Abstract
Spintronics offers promising routes for efficient memory, logic, and computing technologies. The central challenge in spintronics is electrically manipulating and detecting magnetic states in devices. The electrical control of magnetization via spin-orbit torques is effective in both conducting and insulating magnetic layers. However, the electrical readout of magnetization in the latter is inherently difficult, limiting their use in practical applications. Here, we show magnetoresistive detection of perpendicular magnetization reversal in an electrically insulating ferrimagnet, terbium iron garnet (TbIG). To do so, we use TbIG|Cu|TbCo, where TbCo is the reference conducting ferrimagnet and Cu is a nonmagnetic spacer. Current injection through Cu|TbCo allows us to detect the magnetization reversal of TbIG with a simple resistance readout during an external magnetic field sweep. By examining the effect of measurement temperature, TbCo composition, and Cu thickness on the sign and amplitude of the magnetoresistance, we conclude that the spin-dependent electron scattering at the TbIG|Cu interface is the underlying cause. Magnetoresistive detection of perpendicular switching in a ferrimagnetic garnet may enable alternative insulating spintronic device concepts.
Similar content being viewed by others
Introduction
Ferrimagnetic garnets (FMGs) are ubiquitous in solid-state physics. They host a wide variety of useful properties, such as ultralow damping, high magnon density, tunable magnetic anisotropy and saturation magnetization, and highly ordered single-crystal structures with sharp surfaces and interfaces1. Furthermore, single-crystal epitaxial FMGs can be grown from a few micrometers down to a few nanometers of thickness via physical and chemical deposition techniques on suitable substrates and, yet, retain bulk-like properties. As a result, FMGs have served as an excellent material testbed for a multitude of spintronic phenomena in the past few years2,3,4,5,6,7,8. More recently, there has been a growing effort in exploiting FMGs as active components in magnonic integrated circuits9 and spintronic memory devices10. Research into the latter has been particularly fruitful owing to the development of ultrathin FMGs with perpendicular magnetic anisotropy (PMA)11,12 and the highly efficient control of their magnetization vector by current-induced spin-orbit torques8,10,13,14,15,16,17.
While the above advances are promising for the integration of FMGs in future computing technologies, the electrical detection of magnetization in this material family is still a critical challenge. The spin Seebeck, local and non-local spin Hall magnetoresistance, and thermal spin drag effects have been utilized for the electrical detection of magnetization in FMGs3,4,5,18. However, all of these phenomena rely on voltages induced by inverse spin Hall effect in an adjacent nonmagnetic metal, such as Pt, hence fundamentally limiting the output signal amplitudes and materials that can be used for the purpose. Electrical detection of the perpendicular magnetization vector in FMGs possessing PMA, crucial for domain wall and skyrmion-based racetrack devices, and for downscaling the lateral size of memory cells, is particularly strenuous. Thus far, the anomalous Hall effect (AHE) driven by interfacial spin-dependent scattering4,19,20,21 is used as the sole electrical method for magnetization vector detection in PMA FMGs10,22, yielding minute output signals, nonetheless in a technologically-prohibitive four-contact Hall cross device geometry.
Magnetization vector detection in conventional spintronic devices is realized by tunnel and giant magnetoresistances (GMR)23,24,25,26. The latter, discovered in the 1980s, has led to miniaturized GMR sensors, revolutionizing both the magnetic non-volatile data storage and field sensing technologies27. What lies at the core of the GMR is the spin valve effect, arising from the spin-dependent electron scattering at the bulk and interfaces of ferromagnetic materials28. GMR spin valves typically consist of conducting magnetic layers separated by nonmagnetic metal spacers. The electrical resistance of such systems exhibits a large asymmetry between the parallel and antiparallel alignment of the magnetizations of adjacent magnetic layers, which serve as the reference and free layers, respectively. GMR can then be used to effectively probe the magnetization reversal or rotation of the free layer with respect to the reference, also in a current-in-plane (CIP) geometry, leading to simple two-terminal devices. To date, FMGs have been excluded from such device concepts even though the GMR-based sensing of FMGs’ magnetization vector would be highly desirable. Few earlier reports have characterized the spin valve effect at other magnetic insulator|metal interfaces, but these were limited to in-plane magnetization systems and cryogenic temperature measurements29,30,31. While the presence of the spin valve effect is allowed at an FMG|metal interface in principle, its experimental observation remains elusive.
In this work, we show a robust spin valve effect at the interface of a typical FMG, terbium iron garnet (Tb3Fe5O12, TbIG), enabling us to detect 180° perpendicular magnetization reversal via simple resistance measurements at room temperature. We achieve such spin valve behavior in a TbIG|Cu|TbCo trilayer (see Fig. 1a) where the TbIG is engineered to be the free layer whereas TbCo acts as the reference magnetic layer. We observe abrupt longitudinal resistance changes during a swept magnetic field upon crossing the coercive fields of the respective layers, analogous to the CIP-GMR, albeit with a smaller amplitude with respect to a fully metallic stack. The effect of measurement temperature, TbCo layer composition, and spacer layer thickness on the sign and amplitude of the magnetoresistance collectively pinpoint the spin valve effect at the TbIG|Cu interface as the predominant origin of the observed phenomenon. Theoretical calculations based on layer-resolved Boltzmann transport equations are in excellent agreement with our experimental findings and further consolidate the presumed origin of the magnetoresistance effect. The efficient reading of the magnetization vector in FMGs in a two-terminal CIP geometry reported here provides a new platform for spintronic device concepts using magnetic insulators as active components.
Results and discussion
Layer composition and magnetic characterization
We deposited TbIG(25)|Cu(1-5)|TbxCo1-x(8)|Pt(3) (thicknesses in nm, subscript x denotes atomic %) stacks and other reference layers by means of magnetron sputtering, and patterned them into standard Hall bar devices (see Fig. 1b and Methods). Here, TbIG and TbxCo1-x (TbCo for short, x = 0.3 unless specified otherwise) are used as the soft and hard magnetic layers, respectively, due to the lower (higher) coercivity of the former (latter). We preferred a Tb-based ferrimagnetic metallic alloy over an elemental transition metal such as Co, since the former exhibits a large and tunable bulk PMA over a broad range of composition, thickness, and temperature, independently of the under/over layer, thus eliminating the laborious engineering of the interfacial PMA in the latter32,33,34. The thickness of the Cu spacer is varied between 1 and 5 nm and Cu is chosen due to its high spin conductivity when interfaced with FMGs and TbCo35,36. Finally, Pt is used as capping to avoid oxidation of TbCo and it has no active role in the spin transport experiments reported in this paper, therefore will not be mentioned in the remainder of the text. We note that no significant difference is obtained when changing the capping layer to another metal, for example Ti.
The magnetization behavior of TbIG and TbCo were examined by polar magneto-optic Kerr effect (MOKE, Fig. 1c) and AHE (Fig. 1d) measurements with a swept out-of-plane field (Hz). In the former, we observed a clear hysteresis loop typical of PMA systems with 100% remanence, and large coercivity Hc ~ 35 mT. A closer look-up to the lower field region reveals minor signal jumps at ~±10 mT. The inner loop measurement focusing on this region (see inset – dark green curve) indicates a second magnetic signal with a much lower amplitude, superimposed to the larger hysteresis loop. The Hc value of this inner loop corresponds to the one measured for TbIG prior to the Cu|TbCo deposition (see inset - light green curve), hence this signal corresponds to TbIG. The similar coercivity of the TbIG before and after deposition of the Cu|TbCo indicates negligible exchange coupling between the two magnetic layers. The Hall resistance (RH) measurement shows the hysteresis loop originating from the AHE in TbCo with Hc ~ 35 mT, consistent with the MOKE result. However, an inner loop measurement similar to Fig. 1c—inset does not show any signal related to the TbIG reversal. Because of the absence of current flow through TbIG, the AHE signal cannot be generated in this layer and the interfacial AHE is also inoperative due to the negligible spin Hall effect in Cu. These measurements clearly demonstrate that the magnetization vector of TbIG in the above stack can only be probed optically but not electrically with standard Hall measurements.
Magnetoresistive detection of perpendicular switching
We then examine the longitudinal resistance behavior of the above stack and compare it with reference material systems. The GMR in magnetic transition-metal multilayers is known to originate from the spin-dependent scattering in the spin-split d bands37,38, typically leading to an increase of the resistance when the magnetization (M) of consecutive layers is antiparallel compared to the parallel case. Figure 2a shows the resistance behavior of a fully metallic Co|Cu|TbCo PMA spin valve device during an Hz sweep. We observe two reversal events at low and high fields, corresponding to the switching of Co and TbCo, respectively, resulting in two distinct resistance levels in the parallel and antiparallel configurations, expectedly of the CIP-GMR. The magnitude of the GMR is 4.9%, comparable to previous reports on similar systems36,39. Next, we measure Cu/TbCo deposited on a non-magnetic gadolinium gallium garnet (Gd3Ga5O12, GGG) substrate (Fig. 2b). Here, the spin valve behavior is not observed. Instead, the resistance displays a field-dependent variation resembling a bowtie shape. This unconventional resistance behavior was previously reported and attributed to the magnon magnetoresistance40 and/or magnetoresistance due to the sperimagnetism of TbCo41. This effect requires a conducting magnetic layer and exhibits a quasi-linear positive or negative slope depending on the relative direction of M and Hz.
Figure 2c shows the magnetoresistance of the TbIG|Cu|TbCo trilayer. The resistance clearly undergoes four distinct switching events corresponding to the perpendicular switching of TbIG and TbCo, superimposed to the quasi-linear background magnetoresistance described above. Initially, at large positive fields, the magnetizations of TbIG and TbCo are parallel and aligned with Hz. Upon reducing Hz, the resistance increases linearly until ~−10 mT at which field the magnetization of TbIG reverses from up to down and a sudden resistance increase occurs. As Hz is reduced further, the resistance increase continues, until the coercivity of TbCo is reached at ~−35 mT, where the resistance drops sharply, followed by further gradual Hz-dependent decrease. A reciprocal sequence is observed when Hz is swept from the negative to positive direction. To better illustrate the GMR-like behavior, in Fig. 2d, we plot the magnetoresistance after subtraction of the background due to the unusual magnetoresistance of TbCo not related to the GMR effect. Finally, Fig. 2e shows the minor loops, corresponding to the reversal of M of TbIG, when the TbCo layer is pre-set in the up (+z) and down (−z) direction. In these measurements, we observe the hysteretic resistance behavior in both cases with an opposite sign due to the reversal of the reference layer. Based on the amplitude of the jump in Fig. 2e, we estimate the relative change of resistance ΔR/R0 = 1.4 × 10−5, where R0 is the resistance at zero applied field.
The signals reported in Fig. 2c–e are consistent with a positive GMR in TbIG|Cu|TbCo. The sign of the GMR in all-metallic systems is dictated by the spin-dependent scattering asymmetry at the bulk and interfaces of the magnetic layers. In TbCo, the spin-polarized conduction is mostly dominated by the s-d electrons of Co, hence the Co magnetization dictates the bulk and interface contribution to the GMR as well as the sign of the AHE. The positive AHE in Fig. 1d and the positive GMR in Fig. 2a establish that the net magnetization in TbCo is parallel to the Co sublattice in the TbIG|Cu|TbCo stack. Likewise, independent measurements reported in our earlier study (see ref. 12) and Supplementary Note 1 show that the net magnetization in TbIG is Fe sublattice dominated. Since TbIG is an insulator, we expect only the TbIG/Cu interface to contribute to the GMR. We tested this by measuring the GMR in 7nm-thick TbIG film, which shows comparable ΔR/R0 with respect to 25 nm-thick TbIG (see Supplementary Note 2). Therefore, the positive GMR in TbIG|Cu|TbCo demonstrates that the sign of the spin-dependent scattering asymmetry at both the TbIG|Cu and Cu|TbCo interfaces is the same and positive with respect to the standard convention.
Temperature-dependence of the magnetoresistance
To examine further the effect of the relative orientation of the ferrimagnetic sublattices on the sign, and the influence of the measurement temperature on the amplitude of ΔR/R0, we studied the magnetoresistance in TbIG|Cu|TbCo as a function of temperature (T), across the magnetic compensation temperature (TM) of TbIG. In Fig. 3a, we plot representative data during a Hz sweep measured at T = 225 K and 175 K, i.e., above and below the TM of TbIG, respectively. We found TM of TbIG ~200 K for this specific sample (see Supplementary Note 1). Because of the linear magnetoresistance background from TbCo the overall shape of the signal becomes intricate for T ≤ 200 K. Nevertheless, we observe that the resistance changes due to TbIG reversal (marked with black arrows) are upward for T = 225 K and downward for T = 175 K, indicating a clear sign change of ΔR/R0. This is further highlighted in Fig. 3b with the minor loop measurements corresponding to the magnetization reversal of TbIG when the TbCo layer is fixed along the up (+z) direction. Above TM (T = 225 K) we observe a negative hysteresis loop (similar to the room temperature measurement reported in Fig. 2e) whereas below TM (T = 175 K) the loop becomes positive.
In Fig. 3c we plot ΔR/R0 in the entire temperature range tested in this study. The sign reversal of ΔR/R0 at TM of TbIG confirms that the spin-dependent reflection at the TbIG|Cu interface, similarly to the interfacial AHE42, is not governed by the net magnetization, but instead, by the orientation of the Fe sublattice. In spite of the sign change at T ~ 200 K, the absolute value of ΔR/R0 increases smoothly and monotonically (open dots in Fig. 3c) with the decreasing temperature. This is expected from the strong temperature dependence of the GMR effect due to the increased spin conductivity of Cu at lower temperatures43.
TbCo composition and Cu spacer thickness dependence
The amplitude and sign of the GMR can be modulated by the TbCo composition and Cu spacer thickness. To investigate the former, we measured ΔR/R0 in TbIG|Cu(2)|TbxCo1−x(8 nm) layers with x ranging between 0.3 and 0.65 and plotted in Fig. 4a. We note that for x < 0.3 the films were magnetized in-plane and for x > 0.65 they were paramagnetic (see Supplementary Note 3). We find that ΔR/R0 strongly depends on the Tb content, displaying a rapid decrease going from x = 0.3 to 0.5. When the Tb amount reaches x = 0.55, the magnetization becomes Tb sublattice dominated and ΔR/R0 becomes negative (i.e., R is lower when the magnetization of TbIG and TbxCo1−x are antiparallel). This is analogous to the sign reversal observed upon crossing the TM of TbIG reported in Fig. 3c, but obtained at room temperature with a modification of the TbxCo1-x composition instead (see also Supplementary Note 4). Overall, |ΔR/R0| undergoes a ~ 22-fold decrease when the Tb concentration is increased from 0.3 to 0.6, and finally vanishes at x = 0.65. This result indicates the essential role played by Co in the spin-polarized current generation and spin-dependent scattering in the bulk and interfaces of TbCo.
Figure 4b reports the effect of the Cu spacer thickness (t) on ΔR/R0 in TbIG|Cu(t)|TbCo layers. The largest effect is found for Cu(2 nm), plots of the R as a function of HZ for all the Cu spacer thickness are reported in the Supplementary Note 5. Increasing t results in a decrease of ΔR/R0, as expected due to the increased current shunting and reduced spin coherence43. On the other hand, for a Cu thickness of 1 nm, a slightly lower ΔR/R0 is observed with respect to Cu(2 nm), whereas the effect is, in principle, expected to be enhanced. Atomic force microscopy analysis of the Cu films shows a root mean square roughness of ~0.7 nm, which is similar to the lowest Cu thickness used (see Supplementary Note 6). Therefore, the lower uniformity and larger interface/volume ratio of 1 nm-thick Cu cause additional resistance, that does not participate in the magnetoresistance and negatively affects the spin-dependent properties and interface quality with the TbCo layer. Indeed, we observe a correlation between the Cu thickness and the coercivity and PMA of TbCo, indicating a sharper interface when the Cu thickness is increased, promoting a higher quality TbCo. This might be the reason why the magnetoresistance is still substantial despite larger current shunting when the Cu spacer is increased to 5 nm. The strong dependence of the magnetic properties of TbCo alloys on the underlayer material, thickness and interface quality is well known44. Additionally, discrepancies in the spin-dependent properties of the TbIG|Cu interface for TbIG grown on different dates on different substrates could influence the data presented in Fig. 4b. Although the essential features and trends expected of the thickness dependence of ΔR/R0 are observed, the data in Fig. 4b cannot reflect a universal behavior. Therefore, we believe that a more systematic study of the influence of the spacer layer thickness on ΔR/R0 should be conducted by continuously varying the Cu thickness on a single substrate to ensure the uniformity of the TbIG properties, which falls outside our technical capabilities. Finally, to confirm the relevance of the spacer layer with low spin-orbit coupling (high spin conductivity) on the magnetoresistance, we replaced Cu with 2 nm of Pt which exhibits large spin-orbit coupling. We did not detect any spin valve effect within our experimental detection limit. This negative result is anticipated due to the very short spin diffusion length of Pt (typically <2 nm), dephasing nearly the entire spin current generated in the TbCo and at the Pt/TbCo interface36. Furthermore, the absence of spin valve signal with the Pt spacer excludes the magnetic proximity effect at the TbIG|metal interface as the potential origin of the magnetoresistance, since Pt is much more susceptible to proximity magnetism than Cu. We note that ΔR/R0 values of all the materials examined in this work can be found in Supplementary Table 1.
Boltzmann transport calculations
We calculated the magnetization-dependent resistivity of TbIG|Cu|TbCo trilayer by solving the following linearized Boltzmann transport equation with a layer-by-layer approach38,45:
Here \(m\) and \(\tau\) are the effective mass and momentum relaxation time and mass of conduction electrons, \({f}_{0}\) is the equilibrium electron distribution function, \(g({{{{{\boldsymbol{v}}}}}},z)\) is the deviation from f0 induced by the external electric field with amplitude E applied along x. Full translation symmetry is assumed in the x-y plane (i.e., the layer plane) so that the spatial dependence of \(g\) only occurs in the thickness direction parallel to the z-axis. To further simplify our calculations, we assumed the same effective mass, relaxation time, and Fermi energy \({\varepsilon }_{F}\) for the conducting Cu and TbCo layers, which would be sufficient for the purpose of an order of magnitude estimation of the ΔR/R0 ratio of the trilayer system. The calculation can be extended straightforwardly to involve different values of the above-mentioned materials parameters without essential change to the formulation.
In order to capture the interfacial spin-dependent scattering, we divide \(g\) into four additive components depending on the orientation of an electron’s spin moment with respect to the magnetization of a magnetic layer and the sign of vz (i.e., the z-component of the electronic group velocity). The general solutions of Eq. (1) can be written as
where the “\(+\)” and “\(-\)” signs denote electrons with \({v}_{z}\) being positive and negative, respectively, the arrow \(\uparrow (\downarrow )\) characterizes orientation of spin parallel (antiparallel) to the local magnetization of the magnetic layer in question. The general solutions take the same form for electrons in the Cu and TbCo layers, except for the coefficients, \({C}_{\pm \uparrow (\downarrow )},\) which need to be determined by boundary conditions.
To calculate the ΔR/R0 ratio, scatterings at three interfaces of the trilayer need to be taken into account through the boundary conditions, namely, 1) the spin-dependent reflection at the out surface of the TbCo layer, 2) the specular transmission and reflection at the interface between the metallic TbCo|Cu interface, and 3) the spin-dependent specular reflection at the Cu|TbIG interface. In addition, when the magnetizations of the TbCo and TbIG layers are antiparallel, we also take into account the change of spin quantization axis in the middle of the Cu layer. It is reasonable to assume specular reflection at the metallic interface is negligible and scattering at the outer surface of the TbCo layer is completely diffusive. And near the magnetic interface between the Cu and TbIG layer, the portions of electron fluxes that are specularly reflected from the interface are, in principle, also spin dependent21, as “spin-up” and “spin-down” electrons see different energy barriers effectively due to the exchange coupling (\({J}_{{ex}}\)) between them and the magnetization of the TbIG layer even though the magnetic layer is insulating.
By inserting the general solutions of \({g}_{\pm \uparrow (\downarrow )}\) for each layer into the above boundary conditions, the unknowns in Eq. (2) can be determined, allowing us to further evaluate the spatially-averaged longitudinal conductivity of the i layer via \({\sigma }^{(i)}=\frac{1}{{d}_{i}E}\int {dz}\int {d}^{3}{{{{{\boldsymbol{v}}}}}}{v}_{x}({g}_{\uparrow }+{g}_{\downarrow })\), where \({d}_{i}\) is the thickness of the ith layer. The total resistivities for parallel and antiparallel magnetization configurations, denoted by \({\rho }_{\uparrow \uparrow }\) and \({\rho }_{\uparrow \downarrow }\) respectively, are obtained by inverting the corresponding conductivity tensors. Finally, the ΔR/R0 ratio is evaluated via \(\Delta R/{R}_{0}=\left({\rho }_{\uparrow \downarrow }-{\rho }_{\uparrow \uparrow }\right)/{\rho }_{\uparrow \uparrow }\). For the TbCo|Cu interface, the transmission coefficients are taken to be \({T}_{\uparrow }=0.5\) and \({T}_{\downarrow }=0.95\). Note that the roughness of the interface can be characterized phenomenologically by the spin-dependent diffusive scattering parameter defined as \({D}_{\uparrow (\downarrow )}=1-{T}_{\uparrow (\downarrow )}\)45. For \({J}_{{ex}} \sim 0.01\) eV and the averaged energy barrier of the insulator \({V}_{b} \sim 12\) eV2,21, the reflection coefficients are estimated to be \({R}_{\uparrow }=0.4995\) and \({R}_{\downarrow }=0.5005\). Note that both transmission and reflection coefficients implicitly include the spin transparency of the interfaces governed by the spin mixing conductance. This spin asymmetry of electron scatterings at the two magnetic interfaces gives rise to a ΔR/R0 ratio of 6.2 × 10−5, close to the experimental value of 7.0 × 10−5 measured at 10 K. Detailed calculations are provided in the Supplementary Note 7.
Conclusions
In summary, we demonstrate a simple magnetoresistive detection of perpendicular magnetization reversal in an insulating ferrimagnetic material TbIG, by using the spin valve effect. The detection relies on current-in-plane magnetoresistance measurements in a TbIG|Cu|TbCo trilayer system where the conducting ferrimagnet TbCo is used as a reference magnetic layer and spin polarizer. The material and temperature dependence of the magnetoresistance and theoretical calculations collectively pinpoint the spin-valve effect at the TbIG|Cu interface as the underlying cause of the observed phenomenon. To the best of our knowledge, this work constitutes the first demonstration of the spin valve effect using ferrimagnetic garnets, which are currently under the spotlight in spintronics research. While the effect is relatively small for any microelectronic applications as of yet, it can be enhanced by orders of magnitude by materials and device engineering, and support from theory.
On the materials side, ferromagnetic materials with higher spin polarization such as Heusler alloys with an optimized thickness could provide a pathway to increase the magnetoresistance. To obtain even larger gains, the spacer layer can be chosen from those having a very long spin coherence length and promoting better spin mixing conductance with the insulating and conducting magnetic layers forming the device. Potential candidates include two-dimensional materials such as graphene, transition metal dichalcogenides (TiSe2, MoS2, etc.), conducting oxides (SrVO3, etc.) and other light metals (Cr, Mn, etc.). Our work will also stimulate theoretical efforts, as the most suitable materials could be determined by using relevant first-principles calculations.
On the device side, the magnetoresistive reading reported here will enable non-volatile binary memory cells where a magnetic insulator could be used as an active component instead of conventional magnetic conductors. In such devices, using a magnetic insulator would bring about a series of advantages such as higher structural stability, broader magnetic tunability, ultrafast switching times, and low power consumption, among others. It is also possible to use the magnetoresistance output to identify and characterize the skyrmions and domain walls in an insulating racetrack memory and study their field/current-driven dynamics in real time. Insulating domain wall- and skyrmion-based devices enabled by magnetoresistive reading could pave the way for alternative analog-like memory concepts that can be used in neuromorphic computing.
Methods
Samples preparation
25 nm-thick TbIG thin films were deposited on GGG(111) substrates by radio frequency sputtering at 800 °C from a stoichiometric target. The deposition rate was ∼0.4 nm/min at the applied power of 150 W in 3 mTorr of a mixture of Ar and O2 with a ratio of 30:2 and the base pressure in the chamber was below 7 × 10−8 Torr. Detailed characterization and optimization procedures of our TbIG films are described in ref. 12. To fabricate the six-terminal Hall bar devices, the continuous TbIG films were covered in photoresist and patterned by laser-writer optical lithography. Finally, the metallic stack described further below was deposited and lift-off was performed. The Hall bar dimensions are l = 30–90 μm for the current line length, l/4 its width and l/10 the Hall branch width.
The metallic stack consisted of M(t)|TbxCo1−x(8 nm)|Pt(3 nm) and M(t)|TbxCo1−x(8 nm)|Ti(3 nm) multilayers deposited by d.c. magnetron sputtering at room temperature in 3 mTorr Ar. The TbxCo1−x alloys were obtained by co-sputtering pure Co and Tb targets and the relative atomic concentration of the two elements was controlled by the relative sputtering power. The thickness t of the metal (M) spacer layer varied between 1 and 5 nm. The deposition rates were as follows: 0.13514 nm/s at 100 W for Cu, 0.104 nm/s at 200 W for Co, 0.082 nm/s t 50 W for Tb, 0.186 nm/s at 50 W for Pt and 0.057 nm/s at 200 W for Ti. The following reference samples were also prepared: Cu(2 nm)|Tb0.3Co0.7(8 nm)|Pt(3 nm) on GGG(111) substrate, Ti(3 nm)|Pt(3 nm)|Co(1 nm)|Cu(2 nm)|Tb0.3Co0.7(8 nm)|Pt(3 nm) on Si, Ti(3 nm)|Pt(3 nm)|Co(1 nm)|Cu(2 nm)|Tb0.65Co0.35(8 nm)|Pt(3 nm) on Si and Pt(1.5 nm)|Cu(1.5 nm)|Tb0.3Co0.7(8 nm)|Pt(3 nm) on TbIG.
Magnetic and electrical characterization
The magnetic hysteresis and anisotropy axis of the films were examined using a home-built MOKE setup in a polar geometry with a 532 nm wavelength green laser. The room temperature magnetoresistance measurements were performed by recording the resistance (R) as a function of H between the extremes of the current line using a Keithley DMM6500 digital multimeter and DC test current of 1 mA. For the temperature dependence of the magnetoresistance, selected samples were inserted inside a physical property measurement system and measured in the range of 10–300 K with an AC probing current of 1 mA (root mean square) and frequency \(\omega /2\pi\) = 999 Hz. The Hall effect measurements were performed at room temperature using a Zurich Instruments MFLI digital lock-in amplifier. An AC probing current of amplitude 0.5–1 mA (root mean square) and frequency \(\omega /2\pi\) = 1092 Hz was sent across the current line and the first harmonic voltage (\({R}_{H}\)) was measured across the Hall arms.
Data availability
All the data supporting the findings of this study are available upon request from the corresponding author.
Code availability
The computer code used for data analysis is available upon request from the corresponding author.
References
Yang, Y., Liu, T., Bi, L. & Deng, L. Recent advances in development of magnetic garnet thin films for applications in spintronics and photonics. J. Alloy. Compd. 860, 158235 (2021).
Kajiwara, Y. et al. Transmission of electrical signals by spin-wave interconversion in a magnetic insulator. Nature 464, 262–266 (2010).
Uchida, K. I. et al. Observation of longitudinal spin-Seebeck effect in magnetic insulators. Appl. Phys. Lett. 97, 172505 (2010).
Nakayama, H. et al. Spin Hall magnetoresistance induced by a nonequilibrium proximity effect. Phys. Rev. Lett. 110, 206601 (2013).
Cornelissen, L. J. et al. Long-distance transport of magnon spin information in a magnetic insulator at room temperature. Nat. Phys. 11, 1022–1026 (2015).
Meyer, S. et al. Observation of the spin Nernst effect. Nat. Mater. 16, 977–981 (2017).
Seifert, T. S. et al. Femtosecond formation dynamics of the spin Seebeck effect revealed by terahertz spectroscopy. Nat. Commun. 9, 2899 (2018).
Caretta, L. et al. Relativistic kinematics of a magnetic soliton. Science 370, 1438–1442 (2020).
Chumak, A. V., Vasyuchka, V. I., Serga, A. A. & Hillebrands, B. Magnon spintronics. Nat. Phys. 11, 453–461 (2015).
Avci, C. O. et al. Current-induced switching in a magnetic insulator. Nat. Mater. 16, 309–314 (2017).
Quindeau, A. et al. Tm3Fe5O12/Pt heterostructures with perpendicular magnetic anisotropy for spintronic applications. Adv. Electron. Mater. 3, 1600376 (2017).
Damerio, S. & Avci, C. O. Sputtered terbium iron garnet films with perpendicular magnetic anisotropy for spintronic applications. J. Appl. Phys. 133, 073902 (2023).
Shao, Q. et al. Role of dimensional crossover on spin-orbit torque efficiency in magnetic insulator thin films. Nat. Commun. 9, 3612 (2018).
Avci, C. O. et al. Interface-driven chiral magnetism and current-driven domain walls in insulating magnetic garnets. Nat. Nanotechnol. 14, 561–566 (2019).
Vélez, S. et al. High-speed domain wall racetracks in a magnetic insulator. Nat. Commun. 10, 4750 (2019).
Avci, C. O. Current-induced magnetization control in insulating ferrimagnetic garnets. J. Phys. Soc. Jpn. 90, 081007 (2021).
Vélez, S. et al. Current-driven dynamics and ratchet effect of skyrmion bubbles in a ferrimagnetic insulator. Nat. Nanotechnol. 17, 834–841 (2022).
Avci, C. O. et al. Nonlocal detection of out-of-plane magnetization in a magnetic insulator by thermal spin drag. Phys. Rev. Lett. 124, 027701 (2020).
Huang, S. Y. et al. Transport magnetic proximity effects in platinum. Phys. Rev. Lett. 109, 107204 (2012).
Chen, Y. T. et al. Theory of spin Hall magnetoresistance. Phys. Rev. B 87, 144411 (2013).
Zhang, S. S. L. & Vignale, G. Nonlocal anomalous Hall effect. Phys. Rev. Lett. 116, 136601 (2016).
Meyer, S. et al. Anomalous Hall effect in YIG|Pt bilayers. Appl. Phys. Lett. 106, 132402 (2015).
Baibich, M. N. et al. Giant magnetoresistance of (001)Fe/(001)Cr magnetic superlattices. Phys. Rev. Lett. 61, 2472–2475 (1988).
Binasch, G., Grünberg, P., Saurenbach, F. & Zinn, W. Enhanced magnetoresistance in layered magnetic structures with antiferromagnetic interlayer exchange. Phys. Rev. B 39, 4828 (1989).
Yuasa, S., Nagahama, T., Fukushima, A., Suzuki, Y. & Ando, K. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions. Nat. Mater. 3, 868–871 (2004).
Parkin, S. S. P. et al. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nat. Mater. 3, 862–867 (2004).
Daughton, J. M. GMR applications. J. Magn. Magn. Mater. 192, 334–342 (1999).
Dieny, B. Giant magnetoresistance in spin-valve multilayers. J. Magn. Magn. Mater. 136, 335–359 (1994).
Snoeck, E. et al. Experimental evidence of the spin dependence of electron reflections in magnetic CoFe2O4/Au/Fe3O4 trilayers. Phys. Rev. B 73, 104434 (2006).
Van Dijken, S., Fain, X., Watts, S. M. & Coey, J. M. D. Negative magnetoresistance in Fe3O4/Au/Fe spin valves. Phys. Rev. B 70, 052409 (2004).
Tripathy, D. & Adeyeye, A. O. Giant magnetoresistance in half-metallic Fe3O4 based spin valve structures. J. Appl. Phys. 101, 09J505 (2007).
Lee, J. W., Park, J. Y., Yuk, J. M. & Park, B. G. Spin-orbit torque in a perpendicularly magnetized ferrimagnetic Tb-Co single layer. Phys. Rev. Appl. 13, 044030 (2020).
Finley, J. & Liu, L. Spin-orbit-torque efficiency in compensated ferrimagnetic cobalt-terbium alloys. Phys. Rev. Appl. 6, 054001 (2016).
Hansen, P., Klahn, S., Clausen, C., Much, G. & Witter, K. Magnetic and magneto-optical properties of rare-earth transition-metal alloys containing Dy, Ho, Fe, Co. J. Appl. Phys. 69, 3194–3207 (1991).
Du, C., Wang, H., Yang, F. & Hammel, P. C. Enhancement of pure spin currents in spin pumping Y3Fe5O12/Cu/metal trilayers through spin conductance matching. Phys. Rev. Appl. 1, 044004 (2014).
Avci, C. O., Lambert, C. H., Sala, G. & Gambardella, P. A two-terminal spin valve device controlled by spin-orbit torques with enhanced giant magnetoresistance. Appl. Phys. Lett. 119, 032406 (2021).
Parkin, S. S. P. Origin of enhanced magnetoresistance of magnetic multilayers: Spin-dependent scattering from magnetic interface states. Phys. Rev. Lett. 71, 1641–1644 (1993).
Hood, R. Q. & Falicov, L. M. Boltzmann-equation approach to the negative magnetoresistance of ferromagnetic-normal-metal multilayers. Phys. Rev. B 46, 8287–8296 (1992).
Gottwald, M. et al. Magnetoresistive effects in perpendicularly magnetized Tb-Co alloy-based thin films and spin valves. J. Appl. Phys. 111, 083904 (2012).
Mihai, A. P., Attané, J. P., Marty, A., Warin, P. & Samson, Y. Electron-magnon diffusion and magnetization reversal detection in FePt thin films. Phys. Rev. B 77, 060401(R) (2008).
Park, J. et al. Unconventional magnetoresistance induced by sperimagnetism in GdFeCo. Phys. Rev. B 103, 014421 (2021).
Rosenberg, E. R. et al. Magnetism and spin transport in rare-earth-rich epitaxial terbium and europium iron garnet films. Phys. Rev. Mater. 2, 094405 (2018).
Tripathy, D., Adeyeye, A. O. & Shannigrahi, S. Effect of spacer layer thickness on the magnetic and magnetotransport properties of Fe3O4/Cu/Ni80Fe20 spin valve structures. Phys. Rev. B 75, 022403 (2007).
Tolley, R. et al. Generation and manipulation of domain walls using a thermal gradient in a ferrimagnetic TbCo wire. Appl. Phys. Lett. 106, 242403 (2015).
Camley, R. E. & Barna, J. Theory of giant magnetoresistance effects in magnetic layered structures with antiferromagnetic coupling. Phys. Rev. Lett. 63, 664 (1989).
Acknowledgements
S.D. and C.O.A. acknowledge funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (project MAGNEPIC, grant agreement no. 949052). C.O.A. and W.J. acknowledge funding from the Spanish Ministry of Science and Innovation (MICIU/AEI/10.13039/501100011033) through grant reference no. CNS2022-136060. Work by A.S., M.M., and S.S.-L.Z. was supported by the College of Arts and Sciences, Case Western Reserve University. The authors thank M. Fettizio for the insightful discussions.
Author information
Authors and Affiliations
Contributions
C.O.A. conceived the idea and supervised the study. S.D. designed and prepared the samples, carried out the measurements and analyzed the data, with help from W.J. S.S.-L.Z. devised the magnetotransport theory, with the theoretical calculation and analysis of the transport coefficients carried out by A.S. and M.M. S.D. and C.O.A. wrote the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Communications Physics thanks the anonymous reviewers for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Damerio, S., Sunil, A., Janus, W. et al. Magnetoresistive detection of perpendicular switching in a magnetic insulator. Commun Phys 7, 114 (2024). https://doi.org/10.1038/s42005-024-01604-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42005-024-01604-x
- Springer Nature Limited