Abstract
Two-dimensional and quasi-two-dimensional materials are important nanostructures because of their exciting electronic, optical, thermal, chemical and mechanical properties. However, a single-layer nanomaterial may not possess a particular property adequately, or multiple desired properties simultaneously. Recently a new trend has emerged to develop nano-heterostructures by assembling multiple monolayers of different nanostructures to achieve various tunable desired properties simultaneously. For example, transition metal dichalcogenides such as MoS2 show promising electronic and piezoelectric properties, but their low mechanical strength is a constraint for practical applications. This barrier can be mitigated by considering graphene-MoS2 heterostructure, as graphene possesses strong mechanical properties. We have developed efficient closed-form expressions for the equivalent elastic properties of such multi-layer hexagonal nano-hetrostructures. Based on these physics-based analytical formulae, mechanical properties are investigated for different heterostructures such as graphene-MoS2, graphene-hBN, graphene-stanene and stanene-MoS2. The proposed formulae will enable efficient characterization of mechanical properties in developing a wide range of application-specific nano-heterostructures.
Similar content being viewed by others
Introduction
A generalized analytical approach is presented to derive closed-form formulae for the effective in-plane elastic moduli of hexagonal multiplanar nano-structures and heterostructures. Hexagonal nano-structural forms are common in various two-dimensional and quasi-two-dimensional materials. The fascinating properties of graphene1, a two-dimensional allotrope of carbon with hexagonal nanostructure, has led to an enormous interest and enthusiasm among the concerned scientific community for investigating more prospective two-dimensional and quasi-two-dimensional materials that could possess interesting electronic, optical, thermal, chemical and mechanical characteristics2,3,4. The interest in such hexagonal two-dimensional materials has expanded over the last decade from hBN, BCN, graphene oxides to Chalcogenides like MoS2, MoSe2 and other forms of two-dimensional materials like stanene, silicene, sermanene, phosphorene, borophene etc.5,6. Among these two-dimensional materials, hexagonal honeycomb-like nano-structure is a prevalent structural form3. Four different classes of single-layer materials with hexagonal nano-structure exist from a geometrical point of view, as shown in Fig. 1(a–d). For example, graphene7 consists of a single type of atom (carbon) to form a honeycomb-like hexagonal lattice structure in a single plane, while there is a different class of materials that possess hexagonal monoplanar nanostructure with different constituent atoms such as hBN8, BCN9 etc. Unlike these monoplanar hexagonal nanostructures, there are plenty of other materials that have the atoms placed in multiple planes to form a hexagonal top view. Such multiplanar hexagonal nanostructures may be consisted of either a single type of atom (such as stanene10,11, silicene11,12, germanene11,12, phosphorene13, borophene14 etc.), or different atoms (such as MoS2 15, WS2 16, MoSe2 17, WSe2 16, MoTe2 18 etc.). Even though these two-dimensional materials show promising electronic, optical, thermal, chemical and mechanical characteristics for exciting future applications, a single nanomaterial may not possess a particular property adequately, or multiple desired properties simultaneously. To mitigate this lacuna, recently a new trend has emerged to develop nano-heterostructures by assembling multiple monolayers of different nanostructures for achieving various tunable desired properties simultaneously.
(a) Top view and side views of single-layer hexagonal nanostructures where all the constituent atoms are same and they are in a single plane (e.g. graphene). (b) Top view and side views of single-layer hexagonal nanostructures where the constituent atoms are not same but they are in a single plane (e.g. hBN, BCN). (c) Top view and side views of single-layer hexagonal nanostructures where the constituent atoms are same but they are in two different planes (e.g. silicene, germanene, phosphorene, stanene, borophene). (d) Top view and side views of single-layer hexagonal nanostructures where the constituent atoms are not same and they are in two different planes (e.g. MoS2, WS2, MoSe2, WSe2, MoTe2). (e) Three dimensional view and side views of heterostructures consisted of only monoplanar layers of materials (such as graphene-hBN heterostructures). (f) Three dimensional view and side views of heterostructures consisted of only multiplanar layers of materials (such as stanene-MoS2 heterostructures). (g,h) Three dimensional view and side views of heterostructures consisted of both monoplanar and multiplanar layers of materials (such as graphene-MoS2 and graphene-stanene heterostructures).
Although the single-layer of two-dimensional materials have hexagonal lattice nano-structure (top-view) in common, their out-of-plane lattice characteristics are quite different, as discussed in the preceding paragraph. Subsequently, these materials exhibit significantly different mechanical and electronic properties. For example, transition metal dichalcogenides such as MoS2 show exciting electronic and piezoelectric properties, but their low in-plane mechanical strength is a constraint for any practical application. In contrast, graphene possesses strong in-plane mechanical properties. Moreover, graphene is extremely soft in the out-of-plane direction with a very low bending modulus, whereas the bending modulus of MoS2 is comparatively much higher, depending on their respective single-layer thickness19. Having noticed that graphene and MoS2 possess such complementary physical properties, it is a quite rational attempt to combine these two materials in the form of a graphene-MoS2 heterostructure, which could exhibit the desired level of electronic properties and in-plane as well as out-of-plane strengths. Besides intense research on different two dimensional hexagonal nano-structural forms, recently the development of novel application-specific heterostructures has started receiving considerable attention from the scientific community due to the tremendous prospect of combining different single layer materials in intelligent and intuitive ways to achieve several such desired physical and chemical properties20,21,22,23,24,25,26.
The hexagonal nano-heterostructures can be broadly classified into three categories based on structural configuration, as shown in Fig. 1: heterostructure containing only mono-planar nanostructures (such as graphene-hBN heterostructure)22,23,27, heterostructure containing both mono-planar and multi-planar nanostructures (such as graphene-MoS2 heterostructure19,21, graphene-stanene heterostructure24, phosphorene-graphene heterostructure28, phosphorene-hBN heterostructure28, multi-layer graphene-hBN-TMDC heterostructure26) and heterostructure containing only multi-planar nanostructures (such as stanene-MoS2 heterostructure25, MoS2-WS2 heterostructure20). Recently different forms of multi-layer heterostructures have started receiving immense attention from the scientific community for showing interesting chemical, thermal, optical, electronic and transport properties24,25,29,30. Even though the heterostructures show various exciting physical and chemical characteristics, effective mechanical properties such as Young’s moduli and Poisson’s ratios are of utmost importance for accessing the viability in application of such nano-heterostructures in various nanoelectromechanical systems. The research in this field is still in a very nascent stage and investigations on elastic properties of these built-up structural forms are very scarce to find in literature20,21.
The common practises to investigate these nanostructures are first principle studies/ab-initio and molecular dynamics, which can reproduce the results of experimental analysis with the cost of computationally expensive and time consuming supercomputing facilities. Moreover, availability of interatomic potentials can be a practical barrier in carrying out molecular dynamics simulation for nano-heterostructures, which are consisted of multiple materials. The accuracy of molecular dynamics simulation depends on the interatomic potentials and the situation can become worse in case of nano-heterostructures due to the possibility of having lesser accuracy for built-up structural forms. Molecular mechanics based analytical closed form formulae are presented by many researchers for materials having hexagonal nano-structures in a single layer such as graphene, hBN, stanene, MoS2 etc.7,8,31,32,33. This approach of mechanical property characterization for single-layer nanostructures is computationally very efficient, yet accurate and physically insightful. However, the analytical models concerning two-dimesional hexagonal nano-structures developed so far are limited to single-layer structural forms; development of efficient analytical approaches has not been attempted yet for nano-heterostructures. Considering the future prospect of research in this field, it is essential to develop computationally efficient closed-form formulae for the elastic moduli of nano-hetrostructures that can serve as a ready reference for the researchers without the need of conducting expensive and time consuming molecular dynamics simulations or laboratory experiments. This will accelerate the process of novel material development based on the application-specific need of achieving multiple tunable properties simultaneously to a desirable extent.
In this article, we aim to address the strong rationale for developing a generalized compact analytical model leading to closed-form and high fidelity expressions for characterizing the mechanical properties of a wide range of hexagonal nano-heterostructures. Elastic properties of four different heterostructures (graphene-hBN, graphene-MoS2, graphene-stanene and stanene-MoS2), belonging to all the three classes as discussed in the preceding paragraphs, are investigated considering various stacking sequences. The analytical formulae for elastic moduli of heterostructures are applicable to any number of different constituent single-layer materials with multi-planar or mono-planar hexagonal nanostructures.
Results
Closed-form analytical formulae for the elastic moduli of heterostructures
In this section, the closed-form analytical expressions of elastic moduli for generalized multiplaner hexagonal nano-heterostructures are presented. The molecular mechanics based approach for obtaining the equivalent elastic properties of atomic bonds is well-documented in scientific literature31,34,35. Besides that the mechanics of mono-planar hexagonal honeycomb-like structure is found to be widely investigated across different length scales36,37,38,39,40. Therefore, the main contribution of this article lies in proposing computationally efficient and generalized analytical formulae for nano-heterostructures (having constituent single-layer materials with monoplanar and multiplanar structural form) and thereby presenting new results for various stacking sequence of different nano-heterostructures belonging to the three different classes as described in the preceding section (graphene-MoS2, graphene-hBN, graphene-stanene and stanene-MoS2).
For atomic level behaviour of nano-scale materials, the total interatomic potential energy can be expressed as the sum of various individual energy terms related to bonding and non-bonding interactions34. Total strain energy (E) is expressed as the sum of energy contributions from bending of bonds (E b ), bond stretching (E s ), torsion of bonds (E t ) and energies associated with non-bonded terms (E nb ) such as the van der Waals attraction, the core repulsions and the coulombic energy (refer to Fig. 2).
(a,b) Top view and side view of a generalized form of multiplanar hexagonal nano-structure. (The in-plane angles θ and ψ are indicated in Fig. 2(a), wherein it is evident that \(\psi ={90}^{\circ }-\frac{\theta }{2}\). The out-of-plane angle α is indicated in Fig. 2(b)). (c) Energy components associated with the in-plane (1–2 plane) and out-of-plane (1–3 plane) deformation mechanisms (Direction 1 and 2 are indicated in the figure. Direction 3 is perpendicular to the 1–2 plane. Here A and B indicate two different atoms).
However, among all the energy components, effect of bending and stretching are predominant in case of small deformation31,35. For the multiplanar hexagonal nano-structures (such as stanene and MoS2), the strain energy caused by bending consists of two components, in-plane component (E bI ) and out-of-plane component (E bO ). The out-of-plane component becomes zero for monoplanar nanostructures such as graphane and hBN. Thus the total interatomic potential energy (E) can be expressed as
where Δl, Δθ and Δα denote the change in bond length, in-plane and out-of-plane angle respectively. The quantities k r and k θ represents the force constants for bond stretching and bending respectively. The molecular mechanics parameters (k r and k θ ) and structural mechanics parameters (EA and EI) of a uniform circular beam with cross-sectional area A, length l, Young’s modulus E, and second moment of area I, are related as: \({K}_{r}=\frac{EA}{l}\) and \({k}_{\theta }=\frac{EI}{l}\) 31,34,35. Based on this relationship, the closed form expressions for the effective elastic moduli of multilayer hexagonal nano-heterostructures are derived following a multi-stage idealization scheme using force equilibrium and deformation compatibility conditions. The closed form expressions for the two in-plane Young’s moduli of nano-heterostructures are derived as
The subscript i in the above expressions indicates the molecular mechanics and geometrical properties (as depicted in Fig. 2(a,b)) corresponding to i th layer of the heterostructure. The overall thickness of the heterostructure is denoted by t. n represents the total number of layers in the heterostructure. Expressions for the two in-plane Poisson’s ratios are derived as
Here ν 12 and ν 21 represent the in-plane Poisson’s ratios for loading directions 1 and 2 respectively. Thus the elastic moduli of a hexagonal nano-heterostructure can be obtained using the closed-form analytical formulae (Equations 3–6) from molecular mechanics parameters (k r and k θ ), bond length (l), in-plane bond angle (ψ) and out-of-plane angle (α), which are well-documented in the molecular mechanics literature. The analytical formulae are valid for small deformation of the structure (i.e. the linear region of stress-strain curve). The effect of inter-layer stiffness contribution due Lennard-Jones potentials are found to be negligible for the in-plane elastic moduli considered in this study and therefore, neglected in the analytical derivation (refer to section 7 of the supplementary material).
Validation and analytical predictions for the elastic moduli of heterostructures
Results are presented for the effective elastic moduli of hexagonal multi-layer nano-heterostructures based on the formulae proposed in the preceding section. As investigations on nano-heterostructures is a new and emerging field of research, the results available for the elastic moduli of different forms of heterostructures is very scarce in scientific literature. We have considered four different nano-heterostructures to present the results: graphene-MoS2, graphene-hBN, graphene-stanene and stanene-MoS2 (belonging to the three categories as depicted in the introduction section). Though all these four heterostructures have received attention from the concerned scientific community for different physical and chemical properties recently, only the graphene-MoS2 heterostructure has been investigated using molecular dynamics simulation for the Young’s modulus among all other elastic moduli20,21. Thus we have validated the proposed analytical formulae for Young’s moduli of graphene-MoS2 heterostructure with available results from literature. New results are presented for the two in-plane Poisson’s ratios of graphene-MoS2 heterostructure using the analytical formulae, which are validated by carrying out separate molecular dynamics simulations. Having the developed analytical formulae validated for the two Young’s moduli and Poisson’s ratios, new results are provided for the other three considered heterostructures accounting for the effect of stacking sequence. Moreover, it can be noted that for single layer of the heterostructure (i.e. for n = 1), the proposed analytical formulae can be used to predict the effective elastic moduli of monoplanar (i.e. α = 0) and multiplanar (i.e. α ≠ 0) materials. The analytical predictions for the Young’s moduli and Poisson’s ratios of such single-layer materials are further validated with reference results from literature, as available.
As shown in Tables 1–5, in the case of single-layer hexagonal nanostructures (n = 1) belonging to all the four classes as described in the preceding section (graphene, hBN, stanene and MoS2), the in-plane Young’s moduli obtained using the proposed analytical formulae are in good agreement with reported values in literature for graphene, hBN, stanene and MoS2. These observations corroborate the validity of the proposed analytical formulae in case of a single-layer. However, in case of Poisson’s ratios, the reported values in scientific literature for graphene and hBN show wide range of variability, while the reference values of Poisson’s ratios for stanene and MoS2 are very scarce in available literature. The results predicted by the proposed formulae agree well with most of the reported values for Poisson’s ratios.
Table 1 presents the value of two Young’s moduli obtained from the proposed analytical formulae for nano-heterostructures considering different stacking sequences of graphene and MoS2. The results are compared with the numerical values reported in scientific literature. It can be noted that the difference between E 1 and E 2 is not recognized in most of the previous investigations and the results presented as E 1 = E 2. The Young’s moduli E 1 and E 2 are found to be different for multiplanar single-layer nanostructural forms (such as stanene and MoS2). A similar trend has been reported before by Li41 for MoS2. Thus the effective Young’s moduli of the heterostructures with at least one layer of multiplanar structural form is expected to exhibit different E 1 and E 2 values. In Table 1 it can be observed that for single and bi-layer of graphene E 1 = E 2, while for single and bi-layer of MoS2 E 1 ≠ E 2. In case of heterostructures consisting of both graphene and MoS2 the value of E 2 is observed to be higher than E 1. However, the numerical values of E 1 for different stacking sequences are found to be in good agreement with the values of Young’s modulus reported in literature (presumably obtained for direction-1) corroborating the validity of the developed closed-form expressions. We have carried out separate molecular dynamics simulations for graphene – MoS2 heterostructures to validate the analytical predictions of Poisson’s ratios, as Poisson’s ratios have not been reported for graphene–MoS2 heterostructures in literature. The analytical predictions of Poisson’s ratios reported in Table 1 are found to be in good agreement with the results of molecular dynamics simulations. Similar to the results of Young’s moduli for graphene-MoS2 heterostructure, the two in-plane Poisson’s ratios (ν 12 and ν 21) are found to have different values when at least one multi-planar structural form is present in the heterostructure. Thus having the analytical formulae for all the elastic moduli validated, we have provided new results for three other nano-heterostructures in the following paragraphs based on Equations 3–6.
Table 2 provides the results for elastic moduli of graphene-hBN heterostructure considering different stacking sequences. It is observed that the two Young’s moduli and two in-plane Poisson’s ratios are equal (i.e. E 1 = E 2 and ν 12 = ν 21) in case of graphene-hBN heterostructure as these are consisted of only mono-planar structural forms. Table 3 presents the results for elastic moduli of graphene-stanene heterostructure considering different stacking sequences. As stanene has a multi-planar structural form, the two Young’s moduli and two in-plane Poisson’s ratios show different values (i.e. E 1 ≠ E 2 and ν 12 ≠ ν 21) when at least one of the constituent layers of the heterostructure is stanene. Table 4 presents the results for elastic moduli of stanene-MoS2 heterostructure considering different stacking sequences. As stanene and MoS2 both have multi-planar structural form, the two Young’s moduli and two in-plane Poisson’s ratios show considerably different values (i.e. E 1 ≠ E 2 and ν 12 ≠ ν 21). The results of different elastic moduli corresponding to various stacking sequences are noticed to have an intermediate value between the respective elastic modulus for single layer of the constituent materials, as expected on a logical basis.
The physics based analytical formulae for nano-heterostructures presented in this article are capable of obtaining the elastic moduli corresponding to any stacking sequence of the constituent layer of nano-materials. However, from the expressions it can be discerned that the numerical values of elastic moduli actually depend on the number of layers of different constituent materials rather than their exact stacking sequences. From a mechanics view-point, this is because of the fact that the in-plane properties are not a function of the distance of individual constituent layers from the neutral plane of the entire heterostructure. Figures 3, 4, 5, 6 present the variation of different elastic moduli with number of layers of the constituent materials considering the four different heterostructures belonging from the three different categories, as described in the preceding section. It is observed that the trend of variation for two Young’s moduli and two in-plane Poisson’s ratios are similar for graphene-MoS2 and graphene-stanene heterostructures with little difference in the actual numerical values. The variation of elastic moduli for graphene-hBN heterostructure are presented for E 1 and ν 12 as the numerical values are exactly same for the two Young’s moduli and two in-plane Poisson’s ratios, respectively. The plots furnished in this section can readily provide an idea about the trend of variation of elastic moduli with stacking sequence of multi-layer nano-heterostructures in a comprehensive manner; exact values of the elastic moduli corresponding to various stacking sequences can be easily obtained using the proposed computationally efficient closed-form formulae.
(a) Variation of in-plane Young’s modulus (E 1) with number of layers in a graphene-hBN heterostructure (Variation of E 2 with number of layers in a graphene-hBN heterostructure is same as E 1). (b) Variation of the in-plane Poisson’s ratio (ν 12) with number of layers in a graphene-hBN heterostructure (Variation of ν 21 with number of layers in a graphene-hBN heterostructure is same as ν 12).
Discussion
We have presented computationally efficient analytical closed-form expressions for the effective elastic moduli of multi-layer nano-heterostructures, wherein individual layers may have multiplanar (i.e. α ≠ 0) or monoplanar (i.e. α = 0) configurations. It is interesting to notice that the generalized analytical formulae developed for the Young’s moduli of heterostructures can be reduced to the closed-form expressions provided by Shokrieh and Rafiee31 for graphene considering single-layer (i.e. n = 1), α = 0 and ψ = 30°.
It can be noted from the presented results that the single-layer materials having regular monoplanar hexagonal nano-structures (such as graphene and hBN) have equal value of elastic modulus in two perpendicular directions (i.e. E 1 = E 2 and ν 12 = ν 21). However, for single-layer materials with multiplanar nanostructure, the elastic modulus for direction-2 is more than that of direction-1, even though the difference is not significant. Similar observation is found to be reported in literature41. For single-layer of materials, the formulae of elastic moduli deduced from Equations 3–6 by replacing n = 1, perfectly obeys the Reciprocal theorem (i.e. E 1 ν 21 = E 2 ν 12)42. In case of nano-heterostructures, the Young’s moduli and Poisson’s ratios possess different values if at least any one of the layers have a material with multiplanar hexagonal nano-structure (i.e. E 1 ≠ E 2 and ν 12 ≠ ν 21). An advantage of the proposed bottom-up approach of considering layer-wise equivalent material property is that it allows us to neglect the effect of lattice mismatch in evaluating the effective elastic moduli for multi-layer heterostructures consisting of different materials. In the derivation for effective elastic moduli of such heterostructues, the deformation compatibility conditions of the adjacent layers are satisfied. This is expected to give rise to some strain energy locally at the interfaces, which is noted in previous studies21. From the derived expressions it can be discerned that the numerical values of elastic moduli actually depend on the number of layers of different constituent materials rather than their stacking sequences. In case of multi-layer nanostructures constituted of the layers of same material (i.e. bulk material), it can be expected from Equations 3 and 4 that the Young’s moduli would reduce due to the presence of inter-layer distances, which, in turn, increase the value of overall thickness t.
Effective mechanical properties such as Young’s moduli and Poisson’s ratios are of utmost importance to access the viability for the use of nano-heterostructures in various nanoelectromechanical applications. The major contribution of this work is to develop the generalized closed-form analytical formulae for multi-layer nano-heterostructures. Thses formulae are also applicable to single-layer of materials with monoplanar as well as multiplanar nanostructures. Thus the developed analytical formulae for elastic moduli can be used as an efficient reference for the entire spectrum of materials with lattice-like structural form and the heterostructures obtained by combining multiple layers of different such materials with any stacking sequence. Such generalization in the derived formulae, with the advantage of being computationally efficient and easy to implement, opens up a tremendous potential scope in the field of novel application-specific heterostructure development. We have validated the proposed expressions considering multiple stacking sequences with existing results of literature and separate molecular dynamics simulations for the Young’s moduli and Poisson’s ratios of graphene-MoS2 heterostructure, respectively. In-depth new results are presented for the Young’s moduli and Poisson’s ratios of three other nano-heterostructures (graphene-hBN, graphene-stanene and stanene-MoS2). Even though the results are presented in this article considering only two different constituent materials in a single heterostructure (such as graphene-MoS2, graphene-hBN, graphene-stanene and stanene-MoS2), the proposed formulae can be used for heterostructures containing any number of different materials26. The physics-based analytical formulae are capable of providing a comprehensive in-depth insight on the behaviour of such multilayer heterostructures. Noteworthy feature of the present analytical approach is the computational efficiency and cost-effectiveness compared to conducting nano-scale experiments or molecular dynamics simulations. Thus, besides deterministic analysis of elastic moduli, as presented in this paper, the efficient closed-form formulae could be an attractive option for carrying out uncertainty analysis43,44,45,46,47,48,49,50 based on a Monte Carlo simulation based approach (refer to section 8 of the supplementary material). The bottom-up approach based concept to develop expressions for hexagonal nano-heterostructures can be extended to other forms of nanostrcutures in future.
After several years of intensive investigation, research concerning graphene has logically reached to a rather mature stage. Thus investigation of other two dimensional and quasi-two dimensional materials have started receiving the due attention recently. However, the possibility of combining single layers of different two dimensional materials (heterostructures) has expanded this field of research dramatically; well beyond the scope of considering a simple single layer graphene or other 2D material. The interest in such heterostructures is growing very rapidly with the advancement of synthesizing such materials in laboratory22,23, as the interest in graphene did few years ago. The attentiveness is expected to expand further in coming years with the possibility to consider different tunable nanoelectromechanical properties of the prospective combination (single and multi-layer structures with different stacking sequences) of so many two dimensional materials. This, in turn introduces the possibility of opening a new dimension of application-specific material development that is analogous to metamaterials51,52 in nano-scale. The present article can contribute significantly in this exciting endeavour.
In summary, we have developed computationally efficient physics-based analytical expressions for predicting the equivalent elastic moduli of multi-layer nano-heterostructures. The proposed expressions are validated for graphene–MoS2 heterostructures by carrying out separate molecular dynamics simulations and available results from literature. New results are presented for graphene–hBN, graphene–stanene and stanene–MoS2 heterostructures using the developed analytical framework. As the proposed closed-form formulae are general in nature and applicable to wide range of materials and their combinations with hexagonal nano-structures, the present article can serve as a ready reference for characterizing the material properties in future nano-materials development.
Methods
Analytical framework for equivalent elastic moduli of nano-heterostructures
A concise description of the basic philosophy behind the developed analytical framework is explained in this section (detail derivations are provided as supplementary material with this manuscript). A multi-stage bottom-up idealization scheme is adopted for deriving the closed-form expressions, as depicted in Fig. 7. In the first stage, the effective elastic moduli of each individual layer are determined based on a continuum based approach. This is equivalent to the effective elastic properties of a single-layer nanostructure. The multi-layer heterostructure can be idealized as a layered plate-like composite structural element with respective effective elastic properties and geometric dimensions (such as thickness) of each layer. To ensure the consistency in deformation of the adjacent layers, each of the layers are considered to have equal effective deformation in a particular direction. The equivalent elastic property of the entire heterostructure is determined based on force equilibrium and deformation compatibility conditions. The molecular mechanics parameters (k r and k θ ), bond length and bond angles for different materials, which are used to obtain numerical results based on Equations 3–6, are provided in the next paragraph.
The molecular mechanics parameters and geometric properties of the bonds are well-documented in scientific literature. In case of graphene, the molecular mechanics parameters k r and k θ can be obtained from literature using AMBER force filed53 as k r = 938 kcal mol−1 nm−2 = 6.52 × 10−7 Nnm−1 and k θ = 126 kcal mol−1 rad−2 = 8.76 × 10−10 Nnm rad−2. The out-of-plane angle for graphene is α = 0 and the bond angle is θ = 120° (i.e. ψ = 30°), while bond length and thickness of single-layer graphene can be obtained from literature as 0.142 nm and 0.34 nm respectively7. In case of hBN, the molecular mechanics parameters k r and k θ can be obtained from literature using DREIDING force model54 as k r = 4.865 × 10−7 Nnm−1 and k θ = 6.952 × 10−10 Nnm rad−2 55. The out-of-plane angle for hBN is α = 0 and the bond angle is θ = 120° (i.e. ψ = 30°), while bond length and thickness of single-layer hBN can be obtained from literature as 0.145 nm and 0.098 nm respectively8. In case of stanene, the molecular mechanics parameters k r and k θ can be obtained from literature as k r = 0.85 × 10−7 Nnm−1 and k θ = 1.121 × 10−9 Nnm rad−2 56,57. The out-of-plane angle for stanene is α = 17.5° and the bond angle is θ = 109° (i.e. ψ = 35.5°), while bond length and thickness of single layer stanene can be obtained from literature as 0.283 nm and 0.172 nm respectively56,57,58,59. In case of MoS2, the molecular mechanics parameters k r and k θ can be obtained from literature as k r = 1.646 × 10−7 Nnm−1 and k θ = 1.677 × 10−9 Nnm rad−2, while the out-of-plane angle, bond angle, bond length and thickness of single layer MoS2 are α = 48.15°, θ = 82.92° (i.e. ψ = 48.54°), 0.242 nm and 0.6033 nm respectively15,60,61,62.
Molecular dynamics simulation for Poisson’s ratios of graphene–MoS2 heterostructures
We have followed a similar method as reported in literature21,63,64 for calculating the Poisson’s ratios of graphene–MoS2 bilayers and heterostructures through molecular dynamics simulation. The interatomic potential used for carbon-carbon, molybdenum-sulfur interactions are the second-generation Brenner interatomic potential65,66. We have stabilized the heterostructures following the same method as described in literature21. The MoS2 and graphene layers of the heterostructures are coupled by van der Waals interactions, as described by the Lennard-Jones potential. The adopted cut-off is 10.0A° for M/G/M and 5.0A° for G/M/G heterostructures. These cut-off values are determined by stabilizing and minimizing the M/G/M and G/M/G heterostructures21.
References
Novoselov, K. et al. Two-dimensional gas of massless dirac fermions in graphene. Nature 438, 197–200 (2005).
Balendhran, S., Walia, S., Nili, H., Sriram, S. & Bhaskaran, M. Elemental analogues of graphene: silicene, germanene, stanene, and phosphorene. Small 11, 640–652 (2015).
Xu, M., Liang, T., Shi, M. & Chen, H. Graphene–like two–dimensional materials. Chemical Reviews 113, 3766–3798 (2013).
Das, S., Robinson, J. A., Dubey, M., Terrones, H. & Terrones, M. Beyond graphene: Progress in novel two-dimensional materials and van der waals solids. Annual Review of Materials Research 45, 1–27 (2015).
Geim, A. K. & Grigorieva, I. V. Van der waals heterostructures. Nature 499, 419–425 (2013).
Zhang, Y. J., Yoshida, M., Suzuki, R. & Iwasa, Y. 2d crystals of transition metal dichalcogenide and their iontronic functionalities. 2D Materials 2, 044004 (2015).
Scarpa, F., Adhikari, S. & Phani, A. S. Effective elastic mechanical properties of single layer graphene sheets. Nanotechnology 20, 065709 (2009).
Boldrin, L., Scarpa, F., Chowdhury, R. & Adhikari, S. Effective mechanical properties of hexagonal boron nitride nanosheets. Nanotechnology 22, 505702 (2011).
Huang, C. et al. Carbon-doped BN nanosheets for metal-free photoredox catalysis. Nature Communications 6, 7698 (2015).
Zhu, F. et al. Epitaxial growth of two-dimensional stanene. Nature materials 14, 1020–1025 (2015).
Mortazavi, B. et al. First-principles investigation of mechanical properties of silicene, germanene and stanene. Physica E: Low-dimensional Systems and Nanostructures 87, 228–232 (2017).
Ni, Z. et al. Tunable bandgap in silicene and germanene. Nano Letters 12, 113–118 (2012).
Liu, H. et al. Phosphorene: An unexplored 2d semiconductor with a high hole mobility. ACS Nano 8, 4033–4041 (2014).
Mannix, A. J. et al. Synthesis of borophenes: Anisotropic, two-dimensional boron polymorphs. Science 350, 1513–1516 (2015).
Brunier, T. M., Drew, M. G. B. & Mitchell, P. C. H. Molecular mechanics studies of molybdenum disulphide catalysts parameterisation of molybdenum and sulphur. Molecular Simulation 9, 143–159 (1992).
Zhao, W. et al. Evolution of electronic structure in atomically thin sheets of ws2 and wse2. ACS Nano 7, 791–797 (2013).
Coehoorn, R. et al. Electronic structure of mose2, mos2, and wse2. i. band-structure calculations and photoelectron spectroscopy. Physical review B 35, 6195–6202 (1987).
Ruppert, C., Aslan, O. B. & Heinz, T. F. Optical properties and band gap of single- and few-layer mote2 crystals. Nano Letters 14, 6231–6236 (2014).
Elder, R. M., Neupane, M. R. & Chantawansri, T. L. Stacking order dependent mechanical properties of graphene/mos2 bilayer and trilayer heterostructures. Applied Physics Letters 107, 073101 (2015).
Liu, K. et al. Elastic properties of chemical-vapor-deposited monolayer mos2, ws2, and their bilayer heterostructures. Nano Letters 14, 5097–5103 (2014).
Jiang, J.-W. & Park, H. S. Mechanical properties of mos2/graphene heterostructures. Applied Physics Letters 105, 033108 (2014).
Zhang, C. et al. Direct growth of large-area graphene and boron nitride heterostructures by a co-segregation method. Nature Communications 6 (2015).
Li, Q., Liu, M., Zhang, Y. & Liu, Z. Hexagonal boron nitride–graphene heterostructures: Synthesis and interfacial properties. Small 12, 32–50 (2016).
Chen, X. et al. Electronic structure and optical properties of graphene/stanene heterobilayer. Physical Chemistry Chemical Physics 18, 16302–16309 (2016).
Ren, C.-C., Feng, Y., Zhang, S.-F., Zhang, C.-W. & Wang, P.-J. The electronic properties of the stanene/mos2 heterostructure under strain. RSC Adv. 7, 9176–9181 (2017).
Wang, X. & Xia, F. Van der waals heterostructures: stacked 2d materials shed light. Nature materials 14, 264–265 (2015).
Bruzzone, S., Logoteta, D., Fiori, G. & Iannaccone, G. Vertical transport in graphene-hexagonal boron nitride heterostructure devices. Scientific reports 5 (2015).
Cai, Y., Zhang, G. & Zhang, Y.-W. Electronic properties of phosphorene/graphene and phosphorene/hexagonal boron nitride heterostructures. The Journal of Physical Chemistry C 119, 13929–13936 (2015).
Barrios-Vargas, J. E. et al. Electrical and thermal transport in coplanar polycrystalline graphene–hbn heterostructures. Nano Letters 17, 1660–1664 (2017).
Mortazavi, B. & Rabczuk, T. Multiscale modelling of heat conduction in all-mos2 single-layer heterostructures. RSC Adv. 7, 11135–11141 (2017).
Shokrieh, M. M. & Rafiee, R. Prediction of young’s modulus of graphene sheets and carbon nanotubes using nanoscale continuum mechanics approach. Materials & Design 31, 790–795 (2010).
Le, M.-Q. Prediction of young’s modulus of hexagonal monolayer sheets based on molecular mechanic. s. International Journal of Mechanics and Materials in Design 11, 15–24 (2015).
Mukhopadhyay, T., Mahata, A., Adhikari, S. & Zaeem, M. A. Effective elastic properties of two dimensional multiplanar hexagonal nanostructures. 2D Materials 4, 025006 (2017).
Chang, T. & Gao, H. Size-dependent elastic properties of a single-walled carbon nanotube via a molecular mechanics model. Journal of the Mechanics and Physics of Solids 51, 1059–1074 (2003).
Gelin, B. R. Molecular Modeling of Polymer Structures and Properties (Hanser Gardner Publications, 1994).
Mukhopadhyay, T. & Adhikari, S. Effective in-plane elastic moduli of quasi-random spatially irregular hexagonal lattices. International Journal of Engineering Science 119, 142–179 (2017).
Mukhopadhyay, T., Adhikari, S. and Batou, A. Frequency domain homogenization for the viscoelastic properties of spatially correlated quasi-periodic lattices. International Journal of Mechanical Sciences, https://doi.org/10.1016/j.ijmecsci.2017.09.004 (2017).
Gibson, L. and Ashby, M. F. Cellular Solids Structure and Properties. Cambridge University Press, Cambridge, UK (1999).
Mukhopadhyay, T. & Adhikari, S. Free vibration analysis of sandwich panels with randomly irregular honeycomb core. Journal of Engineering Mechanics 142, 06016008 (2016).
Mukhopadhyay, T. & Adhikari, S. Effective in-plane elastic properties of auxetic honeycombs with spatial irregularity. Mechanics of Materials 95, 204–222 (2016).
Li, T. Ideal strength and phonon instability in single-layer mos 2. Physical Review B 85, 235407 (2012).
Mukhopadhyay, T. & Adhikari, S. Equivalent in-plane elastic properties of irregular honeycombs: An analytical approach. International Journal of Solids and Structures 91, 169–184 (2016).
Vu-Bac, N., Lahmer, T., Zhuang, X., Nguyen-Thoi, T. & Rabczuk, T. A software framework for probabilistic sensitivity analysis for computationally expensive models. Advances in Engineering Software 100, 19–31 (2016).
Mukhopadhyay, T., Mahata, T., Dey, S. & Adhikari, S. Probabilistic analysis and design of hcp nanowires: An efficient surrogate based molecular dynamics simulation approach. Journal of Materials Science & Technology 32, 1345–1351 (2016).
Mahata, A., Mukhopadhyay, T. & Adhikari, S. A polynomial chaos expansion based molecular dynamics study for probabilistic strength analysis of nano-twinned copper. Materials Research Express 3, 036501 (2016).
Mukhopadhyay, T., Chakraborty, S., Dey, S., Adhikari, S. & Chowdhury, R. A critical assessment of kriging model variants for high-fidelity uncertainty quantification in dynamics of composite shells. Archives of Computational Methods in Engineering 240(3), 495–518 (2017).
Dey, S., Mukhopadhyay, T., Sahu, S. K. & Adhikari, S. Stochastic dynamic stability analysis of composite curved panels subjected to non-uniform partial edge loading. European Journal of Mechanics - A/Solids 67, 108–122 (2018).
Metya, S., Mukhopadhyay, T., Adhikari, S. & Bhattacharya, G. System reliability analysis of soil slopes with general slip surfaces using multivariate adaptive regression splines. Computers and Geotechnics 87, 212–228 (2017).
Dey, S. et al. Probabilistic characterisation for dynamics and stability of laminated soft core sandwich plates. Journal of Sandwich Structures & Materials, https://doi.org/10.1177/1099636217694229.
Naskar, S., Mukhopadhyay, T., Sriramula, S. & Adhikari, S. Stochastic natural frequency analysis of damaged thin-walled laminated composite beams with uncertainty in micromechanical properties. Composite Structures 160, 312–334 (2017).
Li, X. & Gao, H. Mechanical metamaterials: Smaller and stronger. Nature materials 15, 373–374 (2016).
Mukhopadhyay, T. & Adhikari, S. Stochastic mechanics of metamaterials. Composite Structures (2016).
Cornell, W. D. et al. A second generation force field for the simulation of proteins, nucleic acids, and organic molecules. Journal of the American Chemical Society 117, 5179–5197 (1995).
Mayo, S. L., Olafson, B. D. & Goddard, W. A. Dreiding: a generic force field for molecular simulations. The Journal of Physical Chemistry 94, 8897–8909 (1990).
Li, C. & Chou, T.-W. Static and dynamic properties of single-walled boron nitride nanotubes. Journal of nanoscience and nanotechnology 6, 54–60 (2006).
Modarresi, M., Kakoee, A., Mogulkoc, Y. & Roknabadi, M. Effect of external strain on electronic structure of stanene. Computational Materials Science 101, 164–167 (2015).
Wang, D., Chen, L., Wang, X., Cui, G. & Zhang, P. The effect of substrate and external strain on electronic structures of stanene film. Phys. Chem. Chem. Phys. 17, 26979–26987 (2015).
Tang, P. et al. Stable two-dimensional dumbbell stanene: A quantum spin hall insulator. Phys. Rev. B 90, 121408 (2014).
Van den Broek, B. et al. Two-dimensional hexagonal tin: ab initio geomaetry, stability, electronic structure and functionalization. 2D Materials 1, 021004 (2014).
Bronsema, K., De Boer, J. & Jellinek, F. On the structure of molybdenum diselenide and disulfide. Zeitschrift für anorganische und allgemeine Chemie 540, 15–17 (1986).
Wieting, T. & Verble, J. Infrared and raman studies of long-wavelength optical phonons in hexagonal mos2. Physical Review B 3, 4286 (1971).
Ma, Z. & Dai, S. Ab initio studies on the electronic structure of the complexes containing mo–s bond using relativistic effective core potentials. Acta Chimica Sinica English Edition 7, 201–208 (1989).
Cooper, R. C. et al. Nonlinear elastic behavior of two-dimensional molybdenum disulfide. Physical Review B 87, 035423 (2013).
Tsai, J.-L. & Tu, J.-F. Characterizing mechanical properties of graphite using molecular dynamics simulation. Materials & Design 31, 194–199 (2010).
Brenner, D. W. et al. A second-generation reactive empirical bond order (rebo) potential energy expression for hydrocarbons. Journal of Physics: Condensed Matter 14, 783 (2002).
Liang, T., Phillpot, S. R. & Sinnott, S. B. Parametrization of a reactive many-body potential for mo21s systems. Phys. Rev. B 79, 245110 (2009).
Lee, C., Wei, X., Kysar, J. W. & Hone, J. Measurement of the elastic properties and intrinsic strength of monolayer graphene. Science 321, 385–388 (2008).
Tu, Z.-c & Ou-Yang, Z.-c Single-walled and multiwalled carbon nanotubes viewed as elastic tubes with the effective young’s moduli dependent on layer number. Phys. Rev. B 65, 233407 (2002).
Alzebdeh, K. I. An atomistic-based continuum approach for calculation of elastic properties of single-layered graphene sheet. Solid State Communications 177, 25–28 (2014).
Lee, C. et al. Elastic and frictional properties of graphene. physica status solidi (b) 246, 2562–2567 (2009).
Bertolazzi, S., Brivio, J. & Kis, A. Stretching and breaking of ultrathin MoS2. ACS Nano 5, 9703–9709 (2011).
Woo, S., Park, H. C. & Son, Y.-W. Poisson’s ratio in layered two-dimensional crystals. Phys. Rev. B 93, 075420 (2016).
Liu, F., Ming, P. & Li, J. Ab initio calculation of ideal strength and phonon instability of graphene under tension. Physical Review B 76, 064120 (2007).
Jiang, J.-W., Wang, J.-S. & Li, B. Young’s modulus of graphene: A molecular dynamics study. Phys. Rev. B 80, 113405 (2009).
Brenner, D. W. Empirical potential for hydrocarbons for use in simulating the chemical vapor deposition of diamond films. Phys. Rev. B 42, 9458–9471 (1990).
Song, L. et al. Large scale growth and characterization of atomic hexagonal boron nitride layers. Nano Letters 10, 3209–3215 (2010).
Kudin, K. N., Scuseria, G. E. & Yakobson, B. I. C 2 f, bn, and c nanoshell elasticity from ab initio computations. Physical Review B 64, 235406 (2001).
Le, M.-Q. Young’s modulus prediction of hexagonal nanosheets and nanotubes based on dimensional analysis and atomistic simulations. Meccanica 49, 1709–1719 (2014).
Jiang, L. & Guo, W. A molecular mechanics study on size-dependent elastic properties of single-walled boron nitride nanotubes. Journal of the Mechanics and Physics of Solids 59, 1204–1213 (2011).
Akdim, B., Pachter, R., Duan, X. & Adams, W. W. Comparative theoretical study of single-wall carbon and boron-nitride nanotubes. Phys. Rev. B 67, 245404 (2003).
Oh, E.-S. Elastic properties of boron-nitride nanotubes through the continuum lattice approach. Materials Letters 64, 859–862 (2010).
Lorenz, T., Teich, D., Joswig, J.-O. & Seifert, G. Theoretical study of the mechanical behavior of individual TiS2 and MoS2 nanotubes. The Journal of Physical Chemistry C 116, 11714–11721 (2012).
Jiang, J.-W., Qi, Z., Park, H. S. & Rabczuk, T. Elastic bending modulus of single-layer molybdenum disulfide (mos2): finite thickness effect. Nanotechnology 24, 435705 (2013).
Acknowledgements
T.M. acknowledges the financial support from Swansea University through the award of Zienkiewicz Scholarship. S.A. acknowledges the support of the ‘Engineering Nonlinearity’ program grant (EP/K003836/1) funded by the EPSRC. M.A.Z. acknowledges the funding support from the National Science Foundation under Grant No. NSF-CMMI 1537170. The authors are also grateful for computer time allocation provided by the Extreme Science and Engineering Discovery Environment (XSEDE) under award number TG-DMR140008.
Author information
Authors and Affiliations
Contributions
T.M. and A.M. primarily conceived the idea of developing analytical expressions for nano-heterostructures. T.M. derived the analytical formulae and prepared the manuscript. A.M. carried out the molecular dynamics simulations for the Poisson’s ratios of graphene-MoS2 heterostructure. S.A. and M.A.Z. contributed significantly throughout the entire period by providing necessary scientific inputs.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mukhopadhyay, T., Mahata, A., Adhikari, S. et al. Effective mechanical properties of multilayer nano-heterostructures. Sci Rep 7, 15818 (2017). https://doi.org/10.1038/s41598-017-15664-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-15664-3
- Springer Nature Limited