Abstract
Recalescence rate (R) in cooling curve is well known that affected by undercooling in solidification, but the accurate relationship of them is not clear yet. In this paper, based on the undercooled solidification of Fe-B alloy, the factor affected on recalescence process was investigated. The relationship R = VΔT/D was first found, where V is the growth velocity, ΔT the recalescence degree (approximate the undercooling), D the focus region diameter dependent on the distance of the pyrometer. With this result the solidification interface growth velocity can be predicted from recalescence of cooling curve, vice versa. In addition, an approximate relation between growth velocity and the size of the critical nucleus was shown.
Similar content being viewed by others
Introduction
The liquid states, such as water drops and metallic melts, can be maintained at temperatures which are many degrees below their true freezing points, i.e. undercooled state1. Under undercooled state, temperature will rise suddenly due to the fusion latent heat release, i.e. recalescence. Recalescence is discovered and given the generic title’recalescent’ early in 18682. At that time, the thermoelectric pyrometer was unknown, thus the recalescence curves could not be record although it can be observed. In 1898, Roberts-Austen W.C. revealed that the recalescences had been found in metallic gold, copper, bismuth, antimony, lead, and tin, has been described it as “A sudden glowing in a cooling metal caused by liberation of the latent heat of transformation”. Now then on, many studies pay operational attention on the recalescence of solidification process3,4,5,6,7,8,9,10,11,12,13,14,15. Olefield reported a furnace could measure the recalescence curve in casting. Flemings et al. measured the solidification rate in undercooled melts with a video system combining recalescence curve4. Suzuki et al. studied the recalescence in the solidification of Fe-P alloy, and they estimated the dendrite growth velocity with sample diameter divided by the recalescence times from thermal data. Although this method is not accurate owing to the recalescence time does not equals to solidification time actually, the experiment demonstrated that the recalescence rate have similar change tendency with that of the dendrite tip velocity5. Subsequently, Levi et al. revealed the connection of the recalescence curves and transition fraction, although the relationship between the transition fraction and transition time is still a problem6. Yahosseini et al. proposed a model to predict the recalescence process during solidification of metal droplets in the gas atomization process7. Shukla et al. also gave a mathematical model (including recalensece process) based on classical nucleation theory to predict undercooling of droplets8. Lee et al. developed the model for predict cooling curves and solid fraction for eutectic solidification of Gas-atomized alloy droplets9. All of them, however, cannot predict the recalescence (temperature change) actually because recalescence is also related to the parameters of thermometer (see section Discussion). By computer simulation, Geer et al. has given a numerical model for the prediction of grain size in inoculated castings on aluminum alloys. But the recalescence temperature change details was neglected due to unknown of the recalescence rate relationship10. Liang et al. studied the correlation of recalescence with grain refinement of magnesium alloys, and they found that grain size depends on the recalescence undercooling11. Bejan has reported the theoretically reason for the recalescence curve must be S-shaped in accord with the constructed law of design in nature12. Kapturkiewicz et al. gave the cooling curve model of austenite process although it was not fitting well with experiment13. Chen studied the eutectic modification level of Al–7Si alloy by computer aided recognition of thermal analysis cooling curves14. Marcano determined the fraction determination by using cooling curve analysis15. Li et al. employed High speed camera (HSC) to monitor the recalescence behaviors of single solid solution phase and eutectic in Al2O-ZrO2 system16. For all those studies, it is just known the recalescence rate increases with the undercooling, but it is not clear that what is the accurate relationship between recalescence rate and liquid-solid interface growth velocity. Without the relationship, the thermal history (cooling curves) and the growth velocity of solidification can not be predicted directly by each other.
In this study, the recalescence rate and growth velocity will be investigated by undercooled solidification of Fe-3.97 wt% B alloy melt. Then the simple relationship was further deduced and discussed.
Results
If solidification processes at a certain undercooling, the recalescence will be observed in the cooling curves. Figure 1 shows the cooling curves of Fe-3.97 wt%B alloy solidified under different undercooling(L → Fe + Fe2B). As shown in the inset of Fig. 1, recalescence process display as ‘S-shape’ in transformation. Given the recalescence time as Δτ and recalescence temperature as ΔT, thus the recalescence rate R can be expressed as R = ΔT/Δτ. As can be seen, the recalescence process does not varies linear with time, thus the recalescence rate R is average value. Schleip el al have given the measurement method of Δτ in ref. 17. It is worth noting that the recalescence highest temperature for all the cooling curves is very close in resemblance to the eutectic melting point (1174 °C) in rapid solidification. This is because that the eutectic transition is similar to that of pure metal, i.e. solidification interface is uniform in temperature and composition.
To observe the recalescence in sample surface, Fig. 2a shows the solidification interface moving process with undercooling of ΔT = 120 K from HSC. Figure 2b shows the solidification interfaces for difference undercooling’s. It is found that the morphologies of interfaces have minor differences for different undercoolings (ΔT = 70 K~254 K), but the moving rate changes rapidly. The growth velocity of solidification interface (V) are determined from interface moving distance (S) divided by the times (t), i.e. V = S/t.
Figure 3a shows the recalescence rate R measured from the cooling curve like Fig. 1. It can be seen that the value R increases exponentially with undercooling. Figure 3b shows the interface moving velocity V measured from the HSC image like Fig. 2a. As seen, the value of V also increases exponentially with undercooling. Thus, the values of R and V have a similar change trend. Therefore, there is connection between them. To study the relation of V and R, the value of V/R is shown in Fig. 4. It can be found the value of V/R is not a constant, but it decreases with undercooling. From the change trend, V/R may be inversely proportional to undercooling, accordingly, it needs to be discussed.
Discussions
Generally, using pyrometer to measure the thermal history of solidification, the sample size is larger than the focus region of pyrometer. To illustrate the relation of recalescence rate and the interface growth velocity, the schematic is shown in Fig. 5. Given the diameter of focus region as D, the time for the solidification interface across the region as Δτ, then the growth velocity (V) and recalescence rate(R) can be expressed as
where V is the solidification interface growth velocity. ΔT is the recalescence degree or undercooling. Many experiments have shows that, the recalescence degree for primary phase solidification can be thought as linear with solidification undercooling, while that for pure metal or eutectic transformations, is nearly equal to the solidification undercooling18. in the present study, it is assumed that the ΔT equals to the undercooling. Then, it can be obtained,
The growth velocity, V is determined by undercooling19; D is accurate by the distance between the pyrometer and the sample. Equation (3) indicates that, with the same undercooling, the larger value of D, the smaller value of recalescence rate R is. With a same distance between the pyrometer and the sample (constant D), the larger undercooling ΔT is, the larger value of recalescence rate R is.
If growth velocity V is calculated by theory model19, then the recalescence rate will be predicted according to Eq. (3), then more accurate cooling curves can be obtained combining with other model. Equation (3) also indicates that, using the same pyrometer, the recalescence rate in the cooling curve is settled by the distance and undercooling, which determined the focus region diameter D and interface growth velocity V, respectively.
For the present study, the focus region diameter D is about 3–6 mm on condition of the distance of 650 mm between sample and the pyrometer according to the equipment instruction. After substituting average value D = 4.5 mm in Eq. (3), the relation of V/R and ΔT can be calculated as shown in Fig. 4. It can be found that the experiment data trend is consistent with calculation, although there is small deviation. The deviation may be from: (1) ΔT of measurement is smaller than the accurate undercooling as it is from the recalescence degree; (2) the growth velocity is measured from the round sample surface but not smooth one, it is smaller than the accurate value.
Furthermore, it is often assumed that, V ∝ ΔT2 for the undercooled solidification20, thus from Eq. (3), R ∝ ΔT3, so we often see that the recalescence rate increases rapidly with undercooling.
As our knowledge, the recalescence degree is never higher than 0.2Tm, although the largest undercooling can be larger than 0.2Tm21. According to Eq. (3), the smallest V/R approach to D/0.2Tm. For the current Fe-3.97 wt%B alloy, Tm~1455 K, with D = 4.5 mm, so the extreme (smallest) value of V/R is 0.0155 mm/K. This result can be confirmed by the trend of experiment data in Fig. 4.
In addition, it is known that the critical radius of nucleation can be expressed as22
Where γ (J m−2) is the interfacial tension; Tm is the melting point; ΔHf is the latent heat of fusion (J m−3), ΔT is the undercooling (K). From Eqs. (3 and 4), gives
where k is constant \((\frac{2\gamma {T}_{m}}{\varDelta {H}_{f}D})\). It indicates the critical radius, r* is inverse properties to the value of R/V, i.e. nucleation is connected with growth rate.
Conclusions
The recalescence rate of cooling curves for rapid solidification have a similar trend with solidification interface growth velocity. Based on the experimental data of Fe-3.97 wt%B alloy, the theory relationship of recalescence rate and growth velocity is obtained as V/R = D/ΔT. It indicates that, the recalescence rate in the cooling curve does not only depends on the solidification undercooling, but also on the measured distance and measured area of pyrometer. With this relationship the interface growth velocity can be predicted by the cooling curves directly. Lastly, a relationship of the critical nucleation radius, recalescence rate and growth velocity is found as Rr*/V = constant, which suggests that the growth process has something to do with nucleation radius.
Methods
To investigate the recalescence process in solidification, Fe-3.97 wt%B alloy sample is preferred. The sample weighed about 4 g was put in a quartz crucible covered by small amounts of B2O3 glass, then the crucible was placed around the medium positions of induction coils of a high frequency induction melting furnace. Then the sample were cyclically heated and cooled until the different undercoolings achieved. Thermal profiles of each sample were monitored by a one-color pyrometer with 10 ms delay time. An HSC instrumentation system with a high resolution of 1600 × 1600 pixels, I-Speed 221 was used to observe the recalescence process for each transformation. The instrument was focused on the sample surface from front view (the diameter of the crucible is 13.5 mm).
References
Tavakoli, F., Davis, S. H. & Kavehpour, H. P. Freezing of super cooled water drops on cold solid substrates: initiation and mechanism. Journal of Coatings Technology and Research 12, 869–875 (2015).
Barrett W. F. Historical Note on Recalescence. Nature, 235–236 (1910).
Roberts-Austen, W. C. Suffusion in Metals and Alloys. Nature 58, 619–621 (1898).
Suzuki, M., Piccone, T. J. & Flemings, M. C. Measurements of Rapid Solidification Rate in Highly Undercooled Melts with a Video System. Metallurgical Transactions A 22A, 2825–2828 (1991).
Suzuki, M., Piccone, T. J., Flemings, M. C. & Brody, H. D. Solidification of highly undercooled Fe-P alloys. Metallurgical Transactions A 22, 2761–2768 (1991).
Levi, C. G. & Mehrabian, R. Heat Flow during Rapid Solidification of Undercooled Metal Droplets. Metallurgical Transactions A 13, 221–234 (1982).
Yahosseini, M. R. S., Simchi, A., Varahram, N. & Davami, P. Modeling of rapid solidification process in the gas atomization of molten metals. IJMSE 2, 9–15 (2005).
Shukla, P., Mandal, R. K. & Ojha, S. N. Non-equilibrium solidification of undercooled droplets during atomization process. Bulletin of Materials Science 24, 547–554 (2001).
Lee, E. S. & Ahn, S. Solidification progress and heat transfer analysis of gas-atomized alloy droplets during spray forming. Acta Metallurgic Et Materialia 42, 3231–3243 (1994).
Greer, A. L., Bunn, A. M., Tronche, A., Evans, P. V. & Bristow, D. J. Modelling of inoculation of metallic melts: application to grain refinement of aluminum by Al–Ti–B. Acta Materialia 48, 2823–2835 (2000).
Gao, L., Liang, S., Chen, R. & Han, E. Correlation of recalescence with grain refinement of magnesium alloys. Transactions of Nonferrous Metals Society of China, Suup-S1 (2008).
Bejan, A., Lorente, S., Yilbas, B. S. & Sahin, A. Z. Why solidification has an s-shaped history. Scientific Reports 3, 1711–1711 (2013).
Kapturkiewicz, W., Fras, E. & Burbelko, A. A. Computer simulation of the austenitizing process in cast iron with pearlitic matrix. Materials Science and Engineering A 413, 352–357 (2005).
Chen, X., Geng, H. & Li, Y. Study on the eutectic modification level of Al–7Si alloy by computer aided recognition of thermal analysis cooling curves. Materials Science & Engineering A 419, 283–289 (2006).
Marcano, D., Mendez, P., Gibbs, J. W. & Kannengiesser, T. Martensite fraction determination using cooling curve analysis. Solid State Phenomena 172-174, 221–226 (2011).
Li, M., Nagashio, K. & Kuribayashi, K. On the origin of recalescence behaviors of undercooled single-phase mullite and double-phase Al2O3-ZrO2 eutectic melts. Scripta Materialia 47(4), 213–218 (2002).
Schleip, E., Willnecker, R., Herlach, D. M. & Gorler, G. P. Measurements of Ultrarapid Solidification Rates in Greatly Undercooled Bulk Melts with a High Speed Photosensing Device. Mater. Sci. Eng. 98, 39–42 (1988).
Yang, W., Liu, F., Wang, H. F., Chen, Z., Yang, G. C. & Zhou, Y. H. Non-equilibrium transformation path for bulk undercooled hypereutectic Fe–B alloy. Journal of Alloys and Compounds 491, 118–122 (2010).
Kuang, W. W., Christian, K., Wang, H. F., Liu, F. & Herlach, D. M. Eutectic dendrite growth in undercooled Fe83B17 alloy: Experiments and modeling. Scripta Materialia 105, 34–37 (2015).
Willnecker, R., Herlach, D. M. & Feuerbacher, B. Evidence of nonequilibrium processes in rapid solidification of undercooled metals. Physical Review Letters 62, 2707–2710 (1989).
Cahn, R. W. Dropping below freezing point. Nature 349, 736–737 (1991).
Ghomashchi, R. & Nafisi, S. Some remarks on cooling curves as a principle tool for solidification characterization. Journal of Crystal Growth 458, 129–132 (2017).
Acknowledgements
This work was financially supported by the Natural Science Foundation of China (Nos. 51671151 and 51401156), the State Key Laboratory of Solidification Processing in NWPU (No. SKLSP201812) and Foundation of Shaanxi Provincial Department of Education (No. 18JS050).
Author information
Authors and Affiliations
Contributions
Junfeng Xu designed the project, analyzing the data and wrote the paper. Tian Yang gave the discussions of the results and revised the paper. Xiao Wang did the experiments of Fe-B alloys in Supplementary information. Zhuo Li did the experiments of Ni-B alloys in Supplementary information. Ying Xiao analyzed the high speed video images in Supplementary information. Zengyun Jian analyzed the results in Supplementary information.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xu, J., Yang, T., Li, Z. et al. The recalescence rate of cooling curve for undercooled solidification. Sci Rep 10, 1380 (2020). https://doi.org/10.1038/s41598-019-56079-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-56079-6
- Springer Nature Limited
This article is cited by
-
Microstructural Characterization of 70 Wt Pct WC-NiBSi Deposited by PTA-AM
Metallurgical and Materials Transactions A (2024)
-
A Novel Method to Measure the High Temperature Melt Volume Change
Transactions of the Indian Institute of Metals (2023)
-
Role of Remelting in Grain Refinement of Undercooled Single-Phase Alloys
Metallurgical and Materials Transactions A (2022)
-
Morphological transition of silicate crystals solidified from highly undercooled aerodynamically levitated melt droplets
SN Applied Sciences (2021)
-
Speed of Recalescence as a Measure of Graphite Nucleation in Spheroidal Graphite Cast Iron Castings
International Journal of Metalcasting (2021)