Abstract
Triangular growth patterns of pristine two-dimensional (2D) transition metal dichalcogenides (TMDs) are ubiquitous in experiments. Here, we use first-principles calculations to investigate the growth of triangular shaped oxide islands upon layer-by-layer controlled oxidation in monolayer and few-layer \(\hbox {WSe}_{2}\) systems. Pristine 2D TMDs with a trigonal prismatic geometry prefer the triangular growth morphology due to structural stability arising from the edge chalcogen atoms along its three sides. Our ab-initio energetics and thermodynamic study show that, since the Se atoms are more susceptible to oxygen replacement, the preferential oxidation happens along the Se zigzag lines, producing triangular islands of transition metal oxides. The thermodynamic stability arising from the preferential triangular self-formation of TMD based oxide heterostructures and their electronic properties opens a new avenue for their exploration in advanced electronic and optoelectronic devices.
Similar content being viewed by others
Introduction
The successful synthesis of graphene1,2 has led to an impressive surge in the exploration of atomically thin layered materials. Due to their reduced degrees of freedom, the quantum mechanical effects become significant, giving rise to fascinating electronic, mechanical, and optical properties otherwise absent in bulk materials3,4. However, the absence of a band gap in graphene presents a serious impediment in semiconductor electronics applications. This has tempted researchers to explore other low dimensional materials with varying functionalities5,6,7,8,9,10. Among them, 2D semiconducting TMDs, like \(\hbox {WSe}_{2}\) and \(\hbox {MoS}_{2}\), have attracted renewed interest because of its sizeable direct band gap and high carrier mobility at room temperature, which has interesting electronic, optoelectronic and valleytronic properties11,12,13,14,15,16. The high on-off ratio and intrinsic voltage gain of semiconducting 2D TMDs have enabled them to be used as atomically thin transistors12,17,18,19,20,21, photodetectors22,23,24 and light-emitting diodes25,26,27 with performance comparable to the well-known silicon devices.
2D TMDs can be prepared by various methods, like vapor-phase chemical reactions, wet-chemical synthesis and liquid exfoliation13,28. Apart from the edges or defect sites, which are chemically active, pristine layered dichalcogenides are mostly passive due to the absence of any dangling bonds29. Despite the variety of properties, all monolayer pristine TMD systems with trigonal prismatic geometry are obtained as triangular nanoflakes on synthesis11. Experimental and theoretical studies on the growth mechanism of monolayer TMD nanoclusters suggest that the triangular geometry with all chalcogen atom edges are energetically most favorable30,31,32,33. Chalcogen terminated triangular nanodots of TMDs exhibit many interesting physical and chemical properties, like strong spin anisotropy near the Fermi energy with collective spin states at the edges that can be utilized in efficient spin-filtering devices34.
Our recent experimental and theoretical work35,36 in monolayer and few-layer \(\hbox {WSe}_{2}\) systems has further shown that, in the presence of an ozone environment, the surface Se atoms are preferentially replaced by O atoms, forming triangular oxide patches on pristine TMDs. This layer-selective oxidation of \(\hbox {WSe}_{2}\) films has also been realized using laser heating37, ambient air38 and oxygen plasma doping, which is similar to conventional semiconductors39. The triangular island formation has also been reported in other studies40. Due to the temperature-dependent oxidation process, the triangular oxide patches increase in size, keeping their shape intact, until the full surface gets oxidized. The next layer of underlying pristine TMD starts getting oxidized only at elevated temperatures. This atomically thin TMD based oxide-semiconductor heterostructure created by layer-by-layer oxidation has interesting tunable electronic properties36. Moreover, charge transfer to the surface oxide layer makes them hole-doped35. Hence, these heterostructures can be used as field-effect transistors41 and photogating devices42.
Motivated by the enormous potential of these TMD based oxide heterostructures in electronic and optoelectronic device applications and their unique electronic properties, here we theoretically investigate these systems. We take a cue from the preferential self-formation of triangular nanoflakes of pristine TMDs and explore the underlying reason for similar triangular growth morphology of oxide islands on such pristine TMD systems. We have chosen our system to be \(\hbox {WSe}_{2}\). However, our observations are expected to remain unchanged for any semiconducting 2D TMD system with trigonal prismatic geometry, as observed in our previous study36. We employ ab-initio techniques to capture the quantum mechanical effect in these reduced dimensions and systematically present our results in the following sections.
Computational method
For structural relaxation and to study the electronic properties, we use first-principles calculations based on density functional theory (DFT) as implemented in the Vienna ab-initio simulations package (VASP)43. The calculations are performed at the level of the generalized gradient approximation (GGA) with the Perdew-Burke-Ernzerhof (PBE) exchange and correlation functional44. The electronic wave-functions are expanded using a plane-wave basis set with a cutoff energy of 520 eV. The 2D periodic tungsten selenide-oxide heterostructures are represented in a \(4 \times 5\) super cell. A vacuum space of 15 Å is applied along the non-periodic direction to avoid any interaction within adjacent unit cells. For geometric relaxation and subsequent electronic property calculations, we consider Brillouin zone sampling over a \(4 \times 4 \times 1\) and \(16 \times 16 \times 1\) \(\Gamma \)-centered Monkhorst-Pack k-mesh grid, respectively. All structures are relaxed along with the lattice vectors until the force on each atom reaches 0.01 eV/Å. The convergence criterion for electronic minimization is set to \(10^{-5}\) eV. We use the Gibbs2 code45,46,47 to calculate the thermodynamic properties of the heterostructures within the framework of the quasi-harmonic Debye model (see Supplementary Information).
Results and discussion
We begin by taking a \(4 \times 5\) super cell of a 2D monolayer of \(\hbox {WSe}_{2}\) and gradually replace the lines of Se atoms with lines of O atoms, step-by-step, in a triangular and in a rectangular fashion as shown in Fig. 1a,b, respectively. Due to the asymmetry in super cell geometry, the hexagonal first Brillouin zone gets distorted, as can be seen in Fig. 1c. For ab-initio energetics study, we first optimize the structures and then calculate the stabilization energies of this tungsten selenide-oxide in-plane heterostructures (see Table S1 of Supplementary Information). The stabilization energy is defined as, \(E_S = E_{Total} - \sum _{i}N_iE_i\), where \(E_S\) is the stabilization energy, \(E_{Total}\) is the total energy of the system at room temperature (298 K) and 0 GPa pressure, as obtained from the Gibbs2 code45,46,47. \(N_i\) and \(E_i\) are the number and the energy of a single atom of the i-th species (\(i=\) W, Se, O), respectively. We have seen an increase in stabilization energy upon gradual layer-by-layer oxidation of few-layer TMDs in our previous study36. Here, the gradual in-plane oxidation of monolayer \(\hbox {WSe}_{2}\) too provides higher stabilization. Since the overall stabilization energy increases with the number of O atom replacement, to compare the stability of the triangular and rectangular oxide islands, we present the stabilization energy normalized to the number of substituted O atoms as a function of the number of Se lines replaced in Fig. 1d. It clearly shows that the stability of triangular oxide islands is higher than that of the rectangular ones. The stabilization energy plots for both the geometrical shapes approach towards a saturation value, which is the characteristic stabilization energy of monolayer \(\hbox {WO}_{2}\), that is when O atoms replace all the Se atoms. We have not explicitly included the contribution of zero point energy (ZPE) originating from the atomic vibrational modes in calculating \(E_S\) due to expensive phonon frequency computations.
However, we consider the Debye model in quasi-harmonic approximation as implemented in the Gibbs2 code45,46,47 to implicitly account for the effect of zero point energy (ZPE) and the vibrational contribution to the enthalpy and entropy (see Supplementary Information). Moreover, we theoretically probe the thermal effects on the TMD-based oxide heterostructures’ stability since, in experiments, the layer-by-layer oxidation is temperature-controlled35. The molar Gibbs Free Energy at room temperature (298 K) and 0 GPa pressure, derived from the model (see Fig. S1–S8 in Supplementary Information), is normalized to the number of O atoms as a function of the number of Se lines replaced, as shown in Fig. 1e (see also the Table S1 of Supplementary Information). We observe that the thermodynamic stability trend, as depicted in Fig. 1e, is identical to the structural stability due to \(E_S\), as shown in Fig. 1d. Hence, the thermodynamic calculations clearly demonstrate that the triangular phases of the heterostructures are more stable than the rectangular phases.
Having discussed the stability of the triangular oxide islands, we investigate the energetics of the Se substitution by O and the trend for the clusterization of the oxygen atoms into triangular patches at zero temperature. This is related to the short- and long-range ordering of the oxygen atoms within the two layers of chalcogen atoms. We consider a \(2 \times 2\) supercell of a 2D monolayer of \(\hbox {WSe}_{2}\) and replace one of the Se atoms at the top surface by O atom initially. Now, we investigate the most probable positions of further O replacement, as depicted by the numeric in Fig. 2a. We observe that the Se atom at immediately adjacent bottom surface (position 1’) to the initial O atom is energetically more favorable to be replaced than that in the top surface (position 1). The same trend continues with successive Se replacements (see Fig. 2a). This shows the nucleation for oxidation prefers the Se replacement in the top and bottom surfaces simultaneously rather than replacing Se atoms step-by-step in the entire top surface. This gives a clear indication of how the oxide islands initially nucleate in the pristine TMD layer.
Furthermore, to explain the preferential triangular self-formation of the oxide islands, we consider a \(4 \times 5\) super cell of the selenide-oxide heterostructure with pre-formed triangular oxide islands and investigate the preference of the next Se atom replacement, as depicted by the numeric in Fig. 2b. The corresponding relative stabilization energy plot shows that the Se atom (position 1) adjacent to the pre-formed oxide triangle is energetically more favorable to be replaced by the O atom. Therefore, the oxide island preferentially grows in a compact triangular fashion rather than dispersed in random positions (2 and 3). This theoretically explains the triangular growth morphology of the 2D TMD oxide heterostructures, as seen in experiments35.
We further investigate the electronic properties of this in-plane heterostructures. It is well known that monolayer TMDs are direct band gap semiconductors, as shown in Fig. 3a. This results in a characteristic peak in photoluminescence spectra35,48. However, it has been observed that upon oxidation, this peak disappears35. In Fig. 3b, we present the energy dispersion of 2D \(\hbox {WSe}_{2}\) monolayer with triangular oxide island, as shown in Fig. 1a. It shows an indirect band gap semiconducting behavior, explaining the photoluminescence peak’s disappearance, as observed in the previous experiments. The projected density of states (see Fig. 3b’) shows the hybridization of W, Se, and O orbitals in the entire energy window. The top-most valence band, which arises mainly from the W and O orbitals, gets detached from the bulk valence bands and shows almost dispersion-less behavior. Actually, the triangular oxide islands behave like discrete quantum dots, embedded in the \(\hbox {WSe}_{2}\) plane with negligible hopping among them and therefore result in the dispersion-less character of the top-most valence band. On the contrary, the rectangular oxide island as shown in Fig. 1b also shows an indirect band gap semiconducting behavior (see Fig. 3c,c’). However, due to the periodic nature of the quasi-1D rectangular oxide strip, no dispersion-less band arises near Fermi energy, unlike its triangular counterpart. Complete oxidation of the monolayer \(\hbox {WSe}_{2}\) leads to an indirect band gap semiconductor (see Fig. 3d) and consequent disappearance of photoluminescence peak. The energy dispersions for the systems with progressive triangular and rectangular oxidation are presented in Fig. S9–S14 in Supplementary Information. As can be seen, the systems with different sizes of triangular oxide islands show a band gap of \(\sim \) 1.6–1.8 eV. The consideration of hybrid functionals can produce a more accurate band gap than the GGA-PBE level of calculation that is known to underestimate the same49. Therefore, it is expected that these systems with triangular oxide islands will show optical absorption in the visible spectrum with possible light-harvesting applications.
Conclusion
To summarize, we have investigated the reason behind the preferential triangular growth morphology of oxide islands on monolayer \(\hbox {WSe}_{2}\) that can be generalized for other 2D pristine TMDs. Our ab-initio energetics and thermodynamic study show that the origin of these intriguing triangular oxides in TMD systems is due to the preferential O substitution at selenium zigzag edges. This lends credence to experimental results35,50 and can be extended to most 2D TMDs. Moreover, the TMD based oxide heterostructures can have potential use in various electronic and optoelectronic device applications.
References
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Castro Neto, A. H., Guinea, F., Peres, N. M. R., Novoselov, K. S. & Geim, A. K. The electronic properties of graphene. Rev. Mod. Phys. 81, 109–162 (2009).
Wakabayashi, K. & Dutta, S. Nanoscale and edge effect on electronic properties of graphene. Solid State Commun. 152, 1420–1430 (2012).
Butler, S. Z. et al. Progress, challenges, and opportunities in two-dimensional materials beyond graphene. ACS Nano 7, 2898–2926 (2013).
Akinwande, D., Petrone, N. & Hone, J. Two-dimensional flexible nanoelectronics. Nat. Commun. 5, 5678 (2014).
Das, S., Robinson, J. A., Dubey, M., Terrones, H. & Terrones, M. Beyond graphene: progress in novel two-dimensional materials and van der Waals solids. Annu. Rev. Mater. Res. 45, 1–27 (2015).
Bhimanapati, G. R. et al. Recent advances in two-dimensional materials beyond graphene. ACS Nano 9, 11509–11539 (2015).
Novoselov, K. S., Mishchenko, A., Carvalho, A. & Castro Neto, A. H. 2D materials and van der Waals heterostructures. Science 353, aac9439 (2016).
Jariwala, D., Marks, T. J. & Hersam, M. C. Mixed-dimensional van der Waals heterostructures. Nat. Mater. 16, 170–181 (2017).
Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically thin MoS 2: a new direct-gap semiconductor. Phys. Rev. Lett. 105, 136805 (2010).
Wang, Q. H., Kalantar-Zadeh, K., Kis, A., Coleman, J. N. & Strano, M. S. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).
Qian, X., Liu, J., Fu, L. & Li, J. Quantum spin Hall effect in two-dimensional transition metal dichalcogenides. Science 346, 1344–1347 (2014).
Jariwala, D., Sangwan, V. K., Lauhon, L. J., Marks, T. J. & Hersam, M. C. Emerging device applications for semiconducting two-dimensional transition metal dichalcogenides. ACS Nano 8, 1102–1120 (2014).
Choi, W. et al. Recent development of two-dimensional transition metal dichalcogenides and their applications. Mater. Today 20, 116–130 (2017).
Podzorov, V., Gershenson, M. E., Kloc, C., Zeis, R. & Bucher, E. High-mobility field-effect transistors based on transition metal dichalcogenides. Appl. Phys. Lett. 84, 3301–3303 (2004).
Radisavljevic, B., Whitwick, M. B. & Kis, A. Integrated circuits and logic operations based on single-layer MoS2. ACS Nano 5, 9934–9938 (2011).
Kim, S. et al. High-mobility and low-power thin-film transistors based on multilayer MoS2 crystals. Nat. Commun. 3, 1011 (2012).
Chang, H.-Y. et al. High-performance, highly bendable MoS2 transistors with high-K dielectrics for flexible low-power systems. ACS Nano 7, 5446–5452 (2013).
Nourbakhsh, A. et al.\(\text{ MoS}_{2}\) field-effect transistor with Sub-10 nm channel length. Nano Lett. 16, 7798–7806 (2016).
Yin, Z. et al. Single-layer MoS2 phototransistors. ACS Nano 6, 74–80 (2012).
Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2. Nat. Nanotechnol. 8, 497–501 (2013).
Park, S. et al. Direct determination of monolayer \(\text{ MoS}_{2}\) and \(\text{ WSe}_{2}\) exciton binding energies on insulating and metallic substrates. 2D Mater 5, 025003 (2018).
Pospischil, A., Furchi, M. M. & Mueller, T. Solar-energy conversion and light emission in an atomic monolayer p–n diode. Nat. Nanotechnol. 9, 257–261 (2014).
Baugher, B. W. H., Churchill, H. O. H., Yang, Y. & Jarillo-Herrero, P. Optoelectronic devices based on electrically tunable p-n diodes in a monolayer dichalcogenide. Nat. Nanotechnol. 9, 262–267 (2014).
Ross, J. S. et al. Electrically tunable excitonic light-emitting diodes based on monolayer WSe2 p–n junctions. Nat. Nanotechnol. 9, 268–272 (2014).
Lv, R. et al. Transition metal dichalcogenides and beyond: synthesis, properties, and applications of single- and few-layer nanosheets. Acc. Chem. Res. 48, 56–64 (2015).
Yamamoto, M., Einstein, T. L., Fuhrer, M. S. & Cullen, W. G. Anisotropic etching of atomically thin \(\text{ MoS}_{2}\). J. Phys. Chem. C 117, 25643–25649 (2013).
Helveg, S. et al. Atomic-scale structure of single-layer MoS2 nanoclusters. Phys. Rev. Lett. 84, 951–954 (2000).
Walton, A., Lauritsen, J., Topsøe, H. & Besenbacher, F. MoS2 nanoparticle morphologies in hydrodesulfurization catalysis studied by scanning tunneling microscopy. J. Catal. 308, 306–318 (2013).
Lauritsen, J. et al. Atomic-scale insight into structure and morphology changes of MoS2 nanoclusters in hydrotreating catalysts. J. Catal. 221, 510–522 (2004).
Lauritsen, J. V. et al. Size-dependent structure of MoS2 nanocrystals. Nat. Nanotechnol. 2, 53–58 (2007).
Zhou, Y., Yang, P., Zu, H., Gao, F. & Zu, X. Electronic structures and magnetic properties of MoS2 nanostructures: atomic defects, nanoholes, nanodots and antidots. Phys. Chem. Chem. Phys. 15, 10385–10394 (2013).
Yamamoto, M. et al. Self-limiting layer-by-layer oxidation of atomically thin \(\text{ WSe}_{2}\). Nano Lett. 15, 2067–2073 (2015).
Das, S. R., Wakabayashi, K., Yamamoto, M., Tsukagoshi, K. & Dutta, S. Layer-by-layer oxidation induced electronic properties in transition-metal dichalcogenides. J. Phys. Chem. C 122, 17001–17007 (2018).
Tan, C. et al. Laser-assisted oxidation of multi-layer tungsten diselenide nanosheets. Appl. Phys. Lett. 108, 083112 (2016).
Kotsakidis, J. C. et al. Oxidation of monolayer WS2 in ambient is a photoinduced process. Nano Lett. 19, 5205–5215 (2019).
Liu, X., Qu, D., Yuan, Y., Sun, J. & Yoo, W. J. Self-terminated surface monolayer oxidation induced robust degenerate doping in MoTe2 for low contact resistance. ACS Appl. Mater. Interfaces 12, 26586–26592 (2020).
Li, H. et al. Mechanical exfoliation and characterization of single- and few-layer nanosheets of \(\text{ WSe}_2\), \(\text{ TaS}_{2}\), and \(\text{ TaSe}_{2}\). Small 9, 1974–1981 (2013).
Yamamoto, M., Nakaharai, S., Ueno, K. & Tsukagoshi, K. Self-limiting oxides on \(\text{ WSe}_2\) as controlled surface acceptors and low-resistance hole contacts. Nano Lett. 16, 2720–2727 (2016).
Yamamoto, M., Ueno, K. & Tsukagoshi, K. Pronounced photogating effect in atomically thin \(\text{ WSe}_2\) with a self-limiting surface oxide layer. Appl. Phys. Lett. 112, 181902 (2018).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Blanco, M., Francisco, E. & Luaña, V. GIBBS: isothermal-isobaric thermodynamics of solids from energy curves using a quasi-harmonic Debye model. Comput. Phys. Commun. 158, 57–72 (2004).
Otero-de-la-Roza, A. & Luaña, V. Gibbs2: a new version of the quasi-harmonic model code. I. Robust treatment of the static data. Comput. Phys. Commun. 182, 1708–1720 (2011).
Otero-de-la-Roza, A., Abbasi-Pérez, D. & Luaña, V. Gibbs2: a new version of the quasiharmonic model code. II. Models for solid-state thermodynamics, features and implementation. Comput. Phys. Commun. 182, 2232–2248 (2011).
Ajayi, O. . A. et al. Approaching the intrinsic photoluminescence linewidth in transition metal dichalcogenide monolayers. 2D Mater 4, 031011 (2017).
Xu, W., Gan, L., Wang, R., Wu, X. & Xu, H. Surface adsorption and vacancy in tuning the properties of tellurene. ACS Appl. Mater. Interfaces 12, 19110–19115 (2020).
Yoon, A. et al. Van der Waals epitaxial formation of atomic layered \(\alpha \)-MoO3 on MoS2 by oxidation. ACS Appl. Mater. Interfaces 12, 22029–22036 (2020).
Acknowledgements
S.R.D. and S.D. thank IISER Tirupati for Intramural Funding and Science and the Engineering Research Board (SERB), Department of Science and Technology (DST), Government of India, for the Early Career Research Award grant (ECR/2016/000283). K.W. acknowledges support from JSPS KAKENHI Grants JP18H01154, JP15K21722, JP15K13507. S.D. and K.W. acknowledge the financial support from Hyogo Overseas Research Network (HORN) and Kwansei Gakuin University International Research Collaboration grant.
Author information
Authors and Affiliations
Contributions
S.D., K.W., and K.T. have defined the project. S.R.D. has performed the calculations. All the authors have analyzed the results. S.R.D. and S.D. have written the manuscript in consultation with K.W. and K.T..
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Das, S.R., Wakabayashi, K., Tsukagoshi, K. et al. Ab-initio investigation of preferential triangular self-formation of oxide heterostructures of monolayer \(\hbox {WSe}_{2}\). Sci Rep 10, 21737 (2020). https://doi.org/10.1038/s41598-020-78812-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-78812-2
- Springer Nature Limited