Abstract
Despite many efforts, the outcomes obtained with field-assisted processing of materials still rely on long-term coupling with other electroless processes. This conceals the efficacy and the intrinsic contributions of electric current. A new device utilizing electrical nano pulsing (ENP) has been designed and constructed to bring quasi-instantaneous modifications to the micro- and nano-structure in materials. Featuring ultra-high intensity (~ 1011 A/m2) and ultra-short duration (< 1 μs), the ENP technology activates non-equilibrium structural evolutions at nanometer spatial scale and nanosecond temporal scale. Several examples are provided to demonstrate its utility far outpacing any conventional materials processing technology. The ENP technology gives a practical tool for exploring the intrinsic mechanism of electric-field effects and a pathway towards the rapid industrial manufacturing of materials with unique properties.
Similar content being viewed by others
Introduction
One of the permanent missions for materials science community is to persistently improve the microstructure of various material systems and obtain expected mechanical or functional properties required by specific application scenarios1,2,3. Given this, a steady stream of research has been emerging for the development of innovative processing technologies, such as field-assisted sintering4, ionic liquids5, ion beam modification6, 3D printing7, surface modification8, etc. Conventional thermal treatment is still showing impressive potential for properties improvement9, phase regulation10, grain refinement11, etc. However, the long processing duration is a particularly problematic concern in the exploration of advanced treatment technologies. The physical field-involved treatment techniques are appealing in achieving the alteration of surface morphology of materials, like the inorganic layer on electrolyte surface by plasma electrolytic oxidation12 and the textured thin layer on metal surface by direct laser interference lithography13. However, few breakthroughs have been made on controls at deeper spatial scale or shorter time scale and they are generally material specific.
As a ubiquitous physical phenomenon both in natural and artificial environments, electric field has been employed in many modern engineering fields to develop high-performance materials with unique functional and structural properties. Active research on electrically assisted treatment of solid materials started from the discovery of electroplastic effect14. Later, fast-sintering technologies were proposed for powder materials manufacturing, such as flash sintering (FS)15, ultra-fast high temperature sintering (UHS)16 and spark plasma sintering (SPS)4,17. Typical electric field-assisted material processing techniques are generally benefiting from high heating rate and high temperature due to Joule-heating effect. Nevertheless, the pulsed electric current, a type of instantaneous current whose amplitude changes suddenly and periodically over time, is characterized by its distinctive electric stimulus on altering the microstructure and properties of parts4,18,19. Compared with continuous electric current, millisecond electric pulses can produce better electroplastic behavior by activating the dislocation reconfiguration in Ti–Al alloy, thereby increasing its tensile elongation and maximum strength20. The reduced critical nucleation radius by sub-millisecond electric pulses can generate recrystallization behavior and better plasticity in pure nickel wires subjected to thermomechanical torsion deformation21. The industrial-scale application of SPS equipment has also proven the success of millisecond-level electric pulse in promoting the densification of porous body4. Beyond these, microsecond electric pulses22 contribute to the microstructure refinement and strengthening in cast TC4 titanium-based alloy by promoting the formation of new β phase morphology during thermal-hydrogen treatment23. Due to the accelerated hydrogen diffusion by introducing electrical free energy, microsecond electric pulses can even be employed for the de-hydrogenation in steels and their ductility recovery under tensile deformation24,25. Furthermore, low-intensity nanosecond electric pulses can find their biological applications in the modulation of cytoplasmic ion concentration of cancerous cells26 and the electric excitation of skin neurons27. In fact, electric pulsing processing of conductive materials is often combined with other electroless processes, rather than being treated as a stand-alone treatment. This may complicate the argument that the conventional processes, such as mechanical deformation or chemical diffusion, can produce synergistically enhanced or destructive outcomes when combined with electrical pulses. Although the field effect is reported to be more significant with more intense electric field28,29, the intrinsic influences of electrical pulses on microstructural modifications are difficult to intuitively highlight in this case. Moreover, short-duration electric pulse with the ON-phase period down to milli- or microseconds has been widely applied to many conductive material systems, but the entire process often does not last on the same but a much longer time scale30. Single or multiple low-intensity electrical pulses often fail to trigger the anticipated modification results, whereas the detectable outcomes rely on the energy accumulation from massive low-frequency electric bursts. This becomes an obstacle to the reliable high-throughput materials processing unless high current intensity, high frequency and short pulse duration can be acquired simultaneously in the electric pulsing technology. Therefore, constructing the high-energy electric micro-nano pulsing technology with desirable output characteristics and utilizing its thermal and/or electric field effects for quasi-instantaneous materials processing should exhibit attractive scientific significance and industrial potential.
Here we introduce a unique electric pulsing treatment method based on the fast capacitor discharging technique, called electric nano pulsing (ENP) technology, featuring ultra-high voltage (up to 1000 V), ultra-high current density (up to 1011–1012 A/m2), ultra-short pulse duration (less than 1 μs) and ultra-high pulsing frequency (up to 100 kHz). The high intensity impulse current released into polycrystalline materials within the micro-nano seconds enable the extremely rapid Joule heating effect and the ultra-strong electric field effect, thereby having the ability to activate the non-equilibrium structural evolutions of both grain boundaries (GBs) and grain insides (GIs) at nanometer spatial scale and nanosecond temporal scale. This is far more advanced than existing conventional electric pulsing treatment.
Materials and methods
The design and performance of ENP device
The schematics of the ENP device is shown in Fig. 1A, with a diagram (Fig. 1B) briefly clarifying its electric circuit features. The DC power supplier enables the energy storage of integrated power module (IPM) through high voltage electricity up to 1000 V, and the energy release can be triggered by pulse signal generator outputting the ultra-short square wave signal ranging from 100 ns to a few hundreds of microseconds. The flexibly customized design of IPM (EHT Inc., Seattle, USA) mainly contains fast capacitors with solid-state switch, which allows the achievement of ultra-short rise or fall time of a high-intense electric current pulsing. In the ENP device, a group of parallel constant resistances (~ 95 mΩ) are embedded on printed circuit board (PCB) board for over current protection, and its total inductance is 22.5 nH. Two types of sample setups are designed for experimentations, named “bus-bar” and “through-hole” respectively. The fine wires or thin flakes can be attached directly to the fixed upper/lower electrodes 3.5 mm apart in “bus-bar” setup; alternatively, the rods can be connected to the fixed electrodes distributed on both sides of the PCB by the pressure exerted by the soldered fasteners in “through-hole” setup. Given that the ENP device exhibits great flexibility in the sample-electrode configurations, materials processing for both powders and bulks is highly possible for various practical purposes with the support of IPM component. The proposed ENP technology in this work has an intensity 101–102 times stronger than other existing electric pulsing techniques, whilst simultaneously has a distinctive nanosecond level pulsing duration14,20,21,23,24,25,31,32,33,34,35,36,37,38,39,40,41,42,43,44,45,46,47. With the fast-discharging technology, the current density in the ENP device can be excited to hundreds of billions of Amps per square meter within 100 ns, based on the front edge of output pulsing signals in Fig. 1C and D. Its reliability is thus guaranteed by the capability of providing precise and stable ultra-short current pulsing. The seconds-level EP techniques are often unattractive with very long duration and low intensity. Although milli-EP and micro-EP technologies have seen improvements in current intensity, they still have not gotten rid of the low frequency limit (generally much less than 103 Hz) (Fig. 1E). On the premise of improving current intensity, the ENP technology has further increased the pulse frequency by two orders of magnitude, reaching an extraordinary 105 Hz. These excellent features can also inspire a whole new concept of material processing, namely, the ENP-assisted instantaneous modification of localized material microstructures (surface, GBs or GIs). The principle of ENP processing is that quasi-instantaneous materials processing can be achieved by applying the high frequency electric pulsing with ultra-high current intensity and ultra-short pulsing duration. The ultra-high current intensity is in favor of emphasizing the contribution of field effects, whilst the ultra-short pulsing duration ensures the availability of quasi-instantaneous processing and avoids the negative effects of excessive Joule heating. Figure 1D and G display some images of exemplary materials during or after ENP processing. Apparently, the proposed ENP technology is capable of both the electrically stimulated treatment of materials under short-duration pulses and the rapid thermal treatment under high-frequency pulses. The resulting non-equilibrium microstructural evolution in the localized regions of materials and the accompanying other phenomena possibly can be drastically enhanced compared to the conventional techniques, which are the attractive scientific topics in the future.
Materials and experimental procedure of ENP processing
The commercial AWG26 Ni-based superalloy wire (softening annealed; 80Ni–18.5Cr–1.5Si in wt%; D = 403.9 μm; FCC lattice with a = 0.3539 nm) is used as target material. The quasi-instantaneous processing on both localized surface and interior of this superalloy is explored based on the ENP technology. Ni-based superalloys with good mechanical performance and oxidation resistance are one of the most extensively studied superalloys and have wide industrial applications at high temperature environments48. This Ni–Cr–Si superalloy wire has good electric conductivity (84 mΩ/cm) at room temperature and low temperature coefficient of resistance (8.5 × 10–5/K), which ensure it to be a suitable material in ENP processing. A 12 mm-length Ni–Cr–Si superalloy wire was installed in the “bus-bar” setup, with alumina ceramic flake pressed onto it for ideal electrode-sample contact. The total resistance of the whole sample setup is measured to be ~ 80.5 mΩ. The fast capacitor was charged at an input voltage of 600 V. The high-intensity electric pulsing with an input signal duration of 1 μs and an ON-to-OFF pattern of 1:9 (10% duty cycle) was released into the wire in the air atmosphere. Therefore, one pulsing signal was sent to the target material every 10 μs, and the pulse frequency is 100 kHz accordingly. A total of eight pulses were generated and the whole processing time was 80 μs. Once the electric pulses were triggered, the entire processing could happen suddenly. The current density profile of one of output pulsing signals is shown in Fig. 1C. The peak current density along the wire can reach 3.15 × 1010 A/m2, which is sufficiently high to bring instantaneous modification to the material microstructure. Another ENP processing with a total of two pulses at a frequency of 100 kHz and a peak current density of 6.98 × 1010 A/m2 was conducted as well. In this work, the rationale for selecting those parameters is that under the premise of ensuring short duration and high intensity, ultra-fast processing can be applied to make the temperature of this superalloy exactly reach its melting point. The estimation of the skin depth in this pulsing condition (~ 523 μm) indicates a uniform current and temperature distributions across the wire cross-section. This estimation is confirmed in the next section by modeling results of the temperature distribution in this wire. For comparison, the conventional heating of identical nichrome wires was conducted by placing them into an atmospheric furnace preset at 1400 °C (melting point) for 10 s. The capability of the ENP technology goes beyond the rapid surface modification, whilst its role in tailoring the GBs morphology and the GIs defects should not be underestimated49. Here we provide some straightforward examples on the quasi-instantaneous localized processing of the surface thin oxidation coating as well as the internal dislocation hardening in this conductive material.
Modeling of temperature field on Nichrome alloy during ENP processing
The uniformity of the heating depends on the magnitude of the skin effect, which, in turn, is a function of the shape and periodicity of electric pulses. Experimental measurement of the temperature evolution during electrical nano pulsing is a significant challenge. In our experiments, temperature was estimated numerically based on the known electrical current pulse shapes and duty cycle. The shape of the electrical current pulses used in this experiment with nichrome wire is shown in Fig. 1C. The evolution of electric field strength across the wire cross-section follows the equation50:
where \(\rho = r/R\) and \(\tau = t/\tau_{0}\) are dimensionless variables. Here \(\tau_{0} = R^{2} \mu_{0} \sigma_{0}\) could be treated as the characteristic time of skin effect, which is equal to 4 × 10−8 s in this case. \(r\) is the radial coordinate in the circular section of nichrome wire with the radius equal to \(R\), and \(t\) is the time. \(\mu_{0}\) and \(\sigma_{0}\) are the magnetic permeability and the conductivity of nichrome alloy at room temperature, correspondingly. The boundary condition for this equation is obtained because of continuity of the electric field strength through the wire boundary50:
where \(\dot{I}\) is the time derivative of the total electrical current through the wire, which can be calculated from the current pulse configuration (as shown in Fig. 1C). The electrical current density across the wire cross-section can be related to the electrical field strength by the Ohm’s law:
All material parameters of this nichrome alloy that are used in these calculations are given in Table 151,52. The direct finite-difference calculations of Eq. (1) have confirmed that the electric current during this one microsecond pulse is almost uniform across the wire cross-section. The temperature evolution across the wire cross-section is described by traditional thermal diffusion equation. With the use of dimensionless parameters, it has the following form50:
and,
where \(\rho_{m}\) is the density of nichrome alloy, \(C_{p}\) is the heat capacity of nichrome alloy. \(k\left( T \right)\) is the thermal conductivity of nichrome alloy and \(k_{0}\) is its value at room temperature. Heat irradiation and convection are considered in the boundary condition as following:
where ϵ is the emissivity, \(k_{B}\) is the Stephan–Boltzmann constant and \(T_{0}\) is the ambient temperature. The convective heat transfer coefficient \(h\) for the wire can be calculated as53:
where \(Ra\) and \(Pr\) are the Rayleigh and Prandtl numbers calculated based on the physical parameters of air at room temperature. In this experiment with nichrome wire, eight consecutive one-microsecond pulses were used with the 10% duty cycle. Equations were solved by finite difference method with FORTRAN code. Taking the electric field uniformity into consideration, the temperature evolution and distribution in nichrome wire during this quasi-instantaneous ENP processing can be predicted.
Results
Quasi-instantaneous and localized processing via ENP technology-temperature field and grain structure stability
One of the most common concerns regarding the quasi-instantaneous ENP processing at micro-nano seconds scale is the distribution of electric field and temperature within the treated material component’s cross-section, which, to large extent, determines whether this proposed ENP technology can be compatible with industrial applications. By simulation, the rise of temperature at alloy center exhibits stepped increment in this case (Fig. 2A), with the maximum wire temperature being about 1643 K, which is very close to the melting point of this nichrome alloy in this work (1673 K). This agrees with the experimental observation that releasing extra electric energy will cause the bulk melting of this nichrome alloy. The corresponding temperature rate profile shows that the proposed ENP technology can bring this nichrome alloy an extraordinary heating rate of the magnitude of 108 K/s during the pulsing releasing whilst the cooling during the rest time is negligible (Fig. 2B). It is noted that the temperature difference between the alloy component’s center and the edge, although gradually increasing over the pulse time, can maintain at a sufficiently low value (less than 12 K) (Fig. 2C).
Another important feature of ENP technology is the localized modification of material structure at micro-nano structure level without significant change of grain structure. Figure 2 also shows the EBSD inverse pole figures and the grain size distributions of nichrome alloy wires after conventional heating and after ENP processing. For conventional heating, the nichrome alloy wires were loaded into a conventional furnace preheated to 1400 °C for 10 s to achieve the highest possible heating rate and the shortest possible duration time as close as possible to the condition in ENP processing. The annealing twins are commonly seen in this Ni-based superalloy with FCC structure subjected to thermal treatment54. This comparison clearly shows that the grain structure of alloy matrix remains almost unchanged after ENP processing, while the conventional heating brings it a drastic modification. Many thermal processing technologies by heat conduction/radiation or by Joule heating generally require a duration time of at least dozens of seconds or even much longer. One can see from Fig. 2D,E,G,H that the nichrome alloy grains undergo a significant growth in size after only 10 s of conventional heating, with the mean grain size increasing by nearly three times that of the raw sample (from 4.8 to 13.4 µm), and an unexpected maximum size of 146.2 µm. However, compared with conventional heating, no obvious change in grain morphology occurs after the ENP processing, as illustrated by their similar distribution range and mean size (Fig. 2I). The raw nichrome wire has a pronounced grain orientation texture. The <001> and <111> orientations are preferred to align with (001) direction (axial direction of wire), whilst the radial direction have a random orientation distribution (Fig. 2D). This orientation feature, at a smaller structural level, is modified after ENP processing (Fig. 2F) and has been significantly damaged after conventional heating. The grains at radius directions exhibit some preferred orientations, and the closest-packed plane {111} no longer tends to be parallel to the wire cross-section (Fig. 2E). The inspection of the orientation difference at GBs also indicates that the high-angle GBs still hold the majority (> 90%) both in raw sample and after ENP processing, whereas conventional heating promotes the formation of more low-angle GBs (> 10%) (Fig. 3). More emphasis will be put on the quantification of Σ3n special grain boundaries by EBSD data in next works, as this is at the heart of properties optimization via grain boundary engineering (GBE)55.
The quasi-instantaneous ENP processing as defect reconfiguration technology
The massive energy released into nichrome alloy via ENP processing can also bring the non-equilibrium modifications on material’s internal microstructure within micro- or nanosecond scale. One of representative manifestations is the influence of change of grain insides (GIs) on hardening effects by producing dislocations. It is expected that the intense electric pulsing promotes dislocation motion due to electroplastic effect and, indeed, the wire length after ENP processing is increased due to its plastic deformation. The observations by transmission electron microscopy (TEM) display a dramatic difference in dislocation morphology between raw and ENP processed samples. As shown in Fig. 4A, the raw nichrome alloy has a dislocation entanglement structure produced by plastic deformation. These pre-existing dislocations should be generated by cold rolling of raw nichrome wire and reserved after its softening annealing. As expected, conventional heating near melting point promotes the dislocation mobility and the annihilation of opposite-signed dislocations, thereby reducing the dislocation density significantly (Fig. 4B). Surprisingly, this ENP processing not only promote the avalanche generation of dislocations, but also alternate the dislocation configuration in a dramatic way. Here some representative examples are presented. In ENP processed nichrome wire with two pulses at a current density of 6.98 × 1010 A/m2, a large number of jagged dislocations with heavily curved and randomly oriented topography can be observed by imaging at (011) zone axis (Fig. 4C), with selected area diffraction pattern shown in Fig. 4D. It probably results from the cross-slip of extended screw dislocations or the point pinning of dislocation lines under this ENP process. Similar dislocation reconfiguration is also found in pulsing deformed Ti–Al alloy, which is described as the homogeneous wavy slip and the source of electroplasticity20. It is supposed to harden this ENP processed alloy by suppressing planar slip and increasing work hardening rate. Additionally, in ENP processed nichrome wire with eight pulses at a current density of 3.15 × 1010 A/m2, a group of dislocation walls with orderly interwoven and periodically arranged topography can be observed by imaging at (011) zone axis (Fig. 4E,F). These dislocation walls are the boundaries that divide the matrix into small cell-like regions (cell blocks) with relatively low density. This is caused by the multiplication and rearrangement of entangled dislocations with respect to the motion direction of drifting electrons in this ENP process. Similar universal parallel distribution of dislocations is also found in quenched steel after electropulsing, which is described as “seaweed” structure formed by electron wind force56. It can bring the electroplastic effect by combined action of Joule heating and reduced residual stress. The arguments on the dislocation rearrangement by electropulsing treatment and its resulted electroplasticity are diverse. The participation of Joule heating should be in favor of increased plasticity, but the origin of electroplasticity and its impact on mechanical properties have not been explained consistently57,58,59. It is commonly assumed that electropulsing promotes the dislocation motion by electron wind force, but our results here indicate that different ENP parameters, including current intensity, pulsing duration, and pulsing rising rate60, can produce specific mechanism of dislocations-pulsing interaction, finally contributing to the exhibition of various dislocation configurations. The ENP technology can stimulate specific electro-microstructure interaction by precisely controlling the input of this powerful and responsive electric energy in a material system and provide a creative tooling for exploring the mechanism of relevant electric field effects.
Tensile testing of nichrome alloy wires was conducted to analyze the mechanical impact of ENP processing (Fig. 5), with their fracture surfaces shown in Fig. 6. Experimental results show that slight softening phenomenon with a small decrease of ultimate fracture strength is observed in this alloy after ENP processing, despite the dislocation reconfiguration produced by electropulsing (Fig. 5). This can result from the temperature rise by Joule heating, whilst the heavy dislocation generation or reconfiguration is locally happened in a few specific grains. It is inferred that this softening effect on materials can be avoided in ENP processing by suppressing Joule heating. The yield stress does not show a signification change due to the unaffected grain size after ENP processing. Conventional thermal treatment brings this nichrome alloy to an all-round property degradation, because of dislocation annihilation, abnormal grain growth and loose oxide mixture on the surface. Remarkably, the elastic modulus of nichrome alloy after ENP processing changes from 315 to 140 GPa, which indicates an obvious transformation of the initial anisotropic texture in a raw sample produced by cold rolling to the relaxed isotropic structure. Our experiments show almost instant release of the stored mechanical energy by previous cold deformation in the nichrome alloy wire under ENP processing without significant change of its grain structure. This means the localization of electrical pulsing impacts predominantly at the dislocation level. Just by releasing a few electric pulses, their high intensity nature ensures the significant non-thermal effects. Homogenization and uniformization of material properties in Ni-based superalloys during electropulsing treatment have been detected61. However, it takes place in micro-nano seconds and without detectable recrystallization in our case. This effect produced by electropulsing can be used for the improvement of material properties62.
The quasi-instantaneous ENP processing as surface nanocoating technology
The rapid heating speed by this high-intensity ENP technology in air atmosphere can activate the altered oxidation behavior of the nichrome alloy, forming a unique oxidation coating on surface (Fig. 7). Generally, in the oxidation of nichrome alloys, loose NiO and Cr2O3 are preferentially formed and finally transformed into NiCr2O4 spinel in the case of prolonged oxidation63. It is interesting that, with the ENP processing, a dense chromium oxide nanocoating with triple hierarchical structure on alloy exterior surface can be obtained after eight consecutive pulses are released. This rough coating surface displays a fold-like morphology at micro-scale (Fig. 8A,B) and the zoom-in image shows some sub-nanoscale ravines inside (Fig. 8C). The inspection at higher resolution further shows that this surface coating is composed of the stacking of massive well-faceted nanocrystals (< 200 nm) (Fig. 8D). As an outcome of instantaneous surface localized modification, this dense hierarchical micro-nano structure on exterior surface conceivably possesses high hardness and specific surface area, which may find many applications in wear-resistant and gas sensors. It should be noted that the proposed ENP coating technology can be conducted in various gas environments with different conductive alloys as substrate, thereby fabricating surface ceramic layers or even thin films flexibly. The composition by EDS measurement (Figs. 9, 10) further clarifies that this surface oxidation coating mainly contains the chromium oxide, while almost no formation of nickel-containing oxides is involved during ENP processing. In fact, this non-equilibrium structure stimulated by the ENP processing is completely unobtainable under conventional thermal method at 1400 °C (melting point) for ten seconds (Fig. 11), which only leads to roughened and loose surface layer with the hardness decreasing and the tribological properties degradation64. The spheroidization and coarsening of crystals observed will also damage their electrical and gas-sensitive properties65.
The cross-section morphology of this nanocoating by quasi-instantaneous ENP processing is given in Fig. 12, with a comparison to that by conventional heating. The mounted nichrome alloys are etched by 10%HCl/3%CuSO4 ethanol solution to enhance the visualization of nanocoating. It should be Cr2O3/NiO/SiO2 mixture formed in alloy by conventional furnace (Fig. 13). Studies find that long-time thermal heating, even at lower temperatures, can generate the surface mixed oxides and the matrix intergranular oxides63,66. However, as shown in Fig. 12C, a dense double-layer composite coating with a thickness of about half a micrometer on nichrome alloy surface can be achieved by the ENP processing. Its transient nature can be one explanation for the formation of ultra-thin Cr2O3 coatings (~ 200 nm) because of kinetically insufficient time for crystal growth. Yet, ENP processing surprisingly produces not only a denser Cr2O3 coating but also one extra ultra-thin amorphous Si–Cr–O nanocoating beneath it (Fig. 8H). This double-layer ultra-thin coating covers the nichrome alloy well, without excessive detrimental oxygen intergranular diffusion into alloy matrix (Fig. 8E,I). High-intensity ENP processing not only promotes the formation of Si/Cr-contained oxidation coating by enhancing diffusion, but also enlarges the diffusivities of Cr and Si in varying degrees67. Therefore, this separated double-layered nanocoating can be obtained on localized alloy surface in microseconds by ENP processing, which is required a long critical time by conventional thermal methods68,69. Our experiments demonstrate the potential of ENP processing for a rapid development of protective coatings. Some studies find the preferred formation of unwanted NiO oxide on Ni–Cr based superalloy surface after short-term heat exposure68,70, which does not have necessary protective function71. In our case, electropulsing produces thin protective Cr2O3 layer strongly adhered to the alloy matrix. The folded structure of the coating layer indicates that despite high temperature reached during ENP processing, grain boundary diffusion still has main contribution into the mass transport72. All these outcomes are undoubtedly from the enhanced field effects produced by this unique ENP processing. Such adherent ultra-thin double-layered coating with well-bonded and defect-free interface with alloy matrix (Fig. 8F,G) should have good anti-corrosion protection ability71 and bring this nichrome alloy with better room temperature gas sensitivity and mechanical properties73,74.
Discussion
By electric nano pulsing (ENP) technology, the massive electric energy released into polycrystalline materials within the micro-nano seconds enables the extremely rapid Joule heating effects and the ultra-strong electric field effects, bringing the intense non-equilibrium microstructure evolutions at nanometer spatial scale and nanosecond temporal scale, which cannot be achieved through conventional thermal treatment. Potential applications of this high-intensity ENP technology can be excavated in the related industrial fields, towards an upgraded high-rate manufacturing in micro-nano seconds’ level. ENP not only opens a new technical avenue for the quasi-instantaneous materials processing by electrically assisted treatment, but also contributes to the refinement of field-assisted materials processing via exploring the application or mechanism of relevant field effects.
The feature of instantaneous treatment can promote the potential of the ENP technology for versatile and efficient microstructure processing of alloys, because the samples can be easily attached to the fixed electrodes to achieve the continuous ENP processing. The highly compatible electrodes in the developed ENP device can be designed as flexible ones to adapt to the instantaneous processing of complex-shaped parts. They can even be designed to load multiple samples at once for the high-throughput ENP processing in multi-tasking scenarios. In addition, ENP should be a scientific tool to explore the intrinsic mechanism of field effects on its interaction with microstructure in materials. It allows a finely controllable electropulsing profile such that it can be applied for the instantaneous stimulation of desired field effects in a tunable manner. The exclusive study of field effects requires to de-couple them from the outcomes by Joule heating. Just by releasing few single electric nano pulses, its high intensity nature ensures the significant non-thermal effects whilst its short duration nature ensures the reduced influences by thermal effects. Like other electropulsing technologies, ENP can be used for nanopowders synthesis by electric explosion or for the capacitive discharge welding by joint connection with high efficiency and short processing time. Due to its ultra-fast and heavily non-equilibrium nature, ENP can also be used for improving the strength-plasticity synergy in engineering materials by promoting grain refinement and GBs reconstruction. ENP can be extended to process a wide range of non-conductive materials by inserting conductive parts, like graphite felt, to obtain their instantaneous thermal treatment. By this, ENP can even be coupled with novel sintering method to develop ENP-based flash sintering or ENP-based ultra-fast high-temperature sintering that achieves instantaneous consolidation of powders within micro-nano seconds.
Conclusion
For the first time, extraordinary electropulsing technology of electric nano pulsing has been introduced to realize the quasi-instantaneous processing on the localized microstructures in materials, which achieves ultra-high voltage (up to 1000 V), ultra-high current density (up to 1011–1012 A/m2), ultra-short pulse duration (less than 1 μs) and ultra-high pulsing frequency (up to 100 kHz) simultaneously. The massive electric energy released into polycrystalline materials within the micro-nano seconds enables the extremely rapid Joule heating effects and the ultra-strong electric field effects, bringing the intense non-equilibrium microstructure evolutions at nanometer spatial scale and nanosecond temporal scale, including surface nanocoating and defect reconfiguration. They absolutely cannot be achieved through conventional thermal treatment. Potential applications of this high-intensity ENP technology can be excavated in the related industrial fields, towards an upgraded high-rate manufacturing in micro-nano seconds’ level. ENP not only opens a new technical avenue for the quasi-instantaneous materials processing by electrically assisted treatment, but also contributes to the refinement of electropulsing treatment for exploring the application or mechanism of relevant field effects (Supplementary Movies S1, S2).
Data availability
All data generated or analyzed during this study are included in this published article (and its Supplementary Information files).
References
Lu, K. Stabilizing nanostructures in metals using grain and twin boundary architectures. Nat. Rev. Mater. 1, 16019. https://doi.org/10.1038/natrevmats.2016.19 (2016).
Thompson, D. P. Cooking up tougher ceramics. Nature 417, 237–237 (2002).
Shen, Z., Zhao, Z., Peng, H. & Nygren, M. Formation of tough interlocking microstructures in silicon nitride ceramics by dynamic ripening. Nature 417, 266–269 (2002).
Olevsky, E. A. & Dudina, D. V. Sintering by low-voltage electric pulses (including spark plasma sintering (SPS)) in Field-Assisted Sintering: Science and Applications 89–191 (Springer Nature, 2018).
Szalaty, T. J., Klapiszewski, L. & Jesionowski, T. Recent developments in modification of lignin using ionic liquids for the fabrication of advanced materials: A review. J. Mol. Liq. 301, 112417. https://doi.org/10.1016/j.molliq.2019.112417 (2020).
Agullo-Lopez, F., Climent-Font, A., Munoz-Martin, A., Olivares, J. & Zucchiatti, A. Ion beam modification of dielectric materials in the electronic excitation regime: Cumulative and exciton models. Prog. Mater. Sci. 76, 1–58 (2016).
Bandyopadhyay, A., Traxel, K. D. & Bose, S. Nature-inspired materials and structures using 3D printing. Mater. Sci. Eng. R 145, 100609. https://doi.org/10.1016/j.mser.2021.100609 (2021).
Tao, F. et al. Different surface modification methods and coating materials of zinc metal anode. J. Energy Chem. 66, 397–412 (2022).
Wang, J. et al. Simultaneous improvement of strength and damping capacities of Mg–8Li–6Y–2Zn alloy by heat treatment and hot rolling. J. Alloys Compd. 927, 167027. https://doi.org/10.1016/j.jallcom.2022.167027 (2022).
Hazarabedian, M. S. et al. Formation of intergranular phases in precipitation hardening nickel-based alloy 725. Acta Mater. 236, 118108. https://doi.org/10.1016/j.actamat.2022.118108 (2022).
He, H., Yi, Y., Huang, S. & Zhang, Y. An improved process for grain refinement of large 2219 Al alloy rings and its influence on mechanical properties. J. Mater. Sci. Technol. 35, 55–63 (2019).
Kaseem, M., Fatimah, S., Nashrah, N. & Ko, Y. G. Recent progress in surface modification of metals coated by plasma electrolytic oxidation: Principle, structure, and performance. Prog. Mater. Sci. 117, 100735. https://doi.org/10.1016/j.pmatsci.2020.100735 (2021).
Kuczynska-Zemla, D. et al. Microstructure and mechanical properties of titanium subjected to direct laser interference lithography. Surf. Coat. Technol. 364, 422–429 (2019).
Sprecher, A. F., Mannan, S. L. & Conrad, H. On the mechanisms for the electroplastic effect in metals. Acta Metall. 34, 1145–1162 (1986).
Cologna, M., Rashkova, B. & Raj, R. Flash sintering of Nanograin Zirconia in < 5 s at 850°C. J. Am. Ceram. Soc. 93, 3556–3559 (2010).
Wang, C. et al. A general method to synthesize and sinter bulk ceramics in seconds. Science 368, 521–526 (2020).
Lee, G. et al. Effect of electric current on densification behavior of conductive ceramic powders consolidated by spark plasma sintering. Acta Mater. 144, 524–533 (2018).
Islam, Z., Wang, B. & Haque, A. Current density effects on the microstructure of zirconium thin films. Scr. Mater. 144, 18–21 (2018).
Noell, P. J., Rodelas, J. M., Ghanbari, Z. N. & Laursen, C. M. Microstructural modification of additively manufactured metals by electropulsing. Addit. Manuf. 33, 101128. https://doi.org/10.1016/j.addma.2020.101128 (2020).
Zhao, S. et al. Defect reconfiguration in a Ti–Al alloy via electroplasticity. Nat. Mater. 20, 468–472 (2021).
Lin, Y., Han, L. & Wang, G. Coupling effect of torsion and electric pulse treatment on grain boundary regulation and plasticizing of nickel wire. Mater. Sci. Eng. A 857, 143747. https://doi.org/10.1016/j.msea.2022.143747 (2022).
Yurlova, M. S. et al. Electric pulse consolidation: An alternative to spark plasma sintering. J. Mater. Sci. 49, 952–985 (2014).
Ma, R. & Zhang, X. Refining the microstructure to strengthen casting titanium alloy by electric pulse. Mater. Sci. Eng. A 849, 143519. https://doi.org/10.1016/j.msea.2022.143519 (2022).
Yi, K. et al. Eliminating reversible hydrogen embrittlement in high-strength martensitic steel by an electric current pulse. Int. J. Hydrog. Energy 47, 17045–17055 (2022).
Kumar, A. & Paul, S. K. Restoration of ductility in hydrogen embrittled dual-phase (DP 780) steel by the electric pulse treatment. Mater. Sci. Eng. A 847, 143256. https://doi.org/10.1016/j.msea.2022.143256 (2022).
Awasthi, K., Chang, F., Wu, T., Hsu, H. & Ohta, N. Modulation of calcium signaling by nanosecond electric pulses and cell death through apoptosis in A549 lung cancerous cells. Sens. Actuators B Chem. 369, 132348. https://doi.org/10.1016/j.snb.2022.132348 (2022).
Silkunas, M., Gudvangen, E., Novickij, V. & Pakhomov, A. G. Sub-MHz bursts of nanosecond pulses excite neurons at paradoxically low electric field thresholds without membrane damage. Biochim. Biophys. Acta Biomembr. 1864, 184034. https://doi.org/10.1016/j.bbamem.2022.184034 (2022).
Francis, J. S. C. & Raj, R. Flash-sinterforging of Nanograin Zirconia: Field assisted sintering and superplasticity. J. Am. Ceram. Soc. 95, 138–146 (2012).
Narayan, J. A new mechanism for field-assisted processing and flash sintering of materials. Scr. Mater. 69, 107–111 (2013).
Liang, C. & Lin, K. The microstructure and property variations of metals induced by electric current treatment: A review. Mater. Charact. 145, 545–555 (2018).
Okazaki, K., Kagawa, M. & Conrad, H. A study of the electoplastic effect in metals. Scr. Metall. 12, 1063–1068 (1978).
Okazaki, K., Kagawa, M. & Conrad, H. Additional results on the electroplastic effect in metals. Scr. Metall. 13, 277–280 (1979).
Conrad, H., Karam, N. & Mannan, S. Effect of electric current pulses on the recrystallization of copper. Scr. Metall. 17, 411–416 (1983).
Conrad, H., Karam, N. & Mannan, S. Effect of prior work on the influence of electric current pulses on the recrystallization of copper. Scr. Metall. 18, 275–280 (1984).
Conrad, H., Karam, N., Mannan, S. & Sprecher, A. F. Effect of electric current pulses on the recrystallization kinetics of copper. Scr. Metall. 22, 235–238 (1988).
Dai, W. & Wang, X. Effect of electric current on the inclusions in a Cu–Zn alloy. Mater. Trans. 51, 892–895 (2010).
Zhu, Y. H., Jiang, Y. B. & Liu, X. M. Electropulsing induced circular phase transformations of a cold-deformed ZA27 alloy. J. Alloys Compd. 737, 630–636 (2018).
Zhu, R. F. et al. The improved superelasticity of NiTi alloy via electropulsing treatment for minutes. J. Alloys Compd. 584, 225–231 (2014).
Zhu, R., Jiang, Y., Guan, L., Li, H. & Tang, G. Difference in recrystallization between electropulsing-treated and furnace-treated NiTi alloy. J. Alloys Compd. 658, 548–554 (2016).
Hu, G., Tang, G., Zhu, Y. & Shek, C. Electropulsing induced texture evolution in the recrystallization of Fe-3 pct Si alloy strip. Metall. Mater. Trans. A 42, 3484–3490 (2011).
Qin, R. S., Samuel, E. I. & Bhowmik, A. Electropulse-induced cementite nanoparticle formation in deformed pearlitic steels. J. Mater. Sci. 46, 2838–2842 (2011).
Ma, B., Zhao, Y., Ma, J., Guo, H. & Yang, Q. Formation of local nanocrystalline structure in a boron steel induced by electropulsing. J. Alloys Compd. 549, 77–81 (2013).
Park, J. et al. Effect of electric current on recrystallization kinetics in interstitial free steel and AZ31 magnesium alloy. Mater. Charact. 133, 70–76 (2017).
Liu, Y. et al. Recrystallization and microstructure evolution of the rolled Mg-3Al-1Zn alloy strips under electropulsing treatment. J. Alloys Compd. 622, 229–235 (2015).
Roh, J. et al. The mechanical behavior of 5052–H32 aluminum alloys under a pulsed electric current. Int. J. Plast. 58, 84–99 (2014).
Kim, M. et al. Electric current-induced annealing during uniaxial tension of aluminum alloy. Scr. Mater. 75, 58–61 (2014).
Wu, W., Wang, Y., Wang, J. & Wei, S. Effect of electrical pulse on the precipitates and material strength of 2024 aluminum alloy. Mater. Sci. Eng. A 608, 190–198 (2014).
Williams, J. C. & Starke, E. A. Jr. Progress in structural materials for aerospace systems. Acta Mater. 51, 5775–5799 (2003).
Guo, J. D., Wang, X. L. & Dai, W. B. Microstructure evolution in metals induced by high density electric current pulses. Mater. Sci. Technol. 31, 1545–1554 (2015).
Lohofer, G. & Pottlacher, G. Rectangular wires in pulse-heating experiments. Int. J. Thermophys. 26, 1239–1254 (2005).
Majumder, P. & Bhattacharyya, A. A computational study of the impact of the Wiedemann–Franz–Lorenz law on the thermal response of nichrome cylinders. Model. Simul. Mater. Sci. Eng. 16, 015006. https://doi.org/10.1088/0965-0393/16/1/015006 (2008).
Sultanian, B. K. Gas Turbines: Internal Flow Systems Modeling (Cambridge University Press, 2018).
Churchill, S. W. & Chu, H. H. S. Correlating equations for laminar and turbulent free convection from a horizontal cylinder. Int. J. Heat Mass Transf. 18, 1049–1053 (1975).
Zhang, H., Zhou, H., Qin, S., Liu, J. & Xu, X. Effect of deformation parameters on twinning evolution during hot deformation in a typical nickel-based superalloy. Mater. Sci. Eng. A 696, 290–298 (2017).
Cayron, C. Quantification of multiple twinning in face centred cubic materials. Acta Mater. 59, 252–262 (2011).
Xiang, S. & Zhang, X. Dislocation structure evolution under electroplastic effect. Mater. Sci. Eng. A 761, 138026. https://doi.org/10.1016/j.msea.2019.138026 (2019).
Zhang, W., Sui, M. L., Zhou, Y. Z. & Li, D. X. Evolution of microstructures in materials induced by electropulsing. Micron 34, 189–198 (2003).
Kim, M. et al. Elucidating the origin of electroplasticity in metallic materials. Appl. Mater. Today 21, 100874. https://doi.org/10.1016/j.apmt.2020.100874 (2020).
Li, X., Xu, Z., Guo, P., Peng, L. & Lai, X. Electroplasticity mechanism study based on dislocation behavior of Al6061 in tensile process. J. Alloys Compd. 910, 164890. https://doi.org/10.1016/j.jallcom.2022.164890 (2022).
Molotskii, M. I. Theoretical basis for electro- and magnetoplasticity. Mater. Sci. Eng. A 287, 248–258 (2000).
Zhang, H. et al. Static recrystallization microstructure evolution in a cold-deformed Ni-based superalloy during electropulsing treatment. Crystals 10, 884. https://doi.org/10.3390/cryst10100884 (2020).
Hao, J., Qin, S., Yan, L. & Zhang, X. Breaking thermodynamic and kinetic barriers in superalloy homogenization process by electropulsing to improve mechanical properties. J. Alloys Compd. 873, 159854. https://doi.org/10.1016/j.jallcom.2021.159854 (2021).
Zhang, H., Liu, Y., Chen, X., Zhang, H. & Li, Y. Microstructural homogenization and high-temperature cyclic oxidation behavior of a Ni-based superalloy with high-Cr content. J. Alloys Compd. 727, 410–418 (2017).
He, N., Li, H., Ji, L., Liu, X. & Chen, J. Investigation of metal elements diffusion in Cr2O3 film and its effects on mechanical properties. Ceram. Int. 46, 6811–6819 (2020).
Almaev, A. V. et al. Structural, electrical and gas-sensitive properties of Cr2O3 thin films. Superlattices Microstruct. 151, 106835. https://doi.org/10.1016/j.spmi.2021.106835 (2021).
Romedenne, M., Haynes, A. & Pillai, R. Cyclic oxidation behavior of selected commercial NiCr-alloys for engine exhaust valves in wet air environment between 800 and 950 °C. Corros. Sci. 211, 110817. https://doi.org/10.1016/j.corsci.2022.110817 (2023).
Xu, W., Maksymenko, A., Hasan, S., Melendez, J. J. & Olevsky, E. Effect of external electric field on diffusivity and flash sintering of 8YSZ: A molecular dynamics study. Acta Mater. 206, 116596. https://doi.org/10.1016/j.actamat.2020.116596 (2021).
Liu, C. T., Ma, J. & Sun, X. F. Oxidation behavior of a single-crystal Ni-base superalloy between 900 and 1000 °C in air. J. Alloys Compd. 491, 522–526 (2010).
Cao, J., Zhang, J., Chen, R., Ye, Y. & Hu, Y. High temperature oxidation behavior of Ni-based superalloy GH202. Mater. Charact. 118, 122–128 (2016).
Ul-Hamid, A. A TEM study of the oxide scale development in Ni–Cr alloys. Anti-Corros. Method. M. 51, 216–222 (2004).
Mazumder, S., Pantawane, M. V. & Dahotre, N. B. Influence of high heating rates on evolution of oxides on directed laser energy additively fabricated IN718. NPJ Mater. Degrad. 5, 45. https://doi.org/10.1038/s41529-021-00193-2 (2021).
Atkinson, H. V. A review of the role of short-circuit diffusion in the oxidation of nickel, chromium, and nickel-chromium alloys. Oxid. Met. 24, 177–197 (1985).
Miremadi, B. K., Singh, R. C., Chen, Z., Morrison, S. R. & Colbow, K. Chromium oxide gas sensors for the detection of hydrogen, oxygen and nitrogen oxide. Sens. Actuators B Chem. 21, 1–4 (1994).
Samra, H. A., Kumar, A., Xia, J., Staedler, T. & Jiang, X. Development of a new generation of amorphous hard coatings based on the Si–B–C–N–O system for applications in extreme conditions. Surf. Coat. Technol. 223, 52–67 (2013).
Acknowledgements
The assistance with TEM experiments from Mingjie Xu (University of California, Irvine) and the assistance with EBSD experiments from Sabine Faulhaber (University of California, San Diego) are acknowledged. This work was supported by US Department of Energy, Office of Basic Energy Sciences Grant SC0022244 (EAO, WX).
Author information
Authors and Affiliations
Contributions
E.A.O. and W.X. initiated the research and developed the ENP concept. R.J., W.X. and E.T. designed the overall ENP experiments. R.J. and W.X. carried out the ENP processing and materials characterizations. R.J. and T.G. conducted the tensile tests of samples. R.J. conducted the sample characterizations and imaging. A.M. conducted the temperature simulation analysis. R.J. wrote and revised the manuscript. E.A.O., A.M., and E.T. collectively revised the manuscript. All the authors discussed the results and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Olevsky, E.A., Jiang, R., Xu, W. et al. Quasi-instantaneous materials processing technology via high-intensity electrical nano pulsing. Sci Rep 14, 434 (2024). https://doi.org/10.1038/s41598-023-50698-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-50698-w
- Springer Nature Limited