Abstract
Iridates provide a fertile ground to investigate correlated electrons in the presence of strong spin-orbit coupling. Bringing these systems to the proximity of a metal-insulator quantum phase transition is a challenge that must be met to access quantum critical fluctuations with charge and spin-orbital degrees of freedom. Here, electrical transport and Raman scattering measurements provide evidence that a metal-insulator quantum critical point is effectively reached in 5% Co-doped Sr2IrO4 with high structural quality. The dc-electrical conductivity shows a linear temperature dependence that is successfully captured by a model involving a Co acceptor level at the Fermi energy that becomes gradually populated at finite temperatures, creating thermally-activated holes in the Jeff = 1/2 lower Hubbard band. The so-formed quantum critical fluctuations are exceptionally heavy and the resulting electronic continuum couples with an optical phonon at all temperatures. The magnetic order and pseudospin-phonon coupling are preserved under the Co doping. This work brings quantum phase transitions, iridates and heavy-fermion physics to the same arena.
Similar content being viewed by others
Introduction
A rare combination of strong spin–orbit coupling and substantial electron correlations in 5d5 iridates leads to exotic quantum states and remarkable physical phenomena such as spin liquid phases1, Kitaev physics2,3,4, Fermi arcs in the electronic structure with a possible connection to high-Tc superconductivity5,6,7,8,9,10, and control of the crystal structure and magnetic properties by an electric current11,12. An intensively investigated iridate is Sr2IrO4 (SIO), crystallizing in a tetragonal structure with an ABCD stacking of layers with tilted IrO6 octahedra, as shown in Fig. 1a, b13,14. As for the electronic structure, the octahedral crystal field splits the Ir 5d level into t2g and eg levels. The strong spin–orbit coupling breaks the sixfold degeneracy of the t2g levels, giving rise to lower Jeff = 3/2 and upper Jeff = 1/2 sublevels. Finally, the Jeff = 1/2-derived band is broken into lower and upper Hubbard bands, rendering SIO insulating15,16,17. The Ir pseudospins order in a noncollinear magnetic structure below TN ~ 240 K (see Fig. 1b)16,18,19. Injection of charge carriers through electron or hole doping tends to reduce TN, although it is seems possible to destroy the insulating state without necessarily destroying the magnetic order20 and vice-versa21. The most obvious approach to access the possible quantum critical fluctuations (QCF)22,23 associated with a metal-insulator transition would be to force the closure of the bandgap by application of external pressures. Nonetheless, the nonmetallic state persists up to at least 185 GPa despite the identification of exotic states at intermediate pressures24,25,26,27,28,29. The alternative approach employed here involves the quest for a specific dilute cationic substitution that induces acceptor or donor impurity levels within the bandgap without actually charge doping the Ir-derived bands at T = 0 K, as shown in Fig. 1c. A possible contender might be the Sr2Ir1−xRhxO4 system, as Rh and Ir are in the same group of the periodic table. However, it has been demonstrated that dilute Rh-substitution induces Rh3+/Ir5+ charge partitioning, in practice doping the system with holes and rapidly suppressing the magnetic order30,31,32,33,34,35,36,37,38,39,40,41. Thus, the energy of the Rh3+ acceptor level is inferred to lay below the Fermi energy, \({E}_{{\text{Rh}}^{3+}}\,<\,{E}_{\text{F}}\), at least for x < 0.24. Another candidate is the Sr2Ir1−xCoxO4 system. Based on first principle calculations for Sr2Ir0.5Co0.5O4, it was inferred that Co3+/Ir5+ charge partitioning is energetically stable42, which was confirmed by subsequent experiments on this material43,44,45. On the other hand, more dilute Co substitutions have not been investigated in much detail yet, although it is already known that even moderate Co substitution levels (x ≤ 0.1) are not sufficient to reduce TN appreciably46. In this work, we investigate the charge transport, magnetic, structural, and vibrational properties of Sr2Ir0.95Co0.05O4 (SICO). We demonstrate that this material shows charge transport quantum critical behavior that is consistent with a simple picture where the Co3+ acceptor level coincides with the top of the lower Hubbard band at EF (see Fig. 1c), triggering QCF with remarkably large renormalized masses.
Results
Structural characterization
X-ray powder diffraction profiles of SICO and SIO are shown for a selected angular interval in Fig. 2a, b, respectively. The whole profiles are shown in the Supplementary Figs. S1 and S2. Our data show asymmetric Bragg peak lineshapes in SICO (see Fig. 2b), revealing stacking faults47. This is likely caused by the random contribution to the interatomic elastic potencial caused by the Co substitution in SICO, disturbing the long-range ABCD stacking pattern of SIO (see Fig. 1a). The internal structural integrity of the layers is investigated by vibrational spectroscopy. Raman spectra of both samples are shown in Fig. 2c at T = 20 K. The main observed phonon modes, labeled as M1 − M426, show similar positions and lineshapes for both compounds, being only slightly broader for SICO. An additional feature is observed at ~340 cm−1 in SIO, indicative of a stoichiometric sample48,49, whereas in SICO this feature is washed out and broad additional signals are observed at ~260 and ~420 cm−1. The 260 cm−1 peak was previously observed and becomes stronger in more disordered samples48,49. The weak intensity of the additional Raman features associated with disorder and the relatively sharp M1 − M4 modes in SICO indicate that the individual layer structures are preserved to a large extend through the 5% Co substitution, in contrast to the Sr2Ir1−xRuxO4 series that shows much larger modifications in the phonon Raman spectra even at low doping levels49.
Charge transport at zero magnetic field
The electrical resistivity curves ρ(T) of SIO and SICO are shown in Fig. 3a. The values of ρ(T) are significantly reduced for SICO with respect to the parent compound. In addition, the temperature dependence of the former is remarkably well captured by a simple power-law behavior, ρ(T) = A−1 ⋅ T−x with x = 1.075(1), over the entire investigated temperature interval 3 < T < 300 K (dashed line in Fig. 3a). Such power-law behavior is not found in SIO (see Supplementary Fig. S3). Figure 3b displays the same data in terms of electrical conductivity σ(T) in a double-log scale for SICO only. The fit to the low-temperature data (T < 6 K) is optimized by a slightly different exponent x = 1.003(6) that is even closer to unity. Note that the positive exponent implies that σ → 0 as T → 0, i.e., the material is nonmetallic. On the other hand, an exponential behavior \(\sigma (T)\propto \exp [-{({T}_{0}/T)}^{\alpha }]\) is expected for insulating materials, with 1/4 ≤ α ≤ 1 for either a bandgap insulator (α = 1) or for a variable range hopping mechanism where the specific α is defined by the system dimensionality and the specific energy-dependence of the density of states n(E) near EF50. Neither of such exponential behaviors for σ(T) are observed for SICO (see Supplementary Fig. S4), so this material is not classified either as a Mott, Slater or an Anderson insulator. Actually, according to very general scaling considerations, a power-law behavior σ(T) ∝ Tx signals a metal-insulator quantum phase transition22. The positive exponent contrasts with the negative values found in metallic materials where the quantum criticality is not due to the proximity of a metal-insulator transition but interfaces two different conducting states, such as in a magnetic/heavy fermion quantum phase transition51,52. The specific value x ~ +1 for SICO must be captured by an appropriate microscopic model (see below).
Magnetic properties and magnetoresistance
Magnetization M(T) curves of SICO and SIO are shown in Fig. 4a, taken on warming after zero-field cooling and warming after field cooling, with H = 5 kOe. Both compounds order at TN ~ 240 K, in line with ref. 46. The shapes of the M(T) curves of SIO and SICO are distinct and the magnetization values are substantially reduced by the Co substitution. The latter result either indicates that the Co moments partially compensate the Ir net moments or the magnetic canting angle of the Ir moments (see Fig. 1b) is reduced for SICO. Also, both materials feature a separation of the zero-field cooling and warming after zero-field cooling curves that becomes more prominent below T ~ 100 K53. This is understood in terms of a field-induced transition of the ↓↑↑↓ magnetic structure and symmetry-related domains at zero-field to ↑↑↑↑ under an applied field along the ab-plane Hab ~ 2 kOe16,48,54. In a polycrystal, the Ha projection is different for each crystallite, and with an external field H = 5 kOe a substantial fraction of the crystallites will still have Ha < 2 kOe, leading to a coexistence of different phases at low temperatures in proportions that are arguably sensitive to the thermomagnetic sample history. This is manifested not only in the different zero-field cooling and warming after zero-field cooling M(T) curves, but also in the hysteresis of the isothermal M(H) curves (see Fig. 4b and ref. 13).
Figure 4c shows the magnetoresistance of SIO and SICO at T = 60 K taken after zero-field cooling (see Supplementary Fig. S5 for magnetoresistance at other temperatures). SIO shows a substantial negative magnetoresistance of ~9% for H = 35 kOe. A field-hysteretic behavior is also observed. This phenomenon is again originated in the field-induced transition between the ↓↑↑↓ and ↑↑↑↑ structures, where the former is substantially more resistive20. Remarkably, the initial high-resistance state is not recovered by cycling the field. This is likely due to a powder distribution of internal fields that are created after the ↑↑↑↑ state is first activated, which may prevent the homogeneous high-resistance ↓↑↑↓ state to be simultaneously recovered over the entire sample volume. The magnetoresistance of SICO is largely suppressed with respect to SIO (see Fig. 4c), remaining below 1% up to H = 35 kOe. This indicates that, for SICO, the additional electronic scattering channel introduced by the Co impurities reduces the mean-free path of the thermally-activated charge carriers, overwhelming the magnetic scattering channel that is responsible for the large magnetoresistance of SIO. We therefore estimate that the electronic mean free path of SICO is D ~ 8 Å, which is the average separation between the Co scattering centers for 5% substitution. We should note that in SIO the conductivity in the ab plane is higher than along c20,55. Thus, in polycrystals the resistivity and magnetoresistance curves are presumably dominated by the charge transport in the ab plane. This is also likely valid for SICO, although this assumption is not essential for the conclusions of this work.
Electron-phonon and pseudospin-phonon couplings
We now return to a more detailed investigation of the Raman spectra (Fig. 2c and Supplementary Fig. S6). The M1 lineshape of SICO is fitted to the Fano expression I(ω) = I0(q + ϵ)2/(1 + ϵ2), where I0 is the intensity, ϵ = (ω − ω0)/Γ, ω0 and Γ are the phonon frequency and linewidth, respectively, and 1/q is the asymmetry parameter that measures the coupling of the phonons with the electronic continuum56 (see Fig. 5a). In opposition to SICO, the M1 lineshape for SIO is symmetric at low temperatures, in agreement with previous studies57,58. Figure 5b shows the temperature dependence of ∣1/q∣ for mode M1 of SICO. A substantial asymmetry parameter ∣1/q∣ = 0.15 is observed at the base temperature. This reveals a continuum of low-energy excitations at T → 0 that is not present in SIO. Considering that a hypothetical metallic state in SICO is dismissed by resistivity data, this result indicates that the insulating gap in SICO must be below ~0.02 eV, placing this material very close to a quantum critical point. The ∣1/q∣ parameter tends to increase on warming, with anomalies at T ~ 100 K and ~TN. In particular, the anomaly at T ~ 100 K suggests there is another physically meaningful temperature below TN for SICO, as previously inferred for SIO12,20,53,59,60. The reduced magnetization below ~100 K also supports this conclusion (see Fig. 4a).
Figure 5c shows the temperature dependence of the frequency of the M3 mode for SIO and SICO fitted with Lorentzian lineshapes (∣1/q∣ = 0), in comparison to the expected anharmonic behavior \({{\Delta }}{\omega }_{\text{anh}}(T)=A[1+2/({{\rm{e}}}^{\hslash {\omega }_{0}/2{k}_{\text{B}}T}-1)]\)61. Both compounds show anomalous shifts of this mode below TN. This result is ascribed to the pseudospin-phonon coupling effect62,63,64. The anomalous hardenings after subtraction of the anharmonic term are shown in Fig. 5d. The magnitude of the pseudospin-phonon anomaly is not reduced for SICO in comparison to SIO, indicating that the microscopic magnetic network of Ir pseudospins is still well preserved in SICO. The other M1 − M4 phonon parameters are shown in the Supplementary Fig. S7.
Discussion
We propose the schematic energy diagram displayed in Fig. 1c to explain our experimental results. The quantum critical point occurs as the localized Co3+ acceptor level matches the top of the lower Hubbard band at EF. At low temperatures, the Co3+ acceptor level is empty, thus the nominal oxidation state is Co4+ and no charge carrier is present. Upon warming, such impurity level becomes gradually occupied by the electrons originated from the lower Hubbard band due to the thermal energy, shifting the Co oxidation state towards the Co3+ side and hole-doping the lower Hubbard band. The density of states of the lower Hubbard band nearby EF is
where \(E^{\prime} \equiv | E-{E}_{\text{F}}|\) and m* is the lower Hubbard band effective mass65. The number of thermally-activated holes per unit volume at low temperatures is
where Γ(u) is the gamma function. These carriers have mean energy \(\bar{E}(T)=3{k}_{\text{B}}T/2\). We now treat these thermally-activated holes semiclassically with a renormalized mass mren that is not necessarily equal to m*. The time between collisions is
where D is the carrier mean free path. From the Drude relation σ(T) = q2N(T)τ/mren, where q is the electron charge, we obtain
Thus, this simple model is able to reproduce the observed power-law behavior for the electrical conductivity σ(T) = ATx with the correct exponent x = 1. Also, the experimental coefficient A = 0.315Ω−1 m−1 K−1 (see Fig. 3b) can be used to obtain further information on
Using D ~ 8 Å (see above) and considering that m* > me, we obtain mren ≳ 700 me, where me is the free electron mass ! Such a huge estimated renormalized mass is indicative of heavy-fermion physics. Indeed, the energy diagram displayed in Fig. 1c, with a localized impurity level near EF, suggests an analogy with heavy-fermion materials with localized 4f levels near EF. The important difference here is that the “conduction electrons” are actually thermally-excited QCF. The absence of charge carriers as T → 0 means there is no Sommerfeld coefficient γ for the specific heat cP(T) associated with the QCF captured by our model. Rather, the low-temperature cP(T) from the QCF should actually scale with \(d[N(T)\bar{E}(T)]/dT\propto {T}^{3/2}\), possibly mixing with magnon contributions. These considerations imply that the linear σ(T) curve presented here is likely the most direct macroscopic manifestation of the QCF in SICO.
The observation of QCF in SICO, with similar TN ~ 240 K and pseudospin-phonon coupling strength in comparison to SIO, demonstrates that the quantum critical points associated with the charge transport and magnetic transitions are distinct in these iridates. This is reasonable once a non-zero density of charge carriers is presumably necessary to destroy the magnetic ordering at T = 0 K. The thermally-activated holes possess charge and spin–orbital degrees of freedom, and this system offers an opportunity to access the resulting QCF in the magnetically ordered regime.
Conclusion
In summary, a detailed analysis of our electrical resistivity and Raman scattering data uncovers the presence of QCF in SICO. The inferred quantum phase transition is related to the crossing of the Co3+ acceptor level with the top of the lower Jeff = 1/2 band at EF. The linear behavior observed in σ(T) is captured by a Drude-like semiclassical model that indicates a large renormalized electron mass for the thermally-activated charge carriers.
Methods
Sample synthesis
The Sr2IrO4 (SIO) and Sr2Ir0.95Co0.05O4 (SICO) polycrystalline samples were synthesized by a standard solid-state reaction method employing high-purity SrCO3, IrO2 and CoO as described in ref. 26. Since the reagents are mixed in stoichiometric proportions, this method leaves minimum margin for compositional Sr/Ir/Co variations, which is critical for the conclusions of this work. Also, the large absolute resistivity values at low temperatures of SIO, and especially the large low-T/high-T ratio ρ(50 K)/ρ(300 K) ~ 104 (see Fig. 3a) compares to the highest reported values in the literature30, unfavoring the possibility of any relevant doping due to off-stoichiometric oxygen content in this sample. This conclusion is likely extensible to SICO, considering that both samples were synthesized by the same procedure.
X-ray diffraction and energy-dispersive X-ray spectroscopy
Laboratory X-ray diffraction data were taken in a Bruker D2 diffractometer equipped with a linear detector, employing Cu Kα radiation (λ = 1.542 Å). Rietveld refinements were performed with the GSAS-II suite66. The refined Co occupancy at the Ir site is 4.2(7)% for SICO, close to the 5% nominal value. The other refined crystallographic parameters are given in the Supplementary Table S1. Energy-dispersive X-ray spectroscopy measurements were performed on two different spots of SICO using a scanning electron microscope FEI Nanolab 200 and confirm a homogeneous Co concentration of 5(1)%. Synchrotron X-ray powder diffraction measurements at ambient temperature were also carried out at the XDS beamline of the Brazilian Synchrotron Light Laboratory (LNLS)67 with λ = 0.61986 Å employing the experimental setup described in ref. 27. The structure illustrations in Fig. 1 were produced with the aid of the program VESTA68.
Electrical and magnetic measurements
Electrical resistivity and magnetoresistance were measured using a standard four-point technique with a dc bridge in an applied magnetic field up to H = 90 kOe in a commercial system. The dc-magnetization measurements were performed with a Superconducting Quantum Interference Device magnetometer (SQUID) and a SQUID with a Vibrating Sample Magnetometer (SQUID-VSM).
Raman scattering
Raman scattering experiments were performed in a quasi-backscattering geometry using the 488.0 nm line of Ar+ laser with focus spot size ~50 μm. The laser power was kept below 20 mW. A Jobin-Yvon T64000 triple-grating spectrometer with 1800 mm−1 gratings was employed. A LN2-cooled multichannel charge-coupled device was used to collect and process the scattered data. The sample was mounted on a cold finger of closed-cycle He cryostat with base temperature 20 K.
Data availability
The authors declare that the main data supporting the findings of this study are available within the article and its Supplementary Information file. Extra data are available from the corresponding author upon reasonable request.
References
Okamoto, Y., Nohara, M., Aruga-Katori, H. & Takagi, H. Spin-liquid state in the S = 1/2 hyperkagome antiferromagnet Na4Ir3O8. Phys. Rev. Lett. 99, 137207 (2007).
Jackeli, G. & Khaliullin, G. Mott insulators in the strong spin-orbit coupling limit: from Heisenberg to a quantum compass and Kitaev models. Phys. Rev. Lett. 102, 017205 (2009).
Price, C. C. & Perkins, N. B. Critical properties of the Kitaev-Heisenberg model. Phys. Rev. Lett. 109, 187201 (2012).
Singh, Y. et al. Relevance of the Heisenberg-Kitaev model for the honeycomb lattice iridates A2IrO3. Phys. Rev. Lett. 108, 127203 (2012).
Wang, F. & Senthil, T. Twisted Hubbard model for Sr2IrO4: Magnetism and possible high temperature superconductivity. Phys. Rev. Lett. 106, 136402 (2011).
Watanabe, H., Shirakawa, T. & Yunoki, S. Monte Carlo study of an unconventional superconducting phase in iridium oxide Jeff = 1/2 mott insulators induced by carrier doping. Phys. Rev. Lett. 110, 027002 (2013).
Meng, Z. Y., Kim, Y. B. & Kee, H.-Y. Odd-parity triplet superconducting phase in multiorbital materials with a strong spin-orbit coupling: Application to doped Sr2IrO4. Phys. Rev. Lett. 113, 177003 (2014).
Kim, Y. K. et al. Fermi arcs in a doped pseudospin-1/2 Heisenberg antiferromagnet. Science 345, 187–190 (2014).
Yan, Y. J. et al. Electron-doped Sr2IrO4: an analogue of hole-doped cuprate superconductors demonstrated by scanning tunneling microscopy. Phys. Rev. X 5, 041018 (2015).
Kim, Y. K., Sung, N. H., Denlinger, J. D. & Kim, B. J. Observation of a d-wave gap in electron-doped Sr2IrO4. Nature Physics 12, 37–41 (2016).
Cao, G. et al. Electrical control of structural and physical properties via strong spin-orbit interactions in Sr2IrO4. Phys. Rev. Lett. 120, 017201 (2018).
Ye, F., Hoffmann, C., Tian, W., Zhao, H. & Cao, G. Pseudospin-lattice coupling and electric control of the square-lattice iridate Sr2IrO4. Phys. Rev. B 102, 115120 (2020).
Crawford, M. K. et al. Structural and magnetic studies of Sr2IrO4. Phys. Rev. B 49, 9198–9201 (1994).
Huang, Q. et al. Neutron powder diffraction study of the crystal structures of Sr2RuO4 and Sr2IrO4 at room temperature and at 10 K. Journal of Solid State Chemistry 112, 355–361 (1994).
Moon, S. J. et al. Dimensionality-controlled insulator-metal transition and correlated metallic state in 5d transition metal oxides Srn+1IrnO3n+1 (n = 1, 2, and ∞). Phys. Rev. Lett. 101, 226402 (2008).
Kim, B. J. et al. Phase-sensitive observation of a spin-orbital Mott state in Sr2IrO4. Science 323, 1329–1332 (2009).
Arita, R., Kuneš, J., Kozhevnikov, A. V., Eguiluz, A. G. & Imada, M. Ab initio studies on the interplay between spin-orbit interaction and coulomb correlation in Sr2IrO4 and Ba2IrO4. Phys. Rev. Lett. 108, 086403 (2012).
Ye, F. et al. Magnetic and crystal structures of Sr2IrO4: a neutron diffraction study. Phys. Rev. B 87, 140406 (2013).
Boseggia, S. et al. Locking of iridium magnetic moments to the correlated rotation of oxygen octahedra in Sr2IrO4 revealed by X-ray resonant scattering. Journal of Physics: Condensed Matter 25, 422202 (2013).
Ge, M. et al. Lattice-driven magnetoresistivity and metal-insulator transition in single-layered iridates. Phys. Rev. B 84, 100402 (2011).
Wang, J. C. et al. Decoupling of the antiferromagnetic and insulating states in Tb-doped Sr2IrO4. Phys. Rev. B 92, 214411 (2015).
Dobrosavljevic, V., Trivedi, N. & Valles, J. M. Conductor-Insulator Quantum Phase Transitions. (Oxford University Press, 2012).
Sachdev, S. Quantum magnetism and criticality. Nat. Phys. 4, 173–185 (2008).
Haskel, D. et al. Pressure tuning of the spin-orbit coupled ground state in Sr2IrO4. Phys. Rev. Lett. 109, 027204 (2012).
Zocco, D. A. et al. Persistent non-metallic behavior in Sr2IrO4 and Sr3Ir2O7 at high pressures. J. Phys. 26, 255603 (2014).
Samanta, K., Ardito, F. M., Souza-Neto, N. M. & Granado, E. First-order structural transition and pressure-induced lattice/phonon anomalies in Sr2IrO4. Phys. Rev. B 98, 094101 (2018).
Samanta, K., Tartaglia, R., Kaneko, U. F., Souza-Neto, N. M. & Granado, E. Anisotropic lattice compression and pressure-induced electronic phase transitions in Sr2IrO4. Phys. Rev. B 101, 075121 (2020).
Haskel, D. et al. Possible quantum paramagnetism in compressed Sr2IrO4. Phys. Rev. Lett. 124, 067201 (2020).
Chen, C. et al. Persistent insulating state at megabar pressures in strongly spin-orbit coupled Sr2IrO4. Phys. Rev. B 101, 144102 (2020).
Klein, Y. & Terasaki, I. Insight on the electronic state of Sr2IrO4 revealed by cationic substitutions. J. Phys. 20, 295201 (2008).
Qi, T. F. et al. Spin-orbit tuned metal-insulator transitions in single-crystal Sr2Ir1−xRhxO4 (0 ≤ x ≤ 1). Phys. Rev. B 86, 125105 (2012).
Clancy, J. P. et al. Dilute magnetism and spin-orbital percolation effects in Sr2Ir1−xRhxO4. Phys. Rev. B 89, 054409 (2014).
Ye, F. et al. Structure symmetry determination and magnetic evolution in Sr2Ir1−xRhxO4. Phys. Rev. B 92, 201112 (2015).
Brouet, V. et al. Transfer of spectral weight across the gap of Sr2IrO4 induced by La doping. Phys. Rev. B 92, 081117 (2015).
Chikara, S. et al. Sr2Ir1−xRhxO4(x < 0.5): An inhomogeneous \({j}_{{\rm{eff}}}=\frac{1}{2}\) Hubbard system. Phys. Rev. B 92, 081114 (2015).
Cao, Y. et al. Hallmarks of the Mott-metal crossover in the hole-doped pseudospin-1/2 Mott insulator Sr2IrO4. Nat. Commun. 7, 11367 (2016).
Sohn, C. H. et al. X-ray absorption spectroscopy study of the effect of Rh doping in Sr2IrO4. Sci. Rep. 6, 23856 (2016).
Chikara, S. et al. Charge partitioning and anomalous hole doping in Rh-doped Sr2IrO4. Phys. Rev. B 95, 060407 (2017).
Louat, A. et al. Formation of an incoherent metallic state in Rh-doped Sr2IrO4. Phys. Rev. B 97, 161109 (2018).
Xu, B. et al. Optical signature of a crossover from Mott- to Slater-type gap in Sr2Ir1−xRhxO4. Phys. Rev. Lett. 124, 027402 (2020).
Zwartsenberg, B. et al. Spin-orbit-controlled metal-insulator transition in Sr2IrO4. Nat. Phys. 16, 290–294 (2020).
Ou, X. & Wu, H. Coupled charge-spin-orbital state in Fe- or Co-doped Sr2IrO4. Phys. Rev. B 89, 035138 (2014).
Mikhailova, D. et al. Charge transfer and structural anomaly in stoichiometric layered perovskite Sr2Co0.5Ir0.5O4. Eur. J. Inorg. Chem. 2017, 587–595 (2017).
Chin, Y.-Y. et al. Relation between the Co-O bond lengths and the spin state of Co in layered cobaltates: a high-pressure study. Sci. Rep. 7, 3656 (2017).
Agrestini, S. et al. Probing the Jeff = 0 ground state and the Van Vleck paramagnetism of the Ir5+ ions in layered Sr2Co0.5Ir0.5O4. Phys. Rev. B 97, 214436 (2018).
Gatimu, A. J., Berthelot, R., Muir, S., Sleight, A. W. & Subramanian, M. Synthesis and characterization of Sr2Ir1-xMxO4 (M=Ti, Fe, Co) solid solutions. J. Solid State Chem. 190, 257–263 (2012).
Estevez-Rams, E., Leoni, M., Scardi, P., Aragon-Fernandez, B. & Fuess, H. On the powder diffraction pattern of crystals with stacking faults. Philosophical Magazine 83, 4045–4057 (2003).
Sung, N. H. et al. Crystal growth and intrinsic magnetic behaviour of Sr2IrO4. Philosophical Magazine 96, 413–426 (2016).
Glamazda, A. et al. Effects of hole doping on magnetic and lattice excitations in Sr2Ir1−xRuxO4 (x = 0 − 0.2). Phys. Rev. B 89, 104406 (2014).
Mott, N. Conduction in Non-Crystalline Materials. (Oxford: Clarendon Press, 1993).
Schlottmann, P. Non-Fermi liquid behavior in heavy fermion systems. vol. 23 of Handbook of Magnetic Materials, 85–160 (Elsevier, 2015). https://www.sciencedirect.com/science/article/pii/B9780444635280000024.
Paschen, S. & Si, Q. Quantum phases driven by strong correlations. Nat. Rev. Phys. 3, 9–26 (2021).
Bhatti, I. N., Rawat, R., Banerjee, A. & Pramanik, A. K. Temperature evolution of magnetic and transport behavior in 5d Mott insulator Sr2IrO4: significance of magneto-structural coupling. J. Phys. 27, 016005 (2014).
Porras, J. et al. Pseudospin-lattice coupling in the spin-orbit Mott insulator Sr2IrO4. Phys. Rev. B 99, 085125 (2019).
Cao, G., Bolivar, J., McCall, S., Crow, J. E. & Guertin, R. P. Weak ferromagnetism, metal-to-nonmetal transition, and negative differential resistivity in single-crystal Sr2IrO4. Phys. Rev. B 57, R11039–R11042 (1998).
Fano, U. Effects of configuration interaction on intensities and phase shifts. Phys. Rev. 124, 1866–1878 (1961).
Gretarsson, H. et al. Two-magnon Raman scattering and pseudospin-lattice interactions in Sr2IrO4 and Sr3Ir2O7. Phys. Rev. Lett. 116, 136401 (2016).
Cetin, M. F. et al. Crossover from coherent to incoherent scattering in spin-orbit dominated Sr2IrO4. Phys. Rev. B 85, 195148 (2012).
Chikara, S. et al. Giant magnetoelectric effect in the \({J}_{{\rm{eff}}}=\frac{1}{2}\) Mott insulator Sr2IrO4. Phys. Rev. B 80, 140407 (2009).
Bhatti, I. N. & Pramanik, A. Insight into the magnetic behavior of Sr2IrO4: a spontaneous magnetization study. Phys. Lett. A 383, 1806–1809 (2019).
Balkanski, M., Wallis, R. F. & Haro, E. Anharmonic effects in light scattering due to optical phonons in silicon. Phys. Rev. B 28, 1928–1934 (1983).
Baltensperger, W. & Helman, J. S. Influence of magnetic order in insulators on optical phonon frequency. Helv. Phys. Acta 41, 668 (1968).
Granado, E. et al. Magnetic ordering effects in the Raman spectra of La1-xMn1-xO3. Phys. Rev. B 60, 11879–11882 (1999).
Samanta, K., Rigitano, D., Pagliuso, P. G. & Granado, E. Isospin-phonon coupling and Fano-interference in spin-orbit Mott insulator Sr2IrO4. Appl. Phys. Lett. 114, 152402 (2019).
Ashcroft, N. W. & Mermin, N. D. Solid State Physics (Harcourt College Publishers, 1976).
Toby, B. H. & Von Dreele, R. B. GSAS-II: the genesis of a modern open-source all purpose crystallography software package. J. Appl. Crystallogr. 46, 544–549 (2013).
Lima, F. A. et al. XDS: a flexible beamline for X-ray diffraction and spectroscopy at the Brazilian synchrotron. J. Synchrotron Radiat. 23, 1538–1549 (2016).
Momma, K. & Izumi, F. VESTA3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Crystallogr. 44, 1272–1276 (2011).
Acknowledgements
We would like to acknowledge M. A. Avila for providing assistance in the SQUID-VSM measurements. This work was supported by Fapesp Grants 2016/00756-6, 2017/10581-1, 2018/20142-8, 2018/11364-7, and 2018/18653-4, as well as CNPq Grants 308607/2018-0, 304496/2017-0, and 409504/2018-1, Brazil. LNLS is acknowledged for the concession of beamtime. The authors also acknowledge the Center for Semiconducting Compounds and Nanotechnologies (CCS) at UNICAMP for providing the equipment and technical support for the energy-dispersive X-ray spectroscopy measurements.
Author information
Authors and Affiliations
Contributions
K.S., J.C.S., P.G.P., and E.G. conceived the experiments. Experimental data were taken by K.S., J.C.S., D.R., and A.I.M. under supervision of P.G.P. and E.G. Data analysis was performed by K.S., J.C.S., A.I.M., and E.G. The model was developed by E.G. The paper was written by K.S. and E.G. with input from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Samanta, K., Souza, J.C., Rigitano, D. et al. Quantum criticality in a layered iridate. Commun Phys 4, 89 (2021). https://doi.org/10.1038/s42005-021-00591-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s42005-021-00591-7
- Springer Nature Limited
This article is cited by
-
Effects of the on-site energy on the electronic response of Sr3(Ir1−xMnx)2O7
Scientific Reports (2022)