Abstract
Regarding crystalline film growth on large lattice-mismatched substrates, there are two primary modes by which thin films grow on a crystal surface or interface. They are Volmer-Weber (VW: island formation) mode and Stranski-Krastanov (SK: layer-plus-island) mode. Since both growth modes end up in the formation of three-dimensional (3D) islands, fabrication of single crystalline films on lattice-mismatched substrates has been challenging. Here, we demonstrate another growth mode, where a buffer layer consisting of 3D islands initially forms and a relaxed two-dimensional (2D) layer subsequently grows on the buffer layer. This 3D-2D mode transition has been realized using impurities. We observed the 3D-2D mode transition for the case of ZnO film growth on 18%-lattice-mismatched sapphire substrates. First, nano-sized 3D islands grow with the help of nitrogen impurities. Then, the islands coalesce to form a 2D layer after cessation of the nitrogen supply, whereupon an increase in the surface energy may provide a driving force for the coalescence. Finally, the films grow in 2D mode, forming atomically flat terraces. We believe that our findings will offer new opportunities for high-quality film growth of a wide variety of materials that have no lattice-matched substrates.
Similar content being viewed by others
Introduction
Success in developing semiconductor devices has been limited thus far because of lattice-mismatch problems between growth layers and substrates. ZnO-based devices are such examples. ZnO is a multi-functional material with a wide range of existing and emerging applications1,2, such as transparent conducting electrodes3,4,5,6, surface-acoustic-wave (SAW) devices7,8, plasmonic devices9, thin film transistors10,11,12,13,14, resistance switching memristors15, gas sensors16,17, photo detectors18,19, and x-ray imaging systems20. Recently, ZnO has been recognized as a candidate for high-performance ultraviolet light emitting diodes (LED) and laser diodes (LD) because of its wide and direct bandgap of 3.37 eV21,22. The large exciton binding energy (60 meV) is an advantage over a commercial LED material, GaN (25 meV). The most common substrate for ZnO film growth is sapphire because of its high crystal quality and the availability of large size wafers. However, the large lattice mismatch between ZnO and sapphire (18%) results in considerable stress in ZnO films. Stress influences the dislocation density23, the surface morphology, and optical properties24 of thin films that have significant numbers of grain boundaries and/or crystal mosaics25,26,27.
Regarding the heteroepitaxy of large lattice-mismatched systems, there are two primary modes by which thin films grow on a crystal surface or interface. They are i) Volmer-Weber (VW: island formation) mode28 and ii) Stranski-Krastanov (SK: layer-plus-island) mode (Fig. 1a,b)29,30. Since both growth modes end up in the formation of three-dimensional (3D) islands, fabrication of single crystalline films on lattice-mismatched substrates has been challenging28,29,30.
Here, we demonstrate another growth mode, where a relaxed buffer layer consisting of 3D islands initially forms and relaxed two-dimensional (2D) layers subsequently grow on the buffer layer (island-plus-layer growth mode) (Fig. 1c). We describe the difference between the SK mode and the island-plus-layer growth mode. In SK mode, a highly strained 2D layer initially forms, taking advantage of the low surface energy compared to that of 3D islands. As the 2D layer grows, however, the total free energy increases with increasing film thickness because the elastic energy stored in the system increases. Finally, at a critical thickness, a 2D to 3D growth mode transition occurs such that the lattice strain is relaxed and thus the total free energy is minimized. That is, the 2D to 3D mode transition occurs when the elastic energy cost of the 2D growth exceeds the surface energy cost of islanding. In contrast, in the island-plus-layer growth mode, a buffer layer consisting of densely packed nano-sized 3D islands initially grows. Here, the cost of islanding is reduced by insoluble impurities that are adsorbed on the surface31,32,33,34. Since such small islands with large surface-to-volume ratios relieve the elastic strain effectively at the surface35,36, the islands have good in-plane and out-of-plane alignment of the crystal axis. After the lattice strain is relaxed, we desorb the impurity atoms from the surface, which leads to the coalescence of the 3D islands (2D layer formation). This transition from the 3D to 2D growth mode occurs only when the lattice planes of initially formed 3D islands in the buffer layer are well aligned with those of the substrates; otherwise, coalescence of islands does not occur. The possibility of this 3D-2D mode transition has been theoretically predicted by Tinjod et al., who presented a simple equilibrium model, taking into account not only the lattice mismatch, but also the dislocation formation energy and the surface energy37.
Here, we experimentally demonstrate the 3D-2D mode transition for the case of ZnO film growth on 18%-lattice-mismatched sapphire substrates, where nitrogen atoms are employed as impurities. Not only the roles of impurities but also other key parameters to realize the 3D-2D mode transition are discussed.
Results
3D-2D mode transition during ZnO growth on 18%-lattice-mismatched sapphire substrates
We observed the 3D-2D mode transition during ZnO film growth on 18%-lattice-mismatched sapphire substrates. AFM images in Fig. 2 show the evolution of surface morphology upon deposition of a 10-nm-thick buffer layer and 1–1000 nm of ZnO films deposited on the buffer layer. We first deposited 10-nm-thick buffer layers with N2 gas at 735 °C, then ceased supplying N2 gas, and deposited 1–1000 nm-thick ZnO films without N2 gas on the buffer layers. No post-deposition annealing was performed. For comparison, an AFM image of a 1000-nm-thick ZnO film fabricated without a buffer layer is shown in Fig. 2j. As shown in Fig. 2a, the buffer layer fabricated with N2 consists of densely packed nano-sized 3D islands. After cessation of the N2 gas supply, crystal grains originating from each island grow in the buffer layers, and they coalesce to form 2D layers (Fig. 2b–e). Eventually, ZnO films grow in 2D mode, where the films have an atomically flat surface with steps of 0.26 nm in height (Fig. 2h,i). This height corresponds to half of the c-axis length of ZnO. By contrast, in the case without N2, the growth of ZnO film ended up in the formation of 3D structures as shown in Fig. 2j, and the root-mean-square (RMS) roughness (Rq) of the surface is significantly large at 30 nm. These results clearly show that nitrogen plays a key role in determining the growth mode of ZnO films on sapphire substrates, and we discuss the mechanism later.
High crystal quality of ZnO films grown through the 3D-2D mode transition was proved by x-ray diffraction analysis. Figure 3 shows the rocking curves around the symmetric (0002) and asymmetric (\(10\bar{1}1\)) reflections of the 1000-nm-thick ZnO film on the buffer layer fabricated with N2. The inset shows the linear plots. For comparison, rocking curves of a 1000-nm-thick ZnO film fabricated without a buffer layer are shown. For the ZnO film on the buffer layer (3D → 2D), the full width at half maximum (FWHM) of the (0002) and (\(10\bar{1}1\)) planes are 0.01° and 0.09°, respectively. These values are significantly small compared with those of the ZnO film grown without a buffer layer, where the FWHM of the (0002) and (\(10\bar{1}1\)) planes are 0.25° and 0.35°, respectively. The edge-type threading dislocation densities are estimated using the relation, \({{N}}_{{E}}={{\beta }_{{E}}}^{2}/(4.36\times |{{\rm{b}}}_{{E}}{|}^{2})\), where \({{\boldsymbol{\beta }}}_{{\boldsymbol{E}}}\) is the FWHM value of the rocking curve for the (0002) plane, and \(|{{\rm{b}}}_{{E}}|\) is the length of the Burgers vectors for the edge component \((|{{\rm{b}}}_{{E}}|=11\bar{2}0/3=0.1083\,{\rm{nm}})\)38,39,40. The estimated edge-type dislocation densities of the films grown with and without the buffer layer are 6.0 × 107 cm−2 and 3.7 × 1010 cm−2, respectively. These results indicate that ZnO films grown through the 3D-2D mode transition possess high crystal quality with low defect density as well as good in-plane and out-of-plane alignment of the crystal axis. Transmission electron microscopy (TEM) measurements also reveal the high crystal quality of the ZnO film grown through the 3D-2D mode transition. Figure 4 shows the bright field TEM images of ZnO films on sapphire substrates. The film grown on the buffer layer fabricated with N2 (3D → 2D) is a single crystal with a significantly flat surface, whereas the film fabricated without a buffer layer possesses a polycrystalline structure with a rough surface. In addition, we found that the electrical properties are improved by using the buffer layer. All the films prepared in this study exhibit n-type behaviour; however, the films grown on the buffer layer (3D → 2D) have low residual carrier density (2 × 1017 cm−3) and high carrier mobility (90 cm2/Vs), one order of magnitude lower and 1.5 times higher than the film fabricated without a buffer layer, respectively.
Role of impurity
We now discuss the roles of impurities that lead to the 3D-2D mode transition of ZnO film growth on sapphire substrates. Figure 5 shows AFM images of 10-nm-thick buffer layers fabricated with and without N2. Significant changes in the grain size and in the surface roughness are observed. The lateral island size of the film deposited with N2 is about 10 nm, one order of magnitude smaller than that of the film deposited without N2. Since N2 molecules themselves are chemically stable (not active), we consider that N atoms play important roles in determining the island size. As we described elsewhere, N atoms in low-pressure plasmas are mainly generated by electron-impact processes41. These processes consist of dissociative collisions between an electron and a N2 molecule and dissociative collisions between an electron and a N2 molecular ion:
Reaction B occurs through an ionization collision between an electron and a N2 molecule:
In pure N2 plasmas, the dominant process for N-atom production is reaction A because of the large rate coefficient42. For example, at the electron temperature of 2 eV in a plasma where the electron energy distribution functions are Maxwellian, the rate coefficients of reaction A and reaction C are about 5 × 10−11 and 5 × 10−12 cm−3s−1, respectively43. In Ar-N2 plasmas, there is another contribution to N-atom production: charge exchange between the N2 molecule and Ar ion:
which is followed by reaction B that has a large rate coefficient of 2 × 107 cm−3s−1 43.
In conclusion, the dissociation ratio [N]/[N2] is about 10−3 in our Ar-N2 magnetron plasma with an electron temperature of 3 eV44. That is, the N-atom density in the plasma is of the order of 1010 cm−3, which was confirmed by means of vacuum ultraviolet absorption spectroscopy (VUVAS)45,46. This value is comparable to the O-atom density in the plasma originating from ZnO sputtering targets. In contrast, the concentration of N-atoms incorporated into the ZnO film is significantly small at 1017–18 cm−3 (see Supplementary Fig. S1), which is 4–5 orders of magnitude lower than the oxygen concentration in the film. This low nitrogen concentration in the film is due to the low solubility in ZnO27,47,48, and this property of nitrogen is what we consider to lead to grain size decrease. That is, the low solubility makes N-atoms segregate on the surface as well as at the grain boundaries, and thus lower the surface free energy per unit area31,32,33,34. In fact, we observed that nitrogen species are segregated on the film surface by measuring the depth profile of nitrogen concentration of the buffer layer with secondary ion mass spectroscopy (SIMS) (see Supplementary Fig. S1). As a result, in the buffer layer, relaxed small islands form, instead of strained large islands, because the gain of elastic relaxation energy overcompensates for the cost due to extra surface energy (a smaller island has a higher surface-to-volume ratio). After cessation of the N-atom supply, however, the surface energy drastically increases. This increase in the surface energy may provide a driving force for the coalescence of 3D islands, and consequently causes 3D to 2D mode transition as described above. By contrast, in the case without N2, it is hard to form 3D islands as small as the islands fabricated with N2, because the cost of increased surface energy exceeds the gain of elastic energy.
Next, we examine effects of nitrogen on the crystal quality of the buffer layer itself. Figure 6 shows XRD phi scans of the asymmetric (\(10\bar{1}1\)) reflection of the buffer layer deposited with and without N2, where the diffraction intensity is plotted on a logarithmic scale. In both cases, peaks at 60° with respect to each other are observed, indicating the 3D islands in the buffer layers have six-fold symmetry of the hexagonal lattice. This is evidence of epitaxial growth of the 3D islands on the sapphire substrates, where the epitaxial relationship between ZnO and sapphire is [0001]ZnO | |[0001]sapphire and [\(10\bar{1}0\)] ZnO | |[\(11\bar{2}0\)]sapphire. There is, however, a significant difference in the crystal quality between buffer layers fabricated with and without N2. The FWHM of the phi scans for the buffer layer fabricated with N2 is small at 0.33°, suggesting that the islands have small twist angles. This value is about one-fourth of the buffer layer fabricated without N2. Furthermore, no rotated domains are observed for the case with N2, whereas a small but significant amount of rotated domains are observed for the case without N2 (encircled by a dotted line in Fig. 6b). This difference in the in-plane alignment is explained as the result of the difference in the island size. In the small islands fabricated with N2, the strain relaxation occurs efficiently at the surface of the 3D islands36,49. In contrast, the lattice strain in the large islands fabricated without N2 is not fully released through island formation because of the low surface-to-volume ratios. Thus, a large amount of misfit dislocations form in the islands to gain elastic relaxation energy, leading to somewhat poor crystal-axis alignment.
This hypothesis is consistent with the above-mentioned observation of the crystal quality of subsequently grown 1000-nm-thick ZnO films, where the edge-type dislocation density of ZnO films grown on the buffer layer fabricated with N2 is three orders of magnitude lower than that of the film fabricated without the buffer layer. We consider that the good in-plane alignment along with the smooth surface of the buffer layer fabricated with N2 promote the above-mentioned coalescence of 3D islands of the subsequently grown layers.
Key parameters of 3D-2D mode transition
As mentioned above, the size of the 3D islands and the surface smoothness seem to be the keys for growth of high-quality films through the 3D-2D mode transition. Here, we discuss the impact of these parameters of the buffer layers on the subsequently grown 1000-nm-thick layers. Figure 7 shows AFM images of 10-nm-thick buffer layers fabricated at 700–780 °C and subsequently grown 1000-nm-thick layers on the buffer layers. All 1000-nm-thick ZnO films were fabricated at 700 °C. The deposition temperature of the buffer layer apparently influences the surface morphology of subsequently grown 1000-nm-thick ZnO films, and we consider that the size of the 3D island is one of the keys. Figure 8 shows the distribution of the island radius and the average radius of the buffer layers, derived from AFM images, as a parameter of deposition temperature. A very sharp drop in the average radius is observed at 735 °C, where the subsequently grown 1000-nm-thick ZnO film has an atomically flat surface with straight step edges as shown in Fig. 7b (right). This is the result of small islands having large surface-to-volume ratios, bring about efficient release of strain energy at the grain surfaces. The buffer layer fabricated at 700 °C has islands with an average radius of 9 nm, 1.3 times larger than that of the buffer layer fabricated at 735 °C. On this buffer layer, the ZnO film grows in 2D mode but has curved-step edges and a large number of pits, attributed to the residual strain in the film.
Surface smoothness, characterized by surface height distribution, of the buffer layers is another key for the 3D-2D mode transition. For example, if we compare the buffer layers fabricated at 700 °C and 780 °C, there is no significant difference in RMS roughness (Rq) (Fig. 7a,c, left). However, the morphologies of the subsequently grown 1000-nm-thick ZnO films are quite different. ZnO film on the buffer layer fabricated at 700 °C grew in 2D mode, where the surface has step-terrace structures with RMS roughness of 0.99 nm (Fig. 7a, right), while ZnO film on the buffer layer fabricated at 780 °C grew in 3D mode, where the film has a rough surface with RMS roughness of 30.7 nm (Fig. 7c, right). This is attributed to the difference not only in the island size but also in the surface smoothness that is not just defined by the RMS roughness of the buffer layers. Figure 9 shows the surface height distribution, derived from AFM images, of buffer layers fabricated at 700–780 °C. For the buffer layer fabricated at 780 °C, a tail appears around z = 1–2 nm in the distribution (Fig. 9b), yet such a tail is not clearly observed when the distribution is plotted on a linear scale (Fig. 9a). This result indicates that the surface has some spikes that limit the migration of adatoms and/or lead to secondary nucleation, resulting in the subsequent growth to be not in 2D mode but in 3D mode.
In addition, we consider that the morphological changes of buffer layers with the deposition temperature are brought about by the change in the nitrogen coverage on the surface. In fact, we observed that the deposition rate of buffer layers increases from 0.18 to 0.22 nm/s as the deposition temperature increases from 700 to 780 °C50. This change in the deposition rate indicates the change in the coverage of N-atoms on the surface because the adsorbed but non-soluble impurities should reduce the supply of sputtered species on the surface31,50. A more detailed discussion will appear elsewhere.
Finally, we briefly address the differences between our buffer layers fabricated with impurities and low-temperature (LT) buffer layers developed for GaN growth on 15%-lattice-mismatched sapphire substrates51,52. Their major roles are essentially the same: promotion of lateral growth of the subsequent layers, and suppression of dislocations in the layers. However, we found some differences in the details, and here we discuss two of them.
The LT buffer layers for GaN consist of fine crystallites embedded in an amorphous matrix and the morphology is obtained by controlling the growth temperature51,52. The fine crystallites have the same orientation as the substrate and serve as nucleation centres for the subsequently grown GaN film. On the buffer layer, GaN crystals that originate from the fine crystallites grow laterally, owing to the low interfacial free energy between GaN crystals and the buffer layer, and finally coalesce to form a single crystal film. That is, the roles of the LT-buffer layer are to supply the nucleation sites with the same crystal orientation as the substrate, and to realize low interfacial free energy between GaN and the substrates, leading to lateral growth of GaN crystals on the buffer layer. In our case, on the other hand, buffer layers consist of densely packed nano-sized grains that have the same orientation as the substrate. Our nano-sized grains that have a high surface-to-volume ratio relieve the strain efficiently at the surface, resulting in the low dislocation density. On the buffer layer, relaxed crystals grow originating from each grain in the buffer layers, and they coalesce to form a 2D layer due to the low interfacial energy between the 2D layers and the buffer layers. Here, we consider that a drastic increase in the surface energy provides the driving force for the coalescence of crystal grains. During buffer layer formation, the surface energy is lowered by adsorbed impurities, and this is why nano-sized grains are obtained. After cessation of the impurity supply, the surface energy increases due to desorption of impurities, providing a driving force for coalescence of crystal grains.
Another difference from the LT-buffer layer for GaN growth is in the methodology to control the film morphology. For the case of LT-buffer layers, the tuning nob adjusts the deposition temperature, whereas we control the film morphology through manipulating the adsorption/desorption behaviours of impurities. We consider that our method works well especially for materials like ZnO that are easily crystallized even at room temperature.
In summary, by manipulating the surface energy through adsorption/desorption behaviours of N-atoms, single crystalline ZnO films are grown on 18%-lattice-mismatched substrates via 3D-2D mode transition. Here, buffer layers consisting of nano-sized 3D islands initially grow with the help of impurities. After cessation of the impurity supply, the islands rapidly coalesce to form a 2D layer, where an increase in the surface energy provides a driving force for coalescence. Finally, the films grow in 2D mode and have an atomically flat surface. There are two important parameters for the growth of high-quality films through the 3D-2D mode transition: the size of the 3D island and the surface height distribution of the 3D island layer. In small islands, having large surface-to-volume ratios, the strain relaxation occurs at the surface of the 3D islands. As a result, in-plane aligned 3D islands with low defect density are grown. Such 3D islands lead to the coalescence of 3D islands of the subsequently grown layers if the 3D layer has a smooth surface promoting the adatom migration. We believe that our findings on this new growth mode will open up a new pathway for high-quality film growth of a wide variety of materials that have no lattice-matched substrates.
Methods
All films were fabricated by radio frequency (RF) magnetron sputtering. First, 10-nm-thick buffer layers were fabricated with N2 gas on c-plane sapphire substrates at 700–735 °C. ZnO ceramic targets (2 inch, >99.99 purity) were used, and the supplied RF power was 100 W. The used gases were Ar and N2, and the flow rates were 24 and 1 sccm, respectively. The total gas pressure was 0.35 Pa. Vacuum ultraviolet absorption spectroscopy (VUVAS) was performed during the deposition to monitor the absolute value of N-atoms and O-atoms in the sputtering plasma. The VUVAS system was equipped with a micro discharge hollow–cathode lamp, and the VUV light passing through the sputtering plasma was detected by a VUV monochromator and a photomultiplier tube45,46. Plasma parameters were measured by a Langmuir probe set at 50 mm above the cathode, where the electron density and the electron temperature were about 6 × 109 cm−3 and 3 eV, respectively44. The thickness of the buffer layers was confirmed by x-ray reflectometry. The nitrogen concentration of the films was measured by secondary ion mass spectroscopy (SIMS).
Next, 1000-nm-thick ZnO films were deposited on the 10-nm-thick buffer layers. Here, no intentional introduction of impurities into the deposition atmosphere was performed. The substrate temperature was 700 °C. Ar and O2 were used as sputtering gases, and the flow rates were 45 and 5 sccm, respectively. The total gas pressure was 0.70 Pa. Two ZnO ceramic targets (2 inch, >99.99 purity) were used and the RF power supplied to the cathodes was 60 W. The thickness of ZnO films was confirmed by scanning electron microscopy. No post-deposition annealing was performed.
The crystal quality was evaluated by x-ray diffraction (XRD) using a four-circle texture diffractometer and Cu Kα 1 radiation. Transmission electron microscopy (TEM) was done with a JEOL JEM-ARM200F using cross-sectional preparation. The surface morphologies were measured by tapping mode atomic force microscopy (AFM). Electrical properties were evaluated by Hall-effect measurements using the four-point van der Pauw configuration at room temperature.
References
Özgür, Ü. et al. A comprehensive review of ZnO materials and devices. J. Appl. Phys. 98, 1–103 (2005).
Moezzi, A., McDonagh, A. M. & Cortie, M. B. Zinc oxide particles: Synthesis, properties and applications. Chem. Eng. J. 185–186, 1–22 (2012).
Look, D. C. Recent advances in ZnO materials and devices. 80, 383–387 (2001).
Itagaki, N. et al. Highly conducting and very thin ZnO: AI films with ZnO buffer layer fabricated by solid phase crystallization from amorphous phase. Appl. Phys. Express 4, 011101 (2011).
Suhariadi, I. et al. Effects of nitrogen on crystal growth of sputter-deposited ZnO films for transparent conducting oxide. Jpn. J. Appl. Phys. 52, 11NB03 (2013).
Look, D. C. et al. Model for thickness dependence of mobility and concentration in highly conductive zinc oxide. Opt. Eng. 52, 033801 (2013).
Fuo, Y. Q., Li, Y., Zhao, C., Plasido, F. & Walton, A. J. Surface acoustic wave nebulization on nanocrystalline ZnO film. Appl. Phys. Lett. 101, 194101 (2012).
Du, X. Y. et al. ZnO film thickness effect on surface acoustic wave modes and acoustic streaming. Appl. Phys. Lett. 93 (2008).
Allen, J. W. et al. Infrared plasmonics via ZnO. J. Nano Res. 28, 109–119 (2014).
Hoffman, R. L., Norris, B. J. & Wager, J. F. ZnO-based transparent thin-film transistors. Appl. Phys. Lett. 82, 733 (2003).
Carcia, P. F., McLean, R. S., Reilly, M. H. & Nunes, G. Jr. Transparent ZnO thin-film transistor fabricated by rf magnetron sputtering. Appl. Phys. Lett. 82, 1117 (2003).
Park, S. K. et al. Transparent and Photo-stable ZnO Thin-film Transistors to Drive an Active Matrix Organic-Light- Emitting-Diode Display Panel. Adv. Mater. 21, 678–682 (2009).
Dahiya, A. S., Sporea, R. A., Poulin-Vittrant, G. & Alquier, D. Stability evaluation of ZnO nanosheet based source-gated transistors. Sci. Rep. 9, 1–12 (2019).
Lee, C. T., Chen, C. C. & Lee, H. Y. Three dimensional-stacked complementary thin-film transistors using n-type Al:ZnO and p-type NiO thin-film transistors. Sci. Rep. 8, 2–8 (2018).
Barnes, B. K. & Das, K. S. Resistance Switching and Memristive Hysteresis in Visible-Light-Activated Adsorbed ZnO. Thin Films. Sci. Rep. 8, 1–10 (2018).
Jing, Z. & Zhan, J. Fabrication and Gas-Sensing Properties of Porous ZnO Nanoplates **. Adv. Mater. 20, 4547–4551 (2008).
Ahn, M. W. et al. Gas sensing properties of defect-controlled ZnO-nanowire gas sensor. Appl. Phys. Lett. 93, 263103 (2008).
Liu, X. et al. All-printable band-edge modulated ZnO nanowire photodetectors with ultra-high detectivity. Nat. Commun. 5, 1–9 (2014).
Itagaki, N. et al. Synthesis and characterization of ZnInON semiconductor: A ZnO-based compound with tunable band gap. Mater. Res. Express 1, (2014).
Xu, M. et al. Transient Radiation Imaging Based on a ZnO:Ga Single-Crystal Image Converter. Sci. Rep. 8, 1–7 (2018).
Tsukazaki, A. et al. Repeated temperature modulation epitaxy for p-type doping and light-emitting diode based on ZnO. Nat. Mater. 4, 42–45 (2005).
Tsukazaki, A. et al. Blue Light-Emitting Diode Based on ZnO. Jpn. J. Appl. Phys. 44, L643–L645 (2005).
Amano, H. et al. Stress and defect control in GaN using low temperature interlayers. Japanese J. Appl. Physics, Part 2 Lett. 37, 10–13 (1998).
Kisielowski, C. et al. Strain-related phenomena in GaN thin films. Phys. Rev. B - Condens. Matter Mater. Phys. 54, 17745–17753 (1996).
Khranovskyy, V. et al. Improvement of ZnO thin film properties by application of ZnO buffer layers. J. Cryst. Growth 308, 93–98 (2007).
Kaidashev, E. M. et al. High electron mobility of epitaxial ZnO thin films on c-plane sapphire grown by multistep pulsed-laser deposition. Appl. Phys. Lett. 82, 3901–3903 (2003).
Kuwahara, K. et al. High quality epitaxial ZnO films grown on solid-phase crystallized buffer layers. Thin Solid Films 520, 4674–4677 (2012).
Floro, J. A., Hearne, S. J., Hunter, J. A. & Kotula, P. The dynamic competition between stress generation and relaxation mechanisms during coalescence of Volmer – Weber thin films. J. Appl. Phys. 89, 4886 (2001).
Mo, Y. W., Savage, D. E., Swartzentruber, B. S. & Lagally, M. G. Kinetic pathway in Stranski-Krastanov growth of Ge on Si(001). Phys. Rev. Lett. 65, 1020 (1990).
Teichert, C. Self-organization of nanostructures in semiconductor heteroepitaxy. Phys. Rep. 365, 335–432 (2002).
Dirksen, J. A. & Ring, T. A. Fundamentals of Crystallization: Kinetic Effects on Particle Size Distributions and Morphology. Chem. Eng. Sci. 46, 2389–2427 (1991).
Hondros, E. D. The effect of adsorbed oxygen on the surface energy of B.C.C. iron. Acta Metallurgica 16, 1377–1380 (1968).
Hamdi, B., Kessaissia, Z., Donnet, J. B. & Wang, T. K. Variation of surface energy of a bentonite by chemical and thermal treatments. Ann. Chim. Sci. des Matériaux 24, 63–73 (1999).
Sundman, B. A Direct Determination of the Anisotropy of the Surface Free Energy of Solid Gold, Silver, Copper, Nickel and Alpha and Gamma Iron. Acta Metallurgica 12, 64 (1964).
Ross, F. M., Tersoff, J. & Tromp, R. M. Coarsening of self-assembled ge quantum dots on Si(001). Phys. Rev. Lett. 80, 984–987 (1998).
Tersoff, J. & Tromp, R. M. Shape Tranisition in Growth of Strained Islands: Sontaneous Formation of Quantum Wires. Phys. Rev. Lett. 70, 2782–2786 (1993).
Tinjod, F. et al. Key parameters for the formation of II – VI self-assembled quantum dots. 371, 63–66 (2004).
Dunn, C. G. & Koch, E. F. Comparison of dislocation densities of primary and secondary recrystallization grains of Si-Fe. Acta Metall. 5, 548–554 (1957).
Sawai, Y., Hazu, K. & Chichibu, S. F. Surface stoichiometry and activity control for atomically smooth low dislocation density ZnO and pseudomorphic MgZnO epitaxy on a Zn-polar ZnO substrate by the helicon- wave-excited-plasma sputtering epitaxy method. J. Appl. Phys. 108, 063541 (2010).
Chierchia, R. et al. Microstructure of heteroepitaxial GaN revealed by x-ray diffraction. 93, 8918 (2003).
Itagaki, N. et al. Electron-temperature dependence of nitrogen dissociation in 915 MHz ECR plasma. Thin Solid Films 435, 259–263 (2003).
Czerwiec, T., Greer, F. & B, G. D. Nitrogen dissociation in a low pressure cylindrical ICP discharge studied by actinometry and mass spectrometry. J. Phys. D. Appl. Phys. 38, 4278–4289 (2005).
Kumar, S. & Ghosh, P. K. Dissociation of nitrogen in flowing DC glow plasmas. J. Phys. D. Appl. Phys. 26, 1419–1426 (1993).
Bornholdt, S. et al. Characterization of the energy flux toward the substrate during magnetron sputter deposition of ZnO thin films. Plasma Sources Sci. Technol. 22, 025019 (2013).
Takashima, S. et al. Vacuum ultraviolet absorption spectroscopy employing a microdiacharge hollow-cathode lamp for absolute density measurements of hydrogen atoms in reactive plasmas. Appl. Phys. Lett. 75, 3929–3931 (1999).
Hori, M. et al. Measurement and control of absolute nitrogen atom density in an electron-beam-excited plasma using vacuum ultraviolet absorption spectroscopy. J. Appl. Phys. 88, 1756–1759 (2002).
Sumiya, M. et al. SIMS analysis of ZnO films co-doped with N and Ga by temperature gradient pulsed laser deposition. Appl. Surf. Sci. 223, 206–209 (2004).
Suhariadi, I., Shiratani, M. & Itagaki, N. Growth mechanism of ZnO deposited by nitrogen mediated crystallization. Mater. Res. Express 1, 36403 (2014).
Orr, B. G., Kessler, D., Snyder, C. W. & Sander, L. A Model for Strain-Induced Roughening and Coherent Island Growth. Europhys. Lett. 19, 33–38 (1992).
Ide, T. et al. Effects of morphology of buffer layers on ZnO/sapphire heteroepitaxial growth by RF magnetron sputtering. MRS Proc. 1741, mrsf14-1741–aa09-12 (2015).
Akasaki, I., Amano, H., Koide, Y., Hiramatsu, K. & Sawaki, N. Effects of AlN buffer layer on crystallographic structure and on electrical and optical properties of GaN and Ga1−xAlxN (0<x<0.4) films grown on sapphire substrate by MOVPE. J. Cryst. Growth 98, 209–219 (1989).
Amano, H., Akasaki, I., Hiramatsu, K., Koide, N. & Sawaki, N. Effects of the buffer layer in metalorganic vapour phase epitaxy of GaN on sapphire substrate. Thin Solid Films 163, 415–420 (1988).
Acknowledgements
We acknowledge Prof. Makio Uwaha of Aichi Institute of Technology and Prof. Henri Mariette of University Grenoble-Alpes for helpful discussions on the 3D-2D mode transition during epitaxial growth on large lattice-mismatched substrates. This work was supported by NTT Basic Research Laboratories, Samco Science and Technology Foundation, and JSPS KAKENHI Grant Number 18H01206.
Author information
Authors and Affiliations
Contributions
N.I. conceived the idea for the study and designed the experiments. N.I., Y.N., and R.N. grew ZnO films and evaluated them. K.T. and M.H. developed and performed VUVAS measurements. All authors discussed the results, and N.I. wrote the paper. K. Kamataki, K. Koga, and M.S. critically reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Itagaki, N., Nakamura, Y., Narishige, R. et al. Growth of single crystalline films on lattice-mismatched substrates through 3D to 2D mode transition. Sci Rep 10, 4669 (2020). https://doi.org/10.1038/s41598-020-61596-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-61596-w
- Springer Nature Limited