Abstract
A pioneering robust and green heterogeneous acidic catalyst (CSA@g-C3N4) was rationally designed via immobilization of camphorsulfonic acid (CSA) on the g-C3N4 surface under mild conditions. Grafting CSA in the g-C3N4 lattice is distinguished as the root cause of facilitating the structure change of g-C3N4, leading to a unique morphology, accordingly the remarkable catalytic efficiency of CSA@g-C3N4. The morphology of new as-prepared nano-catalyst was specified by means of FT-IR, XRD, SEM, EDS, TEM, TGA, and BET. For the first time, it is exhibited that the efficient catalyst CSA@g-C3N4 can productively accomplish the three-component reactions with high yields and also serve as an inspiration for easily performing various sorts of MCRs based on our finding. The recommended synthesis pathway of chromenes derivatives is facile and cost-effective which applies a condensation reaction of salicylaldehyde, thiophenol, and malononitrile followed by ready purification in a benign manner. Moreover, the CSA@g-C3N4 nanocomposite can be promptly reused, illustrating no sensational decrease in the catalytic activity after ten times.
Similar content being viewed by others
Introduction
Today, solid acid catalysts have earned pervasive notice in organic synthesis as well as transformation. Since, they are non-toxic, chemically stable, non-corrosive, economical, highly selective, considerably active, and reusable with no depletion in activity, which can also be easily operated under the mild reaction conditions followed by a simple separation process1,2,3. Moreover, acidity classification either Brønsted or Lewis, the acidic site potency and accessibility, alongside support specification concerning porosity, surface area, and thermal and chemical stability, are counted as key parameters affecting the solid acid catalysts traits and efficiencies. Thereby, the performance of the catalysts can be promoted via exploiting an appropriate support4, 5.
More specially, the benign and green catalyst of graphite-like carbon nitride (g-C3N4) is of extensive attention due to some potential attributes6,7,8,9,10,11. In addition, g-C3N4 seems to be a prime candidate in selective organic transformation as catalysts ascribed to its exclusive features and low cost12,13,14,15,16,17. A satisfactory approach to increase the surface area would be the fabrication of mesoporous carbon nitride via assigning pores within the scaffold. This happens by employing various types of templates in which emerging number of problems is inevitable. In other words, withdrawing hard templates cause non-environmental attributes, and deploying soft templates leads to undesired residuals into the g-C3N4 construction18,19,20,21,22. In other trials by scientists, porous carbon nitrides with the escalated surface area have been manufactured without utilizing templates as outlined in the following. For that reason, acid treatment of the bulk g-C3N4 or even consuming other materials, precursors pretreatment as another procedure have become promising trends for creating porous structure23,24,25,26,27. Notably, multi polyhydroxyl arrangements of the sulfonic groups could adjust spreading the electrons on the surface of the catalyst, which expedites the half-reactions of electrons28. On the side of recent concerns regarding environmental issues, metal-free organocatalysts can be the opportune recommendation. Another fascinating substance for being applied in several organic transformations, including multicomponent reactions, is camphorsulfonic acid (CSA) as a productive, non-hazardous, affordable, benign, commercially accessible, and soluble in water Brønsted acid catalyst29, 30.
Modern organic chemistry has put a specific focus on identifying new synthetic procedures to expedite the formation of organic compounds. To meet this challenge, the establishment of multicomponent reactions (MCRs) is regarded as a worthwhile approach applied to the production of complex molecules through executing several stages in a single process31, 32. Accordingly, MCRs play a leading role in the synthesis of various key heterocyclic compounds, for example, chromenes derivatives. Additionally, chromene moiety is frequently spotted as a crucial constructional unit either in biologically active or natural materials, such as flavonoids, alkaloids, anthocyanins plus tocopherols. More precisely, one of the most critical uses of functionally substituted chromene can be synthesizing compounds with the potential to be exploited in the medicinal chemistry branch33,34,35,36,37,38,39,40,41.
The application of solid acid catalysts in various areas has grabbed scientists’ attention in recent years as if it has become an attractive field42,43,44. On the other hand, the synthesis of chromene compounds employing diverse methodologies, including the use of acid catalysts or other methods, has been discussed in various articles in recent years. Hence, these reports have tried to express that developing a new reaction route for fabricating novel chemical compounds with different molecular constructions is of remarkable value in chemistry plus biology areas. Accordingly, developing approaches in which cost-effective catalysts along with more moderate conditions of reaction can be exploited has grabbed ascending attention in synthesizing structurally different frameworks. In this context, Lewis acids such as Al(OTf)3 or FeCl3 and a less toxic solid acid p-TSA catalyst as a Brønsted Acid have been used for the chemoselective synthesis of 4H-chromenes. In a comparison based on the recorded reports, it can be concluded that, in general, the use of Brønsted acids as a catalyst rather than Lewis acids increases the yield of products in addition to a significant decrease in the reaction time for chromene production45,46,47. One of the recently mentioned solid acid catalysts is MNPs•GO-CysA, which has been effective in the one-pot synthesis of 4H-chromene scaffolds from three components48. In this regard, nanostructured carbon compounds have raised tremendous interest in authentic documents around nanomaterials owing to promising qualities, such as low price, air stability, and corrosion resistance to be deployed in various chemical as well as industrial operations. Among other catalysts from a category of carbon compounds (graphene oxide) that have been explored for synthesizing 4H-chromene derivatives, Fe3O4‐supported sulfonated graphene oxide and the piperazine immobilized on the graphene oxide surface can be pointed out49, 50. Among other classes of new catalysts for chromene synthesis, MOFs should also be taken into consideration. Furthermore, heterogeneous solid acid catalyst systems, on the basis of metal organic frameworks, could be achieved by introducing acid sites on the MOF surface via chemical modifications, for example, Fe3O4@UiO@DAS51. In another case, the use of various Fe3O4-based hydrotalcites acting as acid–base bifunctional catalysts was stated to synthesize different 4H-chromene derivatives by a three-component reaction52. To gain the potential advantages of applying multifunctional catalysts in MCRs along with designing productive and green approaches in organic synthesis as a part of our research prospect, it can even be referred to the reports in which methods other than utilizing solid acid catalysts have been used for chromene synthesis. In this framework, agricultural wastes as an alternative source for toxic and dangerous catalysts for the environment have shown the capability to serve as green catalysts due to their ease of biodegradability. Moreover, water extract of pomegranate peel ash (WEPPA), water extract of lemon fruit shell ash (WELFSA), and Water extract of mango peel ash (WEMPA) are some examples of natural aqueous medium catalysts that have participated in producing 4H-chromene derivatives through the multicomponent reactions under exposure to microwave in recent years53,54,55. In an engaging report, multi-component reactions in combination with photocatalytic processes for 4H-chromene synthesizing have been investigated56. Additionally, green electrocatalytic multicomponent synthesis has been studied as another technique of 4H-chromenes production, exploiting potassium iodide as an electrolyte in undivided cell, which production yields of 86% have been reported57. Furthermore, ionic liquids have demonstrated an extensive domain of applications as either promoters or reaction medium in the case of multi-component reactions. In the last few years, a number of procedures employing various sorts of ionic liquids have been introduced to gain 4H-chromene derivatives58. Multicomponent reactions (MCR) provision deep knowledge regarding 4H-chromene formation. Furthermore, considerable catalytic schemes have evolved over recent years for the multicomponent synthesis of 4H-chromene derivatives, including RGO-SO3H59, GO/α-Fe2O3/CuL60, MNPs@Cu61, g-C3N462, Pd@g-C3N463, CaMgFe2O464, morpholine65, CAEDA66, mica/Fe3O467, amino grafted MOFs68, DABCO69, Fe3O4@Sal@Cu70, Fe3O4@GO-NH71, KCC-1@NH272, Nano-SiO273, SnO2 NPs74, Ag2O/GO/TiO275, and borax76. Yet, there are several drawbacks concerning plenty of expressed catalysts, including environmental contamination, high price, challenging catalyst removal, and requiring coarse reaction conditions. There are still tremendous requests for designing more practical, facile, benign, and efficient methods to synthesize these classifications of heterocyclic compounds ascribed to their prominence and expansive application.
As-mentioned valuable traits of chromenes derivatives act as incentives to develop productive and environmentally friendly procedures for 4H-chromenes framework synthesis employing CSA@g-C3N4. We have been prompted to prepare a novel heterogeneous catalyst via surface modification of g-C3N4 using camphorsulfonic acid for the first time. This protocol supports the impacts of green chemistry in synthesizing the chromenes derivatives through a three-component reaction while utilizing acid to accelerate catalytic activity at the same time.
Result and discussion
Extraordinary surface tailoring of g-C3N4 was effectively achieved through the embedding of camphorsulfonic acid (CSA) to produce CSA@g-C3N4. This fruitful synthesized catalyst maps out new routes toward the progressions of forthright synthesis of 4H-chromenes derivatives. Nano-carbon nitride-supported camphorsulfonic acid as a unique catalyst was designed and fabricated in the convenient pathway delineated in Figure S1 (see details in the Figure S1). The catalyst of CSA@g-C3N4 was characterized via various methods, namely FT-IR, XRD, SEM, EDS, TEM, TGA, and BET.
Characterization of synthesized CSA@g-C3N4
Fourier transform infrared spectroscopy (FT-IR)
FT-IR (Fourier transform infrared spectroscopy) was assisted to indicate the functional groups, construction added to chemical bonds vibration of the as-prepared catalyst depicted in Fig. 1. The broad bands nearby 3000 to 3500 cm−1 mostly reveals the NH stretching vibrational modes associated with NH2 groups belong to g-C3N4 in addition to O–H bands attributed to the adsorbed water on the surface of catalyst77. The heterocyclic stretching vibration of C=N was detected by absorption band located at the area close to 1636 cm−1. The absorption bands at the 1408–1565 cm−1 zone were corresponded to C-N vibrational spectra of nitrogen-entailing aromatic rings (N–C=N) regarding to s-triazine as well as tri-s-triazine which are existed in the g-C3N4. Moreover, manufacturing of g-C3N4 from heptazine blocks was evidently approved by a sharp peak at 806 cm−1 assigned to heptazine rings bending vibration78. The apparent bands at 1241 and 1321 cm−1 allocated to S–O and O=S=O stretching vibration, respectively, in the FT-IR spectrum imply that the g-C3N4 encompasses –SO3H groups. The appearance of NH, acidic SO3H together with absorbed water was confirmed via wide stretching absorption placed in the area of 2100–3000 cm−179. Ascribed to the FT-IR spectrum of nano-CSA@g-C3N4 specifies the existence of the camphorsulfonic acid on the surface of pure g-C3N4.
X-ray powder diffraction (XRD)
A large-angle x-ray powder diffraction (XRD) technique is a tool for inspecting the impact of -SO3H groups on the g-C3N4 crystalline features. Figure 2 depicts the XRD patterns of g-C3N4 before and after modification by camphorsulfonic acid. The crystalline nature of the carbon nitride polymer was ascertained through two peak intensities. The main one with high intensity was marked at 2θ = 27.4° (002) (JCPDS card No. 87-1526) attached to the s-triazine units interplanar stacking ordering. On the other side, the diffraction characteristic peak with low intensity at 2θ = 13.2° (100) illustrated the attendance of graphite-resembling interlayer structural packing of aromatic heterocyclic units80, 81. Additionally, the similarity between the crystalline peaks of pure g-C3N4 and CSA@g-C3N4 affirmed the crystalline phase stability of g-C3N4 showing no destructive effect throughout surface modification process by camphorsulfonic acid. More emphatically, by modifying the surface of g-C3N4 and subsequently changing the morphology, emerging a strong XRD peak intensity was not for beyond the prediction.
Scanning electron microscopy (SEM)
The scanning electron microscopy (SEM) images of CSA@g-C3N4 nano-catalyst to evaluate surface morphology plus distinguishing the shape as well as size of particles is shown in Fig. 382. The as-prepared catalyst nano-scale was clarified owing to the images gathered from SEM. A layered, even, sheet-resembling architecture with irregular configuration could be displayed which agglomeration of some particles were occurred, according to Fig. 3. Further, noticeable alteration in the both size and shape of the g-C3N4 did not observed after embedding camphorsulfonic acid on the surface of g-C3N4.
Energy dispersive X-ray (EDX)
The energy-dispersive X-ray spectroscopy (EDX) was employed to analyze the elemental distribution or chemical specification of the synthesized catalyst83. Fig. S2 displays the EDS analysis of CSA@g-C3N4. The EDX spectrum indicated the attendance of carbon, nitrogen, oxygen plus sulfur which certifies the successful grafting of camphorsulfonic acid on the surface of g-C3N4 (see details in the Figure S2).
Transmission electron microscopy (TEM)
Transmission electron microscopy (TEM) was exploited to gain supplementary confirmation for the morphology in addition to the size distribution of the nano-catalyst. Figure 4 displays the transmission electron microscopy (TEM) images corresponding to the CSA@g-C3N4 for assessing its surface morphology. Moreover, the layered, even, sheet-like framework with its irregular structure was observed and the agglomeration of some particles were also occurred. Accordingly, the acquired results were satisfactorily consistent with SEM images.
The thermo gravimetric analysis (TGA)
Thermal gravimetric analysis (TGA) in parallel with derivative thermogravimetry (DTG) were performed to assess the thermal characteristics of the incorporation of camphorsulfonic acid on the catalyst surface. TGA curves corresponding to bare CSA and pure g-C3N4 with the as-prepared catalyst of CSA@g-C3N4 are exhibited in Fig. 5. The TGA curves were taken under temperature up to 800 °C with steady heating rate of 10 °C min−1 undergoing air atmosphere as portrayed in Fig. 5. TGA thermographs exhibited the occurrence of several phase transformations as well as transforming reactions across such procedures. In the first stage at the temperature less than 200 °C, the removal of some of those organic compounds exploited in the production process of catalyst or absorbed water stirred up a scant mass loss. Besides, the weight of the nano-catalyst quickly declined in the temperature ranged from 125 to 440 °C owing to the remaining polyhydroxy components in the CSA@g-C3N4. Moreover, the significant endothermal peak could be seen in the range of 150 to 500 °C owing to the -SO3H groups thermal decomposition, which leads to the mild decline in weight, equals to 3.65%. A mild descending in weight was occurred in a temperature ranged from 500 to 800 °C rooted in degradation of the CSA@g-C3N4 lattice. In agreement with TGA results, the notable thermal stability of CSA@g-C3N4 was specified which vividly depicts its safe application in organic reactions when the temperature is high84. According to the literature85, 86, the content of CSA on the g-C3N4 can be calculated via the TGA curve. As can be seen, 0.22% of primary weight loss is related to the loss of physically adsorbed water. In the following, the second weight change of 3.65 wt% is relevant to the slow mass loss of -SO3H groups, which exist in CSA. Subsequently, because of the high temperature, g-C3N4 was totally decomposed or sublimated; hence, the mass percentage reached 53.69% at this stage. It can be deduced that the remaining compound was CSA, and a value of 42.44% was observed for the residual weight fraction without accounting the -SO3H groups. Therefore, it can be concluded that the CSA amount in the porous CSA@g-C3N4 nanocomposites would be equal to 46.09%.
The Brunauer–Emmett–Teller (BET)
The Brunauer–Emmett–Teller (BET) surface area (SBET) of g-C3N4 and as-prepared catalyst were surveyed87. The pore size distribution was valued via the technique of the Barrett–Joyner–Halenda (BJH) in compliance with the nitrogen isotherm adsorption branch. Table S1 outlines the BET surface area together with pore factors related to pure g-C3N4 and surface engineered catalyst powder acquired in accordance with nitrogen adsorption–desorption isotherm by use of the BJH technique. The more considerable BET surface area for modified catalyst by embedding CSA was attained when compared to the pure g-C3N4. Moreover, the results demonstrate the greater porosity and pore volume for CSA@g-C3N4 rather than g-C3N4 (see details in the Table S1). The immobilization of CSA onto g-C3N4 scaffold would bring on increasing the surface area along with pore volume for new nano-catalyst. The amplified surface area and pore volume are two impactful parameters on boosting the kinetics of catalytic reaction subsequent to increasing the mass transfer. The higher surface area for the as-prepared catalyst was recognized by BET results rather than the pure g-C3N4. The increased surface area was an axiomatic justification for enhancing active sites as well as adsorption of the substrate. The modified catalyst meanwhile illustrated escalated catalytic performance due to the expansive specific surface area assisting, effectively conducting the 4H-chromenes formation in a three-component reaction.
Surface acidity studies
To determine the acidity strength of pure g-C3N4 and CSA@g-C3N4, the temperature-programmed desorption (TPD) method can efficiently be employed. The basic nature of ammonia is the reason behind selecting an ammonia probe to specify the acidity owing to its facile adsorption on acidic sites by NH3-TPD88,89,90. Figure 6 compares the temperature-programmed desorption of ammonia (NH3-TPD) profiles corresponding to pure g-C3N4 and CSA@g-C3N4 within the temperature scope of 100 to 600 °C. Based on NH3-TPD, the weak as well as medium strength acid sites can be revealed in the low temperature between 103 and 300 °C of ammonia desorption, while the high temperatures between 300 and 600 °C in ammonia desorption illustrate the strong acid sites. In fact, by increasing the temperature, the amount of the weak-strength acid sites would decline, while the portion of the medium-strength acid sites would enhance so that strong-strength acid sites would emerge. Furthermore, the TPD profile associated with CSA@g-C3N4 resembles pure g-C3N4, showing two differences, reasonably higher intensity together with the more acid sites. Table 1 summarizes the acquired results, portraying the total amounts of acid sites calculated by integrating the NH3 desorption peaks. Additionally, the total acidity of the CSA@g-C3N4 catalyst equals 1124.9 µmol/g, which has dramatically increased compared to the pure g-C3N4. It should be taken into account that the root cause of the strong Brønsted acidity related to the nano-catalyst of CSA-treated g-C3N4 is the attendance of considerable density of acid sites on the g-C3N4 surface brought by -SO3H groups, which was certified by the NH3-TPD, as demonstrated in Table 1.
Evaluation of CSA@g-C3N4 activity for the synthesis of 4H-chromenes derivatives via the one-step multicomponent approach
A single-pot reaction produces a product via a combination of three reactants or more containing structural features of every applied reagent, all these happen in a process known as MCR. In this work, MCRs merits, such as selectivity and possessing atom economy have been exploited for chromene formation, which plays a leading role in modern synthetic procedures. The topic of this study is the employment of a powerful catalyst for developing MCRs where the absence of a catalyst would trigger not performing the reaction efficiently. According to our captivation in organic synthesis, also being inspired by our previous works focusing on heterocyclic chemistry synthesis; a remarkable output was given, introducing salicylaldehyde as an easy substrate. Therefore, a facile approach was launched in this project for straightforward synthesizing of 4H-chromenes derivatives in a one-pot polymerization, containing salicylaldehyde, malononitrile, various nucleophiles such as thiols, and amines, with employing the catalyst of CSA@g-C3N4 with pleasant yields under mild conditions at room temperature.
An appropriate support material for non-metal incorporation on the active sites can be graphitic carbon nitride (g-C3N4), having a configuration similar to graphite to improve the catalytic activity. Accordingly, the CSA doped g-C3N4 was productively synthesized to upgrade the catalytic performance for three-component reaction in the path of chromene production, decreasing the reaction time, promoting the yield of the reaction, and extending the of ratio product manufactured as well. Along the lines of this strategy, the model reaction between salicylaldehyde, malononitrile, and thiophenol was delved into the assessment of the most optimum reaction condition. It should be note that several solvents such as ethanol (C2H5OH), dichloromethane (CH2Cl2), glycerol (C3H8O3), acetonitrile (CH3CN), water (H2O), ethyl acetate (CH3CO2Et), tetrahydrofuran (THF), and dimethylformamide (DMF) were utilized in this reaction.
Table 2 assesses the optimum conditions to determine the type as well as amount of catalyst and also the solvent type for achieving the highest efficiency. The pure g-C3N4 completed the regarded three-component reaction by the yield of 18% to synthesize chromene while CSA performed the reaction alone in 2 h by yield of 71% (Table 2, Entries 13 and 14). The efficient catalyst of CSA@g-C3N4, which was synthesized for this work, outstandingly elevated the performance of the reaction. Different amounts of catalyst were examined to comprehend the most effective value. When the three-component reaction was conducted by salicylaldehyde, thiophenol and malononitrile without exploiting catalyst, the yield of 25% could be obtained for chromene production (Table 2, Entry 5). Consequently, increasing the amount of catalyst was sensibly enhanced the performance of reaction with respect to results (Table 2, Entries 1–4). To precisely study the reaction on path of seeking the most appropriate conditions, several protic and aprotic solvents were evaluated. The output was identifying ethanol as suitable solvent for three-component reaction of chromene production (Table 2, Entries 1 and 6–12). The optimization results implies that the best efficiency of 92% for chromene synthesis associated with three-component reaction of salicylaldehyde, thiophenol and malononitrile was obtained by deploying 40 mg catalyst of CSA@g-C3N4 in ethanol (1 mL) as solvent after 2 h at 60 °C.
Table 3 compares the different catalysts of CSA@g-C3N4 that have been synthesized by different amounts of loading CSA on the surface of the g-C3N4 catalyst. Actually, 4H-chromenes synthesis was performed under the mentioned optimum conditions, where the only objective was searching for the optimum value of CSA for loading on the g-C3N4 surface. Ultimately, the results obtained from Table 3 illustrated that the maximum efficiency would be gained for conducting the reaction by using 2 g of CSA is loaded on the g-C3N4 surface.
Derived from the fascinating results, elucidating the efficient impact of the powerful catalyst of CSA@g-C3N4 on multicomponent reactions, it was decided to conduct an additional investigation by carrying out further reactions through different substituted salicylaldehyde with thiols under the expressed conditions. Table 4 discusses about reactions between salicylaldehydes derivatives and several thiophenols in the presence of CSA@g-C3N4 catalyst. In this regard, salicylaldehydes with bromo as well as methoxy substitutions reacted with thiophenols such as thiophenol, para-bromothiophenol, para-methylthiophenol, para-methoxythiophenol, para-chlorothiophenol, and 2-naphthalenethiol at the temperature of 60 °C for 2 to 4 h. In such reactions, 4H-chromene derivatives can be gained by yields of 74% to 95% via both electron-rich salicylaldehyde, for example, 3-methoxysalicylaldehyde and electron-deficient salicylaldehyde, for instance, 5-bromosalicylaldehyde. Moreover, the results indicate the high efficiencies for all three-component reactions; it should be noted that applying 3-methoxysalicylaldehyde obtained a bit less yield rather than salicylaldehyde and 5-bromosalicylaldehyde. With this respect, mentioned aromatic thiols delivered chromene significant yields subjected to mild reaction conditions. Additionally, 2-naphthalenethiol illustrates a lower efficiency compared to thiophenol and thiophenols with substitutions in para position. Not only electron-withdrawing but also electron-donating substituent on the thiophenol showed any distinction in the selectivity as well as the reactivity of the reaction.
In continuation of gaining a better perceiving of the three-component reaction of chromene synthesis, when different nucleophiles, including secondary aliphatic amines, reacts with salicylaldehyde and malononitrile under the same reaction conditions, the generalization of this benign would obviously be approved. Moreover, a three-component condensation of salicylaldehyde, malononitrile, plus secondary amines undergoing the resembling reaction conditions was conducted to serve a quick approach to benzopyrano[2,3-d]pyrimidine to emphasize the capacity of this environmentally friendly method. Table 5 explores the synthesizing 4H-chromeno[2,3-d]pyrimidines derivatives attained via three-component reaction between salicylaldehyde, 5-bromosalicylaldehyde, and 3-methylsalicylaldehyde with malononitrile and diverse amines by the assistance of 40 mg CSA@g-C3N4 catalyst in existence of 3 mL ethanol as solvent at 60 °C for 3 to 5 h. Likewise, secondary aliphatic amines, which include piperidine, 4-methylpiperidine, morpholine, pyrrolidine, and diethylamine experienced a three-component reaction, bringing about the promised product in excellent yields. This three-component reaction was readily and practically accomplished by exploiting the robust as-prepared catalyst at the temperature of 60 °C. The highest yield of 90% for producing 4H-chromeno[2,3-d]pyrimidine was acquired when salicylaldehyde reacted with piperidine and 4-methylpiperidine (Table 5, Entries 1 and 2). On the other side, a reaction between 3-methylsalicylaldehyde with pyrrolidine resulted in the lowest yield of 68% (Table 5, Entry 8).
To evaluate the catalytic performance of CSA@g-C3N4 nanocomposite, a comparison table (Table 6) from previously reported data is represented, which consists of the parameters, such as catalyst, yields, reaction time, and reaction conditions in synthesis of 4H-chromenes. The results depict that several drawbacks exist in previously reported methodologies, including high-price catalysts, non-reusable catalysts, harsh conditions for catalyst synthesizing, challenging separation, long reaction time, and low yield. As a whole, the present protocol shows considerable plus points over some of the other former reported methods owing to applying CSA@g-C3N4 as the catalyst.
Reusability of CSA@g-C3N4
More notably, recyclability is of substantial importance in provisioning environmental sustainability together with economic pursuits. With respect to tackling this dilemma, the reusability of CSA@g-C3N4 for assessing its stability was checked in the direct synthesis of 4H-chromenes derivatives (Fig. 7). To recover the catalyst, it was separated through centrifuge first of all, then washed by warm ethyl acetate and ethanol in two steps, and finally, dried at room temperature to exploited again in chemical reactions. Moreover, the reusability and performance of the catalyst were assessed by executing several reactions in ten stages, based on the model reaction, utilizing thiophenol, malononitrile, and salicylaldehyde in attendance of solvent of ethanol and 40 mg of catalyst, results can be seen in Fig. 7. At least four times reusing caused a notable drop neither in catalytic activity nor in efficiency of the CSA@g-C3N4 catalyst, demonstrating the recycling capacity of this catalyst. It can be stated that almost from the fifth stage, the reaction efficiency gradually declines. In reviewing the results, the catalyst nature satisfactorily was not shifted throughout the recycling reactions. The elemental mapping of CSA@g-C3N4 and the EDS analysis of reused catalyst after ten runs were placed in the supporting information (see details in the Figure S3).
Experimental section
Materials and equipment
The entire chemicals were procured from the distinguished companies namely Merck and Aldrich while possessing high purities over 99%. The development of reactions were scrutinized via Thin-layer chromatography (TLC) in which silica gel 60 F254 was employed to immobilize the aluminum plates, visualized by UV illumination, afterwards. To evaluate the nano-catalyst traits, various procedures, for instance FT-IR, XRD, TGA, SEM, EDS, TEM added to BET were deployed. FT-IR 8400 manufactured by Shimadzu company was operated to record Fourier transform infrared spectroscopy (FT-IR) with a domain ranged from 400 to 4000 cm−1 for packed powder plates. The X-Ray diffraction (XRD) patterns attributed to the catalysts were gained from the AG D5000 tool (Siemens, Germany) to discern crystalline construction using Cu-Kα (λ = 1.54° A) as emission source. A scanning electron microscope (SEM) was utilized at 10 kV to determine the particle size of as-prepared catalyst. A scanning electron microscope apparatus (BAL-TEC SCD 005) was exploited. A helpful instrument of Energy-dispersive X-ray spectroscopy (EDS) was appointed to inspect the elemental distribution of synthesized catalyst implemented on an equipment model of MRIA3 TESCAN-XMU (Czechia). TEM images were recorded on a Philips EM 208S transmission electron microscope through the accelerating voltage adjusted to 100 kV. TGA was carried out to approve the reliability of catalyst synthesis as well as the thermal stability, which conducts a STA504 instrument at the temperature span from 0 to 800 °C with the heating rate value of 5 °C min−1 subjected to air atmosphere. A BELSORP Mini II nitrogen adsorption apparatus was a proper methodology to calculate the nitrogen adsorption–desorption isotherm at 77 K with respect to the Brunauer–Emmett–Teller (BET) surface area (SBET) accompanying the pore factors of representative samples while degassing treatment was performed at the temperature of 200 °C. Additionally, pore size distribution was measured according to the N2 adsorption isotherm through applying the Barrett-Joyner-Halenda (BJH) computational procedure based on the Halsey equation. The temperature-programmed desorption of ammonia (NH3-TPD) procedure was conducted to assess the acidic characterization of the samples via an NS-93 (NanoSORD) model with a temperature span from 100 to 600 °C.
Preparation of g-C3N4
However, there are diverse methodologies for synthesizing g-C3N4, hence, a simple protocol along with cost-effective precursors are accounted as two deciding parameters which were considered in this work to prepare nano-catalyst. Subsequently, melamine by the value of 10 g was transferred to a furnace using a covered steel crucible to be subjected to 550 °C heating at a 5 °C/min heating rate for a time period of 3 h. After cooling off to room temperature, carbon nitride (g-C3N4) yellow powder was gained. Eventually, calcination of melamine would be completed. The bulk carbon nitride was conveyed to a furnace with a temperature set point of 550 °C for 2 h to deliver nano-scale particles of graphitic carbon nitride.
Synthesis of CSA@g-C3N4
A round-bottom flask was chosen to hold a mixture of 25 ml dry DMF, 2 g CSA, and 2 g g-C3N4 to be heated up to 100 °C in a period of 12 h. Then, the entire acquired mixture was allowed to be cooled to room temperature prior to adding water and centrifuging. Consequently, CSA@g-C3N4 was reached after washing the solid multiple times via ethyl acetate and getting dried exposure to vacuum conditions at the temperature of 80 °C for 4 h.
General strategy for the preparation of 4H-chromenes derivatives by using CSA@g-C3N4
A 5-mL balloon was deployed to carry 1 mL ethanol, 1 mmol of salicylaldehyde, 1 mmol of malononitrile, 1 mmol of the nucleophile, and 40 mg of CSA@g-C3N4, which were stirred for 2 h at the temperature of 60 °C. TLC detected the endpoint of the reaction, then 5 mL of water was poured during stirring, and the residue was gathered via filtration, afterward. The acquired solids or viscous liquids were washed by water, clarified through either column chromatography, or with the assistance of recrystallization utilizing diethyl ether or ethanol to provide pure produce.
General protocol for the production of 4H-chromeno[2,3-d]pyrimidines via CSA@g-C3N4
In a 5-mL balloon equipped with a magnetic agitator, which consists of 3 mL of ethanol, salicylaldehyde, malononitrile, and secondary amines by the volume of 2, 1, and 1 mmol, respectively, were added, mixed at the temperature of 60 °C for 3 to 5 h. Additionally, TLC was operated as a helpful methodology to track the progression of the reaction, the catalyst was also separated by way of centrifuging subsequent to completely performing the reaction. In the end, to purify the products, ethanol, methanol, ethyl acetate, or tetrahydrofuran were found to be appropriate solvents.
Conclusions
Novel catalyst of CSA@g-C3N4 introduced in this study embodies glaring traits such as high stability as well as non-toxicity accounted as a prime candidate for synthesizing chromenes through three-component reactions consisting of salicylaldehyde, thiophenol, and malononitrile. Incorporation of camphorsulfonic acid (CSA) into g-C3N4 is set to be a constructive and highly practical strategy for enabling immense catalytic activity along with providing simplicity, cost-effectiveness, and time-saving for conducting the process. The new organocatalyst of CSA@g-C3N4 was structured from low-price as well as straightforward substrates while removing metal to chase the goal of becoming a benign protocol through a mild organic transformation which is currently placed on the top dominant trends of both industry and academia. It was comprehended that the acidification of g-C3N4 brings about high yields in comparison with pure g-C3N4, entailing a facile purification after a mild and rapid reaction. The novel heterogeneous catalyst was identified via several methods, including FT-IR, XRD, SEM, EDS, TEM, TGA, and BET. Additionally, this catalyst is recyclable after executing at least ten reaction cycles without any drop in catalytic performance, which can reach the development of a sustainable process.
Data availability
The datasets used and/or analysed during the current study available from the corresponding author on reasonable request.
References
Haile, S. M., Boysen, D. A., Chisholm, C. R. & Merle, R. B. Solid acids as fuel cell electrolytes. Nature 410, 910–913 (2001).
Clark, J. H. Solid acids for green chemistry. Acc. Chem. Res. 35, 791–797 (2002).
Hosseini, S. & Amoozadeh, A. Nano-TiO2-P25-SO3H as a new and robust photo-catalyst: The acceleration effect of selective oxidation of aromatic alcohols to aldehydes under blue LED irradiation. J. Photochem. Photobiol. A Chem. 364, 516–523 (2018).
Gupta, P. & Paul, S. Solid acids: Green alternatives for acid catalysis. Catal. Today 236, 153–170 (2014).
Hosseini, S., Amoozadeh, A. & Akbarzadeh, Y. Nano-WO3-SO3H as a new photocatalyst insight through covalently grafted brønsted acid: Highly efficient selective oxidation of benzyl alcohols to aldehydes. Photochem. Photobiol. 95, 1320–1330 (2019).
Xu, J. & Antonietti, M. The performance of nanoparticulate graphitic carbon nitride as an amphiphile. J. Am. Chem. Soc. 139, 6026–6029 (2017).
Huang, Y. et al. Facile synthesis of Pd nanoparticles incorporated into ultrathin crystalline g-C3N4 with enhanced photocatalytic performance. Cryst. Growth Des. 20, 7526–7532 (2020).
Xu, J. et al. Liquid-based growth of polymeric carbon nitride layers and their use in a mesostructured polymer solar cell with V oc exceeding 1 V. J. Am. Chem. Soc. 136, 13486–13489 (2014).
Xu, J. et al. g-C3N4 modified TiO2 nanosheets with enhanced photoelectric conversion efficiency in dye-sensitized solar cells. J. Power Sources 274, 77–84 (2015).
Wen, J., Xie, J., Chen, X. & Li, X. A review on g-C3N4-based photocatalysts. Appl. Surf. Sci. 391, 72–123 (2017).
Zhang, L. et al. Metal-free g-C3N4 photocatalyst by sulfuric acid activation for selective aerobic oxidation of benzyl alcohol under visible light. Mater. Res. Bull. 59, 84–92 (2014).
Zheng, Y. et al. Nanoporous graphitic-C3N4@carbon metal-free electrocatalysts for highly efficient oxygen reduction. J. Am. Chem. Soc. 133, 20116–20119 (2011).
Sano, T. et al. Activation of graphitic carbon nitride (gC3N4) by alkaline hydrothermal treatment for photocatalytic NO oxidation in gas phase. J. Mater. Chem. A 1, 6489–6496 (2013).
Zhang, P., Li, H. & Wang, Y. Post-functionalization of graphitic carbon nitrides by grafting organic molecules: Toward C–H bond oxidation using atmospheric oxygen. Chem. Commun. 50, 6312–6315 (2014).
Azhdari, A., Azizi, N., Sanaeishoar, H. & Tahanpesar, E. Amidosulfonic acid supported on graphitic carbon nitride: Novel and straightforward catalyst for Paal-Knorr pyrrole reaction under mild conditions. Monatshefte für Chemie-Chemical Monthly 152, 625–634 (2021).
Heydari, M., Azizi, N., Mirjafari, Z. & Hashemi, M. M. Aluminum anchored on g-C3N4 as robust catalysts for Mannich reaction at ambient temperature. J. Mol. Struct. 1259, 132731 (2022).
Azizi, N., Ahooie, T. S., Hashemi, M. M. & Yavari, I. Magnetic graphitic carbon nitride-catalyzed highly efficient construction of functionalized 4H-pyrans. Synlett 29, 645–649 (2018).
Li, H., Wang, L., Liu, Y., Lei, J. & Zhang, J. Mesoporous graphitic carbon nitride materials: Synthesis and modifications. Res. Chem. Intermed. 42, 3979–3998 (2016).
Tan, S. et al. Meso-g-C3N4/g-C3N4 nanosheets laminated homojunctions as efficient visible-light-driven photocatalysts. Int. J. Hydrog. Energy 42, 25969–25979 (2017).
Yang, Z., Zhang, Y. & Schnepp, Z. Soft and hard templating of graphitic carbon nitride. J. Mater. Chem. A 3, 14081–14092 (2015).
Yan, H. Soft-templating synthesis of mesoporous graphitic carbon nitride with enhanced photocatalytic H2 evolution under visible light. Chem. Commun. 48, 3430–3432 (2012).
Xu, J., Wang, Y. & Zhu, Y. Nanoporous graphitic carbon nitride with enhanced photocatalytic performance. Langmuir 29, 10566–10572 (2013).
Dong, G. & Zhang, L. Porous structure dependent photoreactivity of graphitic carbon nitride under visible light. J. Mater. Chem. 22, 1160–1166 (2012).
Dong, G., Ho, W., Li, Y. & Zhang, L. Facile synthesis of porous graphene-like carbon nitride (C6N9H3) with excellent photocatalytic activity for NO removal. Appl. Catal. B Environ. 174, 477–485 (2015).
Ma, H., Shi, Z., Li, Q. & Li, S. Preparation of graphitic carbon nitride with large specific surface area and outstanding N2 photofixation ability via a dissolve-regrowth process. J. Phys. Chem. Solids 99, 51–58 (2016).
Dong, Y. et al. Morphological control of tubular g-C3N4 and their visible-light photocatalytic properties. Mater. Lett. 196, 100–103 (2017).
Wang, X. L. & Yang, H. G. Facile fabrication of high-yield graphitic carbon nitride with a large surface area using bifunctional urea for enhanced photocatalytic performance. Appl. Catal. B Environ. 205, 624–630 (2017).
Balu, S., Chen, Y.-L., Juang, R.-C., Yang, T.C.-K. & Juan, J. C. Morphology-controlled synthesis of α-Fe2O3 nanocrystals impregnated on g-C3N4–SO3H with ultrafast charge separation for photoreduction of Cr(VI) under visible light. Environ. Pollut. 267, 115491 (2020).
Kaur, G., Bala, K., Devi, S. & Banerjee, B. Camphorsulfonic acid (CSA): An efficient organocatalyst for the synthesis or derivatization of heterocycles with biologically promising activities. Curr. Green Chem. 5, 150–167 (2018).
Paul, N., Murugavel, M., Muthusubramanian, S. & Sriram, D. Camphorsulfonic acid catalysed facile tandem double Friedlander annulation protocol for the synthesis of phenoxy linked bisquinoline derivatives and discovery of antitubercular agents. Bioorg. Med. Chem. Lett. 22, 1643–1648 (2012).
Elinson, M. N. et al. Solvent-free cascade reaction: Direct multicomponent assembling of 2-amino-4H-chromene scaffold from salicylaldehyde, malononitrile or cyanoacetate and nitroalkanes. Tetrahedron 66, 4043–4048 (2010).
Srivastava, N., Verma, M., Thakur, A., Bharti, R. & Sharma, R. Contemporary progress in the applications of iron-based magnetic nanoparticles in multicomponent synthesis: A review. Curr. Org. Chem. 26, 2122–2142 (2022).
Oshiro, P. B., Lima, P. S. D. S. G., De Menezes, M. L. & da Silva-Filho, L. C. Synthesis of 4H-chromenes promoted by NbCl5 through multicomponent reaction. Tetrahedron. Lett. 56, 4476–4479 (2015).
dos Santos, W. H. & da Silva-Filho, L. C. New method for the synthesis of chromeno [4, 3-b] chromene derivatives via multicomponent reaction promoted by niobium pentachloride. Tetrahedron Lett. 58, 894–897 (2017).
Akocak, S. et al. One-pot three-component synthesis of 2-amino-4H-chromene derivatives by using monodisperse Pd nanomaterials anchored graphene oxide as highly efficient and recyclable catalyst. Nano-Struct. Nano-Objects 11, 25–31 (2017).
Boominathan, M., Nagaraj, M., Muthusubramanian, S. & Krishnakumar, R. V. Efficient atom economical one-pot multicomponent synthesis of densely functionalized 4H-chromene derivatives. Tetrahedron 67, 6057–6064 (2011).
Sabry, N. M., Mohamed, H. M., Khattab, E. S. A., Motlaq, S. S. & El-Agrody, A. M. Synthesis of 4H-chromene, coumarin, 12H-chromeno [2, 3-d] pyrimidine derivatives and some of their antimicrobial and cytotoxicity activities. Eur. J. Med. Chem. 46, 765–772 (2011).
Patil, S. A. et al. New substituted 4H-chromenes as anticancer agents. Bioorgan. Med. Chem. Lett. 22, 4458–4461 (2012).
Pradhan, K., Paul, S. & Das, A. R. Magnetically retrievable nano crystalline CuFe2O4 catalyzed multi-component reaction: A facile and efficient synthesis of functionalized dihydropyrano [2, 3-c] pyrazole, pyrano [3, 2-c] coumarin and 4 H-chromene derivatives in aqueous media. Catal. Sci. Technol. 4, 822–831 (2014).
Katiyar, M. K. et al. Synthetic strategies and pharmacological activities of chromene and its derivatives: An overview. J. Mol. Struct. 1263, 133012 (2022).
Wen, Z., Yang, K. C., Deng, J. F. & Chen, L. Advancements in the preparation of 4H-chromenes: An overview. Adv. Synth. Catal. 365, 1290–1331 (2023).
Liu, Z.-Q. et al. Alkene-modified Fe3O4 nanoparticle-mediated construction of functionalized mesoporous poly(ionic liquid)s: Synergistic catalysis of mesoporous confinement effect and hydrogen proton for organic transformations. Mol. Catal. 504, 111437 (2021).
Yu, Y.-Y., Liu, Z.-Q., Zhang, G.-Q., Liu, Y.-J. & Ying, A.-G. Rationally designed novel multifunctional poly(ionic liquid) s for ultra-selective valorization of Yiwu lignite to monocyclic aromatic compounds. J. Clean. Prod. 330, 129775 (2022).
Yu, Y.-Y. et al. Synergistic catalysis: A powerful new strategy for the production of lignin-derived aromatic monomers. Fuel Process. Technol. 235, 107388 (2022).
Chen, S. et al. A Lewis acid-catalyzed tandem reaction enabling 2-arylglycerol derivative as versatile 1,3-biselectrophiles for the synthesis of 4H-chromenes and 2-pyridinones. Chin. Chem. Lett. 8, 108130 (2023).
Han, L., Quan, X., Shao, X., Xu, X. & Li, Z. Lewis acid-controlled divergent condensation of 1,1-bis (methylthio)-2-nitroethylene and salicylaldehydes for the synthesis of 3-nitrocoumarins and 4H-chromenes. Tetrahedron Lett. 118, 154080 (2023).
Kshatriya, R. et al. Brønsted acid catalyzed domino synthesis of functionalized 4H-chromens and their ADMET, molecular docking and antibacterial studies. ChemistrySelect 4, 7943–7948 (2019).
Matloubi Moghaddam, F., Eslami, M. & Hoda, G. Cysteic acid grafted to magnetic graphene oxide as a promising recoverable solid acid catalyst for the synthesis of diverse 4H-chromene. Sci. Rep. 10, 20968 (2020).
Sharma, S. et al. Fe3O4-supported sulfonated graphene oxide as a green and magnetically separable nanocatalyst for synthesis of 2-amino-3-cyano-4 H-chromene derivatives and their in-silico studies. Synth. Commun. 52, 1926–1955 (2022).
Khazaee, A., Jahanshahi, R., Sobhani, S., Skibsted, J. & Sansano, J. M. Immobilized piperazine on the surface of graphene oxide as a heterogeneous bifunctional acid–base catalyst for the multicomponent synthesis of 2-amino-3-cyano-4H-chromenes. Green. Chem. 22, 4604–4616 (2020).
Khodabakhshi, M. R. & Baghersad, M. H. Magnetic UiO-66 functionalized with 4,4′-diamino-2,2′-stilbenedisulfonic as a highly recoverable acid catalyst for the synthesis of 4H-chromenes in green solvent. Sci. Rep. 12, 5531 (2022).
Nope, E. et al. Solvent-free microwave-assisted multicomponent synthesis of 4H-chromenes using Fe3O4-based hydrotalcites as bifunctional catalysts. ChemistrySelect 7, e202104360 (2022).
Hiremath, P. B. & Kamanna, K. A microwave accelerated sustainable approach for the synthesis of 2-amino-4H-chromenes catalysed by WEPPA: A green strategy. Curr. Microw. Chem. 6, 30–43 (2019).
Sarmah, D., Borah, K. K. & Bora, U. Aqueous extracts of biomass ash as an alternative class of green solvents for organic transformations: A review update. Sustain. Chem. Pharm. 24, 100551 (2021).
Badiger, K. B., Giddaerappa, R., Hanumanthappa, R., Sannegowda, L. K. & Kamanna, K. An agro-waste based eco-friendly synthesis, electrochemical behavior and anti-oxidant properties evaluation of pyrano [2, 3-c] pyrazole and pyrazolyl-4H-chromenes derivatives. ChemistrySelect 7, e202104033 (2022).
Chen, L. et al. Visible light-induced green synthesis of 2-amino-4H-chromenes. Environ. Chem. Lett. 18, 2157–2163 (2020).
Ryzhkova, Y. E. et al. Green electrocatalytic Assembling of salicylaldehydes, kojic acid, and malonic acid derivatives into 2-amino-4H-chromenes as potent anti-inflammatory agents. ChemistrySelect 7, e202202872 (2022).
Chatterjee, R., Bhukta, S. & Dandela, R. Ionic liquid-assisted synthesis of 2-amino-3-cyano-4H-chromenes: A sustainable overview. J. Heterocycl. Chem. 59, 633–654 (2022).
Behravesh, S., Fareghi-Alamdari, R. & Badri, R. Sulfonated reduced graphene oxide (RGO-SO3H): As an efficient nanocatalyst for one-pot synthesis of 2-amino-3-cyano-7-hydroxy-4H-chromenes derivatives in water. Polycycl. Aromat. Compd. 38, 51–65 (2018).
Gorji, F. M. & Monadi, N. Synthesis and characterization of Cu(II) Schiff base complex immobilized on graphene oxide/α-Fe2O3 as heterogeneous catalyst for the three-component synthesis of 2-amino-4H-chromenes derivatives and dye reduction. Synth. Met. 258, 116199 (2019).
Wanzheng, M., Ebadi, A. G., Javahershenas, R. & Jimenez, G. One-pot synthesis of 2-amino-4H-chromene derivatives by MNPs@Cu as an effective and reusable magnetic nanocatalyst. RSC Adv. 9, 12801–12812 (2019).
Gajurel, S., Sarkar, R., Sarkar, F. K., Kyndiah, L. & Pal, A. K. Versatile and sustainable approach to access biologically relevant chromeno [2, 3-b] pyridine and benzylpyrazolyl coumarin derivatives using graphitic carbon nitride as a reusable heterogeneous catalyst. ACS Omega 7, 48087–48099 (2022).
Santhisudha, S., Mohan, G., Rani, T. S., Reddy, P. V. & Reddy, C. S. Design and synthesis of benzopyranopyrimidinyl phosphonates as cytotoxic and antioxidant agents. Lett. Drug Des. Discov. 16, 721–733 (2019).
Naeimi, H. & Mohammadi, S. Synthesis of 1H-isochromenes, 4H-chromenes and orthoaminocarbonitrile tetrahydronaphthalenes by CaMgFe2O4 base nanocatalyst. ChemistrySelect 5, 2627–2633 (2020).
Naeimi, H. & Mohammadi, S. Synthesis of 1H-isochromenes, 4H-chromenes, and ortho-aminocarbonitrile tetrahydronaphthalenes from the same reactants by using metal-free catalyst. J. Heterocycl. Chem. 57, 50–59 (2020).
Kour, J., Gupta, M. & Sharma, N. Ethylenediamine functionalized cellulose acetate [CAEDA] nanosized solid base catalyst in the synthesis of 2-amino-4H-chromenes and 5-substituted-1H-tetrazoles. ChemistrySelect 6, 2817–2825 (2021).
Maleki, A., Hajizadeh, Z. & Valadi, K. Green and eco-friendly mica/Fe3O4 as an efficient nanocatalyst for the multicomponent synthesis of 2-amino-4H-chromene derivatives. Green. Chem. Lett. Rev. 14, 62–72 (2021).
González-Rodal, D., Palomino, G. T., Cabello, C. P. & Pérez-Mayoral, E. Amino-grafted Cu and Sc metal-organic frameworks involved in the green synthesis of 2-amino-4H-chromenes. Mechanistic understanding. Microporous. Mesoporous. Mater. 323, 111232 (2021).
Anaikutti, P. et al. Indolyl-4H-chromenes: Multicomponent one-pot green synthesis, in vitro and in silico, anticancer and antioxidant studies. J. Mol. Struct. 1266, 133464 (2022).
Ferdousian, R., Behbahani, F. K. & Mohtat, B. Synthesis and characterization of Fe3O4@Sal@Cu as a novel, efficient and heterogeneous catalyst and its application in the synthesis of 2-amino-4H-chromenes. Mol. Divers. 26, 3295–3307 (2022).
Rezaei-Seresht, E., Noroozi, S. & Mahdavi, B. Nanocomposite Fe3O4@GO-NH as a reusable heterogeneous catalyst for the three-component synthesis of 2-amino-4H-chromenes. Org. Prep. Proced. Int. 54, 268–276 (2022).
Oboudatian, H. S. & Safaei-Ghomi, J. Silica nanospheres KCC-1 as a good catalyst for the preparation of 2-amino-4H-chromenes by ultrasonic irradiation. Sci. Rep. 12, 2381 (2022).
Mohamadpour, F. Nano-SiO2 as a reusable nanocatalyst promoted green synthesis of 2-amino-4H-chromenes in an aqueous solution. Biointerface Res. Appl. Chem. 13, 410–421 (2022).
Gari, M. S., Narasaiah, B. P., Pandurengan, A. & Kumar, B. Synthesis and antioxidant activity of some novel 4H-chromene derivatives catalysed by biogenic tin oxide nanoparticles (2023).
Zadeh, F. S., Mohammadi, M. K., Rayatzadeh, A. & Hasanzadeh, N. One pot synthesis of bis(dihydropyrimidinone) and tetrahydro-4H-chromenes derivatives using Ag2O/GO/TiO2 composite nanostructure. Inorg. Nano-Met. Chem. 53, 8–18 (2023).
Adibi, H., Hosseinzadeh, L., Amirafshari, M. & Jalilian, F. Synthesis and characterization of novel 4-aryl-4H-chromene derivatives using borax and evaluation of their anticancer effects. Anticancer Agents Med. Chem. (2023).
Li, G., Yang, N., Wang, W. & Zhang, W. Synthesis, photophysical and photocatalytic properties of N-doped sodium niobate sensitized by carbon nitride. J. Phys. Chem. C 113, 14829–14833 (2009).
Elbanna, O., Fujitsuka, M. & Majima, T. g-C3N4/TiO2 mesocrystals composite for H2 evolution under visible-light irradiation and its charge carrier dynamics. ACS Appl. Mater. Interfaces 9, 34844–34854 (2017).
Rashidizadeh, A., Ghafuri, H., Goodarzi, N. & Azizi, N. Tandem oxidative amidation of alcohols catalyzed by copper modified well-ordered mesoporous graphitic carbon nitride. Solid State Sci. 109, 106427 (2020).
Liu, G. et al. Unique electronic structure induced high photoreactivity of sulfur-doped graphitic C3N4. J. Am. Chem. Soc. 132, 11642–11648 (2010).
Verma, S., Baig, R. N., Nadagouda, M. N. & Varma, R. S. Photocatalytic CH activation and oxidative esterification using Pd@g-C3N4. Catal. Today 309, 248–252 (2018).
Azizi, N., Farzaneh, F. & Habibnejad, N. Recyclable magnetic camphor sulfonic acid: A reliable and highly efficient ionic organocatalyst for benzothiazin-4-one synthesis in green media. Catal. Lett. 8, 1–12 (2022).
Hosseini, S. & Amoozadeh, A. An efficient and robust method for selective conversion of aniline to azobenzene using nano-TiO2-P25-SO3H, under visible light irradiation. Photochem. Photobiol. 97, 278–288 (2020).
Kaur, M. & Pal, K. Synthesis, characterization and electrochemical evaluation of hydrogen storage capacity of graphitic carbon nitride and its nanocomposites in an alkaline environment. J. Mater. Sci. Mater. Electron. 32, 12475–12489 (2021).
Han, Z., Wang, N., Fan, H. & Ai, S. Ag nanoparticles loaded on porous graphitic carbon nitride with enhanced photocatalytic activity for degradation of phenol. Solid State Sci. 65, 110–115 (2017).
Cui, S. et al. g-C3N4/CeO2 binary composite prepared and its application in automobile exhaust degradation. Materials 13, 1274 (2020).
Hosseini, S. & Amoozadeh, A. Plasma treatment as a promising environmentally benign approach for synthesis of valuable multi-gas doped nano-TiO2-P25: An efficient way to boost the photocatalytic performance under visible light illumination. Photochem. Photobiol. 97, 672–687 (2021).
Shamanaev, I. V. et al. Synergetic effect of Ni2P/SiO2 and γ-Al2O3 physical mixture in hydrodeoxygenation of methyl palmitate. Catalysts 7, 329 (2017).
Chong, R. et al. Enhanced photocatalytic reduction of CO2 on rutile TiO2/MgAl layered double oxides with H2O under ambient temperature. Catal. Lett. 150, 1061–1071 (2020).
Choudhary, P. et al. Sulfonic acid functionalized graphitic carbon nitride as solid acid–base bifunctional catalyst for Knoevenagel condensation and multicomponent tandem reactions. Mater. Chem. Front. 5, 6265–6278 (2021).
Gupta, A. K., Kumari, K., Singh, N., Raghuvanshi, D. S. & Singh, K. N. An eco-safe approach to benzopyranopyrimidines and 4H-chromenes in ionic liquid at room temperature. Tetrahedron Lett. 53, 650–653 (2012).
Brahmachari, G. & Das, S. Sodium formate-catalyzed one-pot synthesis of benzopyranopyrimidines and 4-thio-substituted 4H-chromenes via multicomponent reaction at room temperature. J. Heterocycl. Chem. 52, 653–659 (2015).
Bosica, G. & Abdilla, R. Piperazine-amberlyst® 15-catalysed synthesis of 2-amino-4H-chromenes, chromeno [2, 3-b] pyridines and chromeno [2, 3-d] pyrimidines. Tetrahedron Green Chem. 1, 100011 (2023).
Shaterian, H. R. & Aghakhanizadeh, M. Mild preparation of chromeno [2, 3-d] pyrimidines catalyzed by Brønsted acidic ionic liquids under solvent-free and ambient conditions. Res. Chem. Intermed. 39, 3877–3885 (2013).
Nasab, M. J. & Kiasat, A. R. Covalently anchored 2-amino ethyl-3-propyl imidazolium bromideon SBA-15 as a green, efficient and reusable Brønsted basic ionic liquid nanocatalyst for one-pot solvent-free synthesis of benzopyranopyrimidines under ultrasonic irradiation. RSC Adv. 5, 75491–75499 (2015).
Niknam, K. & Borazjani, N. Synthesis of benzopyrano [2, 3-d] pyrimidines using silica-bonded N-propylpiperazine sodium N-propionate as heterogeneous solid base catalyst under solvent-free conditions. Monatsh. Chem. Month. 147, 1129–1135 (2016).
Ghorbani-Vaghei, R. et al. Efficient one-pot synthesis of quinazoline and benzopyrano [2, 3-d] pyrimidine derivatives catalyzed by N-bromosulfonamides. J. Heterocycl. Chem. 54, 215–225 (2017).
Kour, G. & Gupta, M. A nano silver-xerogel (Ag nps@ modified TEOS) as a newly developed nanocatalyst in the synthesis of benzopyranopyrimidines (with secondary and primary amines) and gem-bisamides. Dalton Trans. 46, 7039–7050 (2017).
Acknowledgements
We are grateful to the Chemistry and Chemical Engineering Research Center of Iran for supporting this research.
Author information
Authors and Affiliations
Contributions
Project administration, N.A.; Conceptualization, S.H. and N.A.; Data curation, S.H. and N.A.; Formal analysis, S.H.; Resources, N.A.; Investigation, S.H.; Methodology, S.H. and N.A.; Validation, S.H. and N.A.; Writing-original draft, S.H. All the authors have reviewed the manuscript and agreed the submission and publication.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hosseini, S., Azizi, N. CSA@g-C3N4 as a novel, robust and efficient catalyst with excellent performance for the synthesis of 4H-chromenes derivatives. Sci Rep 13, 18961 (2023). https://doi.org/10.1038/s41598-023-46122-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-46122-y
- Springer Nature Limited