon upconversion in core-shell nanoparticles. Chem. Soc. Rev. 44, 1318–1330 (2015).
Wang, J., Wang, F., Wang, C., Liu, Z. & Liu, X. Single-band upconversion emission in lanthanide-doped KMnF3 nanocrystals. Angew. Chem. Int. Ed. 50, 10369–10372 (2011).
Wang, F., Banerjee, D., Liu, Y., Chen, X. & Liu, X. Upconversion nanoparticles in biological labeling, imaging and therapy. Analyst 135, 1839–1854 (2010).
Wang, F., Wang, J. & Liu, X. Direct evidence of a surface quenching effect on size-dependent luminescence of upconversion nanoparticles. Angew. Chem. Int. Ed. 49, 7618–7622 (2010).
Wang, F. & Liu, X. Recent advances in the chemistry of lanthanide-doped upconversion nanocrystals. Chem. Soc. Rev. 38, 976–989 (2009).
Xia, A., et al. Polypeptide-functionalized NaYF4:Yb3+,Er3+ nanoparticles: red-emission biomarkers for high quality bioimaging using a 915 nm laser. ACS Appl. Mater. Interfaces 6, 18329–18336 (2014).
Bouzigues, C., Gacoin, T. & Alexandrou, A. Biological applications of rare-earth based nanoparticles. ACS Nano 5, 8488–8505 (2011).
Zhou, J., Liu, Z. & Li, F. Upconversion nanophosphors for small-animal imaging. Chem. Soc. Rev. 41, 1323–1349 (2012).
Liu, Q., et al. Sub-10 nm hexagonal lanthanide-doped NaLuF4 upconversion nanocrystals for sensitive bioimaging in vivo. J. Am. Chem. Soc. 133, 17122–17125 (2011).
Chen, G., et al. (α-NaYbF4:Tm3+)/CaF2 core/shell nanoparticles with efficient near-infra red to near-infrared upconversion for high-contrast deep tissue bioimaging. ACS Nano 6, 8280–8287 (2012).
Zhan, Q., et al. Using 915 nm laser excited Tm3+/Er3+/Ho3+-doped NaYbF4 upconversion nanoparticles for in vitro and deeper in vivo bioimaging without overheating irradiation. ACS Nano 5, 3744–3757 (2011).
Dai, Y., et al. Up-conversion cell imaging and pH-induced thermally controlled drug release from NaYF4:Yb3+/Er3+@hydrogel core–shell hybrid microspheres. ACS Nano 6, 3327–3338 (2012).
Tian, G., et al. Mn2+ dopant-controlled synthesis of NaYF4:Yb/Er upconversion nanoparticles for in vivo imaging and drug delivery. Adv. Mater. 24, 1226–1231 (2012).
Cheng, L., et al. Multifunctional upconversion nanoparticles for dual-modal imaging-guided stem cell therapy under remote magnetic control. Adv. Funct. Mater. 23, 272–280 (2013).
Gai, S., et al. Synthesis of magnetic, up-conversion luminescent and mesoporous core-shell-structured nanocomposites as drug carriers. Adv. Funct. Mater. 20, 1166–1172 (2010).
Hou, Z., et al. Electrospinning preparation and drug-delivery properties of an up-conversion luminescent porous NaYF4:Yb3+, Er3+@silica fiber nanocomposite. Adv. Funct. Mater. 21, 2356–2365 (2011).
Hou, Z., et al. Up-conversion luminescent and porous NaYF4:Yb3+,Er3+@SiO2 nanocomposite fibers for anti-cancer drug delivery and cell imaging. Adv. Funct. Mater. 22, 2713–2722 (2012).
Shan, J., et al. Pegylated composite nanoparticles containing upconverting phosphors and meso-tetraphenyl porphine (TPP) for photodynamic therapy. Adv. Funct. Mater. 21, 2488–2495 (2011).
Liu, K., et al. Covalently assembled NIR nanoplatform for simultaneous fluorescence imaging and photodynamic therapy of cancer cells. ACS Nano 6, 4054–4062 (2012).
Chen, Q., et al. Protein modified upconversion nanoparticles for imaging-guided combined photothermal and photodynamic therapy. Biomaterials 35, 2915–2923 (2014).
Wang, C., Tao, H., Cheng, L. & Liu, Z. Near-infrared light induced in vivo photodynamic therapy of cancer based on upconversion nanoparticles. Biomaterials 32, 6145–6154 (2011).
Xia, L., et al. An upconversion nanoparticle-Zinc phthalocyanine based nanophotosensitizer for photodynamic therapy. Biomaterials 35, 4146–4156 (2014).
Qian, H. S., Guo, H. C., Ho, P. C., Mahendran, R. & Zhang, Y. Mesoporous-silica-coated up-conversion fluorescent nanoparticles for photodynamic therapy. Small 5, 2285–2290 (2009).
Tian, G., et al. Red-emitting upconverting nanoparticles for photodynamic therapy in cancer cells under near-infrared excitation. Small 9, 1929–1938 (2013).
Chen, G., Qiu, H., Prasad, P. N. & Chen, X. Upconversion nanoparticles: design, nanochemistry and applications in theranostics. Chem. Rev. 114, 5161–5214 (2014).
Xie, X., et al. Mechanistic investigation of photon upconversion in Nd3+-sensitized core-shell nanoparticles. J. Am. Chem. Soc. 135, 12608–12611 (2013).
Wen, H., et al. Upconverting near-infrared light through energy management in core-shell-shell nanoparticles. Angew. Chem. Int. Ed. 52, 13419–13423 (2013).
Zhou, A., Wei, Y., Wu, B., Chen, Q. & Xing, D. Pyropheophorbide A and c(RGDyK) comodified chitosan-wrapped upconversion nanoparticle for targeted near-infrared photodynamic therapy. Mol. Pharm. 9, 1580–1589 (2012).
Qian, J., et al. Photosensitizer encapsulated organically modified silica nanoparticles for direct two-photon photodynamic therapy and in vivo functional imaging. Biomaterials 33, 4851–4860 (2012).
Lim, M. E., Lee, Y. L., Zhang, Y. & Chu, J. J. Photodynamic inactivation of viruses using upconversion nanoparticles. Biomaterials 33, 1912–1920 (2012).
Shen, J., et al. Engineering the upconversion nanoparticle excitation wavelength: cascade sensitization of tri-doped upconversion colloidal nanoparticles at 800 nm. Adv. Optical Mater. 1, 644–650 (2013).
Wang, Y., et al. Nd3+-sensitized upconversion nanophosphors: efficient in vivo bioimaging probes with minimized heating effect. ACS Nano 7, 7200–7206 (2013).
Zhong, Y., et al. Elimination of photon quenching by a transition layer to fabricate a quenching-shield sandwich structure for 800 nm excited upconversion luminescence of Nd3+-sensitized nanoparticles. Adv. Mater. 26, 2831–2837 (2014).
Wang, R., Li, X., Zhou, L. & Zhang, F. Epitaxial seeded growth of rare-earth nanocrystals with efficient 800 nm near-infrared to 1525 nm short-wavelength infrared downconversion photoluminescence for in vivo bioimaging. Angew. Chem. Int. Ed. 126, 12282–12286 (2014).
Dai, Y., et al. In vivo multimodality imaging and cancer therapy by near-infrared light-triggered trans-platinum pro-drug-conjugated upconverison nanoparticles. J. Am. Chem. Soc. 135, 18920–18929 (2013).
Park, Y. I., et al. Theranostic probe based on lanthanide-doped nanoparticles for simultaneous in vivo dual-modal imaging and photodynamic therapy. Adv. Mater. 24, 5755–5761 (2012).
Wang, C., Cheng, L. & Liu, Z. Drug delivery with upconversion nanoparticles for multi-functional targeted cancer cell imaging and therapy. Biomaterials 32, 1110–1120 (2011).
Schnurpfeil, G., Sobbi, A. K., Spiller, W., Kliesch, H. & Wöhrle, D. Photo-oxidative stability and its correlation with semi-empirical MO calculations of various tetraazaporphyrin derivatives in solution. J. Porphyrins Phthalocyanines 1, 159–167 (1997).
Lee, E. S., Gao, Z. & Bae, Y. H. Recent progress in tumor pH targeting nanotechnology. J. Control. Release 132, 164–170 (2008).
Wang, C., Cheng, L., Xu, H. & Liu, Z. Towards whole-body imaging at the single cell level using ultra-sensitive stem cell labeling with oligo-arginine modified upconversion nanoparticles. Biomaterials 33, 4872–4881 (2012).
Acknowledgements
This research was supported by the National Natural Science Foundation of China (Grant Nos. 21371145, 21303149 and 51332008) and City University of Hong Kong (Project 9678089). We thank Mr. R. Ma at Zhejiang University for help with sample characterizations.
Author information
Authors and Affiliations
Contributions
G.Z. and F.W. conceived the project. F.A., F.W. and G.Z. designed the experiments and wrote the manuscript. Q.J. and X.C. carried out the chemical synthesis and characterization of the nanoparticles. F.A. and X.Z. carried out functionalization, characterization and biological evaluations of loaded nanoparticles.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Ai, F., Ju, Q., Zhang, X. et al. A core-shell-shell nanoplatform upconverting near-infrared light at 808 nm for luminescence imaging and photodynamic therapy of cancer. Sci Rep 5, 10785 (2015). https://doi.org/10.1038/srep10785
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep10785
- Springer Nature Limited
This article is cited by
-
Construction and evaluation of curcumin upconversion nanocarriers decorated with MnO2 for tumor photodynamic therapy
Drug Delivery and Translational Research (2022)
-
808 nm-activable core@multishell upconverting nanoparticles with enhanced stability for efficient photodynamic therapy
Journal of Nanobiotechnology (2020)
-
Emerging NIR light-responsive delivery systems based on lanthanide-doped upconverting nanoparticles
Archives of Pharmacal Research (2020)
-
Effects of Photodynamic Therapy with Redaporfin on Tumor Oxygenation and Blood Flow in a Lung Cancer Mouse Model
Scientific Reports (2019)
-
Multimodal tumor-homing chitosan oligosaccharide-coated biocompatible palladium nanoparticles for photo-based imaging and therapy
Scientific Reports (2018)