Abstract
The complex phase transitions of vanadium dioxide (VO2) have drawn continual attention for more than five decades. Dynamically, ultrafast electron diffraction (UED) with atomic-scale spatiotemporal resolution has been employed to study the reaction pathway in the photoinduced transition of VO2, using bulk and strain-free specimens. Here, we report the UED results from 10-nm-thick crystalline VO2 supported on Al2O3(0001) and examine the influence of surface stress on the photoinduced structural transformation. An ultrafast release of the compressive strain along the surface-normal direction is observed at early times following the photoexcitation, accompanied by faster motions of vanadium dimers that are more complex than simple dilation or bond tilting. Diffraction simulations indicate that the reaction intermediate involved on picosecond times may not be a single state, which implies non-concerted atomic motions on a multidimensional energy landscape. At longer times, a laser fluence multiple times higher than the thermodynamic enthalpy threshold is required for complete conversion from the initial monoclinic structure to the tetragonal lattice. For certain crystalline domains, the structural transformation is not seen even on nanosecond times following an intense photoexcitation. These results signify a time-dependent energy distribution among various degrees of freedom and reveal the nature of and the impact of strain on the photoinduced transition of VO2.
Similar content being viewed by others
Introduction
Vanadium dioxide (VO2) as a classic correlated material continues to attract great attention in various physics, chemistry, and materials science communities, because of its intriguing yet perplexing phase transitions since the first discovery1 as well as potential applications of the switching behaviors at around 340 K or below2,3,4,5,6. Parameters including temperature, pressure and strain7, stoichiometry and doping8, 9, structures and morphologies10, photoexcitation11, and voltage12 can all have significant influence on the phases and structures of VO2. As a result, the fundamental nature of the material’s insulator-to-metal transition has been a topic of major debate for decades13,14,15,16, with experiments and theory supporting either a decisive role of anharmonic lattice vibrations17, or collaborative Mott-Peierls (or Peierls-Mott) mechanisms emphasizing the dynamical V‒V dimers18,19,20, or principally the Mott physics21,22,23,24. On the ultrashort time scale, time-resolved optical pump-probe techniques have been employed to scrutinize the intricate interplay between nonequilibrium carriers and ionic motions in order to reveal the underlying physics25,26,27,28,29,30,31. These wide-ranging results, if taken together, suggest the high sensitivity of VO2 to local disorder and inhomogeneity on the nanoscale32, which signifies the need of more studies in detail with well-characterized specimen conditions33.
From the structural point of view, it is critical to understand, at the atomic level, phase-transition dynamics of a correlated material during the entire transformation process. To date, the reaction path for photoinduced structural phase transition of VO2 has been visualized using time-resolved diffraction methods on bulk34, 35 and strain-free specimens35,36,37,38. The general picture is that on the ultrashort time scale of few hundred femtoseconds (fs) or less, dilation of V‒V dimers in the initial low-temperature monoclinic structure (M 1) plays a critical role in the beginning stage of the phase change11, 34, 37, 39. Intracell structural34, 38 and orbital occupancy37 reorganization proceeds on a picosecond (ps) time, followed by lattice transformation to the tetragonal structure (R) on the time scale of tens to a hundred ps34,35,36, 38. While this stepwise transformation mechanism—with some differences in the details such as the involvement of the second monoclinic M 2 structure38—explains the observed diffraction dynamics, open questions still remain especially when results of the photo- and thermally-induced phase transitions are compared. For instance, a complete photoinduced conversion to the R phase was generally presumed at long times (hundreds of ps and later), although the laser fluence required37 appears to be many times higher than the energy needed thermally40 (the energy threshold question). The percolative nature and nanoscale inhomogeneity of the insulator-to-metal transition in thin films and microcrystals has been observed using near-field nanoimaging techniques21, 32, 33, 41, whereas a coherent motion of vanadium ions for all unit cells was generally used, at least for early delay times, in time-resolved diffraction studies34,35,36,37,38 (the question about homogeneity of the transition42, 43). Furthermore, how lattice strain affects and involves in the phase transition of VO2 7, 22, 23 at ultrashort times has not been well examined. To address these questions with a unified picture, it is necessary to conduct a time-resolved structural study using suitable specimens.
In this contribution, we report the results of ultrafast electron diffraction (UED) made on ultrathin VO2 films epitaxially grown on c-sapphire, which exhibit moderate out-of-plane compressive and in-plane tensile strains. The good crystallinity yet different epitaxial orientations of the VO2 domains allow us to identify the transformation dynamics that take place in different crystallographic directions at different stages of the photoinduced phase transition. Strong evidence is found for non-concerted motions of vanadium ions at ultrashort times, which are conceptually consistent with the observation of nanopuddles and nucleation during the thermal transition21, 33. The observed incomplete conversion to the R phase at long times also provides additional evidence for the material’s high sensitivity to local environments and agrees with the presence of superheated monoclinic structure(s) and suppression of the structural transition by strain7, 23, 44. These results indicate a converging picture for the phase transition of VO2 on the nanoscale.
Results
Sample characterization and strain analysis
The epitaxial VO2 ultrathin films were grown on Al2O3(0001) 10 × 10-mm2 substrates by using a polymer-assisted deposition technique45, 46. The 10-nm thickness was obtained via control of the viscosity of the precursor solution as well as spin-coating and thermal treatment process. Electron diffraction (ED) and x-ray diffraction (XRD) data show the results of similar patterns for every 60° azimuthal rotation (Fig. 1a‒c), signifying a 6-fold epitaxial relation between VO2 and the hexagonal plane of c-sapphire with an in-plane mismatch of ~ ± 2° given the \({\beta }_{{M}_{1}}\) angle of VO2 45, 47. We confirm the \({b}_{{M}_{1}}\) axis, not the \({c}_{{M}_{1}}\) axis, to be along the surface normal direction, namely VO2(010)//Al2O3(0001), by comparing the observed ED patterns with simulated ones based on the kinematic scattering theory (see Supplementary Figs. S1‒S2). This assignment is evident compared to that using XRD results only, given the close reciprocal lattice constants of \({b}_{{M}_{1}}^{\ast }\) and \({c}_{{M}_{1}}^{\ast }\) 47. Using the sapphire diffractions as references, a careful analysis of the XRD θ-2θ, ϕ, and 2θ-ϕ scan data indicates a moderate compressive strain of −0.31% in \({b}_{{M}_{1}}\) (VO2(020) at 2θ = 39.81° and VO2(040) at 2θ = 89.90°), a tensile strain of + 0.17% ( + 0.35%) in \({a}_{{M}_{1}}\) \(({c}_{{M}_{1}})\) (Supplementary Figs. S3‒S4), and a \({\beta }_{{M}_{1}}\) angle of 122.59° that is close to the bulk value48. By monitoring the forbidden diffractions for the R phase, i.e. those with an odd h index from the M 1 phase (Fig. 1a, dashed circles; hereafter referred to as R-forbidden diffractions), we obtained a critical transition temperature of T c = 344 K with a width of 3.1 K in the heating cycle (Fig. 1d), which is consistent with the previous resistivity measurements45.
Characterization of 10-nm ultrathin VO2 on Al2O3(0001). (a‒b) Electron diffraction patterns acquired at selected azimuthal angles (ϕ) at 297 K and 350 K, respectively. Dashed circles indicate a few spots that are symmetry-forbidden in the R phase. (c) X-ray diffraction from a ϕ scan showing the epitaxial relationship. The doublet pattern of VO2 at ~ ± 2° results from the mismatch between \({\beta }_{{M}_{1}}\) of VO2 and the matching angle (60°) of a perfect hexagon. (d) Intensity of the R-forbidden diffractions as a function of temperature in the heating cycle (black dots). A fit to an error function gives a full-width-at-half-maximum (FWHM) of 3.1 K. (e) Epitaxial relationship between VO2 (red and green arrows) and c-Al2O3 (blue and dashed lines). The pair of the \({a}_{{M}_{1}}\) and \({c}_{{M}_{1}}\) axes rotates azimuthally and follow the dashed lines. (f) Major reciprocal vectors in the \({a}_{{M}_{1}}-{c}_{{M}_{1}}\) plane that are associated with the patterns in a and b; black arrows for ϕ = 30°, 90°, 150° and color arrows for ϕ = 0°, 60°, 120°, 180°. (g) A scanning electron micrograph of the ultrathin specimen used. Scale bar: 200 nm.
Hence, each ED pattern acquired is the result of simultaneous probing of crystalline domains from different zone axes that are azimuthally rotated by 60°, with the epitaxial relation of VO2[100] and VO2[001]//Al2O3 \(\langle 10\bar{1}0\rangle \) (dashed lines in Fig. 1e). Such specimen conditions, instead of a randomly-oriented strain-free polycrystalline sample, enable the examination of the effects of surface stress on the VO2 dynamics along specific directions (see below). The zone axes that exhibit R-forbidden diffractions (Fig. 1a, right panel, and black arrows in Fig. 1f) were used in the experiments of photoinduced dynamics. A scanning electron micrograph shows the average size of crystalline domains to be ~170 nm (Fig. 1g).
Structural dynamics
Shown in Fig. 2 are the diffraction differences at selected delay times at the lowest (F ex = 4.4 mJ/cm2) and highest (F ex = 26.0 mJ/cm2) apparent fluences used, referenced to laser-off, nonexcited ED frames. The wavelength was 1030 nm (1.2-eV photons) for an above-gap photoexcitation. It is apparent that a much higher energy density is necessary for the 10-nm film to show sustaining diffraction, thus structural, changes on the nanosecond (ns) scale. The early intensity decrease of the (060) spot and others is visible with dark contrast, where inversion of the intensity change from the dark to bright contrast is seen for a few Bragg diffractions at the high fluence (Fig. 2b). Additionally, the (060) spot (with others also) exhibits a vertical position shift, as indicated by the adjacent dark and bright intensity differences; such a movement signifies a lattice change along the nanoscale, out-of-plane direction. It should be noted that transient electric field effects49, 50 were absent in the current study, as we have experimentally confirmed, at the highest fluence used, no observation of movement of the direct electron beam when it was partially blocked by and partially grazing above the laser-excited specimen. In what follows three categories of the rich structural dynamics observed will be discussed: (i) the ultrafast lattice expansion and strain release derived from the (060) movement, (ii) the in-plane motions of vanadium ions at ultrashort times, and (iii) the transformation to the R phase at long times.
Ultrafast strain release dynamics
By fitting the vertical profile along the center streak of an ED pattern, the position and intensity of the (060) spot at different times were obtained. An ultrafast lattice expansion in \({b}_{{M}_{1}}\) is seen, which reaches a peak value at > 10 ps with a time constant of τ fast = 4.6 ps (Fig. 3a, inset). This out-of-plane expansion in the nanometer dimension is reduced to a sustaining value with a time constant of τ slow ≈ 46 ps. Concurrently, the (060) intensity also exhibits a time-dependent response with similar time constants of τ fast and τ slow, first a drop followed by a rise to an enhanced intensity value that remains at long times (Fig. 3b). These observations signify lattice motions of all ions along the \({b}_{{M}_{1}}\) axis (including oxygen for the unit-cell expansion) however in a non-direct-path fashion (causing stepwise intensity changes) on the ps time scales, following the injection of an energy impulse into the ultrathin material.
Out-of-plane structural dynamics. (a‒b) Lattice expansion (black squares) and (060) diffraction intensity (black dots) as a function time at F ex = 26.0 mJ/cm2. The insets show the early-time dynamics. Blue lines are fits to a single exponential rise or decay function. (c) Lattice expansion at 13‒16 ps (red dots) and at 100‒500 ps (blue squares) as a function of F ex. The corresponding strain relative to the bulk value of \({b}_{{M}_{1}}\) is given on the right. The red arrow indicates the strain associated with the bulk value of b R . The standard deviations calculated from 20 experimental scans are shown for the lowest and highest F ex used.
It is noted that the peak value of the lattice expansion at t = 13‒16 ps is linearly proportional to F ex, except that a saturation appears at the highest apparent fluence used (Fig. 3c, red). The plateau value of 0.7% expansion means b t=12ps = 4.554 Å, which is incidentally almost the same as the bulk value b R of the R phase51. Such a result signifies a complete release of strain at ultrashort times in a highly excited state, from a compressed structure at equilibrium (−0.31% relative to the M 1 bulk) to the supposed final structure of R along the noncorrelated b axis, even though the multi-stage ionic motions are still ongoing and the R phase is yet to be reached. Given the absorption coefficient at 1.2 eV52, photoexcitation of the VO2 specimen is nearly uniform across the 10-nm film thickness. Thus, the observed structural expansion is reasonably the result of lattice anharmonicity in a photoexcited state and is less relevant to a soundwave propagation or diffusion process53.
However, at long times, the largest sustainable lattice expansion in a c-sapphire-supported ultrathin film is found close to that for strain-free M 1, or about −0.34% from the R bulk, for F ex ≥ 15.0 mJ/cm2 (Fig. 3c, blue). Moreover, no long-term lattice expansion is seen at F ex < 5 mJ/cm2, whose excitation threshold behavior coincides with those reported in previous time-resolved studies26,27,28,29, 34, 35, 37, 38. These results, as well as the long-time dynamics discussed below, suggest that the photoinjected energy is redistributed among multiple components of the structural dynamics, including the overshooting and then reduced amount of strain release as well as the intracell ionic motions along different directions (see below). We argue that this may be one of the reasons why an energy density much higher than the enthalpy change (translated to be ~5 mJ/cm2 with 1 to 2-eV photons35) is needed to cause the complete transition from M 1 to R by photoexcitation, even though an onset threshold close to the thermodynamic requirement has often been seen for ultrafast initiation of the structural phase change in bulk and thicker-film specimens28, 35.
Intracell motions of vanadium ions
Intensity changes on varied time scales are observed for diffractions with nonzero \({h}_{{M}_{1}}\) and \({l}_{{M}_{1}}\) indices. For the R-forbidden (i.e., odd-\({h}_{{M}_{1}}\)) spots, their intensities decrease with an effective time constant of τ slow ≈ 46 ps (excluding the early-stage 12 ps), which is the same as that of the (060) intensity rise in the second stage (Fig. 4a). However, an ultrafast intensity drop is specifically seen for \((46\bar{2})/(\bar{4}62)\) within the instrumental response time while the intensity of \((262)/(\bar{2}6\bar{2})\) remains unchanged; afterward, both sets of diffractions show prominent intensity increase on the time scale of τ slow (Fig. 4b and Supplementary Fig. S5). Such multi-stage diffraction evolution is qualitatively consistent with the earlier UED studies34, 35, 37, 38, although we will point out the distinct differences found here in a strained ultrathin specimen.
Time-resolved diffraction changes and intracell motions of vanadium ions. (a) Intensity change of the (060) (black) and R-forbidden spots (red) as a function of time. The solid lines are fits to a single exponential rise or decay function. Inset: Early-time dynamics. (b) Intensity profiles across the \((46\bar{2})/(\bar{4}62)\) and \((262)/(\bar{2}6\bar{2})\) diffractions at selected early times, referenced to laser-off, nonexcited frames. (c) Intracell motions of vanadium ions in the \({a}_{{M}_{1}}-{c}_{{M}_{1}}\) (i.e., x‒z) plane considered. The ions of each pair move in opposite directions with the same distance. Simulated intensity changes of \((46\bar{2})/(\bar{4}62)\) (left panels) and \((262)/(\bar{2}6\bar{2})\) (right panels), referenced to the unperturbed state, are shown for (d) concerted, same movements for both pairs, (e) movements of the first pair only, (f) movements of the second pair only, and (g) concerted motions involving bond-length change and bond twisting for the two pairs in a unit cell. The white dashed lines denote the parameters that give the experimentally observed intensity changes for the respective diffractions. The yellow dashed circles indicate the potential solutions, taking into account both left and right panels.
To unravel the structural dynamics of the photoinduced phase transition, simulations of diffraction intensities were conducted based on the kinematic scattering theory,
where \({f}_{j}^{(e)}(s)\) is the atomic scattering factor of the j-th atom as a function of s, the momentum transfer \(s=|\vec{s}|=(4\pi /\lambda )\cdot \sin (\theta /2)\), λ = 0.0698 Å is the wavelength of the probe electrons, θ is the total scattering angle, and \({\vec{r}}_{j}=({x}_{j}+{\rm{\Delta }}{x}_{j},{y}_{j}+{\rm{\Delta }}{y}_{j},{z}_{j}+{\rm{\Delta }}{z}_{j})\) is the j-th atom’s position with the transient movement within a unit cell. For the observed ultrafast dynamics within the first 3 ps (during which the strain release dynamics and ionic motions along \({b}_{{M}_{1}}\) are still underdeveloped), we first examined a few scenarios of concerted vanadium-ion movements in the \({a}_{{M}_{1}}-{c}_{{M}_{1}}\) (i.e., x‒z) plane in a unit cell, which, for the two ions of a given pair, are in opposite directions but with the same distance (Fig. 4c, red and light blue arrows). Potential solutions were sought to match with the observed intensity decrease of \((46\bar{2})/(\bar{4}62)\) by 24% and no change of \((262)/(\bar{2}6\bar{2})\), including the cases for (1) concerted, same movements for both V‒V pairs in an M 1 unit cell, whose model may share a similar picture as the previous observations of simultaneous bond dilation34, 37 (Fig. 4d); (2) movements of only the first pair with the second being stationary (Fig. 4e); (3) movements of only the second pair with the first being stationary (Fig. 4f); and (4) concerted movements with the two pairs switching the amounts of their bond-length change and twisting motion, whose model originates from the structural comparison between M 1 and M 2 38, 51 (Fig. 4g). However, the theoretical solutions found in the first, second and fourth models are counterintuitive, either positive Δx 1 in Fig. 4d‒e which signifies contraction of the V‒V dimers, or highly negative Δz 1 in Fig. 4g which leads to even more tilt for the first pair instead of a straighter alignment. The solution in Fig. 4f seems physically plausible but indicates highly non-uniform ionic motions—large negative Δx 2 and moderately positive Δz 2 which means nearly equal bond length with reduced tilt for the second V‒V chain, without modification of the first chain.
Intriguingly, the potential solution in Fig. 4f can also produce the bond-breaking feature34, 37 and similar relative intensity changes seen in Fig. 2C at 1 ps of ref. 37; or lead to an intermediate structure containing pairs with different extents of dimerization and tilt and also give resembling relative intensity changes seen in Fig. 4a at 1 ps of ref. 38. However, for a later time at ~20 ps (when the release of strain matures), simulations of the ED pattern changes considering the reaction paths from M 1 to homogeneous bond-breaking, to M 2, or to R (Supplementary Fig. S6) fail to produce a result that matches well with the experimentally observed differences (Fig. 2). Taken together, these findings suggest that consideration of a certain structure (bond-breaking, M 2, or R) for all unit cells as the intermediate state may not be suitable, at least in the present case using a strained ultrathin specimen. This is in contrast with previous studies34, 37, 38.
We note the large position changes of vanadium ions in a unit cell with little adjustments of oxygen when comparing the M 1, M 2, and R structures (Supplementary Fig. S7). With the various degrees of freedom possibly involved on the multidimensional energy landscape, it is highly probable that under the influence of photoexcited carriers with excess above-gap energy, the bonded vanadium ions generally move away from each other due to the dynamical nature of the V‒V dimers18,19,20 but also exhibit hot motions in other directions. Small differences in the local chemical environments and the involvement of strain54 (such as that along \({b}_{{M}_{1}}\) here), as well as higher photon energy above the band gap, likely cause additional non-uniform (hence non-concerted) motions of vanadium ions in the photoexcited material, which may further influence the nucleation of transformed domains at later times. We believe that this picture provides a connection between the photoinduced and thermally-induced phase transitions of VO2, where the transformation proceeds in a mesoscopic, inhomogeneous fashion under the influence of local parameters such as strain and defects33.
Incomplete conversion to the tetragonal structure at long times
Shown in Fig. 5a‒b are the observed ED differences across the phase transition of VO2 using, respectively, thermal heating from 295 to 370 K and photoexcitation at 26.0 mJ/cm2 between negative and 2.74-ns times. The apparent deviation between the two patterns contradicts the usual assumption that the photoinduced conversion from M 1 to R would complete at long times, at least for high fluences. To investigate the cause, theoretical ED simulations were conducted considering the 6-fold epitaxial relationship and possible combinations of the diffractions from the three zone axes (Fig. 1e‒f, black dashed lines and arrows). The agreement between Fig. 5a,c is satisfactory, which is expected for complete conversion of all crystalline grains from all three zones. However, to account for the slight bright contrast seen on the middle row (spots indicated by arrows in Fig. 5b), at least the pattern from the \(\pm (2{c}_{{M}_{1}}^{\ast }-{a}_{{M}_{1}}^{\ast })\) direction, or essentially the diffraction difference from the R-forbidden \({(\bar{1}52)}_{{M}_{1}}/{(15\bar{2})}_{{M}_{1}}\) spots, must be excluded. A better agreement is then resulted (Fig. 5b,d).
Phase transformation of strained ultrathin VO2 and its fluence dependence. (a‒b) Experimentally observed diffraction differences across the phase transition, induced by thermal heating and by photons, respectively. The main deviation is indicated by arrows. (c‒d) Simulated diffraction differences between the M 1 and R phases, including all three zone axes and only two of the three, respectively. (e) Intensity change of the R-forbidden spots as a function of the apparent fluence used, for the specified temporal regions. The error bars are the standard deviations calculated from 10‒20 scans. (f) Femtosecond transient reflectivity at a probe wavelength of 515 nm for various fluences.
The exclusion of contribution from a specific zone axis indicates the presence of untransformed crystalline grains on the ns time scale even after all prior fast dynamics have concluded. Thus, such evidence gives strong support for inhibition of the structural transition by surface stress and persistence of those domains in a superheated state for extended times23, 44. This result may not be surprising, as signs for an inhomogeneous, impeded phase change have appeared in a former study using time-resolved x-ray diffraction microscopy with a sub-ns temporal resolution at a relatively high excitation fluence53. It is also intriguing that the \(\pm (2{c}_{{M}_{1}}^{\ast }-{a}_{{M}_{1}}^{\ast })\) direction is the \({c}_{{M}_{1}}\) axis, which exhibits a greater tensile strain compared to that in other directions. This shows the potential of materials engineering to control a phase transformation with different stimuli including strain55. Here, we note that inhibition of the structural transformation is observed in the photoexcitation experiments where only the supported ultrathin film is photoheated on a cool, unexcited substrate, but not in the thermodynamic measurements where the whole specimen is heated uniformly. In addition, on the atomic scale, it is reasonable that the interfacial structures are not fully rotationally equivalent for the three zone axes due to the lattice mismatch, the growth process, and contact and overlaying of crystalline domains as seen in Fig. 1g.
For the other two zone axes, the R-forbidden \((161)/(\bar{1}6\bar{1})/(26\bar{1})/(\bar{2}61)\) spots lose their intensities completely on sub-ns and ns times at ≥ 20 mJ/cm2. We note that this saturation threshold value obtained from long-time structural dynamics matches with that reported using photoinduced transient reflectivity measurements for ultrafast femtosecond phonon oscillations (Fig. 5e)11. Such consistency leads us to consider that, without the inhibition by surface stress, a complete photoinduced phase transition of VO2 at long times (both electronically and structurally) would require 4 to 5 times of the energy density needed by the thermal phase transition, if 1 to 2-eV photons are used in specimens with strain and/or connected crystalline domains including bulk. In contrast, the initiation threshold is again seen at a lower value of approximately 5 to 7 mJ/cm2 where in our transient reflectivity experiments the positive peak begins to be overtaken by the large negative decrease (Fig. 5e‒f), which is consistent with previous reports11, 29.
Discussion
Based on the observed strain release, ultrafast intracell, and long-time structural dynamics as well as the threshold behavior, it is convincing that the excess energy from photoexcitation is channeled into other degrees of freedom, with different time constants, on the multidimensional energy landscape beyond simple breaking of the correlated vanadium chains at least for the current sample condition with strain and connected crystalline domains. This may be analogous to intramolecular vibrational energy redistribution (IVR) observed in photoexcited molecular reactions56, although for correlated materials sample conditions such as strain, doping, and stoichiometry can all play a significant role in the redistribution phenomena. Given the converging picture obtained from both dynamics and thermodynamic studies, we believe that the energy redistribution mechanism during the photoinduced phase transition of VO2 may not be limited to strained ultrathin specimens but rather broadly applicable to other specimen conditions, especially solid-supported films with domain connectivity. Such a phenomenon has implications for potential use of VO2 involving photons or other forms of energy impulse. For example, the higher energy input required for the photoinduced phase transition when strain and/or connected crystalline domains are involved may be advantageous or disadvantageous depending on the applications. Furthermore, it is possible to use photons with low energy for efficient photodoping, to direct the flow of and hence reduce the energy input38. Given the present results, it is now crucial to use ultrafast diffraction and spectroscopic methods to study specimens with single-domain crystalline nanobeams and with different chemical doping, in order to examine their impacts on the photoinduced phase transition dynamics and further explore useful control parameters.
In summary, the nature of photoinduced phase transition of VO2 is revealed using ultrafast electron diffraction on epitaxially grown ultrathin specimens with moderate strain. The unique specimen conditions allow for investigation of the impacts caused by surface stress on the photoinduced transition dynamics of VO2 along different crystallographic directions. Through analysis of the time-dependent changes of Bragg diffractions, the strain release dynamics and ultrafast intracell motions of vanadium ions at early times were unraveled, and the material’s transformation to the presumed final structure was examined up to the nanosecond scale. Strong evidence is found for energy redistribution among the aforementioned structural dynamics in different degrees of freedom and for nonconcerted ionic motions beyond a well-defined reaction intermediate. The presence of the moderate strain and surface stress can lead to inhibition of the structural transition via photoexcitation, within the temporal window observed. We believe that the insights gained through the current study using time-resolved electron diffraction may also be relevant to the photoinduced phase transitions of other correlated materials.
Methods
Sample Characterization
Reflection high-energy electron diffraction experiments were performed using a near-parallel beam of 30-keV electrons with a beam diameter of ~85 μm at the specimen. Precision control of the sample position was achieved using a 5-axis high-resolution manipulator (3 translational and 2 rotational degrees of freedom, from McAllister Technical Services) coupled to a cryostat (Janis Research) with an internal heater that enables experiments in the temperature range between < 20 K and 500 K. Temperature was measured with 0.01 K precision at the back of the copper sample holder, and specimen temperatures were independently calibrated with an accuracy of < 1 K by a K-type thermocouple directly attached to the sample surface. Through azimuthal rotations, electron diffractions acquired at different zone axes were used to identify the orientation of VO2 films. The transmission-like patterns signify the probing of inner regions beyond the surface layer. The structural phase transition of the specimens was monitored as a function of temperature.
X-ray diffraction (XRD) experiments were conducted using a Rigaku SmartLab diffractometer with the Cu Kα radiation (λ = 1.54060 Å) and a 5-mm limiting slit. The out-of-plane (θ-2θ) scan was used to determine the sample orientation along the surface normal direction. To obtain additional confirmation for the epitaxial relationship, two types of in-plane XRD measurements were made using the parallel-beam alignment at fixed grazing incidence angles (ω). The first is the ϕ scan with the goniometer being rotated azimuthally whereas the detector was fixed at the corresponding 2θ of the plane of interest, with ω being 0.05° and 0.5° for the VO2 film and the substrate, respectively. The second is the 2θ-ϕ scan where the azimuthal rotations of the sample and the detector were coupled.
Ultrafast electron diffraction
Time-resolved electron diffraction experiments were carried out using the fundamental output of an amplified laser system (Pharos-SP, Light Conversion) for photoexcitation (at 1030 nm, 1.20 eV, with a full-width-at-half-maximum (FWHM) of 170 fs). The FWHM of the footprint of the excitation beam was ~500 μm following a near-normal impingement at the specimen. Part of the fundamental laser beam passed through two stages of second-harmonic generation; the resulting ultraviolet (257 nm) laser beam were directed and tightly focused onto a 25-μm LaB6 emitter tip, embedded in a guard ring, inside the electron gun (Kimball Physics) to generate photoelectron pulses as the probe. At the number of electrons ( < 103) per pulse used, the temporal width at the specimen was below 1 ps57, 58.
For structural dynamics, the electron pulses were focused to a 15-μm spot in FWHM, characterized using the knife-edge method. At the incidence of 2.66°, the electron footprint in the reflection geometry was about 300 μm and well within the laser excitation region. The scheme of pulse-front tilt was not employed. The resulting instrumental response time, estimated to be 3 ps given the velocity mismatch between photons and grazing electrons, was experimentally confirmed. At each delay time, both laser-on (photoexcited) and laser-off (nonexcited) frames were acquired in order to capture the actual photoinduced diffraction dynamics and minimize any long-term changes as a result of the laboratory conditions or potential accumulated specimen modifications. Reproducibility of the reported observations was confirmed by repeating the experiments at different apparent fluences multiple times with more than 10 scans and finding the same dynamics in each scan.
To confirm a pure structural origin for the diffraction changes observed, experiments regarding movements of the direct electron beam were conducted, with the VO2 specimen surface being parallel to and partially blocking the electron beam path for potential influence caused by Columbic repulsion between different groups of electrons above the photoexcited region49, 50. At the highest fluence used (26.0 mJ/cm2) no beam movement was observed, thus confirming the absence of photoinduced transient electric field effects. Another piece of supporting evidence is the lack of any background intensity change near the shadow edge at all delay times. Therefore, the lattice expansion associated with the position shifts of the (060) diffraction is real.
Data and materials availability
All data needed to evaluate the conclusions in the paper are present in the paper and the Supplementary Information. Materials related to this paper may be requested from the authors.
References
Morin, F. J. Oxides which show a metal-to-insulator transition at the Néel temperature. Phys. Rev. Lett. 3, 34–36 (1959).
Yang, Z., Ko, C. Y. & Ramanathan, S. Oxide electronics utilizing ultrafast metal-insulator transitions. Annu. Rev. Mater. Res. 41, 337–367 (2011).
Liu, K. et al. Giant-amplitude, high-work density microactuators with phase transition activated nanolayer bimorphs. Nano Lett. 12, 6302–6308 (2012).
Liu, M. K. et al. Terahertz-field-induced insulator-to-metal transition in vanadium dioxide metamaterial. Nature 487, 345–348 (2012).
Gao, Y. F. et al. Nanoceramic VO2 thermochromic smart glass: A review on progress in solution processing. Nano Energy 1, 221–246 (2012).
Wang, T. Y. et al. Increasing efficiency, speed, and responsivity of vanadium dioxide based photothermally driven actuators using single-wall carbon nanotube thin-films. ACS Nano 9, 4371–4378 (2015).
Park, J. H. et al. Measurement of a solid-state triple point at the metal-insulator transition in VO2. Nature 500, 431–434 (2013).
Holman, K. L. et al. Insulator to correlated metal transition in V1-xMoxO2. Phys. Rev. B 79, 245114 (2009).
Patridge, C. J., Whittaker, L., Ravel, B. & Banerjee, S. Elucidating the influence of local structure perturbations on the metal-insulator transitions of V1−xMoxO2 nanowires: Mechanistic insights from an x-ray absorption spectroscopy study. J. Phys. Chem. C 116, 3728–3736 (2012).
Whittaker, L., Patridge, C. J. & Banerjee, S. Microscopic and nanoscale perspective of the metal-insulator phase transitions of VO2: Some new twists to an old tale. J. Phys. Chem. Lett. 2, 745–758 (2011).
Wegkamp, D. & Stähler, J. Ultrafast dynamics during the photoinduced phase transition in VO2. Prog. Surf. Sci. 90, 464–502 (2015).
Zimmers, A. et al. Role of thermal heating on the voltage induced insulator-metal transition in VO2. Phys. Rev. Lett. 110, 056601 (2013).
Goodenough, J. B. The two components of crystallographic transition in VO2. J. Solid State Chem. 3, 490–500 (1971).
Zylbersztejn, A. & Mott, N. F. Metal-insulator transition in vanadium dioxide. Phys. Rev. B 11, 4383–4395 (1975).
Wentzcovitch, R. M., Schulz, W. W. & Allen, P. B. VO2: Peierls or Mott-Hubbard? A view from band theory. Phys. Rev. Lett. 72, 3389–3392 (1994).
Rice, T. M., Launois, H. & Pouget, J. P. Comment on “VO2: Peierls or Mott-Hubbard? A view from band theory”. Phys. Rev. Lett. 73, 3042–3042 (1994).
Budai, J. D. et al. Metallization of vanadium dioxide driven by large phonon entropy. Nature 515, 535–539 (2014).
Biermann, S., Poteryaev, A., Lichtenstein, A. I. & Georges, A. Dynamical singlets and correlation-assisted peierls transition in VO2. Phys. Rev. Lett. 94, 026404 (2005).
Haverkort, M. W. et al. Orbital-assisted metal-insulator transition in VO2. Phys. Rev. Lett. 95, 196404 (2005).
Weber, C. et al. Vanadium dioxide: A Peierls-Mott insulator stable against disorder. Phys. Rev. Lett. 108, 256402 (2012).
Qazilbash, M. M. et al. Mott transition in VO2 revealed by infrared spectroscopy and nano-imaging. Science 318, 1750–1753 (2007).
Laverock, J. et al. Direct observation of decoupled structural and electronic transitions and an ambient pressure monocliniclike metallic phase of VO2. Phys. Rev. Lett. 113, 216402 (2014).
Yang, M. M. et al. Suppression of structural phase transition in VO2 by epitaxial strain in vicinity of metal-insulator transition. Sci. Rep. 6, 23119 (2016).
Brito, W. H., Aguiar, M. C. O., Haule, K. & Kotliar, G. Metal-insulator transition in VO2: A DFT + DMFT perspective. Phys. Rev. Lett. 117, 056402 (2016).
Cavalleri, A. et al. Evidence for a structurally-driven insulator-to-metal transition in VO2: A view from the ultrafast timescale. Phys. Rev. B 70, 161102(R) (2004).
Kübler, C. et al. Coherent structural dynamics and electronic correlations during an ultrafast insulator-to-metal phase transition in VO2. Phys. Rev. Lett. 99, 116401 (2007).
Hilton, D. J. et al. Enhanced photosusceptibility near T c for the light-induced insulator-to-metal phase transition in vanadium dioxide. Phys. Rev. Lett. 99, 226401 (2007).
Pashkin, A. et al. Ultrafast insulator-metal phase transition in VO2 studied by multiterahertz spectroscopy. Phys. Rev. B 83, 195120 (2011).
Wall, S. et al. Ultrafast changes in lattice symmetry probed by coherent phonons. Nat. Commun. 3, 721 (2012).
Cocker, T. L. et al. Phase diagram of the ultrafast photoinduced insulator-metal transition in vanadium dioxide. Phys. Rev. B 85, 155120 (2012).
Wegkamp, D. et al. Instantaneous band gap collapse in photoexcited monoclinic VO2 due to photocarrier doping. Phys. Rev. Lett. 113, 216401 (2014).
O’Callahan, B. T. et al. Inhomogeneity of the ultrafast insulator-to-metal transition dynamics of VO2. Nat. Commun. 6, 6849 (2015).
Liu, M. K. et al. Phase transition in bulk single crystals and thin films of VO2 by nanoscale infrared spectroscopy and imaging. Phys. Rev. B 91, 245155 (2015).
Baum, P., Yang, D.-S. & Zewail, A. H. 4D visualization of transitional structures in phase transformations by electron diffraction. Science 318, 788–792 (2007).
Yang, D.-S., Baum, P. & Zewail, A. H. Ultrafast electron crystallography of the cooperative reaction path in vanadium dioxide. Struct. Dyn. 3, 034304 (2016).
Newton, M. C. et al. Time-resolved coherent diffraction of ultrafast structural dynamics in a single nanowire. Nano Lett. 14, 2413–2418 (2014).
Morrison, V. R. et al. A photoinduced metal-like phase of monoclinic VO2 revealed by ultrafast electron diffraction. Science 346, 445–448 (2014).
Tao, Z. S. et al. The nature of photoinduced phase transition and metastable states in vanadium dioxide. Sci. Rep. 6, 38514 (2016).
Cavalleri, A. All at once. Science 318, 755–756 (2007).
Berglund, C. N. & Guggenheim, H. J. Electronic properties of VO2 near semiconductor-metal transition. Phys. Rev. 185, 1022–1033 (1969).
Dönges, S. A. et al. Ultrafast nanoimaging of the photoinduced phase transition dynamics in VO2. Nano Lett. 16, 3029–3035 (2016).
Corr, S. A., Shoemaker, D. P., Melot, B. C. & Seshadri, R. Real-space investigation of structural changes at the metal-insulator transition in VO2. Phys. Rev. Lett. 105, 056404 (2010).
Mun, B. S. et al. Nonpercolative metal-insulator transition in VO2 single crystals. Phys. Rev. B 84, 113109 (2011).
Cao, J. et al. Extended mapping and exploration of the vanadium dioxide stress-temperature phase diagram. Nano Lett. 10, 2667–2673 (2010).
Ji, Y. D. et al. Epitaxial growth and metal-insulator transition of vanadium oxide thin films with controllable phases. Appl. Phys. Lett. 101, 071902 (2012).
Ji, Y. D. et al. Role of microstructures on the M1-M2 phase transition in epitaxial VO2 thin films. Sci. Rep. 4, 4854 (2014).
Zhao, Y. et al. Structural, electrical, and terahertz transmission properties of VO2 thin films grown on c-, r-, and m-plane sapphire substrates. J. Appl. Phys. 111, 053533 (2012).
Longo, J. M. & Kierkegaard, P. A refinement of structure of VO2. Acta Chem. Scand. 24, 420–426 (1970).
Park, H. & Zuo, J. M. Direct measurement of transient electric fields induced by ultrafast pulsed laser irradiation of silicon. Appl. Phys. Lett. 94, 251103 (2009).
Raman, R. K., Tao, Z., Han, T. R. & Ruan, C.-Y. Ultrafast imaging of photoelectron packets generated from graphite surface. Appl. Phys. Lett. 95, 181108 (2009).
Marezio, M., McWhan, B., Dernier, P. D. & Remeika, J. P. Structural aspects of metal-insulator transitions in Cr-doped VO2. Phys. Rev. B 5, 2541–2551 (1972).
Verleur, H. W., Barker, A. S. Jr. & Berglund, C. N. Optical properties of VO2 between 0.25 and 5 eV. Phys. Rev. 172, 788–798 (1968).
Zhu, Y. et al. Mesoscopic structural phase progression in photo-excited VO2 revealed by time-resolved x-ray diffraction microscopy. Sci. Rep. 6, 21999 (2016).
Liu, M. K. et al. Anisotropic electronic state via spontaneous phase separation in strained vanadium dioxide films. Phys. Rev. Lett. 111, 096602 (2013).
Cao, J. et al. Strain engineering and one-dimensional organization of metal-insulator domains in single-crystal vanadium dioxide beams. Nat. Nanotechnol. 4, 732–737 (2009).
Nesbitt, D. J. & Field, R. W. Vibrational energy flow in highly excited molecules: Role of intramolecular vibrational redistribution. J. Phys. Chem. 100, 12735–12756 (1996).
Gahlmann, A., Park, S. T. & Zewail, A. H. Ultrashort electron pulses for diffraction, crystallography and microscopy: Theoretical and experimental resolutions. Phys. Chem. Chem. Phys. 10, 2894–2909 (2008).
Lobastov, V. A. et al. in Ultrafast optics IV (eds Krausz, F., Korn, G., Corkum, P. & Walmsley, I. A.) 419-435 (Springer, 2003).
Acknowledgements
The authors acknowledge K. Mueller for her help with grazing-incidence x-ray diffraction, and C.-Y. Ruan and Z. Tao for useful discussions. X.H., N.P. and D.-S.Y. acknowledge the support from the R. A. Welch Foundation (Grant No. E-1860) and the University of Houston. W.L., Y.L. and C.C. acknowledge the support from the National Natural Science Foundation of China (No. 11329402). A.J.J. thanks the support from the R. A. Welch Foundation (Grant No. E-0024).
Author information
Authors and Affiliations
Contributions
D.-S.Y. conceived this topic and discussed it with A.J.J. and C.C. The UED measurements and analyses were performed by X.H., N.P., and D.-S.Y. The XRD characterization was performed by N.P. The optimization and fabrication of the epitaxial VO2 films was made by W.L., Y.L., and C.C. The paper was written by D.-S.Y. with contributions from X.H. and N.P. All authors reviewed the manuscript
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
He, X., Punpongjareorn, N., Liang, W. et al. Photoinduced Strain Release and Phase Transition Dynamics of Solid-Supported Ultrathin Vanadium Dioxide. Sci Rep 7, 10045 (2017). https://doi.org/10.1038/s41598-017-10217-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-10217-0
- Springer Nature Limited
This article is cited by
-
Decoupling the metal insulator transition and crystal field effects of VO2
Scientific Reports (2021)
-
Large non-thermal contribution to picosecond strain pulse generation using the photo-induced phase transition in VO2
Nature Communications (2020)
-
Bidirectional micro-actuators based on eccentric coaxial composite oxide nanofiber
Nano Research (2020)
-
Natural and induced growth of VO2 (M) on VO2 (B) ultrathin films
Scientific Reports (2018)