Abstract
High-entropy-alloy (HEA) superconductors are a new class of disordered superconductors. However, commonality of superconducting characteristics of HEA materials is unclear. Here, we have investigated the crystal and electronic structure, and the robustness of superconducting states in a HEA-type metal telluride (MTe; M = Ag, In, Sn, Pb, Bi) under high pressure, and the results were compared with the pressure effects for a middle-entropy system (AgPbBiTe3) and a reference system of PbTe. When the crystal structure is CsCl-type, all phases show superconductivity under high pressure but exhibit different pressure dependences of the transition temperature (Tc). For PbTe, its Tc decreases with pressure. In contrast, the Tc of HEA-type AgInSnPbBiTe5 is almost independent of pressure, for pressures ranging from 13.0 to 35.1 GPa. Those results suggest that the robustness of superconductivity to external pressure is linked to the configurational entropy of mixing at the M site in MTe. Since the trend is quite similar to previous work on a HEA (Ti–Zr–Hf–Nb–Ta), where the robustness of superconductivity was observed up to ~ 200 GPa, we propose that the robustness of superconductivity under high pressure would be a universal feature in HEA-type superconductors.
Similar content being viewed by others
Introduction
The superconductivity of disordered materials has been extensively studied because of an observation made on the insulator-superconductor transition or disorder-induced superconductivity1,2,3. In addition, recent studies on BiS2-based layered superconductors have shown the importance of controlling the local structural disorder to improve superconducting properties4,5,6,7. As a new category of disordered superconductors, high-entropy alloys (HEAs), which are alloys containing five or more elements with an atomic concentration between 5 and 35%8,9, have been extensively studied, leading to the discovery of a wide range of HEA superconductors10,11,12. One of the notable features is the difference in characteristics of superconductivity among conventional metal or alloy superconductors, superconducting thin films, and HEA superconductors11,13. Namely, the dependence of Tc on valence electron count (VEC) for HEAs exhibits interesting trends when that was compared with those for classical alloys (metals) and amorphous alloys13. In the CsCl-type HEAs, the Tc-VEC exhibits opposite trend to that for the classical and amorphous alloys. In the α-Mn phase, although the trend of the Tc-VEC exhibits commonality among HEAs, classical, and amorphous alloys, Tc for HEAs is clearly low. Therefore, detailed investigations are necessary to understand universality of local structure and superconductivity characteristics in HEA-type superconductors. Furthermore, the robustness of superconductivity to extremely high pressure (HP), for pressures up to 190 GPa, in an HEA, (TaNb)0.67(HfZrTi)0.33, was observed14. The high configurational entropy of mixing (ΔSmix) reduces the Gibbs’s free energy, and therefore stabilization of the phase is expected. The equation for calculating the Gibb’s free energy is ΔG = ΔH − TΔSmix, where ΔH is the enthalpy and T is the absolute temperature. ΔSmix can be calculated using the equation ΔSmix = − R ∑i cilnci, where, R is the gas constant and ci is the atomic ratio of the element (i)8. The discovery of the robustness of superconductivity under an extremely high pressure was considered to be related to the high ΔSmix, but similar robustness of superconductivity under an extremely high pressure and a high transition temperature (Tc) of 19 K was observed in a low-entropy Nb–Ti alloy15. Therefore, the effects of ΔSmix on the crystal structure, electronic structure, and superconducting properties of HEAs are still unclear. To address this issue, further investigation of HP effects on HEA-type materials is needed.
We recently developed superconducting HEA-type compounds, in which one of the crystallographic sites is alloyed with the criterion similar to HEAs16. Since compounds with two or more crystallographic sites have unique chemical bonds, various (novel) effects of the introduction of HEA site to electronic and structural properties would be expected, which is so-called cocktail effect in the field of HEAs. In the layered BiS2-based superconductor RE(O,F)BiS2, the rare-earth site (RE) was alloyed with five different RE elements17, and the improvement of superconducting properties (bulk nature of superconductivity) with increasing ΔSmix was observed18. Tc was not affected by ΔSmix, and therefore its insensitivity to ΔSmix in the BiS2-based superconductor is explained using a two-dimensional structure, since similar insensitivity was also observed in an RE123 cuprate with an HEA-type RE site19. In contrast, Tc of NaCl-type metal telluride, which is the target phase of this study, shows that its sensitivity to ΔSmix of HEA-type systems is larger than that of metal tellurides with one or two constituent elements at the metal site20,21.
On the basis of the facts described above, we considered that the metal telluride system is suitable for the discussion of the effects of high ΔSmix on the crystal structure (phase stability) and superconducting properties under high pressure. Here, we studied the crystal structure, electronic structure, and superconducting properties of three tellurides (MTe; M = Ag, In, Sn, Pb, Bi) with different ΔSmix values at the M site: PbTe (ΔSmix = 0), AgPbBiTe3 (ΔSmix = 1.1R), and AgInSnPbBiTe5 (ΔSmix = 1.6R). The pressure evolutions of the crystal structure and electronic transport properties were reported in previous studies22,23,24,25,26. Although PbTe is a semiconductor under ambient and low pressures, it undergoes metallization under high pressures, and a superconducting transition is observed for pressures above 15 GPa22,23. PbTe undergoes structural transitions as follows: cubic NaCl-type (Fm–3m) structure under low pressures, orthorhombic (Pnma) structure under moderate pressures, and cubic CsCl-type (Pm–3m) structure under HP24,25,26. There is a report on synthesis and thermoelectric properties of AgPbBiTe3, but the structural and physical properties of AgPbBiTe3 have not been reported27. In this study, we established a phase diagram of the crystal structures, as well as one for superconductivity versus pressure for both AgPbBiTe3 and AgSnInPbBiTe5. We also studied PbTe to examine the effects of configurational entropy of mixing. The pressure phase diagrams for the three tellurides are used to compare the crystal and electronic structures in detail. The results show that the pressure phase diagram of the crystal structure is largely modified by the effect of ΔSmix. Furthermore, we found that the pressure dependence of Tc in the HP phase (CsCl-type phase) exhibits a clear difference among the three compounds. In the HP phase, the Tc for PbTe decreases with pressure, but that for HEA-type AgInSnPbBiTe5 exhibits a flat dependence, which suggests that the superconducting state of AgInSnPbBiTe5 is robust to pressure. Our present findings show an analogical conclusion in the case of (TaNb)0.67(HfZrTi)0.3314 and suggest that the HEA effects universally enhance the robustness of superconductivity under high pressure.
Results
Electrical resistance
Figure 1a shows the temperature dependence of the electrical resistance of AgInSnPbBiTe5 measured using the conventional four-probe method at ambient pressure. \(T_{{\text{c}}}^{{{\text{zero}}}}\) was 1.8 K, which is slightly lower than that reported in previous research20. We measured the electrical resistance (at National Institute for Materials Science) after several days since the sample was synthesized by HP annealing (at Tokyo Metropolitan University), and a slight aging effect of Tc was noticed in MTe superconductors synthesized under high pressure28,29. We consider that the slight decrease in Tc can be understood by the change in the internal strains because the XRD patterns do not show a remarkable change after aging in the HP-synthesized MTe samples. Therefore, we continued to perform resistance measurements under high pressure using a diamond-anvil cell (DAC).
Figure 1b shows the temperature dependences of the electrical resistance of AgInSnPbBiTe5 measured under various pressures with a DAC. Normal-state resistance decreases with pressure, for pressures up to 9.3 GPa and increases with pressure for pressures above 15.5 GPa. An onset of the superconducting transition was observed at 2 K under 6.5 GPa, and the zero-resistance state was observed at \(T_{{\text{c}}}^{{{\text{zero}}}}\) = 2 K under 10.2 GPa. At low pressures below 6.5 GPa, the onset of superconductivity was not observed. We consider that Tc does not remarkably change but slightly decreases with pressure because a slight decrease in \(T_{{\text{c}}}^{{{\text{onset}}}}\) was observed in the NaCl-type phase of AgPbBiTe3. In the middle-pressure range, two-step transitions were observed, which would be due to the coexistence of two phase under relatively inhomogeneous pressures generated by DAC. As shown in Fig. 2a, the \(T_{{\text{c}}}^{{{\text{onset}}}}\) monotonously increased with pressure until it reached 13.0 GPa, and then it became insensitive to pressure for pressures ranging from 13.0 to 35.1 GPa (P = 35.1 GPa is the chosen maximum pressure for the experiment). The results indicate that the Tc in the CsCl-type structure of AgInSnPbBiTe5 is independent of applied pressure, while lattice constant decreases with pressure. The highest \(T_{{\text{c}}}^{{{\text{zero}}}}\) and \(T_{{\text{c}}}^{{{\text{onset}}}}\) observed in the experiment on AgInSnPbBiTe5 are 4.5 K and 5.3 K, respectively. See Fig. S1 for the determination criterion for \(T_{{\text{c}}}^{{{\text{onset}}}}\).
Pressure evolutions of Tc of metal tellurides with different configurational entropy of mixing. (a) Pressure dependence of \(T_{{\text{c}}}^{{{\text{onset}}}}\) of AgInSnPbBiTe5. Open and filled circles indicate the data taken without a pressure cell, and the data that was measured with DAC. The structural types are indicated according to structural analyses in Fig. 3d. (b) Pressure dependences of \(T_{{\text{c}}}^{{{\text{onset}}}}\) for PbTe, AgPbBiTe3, and AgInSnPbBiTe5. (c) Schematic images of NaCl-type crystal structure and configurational entropy of mixing (ΔSmix) at the M site of PbTe, AgPbBiTe3, and AgInSnPbBiTe5.
To compare the pressure evolution of Tc in AgInSnPbBiTe5 with that of PbTe and AgPbBiTe3, the pressure dependences of \(T_{{\text{c}}}^{{{\text{onset}}}}\) for PbTe and AgPbBiTe3 were examined (see Fig. 2c for structural difference and Figs. S2 and S3 for the resistance measurements), and the resulting \(T_{{\text{c}}}^{{{\text{onset}}}}\)-P plots are shown in Fig. 2b. PbTe is a semiconductor at ambient and low pressures, but exhibits a pressure-induced superconducting transition above 17 GPa in the CsCl-type structure22. At higher pressures, \(T_{{\text{c}}}^{{{\text{onset}}}}\) of PbTe monotonously decreases with pressure. In the case of AgPbBiTe3, superconductivity was observed at P > 2.6 GPa, and at this instance \(T_{{\text{c}}}^{{{\text{onset}}}}\) reached 6.5 K. The \(T_{{\text{c}}}^{{{\text{onset}}}}\) for AgPbBiTe3 slightly decreases at high pressures. In AgInSnPbBiTe5, superconductivity is observed at low pressures as well because the low-pressure phase, having a NaCl-type structure, itself is a metal and shows superconductivity under ambient pressure (Figs. 1a, 2a). As demonstrated in the next section, the crystal-structure type under high pressure is CsCl-type for all the compounds. However, the trend of the pressure dependences of \(T_{{\text{c}}}^{{{\text{onset}}}}\) in the CsCl-type structure exhibit a clear difference among PbTe, AgPbBiTe3, and AgInSnPbBiTe5. The main findings of this study are that the robustness of superconductivity to pressure in HEA-type AgInSnPbBiTe5 is similar to that observed in (TaNb)0.67(HfZrTi)0.3314. To validate the conclusion, we investigated the pressure evolutions of the crystal structure and the electronic structure for those MTe samples under high pressure.
Crystal structure
Figure 3a–c show the pressure-dependent synchrotron X-ray diffraction (SXRD) patterns for the PbTe, AgPbBiTe3, and AgInSnPbBiTe5 samples, respectively. For all the SXRD patterns, we performed the Rietveld refinement to confirm the structural type and to evaluate the lattice constant. See Tables S1–S3 and Figs. S4–S6 for details on refinements. On the basis of the refinement results, we established structural phase diagrams under high pressure (Fig. 3d–f) by plotting the pressure dependence of volume per unit formula (Z). For PbTe, the structural transition from NaCl-type to Pnma occurs at around 6.80 GPa, and the second transition to CsCl-type takes place at 14.28 GPa. Since the transition gradually occurred, the phase diagram contains mixed phases. The results on PbTe are consistent with the previous work by Li et al.24. For AgPbBiTe3 and AgInSnPbBiTe5, similar phase diagrams were obtained, where the NaCl-type structure is stabilized up to ~ 10 GPa, and the Pnma phase is suppressed. The pressure where the CsCl-type phase is induced is common to the case of PbTe. In all the structural types including the CsCl-type phase, the lattice volume continuously decreases with pressure. Although the difference in the stability of the NaCl-type and Pnma structures may be related to the difference in lattice volume at ambient pressure, we consider that the Pnma phase is suppressed, and the NaCl-type phase is stabilized by the effect of alloying at the M site. We note that configurational entropy of mixing does not affect the structure of the CsCl-type phase, and lattice volume of the CsCl-type phase commonly decreases with pressure in three MTe sample.
Pressure evolutions of crystal structure for metal tellurides with different configurational entropy of mixing. (a–c) SXRD patterns for PbTe, AgPbBiTe3, and AgInSnPbBiTe5. Note that the baseline height of the XRD pattern at each pressure scales to the pressure. (d–f) Lattice volumes divided by Z (chemical formula sum in a unit cell) for PbTe, AgPbBiTe3, and AgInSnPbBiTe5 are plotted as a function of pressure. In (d), the analysis results reported in Ref.24 (Li et al.) are represented by orange lines. Structural types are shown in the figures.
Electronic structure
To examine the effects of pressure and HEA states on the electronic structure, we performed X-ray absorption spectroscopy with partial fluorescence mode (PFY-XAS) for PbTe and AgInSnPbBiTe5. See Fig. S7 for pressure dependences of spectra, and analysis results on the Pb-L3 and Bi-L3 spectra. In general, the absorption spectra at the Pb-L3 absorption edge are similar to those at the Bi-L3 absorption edge. On the basis of analogically referring to other Pb- or Bi-containing compounds30,31, we analyzed the spectra by assuming several peaks. An example of the fit for the PFY-XAS spectra at 27 GPa is shown in Fig. 4a. The PFY-XAS spectra were fitted by assuming some Voigt functions with an arctan-like background31. In this study, we focus on the peaks of P1, P2, and P3, where peak P1 could be assigned as a dipole transition of the 2p3/2 electron into the 6s state, and the peaks shown as P2 and P3 correspond to 6d states of t2g and eg, respectively32,33; we measure 2p3/2 → nd (n > 6) transitions at the Pb L3 absorption edge. There is a p density of states (p DOS) above the Fermi level, however, we mainly observe the dipole-allowed transitions of Pb 2p–6s and Pb 2p–6d, and therefore, the observed spectra do not reflect the Pb 6p DOS spectroscopically. The absorption spectra reflect the empty DOS above the Fermi level generally, with a core hole in the final state.
Electronic structure of PbTe and AgInSnPbBiTe5 under high pressure. (a) Typical Pb-L3 PFY-XAS spectrum and an example of the fit to the spectrum for PbTe at 27 GPa. (b) Pressure dependence of the intensity and the energy of the peak P1 for PbTe. (c) Pressure dependence of the intensity of the peaks P2 and P3 for PbTe. (d) Typical Pb-L3 PFY-XAS spectrum and an example of the fit to the spectrum for AgInSnPbBiTe5 at 28.8 GPa. (e) Pressure dependence of the intensity and the energy of the peak P1 for AgInSnPbBiTe5. (f) Pressure dependence of the intensity of the peaks P2 and P3 for AgInSnPbBiTe5.
For PbTe with a NaCl-type structure, there is a narrow band gap, and the p orbitals of Pb and Te near the Fermi energy are hybridized. See Fig. S8 for the calculated DOS for PbTe34. The valence band is mainly composed of Te 5p orbitals, and also contains the contribution from Pb 6p and 6s, while the conduction band is mainly composed of Pb 6p orbitals, but also contains Te 5p contributions. For PbTe with a CsCl-type structure, band gap is totally closed, and the DOS near the Fermi energy is explained by the contributions from Pb 6p and 6s orbitals, as well as the Te 5p orbitals. Therefore, the pressure evolution of the 6s states which could be resolved in our high-resolution spectroscopy, may play an important role on the closing of the band gap as well as the emergence of superconductivity.
The pressure dependences of the intensity and the energy of peak P1 in PbTe is shown in Fig. 4b. The intensity of peak P1 in Fig. 4b gradually increases with pressure, up to about 5 GPa. The increase in the intensity of P1 indicates an increase in the amount of holes in the Pb 6 s states, which indicates a modification of the band structure. In the middle-pressure phase, (between 5 and 15 GPa) the intensity of P1 does not show a significant change, while it increases remarkably in the HP phase (P > 15 GPa). We note that PbTe with a NaCl-type or Pnma structure is a semiconductor with a band gap at the low-pressure regime, and we also note that the metallic phase is induced in a CsCl-type structure for pressures above 15 GPa22,23,34. The increase of the intensity of P1 corresponds with the increase of the unoccupied 6 s states of the Pb. This may correlate with the emergence of the superconductivity after the closing of the band gap at P > 15 GPa.
On the other hand, the energy of peak P1 shifts to a lower incident energy until it reaches a pressure level of 5 GPa. The incident energy and the intensity do not change in the middle-pressure range of 5–17 GPa, and they start decreasing again for pressures above 18 GPa as shown in Fig. 4b. The shift of the energy of peak P1 to a lower incident energy is explained by the upward shift of the Fermi level or change in the DOS at the Fermi level. Theory suggests that the energy shift of peak P1 may be influenced by the reduction of the band gap23 and the theoretical band gap is in the same order as the energy shift of P1 at 5 GPa.
The intensity of P3 (Pb 6d DOS, eg) shows a trend which is similar to the intensity of P1. The intensity of P2 (Pb 6d DOS, t2g) on the other hand decreases with increasing pressure at P > 17 GPa (Fig. 4c). It is interesting that there is a large change in the electronic structure for pressures above 20 GPa, but the crystal structure still retains its CsCl-type structure in this pressure range. In PbTe, superconductivity suddenly appears above 18 GPa, and Tc decreases with pressure monotonically22. The present result possibly suggests that the change in the electronic structure is not favorable for the superconductivity of MTe, when it has transitioned to the CsCl-type structure.
We also measured the PFY-XAS spectra at the Pb-L3 absorption edges for AgInSnPbBiTe5 as shown in Fig. S7. We observed similar trends in the pressure dependence of the electronic structures as those observed for PbTe. An example of the fit at 28.8 GPa is shown in Fig. 4d. The analysis results on P1, P2, and P3 are plotted in Fig. 4e and f. Figure 4e shows a gradual increase of the P1 intensity with pressure, which is similar to the case of PbTe. The trend of P2 is also similar for the entire pressure range, and that of P3 is basically similar between PbTe and AgInSnPbBiTe5. On the other hand, in AgInSnPbBiTe5, Tc increases rapidly in the pressure range of 6–12 GPa and does not show a significant change with further increasing pressure. The pressure-induced change in the s DOS (P1 intensity) does not reflect the rapid increase of Tc at 6–12 GPa as shown in Fig. 4e. The decrease of the P1 energy at 3.1–6.9 GPa may be related to the rapid increase in Tc. The P1 energy also decreases above 13.4 GPa. This suggests the close of the band gap as discussed above for PbTe. The PFY-XAS spectra at the Bi-L3 absorption edge were also taken, and the analysis results are summarized in Fig. S7. In AgInSnPbBiTe5 the pressure-induced change in the electronic structure seems to be common for Bi and Pb sites; the detailed results are shown under the Supporting Information section. In conclusion, the electronic structures of PbTe and AgInSnPbBiTe5 show a similar pressure dependence, even though the structure of PbTe does not change much in the middle-pressure range (Pnma + CsCl phase), which disappears in AgInSnPbBiTe5. Therefore, the difference in the robustness of superconductivity to pressure in the CsCl-type phase between PbTe and AgInSnPbBiTe5 cannot be explained by the pressure evolutions of crystal and electronic structures.
Discussion
From the structural viewpoint, the impact of the introduction of an HEA site is the suppression of the middle-pressure phase with a Pnma structure. In other words, the low-pressure phase with a NaCl-type structure is stabilized up to a higher pressure of P > 10 GPa in AgInSnPbBiTe5, whereas the NaCl-type phase disappears at ~ 5 GPa for PbTe. Interestingly, the trend of lattice constant in the CsCl-type structure under HP is quite similar for PbTe and AgInSnPbBiTe5. However, as revealed in Fig. 2b, the pressure dependences of \(T_{{\text{c}}}^{{{\text{onset}}}}\) clearly differ since \(T_{{\text{c}}}^{{{\text{onset}}}}\) decreases with pressure for PbTe but does not change largely in the CsCl-type phase for AgInSnPbBiTe5. Furthermore, from the electronic-structure viewpoint, we cannot find a clear correlation between the robustness of superconductivity to pressure and the changes in electronic structure under high pressure. Although there is a possibility of the difference of the contribution of the 6p states, which could not be measured in our spectra, to the conduction band to increase the number of the carriers in AgInSnPbBiTe5.
The results show that the pressure phase diagram of the crystal structure is largely modified by the effect of ΔSmix. In contrast, the electronic structures are not sensitive to the effect of ΔSmix. As shown in Fig. S9, it is clear that the difference in the pressure dependence of \(T_{{\text{c}}}^{{{\text{onset}}}}\) in the CsCl-type phases is independent of lattice constant, which implies the importance of configurational entropy of mixing modifying local structures. To understand the HEA effects on structural and electronic properties for MTe under high pressure, further studies using various probes are needed. However, commonality on the robustness of superconductivity to external pressure in the superconducting HEA (TaNb)0.67(HfZrTi)0.3314 and the HEA-type metal telluride AgInSnPbBiTe5 would be demonstrating the universal characteristics of superconductivity in HEA-type materials. Thus, the present results propose that the combination of HP and HEA effects will open a new pathway to the development of new disordered superconductors with exotic superconducting states.
Conclusion
We have studied the crystal and electronic structure and the robustness of superconducting states in a HEA-type metal telluride (MTe; M = Ag, In, Sn, Pb, Bi) under high pressure using a polycrystalline sample, and the results were compared with the pressure effects for a middle-entropy system (AgPbBiTe3) and a reference system of PbTe. PbTe exhibits a structural transition from a NaCl-type to an orthorhombic Pnma structure at low pressures, and further transitions to a CsCl-type structure at high pressures. When the superconductivity of the CsCl-type PbTe is observed, it is found that its superconducting transition temperature (Tc) decreases with pressure. In contrast, in HEA-type AgInSnPbBiTe5, Tc is almost independent of pressure, for pressures ranging from 13.0 to 35.1 GPa. In addition, the middle-entropy system, AgPbBiTe3, shows a slight decrease in Tc with pressure in the CsCl-type structure, which is intermediate trend between PbTe and AgInSnPbBiTe5. Those results suggest that the robustness of superconductivity to external pressure has been enhanced by the increase in configurational entropy of mixing at the metal (M) site in MTe. To further clarify the effects of the modification of the configurational entropy of mixing on the superconducting states and the electronic structure of MTe, synchrotron X-ray absorption spectroscopy with partial fluorescence mode (PFY-XAS) for three MTe polycrystalline samples of PbTe and AgInSnPbBiTe5 were performed. Noticeably, the evolutions of electronic structure under high pressure do not largely differ between PbTe and AgInSnPbBiTe5; hence, the difference in the robustness of superconductivity in PbTe and AgInSnPbBiTe5 under high pressure is not explained by the difference in their electronic structure. According to the results of this work and previous work on a HEA (Ti–Zr–Hf–Nb–Ta), where the robustness of superconductivity was observed up to ~ 200 GPa, we propose that the robustness of superconductivity under high pressure would be a universal feature in HEA-type superconductors.
Methods
The polycrystalline sample of PbTe was synthesized by the solid-state reaction of Pb (99.9%) and Te (99.999%) at 900 °C. To obtain a pellet for resistance measurements, pelletizing and second annealing were performed. The polycrystalline samples of AgPbBiTe3 and AgInSnPbBiTe5 were synthesized using an HP synthesis method where the pressure was kept below 3 GPa, and the temperature kept at 500 °C for 30 min as described in Ref.20. The precursor powders of AgPbBiTe3 and AgInSnPbBiTe5 were synthesized by a solid-state reaction of Ag powders (99.9%) and grains of In (99.99%), Sn (99.999%), Pb (99.9%), Bi (99.999%), and Te (99.999%) at 800 °C, with the nominal compositions.
The electrical resistance measurements were performed at ambient pressure using the conventional four-probe method on a GM refrigerator system. Resistance measurements under high pressure were performed on polycrystalline powder on a Physical Property Measurement System (Quantum Design) using an originally designed diamond anvil cell (DAC) with boron-doped diamond electrodes35,36,37. The sample was placed on the boron-doped diamond electrodes in the center of the bottom anvil. The surface of the bottom anvil, except for the sample space and electrical terminal, were covered with the undoped diamond insulating layer. The cubic boron nitride powders with ruby manometer were used as a pressure-transmitting medium. The applied pressure was estimated by the fluorescence from ruby powders38 and the Raman spectrum from the culet of top diamond anvil39 using an inVia Raman microscope (RENISHAW). The definition of Tc is described in Fig. S1.
Pressure dependences of the synchrotron X-ray powder diffraction (SXRD) patterns were measured at BL12B2, SPring-8, using a 3-pin plate diamond anvil cell (DAC, Almax easyLab Industries) with a CCD detection system at room temperature (~ 293 K). Culet size of the diamond anvil was 0.4 mm with a stainless-steel gasket. We took an arrangement of both incoming and outgoing x-ray beams passing through the diamonds with incident photon energy of 18 keV. A two-dimensional image of the CCD system was integrated using the FIT2D program40. Silicone oil was used as a pressure-transmitting medium, and pressure was monitored using the ruby fluorescence method41. The SXRD data was analyzed through Jana 2006 software42 using the Rietveld method.
The pressure dependence of the high-resolution X-ray absorption spectra was measured at beamline BL12XU, SPring-8. Membrane-controlled DACs with a 0.3 mm culet and that with a 0.4 mm culet were used for PbTe and AgInSnPbBiTe5, respectively, and silicone oil was used as a pressure-transmitting medium. Beryllium gaskets with a 3 mm diameter were pre-indented at the center. The thickness was approximately 67 μm for PbTe and 31 μm for AgInSnPbBiTe5, and the diameters of the sample chamber in the gaskets were approximately 110 μm for PbTe and 140 μm for AgInSnPbBiTe5. We employed X-ray absorption spectroscopy (XAS) with a partial fluorescence mode (PFY-XAS), which has an advantage of a higher resolution as compared to that of normal XAS43,44. We used the Be gasket in plane geometry where both incoming and outgoing x-ray beams passed through the Be gasket. A Johann-type spectrometer equipped with a spherically bent Si(555) analyzer crystal (radius of ~ 1 m), and a Si solid state detector were used to analyze the Bi Lα1 (10.839 keV, 3d5/2–2p3/2) emission at the Bi L3 absorption edge, and Pb Lα1 (10.551 eV, 3d5/2–2p3/2) emission at the Pb L3 absorption edge45. The incident beam is focused at 17 μm × 40 μm by the K-B mirror located at the sample position.
Data availability
The data that support the findings of this study are available from the corresponding author (Y.M.) upon reasonable request.
References
Dubi, Y., Meir, Y. & Avishai, Y. Nature of the superconductor–insulator transition in disordered superconductors. Nature 449, 876 (2007).
Gastiasoro, M. N. & Andersen, B. M. Enhancing superconductivity by disorder. Phys. Rev. B 98, 184510 (2018).
Zhao, K. et al. Disorder-induced multifractal superconductivity in monolayer niobium dichalcogenides. Nat. Phys. 15, 904 (2019).
Mizuguchi, Y. Material development and physical properties of bis2-based layered compounds. J. Phys. Soc. Jpn. 88, 041001 (2019).
Mizuguchi, Y. et al. Evolution of anisotropic displacement parameters and superconductivity with chemical pressure in BiS2-Based REO0.5F0.5BiS2 (RE = La, Ce, Pr, and Nd). J. Phys. Soc. Jpn. 87, 023704 (2018).
Paris, E. et al. Suppression of structural instability in LaOBiS2−xSex by Se substitution. J. Phys. Condens. Matter 30, 455703 (2018).
Nagasaka, K. et al. Intrinsic phase diagram of superconductivity in the BiCh2-based system without in-plane disorder. J. Phys. Soc. Jpn. 86, 074701 (2017).
Yeh, J. W. et al. Nanostructured high-entropy alloys with multiple principal elements: Novel alloy design concepts and outcome. Adv. Energy Mater. 6, 299 (2004).
Ye, Y. F. et al. High-entropy alloy: Challenges and prospects. Mater. Today 19, 349 (2016).
Koželj, P. et al. Discovery of a superconducting high-entropy alloy. Phys. Rev. Lett. 113, 107001 (2014).
Sun, L. & Cava, R. J. High-entropy alloy superconductors: Status, opportunities, and challenges. Phys. Rev. Mater. 3, 090301 (2019).
Kitagawa, J., Hamamoto, S. & Ishizu, N. Cutting edge of high-entropy alloy superconductors from the perspective of materials research. Metals 10, 1078 (2020).
Stolze, K. et al. High-entropy alloy superconductors on an α-Mn lattice. J. Mater. Chem. C 6, 10441 (2018).
Guo, J. et al. Robust zero resistance in a superconducting high-entropy alloy at pressures up to 190 GPa. PNAS 114, 13144 (2017).
Guo, J. et al. Record-high superconductivity in niobium-titanium alloy. Adv. Mater. 33, 1807240 (2019).
Mizuguchi, Y. & Yamashita, A. Superconductivity in HEA-Type Compounds (IntechOpen, 2021).
Sogabe, R., Goto, Y. & Mizuguchi, Y. Superconductivity in REO0.5F0.5BiS2 with high-entropy-alloy-type blocking layers. Appl. Phys. Express 11, 053102 (2018).
Sogabe, R. et al. Improvement of superconducting properties by high mixing entropy at blocking layers in BiS2-based superconductor REO0.5F0.5BiS2. Solid State Commun. 295, 43 (2019).
Shukunami, Y. et al. Synthesis of RE123 high-Tc superconductors with a high-entropy-alloy-type RE site. Physica C 572, 1353623 (2020).
Mizuguchi, Y. Superconductivity in high-entropy-alloy telluride AgInSnPbBiTe5. J. Phys. Soc. Jpn. 88, 124708 (2019).
Kasem, Md. R. et al. Superconducting properties of high-entropy-alloy tellurides M-Te (M: Ag, In, Cd, Sn, Sb, Pb, Bi) with a NaCl-type structure. Appl. Phys. Express 13, 033001 (2020).
Brandt, N. B. et al. Superconductivity of the compounds PbTe and PbSe under high pressure. JETP Lett. 22, 104 (1975).
Xu, L., Zheng, Y. & Zheng, J. C. Thermoelectric transport properties of PbTe under pressure. Phys. Rev. B 82, 195102 (2010).
Li, Y. et al. Phase transitions in PbTe under quasi-hydrostatic pressure up to 50 GPa. High Press. Res. 33, 713 (2013).
Fujii, Y. et al. A new high-pressure phase of PbTe above 16 GPa. Solid State Commun. 49, 135 (1984).
Bencherif, Y. et al. High-pressure phases of lead chalcogenides. Mater. Chem. Phys. 126, 707 (2011).
Sportouch, S. et al. Thermoelectric properties of the cubic family of compounds AgPbBiQ3 (Q = S, Se, Te) very low thermal conductivity materials. Mater. Res. Soc. Symp. Proc. 545, 123 (1999).
Katsuno, M. et al. High-pressure synthesis and superconducting properties of NaCl-type In1−xPbxTe (x = 0–0.8). Condens. Matter 5, 14 (2020).
Mitobe, T. et al. Superconductivity in In-doped AgSnBiTe3 with possible band inversion. Sci. Rep. 11, 22885 (2021).
Swarbrick, J. C. et al. High energy resolution X-ray absorption spectroscopy of environmentally relevant lead (II) compounds. Inorg. Chem. 48, 10748 (2009).
Yamaoka, H. et al. Electronic structures of Bi2Se3 and AgxBi2Se3 under pressure studied by high-resolution x-ray absorption spectroscopy and density functional theory calculations. Phys. Rev. B 102, 155118 (2020).
Rao, K. J. & Wong, J. A XANES investigation of the bonding of divalent lead in solids. J. Chem. Phys. 81, 4832 (1984).
Retoux, R. et al. Valence state for bismuth in the superconducting bismuth cuprates. Phys. Rev. B 41, 193 (1990).
We obtained the electronic band structures of PbTe using CompES-X, NIMS database https://compes-x.nims.go.jp/.
Matsumoto, R. et al. Pressure-induced superconductivity in sulfur-doped SnSe single crystal using boron-doped diamond electrode-prefabricated diamond anvil cell. Rev. Sci. Instrum. 87, 076103 (2016).
Matsumoto, R. et al. Diamond anvil cells using boron-doped diamond electrodes covered with undoped diamond insulating layer. Appl. Phys. Express 11, 053101 (2018).
Matsumoto, R. et al. Pressure-induced superconductivity in sulfur-doped SnSe single crystal using boron-doped diamond electrode-prefabricated diamond anvil cell. J. Phys. Soc. Jpn. 87, 124706 (2018).
Irifune, T. et al. Ultrahard polycrystalline diamond from graphite. Nature 421, 599 (2003).
Piermarini, G. J. et al. Calibration of the pressure dependence of the R1 ruby fluorescence line to 195 kbar. J. Appl. Phys. 46, 2774 (1975).
Hammersley, A. P. et al. Two-dimensional detector software: From real detector to idealised image or two-theta scan. High Press. Res. 14, 235 (1996).
Mao, H. K. & Bell, P. M. High-pressure physics, the 1-megabar mark on the ruby R1 static pressure scale. Science 191, 851 (1976).
Petricek, V., Dusek, M. & Palatinus, L. Crystallographic computing system JANA2006: general features. Z. Kristallogr. 229, 345 (2014).
Hämäläinen, K. et al. Elimination of the inner-shell lifetime broadening in x-ray-absorption spectroscopy. Phys. Rev. Lett. 67, 2850 (1991).
Hämäläinen, K. et al. Spin-dependent x-ray absorption of MnO and MnF2. Phys. Rev. B 46, 14274 (1992).
Yamaoka, H. Pressure dependence of the electronic structure of 4f and 3d electron systems studied by X-ray emission spectroscopy. High Press. Res. 36, 262 (2016).
Acknowledgements
The measurements of the XRD patterns and the PFY-XAS spectra under pressure were performed BL12XU, and BL12B2, SPring-8 under SPring-8 Proposal Nos. 2020A4269, 2021A4253, & 2021B4254 (corresponding to Proposal Nos. 2019-2-261, 2021-1-009, 2021-1-404, & 2021-1-415 of NSRRC). The authors thank O. Miura for his supports in experiments. This work was partially supported by Grant-in-Aid for Scientific Research (KAKENHI) (Nos. 18KK0076, 21K18834, 21H00151) and Tokyo Metropolitan Government Advanced Research (H31-1). We thank Editage for English correction of the manuscript.
Author information
Authors and Affiliations
Contributions
M.R.K., R.M., H.Y., Y.G. and Y.M. designed the research; M.R.K., A.Y., and Y.M. synthesized samples; R.M. and Y.T. performed resistance measurement; H.Y., H.I., and N.H. performed synchrotron experiments and analyzed the spectra of PFY-XAS; M.R.K., Y.N., A.Y., Y.G., and Y.M. analyzed the crystal structure; M.R.K., Y.N., H.Y., and Y.M. wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Kasem, M.R., Nakahira, Y., Yamaoka, H. et al. Robustness of superconductivity to external pressure in high-entropy-alloy-type metal telluride AgInSnPbBiTe5. Sci Rep 12, 7789 (2022). https://doi.org/10.1038/s41598-022-11862-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-11862-w
- Springer Nature Limited