Abstract
Meteoric iron is the metal that humans first obtained and used in the earliest stage of metal culture. Advances in metallographic analysis techniques have revealed that meteoric iron largely comprises kamacite, taenite, and cohenite, which correspond to ferrite, austenite, and cementite in artificial steel, respectively. Although the mechanical properties of meteoric irons were measured previously to understand their origin and history, the genuine mechanical properties of meteoric iron remain unknown because of its complex microstructure and the pre-existing cracks in cohenite. Using micro-tensile tests to analyse the single-crystalline constituents of the Canyon Diablo meteorite, herein, we show that the taenite matrix exhibits excellent balance between yield strength and ductility superior to that of the kamacite matrix. We found that taenite is rich in nitrogen despite containing a large amount of nickel, which decreases the nitrogen solubility, suggesting that solid-solution strengthening via nitrogen is highly effective for the Fe–Ni system. Our findings not only provide insights for developing advanced high-strength steel but also help understand the mysterious relationship between nitrogen and nickel contents in steel. Like ancient peoples believed that meteoric iron was a gift from the heavens, the findings herein imply that this thought continues even now.
Similar content being viewed by others
Introduction
Meteoric irons, known as Fe–Ni alloys with various nickel contents from a minimum of 5 up to 60 mass%, can be classified into several types exhibiting different microstructural features based on their overall nickel content1. The main phases of meteoric iron are kamacite with a body-centred cubic (BCC) structure, taenite with a face-centred cubic (FCC) structure, and cohenite with an orthorhombic structure, which correspond to α-ferrite, γ-austenite, and Fe3C cementite in artificial steel, respectively2,3,4,5,6. The unique microstructure of meteoric iron is formed by the nucleation and growth of kamacite from taenite during the slow cooling of the parent body1, with the cooling period for a 1 K temperature decrease estimated as a few hundred to thousands of years1. Despite the huge difference in cooling rates between artificial steel and meteoric iron (more than 13 orders of magnitudes), the crystallographic features of the FCC to BCC transformation mechanism are similar in artificial steel and meteoric iron2,3,4,5. However, there have been few studies on the mechanical properties of meteoric iron7,8,9,10,11,12. Most measurements of their mechanical properties determined tensile strengths less than ca. 100 MPa, which are relatively low values compared to that of artificial iron-nickel alloys8,11. This is because pre-existing cracks and cavities in the body of meteoric iron hinder the measuring of the strength and ductility of their constituents. To measure the mechanical properties of metallic microconstituents, micropillar-compression tests are frequently perfomed13,14,15. This method is suitable for examining the dislocation motion and sample size effect on the deformation behaviour. However, the deformation restraint on the bottom of the pillar prevents the complete uniaxial stress loading throughout the specimen, making it difficult for the accurate measurement of the yield strength, strain hardening, and elongation. In recent times, advances in micro-mechanical testing techniques have reduced tensile-test specimens to the microstructural scale, i.e. several tens of micrometres, which has allowed for the successful characterisation of steel tensile properties and deformation behaviours16,17,18,19,20. Therefore, we applied the micro-tensile testing technique to the mechanical characterisation of genuine stress–strain behaviours in the constituents of a meteoric iron.
Results and discussion
Microstructural characterisation
Figure 1 shows the optical micrographs, electron back-scatter diffraction (EBSD) patterns, and electron probe microanalysis (EPMA) maps of the typical constituents in a Canyon Diablo meteorite sample. Figure 1a shows the typical microstructural morphology which accounts for the majority of this meteoric iron, and Fig. 1b shows the areas determined as α-iron via EBSD analysis. Additionally, Neumann bands were observed, which are deformation twins in the BCC crystal, as previously reported for some meteoric irons2,3. According to the compositional mapping of alloying elements by EPMA shown in Fig. 1c, there was no segregation of alloying elements in the boxed area in Fig. 1a. Quantitative analysis of the alloying elements (Extended Data Table 1) in the area shown in Fig. 1c revealed that the α-phase could be regarded as ferritic iron containing approximately 6 at.% Ni, i.e. kamacite. A small fraction of taenite (determined by γ-iron in the EBSD analysis) was observed as shown in Fig. 1d,e. The compositional mapping of alloying elements in taenite revealed that the iron content decreased and nickel content increased upon approaching the taenite/kamacite boundary (Fig. 1f). Beyond the area near the taenite/kamacite boundary, taenite was composed of 1.61C, 5.18 N, 0.03P, 72.60Fe, 0.23Co, and 20.35Ni in at.% (Extended Data Table 1). Additionally, cohenite (determined by cementite in the EBSD analysis) was frequently observed, as shown in Fig. 1g,h. Cohenite was composed of 20.66C, 0.53 N, 0.001P, 77.48Fe, 0.17Co, and 1.16Ni in at.%, corresponding to Fe3C cementite (Extended Data Table 1). Furthermore, numerous cracks and small areas of taenite were observed in cohenite (Fig. 1g–i). A micro-tensile test of single-crystalline cohenite revealed that the cleavage fracture occurred on the (011) plane without plastic deformation at the maximum tensile strength of 2.4 GPa (Extended Data Fig. 1). We expect that these are why the previous measurements of the tensile properties of meteoric iron8,11 exhibited low strength levels, because the brittle materials are sensitive to defects. Subsequently, based on the microstructural determination by EBSD and EPMA analyses, we performed micro-tensile tests for kamacite and taenite of the Canyon Diablo meteorite sample.
Stress–strain curves
Figure 2a,b show an example of preparing a micro-sized tensile specimen for taenite. As illustrated in the inverse pole figure map of taenite (Fig. 2a), a micro-tensile specimen with a gauge section of 11 × 20 × 50 μm3 was fabricated using a focused ion beam (Fig. 2b) so that the gauge part was completely single crystalline. We chose this length scale because no significant size effect will appear down to this specimen size21,22,23. Thus, we can evaluate the mechanical properties of the microstructural constituents, which are equivalent to those of the bulk specimen. A single-crystalline specimen of kamacite was prepared in the same way. Figure 2c shows the stress–strain curves obtained by micro-tensile testing of the single-crystalline taenite and kamacite specimens with their loading directions (LDs) nearly parallel to the [123] direction. For kamacite, the yield strength and elongation-to-failure were 350 MPa and 19%, respectively, which are in good agreement with the previous estimated yield strength of 335 MPa and elongation-to-failure of 19%, obtained by the tensile testing of a Gibeon meteorite7 with a Widmanstätten structure and coarse kamacite widths. Meanwhile, the yield strength and elongation-to-failure of taenite were 935 MPa and 65%, respectively. Although there have been no reports on high-nitrogen alloying in nickel-rich austenitic steels because nickel decreases the nitrogen solubility24, introducing high levels of nitrogen into Fe–Cr–Mn alloys25,26 is well known as a remarkable strengthening method via solid-solution strengthening. For example, the yield strength of the Fe–24Cr–10Mn–1.43 N alloy (mass%), which contains an amount of nitrogen comparable to that in the taenite in this study (1.35 N mass%), was measured as 830 MPa26. Therefore, the high yield strength of taenite was presumably attributable to a solid-solution-strengthening mechanism via the interaction between dislocations and interstitial nitrogen atoms27.
Micro-tensile behaviours
Figure 3 shows the deformation and fracture morphology of the kamacite micro-tensile specimen. Slip steps formed at inclination angles of 80° and 54° with respect to the LD after the onset of yielding (Fig. 3a,b), and they propagated while maintaining a constant stress level (Supplementary Video 1). Finally, chisel-edge-type fracture with significant necking occurred (Fig. 3c). Figure 3d shows a stereographic projection of the kamacite specimen based on the EBSD analysis, which indicates that the observed slip steps correspond to the primary slip systems (110) [1\(\overline{1}\)1] and (21\(\overline{1}\)) [1\(\overline{1}\)1], with Schmid factors of 0.47 and 0.49, respectively. This suggested that cross slips occurred on the favourable slip planes with the same slip direction and that the kamacite matrix deformed based on Schmid’s law. Figure 4 shows the deformation and fracture morphology of the taenite micro-tensile specimen. In the taenite specimen, a linear slip step formed at an inclination angle of 62° with respect to the LD at the onset of yielding (Fig. 4a), and thereafter the deformation band extended throughout the gauge part of the specimen (Fig. 4b), like the Lüders deformation (Supplementary Video 2). Finally, the specimen fractured with significant necking (Fig. 4c). The linear slip step observed in the taenite specimen corresponds to the primary slip system of (1\(\overline{1}\)1) [011], with a Schmid factor of 0.47 (Fig. 4a,d). It should be noted that the observed slip steps in the kamacite and taenite specimens exhibited wavy and linear morphologies, respectively. Active slip systems in BCC crystals are in the <111> direction on the {110}, {112}, and {123} planes, whereas those in FCC crystals are in the <110> direction on the {111} planes. Put simply, kamacite (BCC) has more active slip systems than taenite (FCC). Therefore, the difference in slip behaviour was attributable to the difference in the number of slip systems in kamacite and taenite.
The stress–strain curve of taenite (Fig. 2c) revealed a high yield strength without a loss in the good ductility. Figure 5 shows the relationships between the true stress, σT, and strain hardening rate, dσT/dεT, plotted against the true strain, εT, for the taenite specimen. Generally, single-crystalline FCC metals exhibit a transition from the easy-glide stage to linear-hardening stage owing to the interaction of multiple slip systems. In the taenite specimen, indeed, single slip gliding proceeds throughout the gauge part of the specimen (Fig. 4a,b), followed by the strain hardening concurrent with the activation of the secondary slip system (Fig. 5). The onset of plastic instability can be determined by the Considѐre’s condition: dσT/dεT ≤ σT. In the taenite specimen having high yield strength, the strain hardening stage is short because the stress level exceeds the strain hardening rate at an early stage of strain hardening (indicated by the arrow in Fig. 5). In austenitic stainless steels, nitrogen increases not only the strength but also the strain hardening rate25. This indicates that the occurrence of local necking is suppressed in the easy-glide stage, which enables uniform deformation up to a high-strain region.
Micro-tensile tests of the Canyon Diablo meteorite specimens revealed that the nickel-rich austenite with an ultra-high nitrogen content exhibited an excellent relationship between yield strength and ductility. Generally, advanced high-strength austenitic steels, which combine a high strength and moderate ductility via transformation-induced plasticity and twin-induced plasticity, exhibit tensile strengths exceeding ca. 800 MPa. It is a major challenge to increase the yield strength of advanced high-strength austenitic steels because of a risk of hydrogen embrittlement under severe external conditions28. Therefore, we anticipate that our findings will aid in the development of advanced high-strength steels, and motivate research into understanding the relationship between nitrogen and nickel contents in steel.
Methods
Material and microstructural characterisation
The material used in this study was a Canyon Diablo meteorite (type IAB, coarse octahedrite). Small-cut samples were polished with emery paper and a colloidal SiO2 paste. Compositional mappings in the constituents of the meteorite were conducted using a JEOL (JCM-5700) scanning electron microscope (SEM) equipped with an electron probe micro-analyser (EPMA, Shimadzu 1720), and operated at a beam current of 0.1 μA and accelerating voltage of 15 kV. All the measurements were obtained using the Kα signal of C, N, P, Fe, Co, and Ni. Quantitative 12-point analyses were performed in each characteristic phase using a focused beam at a beam current of 0.05 μA and accelerating voltage of 15 kV. The ZAF correction method was applied for the quantitative analysis of chemical compositions using reference samples of Cr3C2, AlN, GaP, Fe, Co, and Ni for each element (C, N, P, Fe, Co, and Ni, respectively). The methods of Duncumb-Reed, Philibert, and Reed were used for correcting the effects of atomic number (Z), absorption (A), and fluorescence (F), respectively. The average values were calculated from the results of the 12-point analyses for each element in phases to estimate the chemical compositions. After the EPMA analysis, the crystal orientation was determined at a scanning step size of 0.4 μm using an SEM instrument equipped with an EBSD detector and orientation imaging microscopy software (TSL OIM v.7.1.0). A clean-up procedure was applied to all the EBSD images to adjust single points having misorientations greater than 5° in comparison with their neighbours. Additionally, points with a confidence index lower than 0.1 were excluded from the analysis based on Field’s study29.
Micro-tensile tests
The samples were thinned to a thickness of approximately 20 μm using emery paper, and both the surfaces were then mirror-finished with a colloidal SiO2 paste. Micro-tensile specimens with a gauge section of 11 × 20 × 50 μm3, 18 × 20 × 50 μm3, and 22 × 20 × 50 μm3 were fabricated using a focused ion beam for taenite, kamacite, and cohenite, respectively. In the regime of this length scale, no difference was observed in the strength22,23 due to the sample size effect which occurs in micropillar compression21. Single-crystalline specimens were prepared with their LDs approximately parallel to the [123] direction for kamacite and taenite, and to the [011] direction for cohenite. Tensile tests were performed at room temperature under laboratory atmospheric conditions with a displacement rate of 0.1 μm s–1, corresponding to a strain rate of 2 × 10–3 s–1. The set-up has been described in more detail in a previous study30. The gauge section of the tensile specimen was monitored during tensile testing using an optical microscope to dynamically measure the strain as a function of time.
Data availability
All data generated or analysed during this study are included in the published article and Supplementary Information and are available from the corresponding author upon reasonable request.
References
Goldstein, J. I., Scott, E. R. D. & Chabot, N. L. Iron meteorites: Crystallization, thermal history, parent bodies, and origin. Chem. Erde-Geochem. 69, 293–325 (2009).
Nolze, G., Geist, V., Neumann, R. S. & Buchheim, M. Investigation of orientation relationships by EBSD and EDS on the example of the Watson iron meteorite. Cryst. Res. Technol. 40, 791–804 (2005).
He, Y., Godet, S., Jacques, P. J. & Jonas, J. J. Crystallographic relations between face- and body-centred cubic crystals formed under near-equilibrium conditions: Observations from the Gibeon meteorite. Acta Mater. 54, 1323–1334 (2006).
Hutchinson, B. & Hagstrom, J. Austenite decomposition structures in the Gibeon meteorite. Metall. Mater. Trans. A 37, 1811–1818 (2006).
Cayron, C. EBSD imaging of orientation relationships and variant groupings in different martensitic alloys and Widmanstätten iron meteorites. Mater. Charact. 94, 93–110 (2014).
Bhadeshia, H. K. D. H. Cementite. Int. Mater. Rev. 65, 1–27 (2020).
Gordon, R. B. Mechanical properties of iron meteorites and the structure of their parent planets. J. Geophys. Res. 75, 439–447 (1970).
Knox, R. Jr. The yield strength of meteoritic iron. Meteoritics 5, 63–74 (1970).
Auten, T. A. On the brittleness of Gibeon meteoritic iron. Meteoritics 8, 189–196 (1973).
Johnson, A. A. & Remo, J. L. A new interpretation of the mechanical properties of the Gibeon meteorite. J. Geophys. Res. 79, 1142–1146 (1974).
Petrovic, J. J. Mechanical properties of meteorites and their constituents. J. Mater. Sci. 36, 1579–1583 (2001).
Cotto-Figueroa, D. et al. Scale-dependent measurements of meteorite strength: Implications for asteroid fragmentation. Icarus 277, 73–77 (2016).
Schwiedrzik, J. et al. In situ micropillar compression reveals superior strength and ductility but an absence of damage in lamellar bone. Nat. Mater. 13, 740–747 (2014).
Khalajhedayati, A., Pan, Z. & Rupert, T. J. Manipulating the interfacial structure of nanomaterials to achieve a unique combination of strength and ductility. Nat. Commun. 7, 10802 (2016).
Wu, G., Chan, K., Zhu, L., Sun, L. & Lu, J. Dual-phase nanostructuring as a route to high-strength magnesium alloys. Nature 545, 80–83 (2017).
Mine, Y., Hirashita, K., Takashima, H., Matsuda, M. & Takashima, K. Micro-tension behaviour of lath martensite structures of carbon steel. Mater. Sci. Eng. A 560, 535–544 (2013).
Mine, Y., Takashima, H., Matsuda, M. & Takashima, K. Microtension behaviour of lenticular martensite structures of Fe–30 mass% Ni alloy. Mater. Sci. Eng. A 618, 359–367 (2014).
Kwak, K., Mayama, T., Mine, Y. & Takashima, K. Anisotropy of strength and plasticity in lath martensite steel. Mater. Sci. Eng. A 674, 104–116 (2016).
Mine, Y., Nakamichi, S., Koga, K., Takashima, K. & Kraft, O. Deformation behaviour of nano-twinned single crystals of an Fe–19Cr–16Ni austenitic alloy. Mater. Sci. Eng. A 675, 181–191 (2016).
Ogata, S., Mayama, T., Mine, Y. & Takashima, K. Effect of microstructural evolution on deformation behaviour of pre-strained dual-phase steel. Mater. Sci. Eng. A 689, 353–365 (2017).
Inoue, A., Kishida, K., Inui, H. & Hagihara, K. Compression of micro-pillars of a long period stacking ordered phase in the Mg–Zn–Y system. Mater. Res. Soc. Symp. Proc. 1516, 151–156 (2013).
Kraft, O., Gruber, P. A., Monig, R. & Weygand, D. Plasticity in confined dimensions. Annu. Rev. Mater. Res. 40, 293–317 (2010).
Kaufmann, D., Schneider, A. S., Monig, R., Volkert, C. A. & Kraft, O. Effect of surface orientation on the plasticity of small bcc metals. Int. J. Plast. 49, 145–151 (2013).
Reed, R. P. Nitrogen in austenitic stainless steels. JOM 41, 16–21 (1989).
Simmons, J. W. Overview: High-nitrogen alloying of stainless steels. Mater. Sci. Eng. A 207, 159–169 (1996).
Tsuchiyama, T., Takaki, S., Ito, H. & Kataoka, K. Fabrication of ultrahigh nitrogen austenitic steels by nitrogen gas absorption into solid solution. Metall. Mater. Trans. A 34, 2591–2599 (2003).
Rawers, J. & Grujicic, M. Effect of metal composition and temperature on the yield strength of nitrogen strengthened stainless steels. Mater. Sci. Eng. A 207, 188–194 (1996).
Mine, Y., Horita, N., Horita, Z. & Takashima, K. Effect of ultrafine grain refinement on hydrogen embrittlement of metastable austenitic stainless steel. Int. J. Hydrogen Energy 42, 15415–15425 (2017).
Field, D. P. Recent advances in the application of orientation imaging. Ultramicroscopy 67, 1–9 (1997).
Ito, T., Mine, Y., Otsu, M. & Takashima, K. Strain measurement of micrometre-sized structures under tensile loading by using scanning white-light interferometry. Mater. Trans. 57, 1252–1256 (2016).
Acknowledgements
We thank Y. Shimada (Chiba University, Japan) and K. Hisazumi (NIPPON STEEL CORPORATION, Japan) for providing the sample, and T. Yamamuro (Kumamoto University, Japan) for helping us with the EPMA experiments. This work was supported by the ‘Special Research Project for Future of Steel Structures’ from the Japanese Society of Steel Construction (2017–2018).
Author information
Authors and Affiliations
Contributions
S.U. carried out the experiments, S.U. and Y.M. analysed the data, Y.M. designed the project, K.T. supervised the project. All authors contributed to the discussion.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ueki, S., Mine, Y. & Takashima, K. Excellent mechanical properties of taenite in meteoric iron. Sci Rep 11, 4750 (2021). https://doi.org/10.1038/s41598-021-83792-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-83792-y
- Springer Nature Limited
This article is cited by
-
Smelting and Selective Reduction of Limonitic Laterite Ore in Mini Blast Furnace
Journal of The Institution of Engineers (India): Series D (2022)