Abstract
In this study, we examined the thermoelectric (TE) properties of co-evaporated p-type antimony telluride (Sb2Te3) thin films on aluminum nitride (AlN)-coated stainless steel foil substrates. We investigated the influence of composition and substrate temperature on the thin-film microstructure and transport properties, by varying the tellurium (Te) concentration in the thin films as well as the substrate temperature during deposition (room temperature (RT) and 300 °C). Thin films prepared with an RT substrate were further annealed at 264 °C to obtain crystallized thin films with high phase purity. Columnar thin films with large grains and a standard multi-oriented crystal structure were obtained when thin films were deposited on substrates heated to 300 °C. Thin films deposited at RT and subsequently annealed at 264 °C had a dense, layered microstructure, with a preferential c-axis or (00 l) texture as the compositions approached phase stoichiometry. The temperature dependence of the thermoelectric properties was measured, and variations were interpreted in terms of the deviation from stoichiometry and the obtained microstructure. A maximum power factor (PF) of 0.87 mW/m ∙ K2 was obtained for off-stoichiometric 65.0 at% Te thin film, which was the highest among the samples deposited at high substrate temperatures. A higher PF of 1.0 mW/m ∙ K2 was found for off-stoichiometric thin films with 64.5 at% Te, which was deposited at RT and subsequently annealed. The improvement of thermoelectric power in films containing excess Te could be related to energy dependent carrier scattering at the Sb2Te3/Te interface.
Similar content being viewed by others
Introduction
Thermoelectric (TE) materials can directly convert thermal energy into electrical energy through the Seebeck effect and electrical energy into thermal energy through the Peltier effect, without entailing any mechanical parts or moving fluids; thus, these material systems are clean, sustainable, and highly reliable. Efficient TE thin-film devices have numerous applications in the microelectronics industry, such as thermal management or spot cooling of various components in a microsystem. TE cooling efficiency and output power depend primarily on the properties of the material. These properties are specified collectively by the material’s figure of merit, ZT, through the relation ZT = (S2T/ρk), where S is the Seebeck coefficient, ρ is the electrical resistivity, k is the thermal conductivity, and T is the temperature in Kelvin. The commercial use of TE energy convertors has yet to become widespread, due to their relatively low energy conversion efficiency. Efforts are currently underway to improve the cost-effectiveness and efficiency of these devices, while reducing the scale of the device dimensions1,2,3,4,5,6.
Telluride (Te)-based compounds have been studied extensively over the past several decades due to their considerable ZT at room temperature (RT). Antimony telluride, Sb2Te3, is a V-IV binary compound with a narrow band gap; this compound has a rhombohedral structure with space group (..) and contains five atoms in each unit cell7,8,9,10,11,12. To improve solid-state power generation and cooling, TE materials in low-dimensional structures, such as thin films, superlattices, and quantum wires, have been investigated for phenomena related to size, interface, and quantum confinement effects13,14,15,16,17,18. Hicks and Dresselhaus15 predicted that low-dimensional nanostructuring would increase the density of states of confined carriers near the Fermi level, while simultaneously enhancing phonon scattering, thereby increasing the ZT. Venkatasubramanian et al.17. reported a record high TE efficiency of 2.4 for a p-type Bi2Te3/Sb2Te3 superlattice structure prepared by molecular beam epitaxy (MBE); a ZT value of 3 was also reported for an n-type PbSeTe/PbTe quantum dot superlattice18. Furthermore, TE properties are known to depend strongly on the microstructure and composition of the TE material. It is relatively easier to control and optimize material preparation conditions with low-dimensional fabrication processes; TE analysis is also much easier.
The development and optimization of TE generators have attracted much interest, due to the explosive growth in the demand for self-powered wearable mobile electronics and sensors19,20,21,22,23. Advances in planar thin-film technology have allowed for a large choice of substrates, including those suitable for use in thin-film, flexible TE devices. Depending on the heat flow direction, a TE device is classified as either planar or vertical22. It has been established that the use of a metallic high thermal conductivity substrate is necessary to minimize the temperature drop across the substrate leading to improved thermal management and efficiency in a TE device24. However, TE measurement of thin films deposited on metallic/conducting substrates is limited by the metallic substrate that creates an electric short-circuit during measurements25. In most reports, Sb2Te3 thin films were deposited on rigid substrates. Several studies have examined TE thin-film depositions on polyimide (PI) substrates13,26,27,28, which, although flexible, do not possess the high thermal conductivity necessary for high power density and uniformity in thin-film properties. Other issues include the degradation of the PI substrate at high processing temperatures26.
A key research area of micro-TE devices involves the application of semiconductor thin-film technology to TE thin-film fabrication to improve device performance. Several techniques have been reported for growing Sb2Te3 TE thin films, such as thermal evaporation13,29,30,31, sputtering26,27,28,32,33,34, flash evaporation35, electrochemical deposition25,36,37, pulse laser deposition38, metal-organic chemical vapor deposition39, and MBE9,10,40. However, some of these processes tend to be complicated, time-consuming, and require expensive precursors and equipment. Therefore, in this study, a thermal evaporation deposition method was selected, which offers the advantages of low-cost fabrication and a short processing time. This work reports on the optimal growth of p-type Sb2Te3 thin films on aluminum nitride (AlN)-coated stainless steel foil substrates by means of co-evaporation, to better understand and circumvent the ZT limitations. Detailed analyses of the film composition, microstructure, and transport properties were conducted in an attempt to optimize TE performance. A major challenge, especially when depositing thin films at higher substrate temperatures, is control over the phase stoichiometry, which frequently leads to the formation of defects in the thin films9,36. These defects significantly influence the thin-film carrier scattering mechanisms and consequently the transport properties, so it is important to control the defect concentration for optimal device performance. Yoo et al. 37 obtained a high Seebeck coefficient for Sb2Te3 thin films, prepared using electro-deposition process, due to the formation of nanodots of Te atoms in the samples. Similarly, Zhang et al.40 reported a high Seebeck coefficient and a high power factor for MBE deposited Sb2Te3/Te multilayer thin films. This work therefore specifically focused on the measurement of transport properties as a function of film composition, in which other parameters such as the substrate type, substrate temperature, and film thickness remained constant. The observed variations in the transport properties were interpreted and special emphasis was placed on the carrier energy filtering effect which is regarded as an attractive method to improve the Seebeck coefficient41,42. The proposed method can be used to fabricate efficient Sb2Te3 thin films without any intentional doping and with the added possibility of extending the technology to include flexible TE devices.
Methods
To ensure structure uniformity and reproducibility of the transport properties, the stainless steel foils underwent a thorough polishing process. Square foil samples (side dimension: 20 mm; thickness: 500 µm) were polished with sand paper and a diamond and silica suspension, followed by cleaning with alcohol and water. The foil thickness after polishing was 250 µm; further thinning was difficult, due to the limitations imposed by the employed polishing apparatus.
AlN thin films were grown on a polished stainless steel substrate, using a direct current (DC) reactive sputtering system (ATC Orion Series, AJA International Inc., Scituate, MA, USA). A high-purity Al (99.999% pure) target (diameter: 2 inches) was used. All substrates were cleaned ultrasonically prior to deposition using isopropanol, acetone, ethanol, and deionized water, and dried with flowing nitrogen. The chamber was evacuated to a vacuum pressure of 5 × 10−7 Torr prior to deposition. The substrate was kept at 300 °C and RT during deposition, respectively, for subsequent TE thin-film experiments conducted at high and low substrate temperatures. AlN thin films deposited at RT were further annealed at 300 °C for 3 hours prior to the thermoelectric thin film deposition. The sample was rotated at 10 rpm to ensure uniformity in film thickness and composition. The DC power applied to the Al target was 100 W and the deposition time was 3 h. During the experiment, the working pressure was maintained at 8 mTorr using a mixture of 5 sccm of argon and 7 sccm of nitrogen flowing in the chamber as the sputtering gas.
In this work, Sb-Te films were deposited by thermal co-evaporation of Sb and Te evaporants using an effusion cell evaporator system (Alpha Plus Co., Ltd., Gyeongsangbuk-do, Korea). Evaporation tubes containing high-purity (99.999%) Sb and Te elemental evaporants were placed in separate heater assemblies, which were connected to independent power supplies. The evaporation rates of each source were adjusted individually via two power controllers and monitored by two quartz crystal sensors. Deposition was performed after evacuating the evaporation chamber to a low vacuum pressure of 3 × 10−7 Torr, and the substrate was rotated to ensure uniformity in film composition and thickness. The compositions of the as-deposited thin films were varied by adjusting the individual source deposition rate. The deposition rate of Sb was fixed at 1.5 Å/s; the deposition rate for Te was varied over the range of 3.5–4.5 Å/s for experiments performed at a high substrate temperature of 300 °C. These samples were further annealed for 3 h at 220 °C inside the vacuum chamber after deposition. For experiments in which the substrate was held at RT during deposition, the Sb deposition rate was fixed at 1.5 Å/s, whereas the deposition rate for Te was varied from 2.5 to 4.0 Å/s with further post-deposition annealing at 264 °C for 1 h inside the vacuum chamber.
To determine the optimized film deposition parameters, the influences of composition and substrate temperature on crystal quality and orientation, microstructure, and TE properties were investigated using high-resolution scanning electron microscopy (HR-SEM), energy dispersive X-ray spectroscopy (EDS), and X-ray diffraction (XRD). The details of the characterization process are described in our previous publications14,43. The Hall measurements were performed on several mm side square samples using an Ecopia HMS-5000 room temperature Hall effect system. Few samples could be prepared for analysis due to certain difficulties and hall measurement data is discussed qualitatively in this study. The in-plane electrical and TE properties were measured using a commercially available system (TFTEP-800, SeePel Co. Ltd., Gunpo, Korea). The Seebeck coefficient was determined as the ratio of the Seebeck voltage (ΔV) across the films with respect to the temperature difference (ΔT). For this purpose, two opposite ends of the samples were thermally connected to two heaters maintained at different temperatures. A four-point probe method was used to determine the electrical resistivity of the samples. The power factor PF, given by S2/ρ, was calculated using the measured values of the electrical resistivity and the Seebeck coefficient. Measurement errors for PF remained <10% in all studied cases.
Results and Discussion
Series of Sb-Te thin films with different compositions were prepared at two substrate temperatures, to determine the main factors influencing the TE properties. Measurement complications associated with the use of a conducting foil substrate were minimized by depositing the films on stainless steel foils pre-coated with an AlN electrical insulation layer. AlN was selected as the insulation layer44, due to its high thermal conductivity45, which effectively minimizes the thermal resistance of the substrate assembly specifically for a cross-plane TE device configuration. In this study, we focused only on the electrical properties of the insulation layer. The extra thickness of the foil also ensured good thermal contact between the substrate and the heater during thin film deposition and annealing. In this regard, although substrate flexibility is compromised to some extent, a sufficient foil thickness ensures microstructure uniformity and measurement reliability of the transport properties over the entire thin-film surface.
To obtain thin films with different compositions, we varied the Te evaporation rate while keeping the deposition rate for Sb constant. To minimize measurement error, film compositions were determined over distinct areas of the sample surface, with only averaged values reported. Hereafter, the films are identified by their Te content (at% composition). The thickness of all of the deposited thin films ranged from 1–2 μm. Tables 1 and 2 shows the nominal compositions and actual compositions of the thin films prepared on substrates kept (during deposition) at high temperature and room temperature respectively, after the thermal annealing steps.
Structural and thermoelectric properties of thin films fabricated at high substrate temperatures
The thin films fabricated on a substrate held at 300 °C during deposition underwent an additional annealing treatment at 220 °C under high vacuum for 3 h. This annealing step carried out at a temperature which was significantly lower than the deposition temperature enhanced the transport properties slightly by virtue of reduced thin film defects while preventing any Te loss through sublimation. The experimental data for film composition, structure and thermoelectric properties presented in this section were measured after the aforementioned annealing step. At high substrate temperatures during deposition, the re-evaporation of Te from the deposited film can become an issue. Thus, high Te evaporation rates were used to deposit thin films with excess Te content. Some samples were prepared by depositing a 20-nm-thick layer of chromium (Cr) metal as a thermal shock resistant adhesion layer prior to the deposition of the TE films34; the effects of the adhesion layer on the TE properties of the films were evaluated.
Figure 1a presents the XRD patterns of selected Sb-Te thin films that show the polycrystalline nature of the prepared samples. The (hkl)-plane indices and peak intensities obtained were in good agreement with the standard powder diffraction patterns for Sb2Te3. The XRD peaks were indexed as the rhombohedral Sb2Te3 phase; the (015) plane peak was the most intense. Other high intensity peaks, including those corresponding to (1010) and (110) plane, were also observed, indicating a standard, multi-oriented Sb2Te3 crystal structure in our thin-film samples. For thin films deposited at high substrate temperatures, XRD peaks of significant intensities could not be observed between Two-Theta values of 5° and 20° which was consistent with the standard Sb2Te3 diffraction patterns (JCPDS-015-0874). The Two-Theta range in Fig. 1 was therefore selected in such a way as to ensure that Sb2Te3, Te as well as substrate peaks of substantial intensities could be clearly observed and easily distinguished. Due to significant deviations from phase stoichiometry, additional XRD peaks representing elemental Te were detected in significantly off-stoichiometric samples. In Fig. 1b, the high-intensity XRD peak data for Sb2Te3 were removed to better illustrate the positions and intensities of the Te peaks. The intensity of Te peaks depended on its relative concentration in the samples. Apart from the additional Te peaks and relative differences in peak intensities, no other significant changes in the XRD patterns were observed when the Te content in the thin film increased; thus, the preferred film orientation was preserved. The intensity, sharpness, and narrow widths of XRD peaks indicated that the thin films had a high crystalline quality. In our XRD patterns for TE films, we did not clearly observe any peaks that represented the underlying AlN thin-film layer. A separate XRD experiment was performed for AlN thin film deposited on a bare stainless steel substrate; the results are shown in Fig. 1c. The (002) plane peak was observed to be the most intense, and the presence of several AlN peaks indicated a significant degree of polycrystallinity in the insulation layer.
X-ray diffraction (XRD) patterns for (a) antimony-tellurium (Sb-Te) thin films deposited at high substrate temperatures, (b) Sb-Te thin films in which high-intensity Sb-Te peaks were removed for better visualization of the additional less-intense Te peaks observed due to deviation from the film stoichiometry, and (c) aluminum nitride (AlN) thin film deposited on stainless steel foil.
Figure 2 presents the surface and cross-sectional images of the selected thin films. All samples, regardless of composition, had a homogeneously distributed and well-defined polycrystalline grain structure with large-sized grains, corresponding to a continuous, well-crystallized thin film for the given deposition conditions. A polycrystalline structure with large grains and intervening voids can be explained in terms of a high substrate temperature. At higher temperatures, the substrate imparts a higher kinetic energy to the deposited atoms. This, in turn, reduces the diffusion time for these atoms to move to proper lattice growth points and results in the rapid formation of large multi-oriented grains via the coalescence of smaller atoms and grains. Cross-sectional SEM images (Fig. 2) show columnar-shaped structure grown along its preferred growth direction, which appears to be somewhat perpendicular to the substrate surface. This indicates that film nucleation and growth in the vertical direction is faster than in the horizontal direction of the plane. The AlN microstructure comprised tightly packed columns grown perpendicular with respect to the substrate surface. The adhesion between the TE thin film and insulation layer was remarkably enhanced by the introduction of a Cr adhesion layer, as detachment did not occur while preparing the sample for SEM cross-sectional analysis.
Figure 3a present the carrier concentration n, mobility µ and calculated density-of-state DOS effective mass m* (discussed later in the manuscript) as a function of Te content whereas Fig. 3b present the temperature dependence of the electrical resistivity, given by ρ = 1/neµ, where e is the electron charge, for thin films deposited with and without a Cr adhesion layer. The thin films with compositions closer to phase stoichiometry had lower electrical resistivity. The electrical resistivity of the thin film increased gradually with Te content, which is consistent with the findings of previous studies13,29,40. The electrical resistivity of the sample increased with the temperature in most cases. The observed linear change in the resistivity with temperature indicates the phase purity of the thin films. The hall mobility decreases upon increasing the Te content of the films while the carrier concentration increases slightly.
(a) Carrier concentration (1025 m−3), mobility (10−3 m2/V.s) and density-of-state (DOS) effective mass (10−30 kg) of the Sb-Te thin films as a function of Te content. Temperature variation of the (b) electrical resistivity, (c) Seebeck coefficient, and (d) power factor (PF) of the Sb-Te thin films prepared at high substrate temperatures.
One way to explain this behavior is by considering that excess Te in off-stoichiometric samples, as confirmed by the XRD analysis, is randomly dispersed in the host thin films in elemental form as a second phase. This excess Te may create a Sb2Te3/Te interface where a potential barrier is formed. The observed decrease in carrier mobility could then be directly related to the carrier scattering at the interface through the following relation presented by Savchuk46:
where Ni is the ionized impurity density. The electrical resistivity increases with Te content because the strong decrease of carrier mobility, due to the inability of low energy carriers to overcome the potential barrier, was not compensated by the slight increase in carrier concentration. The magnitude of electrical resistivity obtained suggests that the deposition temperature was sufficiently high to produce the necessary crystallization, while minimizing excessive re-evaporation of Te. The electrical resistivities of the thin films prepared without a Cr layer were higher than those prepared with the adhesion layer, which was consistent with other reports34.
Figure 3c present the temperature variation of the Seebeck coefficient for thin films deposited with and without a Cr adhesion layer. The Seebeck coefficient for the thin films was positive, which indicates that the films are p-type; the value for the coefficient increased gradually with the Te content of the thin film, beyond that for phase stoichiometry. This finding can be explained in terms of the theoretical model for energy filtering of charge carriers at the Sb2Te3/Te interface. Faleev and Leonard42 explained in detail that the carrier scattering regimes as well as the overall underlying physics related with metal atoms dispersed in a host material is quite different from the one that involves other structural defects (such as point defects). The buildup of a potential barrier due to electronic band bending at the interface ensures that only the carriers with energy higher than the barrier height can pass through whereas carriers with lower or insufficient energy are effectively scattered. This energy dependent carrier scattering, i.e. the carrier energy filtering effect, leads to the enhancement of the Seebeck coefficient. The aforementioned argument could be proved by the Mott relation given by the following equation47:
where kB is the Boltzmann constant, σ is the electrical conductivity, τ is the carrier relaxation time. The relaxation time is defined as the average flight time of charge carriers between successive scattering events. Due to the larger number of carrier scattering events taking place at the Sb2Te3/Te interface, the carrier relaxation time and mobility are affected and their dependence on the carrier energy increases significantly. Consequently for thin films with excess Te, the Seebeck coefficient is improved due to its strong dependence on the energy derivative of the relaxation time i.e. d (lnτ(E))/dE at the Fermi level energy as observed from the aforementioned relations. This indicates that perhaps deviation from stoichiometry may be good in the case of Sb-Te thin films. In all cases, the Seebeck coefficient increased with temperature. The thin film with 64.3 at% Te content and devoid of a Cr adhesion layer had the highest Seebeck coefficient value, of about 142 μV/K at 90 °C, among all cases studied. This was closely followed by a Seebeck coefficient of about 138 μV/K that we measured at 90 °C for the 65.0 at% Te film prepared with a Cr adhesion layer.
Assuming a single parabolic band, a simple electron transport model could also be used to describe the Seebeck coefficient of the thin films according to the following relation12:
where h is the Planck’s constant. Therefore, the Seebeck coefficient depends on both the carrier concentration and DOS effective mass. The above relation was used to calculate DOS effective mass of carriers using the measured values of carrier concentration and Seebeck coefficient at room temperature (Fig. 3a). The effective mass value increases with increasing Te content in the thin film samples which could be considered as additional evidence of the occurrence of the energy dependent carrier scattering or carrier energy filtering effect in off-stoichiometric samples leading to an enhancement of the Seebeck coefficient and a decrease in carrier mobility. Therefore, the tailoring of the Te content in the Sb2Te3 thin films can be a key to optimize its thermoelectric properties.
The PF of the thin films was calculated by dividing the square of the Seebeck coefficient by the electrical resistivity. Figure 3d present the PF and its temperature variations for thin films prepared with and without a Cr adhesion layer. The PF generally increased with temperature, as well as with Te content. Due to the quadratic dependence of the PF on the Seebeck coefficient, the thin films with a larger Seebeck coefficient generally had a higher PF. Among the thin films prepared without a Cr adhesion layer, the highest PF value of 0.77 mW/m ∙ K2 was obtained for the 64.3 at% Te thin film sample. An even larger PF of 0.87 mW/m ∙ K2 was noted for film with a Te content of 65.0 at% prepared with a Cr adhesion layer. Although the Seebeck coefficient in the latter case was not the largest, its relatively lower electrical resistivity was responsible for its better performance. One conclusion that can be drawn from these results is that the TE properties of Sb2Te3 thin films depend strongly on the film composition. Thus, the TE PF can be optimized by controlling the defect concentration in the form of excess Te atoms. We observed a meaningfully higher maximum PF for the off-stoichiometric thin film with a Cr adhesion layer. Lastly, the observed changes in the thin film TE properties are expected to be accompanied by significant changes in the Fermi level position, as well as the overall band structure.
Structural and thermoelectric properties of annealed thin films pre-fabricated using substrates held at room temperature
Retaining a low substrate temperature during film deposition is advantageous, because the thin films synthesized at low temperature usually have a low surface roughness, and are therefore compatible with device fabrication processes. The as-deposited samples were amorphous. Further annealing at 264 °C under high vacuum for 1 h promoted crystallization and the phase purity of the thin films beside causing a reduction in the defect concentration. The annealing temperature was carefully chosen so as not to alter the composition of the thin films obtained in the as-deposited state, because Te can re-evaporate from the thin films at higher annealing temperatures. The compositions of the films listed in this section are re-measured values after thermal annealing.
Figure 4a,b presents the XRD patterns of the selected Sb-Te thin films after annealing. The patterns clearly illustrate the effects of substrate temperature (and the annealing method that followed) on the nucleation and crystal growth processes of the resulting thin films. Preferentially c-axis-oriented thin films were obtained when the compositions were stoichiometric or had smaller deviations. The strong and sharp diffraction peaks (003), (006), (009), (0015), and (0018) that correspond to strong reflections from (00 l) crystal planes are clearly evident in these samples. The intensity of (00 l)-oriented peaks was strong, compared with the standard powder diffraction patterns, and decreased significantly with large deviations from the phase stoichiometry. Other Sb2Te3 peaks, such as (015), (1010), and (110) were also observed, indicating that the thin films have multiple orientations. However, these peaks were considerably weaker in thin film with a Te content of 62.0 at%, indicating that this particular thin film with several strong (00 l) plane peaks (the highest corresponding to the (0015) plane) was c-axis-oriented and well textured, if not epitaxial. Additional peaks that represent elemental Te were detected with large deviations from the film stoichiometry. Furthermore, in most of our (00 l)-oriented thin films, the c-axis may not be perpendicular to the substrate surface, due to the presence of additional non-(00 l) peaks.
The effect of substrate temperature during deposition also influences the grain structure and surface morphology of the resulting thin films, as shown in Fig. 5. The grain size and shape, as well as the binding between grain particles, depend significantly on their energy. The grain size of the annealed films is considerably smaller than the grain size of the thin films obtained for film depositions conducted at high substrate temperatures. The microstructure also shows that the grains are dense, uniform, and compact. These observations can be explained by the slow temperature ramp up of 2.5 °C/min during the annealing process; this approach ensured that the as-deposited atoms had sufficient time to diffuse and fill any intervening voids or interspaces to form a continuous thin-film structure during the crystallization process.
The post-annealing microstructural evolution, previously reported for Bi2Te3 thin films48, was considered a consequence of nucleation and new-grain growth of a stable Sb2Te3 phase from an as-deposited amorphous phase. Furthermore, because the annealing was performed at a lower temperature of 264 °C, the smaller grains did not have sufficient kinetic energy to fuse together to form large-sized grains. Cross-sectional SEM images revealed several layers of grains on the order of the film thickness, thus indicating a slow nucleation process and new layer growth on top of a previously deposited layer. Notably for near stoichiometric thin films having excess Te, grains were observed in the form of layers of platelets, preferentially oriented along the c-axis in which the surface energy would possibly be minimized. In contrast, the thin films with large deviations from stoichiometry assumed a relatively disordered stack configuration of a large number of particle-like grains. These unique, oriented microstructures are expected to favorably influence the electronic and phonon transport in the thin films, as discussed below.
Figure 6a presents the carrier concentration, mobility and DOS effective mass as a function of Te content and Fig. 6b present the temperature dependence of the films’ electrical resistivity. As the Te content in the thin film increased, the electrical resistivity also increased up to a Te concentration of 70.4 at%. A further increase in Te content resulted in a slight reduction in the electrical resistivity. The electrical resistivity increased linearly with increasing measurement temperature which emphasizes the metallic characteristics in the thin films. Enhanced electronic transport was ensured in the annealed samples, due to their compact and dense structure, lower surface roughness, and fewer number of vacancy defects. This, in turn, significantly increased the carrier mobility which explains the relatively smaller electrical resistivity of the annealed samples (compared with the samples that were deposited at high substrate temperatures). The DOS effective mass, calculated using the Eq. (4), also shows smaller effective mass values when compared to the samples deposited at high substrate temperatures also confirming the above argument. Furthermore, carrier transport in a (00 l) oriented and layered structure should not encounter as much interference from interface or grain boundary scattering due to a reduced degree of microstructural randomness. In other words, assuming that significant proportions of the grain boundary interfaces as well as other structural defects in the (00 l) layered structure are oriented parallel to the direction of carrier motion, the carrier mobility is expected to increases significantly. These factors should contribute to additional enhancement in the carrier mobility for samples closer to phase stoichiometry. This also explains the measured low electrical resistivity for annealed samples having compositions closer to stoichiometry.
Figure 6c presents the temperature dependence of the Seebeck coefficient. Similar to the electrical resistivity dependence on temperature, the thermopower increased with temperature, as well as with the Te content in the thin film samples. The enhancement in thermopower with the increase in the Te content of the films is attributed to the carrier energy filtering effect due to the energy dependent carrier scattering at Sb2Te3/Te interface as discussed in the previous section. This was further confirmed by the observed increase in the DOS effective mass of the carrier as the Te content in the sample rises (Fig. 6a). The highest Seebeck coefficient value of 128 μV/K at 90 °C was noted in the case of the thin-film sample with a Te content of 70.4 at%. It would appear that the well-ordered microstructure also has an effect on carrier scattering mechanisms. Assuming that the charge carriers follow classical statistics, the Seebeck coefficient is directly proportional to the carrier scattering parameter according to the following relation49:
where η* is the reduced Fermi level and s is the scattering parameter. The scattering parameter collectively defines all the scattering mechanisms present within the material. In addition to the impurity/interface scattering due to excess Te atoms, carriers are also scattered by interfaces in a random microstructure, vacancies or interspaces, surface roughness and other structural defects due to deviation from a periodic crystallographic structure. The enhanced carrier mobility that comes with the (00 l) layered and ordered crystal structure also entails an overall decrease in carrier scattering processes, as well as a possible reduction in the carrier energy filtering effect in which the fewer number of potential barriers at the grain boundary and defect regions are not sufficient to trap many of the low energy carriers. This may explain why we observed a comparatively lower maximum Seebeck coefficient in the annealed thin films samples. Lastly, the highest value for the Seebeck coefficient was obtained for the thin film with the largest electrical resistivity, due to the combined influence of a relatively high carrier-scattering parameter and a low carrier mobility in off-stoichiometric thin films, as previously discussed.
Figure 6d presents the temperature dependence of the electrical PF, which is calculated by dividing the square of the Seebeck coefficient by the electrical resistivity. The Seebeck coefficient was observed to be highest for the 70.4 at% Te film sample. However, the highest PF of about 1 mW/m ∙ K2 was noted for thin film with 64.5 at% Te composition, due to the relatively lower electrical resistivity value of this film. A PF value of 0.9 mW/m ∙ K2 was obtained for thin film with a Te content of 70.4 at%. These trends again suggest that deviation from stoichiometry (with excess Te content of about 65 at%) leads to a better performance for Sb2Te3 thin film. These results also indicate that a higher PF could be obtained if the thin films were synthesized at lower substrate temperatures, followed by annealing, primarily due to the lower electrical resistivity of such samples. This study therefore provides insights into achieving preferential growth orientation in Sb2Te3 thin films and the favorable effects of the aforementioned special orientation on the TE properties of these thin films.
The thin films prepared using the strategy employed in this work performed well. The largest achievable PF in this work was noted to be either similar to or greater than Sb2Te3 thin films synthesized using many different deposition techniques as well as bulk material50,51. Table 3 shows a comparison of the present work with previous studies for the last 7 years on Sb2Te3 thin films. As can be observed, the thin film power factor obtained in this study was much better than the Te nanodots embedded electrodeposited Sb2Te3 thin films37 and easily comparable (if not better) to the nanoparticles incorporated Sb2Te3/Te multilayer thin films deposited by the expensive MBE technique40. Notably, the third parameter required for ZT calculations is thermal conductivity, which was not measured in this study. However, the presence of excess Te atoms in film matrix may result in an enhanced phonon scattering at Sb2Te3/Te interface thereby impeding the thermal transport through the film. As a consequence, the thermal conductivity should reduce leading to further improvement of the ZT.
Conclusion
P-type Sb2Te3 thin films were successfully grown using vacuum thermal co-evaporation on AlN-coated stainless steel foil. Optimum deposition conditions were determined by evaluating the achieved values of the TE PF. The influences of evaporation rate and substrate temperature on film microstructure, crystal orientation, composition, and transport properties were examined. SEM images and sharp XRD patterns with strong, reduced linewidth peaks indicated polycrystalline thin films with optimum crystalline quality. Columnar thin films with a standard multi-oriented microstructure were obtained when thin films were deposited at a substrate temperature of 300 °C. In contrast, thin films deposited at RT and subsequently annealed at 264 °C had a layered microstructure with a preferential c-axis or (00 l) orientation when compositions approached phase stoichiometry. The TE properties were sensitive to the composition. Off-stoichiometric thin films with excess Te content generally had the best TE performance. The best thin film properties were obtained at a measurement temperature of 90 °C, for films deposited on high-temperature substrates (S = 138 µV/K, and ρ = 21.6 µΩ∙m, with a pre-deposited Cr layer) and annealed films (S = 112 µV/K, and ρ = 12.8 µΩ∙m) at 65.0 and 64.5 at% Te content, representing a maximum PF of 0.87 and 1.0 mW/m ∙ K2, respectively. In general, we observed a high Seebeck coefficient in the (015)-oriented film and a high electrical conductivity in c-axis-oriented thin films, primarily due to the different scattering mechanisms that the charge carrier experiences. Furthermore, the inclusion of a Cr adhesion layer enhanced the TE properties of the thin films. Thus, this work provides a promising approach for preparing TE thin films, with controlled preferential crystal growth and transport properties for potential application in vertical-type micro-TE devices. The same process can be extended to include a flexible electronic configuration, if the thickness of the stainless steel foil is reduced further.
References
Chowdhury, I. et al. On-chip cooling by superlattice-based thin-film thermoelectrics. Nat. Nanotechnol. 4, 235–238 (2009).
Majumdar, A. Helping chips to keep their cool. Nat. Nanotechnol. 4, 214–215 (2009).
Snyder, G. J., Lim, J. R., Huang, C.-K. & Fleurial, J.-P. Thermoelectric microdevice fabricated by a MEMS-like electrochemical process. Nat. Mater. 2, 528–531 (2003).
Su, J. et al. A batch process micromachined thermoelectric energy harvester: Fabrication and characterization. J. Micromech. Microeng. 20, 1–6 (2010).
Tritt, T. M. Thermoelectric materials: Holey and unholey semiconductors. Science. 283, 804–805 (1999).
Maassen, J. & Lundstrom, M. A computational study of the thermoelectric performance of ultrathin Bi2Te3 films. Appl. Phys. Lett. 102, 1–5 (2013).
Goldsmid, H. J. & Douglas, R. W. The use of semiconductors in thermoelectric refrigeration. Br. J. Appl. Phys. 5, 386–390 (1954).
Yim, W. M. & Rosi, F. D. Compound tellurides and their alloys for peltier cooling: A review. Solid State Electron. 15, 1121–1140 (1972).
Kim, Y. et al. Structural and thermoelectric transport properties of Sb2Te3 thin films grown by molecular beam epitaxy. J. Appl. Phys. 91, 715–718 (2002).
Zhang, X. et al. Investigation on the electrical transport properties of highly (00l)-textured Sb2Te3 films deposited by molecular beam epitaxy. J. Appl. Phys. 115, 0–5 (2014).
Hicks, L. D. & Dresselhaus, M. S. Thermoelectric figure of merit of a one-dimensional conductor. Phys. Rev. B. 47, 8–11 (1993).
Snyder, G. J. & Toberer, E. S. Complex thermoelectric materials. Nat. Mater. 7, 105–114 (2008).
Goncalves, L. M., Alpuim, P., Rolo, A. G. & Correia, J. H. Thermal co-evaporation of Sb2Te3 thin-films optimized for thermoelectric applications. Thin Solid Films. 519, 4152–4157 (2011).
Ahmed, A. & Han, S. Preparation and thermoelectric properties of annealed CoSb and CoSb2 thin films deposited through RF co-sputtering. J. Alloy. Compd. 686, 540–548 (2016).
Hicks, L. D. & Dresselhaus, M. S. Effect of quantum-well structures on the thermoelectric figure of merit. Phys. Rev. B. 47, 12727–12731 (1993).
Pinisetty, D. & Devireddy, R. V. Thermal conductivity of semiconductor (bismuth-telluride)-semimetal (antimony) superlattice nanostructures. Acta Mater. 58, 570–576 (2010).
Venkatasubramanian, R., Siivola, E., Colpitts, T. & O’Quinn, B. Thin-film thermoelectric devices with high room-temperature figures of merit. Nature. 413, 597–602 (2001).
Harman, T. C., Walsh, M. P., Laforge, B. E. & Turner, G. W. Nanostructured thermoelectric materials. J. Electron. Mater. 34, 19–22 (2005).
Qu, W., Plötner, M. & Fischer, W. J. Microfabrication of thermoelectric generators on flexible foil substrates as a power source for autonomous microsystems. J. Micromech. Microeng. 11, 146–152 (2001).
Francioso, L. et al. Flexible thermoelectric generator for ambient assisted living wearable biometric sensors. J. Power Sources. 196, 3239–3243 (2011).
Böttner, H. et al. New thermoelectric components using microsystems technologies. J. Microelectromech. Syst. 13, 414–420 (2004).
Glatz, W., Schwyter, E., Durrer, L. & Hierold, C. Bi2Te3-based flexible micro thermoelectric generator with optimized design. J. Microelectromech. Syst. 18, 763–772 (2009).
Bahk, J., Fang, H., Yazawa, K. & Shakouri, A. Flexible thermoelectric materials and device optimization for wearable energy harvesting. J. Mater. Chem. C. 3, 10362–10374 (2015).
Fleurial, J. -P. et al. Thermoelectric microcoolers for thermal management applications, in: Proceedings of the 16th International Conference on Thermoelectrics, Dresden, Germany, August 26–29, 641–645 (1997).
Ma, Y., Ahlberg, E., Sun, Y., Iversen, B. B. & Palmqvist, A. E. C. Thermoelectric characteristics of electrochemically deposited Bi2Te3 and Sb2Te3 thin films of relevance to multilayer preparation. J. Electrochem. Soc. 159, D50–D58 (2012).
Shen, S. et al. Enhancing thermoelectric properties of Sb2Te3 flexible thin film through microstructure control and crystal preferential orientation engineering. Appl. Surf. Sci. 414, 197–204 (2017).
Kusagaya, K. & Takashiri, M. Investigation of the effects of compressive and tensile strain on n-type bismuth telluride and p-type antimony telluride nanocrystalline thin films for use in flexible thermoelectric generators. J. Alloys Compd. 653, 480–485 (2015).
Khumtong, T., Sukwisute, P., Sakulkalavek, A. & Sakdanuphab, R. Microstructure and electrical properties of antimony telluride thin films deposited by RF magnetron sputtering on flexible substrate using different sputtering pressures. J. Electron. Mater. 46, 3166–3171 (2017).
Da Silva, L. W., Kaviany, M. & Uher, C. Thermoelectric performance of films in the bismuth-tellurium and antimony-tellurium systems. J. Appl. Phys. 97, 0–10 (2005).
Tan, M. et al. Oriented growth of A2Te3 (A = Sb, Bi) films and their devices with enhanced thermoelectric performance. Sens. Actuators. A. Phys. 171, 252–259 (2011).
Lin, J. M., Chen, Y. C., Yang, C. F. & Chen, W. Effect of substrate temperature on the thermoelectric properties of the Sb2Te3 thin films deposition by using thermal evaporation method. J. Nanomater. 2015, 1–7 (2015).
Fang, B., Zeng, Z., Yan, X. & Hu, Z. Effects of annealing on thermoelectric properties of Sb2Te3 thin films prepared by radio frequency magnetron sputtering. J. Mater. Sci. Mater. Electron. 24, 1105–1111 (2013).
Chen, T. B. et al. Influence of sputtering power of Te and annealing on Sb-Te thin films fabricated by RF and DC co-sputtering. Adv. Mater. Res. 196, 2400–2403 (2011).
Sasaki, Y. & Takashiri, M. Effects of Cr interlayer thickness on adhesive, structural, and thermoelectric properties of antimony telluride thin films deposited by radio-frequency magnetron sputtering. Thin Solid Films. 619, 195–201 (2016).
Patel, N. G. & Patel, P. G. Electrical properties of polycrystalline Sb2Te3 films. J. Mater. Sci. 26, 2543–2546 (1991).
Kim, M. Y. & Oh, T. S. Electrodeposition and thermoelectric characteristics of Bi2Te3 and Sb2Te3 films for thermopile sensor applications. J. Electron. Mater. 38, 1176–1181 (2009).
Yoo, I. J. et al. Thermoelectric characteristics of Sb2Te3 thin films formed via surfactant-assisted electrodeposition. J. Mater. Chem. A. 1, 5430–5435 (2013).
Bouška, M. et al. Pulsed laser deposited GeTe-rich GeTe-Sb2Te3 thin films. Scientific Reports. 6, 26552 (2016).
Giani, A. et al. Growth of Bi2Te3 and Sb2Te3 thin films by MOCVD. Mater. Sci. Eng. B. 64, 19–24 (1999).
Zhang, Z., Zhang, H., Wu, Y., Zeng, Z. & Hu, Z. Optimization of the thermopower of antimony telluride thin film by introducing tellurium nanoparticles. Appl. Phys. A. 118, 1043–1051 (2015).
Heremans, J. P., Thrush, C. M. & Morelli, D. T. Thermopower enhancement in PbTe with Pb precipitates. J. Appl. Phys. 98, 063703 (2005).
Faleev, S. & Leonard, F. Theory of enhancement of thermoelectric properties of materials with nanoinclusions. Phys. Rev. B. 77, 214304 (2008).
Ahmed, A. & Han, S. Effect of Sb content on the thermoelectric properties of annealed CoSb3 thin films deposited via RF co-sputtering. Appl. Surf. Sci. 408, 88–95 (2017).
Lee, C.-Y., Su, A., Liu, Y.-C., Chan, P.-C. & Lin, C.-H. Sensor fabrication method for in situ temperature and humidity monitoring of light emitting diodes. Sensors. 10, 3363–3372 (2010).
Park, M.-H. & Kim, S.-H. Thermal conductivity of AlN thin films deposited by RF magnetron sputtering. Mat. Sci. Semicon. Proc. 15, 6–10 (2012).
Savchuk, V., Boulouz, A., Chakraborty, S., Schumann, J. & Vinzelberg, H. Transport and structural properties of binary skutterudite CoSb3 thin films grown by dc magnetron sputtering technique. J. Appl. Phys. 92, 5319–5326 (2002).
Cutler, M. & Mott, N. Observation of Anderson localization in an electron gas. Phys. Rev. 181, 1336–1340 (1969).
Jeon, S. J. et al. Microstructure evolution of sputtered Bi-Te films during post-annealing: Phase transformation and its effects on the thermoelectric properties. J. Electrochem. Soc. 158, H808–H813 (2011).
Mishima, Y., Kimura, Y. & Kim, S. W. Enhancement of thermoelectric figure of merit through nanostructural control on intermetallic semiconductors toward high-temperature applications. Nanomaterials. 383–418 (2006).
Dong, G.-H., Zhu, Y.-J. & Chen, L.-D. Microwave-assisted rapid synthesis of Sb2Te3 nanosheets and thermoelectric properties of bulk samples prepared by spark plasma sintering. J. Mater. Chem. 20, 1976–1981 (2010).
Lee, M. H., Kim, K.-R., Rhyee, J.-S., Park, S.-D. & Snyder, G. J. High thermoelectric figure-of-merit in Sb2Te3/Ag2Te bulk composites as Pb-free p-type thermoelectric materials. J. Mater. Chem. C. 3, 10494–10499 (2015).
Mori, R., Kurokawa, T., Yamauchi, K., Tanaka, S. & Takashiri, M. Improved thermoelectric performances of nanocrystalline Sb2Te3/Cr bilayers by reducing thermal conductivity in the grain boundaries and heterostructure interface. Vacuum. 161, 92–97 (2019).
Zheng, Z.-H., Luo, J.-T., Li, F., Liang, G.-X. & Fan, P. Enhanced thermoelectric performance of p-type Sb2Te3 thin films through organic-inorganic hybridization on flexible substrate. Curr. Appl. Phys. 19, 470–474 (2019).
Acknowledgements
This work was supported by the National Research Foundation of Korea (NRF) Grant funded by the Korean Government (MSIP) (NRF-2015R1A5A1036133), and by the Energy Efficiency & Resources Core Technology Program of the Korea Institute of Energy Technology Evaluation and Planning (KETEP) granted financial resource from the Ministry of Trade, Industry & Energy, Republic of Korea (No. 20172010000830).
Author information
Authors and Affiliations
Contributions
A.A. conceived the idea of this study, conducted experiments/analysis, and wrote this manuscript. S.H. supervised experimental procedures, analysis and submission of this manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ahmed, A., Han, S. Optimizing the Structural, Electrical and Thermoelectric Properties of Antimony Telluride Thin Films Deposited on Aluminum Nitride-coated Stainless Steel Foil. Sci Rep 10, 6978 (2020). https://doi.org/10.1038/s41598-020-63954-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-63954-0
- Springer Nature Limited