Abstract
Eight new lanthanide derivatives containing 6-peroxoniobio-4-phosphate building block, [LnIII(H2O)6]2[H4(NbO2)6P4O24]·nH2O [Ln = Eu (1), Gd (2), Tb (3), Dy (4), Ho (5), Er (6), Tm (7), Yb (8), 1–5, 7, 8 n = 12; 6 n = 9], have been successfully obtained using an in-situ strategy and fully characterized in the solid state by single-crystal X-ray diffraction, IR spectra, TG-MS, PXRD. Structural analyses indicate that these isostructural polyanions 1–8 consist of one [P4(NbO2)6O24]10− (P 4 (NbO 2 ) 6 ) clusters and two pendant Ln3+ cations. In these compounds, P 4 (NbO 2 ) 6 clusters are connected by lanthanide cations to form extended two-dimensional architectures. The approach takes advantage of the ability of in-situ formed P 4 (NbO 2 ) 6 cluster to build frameworks by using it as ligands to lanthanide ions. The photoluminescence (PL) and lifetime decay behaviors of 1, 3 and 4 in solid state have been performed at room temperature. The PL emission of 1, 3 and 4 is mainly derived from the characteristic 5D0→7FJ (J = 1, 2, 3, 4), 5D4→7FJ (J = 6, 5, 4, 3) and 4F9/2→6H J (J = 15/2, 13/2, 11/2) transitions of the EuIII, TbIII and DyIII cations, respectively.
Similar content being viewed by others
Introduction
Polyoxometalates (POMs)1, 2 are a unique family of polynuclear anionic metal oxo clusters with properties suitable for many potential applications in catalysis, magnetism, biomedicine, materials science, and nanotechnology3,4,5. Whilst many Mo and W POM clusters can be built in a controlled way, the designed assembly of polyoxoniobate (PONb) is more difficult due to its inherent stability at higher pH. Till 2002, Nyman et al. discovered the first Keggin-type heteropolyoxoniobate anion [SiNb12O40]16− 6, and thereafter, PONb species has become one of the most widely investigated families of molecules in the POM family7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23,24,25,26,27. However, the researches of PONb clusters are mainly focused on alkaline system owing to the basic nature of the hexaniobate Lindqvist ion [Nb6O19]8− (Nb 6 )7, 12, the most common used starting material in PONb chemistry. In this context, the amphoteric or complexed transition-metal (TM) can be introduced to obtain novel heterometallic PONbs12, 22,23,24,25,26,27. Nevertheless, most of the reported TM-containing PONb derivatives are synthesized by hydrothermal or hydrothermal-diffusion methods. In contrast, some Nb-substituted polyoxotungstates of the classic Lindqvist or Keggin derivatives has been produced under acidic solution in the presence of H2O2 28,29,30,31. Recently, we have successfully manipulated the reaction of Nb 6 cluster under acidic condition by an in-situ synthetic strategy19,20,21,22. In this respect, a series of novel oligomeric derivatives have been successfully isolated, for example, {[P2W12Nb6(O2)4O57]2}, {[P2W12Nb6O61]4[Nb4O10]} and {P2W12Nb7O63}4[Nb4O10]}, all of these polyanions were obtained by using the in-situ formed cluster [P2W12(NbO2)6O56]12− (P2W12(NbO2)6) as second building block (SBU)19, 20. In fact, the ability of these oxo-terminal Ot(Nb) groups to react with TM was also recently demonstrated in the examples of {[P2W12Nb6]6Mn15}21 and {[SiW9Nb3]3Mn}22. This is because the substitution of WVI by the lower NbV leads to an increased basicity of the oxygen atoms and thus has a strong nucleophilicity.
Despite these work, we are yet to introduce hetero atom into Nb 6 acidic system to design and synthesize novel hetero-containing PONbs: in 2014 we reported a new AsV-containing polyoxoniobate {As2Nb4(O2)4}32. Its structure resembles that of the peroxo-Nb6 cluster33, in which two peroxo-Nb groups are substituted by two As ligands. Very recently, we also obtained a 6-peroxoniobo-4-phosphate cluster isolated as guanidinium salt ((CN3H6)6[H4P4Nb6(O2)6O24]∙4H2O)34, which has the same polyanion TMA3[H7Nb6P4(O2)6O24]·7H2O reported previously by Casey et al. in 201515. These results drive us to the development of a new in-situ formed SBU system, and suggested that it is possible to design and synthesize novel TM or lanthanide ion derivatives by using the in-situ formed P 4 (NbO 2 ) 6 cluster as second building block.
On the other hand, it should be noted that even though the class of PONb-based lanthanide derivatives was pioneered by Yamase and Naruke as early as 199435, only a few lanthanide-containing PONb clusters have been characterized so far (Table S1). Besides the above-mentioned isostructural polyoxometallolanthanoates, {[Ln3O(OH)3(OH2)3]2Al2(Nb6O19)5} (Ln = Eu, Tb, Er, Lu, Tb4.3Eu1.7)35,36,37,38, Liu et al. reported a series of lanthanide derivatives based on saturated W/Nb mixed-addenda POM in 2012, including {(P2W15Nb3)4Ln6} (Ln = Ce3+, Eu3+)39, {(GeW9Nb3)nEu} (n = 2, 4), {(GeW9Nb3)4Cs(SO4)Eu5}, {(GeW9Nb3)4Cs2Eu4}, {(GeW9Nb3)4Eu5.5} and {GeW9Nb3Eu1.25}40. Very recently, Zheng et al. communicated the first series of giant Nb-W-Ln heterometallic POMs, {Ln12W12(Nb6O19)12} (Ln = Y, La, Sm, Eu, Yb)14.
Herein, we report the formation of a new family of phosphoniobate-based lanthanide derivatives, [LnIII(H2O)6]2[H4(NbO2)6P4O24]·nH2O [Ln = Eu (1), Gd (2), Tb (3), Dy (4), Ho (5), Er (6), Tm (7), Yb (8), 1–5, 7, 8 n = 12; 6 n = 9], making use of the in-situ formed P 4 (NbO 2 ) 6 cluster as second building block. Their crystal structures have been solved by single-crystal X-ray diffraction and further characterized by IR spectra, powder X-ray diffraction (PXRD), and thermogravimetric-mass analyses (TG-MS). Structural analyses show that compounds 1–8 are isostructural and consist of a 6-peroxoniobio-4-phosphate [H4(NbO2)6P4O24]6− fragment and two pendant [Ln(H2O)6]3+ cations, forming an interesting two-dimensional plane and representing the rare PONb-based lanthanide derivatives. In addition, the luminescent properties of 1, 3 and 4 have been investigated systematically.
Results and Discussion
Lindqvist type [Nb6O19]8− (Nb 6 ) anions are known to be stable above pH 10.57, a state in which lanthanide ions are easy to hydrolysis and thus make it difficult to investigate polyoxoniobate-lanthanide (PONb-Ln) materials. In this paper, a new strategy for the synthesis of PONb-Ln derivatives has been developed. Its major experimental strong point is the facile preparation of target compounds from in-situ formed P 4 (NbO 2 ) 6 building block from acidic aqueous solution. Eight new [LnIII(H2O)6]2[H4(NbO2)6P4O24]·nH2O compounds are all synthesized under the similar reaction conditions. The procedure involves forming two solutions. K7H[Nb6O19]·13H2O (0.55 g, 0.40 mmol) was dissolved in a solution consisting of 4.0 mL of 30% aqueous H2O2 and 36 mL of water, acidified to pH ca. 2.5 via addition of 1.0 mL H3PO4 (3.0 M), being as solution A. While solution B comprises LnCl3·nH2O (4.0 mmol) in 2.0 mL of water, which is added into solution A and the pH of the resultant mixture is adjusted to 1.2–2.0, depending on the lanthanide metal used. The mixtures are then heated at 90 °C for 4 hours and filtered and then left at room temperature to crystallize. Single crystals are collected after about two weeks with the average yield 10–20% based on niobium.
Interestingly, the colour of the hexaniobate solution turns from colorless to bright-yellow with the addition of phosphoric acid, suggesting the formation of peroxo {NbO2} group. This is common in the previous {NbO2}-substituted polyoxotungstate chemistry20, 31, and also reinforced by the fact that the solution comprising P 4 (NbO 2 ) 6 is intensely yellow, whereas the solution turns to colorless quite rapidly with the addition of NaHSO3. Importantly, the color of the resultant compounds 1, 2, 3, 4 and 8 is almost same to that of P 4 (NbO 2 ) 6 owing to the corresponding colorless lanthanide chloride, while the color of compounds 5, 6 and 7 is somewhat different, depending on the color of lanthanide chloride used (Fig. 1).
There are several aspects of the synthetic conditions that can influence the formation of these clusters, taking compound 1 as example, a series of reaction sets under different experimental conditions of pH, temperature, heating time and the mole ratio of EuIII/Nb6 were investigated. If the solution of the reactants were left to heat at 90 °C for less than 2 h, we have been unable to isolate single crystals of compound 1, however, it was found that there was no obvious increase in the yields when the heating time was more than 4 h. In addition, the reaction is not particularly sensitive to the amount of EuIII because 1 could be obtained with the mole ratios of EuIII/Nb6 ranging from 6:1 to 16:1, with 10:1 giving the highest yield. It is worth mentioning here that compounds 1−8 can be isolated without the need for extra cations, different from an essential templating role of Cs+ in the formation of Keggin and Wells-Dawson-type niobium-substituted polyoxotungstates28,29,30,31, 41,42,43.
Single-crystal X-ray diffraction analysis reveals that 1−8 are isostructural and comprise a neutral [LnIII(H2O)6]2[H4(NbO2)6P4O24] (Ln2P4(NbO2)6, Ln = Eu (1), Gd (2), Tb (3), Dy (4), Ho (5), Er (6), Tm (7), Yb (8)) subset and some lattice water molecules. The self-assembly of all presented crystal structures can be traced back to coordinative bonding forces and the lanthanide ions are coordinated to POMs, connecting them to two-dimensional frameworks (Fig. 2). All of the compounds crystallize in the space group orthorhombic Pbca and with almost identical unit cell dimensions. This is unsurprising given that the only difference between the clusters is the lanthanide metal present, and thus the structural description is only exemplified by 1.
Structurally, the architecture Eu2P4(NbO2)6 consists of a 6-peroxoniobo-4-phosphate (P 4 (NbO 2 ) 6 ) cluster with two supporting [Eu(H2O)6]3+ fragments on both sides (Fig. 3a). Each P 4 (NbO 2 ) 6 cluster is linked to four [Eu(H2O)6]3+ fragments by four Eu–O–P bridges, whereas every [Eu(H2O)6]3+ moiety is bound to two P 4 (NbO 2 ) 6 clusters by two Eu–O–P bridges, resulting in a two-dimentional framework. Therefore, this subset should be formulated as Eu2P4(NbO2)6. To our knowledge, this is the first observation of the peroxoniobophosphate-based lanthanide derivatives in POM chemistry, although there are many examples of Mo, W POM-based lanthanide aggregates.
Ball-and-stick/polyhedral representations of Eu2P4(NbO2)6 (a), P4(NbO2)6 (b), P2Nb3 (c) and coordination environment of NbO7 (d) and EuO8 (e). All solvent water molecules have been omitted for clarity. Color code: NbO7 blue polyhedral, PO4 pink polyhedral, EuO8 green dodecahedral, Nb blue spheres, P pink spheres, Eu green spheres, O red spheres, peroxo bond red.
It is worth noting that the polyanion P 4 (NbO 2 ) 6 resembles structurally the previously reported [H7Nb6P4O24(O2)6]3− (1′) cluster of Casey and co-authors15. This centrosymmetric cluster can be viewed as two P 2 Nb 3 units fused by two Nb‒µ 2-O‒Nb and two P‒µ 2-O‒Nb bridges (Fig. 3b). The P 2 Nb 3 can be regarded as a peroxohexaniobate33 with a contiguous longitudinal strip of three Nb(O2) groups (one on equatorial position and two on axial position) replaced by two PO4 groups (Figs 3c and S1). In 1, each of the six Nb atoms is ligated by one µ 3-O bridging atom, four µ 2-O bridging atoms, and one terminal peroxo group, giving a pentagonal bipyramid geometry (Fig. 3d). As shown in Table S2, the average Nb–O and Nb–Op bond length is in the range of 1.863(5)–2.110(5) and 1.912(9)–1.969(7) Å, respectively, and the average Op–Nb–Op angle is 43.63°, not significantly different from those in 1′ reported previously15. The remaining sites in the coordination sphere of the lanthanide ions are occupied by six terminal aqua ligands (Eu–O: 2.275(6)–2.504(7) Å, Table S2), resulting in an eight-coordinated dodecahedral geometry (Fig. 3e). Additionally, all the P atoms exhibit conventional tetrahedral coordination polyhedra, and the P–O bond lengths are in the range of 1.496(6)–1.526(6) Å (Table S2), which is shorter than those in 1′, where P–O lengths are 1.508(2)–1.561(2) Å15. The peroxo group bond lengths, O–O, range from 1.389(12) to 1.49(19) Å with the mean value 1.45 Å (Table S2), which is shorter than that for hydrogen peroxide published in 1951 (1.49 Å)44.
The metal–oxygen bond lengths in 1−8 are sorted and plotted in the order of their lengths (Fig. 4), it can be clearly seen that the bond lengths of Nb-peroxo and Nb‒µ 3‒O in 1−8 are almost the same. The Ln‒O bonds length are gradually reduced, which are generally in agreemnt with the ion radius trend in the lanthanide elements.
Bond valence sum (BVS) calculations45 are carried out on all the Ln, Nb, P and O centers (Table S3) and the results show that all the Ln, Nb and P atoms are in the +3, +5 and +5 oxidation states, respectively. The BVS values of the µ 2-O oxygen atoms bridging Nb1–Nb2 (O3) are in the range of 1.29–1.31, suggesting that these oxygen atoms are monoprotonated. In addtition, charge-balance considerations with counter cations suggested that compounds 1−8 should contain the two additional protons, and we think these two protons are delocalized in the polyoxoanions on the basis of the previous studies by Nyman and Niu46, 47.
The Fourier transform infrared spectra (FT-IR) of 1–8, (CN3H6)6[H4P4Nb6(O2)6O24]∙4H2O34 and K7H[Nb6O19]·13H2O (Nb 6 ) were recorded in the range of 4000–450 cm−1 (Figures S2–3). As expected, the overall IR spectra of 1–8 are almost the same because of the isostructural nature (Table 1). All compounds 1–8 exhibit strong and medium bands in the range of 1200–1000 cm−1, associated with antisymmetric stretching of the P–O bond15. However, in comparison with the IR spectrum of the isolated (CN3H6)6[H4P4Nb6(O2)6O24]∙4H2O material, ν(P–O) and ν(Nb–O–Nb) vibration frequencies for 1–8 have different shifts, which may be due to the coordination of lanthanide ions to the phosphorus centers and thus result in the changes of molecular symmetry.
The significant changes in IR spectra (Fig. 5) of 1−8 compared to that of Nb 6 are the appearance of strong intensity bands at 850 cm−1 and in the region 1200-1000 cm−1, which is characteristic of the antisymmetric stretching vibrations of peroxo group29, 31 and P–O bond, respectively. This is in satisfactory agreement with the solid-state structure. Additionally, the above-mentioned results confirm that the 6-peroxoniobio-4-phosphate framework formed in-situ remains intact under the condition of the synthesis, and further indicate that the developed strategy may be further applicable to molecules of the class of PONb-based lanthanide derivatives.
The photoluminescence behaviours of compounds 1, 3 and 4 in solid state at room temperature are depicted in Fig. 6, which displays intense photoluminescence upon excitation at 394, 378 and 388 nm for compounds 1, 3 and 4, respectively. The emission spectrum of compound 1 exhibits four characteristic emission bands at 590, 612, 653 and 698 nm, corresponding to 5D0→7F1,5D0→7F2,5D0→7F3 and 5D0→7F4 transitions of the Eu3+ ions (Fig. 6a). These are in good agreement with previous results39, 48. The 5D0→7F1,3 transitions are magnetic dipole transitions and insensitive to their coordination environments, while 5D0→7F2,4 transitions are electric dipole transitions and sensitive to their local environments49. The transition at 590 nm belongs to the magnetic dipole 5D0→7F1 transition and its emission intensity scarcely varies with the strength of the ligand field exerted on the Eu3+ ions, whereas the highest relative intensity of the 5D0→7F2 transition at 612 nm is the electric dipole transition and implies red emission light of 1. Further, the intensity of 5D0→7F2 transition is extremely sensitive to chemical bonds in the vicinity of the Eu3+ ions. The 5D0→7F2/5D0→7F1 ratio is widely regarded as a measured of the coordination state and site symmetry of the lanthanide50. However, it should be noted that this ratio is easily influenced by other factors such as the polarizability of the ligands. For 1, the value is ca. 13.5 implying the low site symmetry of the Eu3+ ions, which agrees well with the distorted dodecahedral geometry of Eu3+ ions in 1. Furthermore, the excitation spectrum of 1 monitored at the Eu3+ 5D0→7F2 transition (612 nm) contains a narrow band and several weak bands (Fig. 6b). The narrow band at 394 nm is attributed to the 7F0→5L6 transition of the intra-4f6, the three weak peaks in the range of 300–445 nm are assigned to 7F0→5D4 (362 nm), 7F0→5G2 (385 nm), 7F0→5D3 (416 nm) transition, respectively51. In order to obtain the lifetime, the luminescence decay curve of 1 was measured at room temperature by monitoring the strongest emission of 5D0→7F2 (Figs 6c and S4), which can be fitted successfully to a single exponential function as the equation I = A exp(−t/τ). The affording lifetime (τ) is 148.38 μs with a pre-exponential factor (A) of 2045.82.
(a) The emission spectrum of 1 under excitation at 394 nm at room temperature. (b) The emission spectrum of 1 under excitation at 612 nm at room temperature. (c) The decay curve of 1. (d) The emission spectrum of 3 under excitation at 378 nm at room temperature. (e) The emission spectrum of 3 under excitation at 547 nm at room temperature. (f) The decay curve of 3. (g) The emission spectrum of 4 under excitation at 388 nm at room temperature. (h) The emission spectrum of 4 under excitation at 573 nm at room temperature. (i) The decay curve of 4.
Furthermore, the emission spectrum of 3 upon excitation at 378 nm exhibits a maximum at 546 nm corresponding to the 5D4→7F5 transition of Tb3+ ion, while the peaks located at 488, 588 and 620 nm are attributed to the 5D4→7F6, 5D4→7F4 and 5D4→7F3 transitions of Tb3+ ion (Fig. 6d), respectively52,53,54. Interestingly, the excitation spectrum of 3 upon the excitation at 546 nm consists of three dominant emission bands at 343, 353 and 378 nm, which can be ascribed to the 7F6→5L6, 7F6→5L9 and 7F6→5G6 transitions (Fig. 6e), respectively55. The luminescence lifetime of 3 was monitored and can also conform to a single exponential function with a lifetime 18.67 μs (Figs 6f and S5). Meanwhile, the emission spectrum of 4 under excitation at 388 nm displays one high-intensity emission peak at 573 nm and two low-intensity emission peaks at 481 and 663 nm, which is assigned to the 4F9/2→6H13/2, 4F9/2→6H15/2 and 4F9/2→6H11/2 transitions of Dy3+ ions (Fig. 6g), respectively56. It is noteworthy that the intensity of the4F9/2→9H13/2 electric dipole transition is much higher than that of the 4F9/2→6H15/2 magnetic dipole transition, illustrating that the Dy3+ ions reside in low symmetrical environments without inversion. The excitation spectrum of 4 collected by monitoring the emission at 573 nm is presented in Fig. 6h, and the most intense peak is observed at 388 nm (6H15/2→4I13/2), whereas the other three relatively weak peaks are located at 324 nm (6H15/2→6P3/2), 350 nm (6H15/2→6P7/2) and 364 nm (6H15/2→6P5/2), respectively. Interestingly, the lifetime curve for 4 can be well-fitted using a second-order exponential function I = A 1 exp(t/τ 1) + A 2 exp(t/τ 2), affording the luminescence lifetimes τ 1 and τ 2 as 2.77 μs (57.65%) and 10.09 μs (42.35%) (Figs 6i and S6), respectively. The average lifetime τ* is calculated as 5.87 μs based on the formula τ* = (A1τ1 2 + A2τ2 2)/(A1τ1 + A2τ2)57.
The flat, tongue-shaped CIE chromatic diagram represents an internationally agreed method of color identification by combining three primary colors (red, green and blue), which will be seen in light with a wavelength. And with a certain conversion, it is important that only two new values (x and y) can be shown on a two-dimensional chart, where x and y represents the horizontal and vertical axis, respectively. In order to name colors, the emission spectra of 1, 3 and 4 were converted into the x and y coordinates in the CIE chromatic diagram (Fig. 7). The (x, y) values for 1, 3 and 4 are found to be (0.65, 0.35), (0.36, 0.48) and (0.38, 0.43), respectively, corresponding the reddish orange for 1, green for 3 and yellowish green for 4.
Conclusion
In summary, we have developed a new synthetic method for the synthesis of a new family of PONb-based lanthanoid complexes, 1–8. In order to accomplish the synthesis, a new strategy was developed and successfully applied. The experimental aspects of the strategy include in-situ formation of P 4 (NbO 2 ) 6 building block in acidic media, addition of lanthanide chloride salt and pH adjustment to the desired value. All compounds have been fully characterized in the solid state by single-crystal X-ray diffraction, IR spectra, TG-MS, PXRD. Moreover, their luminescence and lifetime decay behaviors were also investigated systematically. This study not only enriches the structural diversity of lanthanide derivatives containing PONb aggregates, but also provides a convenient synthetic route to PONb-based lanthanoid clusters. In future work, we will extend this approach to isolate various symmetries with the aim of providing in-situ formed building block that can be used to design and systematically tailor new luminescent materials with control.
Experimental Section
Materials and methods
All the reagents were obtained from commercial sources and used as received. All solvents were used without further purification. K7H[Nb6O19]·13H2O58 were prepared using literature methods.
Synthesis of 1
K7H[Nb6O19]·13H2O (0.55 g, 0.40 mmol) was dissolved in a solution consisting of 4.0 mL H2O2 (30%) and 36 mL of water. Under rapidly stirring, 1.0 mL H3PO4 (3.0 M) was added. Twenty minutes later (at this point pH was about 2.5), a solution of EuCl3·6H2O (1.47 g, 4.0 mmol in 2 mL H2O) was added. The resultant solution was adjusted to pH 1.53 and heated to 90 °C for 4 h. Then, the mixture was cooled to room temperature and filtered. The clear filtrate was kept at room temperature to allow slow evaporation. Subsequent crystallization over 2 weeks yielded a bright-yellow hydrated salt in 12% yield (based on Nb).
Synthesis of 2–8
Employing GdCl3·6H2O (1.49 g, 4.0 mmol), TbCl3·6H2O (1.50 g, 4.0 mmol), DyCl3·6H2O (1.48 g, 4.0 mmol), HoCl3·6H2O (1.53 g, 4.0 mmol), ErCl3·6H2O (1.52 g, 4.0 mmol), TmCl3·7H2O (1.61 g, 4.0 mmol), YbCl3·6H2O (1.53 g, 4.0 mmol) instead of EuCl3·6H2O (1.47 g, 4.0 mmol) under similar reaction conditions, with the pH value adjusted to 1.96, 1.82, 1.58, 1.74, 1.72, 1.25 and 1.26 for 2–8, respectively. Average yields are 10–20% based on niobium.
Physical measurements
IR spectra (ν = 4000–400 cm−1) of the samples were recorded on a PerkinElmer FT-IR spectrometer using KBr pellets. Powder X-ray diffraction (PXRD) data were recorded on a Bruker D8 Advance instrument with Cu Kα radiation (λ = 1.5418 Å) in the angular range 2θ = 5–50° at 293 K. Thermogravimetric analyses (TGA) were measured on a NETZSCH STA 449 F5 Jupiter thermal analyzer in flowing N2 with a heating rate of 10 °C·min−1. Photoluminescence properties were performed on EDINBURGH FLS 980 fluorescence spectrophotometer.
X-ray crystallography
Suitable single crystals of 1–8 were selected from their respective mother liquors and placed in a thin glass tube. X-ray diffraction intensity was recorded on a Bruker Apex-II CCD diffractometer at 296(2) K with MoKa monochromated radiation (λ = 0.71073 Å). Structure solution and refinement were carried out by using the SHELXS-97 and SHELXL-2014 program package59, 60 for 1–8. Selected details of the data collection and structural refinement of compounds 1–8 can be found in Table S5. Further details of the crystal structure investigation can be obtained from the Fachinformationszentrum Karlsruhe, 76344 Eggenstein-Leopoldshafen, Germany (fax: (+49)7247–808–666; e-mail: crysdata@fiz-karlsruhe.de) on quoting the depository CSD numbers 432370–432377 for 1–8.
References
Pope, M. T. & Müller, A. Polyoxometalate Chemistry: An Old Field with New Dimensions in Several Disciplines. Angew. Chem. Int. Ed. Engl. 30, 34–48 (1991).
Long, D.-L., Burkholder, E. & Cronin, L. Polyoxometalate clusters, nanostructures and materials: From self assembly to designer materials and devices. Chem Soc Rev 36, 105–121 (2007).
Clemente-Juan, J. M., Coronado, E. & Gaita-Ariño, A. Magnetic polyoxometalates: from molecular magnetism to molecular spintronics and quantum computing. Chem. Soc. Rev. 41, 7464–7478 (2012).
Proust, A. et al. Functionalization and post-functionalization: a step towards polyoxometalate-based materials. Chem. Soc. Rev. 41, 7605–7622 (2012).
Wang, S.-S. & Yang, G.-Y. Recent Advances in Polyoxometalate-Catalyzed Reactions. Chem. Rev. 115, 4893–4962 (2015).
Nyman, M. et al. A general synthetic procedure for heteropolyniobates. Science 297, 996–998 (2002).
Nyman, M. Polyoxoniobate chemistry in the 21st century. Dalton Trans. 40, 8049–8058 (2011).
Hou, Y., Alam, T. M., Rodriguez, M. A. & Nyman, M. Aqueous compatibility of group IIIA monomers and Nb-polyoxoanions. Chem. Commun. 48, 6004–6006 (2012).
Guo, G., Xu, Y., Cao, J. & Hu, C. The {V4Nb6O30} Cluster: A New Type of Vanadoniobate Anion Structure. Chem. - Eur. J. 18, 3493–3497 (2012).
Hou, Y., Zakharov, L. N. & Nyman, M. Observing Assembly of Complex Inorganic Materials from Polyoxometalate Building Blocks. J. Am. Chem. Soc. 135, 16651–16657 (2013).
Son, J.-H., Wang, J., Osterloh, F. E., Yu, P. & Casey, W. H. A tellurium-substituted Lindqvist-type polyoxoniobate showing high H2 evolution catalyzed by tellurium nanowires via photodecomposition. Chem Commun 50, 836–838 (2014).
Wu, H.-L., Zhang, Z.-M., Li, Y.-G., Wang, X.-L. & Wang, E.-B. Recent progress in polyoxoniobates decorated and stabilized via transition metal cations or clusters. CrystEngComm 17, 6261–6268 (2015).
Zhang, Y.-T. et al. High-Nuclear Vanadoniobate {Nb48V8} Multiple-Strand Wheel. Inorg. Chem. 54, 11083–11087 (2015).
Jin, L., Li, X.-X., Qi, Y.-J., Niu, P.-P. & Zheng, S.-T. Giant Hollow Heterometallic Polyoxoniobates with Sodalite-Type Lanthanide-Tungsten-Oxide Cages: Discrete Nanoclusters and Extended Frameworks. Angew. Chem. Int. Ed. 55, 13793–13797 (2016).
Son, J.-H., Park, D.-H., Keszler, D. A. & Casey, W. H. Acid-Stable Peroxoniobophosphate Clusters To Make Patterned Films. Chem. - Eur. J. 21, 6727–6731 (2015).
Son, J.-H. & Casey, W. H. A new Keggin-like niobium-phosphate cluster that reacts reversibly with hydrogen peroxide. Chem Commun 51, 12744–12747 (2015).
Zhang, Z.-Y. et al. Antimony-dependent expansion for the Keggin heteropolyniobate family. Chem Commun 51, 3091–3093 (2015).
Son, J.-H. & Casey, W. H. Reversible capping/uncapping of phosphorous-centered Keggin-type polyoxoniobate clusters. Chem Commun 51, 1436–1438 (2015).
Zhang, D. et al. A New Nb28 Cluster Based on Tungstophosphate, [{Nb4O6(OH)4}{Nb6P2W12O61}4]36−. Inorg. Chem. 53, 9917–9922 (2014).
Zhang, D. et al. Two new members of the niobium-substituted polytungstophosphate family based on hexalacunary [H2P2W12O48]12− building blocks. Inorg Chem Front 2, 254–262 (2015).
Zhang, D. et al. A {Nb6P2W12}-Based Hexameric Manganese Cluster with Single-Molecule Magnet Properties. Chem. - Eur. J. 21, 17683–17690 (2015).
Wang, H. et al. Insight into the reactivity of in situ formed {(NbO2)3SiW9}: synthesis, structure, and solution properties of a trimeric polytungstosilicate trapping a {MnNb9} core. Dalton Trans 45, 15236–15241 (2016).
Son, J.-H. & Casey, W. H. Two RhIII -substituted polyoxoniobates and their base-induced transformation: [H2RhNb9O28]6− and [Rh2(OH)4Nb10O30]8−. Dalton Trans 44, 20330–20333 (2015).
Liang, Z., Zhang, D., Ma, P., Niu, J. & Wang, J. A. {Co4O4} Cubane Incorporated within a Polyoxoniobate Cluster. Chem. - Eur. J. 21, 8380–8383 (2015).
Guo, W. et al. Broad-Spectrum Liquid- and Gas-Phase Decontamination of Chemical Warfare Agents by One-Dimensional Heteropolyniobates. Angew. Chem. Int. Ed. 55, 7403–7407 (2016).
Liang, Z. et al. The {Ni10Nb32} aggregate: a perspective on isopolyniobates as ligands. Dalton Trans 45, 16173–16176 (2016).
Liang, Z. et al. {Fe3Nb25} cluster based on an Fe-centred Keggin unit. Dalton Trans. 46, 1368–1371 (2017).
Kim, G.-S. et al. Dimerization of A-α-[SiNb3W9O40]7− by pH-Controlled Formation of Individual Nb–μ-O–Nb Linkages. Inorg. Chem. 42, 5537–5544 (2003).
Kim, G.-S., Zeng, H., VanDerveer, D. & Hill, C. L. A Supramolecular Tetra-Keggin Polyoxometalate [Nb4O6(α-Nb3SiW9O40)4]20−. Angew. Chem. Int. Ed. 38, 3205–3207 (1999).
Judd, D. A., Chen, Q., Campana, C. F. & Hill, C. L. Synthesis, solution and solid state structures, and aqueous chemistry of an unstable polyperoxo polyoxometalate:[P2W12(NbO2)6O56]12−. J. Am. Chem. Soc. 119, 5461–5462 (1997).
Li, S.-J. et al. Reactivity of Polyoxoniobates in Acidic Solution: Controllable Assembly and Disassembly Based on Niobium-Substituted Germanotungstates. Chem. - Eur. J. 16, 13435–13442 (2010).
Geng, Q., Liu, Q., Ma, P., Wang, J. & Niu, J. Synthesis, crystal structure and photocatalytic properties of an unprecedented arsenic-disubstituted Lindqvist-type peroxopolyoxoniobate ion: {As2Nb4(O2)4O14H1.5}4.5−. Dalton Trans. 43, 9843–9846 (2014).
Ohlin, C. A., Villa, E. M., Fettinger, J. C. & Casey, W. H. Distinctly Different Reactivities of Two Similar Polyoxoniobates with Hydrogen Peroxide. Angew. Chem. Int. Ed. 47, 8251–8254 (2008).
Zhao, S. et al. Assembly of niobium-phosphate cluster and in situ transition-metal-containing derivatives. CrystEngComm 19, 2768–2774 (2017).
Ozeki, T., Yamase, T., Naruke, H. & Sasaki, Y. Synthesis and Structure of Dialuminiohexaeuropiopentakis(hexaniobate): a High-Nuclearity Oxoniobate Complex. Inorg. Chem. 33, 409–410 (1994).
Naruke, H. & Yamase, T. Na8H18[{Er3O(OH)3(H2O)3}2Al2-(Nb6O19)5]·40.5H2O. Acta Crystallogr. C 52, 2655–2660 (1996).
Naruke, H. & Yamase, T. Structure of dialuminiohexalutetiopentakis(hexaniobate): comparison with europium and erbium analogues. J. Alloys Compd. 255, 183–189 (1997).
Yamase, T. & Naruke, H. Luminescence and Energy Transfer Phenomena in Tb3+/Eu3+-Mixed Polyoxometallolanthanoates K15H3[Tb1.4Eu1.6(H2O)3(SbW9O33)(W5O18)3]·25.5H2O and Na7H19[Tb4.3Eu1.7O2(OH)6(H2O)6Al2(Nb6O19)5]·47H2O. J. Phys. Chem. B 103, 8850–8857 (1999).
Li, C.-C. et al. Assembly of Saturated Nb/W Mixed-Addendum Polyoxometalate [P2W15Nb3O62]9− and Lanthanide Ions (Ln = Eu, Ce). Eur. J. Inorg. Chem. 2012, 3229–3234 (2012).
Li, S.-J. et al. Constructing nanosized polyanions with diverse structures by the self-assembly of W/Nb mixed-addendum polyoxometalate and lanthanide ion. CrystEngComm 14, 1397–1404 (2012).
Kim, G.-S., Zeng, H., Hill, C. L. et al. X-Ray Structure of Keggin-type Peroxo Polyoxometalate A-α-[Si(NbO2)3W9O3 7]7−. Bull.-KOREAN Chem. Soc. 24, 1005–1008 (2003).
Rhule, J., Weinstock, I., Hill, C. et al. Synthesis, X-ray structure, and hydrolytic chemistry of the highly potent antiviral polyniobotungstate A-α-[Si2Nb6W18O77]8−. Chem. Commun. 1651–1652 (1999).
Li, S.-J. et al. Niobium-substituted arsenotungstates: Controllable transformation between monomers and tetramer. Inorganica Chim. Acta 376, 296–301 (2011).
Abrahams, S. C., Collin, R. L. & Lipscomb, W. N. The crystal structure of hydrogen peroxide. Acta Crystallogr. 4, 15–20 (1951).
Brown, I. D. & Altermatt, D. Bond-valence parameters obtained from a systematic analysis of the Inorganic Crystal Structure Database. Acta Crystallogr. B 41, 244–247 (1985).
Bontchev, R. P. & Nyman, M. Evolution of Polyoxoniobate Cluster Anions. Angew. Chem. Int. Ed. 45, 6670–6672 (2006).
Wang, J.-P., Niu, H.-Y. & Niu, J.-Y. A novel Lindqvist type polyoxoniobate coordinated to four copper complex moieties: {Nb6O19[Cu(2,2′-bipy)]2[Cu(2,2′-bipy)2]2}·19H2O. Inorg. Chem. Commun. 11, 63–65 (2008).
Wang, K.-Y. et al. Ln12-Containing 60-Tungstogermanates: Synthesis, Structure, Luminescence, and Magnetic Studies. Chem. – Eur. J. 21, 18168–18176 (2015).
Xu, Q., Li, L., Liu, X. & Xu, R. Incorporation of Rare-Earth Complex Eu(TTA)4C5H5NC16H33 into Surface-Modified Si−MCM-41 and Its Photophysical Properties. Chem. Mater. 14, 549–555 (2002).
Yamase, T., Kobayashi, T., Sugeta, M. & Naruke, H. Europium(III) Luminescence and Intramolecular Energy Transfer Studies of Polyoxometalloeuropates. J. Phys. Chem. A 101, 5046–5053 (1997).
Shen, X. & Yan, B. A novel fluorescence probe for sensing organic amine vapors from a Eu3+ β-diketonate functionalized bio-MOF-1 hybrid system. J. Mater. Chem. C 3, 7038–7044 (2015).
Ritchie, C., Moore, E. G., Speldrich, M., Kögerler, P. & Boskovic, C. Terbium Polyoxometalate Organic Complexes: Correlation of Structure with Luminescence Properties. Angew. Chem. Int. Ed. 49, 7702–7705 (2010).
Chorazy, S., Nakabayashi, K., Ohkoshi, S. & Sieklucka, B. Green to Red Luminescence Switchable by Excitation Light in Cyanido-Bridged TbIII–WV Ferromagnet. Chem. Mater. 26, 4072–4075 (2014).
Meyer, L. V., Schönfeld, F. & Müller-Buschbaum, K. Lanthanide based tuning of luminescence in MOFs and dense frameworks – from mono- and multimetal systems to sensors and films. Chem. Commun. 50, 8093–8108 (2014).
Xin, M. et al. Single-composition white-emitting NaSrBO3:Ce3+, Sm3+, Tb3+ phosphors for NUV light-emitting diodes. J. Mater. Chem. C 3, 7286–7293 (2015).
Wang, Y.-L. et al. Syntheses, Structures, and Magnetic and Luminescence Properties of a New DyIII-Based Single-Ion Magnet. Inorg. Chem. 52, 7380–7386 (2013).
Li, P., Wang, Z., Yang, Z. & Guo, Q. Tunable blue–green emission phosphor Ca2PO4Cl:Ce3+, Tb3+: Luminescence and energy transfer. Opt. Commun. 332, 83–88 (2014).
Flynn, C. M. Jr. & Stucky, G. D. Sodium 6-niobo (ethylenediamine) cobaltate (III) and its chromate (III) analog. Inorg. Chem. 8, 178–180 (1969).
Sheldrick, G. M. A short history of SHELX. Acta Crystallogr. A 64, 112–122 (2008).
Sheldrick, G. M. Phase annealing in SHELX-90: direct methods for larger structures. Acta Crystallogr. A 46, 467–473 (1990).
Acknowledgements
This work was supported by the National Natural Science Foundation of China (grant numbers 21371048 and 21671056), the NSF from Henan Province (grant numbers 152102410027 and 162300410015), 2015 Young Backbone Teachers Foundation from Henan Province (2015GGJS-017), the Students Innovative Pilot Plan of Henan University (15NA002). D.Z. gratefully acknowledges financial support from China Scholarship Council (201608410252).
Author information
Authors and Affiliations
Contributions
D.Z., J.W. and J.N. designed the project. H.W. synthesized the compounds and performed IR, TG experiments. J.L., J.S., Y.W. performed FL experiments. Z.L. and P.M. analyzed X-ray data. H.W., D.Z. and J.N. wrote the paper.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, H., Li, J., Sun, J. et al. Synthesis, structure, and luminescent properties of a family of lanthanide-functionalized peroxoniobiophosphates. Sci Rep 7, 10653 (2017). https://doi.org/10.1038/s41598-017-10811-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-10811-2
- Springer Nature Limited