Abstract
Cerium doped Gd3Ga3Al2O12 (GGAG) single crystals as well as GGAG:Ce single crystals co-doped by divalent (Mg2+, Ca2+) and tetravalent (Zr4+, Ti4+) ions have been studied by means of time-resolved luminescence as well as the excitation luminescence spectroscopy in vacuum ultraviolet (VUV) and soft X-ray (XUV) spectral range. Tunable laser excitation was applied for time-resolved experiments in order to obtain luminescence decay curves under excitations in Ce3+, Gd3+ and excitonic absorption bands. The influence of the co-dopant ions on the Ce3+ luminescence decay kinetics is elucidated. The fastest luminescence decay was observed for the Mg2+ co-doped crystals under any excitation below bandgap energy indicating the perturbation of the 5d states of Ce3+ by Mg2+ ions. Synchrotron radiation was utilized for the luminescence excitation in the energy range from 4.5 to 800 eV. Special attention was paid to the analysis of Ce3+ excitation spectra in VUV and XUV spectral range where multiplication of electronic excitation (MEE) processes occur. Our results demonstrated that GGAG:Ce single crystals co-doped by Mg2+ ions as well as the GGAG:Ce crystal annealed in vacuum reveal the most efficient excitation of Ce3+ emission in VUV-XUV excitation range. The role of intrinsic defects in MEE processes in the co-doped as well as in the annealed GGAG:Ce single crystals is discussed.
Similar content being viewed by others
Introduction
Nowadays scintillator detectors play an irreplaceable role in high-energy physics, safety systems, space and medical applications1,2,3,4,5. Among other scintillator materials1,2,6,7,8 cerium doped gallium gadolinium aluminum garnet (Gd3Ga3Al2O12:Ce or GGAG:Ce) nowadays is one of the most relevant scintillator materials because it comprises the combination of such properties, as a very high light output of scintillations (58,000 photons/MeV)1, high density (6.63 g/cm3) and relatively fast decay time (90 ns)9,10,11. Furthermore, this material is very suitable for neutron detection and discrimination, thanks to the high Gd cross-section for neutron interaction12,13. However, the practical application of this compound is restricted by long afterglow of Ce3+ emission, which is explained by the intermediate localization of electrons and holes at shallow traps during energy transfers to the Ce3+ emission centers. One of possible ways to accelerate Ce3+ emission decay is the co-doping of the GGAG:Ce single crystals by divalent ions10,14,15,16. In this case, that lack of positive charge induced by divalent ion is compensated by changing the valence of cerium ions from 3 + to 4 + . To create a luminescence center in the form of an excited Ce3+ center, the Ce4+ ion must capture an electron from the conduction band. This means that the processes of energy transfer to emission centers do not include the hole trapping stage, which is necessary in the case of the Ce3+ ion. As a result, radiative relaxation process is significantly accelerated in divalent co-doped crystals14,17. However, this approach has a serious drawback. The co-doping of the GGAG:Ce crystals by divalent ions strongly quenches the scintillation light yield, which is preliminarily explained by the shift of 5d states of Ce3+ towards the bottom of the conduction band as well as due to the creation of the deep traps originated from co-dopant ions. In contrast to divalent ions the effect of co-doping with tetravalent cation has not been sufficiently studied for GGAG:Ce. It is only known that the investigation of Hf4+ doped GGAG:Ce demonstrates the degradation of the light output and longer decay time compared with the conventional GGAG:Ce18. On the other hand, Zr4+ co-doped GSO:Ce has shown 20% higher light output in respect of non-co-doped analogue19.
Therefore, the influence of co-dopant ions on the luminescence properties of GGAG:Ce single crystals must be studied tuning the excitation energy which covers the ranges of intrinsic 4f–5d transitions of Ce3+ ion, excitonic and band-to-band transitions. Thus, in current work we have applied the excitations produced by the tunable laser excitations (in 210–420 nm range) in order to compare time-resolved luminescence characteristics under excitations in Ce3+, Gd3+, defect and excitonic absorption bands of GGAG:Ce single crystals co-doped by divalent and tetravalent ions.
The improvement of energy and time resolution of scintillating materials is of a great concern for the breakthrough in many practical applications. Both of these critical parameters improve if scintillation light yield increases. Therefore, the number of electron–hole pairs generated in a scintillator by an arriving photon/particle defines the energy and time resolutions. Thus, the understanding of the multiplications of electronic excitations processes in GGAG:Ce is necessary, which have been poorly studied so far in this material. Moreover, in the case of doped materials, electrons can multiply the excitation by impact ionization of the impurities if the mean free path of the fast electron is long enough to encounter an impurity ion. The GGAG compound belongs to the class of wide band gap materials having the band gap about 6.2 eV. This energy and higher refers to the vacuum ultraviolet (VUV) and soft X-ray (XUV) spectral range. Luminescence excitation spectra of wide bandgap materials in the VUV region provide important information about the last stage of the cascade process of the electronic excitation multiplication20. In addition, the excitation spectra in wide spectral range allow to estimate the migration energy losses using the correlation between intensities of direct excitation of Ce3+ ions and the excitation via the bulk in the fundamental region. The most suitable excitation source in VUV-XUV range is synchrotron radiation, which was successfully utilized for the excitation spectroscopy of wide band gap materials21,22,23,24,25,26,27,28 and semiconductors as well29,30,31.
The tuneability of synchrotron radiation allows to excite samples by high-energy photons, which corresponds to the energy of hot charge carriers as well as to the energy when multiplication of electronic excitation processes are occurring. In addition, surface quality of the scintillator plays an important role in the photoelectron production efficiency due to a low penetration depth of VUV photons into crystals. The absorption coefficient close to the fundamental absorption region is about 106 cm−1 and excitation penetration is several tens of nanometers20. The electronic excitations generated by VUV quanta may migrate to the surface and not take part in the bulk recombination process. They may recombine at the surface (radiatively or non-radiatively) or escape from the crystal (electron emission). Consequently, understanding of physical mechanisms related to the excitation energy absorption and scattering in a close-to-surface layer and surface area of scintillator crystals is essential. With the increase of the excitation energy, the penetration depth of incident photons becomes larger and it is supposed that only bulk states are excited under XUV photons. Therefore, varying the excitation energy in VUV-XUV range one can manipulate the penetration depth of photons and can distinguish surface and bulk related relaxation processes.
The luminescence yield depends also on the quality of the crystal. The presence of absorbing and scattering centers in the crystal is a common source of scintillation losses1. A post growth annealing of the samples leads to alteration of concentration of point defects in crystals. The most essential changes during annealing occur, however, on the crystals’ surfaces affecting surface loss centers. Taking into account that VUV excitations are very sensitive in respect of surface states it is expected that the crystals with distinguished surface quality may reveal the nature of surface loss centers. To our knowledge VUV excitation spectroscopy data for annealed GGAG:Ce single crystals have not been reported yet.
In the current paper we report time-resolved luminescence and VUV and XUV excitation spectroscopy of co-doped GGAG:Ce single crystals as well as the GGAG:Ce crystals annealed in different atmospheres. The origins of the modification of energy transfer efficiency to the emission center in the co-doped as well as annealed GGAG:Ce single crystals are discussed in the paper. Furthermore, the influence of co-dopant ions on the temporal characteristics of luminescence centers in GGAG:Ce crystals will be elucidated.
Method
All GGAG single crystals studied in current research have been grown by Czochralski method in JSC “Fomos-Materials” (Moscow, Russia). The details of crystals’ growth of doped and co-doped GGAG single crystals have been reported in32. The crystals have been cut in small thin pieces and polished for optical experiments. The cerium concentration in the doped crystals was 3 at%. The concentrations of the co-dopants in the GGAG:Ce single crystals as well samples thicknesses are summarized in Table 1. As one can see from the Table 1, two GGAG:Ce are co-doped by divalent ions (Mg2+ or Ca2+) which induce Ce4+ centers in the corresponding crystals. One crystal was co-doped by Zr4+ ions to test the hypothesis expressed in19 that tetravalent ions can increase luminescence light output. The co-doping of one of GGAG:Ce,Mg single crystals by Ti4+ was justified by the restoration of the luminescence light yield which was deteriorated due to the Mg2+ co-dopants. In addition, the GGAG:Ce single crystal were post annealed in vacuum or in oxygen atmosphere. The annealing details please see in Table 1.
Optical properties of the crystals at room temperature have been studied by means of the Cary 7000 optical spectrophotometer. The low temperature absorption spectra have been obtained in the Perkin-Elmer Lambda 950 UV/VIS/NIR spectrophotometer at 7 K using cryocooler Janis Research CCS-100/204N. Time-resolved luminescence spectra were obtained upon excitation by wavelength-tunable pulsed solid-state laser Ekspla NT342/3UV (210–2300 nm). The emission signal was detected by the Andor iSTAR DH734-18 mm CCD camera coupled to the Andor SR-303i-B spectrometer. Luminescence decay kinetics were measured by a photomultiplier tube PG122 (time resolution better than 5 ns) and digital oscilloscope Tektronix TDS 684A.
A luminescence excitation spectroscopy experiments have been carried out under synchrotron radiation excitation. These experiments have been performed on the photoluminescence endstation FINESTLUMI33,34 of the FinEstBeAMS undulator beamline35, which was constructed and developed at 1.5 GeV storage ring of MAX IV synchrotron facility (Lund, Sweden). The excitation energy range was 4.5–800 eV, while temperature varied from 10 to 300 K. The excitation spectra were normalized utilizing the calibration curve obtained by means of AXUV-100G diode. Luminescence detection in UV–visible spectral range (200–800 nm) was performed by the Andor Shamrock (SR-303i) 0.3 m spectrometer having the grating (300/500). The Andor Shamrock spectrometer was equipped with the photomultiplier photon counting heads (H8259-01 Hamamatsu) covering the spectral range from 200 to 900 nm.
Results and discussion
Absorption spectra
The Fig. 1a demonstrates the absorption spectra of all GGAG crystals studied at room temperature. The low temperature absorption spectrum for the cerium doped GGAG single crystal is shown in Fig. 1b. The absorption spectrum for the undoped GGAG (Fig. 1a) reveals sharp absorption lines due to f–f transitions in Gd3+ ions. These lines can be observed also in doped and co-doped crystals. The absorption spectrum for the GGAG:Ce (Fig. 1a) contains two broad bands at 440 nm (4f–5d1) and 343 nm (4f1–5d2) due to 4f–5d transitions in Ce3+. In addition, the broad absorption band below 270 nm appears in the spectrum for GGAG:Ce if one compares the spectrum for the undoped crystal (Fig. 1a). This band is located below the fundamental absorption edge and it is observed in all cerium doped crystals. However, in the Ca2+ co-doped crystal and especially in the Mg2+ co-doped crystals the intensity of absorption in the UV spectral range (below 300) nm is huge. The optical density this absorption band is high and, therefore, the shape of this band is flawed and much thinner crystals should be measured. The same could be also said about the absorption band of 4f–5d1 transitions, which looks truncated for all co-doped crystals except the most thinner GGAG:Ce crystal. Nevertheless, some preliminary conclusions can be made based on the spectra depicted in Fig. 1a. Obviously, the strong UV absorption observed for the Ca2+ and Mg2+ co-doped crystals is induced by co-dopant ions. Substituting Gd3+ ion in GGAG lattice Ca2+ and Mg2+ ions give extra negative charge, which should be compensated. The charge compensated centers can be vacancies or O- oxygen deficit centers well known in complex oxides36,37,38. However, the most probable compensation is the partial conversion of Ce3+ to Ce4+, which is confirmed by XANES experiments16. Therefore, the intensive UV absorption in the absorption spectra for the Ca2+ and Mg2+ co-doped crystals is explained by the increased concentration of Ce4+ ions16,17,39, namely due to charge transfer transition from O2- to Ce4+ center. On the other hand, the absorption spectrum for the Zr4+ co-doped crystal is almost the same as the spectrum for GGAG:Ce. In the case of Zr4+ substitution of Gd3+ ion one extra positive charge is introduced to the GGAG lattice. The charge compensator in this case is questionable. However, Zr4+ should eliminate any residual Ce4+ ions in the crystal and, obviously, the absorption band (below 270 nm) in the spectra for GGAG:Ce and for Zr4+ co-doped crystals is not due to Ce4+ center. Furthermore, the strong UV absorption in the spectra for the Ca2+ and Mg2+ co-doped crystals is too wide and, perhaps, contains several overlapped absorption bands. Another suggestion is that the different absorption centers are responsible for the UV absorption bands observed in the GGAG:Ce and the Zr4+ co-doped crystals from one side and the Ca2+ and the Mg2+ co-doped crystal from another one. We will return to this discussion in the following sections considering the excitation spectra of Ce3+ emission.
The absorption spectra of the co-doped GGAG:Ce single crystals at room temperature (a). The spectrum for the undoped crystal is given for comparison. The absorption spectrum for the cerium doped GGAG single crystal at 10 K is shown in (b). The inset reveals a fine structure of Gd3+ transitions in the dashed area. Gd3+ absorption lines are assigned to energy levels reported in40.
Luminescence spectra
The emission spectra of Ce3+ emission in the GGAG:Ce single crystal and in the GGAG:Ce co-doped crystals at low temperature under deep VUV (45 eV) excitation are shown in Fig. 2. The spectra are normalized at the maximum intensity of the emission bands. One can see (Fig. 2) that the co-dopant ions influence the shape of Ce3+ emission bands. The Ca2+ ions induce the most essential changes shifting the Ce3+ emission band towards the long wavelength spectral side comparing with the corresponding spectrum of GGAG:Ce crystal. On the other hand, the emission spectrum in the Mg2+ co-doped crystal well coincides with the corresponding spectrum observed in the crystal without co-dopants. The origin of the observed changes in the emission spectra can be connected with the alteration of Al/Ga ratio in the co-doped crystals. It means that one can manipulate the band gap value of this compound tuning the stoichiometry of GGAG:Ce as well as to adjust Ce3+ levels in the forbidden gap41,42. It was established before that the red shifting of the Ce3+ luminescence bands takes place if the ratio of the Al/Ga increases43. Thus, the influence of the Ca2+ and Zr4+ ions on the Al/Ga ratio explains the red shift of the emission spectra in the corresponding crystals depicted in Fig. 2. Another possible explanation is the perturbation of some Ce3+ states by co-dopant ions as it was recently suggested44. It is assumed that the strongest perturbation is induced by ions with biggest ionic radii among co-dopants, i.e. Ca2+ and Zr4+. The Ce3+ emission results from 5d–4f radiation transition. Taking into account that the 4f ground state of Ce3+ is split into two levels (2F7/2 and 2F5/2) each luminescence spectrum (in Fig. 2) is represented by two overlapped emission bands due to 5d-2F7/2 and 5d-2F5/2 transitions. The perturbation can lead not only to the red shift of the emission spectra towards low energy side but also can change the ratio of 5d-2F7/2 and 5d-2F5/2 transitions leading to the more pronounced low energy shoulder in the emission spectra of the Ca2+ and Zr4+ co-doped crystals.
Excitation spectra
The excitation spectra in the 4.7–7.0 eV excitation region of Ce3+ emission are shown in Fig. 3a for all crystals studied at 10 K, while the temperature dependency of the excitation spectra in GGAG:Ce single crystal is depicted in Fig. 3b. Considering these excitation spectra (Fig. 3a, inset) one can see that the excitonic peak position at about 200 nm or 6.2 eV is co-dopant dependent. The excitonic peak for the Ca2+ co-doped crystals slightly red shifted in respect to the excitonic peaks observed for other crystals peaking at 6.15 eV. The excitonic peaks observed for GGAG:Ce, Zr4+ co-doped and Mg + Ti co-doped crystals are similar and have maximum at 6.2 eV. The excitation spectra of Mg2+ co-doped crystals are slightly blue shifted with respect of others Ce3+ excitation spectra peaking at 6.25 eV. Analyzing the excitation spectra in the spectral range close to the excitonic transitions, we can suggest that co-doped ions can slightly modify the stoichiometry of the crystals. In fact, one can slightly change the Al/Ga ratio as well as the content of Gd3+ in the lattice by introducing a co-dopant ion into the GGAG lattice. Based on the concept of the band gap engineering in garnets41,45 the band gap value can be manipulated tuning the Al/Ga ratio in the GGAG. The alterations in the band gap values lead to shifts of the excitonic bands as depicted in Fig. 3a as well as to the shifts of the emission bands (Fig. 2). Indeed, the emission and excitation spectra observed in Figs. 2 and 3a for the Ca co-doped crystal are slightly red shifted in respect to others. On the other hand, the spectra obtained for the Mg co-doped crystal are blue shifted.
The low energy excitation spectra of Ce3+ emission (530 nm) in the co-doped GGAG:Ce crystals at 10 K. Dashed line shows the part of the absorption spectrum for the GGAG:Ce single crystal taken from Fig. 1 for the comparison (a). Inset (a) exhibits the excitonic range of the excitation spectra in details where the colored arrows indicate the position of the corresponding peak (see details in the text). The temperature dependence of the excitation spectra of Ce3+ emission (530 nm) in the GGAG:Ce crystal (b). The arrows show the excitation energies utilized in the time-resolved experiments (see details in the text).
Figure 3b demonstrates the temperature shift of the excitonic peak in the excitation spectrum of Ce3+ emission in the GGAG:Ce single crystal. The temperature behavior of the corresponding spectra observed in the co-doped crystals is similar. Figure 3b demonstrates the blue shift of excitonic peak from 210 to 200 nm decreasing the sample temperature from 295 to 10 K. By analogy with other garnets (YAG, LuAG, etc.) we assume that exciton in GGAG exists in form of a self-trapped state. Therefore, a strong electron phonon coupling takes place and a self-trapped exciton (STE) can be considered as localized center. A temperature behavior of the excitonic peak (Fig. 3b) is typical for STE. The temperature shift of the excitonic peak allows us to apply the 210 nm laser excitation at room temperature for the study of the Ce3+ decay kinetics under direct excitation in the excitonic band (please see the “Time-resolved luminescence”).
Next, we are focusing on the low energy part of the excitation spectra in Fig. 3a. Each excitation spectrum contains the wide excitation band at energies below excitonic transitions (4.5–6.0 eV range peaking at about 5.3 eV). These excitation bands are similar to the high-energy absorption band observed in the absorption spectra (Fig. 1a) of the GGAG:Ce and the Zr4+ co-doped crystals shown by the dashed line in Fig. 3a for comparison. This absorption band was not resolved in the absorption spectra for the Ca2+, Mg2+ and Mg + Ti crystals due to the overlapping with the strong absorption of Ce4+ band. As we already mentioned above the absorption of Ce4+ is due to electron transfer from the valence band to the ground state of Ce4+ forming Ce3+ in ground state. It means that a direct excitation in Ce4+ absorption band does not lead to Ce3+ emission and, therefore, the Ce4+ absorption cannot be revealed in the excitation spectra in Fig. 3a. This result confirms our suggestion that the strong absorption in UV range of the absorption spectra (Fig. 1a) contains at least two overlapped bands: the charge transfer band O2−—Ce4+ and the band peaking about 5.3 eV.
The origin of the 5.3 eV (or UV) band observed in the absorption and the excitation spectra needs further comments. Based on our result we can suggest that the UV band is due to transitions from the Ce3+ ground state to the 5d3 excited state. This suggestion explains why the UV band appears in the absorption spectra of the Ce3+ doped GGAG crystals (Fig. 1) but it is absent in the spectrum for the undoped GGAG. Furthermore, the intensity of the UV excitation band is three times less in both magnesium containing co-doped crystals if to compare with other single crystals studied (Fig. 3a). It means that the concentration of Ce3+ ions is smaller in the magnesium co-doped crystals despite the equal cerium concentration in the furnace charges. However, some part of Ce3+ ions were transformed to the Ce4+ ions in order to compensate the lack of the positive charge due to Mg2+ co-dopant ions. The existence of the Ce4+ ions in the Mg2+ co-doped crystals was confirmed by our recent XANES experiments44. These results also demonstrated that all other crystals, including the Ca2+ co-doped one, do not reveal the existence of Ce4+ ions. Therefore, the Ce3+ concentration should be more or less the same therein. Hence, the intensity of UV excitation band should be similar in the spectra for all crystals excluding the Mg2+ co-doped ones, as one can see in Fig. 3a. Nevertheless, the strong decreasing of the UV excitation band (Fig. 3a) cannot be explained only by a simple concentration decreasing of Ce3+ ions in the Mg2+ co-doped crystals. In addition, the spectral position of the UV absorption band, which we explained as 4f–5d3 absorption in Ce3+ and the Ce4+ absorption band are very close, i.e. these band are spectrally overlapping. Therefore, these two centers in the Mg2+ co-doped crystals compete with each other absorbing photons in UV spectral range. It means that UV photons instead of being absorbed by Ce3+ ion are absorbed by Ce4+ forming Ce3+ in the ground state and do not participate in the luminescence process. It also should be noted that our conclusion about the origin of the 5.3 eV excitation band can be indirectly supported by the theoretically re-assignment of Ce3+ absorption transitions in YAG reported in46.
The excitation spectra of Ce3+ emission in the crystals studied have also significant discrepancies in the VUV spectral range. Figure 4 demonstrates in fact the extension of the excitation spectra in Fig. 3a up to 45 eV. For each excitation spectrum there is the excitation intensity degradation at energies just above the energy fundamental transitions (~ 6.5 eV) reaching minimum value at about 10 eV. Thereafter, the excitation intensity starts to rise up at energies higher than 12–13 eV in all excitation spectra observed in Fig. 4. This energy is roughly equal to the value of 2Eg, where Eg is a band gap energy in GGAG. Such intensity behavior means that so called multiplication of electronic excitations processes are observed. The occurrence of MEE processes means that two or more emission centers are excited per one absorbed photon during inelastic electro-electron scattering. In order to realize successfully the MEE processes, the excitation energy of the incident photon must be higher than the threshold energy, which is 2Eg47. If energy of hot electrons is much higher than the threshold energy (3Eg, 4Eg, etc.), more secondary electrons can be generated and subsequently more luminescence centers can be excited. All spectra in Fig. 4 have similar peculiarities in the spectral range 10–45 eV except the excitation intensity, which distinguishes for different crystals. It implies that the efficiency of MEE processes is sample dependent. One of the possible explanations is following. All single crystals studied contain some amount of intrinsic defects. We suggest that these defects can be efficient traps for hot charge carriers, which leads to the diminishing of MEE processes, and, subsequently plays a negative role in scintillation performing. The best excitation efficiency in VUV spectral range demonstrates the Mg2+ co-doped crystal. It is known that the Mg2+ co-doping of GGAG:Ce crystals leads to the effective elimination of shallow electron traps due to oxygen vacancies or gallium deficiency48. In particular, as it was assumed in48 the Mg2+ co-doping eliminates gallium vacancies from Ce:GGAG crystals when Mg2+ ions occupy the sites of gallium vacancies. This is essentially the same as the case for oxygen vacancies. On the other hand, the Zr4+ and Ca2+ co-doped crystals, perhaps, have some extra centers for non-radiative relaxation of hot charge carriers. We can suppose that such centers can be charge compensators of extra positive charge induced by Zr4+ ions in the Zr4+ co-doped crystal. The low efficiency of MEE processes in the Ca2+ doped crystal is not clear and further studies are needed. We assume, for example, that a comparison of the excitation spectra of GGAG:Ce crystals with different concentrations of Ca2+ ions could reveal this ambiguity.
The importance of lattice defects and their influences on the MEE processes are clearly demonstrated by the next example. Figures 4 and 5 show the comparison of the excitation spectra of Ce3+ emission in the GGAG:Ce single crystal annealed in vacuum and oxygen atmosphere. An absorption coefficient is huge for excitation energy exceeding bandgap energy; therefore, VUV photons are absorbed in very thin surface layer. On the other hand, the penetration depth of the X-rays is much deeper exciting the luminescence centers in samples’ bulk. The penetration depth of VUV and XUV photons can be estimated as the attenuation length of incident photons i.e. the depth into the material measured along the surface normal where the intensity of photons falls to 1/e of its value at the surface. Based on the approach described in details in49,50 the calculated attenuation length of VUV and soft X-ray photons in the energy range from 30 to 1000 eV falling on the GGAG (g = 6.63 g/cm3) is obtained (Fig. S1 of supplementary materials). This result demonstrates that the attenuation lengths is about 10 nm of 30 eV photons, while it reaches 0.5 microns if photon energy increases up to 1000 eV.
The excitation spectra depicted in Fig. 5 are measured in very wide spectral range 5.5–800 eV covering regions of both VUV and soft X-rays photons. By analogy with other excitation spectra (Figs. 3 and 4), the spectra in Fig. 5 are also normalized in the excitonic band. The labels 1s O and M1 Ga in Fig. 5 correspond to the absorption energies by 1s core level of oxygen and M1 edge of gallium, respectively. The inset of Fig. 5 clearly shows that the excitation spectra at low energies for the initial and vacuum annealed crystals are identical, while the excitation intensity decrease in the spectrum of the crystal annealed in oxygen is observed at energies exceeding excitonic energy. This strong intensity drop can be explained by an efficient trapping of charge carriers by non-radiative centers (defects) in the crystal annealed in oxygen. As we mentioned above, in VUV spectral range photons are mostly absorbed in thin surface layer of the crystal. Thus, we suggest that the strong degradation of the luminescence under excitation by VUV photons can be explained by surface defects induced by thermal treatment in oxygen. However, passing from VUV to soft X-ray range where the influence of surface is negligible the intensity of luminescence remains significantly smaller in the annealed in oxygen crystal. It means that the annealing in oxygen induces non-radiative centers (defects) in crystals bulk. The origin of these defects is unclear. Obviously, the concentration of oxygen vacancies cannot increase after annealing in oxygen atmosphere. We assume that the effect of annealing under oxygen pressure can be explained by the violation of stoichiometry in the surface layer. On one hand, some of Ga ions are accommodated at interstitial sites, e.g. the b sites of the garnet structure similarly to GGG crystals51. On the other hand, some Ga2O3 evaporates from the surface during annealing at temperatures higher than 1100 °C51,52. The non-stoichiometry layer depth could be increased up to several micrometers during the ten hours annealing. Therefore, the stoichiometry of the 10 h annealed crystals differs if compared with unannealed samples. GGAG single crystals having slight excess of Ga demonstrated a lower proportionality than the stoichiometric ones42. In addition, MEE could be less efficient in the non-stoichiometry samples due to defect levels induced by non-stoichiometry.
In contrast to the annealing in oxygen atmosphere, oxygen vacancies can be created after annealing in vacuum. However, the excitation spectrum reveals higher luminescence intensity under high-energy excitation than the corresponding spectrum for the initial crystal. It means that annealing in vacuum improves luminescence properties eliminating quenching centers in GGAG:Ce single crystal. The origin of the defects induced or eliminated by annealing in oxygen atmosphere or vacuum should be clarified and further studies are needed varying annealing temperature and time.
Time-resolved luminescence
Figure 6 shows the decay kinetics of Ce3+ emission under tunable laser excitations of all studied GGAG crystals measured at room temperature. Four excitation wavelengths have been chosen: 450 nm, 275 nm, 235 nm and 210 nm. The 450 nm excitation corresponds to the 4f–5d1 transitions in Ce3+ ion. Under 275 nm excitation the transition of 8S7/2 → 6IJ in Gd3+ ion takes place. Furthermore, the 235 nm excitation coincides with the excitation energy of the UV band, which we discussed above and preliminarily attributed to 4f–5d3 transitions in Ce3+ ion. Finally, the 210 nm wavelength corresponds to the excitation of excitonic states in GGAG crystals. The arrows in the room temperature excitation spectrum in Fig. 3b indicate the last three excitation energies.
Luminescence decay kinetics of the Ce3+ emission (530 nm) in the co-doped GGAG:Ce single crystals under 450 nm (a), 275 nm (b), 235 nm (c) and 210 nm (d) excitations at room temperature. Black dashed line in (a) demonstrates an example of single exponential fit if the parameter of the decay time constant is 40 ns.
The decay kinetics of Ce3+ emission under direct excitation of Ce3+ ion via 4f–5d1 transition (Fig. 6a) obey the single exponential law. However, decay time constant is different for different samples. The decay time constant for the decay kinetics observed in the Mg2+ and Mg + Ti co-doped crystals is about 40 ns, while for other crystals this parameter is about 60 ns. Please see the single exponential fit parameters in Figs. S2–S4 of the supplementary materials. We suggest that faster decay of luminescence in the Mg2+ and Mg + Ti co-doped crystals is due to partial non-radiative relaxation of Ce3+ ions near co-dopant impurities. Similar situation canbe observed in Fig. 6c under the 235 nm excitation. Again, the luminescence decay kinetics are faster for the Mg2+ and Mg + Ti co-doped crystals if to compare with other crystals, which reveal identical decay curves. Moreover, decay time constants obtained for each crystal is the same under the 450 nm and the 235 nm excitations. This fact confirms our suggestion above that the 235 nm (5.3 eV or UV) excitation band results from 4f–5d3 transitions in Ce3+ ion.
The luminescence decay kinetics under the 275 nm excitation (Fig. 6b) are drastically different comparing with the considered above (Fig. 6a,c). Under the 275 nm excitation the transition 8S7/2 → 6IJ in Gd3+ ion occurs with further energy transfer to Ce3+ emission center.
The energy transfer mechanism from Gd3+ to Ce3+ is well established in other compounds53,54,55. However, the detailed mechanism of such energy transfer in GGAG:Ce has not been studied. Therefore, we suggest that under the 275 excitation of the 8S7/2 → 6IJ transition the subsequent non-radiative relaxation from 6IJ to the 6PJ level of Gd3+ takes place. Later on the relaxation from excited 6PJ level to 8S7/2 ground state leads either to radiative recombination of characteristic 317 nm emission of Gd3+ or energy transfers exiting the nearest Ce3+ ion. Taking into account that the 6PJ-8S7/2 transition is forbidden electron’s lifetime on the 6PJ excited state is much longer than the decay time of Ce3+ emission. The population of 6PJ excited state of Gd3+ is fed from the 6IJ level and the 6IJ-6PJ transition is also forbidden. Therefore, the energy transfer from Gd3+ to Ce3+ is limited by the population rate of 6PJ, which is relatively slow. As a result, the decay kinetics of Ce3+ emission in Fig. 6b have slow rising fronts. These decay kinetics, in fact, represent superposition of the rise and decay of luminescence intensity. Nevertheless, one can see that the decay processes in the Mg2+ and Mg + Ti co-doped crystals occur faster than in other studied crystals. The faster decay in both magnesium co-doped crystals in Fig. 6b can be explained in the same way as we did before for the decay kinetics under the 450 nm and 235 nm excitations, i.e. by partial non-radiative relaxation of Ce3+ ions near co-dopant impurities. In respect of the decay kinetics under the excitation in Gd3+ absorption band, we should also note that the rise front of luminescence intensity observed in any single crystal in Fig. 6b has not been observed yet. For instance, in56 the decay kinetics of Ce3+ emission obtained in the GGAG:Ce and the Mg2+ co-doped GGAG:Ce crystals under the excitation in Gd3+ absorption band have not demonstrated any rise front of luminescence intensity at any temperature.
The luminescence decay kinetics excited by 210 nm photons (Fig. 6d) reveal deviation from single exponential decay, i.e. there are extra slow decay components in the decay kinetics. It is worth noting that the two-exponential decay fitting cannot properly approximate these decay kinetics. On the other hand, such fitting allows to evaluate roughly time constants of the slow decay component (see Figs. S5–S7 of the supplementary materials). However, main fast components of the decay kinetics in Fig. 6d are similar to those observed under the 450 nm and the 235 nm excitations. The slow components of the luminescence decay kinetics are connected with shallow traps in GGAG lattice. These traps did not influence the decay kinetics under other excitations (Fig. 6a–c) because only transitions within Ce3+ or Gd3+ ions were involved. The 210 nm excitation is capable to directly excite excitonic states in the GGAG lattice. Shallow traps of the crystal can trap charge carriers leading to the delay in Ce3+ radiative recombination. The strongest contribution of slow decay component is observed in the decay kinetics for the Zr4+ co-doped crystal. It means that this crystal contains a higher concentration of shallow traps among all crystals studied. We suggest that the centers, which compensate the extra positive charge induced by Zr4+ ions, can be effective traps for holes. On the other hand, the slow component in the luminescence decay kinetics of the Mg2+ and the Mg + Ti co-doped crystals is negligible small. This is in line with our suggestions analyzing the VUV excitation spectra (Fig. 4) that Mg2+ co-dopant ions suppress intrinsic defects in GGAG:Ce crystals.
Analyzing the decay kinetics of Ce3+ luminescence (Fig. 6a–d) we can conclude that decay kinetics are quite similar under any excitation for each sample. For instance, the decay kinetics observed in the Mg2+ co-doped crystal have the main component of the decay about 40 ns independently on the excitation energy. The slow rise front under the excitation in Gd3+ absorption band and the slow decay components under the excitation in the excitonic band are complimentary to the main decay component of 40 ns. The similar conclusion can be done also about the decay kinetics of other crystals studied. In our opinion, it is significant that the decay kinetics obtained for the Mg2+ and the Mg + Ti crystals are faster than the decay kinetics observed in other crystals under any low energy photo excitations. Decay kinetics of Ce3+ emission in the Mg2+ co-doped and non-co-doped GGAG:Ce single crystals have also been studied in41 under photo excitations in Ce3+ absorption bands. The decay kinetics obtained in41 were the same independently on the Mg2+ content and authors concluded that Mg2+ co-dopant does not noticeably perturb the energy levels of Ce3+. However, our results do not coincide with this conclusion and clearly show the influence of Mg2+ ions on the time evolution under excitation in the Ce3+, Gd3+ and excitonic absorption bands. This result may indicate that the faster scintillations in Mg2+ co-doped GGAG:Ce crystals is not only due to the fast formation of excited Ce3+ center from Ce4+ ion but also because of perturbed 5d states of Ce3+ by Mg2+ co-dopants leading to the partial non-radiative relaxation. Similar conclusion was recently done in57,58 where the Mg2+ induced decrease of the scintillation light in GGAG:Ce films was explained by the overlapping of the lowest-energy excited 5d1 level of Ce3+ and Mg2+ states.
Conclusions
The luminescence properties of cerium doped as well as co-doped GGAG single crystals have been investigated by means of the vacuum ultraviolet (VUV) and soft X-ray (XUV) excitation spectroscopy utilizing synchrotron radiation and by means of time-resolved luminescence spectroscopy under tunable laser excitations. It was shown that GGAG:Ce single crystals having different co-dopant ions reveal distinguished efficiency of multiplication of electronic excitations in VUV spectral range. In addition, the strong influence of the annealing treatment GGAG:Ce single crystal on the Ce3+ luminescence excitation efficiency in VUV and XUV range was obtained. It was suggested that intrinsic defects in GGAG lattice are responsible for the capture of hot charge carriers leading to the degradation of the excitation efficiency in VUV and XUV range. It is found that the best efficiency of multiplication of electronic excitation processes in VUV and XUV range demonstrated in the Mg2+ co-doped GGAG:Ce single crystal. It was also shown that the annealing in vacuum can drastically improve performance of GGAG:Ce crystal increasing luminescence efficiency in VUV and XUV excitation region. It is suggested that the Mg2+ co-doping or the annealing in vacuum strongly suppresses intrinsic defects in GGAG:Ce single crystals removing competing relaxation channels of hot charge carriers.
The combination of time-resolved luminescence spectroscopy and excitation spectroscopy techniques allows to conclude that the excitation band of Ce3+ emission peaking at about 235 nm (5.3 eV) is due to 4f–5d3 transitions in Ce3+ ion in GGAG crystals. It was observed that Ce3+ luminescence decay is faster in the Mg2+ co-doped crystals under any photo excitations below the energy of band-to-band transitions in the GGAG. It means that improved scintillating properties of Mg2+ co-doped GGAG:Ce crystals known in literature are driven not only by the formation of luminescence center from Ce4+ ion but also by the perturbation of Ce3+ ion by Mg2+ co-dopants.
References
Lecoq, P., Gektin, A. & Korzhik, M. Inorganic scintillators for detector systems: Physical principles and crystal engineering. In Particle Acceleration and Detection (Springer, Berlin, 2017).
Korzhik, M., Tamulaitis, G. & Vasilev, A. N. Physics of fast processes in scintillators. In Particle Acceleration and Detection (Springer, Berlin, 2020).
Morishita, Y. et al. Performance comparison of scintillators for alpha particle detectors. Nucl. Inst. Meth. Phys. Res. A 764, 383–386 (2014).
Lecoq, P. Development of new scintillators for medical applications. Nucl. Instrum. Meth. Phys. Res. A 809, 130–139 (2016).
Alenkov, V. et al. Irradiation studies of a multi-doped Gd3Al2Ga3O12 scintillator. Nucl. Inst. Meth. Phys. Res. A 916, 226–229 (2019).
Grigorjeva, L. et al. The study of time-resolved absorption and luminescence in PbWO4 crystals. Nucl. Instrum. Meth. Phys. Res. B 166–167, 329–333 (2000).
Shalaev, A. et al. Luminescence of divalent lanthanide doped BaBr I single crystal under synchrotron radiation excitations. Nucl. Inst. Meth. Phys. Res. B 467, 17–20 (2020).
Pankratov, V. et al. Luminescence and ultraviolet excitation spectroscopy of SrI2 and SrI2:Eu2+. Radiat. Meas. 56, 13–17 (2013).
Kamada, K. et al. 2 inch diameter single crystal growth and scintillation properties of Ce:Gd3Al2Ga3O12. J. Cryst. Growth 352, 88–90 (2012).
Kamada, K. et al. Cz grown 2-in size Ce:Gd3(Al,Ga)5O12 single crystal; relationship between Al, Ga site occupancy and scintillation properties. Opt. Mater. 36(12), 1942–1945 (2014).
Kamada, K., Nikl, M. & Kurosawa, S. Alkali earth co-doping effects on luminescence and scintillation properties of Ce doped Gd3Al2Ga3O12 scintillator. Opt. Mater. 41, 63–66 (2015).
Zorloni, G. et al. Neutron/γ discrimination by an emission-based phoswich approach. Radiat. Meas. 129, 106203 (2019).
Taggart, M. P., Nakhostin, M. & Sellin, P. J. Investigation into the potential of GAGG: Ce as a neutron detector. Nucl. Instrum. Meth. A 931, 121–126 (2019).
Tyagi, M. et al. Effect of codoping on scintillation and optical properties of a Ce-doped Gd3Ga3Al2O12 scintillator. J. Phys. D Appl. Phys. 46(47), 5302–5310 (2013).
Nikl, M. & Yoshikawa, A. Recent R&D trends in inorganic single - crystal scintillator materials for radiation detection. Adv. Opt. Mater. 3, 463–481 (2015).
Wu, Y., Meng, F., Li, Q., Koschan, M. & Melcher, C. L. Role of Ce4+ in the scintillation mechanism of Co-doped Gd3Ga3Al2O12∶Ce. Phys. Rev. Appl. 2, 4009 (2014).
Nikl, M. et al. The stable Ce4+ center: A new tool to optimize Ce-doped oxide scintillators. IEEE Trans. Nucl. Sci. 63, 433–438 (2016).
Kurosawa, S. et al. Luminescent properties of Gd3(Al,Ga)5O12 crystal co-doped with Ce and M4+. J. Phys. Conf. Ser. 619, 012039 (2015).
Shimura, N. et al. Zr doped GSO: Ce single crystals and their scintillation performance. IEEE Nucl. Sci. Conf. R. 5, 2720–2723 (2004).
Rodnyj, P. A. Physical processes in inorganic scintillators. In Laser and Optical Science and Technology (CRC Press, New York, 1997).
Shirmane, L., Feldmann, C. & Pankratov, V. Comparing the luminescence processes of YVO4: Eu and core-shell YVO4@YF3 nanocrystals with bulk-YVO4:Eu. Phys. B: Cond. Mater. 504, 80–85 (2017).
Kuzmanoski, A., Pankratov, V. & Feldmann, C. Energy transfer of the quantum-cutter couple Pr3+–Mn2+ in CaF2:Pr3+, Mn2+ nanoparticles. J. Lumin. 179, 555–561 (2016).
Tuomela, A. et al. Oxygen influence on luminescence properties of rare-earth doped NaLaF4. J. Lumin. 179, 16–20 (2016).
Tuomela, A. et al. Luminescence and vacuum ultraviolet excitation spectroscopy of samarium doped SrB4O7. J. Alloys Comp. 826, 154205 (2020).
Shirmane, L. & Pankratov, V. Emerging blue-UV luminescence in cerium doped YAG nanocrystals. Phys. Stat. Sol. RRL 10, 475–479 (2016).
Pankratov, V. et al. Luminescence properties and energy transfer processes in nanosized cerium doped YAG. IEEE Trans. Nucl. Sci. 55, 1509–1513 (2008).
Nikl, M. Energy transfer phenomena in the luminescence of wide band-gap scintillators. Phys. Stat. Sol. A 202(2), 201–206 (2005).
Nikl, M., Laguta, V. V. & Vedda, A. Energy transfer and charge carrier capture processes in wide-band-gap scintillators. Phys. Stat. Sol. A 204(3), 683–689 (2007).
Pankratov, V., Osinniy, V., Larsen, A. N. & Nielsen, B. B. Si nanocrystals embedded in SiO2: Optical studies in the vacuum ultraviolet range. Phys. Rev. B 83, 045308 (2011).
Grigorjeva, L. et al. Luminescence properties of ZnO nanocrystals and ceramics. IEEE Trans. Nucl. Sci. 55, 1551–1555 (2008).
Pankratov, V. et al. Vacuum ultraviolet excitation luminescence spectroscopy of few-layered MoS2. J. Phys. Cond. Mater. 28, 15301 (2016).
Rus patent 2646407, Single crystal with garnet structure for scintillation detectors and its manufacturing method. Official Publication of Federal Institute of Industrial Property. Bull. No7, 2018
Pankratov, V. et al. Progress in development of a new luminescence setup at the FinEstBeAMS beamline of the MAX IV laboratory. Radiat. Meas. 121, 91–98 (2019).
Pankratov, V. & Kotlov, A. Luminescence spectroscopy under synchrotron radiation: From SUPERLUMI to FINESTLUMI. Nucl. Instr. Meth. Phys. Res. B 474, 35–40 (2020).
Pärna, R. et al. FinEstBeaMS—a wide-range Finnish-Estonian beamline for materials science at the 1.5 GeV storage ring at the MAX IV Laboratory. Nucl. Inst. Meth. Phys. Res. A 859, 83–89 (2017).
Radzhabov, E. A. & Shendrik, RYu. Anomalous europium luminescence in LaF3. Rad. Measur. 90, 80–83 (2016).
Grigorjeva, L. et al. Experimental and theoretical studies of polaron optical properties in KNbO3 perovskite. Solid State Comm. 129, 75–81 (2004).
Pankratov, V. et al. The role of Fe and Cu dopants in electron-hole trapping process in congruent LiNbO3. Opt. Mater. 22, 257–262 (2003).
Blahuta, A. et al. Evidence and consequences of Ce4+ in LYSO:Ce, Ca and LYSO:Ce, Mg single crystals for medical imaging applications. IEEE Trans. Nucl. Sci. 60, 3134–3141 (2013).
Dieke, G. H. Spectra and energy levels of rare earth ions in crystals (Interscience, New York, 1969).
Ogiegło, J. M. et al. Luminescence and luminescence quenching in Gd3(Ga,Al)5O12 scintillators doped with Ce3+. J. Phys. Chem. A 117, 2479–2484 (2013).
Fasoli, M. et al. Band-gap engineering for removing shallow traps in rare-earth Lu3Al5O12 garnet scintillators using Ga3+ doping. Phys. Rev. B 84(8), 081102 (2011).
Sibczynski, P. et al. Characterization of GAGG: Ce scintillators with various Al-to-Ga ratio. Nucl. Inst. Meth. Phys. Res. A 772, 112–117 (2015).
Kozlova, A. P. et al. Luminescence and vacuum ultraviolet excitation spectroscopy of cerium doped Gd3Ga3Al2O12 single crystalline scintillators under synchrotron radiation excitations. Results Phys. 16, 103002 (2020).
Vrubel, I. I. et al. Bandgap engineering in yttrium-aluminum garnet with Ga doping. Cryst. Growth Des. 17, 1863–1869 (2017).
Tanner, P. A., Fu, L., Ning, L., Cheng, B.-M. & Brik, M. G. Soft synthesis and vacuum ultraviolet spectra of YAG:Ce3+ nanocrystals: Reassignment of Ce3+ energy levels. J. Phys. Condens. Mater. 19(21), 216213 (2007).
Ilmas, E. R., Liidya, G. G. & Lushchik, Ch. B. Photon multiplication in crystals. I. Luminescence excitation spectra of ionic crystals in the region 4 to 21 eV. Opt. Spektrosc. 18(3), 453 (1965).
Kitaura, M. et al. Probing shallow electron traps in cerium-doped Gd3Al2Ga3O12 scintillators by UV-induced absorption spectroscopy. Appl. Phys. Exp. 9, 072602 (2016).
Henke, B. L., Gullikson, E. M. & Davis, J. C. X-Ray Interactions: Photoabsorption, scattering, transmission, and reflection at E = 50–30,000 eV, Z = 1–92. Atom. Data Nucl. Data 54(2), 181–342 (1993).
X-Ray Attenuation Length https://henke.lbl.gov/optical_constants/atten2.html (2007).
Metselaar, R., Damen, J. P. M., Larsen, P. K. & Huyberts, M. A. H. Investigation of colour centres in gadolinium gallium garnet crystals. Phys. Stat. Solidi A 34(2), 665–670 (1976).
Carruthers, J. R., Kokta, M., Barns, R. L. & Grasso, M. Nonstoichiometry and crystal growth of gadolinium gallium garnet. J. Cryst. Growth 19(3), 204–208 (1973).
Shalapska, T. et al. Luminescence properties of Ce3+-doped LiGdP4O12 upon vacuum-ultraviolet and x-ray excitation. J. Phys. Condens. Mater. 21, 445901 (2009).
Demchenko, P. et al. Energy migration and Gd3+ ↔ Ce3+ transfer in Ce3+-doped GdP3O9 metaphosphate. J. Phys. D: Appl. Phys. 46, 235103 (2013).
Onderisinova, Z., Kucera, M., Hanus, M. & Nikl, M. Temperature-dependent nonradiative energy transfer from Gd3+ to Ce3+ ions in co-doped LuAG:Ce, Gd garnet scintillators. J. Lumin. 167, 106–113 (2015).
Babin, V. et al. Effect of Mg2+ ions co-doping on luminescence and defects formation processes in Gd3(Ga,Al)5O12:Ce single crystals. Opt. Mater. 66, 48–58 (2017).
Babin, V. et al. Dependence of Ce3+ - related photo- and thermally stimulated luminescence characteristics on Mg2+ content in single crystals and epitaxial films of Gd3(Ga,Al)5O12:Ce,Mg. Opt. Mater. 83, 290–299 (2018).
Babin, V., Herman, P., Kucera, M., Nikl, M. & Zazubovich, S. Effect of Mg2+ co-doping on the photo- and thermally stimulated luminescence of the (Lu,Gd)3(Ga,Al)5O12:Ce epitaxial films. J. Lumin. 215, 116608 (2019).
Acknowledgements
The work of Viktorija Pankratova was supported by the Latvian Science Council grant LZP-2018/2-0358. Vladimir Pankratov gratefully acknowledges the financial support from the Ministry of Education and Science of the Russian Federation in the framework of Increase Competitiveness Program of NUST «MISiS» (Grant No. К3-2018-021). The research leading to this result has also been supported by the project CALIPSO plus under the Grant Agreement 730872 from the EU Framework Programme for Research and Innovation HORIZON 2020. Institute of Solid State Physics, University of Latvia as the Center of Excellence has received funding from the European Union’s Horizon 2020 Framework Programme H2020-WIDESPREAD-01-2016-2017-TeamingPhase2 under grant agreement No. 739508, project CAMART2. The optical absorption spectrum at low temperature reported in this paper were measured on the equipment of the Central of Collective Use “Isotope-geochemical studies” of the Institute of Geochemistry, Siberian Branch, Russian Academy of Sciences. Authors are grateful to A.I. Popov for the fruitful discussions.
Author information
Authors and Affiliations
Contributions
V.P. and A.Š. performed time-resolved luminescence experiments and prepared all figures; A.P.K., K.C., R.S. and V.P. participated in synchrotron beamtime experiments; O.A.B. prepared the crystals; V.P. wrote the main text of the manuscript as well as the revised version; All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pankratova, V., Kozlova, A.P., Buzanov, O.A. et al. Time-resolved luminescence and excitation spectroscopy of co-doped Gd3Ga3Al2O12 scintillating crystals. Sci Rep 10, 20388 (2020). https://doi.org/10.1038/s41598-020-77451-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-77451-x
- Springer Nature Limited